Abstract
Fine-grained SiC-AlN ceramic alloys were synthesized by the reaction of silicon nitride and aluminium nitride powders with additions of carbon and CaO. X-ray diffraction and STEM-EDX analysis showed that they are single phase solid solutions. The SiC-AlN alloys were sintered without additives to full density by hot isostatic pressing at 2173 K and 200 MPa for 2 h. The flexural strength, microhardness and fracture toughness were measured and it was found that SiC-AlN alloys have double the strength and slightly higher fracture toughnesses than conventional monolithic SiC.
Similar content being viewed by others
References
F. Thümmler, in “Sintering processes”, Materials Science Research, Vol. 13, edited by G. C. Kuczynski (Plenum, New York and London, 1980) p. 247.
I. B. Cutler, P. D. Miller, W. Ranfaniello, H. K. Park, D. P. Thompson and K. H. Jark, Nature 275 (1978) 434.
W. Rafaniello, K. Cho and A. V. Virkar, J. Mater. Sci. 16 (1981) 3479.
R. Ruh and A. Zangvil, J. Amer. Ceram. Soc. 65 (1982) 260.
S. K. Kuo, Z. C. Jou, A. V. Virkar and W. Rafaniello, J. Mater. Sci. 21 (1986) 3019.
S. Y. Kuo, A. V. Virkar and W. Rafaniello, J. Amer. Ceram. Soc. 70 (1987) C-125.
A. Zangvil and R. Ruh, ibid. 71 (1988) 884.
M. M. Dobson, in “Silicon Carbide Alloy”, Research Reports in Materials Science, Series One, edited by P. E. Evans (Parthenon, UK, 1986) p. 86.
Y. Sugahara, K. Sugimoto, K. Kuroda and C. Kato, J. Mater. Sci. 16 (1981) 3479.
Jing-Feng Li, A. Kawasaki and R. Watanabe, J. Jpn Soc. Powder Powder Metall. 36 (1989) 740.
S. Dutta, Adv. Ceram. Mater. 3 (1988) 257.
K. Niihara, R. Morena and D. P. Hasselman, J. Mater. Sci. Lett. 1 (1982) 13.
H. Tanaka, Y. Inomata, K. Hara and H. Hasegawa, ibid. 4 (1985) 315.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Li, JF., Watanabe, R. Preparation and mechanical properties of SiC-AlN ceramic alloy. J Mater Sci 26, 4813–4817 (1991). https://doi.org/10.1007/BF00612422
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00612422