Abstract
As an important regulation parameter, shearing process during bitumen modification can be easily adjusted. However, the effect of shearing time on the properties of modified bitumen and its original reason is still unclear. To explore this concern, bitumen/polyethylene (PE)/ethylene-vinyl acetate copolymer (EVA) blend (PMB) with fixed weight ratio of 100/5/5 was studied by imposing different shear time within 1–4 h under 180 °C. It was found longer shearing time could improve rutting resistance but deteriorate the ductility at low temperature. Due to the crystalline nature of PE/EVA and the immiscibility between these polymers and bitumen, the possible reason was firstly explored on terms of crystallinity and phase structure of PMBs. A shearing-heating system connected with optical microscopy was innovatively employed for in-situ phase structure observation. After excluding both effects of crystallization and phase separation on the different properties of PMBs, the relationship between thermal ageing and shearing was subsequently explored. An in-situ quiescent TGA measurement under 180 °C for 3 h revealed a continuous weight loss of PMBs. FTIR results suggested the thermal-oxidation behavior of EVA. Combined these two results, the thermal-oxidation process and hardening effect were the main reasons for different properties of PMBs with different shearing time.
Similar content being viewed by others
References
Rossi CO, Spadafora A, Teltayev B, Izmailova G, Amerbayev Y, Bortolotti V (2015) Polymer modified bitumen: Rheological properties and structural characterization. Colloids Surf, A 480:390–397
Padhan RK, Sreeram A (2018) Enhancement of storage stability and rheological properties of polyethylene (PE) modified asphalt using cross linking and reactive polymer based additives. Constr Build Mater 188:772–780
Karahrodi MH, Jazani OM, Paran SMR, Formela K, Saeb MR (2017) Modification of thermal and rheological characteristics of bitumen by waste PET/GTR blends. Constr Build Mater 134:157–166
Attaelmanan M, Feng CP, Al-Hadidy A (2011) Laboratory evaluation of HMA with high density polyethylene as a modifier. Constr Build Mater 25:2764–2770
Perezlepe A, Martinezboza FJ, Gallegos C (2005) Influence of polymer concentration on the microstructure and rheological properties of high-density polyethylene (HDPE)-modified bitumen. Energy Fuels 19:1148–1152
Hınıslıoğlu S, Ağar E (2004) Use of waste high density polyethylene as bitumen modifier in asphalt concrete mix. Mater Lett 58:267–271
Yousefi AA (2003) Polyethylene dispersions in bitumen: The effects of the polymer structural parameters. J Appl Polym Sci 90:3183–3190
Padhan RK, Gupta AA, Sreeram A (2019) Effect of cross-linking agent on ethylene vinyl acetate/polyoctenamer modified bitumen. Road Mater Pavement Des 20:1615–1623
Su J, Chen S, Zhang J, Xu Z (2010) Combined effect of VA content and pH level of filler on properties of EPDM/SmBO3 and EPDM/ATO composites reinforced by three types of EVA. J Appl Polym Sci 117:1741–1749
Henderson AM (1993) Ethylene-vinyl acetate (EVA) copolymers: a general review. IEEE Electr Insul Mag 9:30–38
Premphet K, Horanont P (2000) Phase structure of ternary polypropylene/elastomer/filler composites: effect of elastomer polarity. Polymer 41:9283–9290
Hoffendahl C, Duquesne S, Fontaine G, Taschner F, Mezger M, Bourbigot S (2015) Decomposition mechanism of fire retarded ethylene vinyl acetate elastomer (EVA) containing aluminum trihydroxide and melamine. Polym Degrad Stab 113:168–179
Li Y, Zhang Y, Zhang Y (2004) Morphology and mechanical properties of HDPE/SRP/elastomer composites: effect of elastomer polarity. Polym Testing 23:83–90
Yan K, Hong Z, You L, Ou J, Miljković M (2021) Influence of ethylene-vinyl acetate on the performance improvements of low-density polyethylene-modified bitumen. J Clean Prod 278:123865
Liang M, Ren S, Fan W, Xin X, Shi J, Hui L (2017) Rheological property and stability of polymer modified asphalt: effect of various vinyl-acetate structures in EVA copolymers. Constr Build Mater 137:367–380
Yuliestyan A, Cuadri AA, García-Morales M, Partal P (2016) Influence of polymer melting point and Melt Flow Index on the performance of ethylene-vinyl-acetate modified bitumen for reduced-temperature application. Mater Des 96:180–188
Wu L, Zhu J, Liao X, Ni K, Zhang Q, An Z et al (2015) Effect of confinement on glass dynamics and free volume in immiscible polystyrene/high-density polyethylene blends. Polym Int 64:892–899
Xu G, Wang H, Zhu H (2017) Rheological properties and anti-aging performance of asphalt binder modified with wood lignin. Constr Build Mater 151:801–808
Nian T, Li P, Wei X, Wang P, Li H, Guo R (2018) The effect of freeze-thaw cycles on durability properties of SBS-modified bitumen. Constr Build Mater 187:77–88
Saboo N, Kumar R, Kumar P, Gupta A (2018) Ranking the rheological response of SBS-and EVA-modified bitumen using MSCR and LAS tests. J Mater Civ Eng 30:04018165
Perezlepe A, Martinezboza FJ, Attane P, Gallegos C (2006) Destabilization mechanism of polyethylene-modified bitumen. J Appl Polym Sci 100:260–267
Galooyak SS, Dabir B, Nazarbeygi AE, Moeini A (2010) Rheological properties and storage stability of bitumen/SBS/montmorillonite composites. Constr Build Mater 24:300–307
Zhu J, Wei S, Li Y, Sun L, Haldolaarachchige N, Young DP et al (2011) Surfactant-free synthesized magnetic polypropylene nanocomposites: rheological, electrical, magnetic, and thermal properties. Macromolecules 44:4382–4391
Mirsepahi M, Tanzadeh J, Ghanoon SA (2020) Laboratory evaluation of dynamic performance and viscosity improvement in modified bitumen by combining nanomaterials and polymer. Constr Build Mater 233:117183
Zhu J, Birgisson B, Kringos N (2014) Polymer modification of bitumen: advances and challenges. Eur Polymer J 54:18–38
Xia T, Chen W, Xu J (2020) Effect of PEG loading on the rheological stability of bitumen/PE/PEG blends based on network structure evolution. Constr Build Mater 237:117696
Keller A (1955) The spherulitic structure of crystalline polymers. Part I. Investigations with the polarizing microscope. J Polym Sci 17:291–308
Shi W, Chen F, Zhang Y, Han CC (2012) Viscoelastic phase separation and interface assisted crystallization in a highly immiscible iPP/PMMA blend. ACS Macro Lett 1:1086–1089
Tanaka H (2013) Phase separation in soft matter: concept of dynamic asymmetry. In: Lecture notes for les Houches 2012 summer school on soft interfaces.
Roman C, García-Morales M (2016) Optical microscopy visualization on droplet relaxation and breakup in a LDPE modified bitumen. Mater Des 107:353–360
Dehouche N, Kaci M, Mokhtar KA (2012) Influence of thermo-oxidative aging on chemical composition and physical properties of polymer modified bitumens. Constr Build Mater 26:350–356
Perezlepe A, Martinezboza FJ, Gallegos C, Gonzalez O, Munoz ME, Santamaria A (2003) Influence of the processing conditions on the rheological behaviour of polymer-modified bitumen. Fuel 82:1339–1348
Binti Joohari I, Giustozzi F (2020) Effect of different vinyl-acetate contents in hybrid SBS-EVA modified bitumen. Constr Build Mater 262:120574
Nivitha MR, Prasad E, Krishnan JM (2019) Transitions in unmodified and modified bitumen using FTIR spectroscopy. Mater Struct 52:7
Hofko B, Alavi MZ, Grothe H, Jones D, Harvey J (2017) Repeatability and sensitivity of FTIR ATR spectral analysis methods for bituminous binders. Mater Struct 50:187
Mirwald J, Nura D, Hofko B (2022) Recommendations for handling bitumen prior to FTIR spectroscopy. Mater Struct 55:26
Luo W-q, Chen J-c (2011) Preparation and properties of bitumen modified by EVA graft copolymer. Constr Build Mater 25:1830–1835
Rodríguez-Vázquez M, Liauw CM, Allen NS, Edge M, Fontan E (2006) Degradation and stabilisation of poly(ethylene-stat-vinyl acetate): 1 – Spectroscopic and rheological examination of thermal and thermo-oxidative degradation mechanisms. Polym Degrad Stab 91:154–164
Acknowledgements
We are grateful to the financial support from the Project funded by China Postdoctoral Science Foundation (Grant No.2022M712713), General Program of Natural Science Foundation of Chongqing (Grant No. CSTB2022NSCQ-MSX0275), Science and Technology Research Program of Chongqing Municipal Education Commission (Grant No. KJQN202201139).
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declared that they have no conflicts of interest to this work.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Xia, T., Xia, S., Xu, J. et al. Influence of shearing process on the property and microstructure of bitumen modified by polyethylene and ethylene-vinyl acetate copolymer. Mater Struct 56, 42 (2023). https://doi.org/10.1617/s11527-023-02131-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1617/s11527-023-02131-x