Abstract
Recently, metal-assisted chemical etching (MaCE) has been demonstrated as a promising technology in fabrication of uniform high-aspect-ratio (HAR) micro- and nanostructures on silicon substrates. In this work, MaCE experiments on 2 μm-wide line patterns were conducted using Au or Ag as catalysts. The performance of the two catalysts show sharp contrast. In MaCE with Au, a HAR trench was formed with uniform geometry and vertical sidewall. In MaCE with Ag, shallow and tapered etching profiles were observed, which resembled the results from isotropic etching. The sidewall tapering phenomena can be explained by the dissolution and re-deposition of the Ag catalyst in the etchant solution. The existence of Ag that was redeposited on the sidewall was further confirmed by energy dispersive spectrum. Also, etchant composition is found to play a profound role in influencing the etching profile by the Ag catalysts.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
J. H. Lau, L. Ching-Kuan, Z. Chau-Jie, W. Sheng-Tsai, C. Yu-Lin, D. Ming-Ji, T. Ra-Min, C. Heng-Chieh, C. Chun-Hsien, C. Ren-Shin, H. Yu-Wei, L. Yuan-Chang, H. Zhi-Cheng, T. Wen-Li, C. Pai-Cheng, F. Huan-Chun, C. Yu-Mei, L. Li-Ling, L. Wei-Chung and K. Ming-Jer, in Electronic Components and Technology Conference (ECTC), 2014 IEEE 64th, p. 290 (2014).
F. Ayazi and K. Najafi, J. Microelectromech. Syst., 9, 288 (2000).
C. Wu, F. Bendriaa, F. Brunelle and V. Senez, Microelectron. Eng., 88, 1878 (2011).
C. Chang and A. Sakdinawat, Nat. Commun., 5 (2014).
X. Li and P. W. Bohn, Appl. Phys. Lett., 77, 2572 (2000).
Z. Huang, N. Geyer, P. Werner, J. de Boor and U. Gösele, Adv. Mater., 23, 285 (2011).
K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee and J. Zhu, Small, 1, 1062 (2005).
Z. Huang, X. Zhang, M. Reiche, L. Liu, W. Lee, T. Shimizu, S. Senz and U. Gösele, Nano Lett., 8, 3046 (2008).
S. W. Chang, V. P. Chuang, S. T. Boles and C. V. Thompson, Adv. Funct. Mater., 20, 4364 (2010).
L. Li and C. P. Wong, in Electronic Components and Technology Conference (ECTC), 2013 IEEE 63rd, p. 2326 (2013).
O. J. Hildreth, W. Lin and C. P. Wong, ACS Nano, 3, 4033 (2009).
O. J. Hildreth, A. G. Fedorov and C. P. Wong, ACS Nano, 6, 10004 (2012).
K. Rykaczewski, O. J. Hildreth, C. P. Wong, A. G. Fedorov and J. H. J. Scott, Nano Lett., 11, 2369 (2011).
K. Rykaczewski, O. J. Hildreth, C. P. Wong, A. G. Fedorov and J. H. J. Scott, Adv. Mater., 23, 659 (2011).
O. J. Hildreth, D. Brown and C. P. Wong, Adv. Funct. Mater., 21, 3119 (2011).
O. J. Hildreth, K. Rykaczewski, A. G. Fedorov and C. P. Wong, Nanoscale, 5, 961 (2013).
F. Güder, Y. Yang, U. M. Küçükbayrak and M. Zacharias, ACS Nano, 7, 1583 (2013).
P. Lianto, S. Yu, J. Wu, C. V. Thompson and W. K. Choi, Nanoscale, 4, 7532 (2012).
L. Li and C.-P. Wong, in Electronic Components and Technology Conference (ECTC), 2014 IEEE 64th, p. 1848 (2014).
L. Li, Y. Liu, X. Zhao, Z. Lin and C.-P. Wong, ACS Appl. Mater. Interfaces, 6, 575 (2014).
L. Li, X. Zhao and C.-P. Wong, ACS Appl. Mater. Interfaces, 6, 16782 (2014).
K. Tsujino and M. Matsumura, Adv. Mater., 17, 1045 (2005).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Li, L., Holmes, C.M., Hah, J. et al. Uniform Metal-assisted Chemical Etching and the Stability of Catalysts. MRS Online Proceedings Library 1801, 1–8 (2015). https://doi.org/10.1557/opl.2015.574
Published:
Issue Date:
DOI: https://doi.org/10.1557/opl.2015.574