Samples of Ni57-xNdxFe18Ga25 with x=2 and 4 were prepared in ribbon form by rapid quenching via melt spinning route. The samples were analyzed by X-ray diffraction (XRD), magnetic measurements and Mössbauer spectroscopy, both in the as-quenched form and after thermal annealing at 900 oC for 2 min and 400 oC for 2 hours. For x=2 the Nd atoms are completely dissolved in the Ni-Fe-Ga matrix, while for x=4 the additional occurrence of the secondary 2:17 phase could be resolved. These findings were supported by the analysis of hyperfine magnetic field distributions obtained from the non-linear least-squares fitting of the Mössbauer spectra.
Similar content being viewed by others
References
C. Picornell, J. Pons, E. Cesari, J. Dutkiewicz, Intermet., 16, 751 (2008).
J. Liu, N. Scheerbaum, D. Hinz, O. Gutfleisch, Acta Mater., 56, 3177 (2008).
L. Gao, Z.Y. Gao, W. Cai, L.C. Zhao, Mater. Sci. Eng. A, 438–440, 1077 (2006).
L. Gao, J.H. Sui, W. Cai, J. Magn. Magn. Mater., 320, 63 (2008).
K. Tsuchiya, A. Tsutsumi, H. Ohtsuka, M. Umemoto, Mater. Sci. Eng. A, 378, 370 (2004).
X. Zhang, J. Sui, Z. Yu, W. Cai, J. Alloys & Comp., 509, 8032 (2011).
J. Sui, X. Zhang, L. Gao, W. Cai, J. Alloys & Comp., 509, 8692 (2011).
N. V. Rama Rao, R. Gopalan, M. Manivel Raja, V. Chandrasekaran, K. G. Suresh, Appl. Phys. Lett., 93, 202503 (2008).
F. Tolea, A.D. Crisan, M. Sofronie, M. Tolea, M. Valeanu, Mater. Today: Proc. 2S, S875 (2015).
F. Tolea, M. Sofronie, A.D. Crisan, M. Enculescu, V. Kuncser, M. Valeanu, J. Alloys & Comp., 650, 664 (2015).
P. Alvarez, P. Gorria, V. Franco, J.S. Marcos, M.J. Perez1, J.L. Sanchez Llamazares, I.P. Orench, J.A. Blanco, J. Phys.: Condens. Matter, 22, 216005 (2010).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sorescu, M., Tolea, F., Valeanu, M. et al. Structure, Magnetic Properties and Hyperfine Parameters of Nd-Substituted Ni-Fe-Ga Heusler Alloys. MRS Advances 2, 1341–1346 (2017). https://doi.org/10.1557/adv.2017.70
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2017.70