Abstract
Background
The bacterial persistence, responsible for therapeutic failures, can arise from the biofilm formation, which possesses a high tolerance to antibiotics. This threat often occurs when a bone and joint infection is diagnosed after a prosthesis implantation. Understanding the biofilm mechanism is pivotal to enhance prosthesis joint infection (PJI) treatment and prevention. However, little is known on the characteristics of Cutibacterium acnes biofilm formation, whereas this species is frequently involved in prosthesis infections.
Methods
In this study, we compared the biofilm formation of C. acnes PJI-related strains and non-PJI-related strains on plastic support and textured titanium alloy by (i) counting adherent and viable bacteria, (ii) confocal scanning electronic microscopy observations after biofilm matrix labeling and (iii) RT-qPCR experiments.
Results
We highlighted material- and strain-dependent modifications of C. acnes biofilm. Non-PJI-related strains formed aggregates on both types of support but with different matrix compositions. While the proportion of polysaccharides signal was higher on plastic, the proportions of polysaccharides and proteins signals were more similar on titanium. The changes in biofilm composition for PJI-related strains was less noticeable. For all tested strains, biofilm formation-related genes were more expressed in biofilm formed on plastic that one formed on titanium. Moreover, the impact of C. acnes internalization in osteoblasts prior to biofilm development was also investigated. After internalization, one of the non-PJI-related strains biofilm characteristics were affected: (i) a lower quantity of adhered bacteria (80.3-fold decrease), (ii) an increase of polysaccharides signal in biofilm and (iii) an activation of biofilm gene expressions on textured titanium disk.
Conclusion
Taken together, these results evidenced the versatility of C. acnes biofilm, depending on the support used, the bone environment and the strain.
Similar content being viewed by others
Background
The constant evolution of biomaterials dedicated to prosthesis and 3D printing scaffolds responds to the increase in demand for implants of bone and joint prostheses due to population aging. However, arthroplasty procedures still face the additional risk factor of infection [1]. Prosthesis joint infections (PJI) occurs in 1–2% of primary arthroplasties and have become a major clinical issue [2]. C. acnes, an anaerobic Gram-positive and skin commensal bacterium known to be involved in acne, can be responsible for up to 10% of bacterial PJI [3, 4]. Its highest incidence was observed in shoulder arthroplasty (accounting for up to 50% of all C. acnes PJIs), with the hypothesis that C. acnes is more prone to naturally colonize the shoulder skin [5, 6]. The complexity of diagnosis in the case of C. acnes-related-PJI is often linked to the absence of clinical symptoms except a mechanical discomfort for the patient [6, 7]. One hypothesis raised to explain such a discrete manifestation is that C. acnes could escape the host immune system and antibiotic treatment due to internalization into host cells (i.e. osteoblast or mesenchymal stem cells), or thanks to biofilm formation [8,9,10]. The internalization of bacteria could affect some of their behaviors like the biofilm formation after bacterial release from the cells [8, 9]. Biofilm is a community of bacteria under different metabolic states, glued in an extracellular matrix essentially composed of proteins, extracellular DNA (eDNA) and exopolysaccharides [11, 12]. Moreover, bacteria embedded in biofilms have the capacity to resist to very high concentration of antibiotics (10 to 100 higher than minimal inhibition concentration, MIC, of planktonic counterparts in vitro), and to host immune system [7, 13]. C. acnes forms biofilm on different prosthesis-related materials like titanium alloys (TiA), cobalt-chromium-molybdenum (CoCrMo), polyether ether ketone (PEEK) and stainless steel used for hybrid prosthesis manufacturing [14, 15], but also polymethylmethacrylate bone cement [16]. Thus, the biofilm appears as a major clinical issue, causing a persistence of bacteria and inducing the necessity to treat patients with high doses of antibiotics during a period of several months, increasing the risk to select resistant bacteria [7].
Biofilm requires a precise comprehension to determine efficient treatments. However, little is known on biofilm characteristics of PJI-associated C. acnes. It has been shown that the biofilm matrix of C. acnes acne isolates consists of major components including eDNA and proteins. These components play important roles for bacteria attachment and biofilm maturation [17]. Additionally, glycolysis residues are present in C. acnes biofilm matrix, with a different from poly-N-acetylglucosamine found in S. aureus biofilm matrix [18, 19]. Transcriptomic and proteomic studies on different C. acnes strains have highlighted genes and proteins implicated in biofilm formation: amino-acid metabolism genes [18], replication and division genes, cell wall synthesis genes, stress-induced genes and strain-dependent virulence genes like Christie–Atkins–Munch–Petersen (CAMP) factor 4 and lysozyme M1 [20]. Both an in vitro biofilm study and a rabbit biofilm-infection model of C. acnes identified an over-production of some proteins like elongation proteins (tuf and fusA), glycolysis and tricarboxylic acid cycle (TCA) enzymes in the biofilms [19, 21].
While these results were obtained on C. acnes biofilms grown on different supports (plastic, cellulose acetate, glass beats after isolation of rabbit bone), few studies described the C. acnes biofilm on prosthesis-mimicking support to represent PJI context. Notably, environmental conditions and surfaces might strongly influence the biofilm structure and composition [22].
C. acnes infection mainly occurs in the presence of prosthesis material [23]. We hypothesize that the nature of implant material plays an important role in C. acnes biofilm development. The aim of this study was to show the need to develop more specific model for study PJIs. For that, non-PJI- and PJI-related C. acnes biofilm formation on plastic support, used in classic in vitro model, and textured titanium representative of bone prosthesis were characterized and compared using different methods. Moreover, the impact of C. acnes internalization by SaOS-2 cells on biofilm development was also investigated.
Materials and methods
Bacterial strains and culture
Clinical C. acnes strains were isolated and collected at the laboratory of bacteriology of Reims University Hospital Center (CHU Reims). Two clinical isolates were non-PJI-related strains (C2 and C5) and two other clinical strains were isolated from bone and prosthesis infection (PJI2 and PJI8). Clinical strains were registered on clinicaltrials.gov (NCT03950063). Their multi locus sequence typing (MLST) profiles, previously identified [9], are listed in Table 1.
C. acnes was isolated on Columbia agar with 5% sheep blood (BioRad, Hercules, California, USA), under anaerobic conditions using the GenBox system (Biomerieux, Marcy l’Etoile, France), at 37 °C, for 5 days. For all assays, one colony from each C. acnes strains was added on 1.5 mL- tube previously filled with Brain Heart Infusion (BHI) broth (BioRad, Hercules, California, USA). After 5 days incubation at 37 °C, absorbance at 600 nm was adjusted to 1 and bacteria were seeded to a final dilution of 1/100 (or 1/10 for RNA extraction) in BHI or diluted BHI (dBHI: 90% sterile water and 10% BHI), in 24 well-plates with different supports and incubated under anaerobic conditions, at 37 °C, for 5 days, for each experiment. Two different media (BHI and dBHI) were tested to compare the classical lab condition (i.e. BHI) to the nutrient-limited condition (i.e. dBHI).
Supports used
In this study, Thermanox™ plastic coverslip (1.3 cm², Thermo Fisher Scientific, Waltham, Massachusetts, USA), raw titanium alloy disks (diameter 12 mm x height 5 mm, 1.1 cm²) (ACNIS, Chassieu, France) and titanium alloy disks shot-peened by CRITT-MI (1.1 cm², Charleville-Mézières, France) were used. Titanium alloy disks (TiAl6V4) used in this study are in accordance with the medical standard ISO 5832-3 (or ASTM F136). The roughness was obtained by microbead projection on the surface of the titanium alloy disk. The difference between both raw and microblasting surface is in the micrometer range. The shot-peened titanium (also name textured titanium) disk obtained was the support chosen as prosthesis mimicking material. Raw titanium disk (with a smooth surface) was used to assess the effect of the texturation as a surface modification could increase bacterial adhesion and biofilm formation and composition. The plastic coverslip was chosen as the classic in vitro model (used as lab condition reference). An initial count was carried out to confirm that the same quantity of bacteria was deposited for each C. acnes strains, allowing their behavior to be compared (see Additional file 1 A).
C. acnes adhesion
Supports were deposited in each well of a 24-wells plate. Then, one milliliter of the bacterial inoculum in BHI or dBHI prepared above (8 × 106 to 1.1 × 107 bacteria/mL) was added to each well. After 5 days anaerobic incubation, supports were immersed in BHI or dBHI to be washed and immediately transferred to a 15 mL tube containing 2 mL of BHI or dBHI to be incubated 5 min in ultrasonic bath (40 kHz) to detach biofilm-embedded bacteria. To quantify non-adherent bacteria, 100 µL were collected before ultrasonication and serial dilutions were done. To quantify live adherent and planktonic bacteria, 100 µL were collected after ultrasonication and serial dilutions were done. Then dilutions were seeded on blood agar plates using automatic seeder EasySpiral (Interscience, Saint-Nom-la-Bretèche, France). After 5 days anaerobic incubation, the number of recovered colony-forming units (CFU) was determined using automatic counter SCAN 1200 (Interscience, Saint-Nom-la-Bretèche, France) and the quantity of live adherent bacteria was determined as follows: CFU/mL (after) – CFUL/mL (before) and area normalized (per cm²). At least three independent experiments were performed with technical duplicate for each C. acnes strain.
Composition of C. acnes biofilm extracellular components
After 5 days of incubation in dBHI, mimicking a nutrient-poor environment, under anaerobic conditions, supports were washed twice in Phosphate Buffered Saline (PBS) and stained with the different labelled solution, listed in Table 2 (Invitrogen, Waltham, Massachusetts, USA, for all fluorescent markers).
Each solution was diluted in sterile NaCl 0.9%. After 30 min of incubation in the dark, at room temperature, each material was washed twice in PBS before being flipped upside-down and placed in a Krystal 24-well plate with glass bottom (Porvair, United Kingdoms). Biofilm was observed and imaged using confocal scanning laser microscopy (CSLM) LSM 710 NLO (ZEISS, Oberkochen, Germany). 3D-reconstruction were created, and fluorescence volumes were quantified, using IMARIS software. Three independent experiments were performed and at least two areas were captured for each condition for titanium disks and plastic coverslip. Controls without bacteria were realized for each labels solution to confirm that the different fluorochrome did not attach on plastic coverslip or titanium disks.
mRNA expression of C. acnes genes
mRNA analysis was undertaken to evaluate the expression of genes implicated in stress response and biofilm formation, previously identified by Jahns AC. et al, 2016 and Achermann Y. et al., 2015 [20, 21]. Each C. acnes strains was seeded in stationary phase culture at a dilution of 1/10 in dBHI in the presence of different supports. The incubation lasted 48 h for planktonic and 5 days for biofilm under anaerobic atmosphere, at 37 °C, adapting from Jahns AC. et al., 2016 [20]. Planktonic bacteria were pelleted by centrifugation 8 min, at 5000 g, 4 °C. After 5 days of incubation, adherent bacteria embedded in biofilm were detached by ultrasonic bath (40 kHz) for 5 min, after two PBS washes and pelleted by centrifugation 8 min, at 5000 g, 4 °C. Pellets were conserved at -80 °C before RNA extraction. Total RNAs were extracted using MasterPure™ RNA Purification Kit (Lucigen, Middleton, Wisconsin, USA) according to the manufacturer’s protocol. Total RNAs (200ng) were then reverse transcribed into complementary DNA (cDNA) using High-Capacity cDNA Reverse Transcription Kit (Applied Biosystems, Waltham, Massachusetts, USA) following the manufacturer’s instructions. Transcription products (10ng) were amplified by qPCR using SYBR Takyon Mix (Eurogentec, Seraing, Belgium) on StepOne Plus™ system (Applied Biosystems, Waltham, Massachusetts, USA) using primers detailed in Table 3. Data analyses were performed with the StepOne™ software v2.3 (Applied Biosystems, Waltham, Massachusetts, USA). Target transcript levels (N-target) were normalized to the housekeeping gene (16SRNA) transcript levels and mRNA level with the equation N-target = 2^∆Ct, where ∆Ct is the Ct value of the target gene after subtraction of Ct for the 16SRNA gene. At least three independent experiments were performed for each C. acnes strain.
C. acnes internalization by SaOS-2
Osteoblast cell line SaOS-2 (ATCC HTB-85™) used for this study, were cultivated in medium composed of Dulbecco’s Modified Eagle Medium (DMEM, Thermo Fisher Scientific, Waltham, Massachusetts, USA) supplemented with 10% fetal bovine serum (FBS, PAN-Biotech GmbH, Aidenbach, Germany) and 1% Penicillin Streptomycin (PS, Thermo Fisher Scientific, Waltham, Massachusetts, USA). The bacterial internalization experiment was adapted from Josse J. et al., 2016 [24]. Briefly, SaOS-2 were seeded in 24-well plates at 104 cells/cm² and incubated at 37 °C, in a 5% CO2 humidified atmosphere, for 72 h, in culture medium. SaOS-2 cells were washed twice with PBS and incubated overnight with PS-free culture medium. The following day, cells were again washed twice with PBS and 1 mL of PS-free culture medium was added in each well. One well was used for evaluation of the number of cells per well. Cells were detached using trypsin-EDTA (Thermo Fisher Scientific, Waltham, Massachusetts, USA) and 10 µL were deposited on Kova slide for counting. Bacteria were centrifugated for 5 min, at 5000 g and the pellets were rinsed twice with PBS. Bacteria were then added to cell cultures to obtain a multiplicity of infection (MOI) of 100:1. After 3 h of interaction, cells were washed twice with PBS and incubated with cell medium containing 100 µg/mL of gentamicin (Fisher Scientific, Hampton, New Hampshire, USA), during 1 h, at 37 °C, in a 5% CO2 humidified atmosphere, to eliminate extracellular bacteria. Cells were again washed twice with PBS, and 1 mL of 0.1% Triton X-100 solution was added in each well, during 5 min, to harvest intracellular bacteria. Lysate were seeded on blood agar plates using automatic seeder EasySpiral (Interscience, Saint-Nom-la-Bretèche, France) and incubated at 37 °C under anaerobic condition for 5 days. The number of recovered CFU was determined using automatic counter SCAN 1200 (Interscience, Saint-Nom-la-Bretèche, France) and the percentage of internalized-bacteria was defined as follows: % of bacteria = ((CFU/mL)/(number of cells x MOI)) x 100. Four independent experiments were performed.
Graphical representation and statistical analysis
Results are represented as whisker plots: the box represents the interquatile range and the whiskers are the minimum and the maximum values, the bar inside the box is for the median value, and each point represents an independent replicate. The average value is indicated by a red bar (or a black bar for Live/Dead graphes). All up- and down-fold variations between conditions were expressed from average values. The statistical significance of the results was assessed using the exact 2-tailed non-parametric Wilcoxon-Mann-Whitney test of GraphPad Prism (v8.0.1) software. Non-parametric statistics were used owing to the lack of a normal distribution of the assessed variables. Differences were considered significant at p < 0.05.
Results
Titanium supports favor C. acnes adhesion
In BHI medium, C2 strain adhered 8.4-fold more on textured titanium disk as compared to plastic coverslip by up (Fig. 1A). No impact of the support’s nature was observed on planktonic growth (see Additional file 1A). As expected, in diluted BHI medium (dBHI), there was a weaker planktonic growth (see Additional file 1B) and a lower number of adhered bacteria. Nevertheless, non-PJI-related strains, C2 and C5, adhered significantly more on textured titanium disks than on plastic coverslip (11.2 and 8.2-fold increase respectively) (Fig. 1B).
As the surface texturing of titanium is an additional difference between plastic and titanium, bacterial adhesion was also evaluated on raw titanium (no texturing) in both condition (BHI and dBHI) (see Additional file 2). No significant differences in adhesion were observed between raw and textured surfaces (Fig. 1A and B and see Additional file 2).
C. acnes adherence increases on textured titanium disk with nutritive or diluted broth (A) Quantity of adherent bacteria cultivated for 5 days with BHI or (B) with dBHI. White bars represent the number of bacteria adhered on plastic coverslips, grey bars represent the number of bacteria adhered on textured titanium disk and green points represent each independent biological replicate. The average value is indicated by a red bar. Wilcoxon-Mann-Whitney test: * p < 0.05. Experiment was performed at least 3 independent times. Name of strains: C is for non-PJI-related strain and PJI is for PJI-related strain
Titanium disks triggers aggregates biofilm formation with polysaccharides and proteins enriched matrix
To go further, C. acnes biofilm in dBHI was observed thanks to CLSM. The quantity of bacteria was more important on textured titanium disk than on plastic coverslip whatever the origin of strains. The difference was more obvious for PJI8 (Fig. 2A). Moreover, we noticed a similar difference between raw titanium and plastic coverslip for PJI-related strains (see Additional file 3 A).
Thanks to 3D-reconstruction, large bacteria aggregates for C2 and C5, on all materials and small aggregates for PJI8 on raw titanium were observed (Fig. 2B and see Additional file 3B). For PJI-related strains, aggregates were mainly present on textured titanium disk (Fig. 2B).
Textured titanium changes proportion of live and damaged bacteria and biofilm morphology. (A) Fluorescence volumes of live and adherent bacteria, labelled by SYTO9™ (green) and damaged and dead bacteria, labelled by PI (red) according to the support. The average value is indicated by a black bar. (B) 3D-representative reconstruction of C. acnes biofilm. Wilcoxon-Mann-Whitney test: * p < 0.05. Experiment was performed 3 independent times
On plastic coverslip, the extracellular components were mainly simple polysaccharides, in particular for non-PJI-related strains. PJI8, which produced lower relative amount of complex polysaccharides than other strains. The other components were in similar lower proportions (Fig. 3A and C). On textured titanium disk, the relative amount of fluorochrome signals were similar between proteins and simple polysaccharides, and lower for eDNA and complex polysaccharides (Fig. 3B and C). On raw titanium disk, these same relative amounts were also observed in biofilm formed, except for PJI2 biofilm which showed a more important part of eDNA compared to textured titanium disk (see Additional files 3 C and 3D).
C. acnes biofilm composition on textured titanium disk is mostly composed by polysaccharides and proteins. (A) C. acnes biofilm composition on plastic coverslip and (B) on textured titanium disk after 5 days with dBHI. The fluorescent volumes of the matrix components: SYPRO Ruby® for proteins (dark red), Wheat Germ Agglutinin (WGA) (blue) and concanavalin A (conA) (purple) for complex and simple polysaccharides respectively, and TOTO-3™ for extracellular DNA (orange) were normalized to fluorescent volumes of SYTO9™ using IMARIS software after acquisitions by CLSM. The average value is indicated by a red bar. Wilcoxon-Mann-Whitney test: p < 0.05, * between fluorescent labels, α versus each fluorochromes and ε versus WGA/TOTO™. (C) 3D-views of matrix biofilm composition of C. acnes. Experiment was performed 3 independent times
Stress and biofilm-formation-related genes expression by C. acnes is reduced on titanium support
According to previous publications [20, 21], a list of genes involved in C. acnes biofilm initiation and formation was defined. We compared the expression of these genes on plastic coverslip and on titanium disks.
First, genes involved in stress response and biofilm ignition were studied. On plastic coverslip, an activation of genes was observed for non-related-PJI strains and PJI2 with an increase of PPA0387 expression in biofilm compared to planktonic for C2 and PJI2 and an increase of SOS response genes expression for C5 (Fig. 4A). Conversely, no variation of recA, lexA and PPA0387 was quantified for PJI8 in bacteria within biofilm compared to planktonic counterparts (Fig. 4A). On textured titanium disk, the profile of gene expression was similar except for C2 strain with notably a slight or an absence of activation (Fig. 4B). The profile of gene expression was the same on textured and raw titanium disks for PJI-related strains, but different for non-related PJI strains with a lower expression of the genes without being significant (see Additional file 4A).
Second, the genes involved in biofilm formation were also evaluated [20, 21]. On plastic coverslip, CAMP1, fusA, and fumC are up-regulated in the biofilm of the four C. acnes strains (with an increase of fumC expression for non-related-PJI strains in biofilm compared to planktonic and of fusA for C5 and PJI2) (Fig. 4C). However, a biofilm-related overexpression of dnaK, eno, PPA2127 and groEL was observed in C2-, C5- and PJI2- biofilm, on plastic coverslip (Fig. 4C). In comparison, on textured titanium disk, gene response was more variable. For the non-PJI-related strain C2, no change of gene expression involved in biofilm was identified except the observation of a down-regulation of gene PPA2127 coding for an adhesin (Fig. 4D). PJI-related strains and C5 tended to exhibit increased expression of most of biofilm related genes notably for CAMP1, dnak, groEL and fumC for PJI2 with an expression significantly more important in biofilm compared to planktonic (Fig. 4D). A similar profile of gene expression was observed on raw titanium disk except for the non-PJI-related strain C5 with an expression lower on raw titanium than on textured titanium (see Additional file 4B).
Globally, gene expression level for C2 are statistically lower on textured titanium than on plastic for lexA, dnak, groEL, fusA, eno and fumC.
mRNA expression of genes is modified for one non-PJI-related strain on textured titanium disk. (A) Difference of expression of stress pathway-related genes when biofilm is formed on plastic coverslip and (B) on textured titanium disk. (C) Levels of expression of gene involved in biofilm formation on plastic coverslip and (D) on textured titanium disk. The average value is indicated by a red bar. Experiment was performed at least 3 independent times. Wilcoxon-Mann-Whitney * p < 0.05 expression in biofilm versus expression in planktonic counterpart, $ p < 0.05 textured titanium versus plastic support
To summarize, C. acnes behavior changed according to the support with: i/ a greater adhesion, and ii/ a biofilm composed by both proteins and polysaccharides and iii/ a strain dependent gene response on titanium disk compared to plastic coverslip. As no notable difference was observed between raw and textured titanium, only textured titanium was used on the further experiments.
C. acnes PJI-related strains adhesion is better on titanium after osteoblast internalization
The internalization has especially impacted C2 and PJI8 bacterial adhesion (Fig. 5A). Adverse response was observed for C2 strain between plastic and textured titanium with a significant decrease (80.2-fold down) on titanium and a not significant increase on plastic compared to non-internalized strain (Fig. 5B). A significant increase was observed for PJI8 on plastic coverslip (4.5-fold up) and on textured titanium (9.2-fold up for PJI8) (Fig. 5B).
Internalization by SaOS-2 increases PJI-related strains adhesion on textured titanium disk. (A) Quantity of adherent bacteria, after internalization, cultivated with dBHI. (B) Ratio after/before internalization. White bars represent the number of bacteria adhered on plastic coverslip, grey bars represent the number of bacteria adhered on textured titanium disk and green points represent each independent biological replicate. The average value is indicated by a red bar. Wilcoxon-Mann-Whitney test: p < 0.05, * between supports and $ versus non-internalized C. acnes. Experiment was performed after 4 independent internalization
Internalization of C. acnes into osteoblasts affects biofilm composition according to the strain and the support
The composition of biofilm formed by bacteria that had been internalized by SaOS-2 was analyzed.
Compared to non-internalized C. acnes strains, a significant decrease of damaged and dead bacteria was observed for internalized-C2 and a non-significant decrease for the other strains on plastic coverslip (Fig. 6A and B). On textured titanium disk, damaged and dead bacteria fluorescent labeling was more important for internalized-C5 and -PJI2 (3.3 to 15.8-fold up) with a significant difference for PJI2, compared to non-internalized strains (Fig. 6B).
Thanks to 3D-reconstruction, a loss of bacteria aggregates was only observed for internalized-C2 compared to non-internalized-C2 (Fig. 6C). Biofilm morphology on textured titanium disks was not modified by internalization for any strains (Fig. 6C).
Internalization slightly modified the proportion of damaged and dead bacteria and biofilm morphology. (A) Fluorescence volumes of live and adherent bacteria, labelled by SYTO9™ (green) and damaged and dead bacteria, labelled by PI (red) according to the support. (B) Ratio after/before internalization of fluorescence volumes. The average value is indicated by a black bar. (C) 3D-representative reconstruction of C. acnes biofilm. Wilcoxon-Mann-Whitney test: p < 0.05, * plastic versus textured titanium and $ versus non-internalized C. acnes. Experiment was performed 3 independent times
On coverslip, non-PJI-related strains formed biofilms with lower levels of proteins (14.9 to 16.4-fold down) and polysaccharides (10.7 to 52.2-fold down) after internalization (Fig. 7A). For PJI-related strains, the biofilm was mostly composed of eDNA (4.2 to 15.5-fold up) with a significant increase for PJI2 on plastic coverslip (Fig. 7A). On textured titanium disk, a decrease of fluorescent signal of proteins was observed for all internalized-strains (1.8 to 3.5-fold down). An increase of labeled-polysaccharides was quantified for C2 (2.9-fold up). Conversely, a significant decrease of polysaccharides was noted for PJI8 after internalization compared to non-internalized strains (3.1-fold down) (Fig. 7B).
Briefly, after internalization, on plastic, biofilm is composed by the same relative amount of all components except for complex polysaccharides for non-PJI-related strains and mostly by eDNA for PJI-related strains (see Additional files 5 A and 5 C). On textured titanium disk, polysaccharides were the main components observed in the biofilm of all internalized-C. acnes strains (see Additional files 5B and 5 C).
Internalization induces modifications on matrix biofilm composition. (A) Ratio after/before internalization on plastic coverslip and (B) textured titanium disk. Fluorescence volumes matrix component were normalized by SYTO9™. The average value is indicated by a red bar. Wilcoxon-Mann-Whitney test realized on all data versus non-internalized C. acnes $ p < 0.05. Experiment was performed 3 independent times
Internalization of C. acnes into osteoblasts blunts mRNA expression for stress and biofilm formation-related genes except for C2 strain on titanium support
The levels of genes expression in biofilm versus planktonic bacteria, after internalization, were compared to non-internalized bacteria. On plastic coverslip, a decrease of all biofilm induction- and formation-genes was observed for C2 (significantly different for the majority of genes) and PJI2 (Fig. 8A). On textured titanium disk, a decrease of stress-induced genes and biofilm-induced genes was observed for PJI-related strains (notably for the majority of genes for PJI2) and the non-PJI-related strain, C5 (Fig. 8B). For internalized-C2, an important increase of all genes was noted on textured titanium disk (notably for chaperonins dnak and groEL and for fumC) (Fig. 8B).
mRNA expression of genes is activated in C2 biofilm on textured titanium disk after internalization. (A) Levels of expression of stress-induced genes and genes involved in biofilm formation on plastic coverslip and (B) textured titanium disk. The average value is indicated by a red bar. Wilcoxon-Mann-Whitney test, $ p < 0.05 compared to non-internalized strain. Experiment was performed at least 3 independent times
Discussion
While PJI remain a major clinical problem, the infectious mechanisms of C. acnes are still unclear [25] and no host inflammation markers is usually detected [26, 27]. The biofilm formation could be the key to this clinical situation, protecting bacteria from immune system attack and antimicrobial treatment. However, the biofilm structure and composition are strongly environment- and support-dependent [16, 22]. The study of C. acnes biofilm on plastic support could thus not be adapted or even inaccurate. The aim of this study was to characterize C. acnes biofilms in PJI context, by comparing non-PJI-related and PJI-related strains behaviors on plastic (classic in vitro model) and titanium surfaces (prosthesis-mimicking material), and by analyzing the impact of bacterial internalization in host cells on further biofilm formation.
Bacterial adhesion is the first step of biomaterial-related infections, and it paves the way to implant colonization [28]. The adhesion of C. acnes on different metal alloys was previously studied and demonstrated metal-dependent biofilm structures [15]. In PJI context, C. acnes colonize the bone and prosthesis interface where the nutrient availability is poor (cortical bone, characterized by low-vascularized tissue), therefore biofilm being strongly dependent to its environment [22], a more faithful model to the PJI context using titanium surfaces and poor media was developed.
In our model, differences in bacterial adhesion were observed between the plastic coverslip and titanium disk: non-PJI-related strains adhered more to textured (or raw) titanium than to plastic coverslip. Although the difference was not significant for PJI-related strains after enumeration of adherent bacteria on agar plates, a significant difference in SYTO-9 and IP-labelled adherent bacteria quantity was observed on raw and textured titanium compared to plastic for PJI8. Variations between those two technics for live and adherent bacteria can be explained by the presence of bacteria under different metabolic states in biofilm, like persister, viable bacteria non-cultivable (VBNC), or dormant bacteria are labeled by fluorochromes but are not detectable by classical culture assay. The live and dead staining observation revealed another difference between non-PJI- and PJI-related strains as the second ones did not form aggregates on plastic. Overall, this reinforces the hypothesis that titanium and plastic surfaces influence C. acnes biofilm formation differently. Titanium surface texturing does not appear to affect bacterial adhesion as no difference was observed between raw and textured titanium. The IP labeling, notably more important for PJI8 on titanium compared to plastic, permitted to observe an importance of bacterial lysis. This phenomenon leads to the release of eDNA essential in biofilm matrix formation.
Indeed, another important characteristic of biofilm is the composition of the matrix, made of extracellular components. In our study, we observed that biofilm matrix is mostly composed of polysaccharides (2.4 to 30-fold up compared to proteins) in the biofilm of all C. acnes strains on plastic coverslip, with a slightly weaker signal of eDNA compared to proteins. These data confirmed previous studies analyzing biofilms formed on plastic [20, 29]. Gannessen AV. et al., 2019, showed a composition of 62.6% of sugars, 9.6% of proteins, and 4% of eDNA in RT5 (acneic strain) biofilm on Petri dishes by dosing compounds [19]. The presence of an almost equivalent signal of proteins and eDNA can be explained by the importance of these compounds on C. acnes adhesion. Indeed, Kuehnast T. et al., 2018, showed that eDNA and proteins play a role in C. acnes adhesion and biofilm maturation on plastic by using proteinase-K and DNAse-I enzymes treatment for several C. acnes strains with different phylotypes [17]. Here, on titanium disks, the proportions of polysaccharides and proteins in C. acnes biofilm were more balanced (0.3 to 1.7-fold up on raw titanium disk and 1.7 to 3.8-fold up for polysaccharides compared to proteins). The presence of a strong protein signal compared to eDNA could also lead us to hypothesize that proteins are more important than eDNA for the biofilm matrix production of C. acnes on titanium. Proteomic studies will have to be carried out to identify which proteins are mainly involved in matrix composition.
C. acnes biofilm being studied only recently, few proteomic and transcriptomic experiments have been carried out [20, 21]. Based on literature, selected genes identified as important for biofilm formation were monitored for their expression in biofilm. We confirmed that these genes are globally induced in biofilm formed on plastic, for all the four strains. Interestingly, the involvement of these genes is different in the biofilm formed on titanium, especially for non-PJI-related strains, showing that other genes, not yet identified, play a role for adhesion on titanium.
SOS response genes (recA and lexA) were strongly expressed in biofilm formed on plastic compared to planktonic bacteria, contrary to their expression in biofilm formed on titanium, which was strain-dependent. The genes involved in proteins biosynthesis (fusA and chaperone dnak), glycolysis (eno), TCA cycle (fumC) and CAMP1 (recognized by TLR-2, an eucaryotic cell membrane receptor) were overexpressed for all strains in the biofilm formed on plastic. These results correlated with the strong presence of proteins in the biofilm matrix composition. On titanium disks, the overexpression of the two genes coding for chaperones proteins (dnak and groEL) and fusA for PJI-related strains showed the importance of proteins for biofilm on titanium. Other genes involved in the synthesis of matrix components were also overexpressed (sucD, eno, fumC) for PJI-related strains. However, the absence of overexpression of these genes in the non-PJI-related strain C2 with a strong down-regulation even being observed underlined a strain-dependent response which could be related clinical context. Thus, we speculate the presence of different proteins with a role in the matrix composition or adhesion between PJI-related and non-PJI-related strains or according to the phylotype, and differently produced according to the nature of the support.
In PJI context, bacteria can interact with host cells. Aubin A. et al., 2017, has shown the capacity of MG63 osteoblast cells to internalize C. acnes [8]. Mongaret C. et al., 2020, confirmed this result with SaOS-2 cell line, showing that internalization increased biofilm formation of some C. acnes strains after intracellular extraction [9]. Dubus M. et al., 2020, had also observed that C. acnes internalization in bone marrow derived mesenchymal stem cells affects their behavior, leading to an increase of biofilm formation on orthopedic material (Titanium alloy and PEEK) when bacteria are released out of the cells [10].
We observed the same phenomenon in our model for PJI2 on titanium and PJI8 on both supports. On contrary, we observed that C. acnes internalization in SaOS-2 influenced adhesion of C2 strain, with a decrease of adhered cells on titanium alloys and a non-significant increase of polysaccharides quantity within the matrix. This increase can be also correlated to an overexpression of eno, involved in glycolysis. Some of the genes involved in protein biosynthesis were strongly expressed in biofilm formed in titanium by internalized C2 compared to the non-internalized one. It could reflect the production of adhesins that could play a different role in bacterial adhesion on titanium. The behavior of internalized C2 strain was also modified on plastic but in a different way: no more aggregates were observed and the quantity of dead cells within biofilm decreased as well as the overall quantity of extracellular components. These modifications could be linked to a strong decrease of the expression of all tested genes involved in biofilm formation on plastic compared to non-internalized C2 bacteria. We conclude that internalization could strongly affected the behavior of specific C. acnes strains like observed for C2 strain. However, the difference between both supports reinforce the hypothesis that C. acnes metabolic pathways involved toward titanium or plastic support are different.
For the three other strains, the internalization affected the quantity of extracellular components by increasing or decreasing the different components levels in a strain-dependent way and especially for biofilms formed on plastic. Thus, on plastic, a decrease of polysaccharides in biofilm was observed for all internalized strains (except complex polysaccharides for PJI8) following internalization, with a rise of eDNA for PJI-related strains. These modifications were not found in biofilm formed on titanium after internalization. The internalization influenced the matrix biofilm by increasing the relative amount of polysaccharides on textured titanium disk. Expressions of genes known to be involved in biofilm formation was modified similarly for the two PJI-related strains and the non-PJI-related strain C5 but differently for C2 strain. These results suggest that different strains responses to bacteria internalization by osteoblasts affect the gene expressions and the future matrix composition involved in biofilm formation. Different hypotheses could be raised as a modification of cell wall [30]. The modification of bacterial cell wall could affect adhesins composition and interactions with support. We speculate that post-translational modifications could also be induced within the host cell modifying or activating enzymes involved in different pathways such as proliferation or synthesis of matrix components. Moreover, as the C2 strain does not respond the same as the C5 strain, the hypothesis of the existence of a link between phylotype and internalization can be asked.
We confirmed that the impact of internalization is strain-dependent. The non-PJI-related strain, C2, does not react in the same way to internalization that the other strains. Dubus M. et al., 2022, have shown modifications of elasticity of bacteria cell wall and of IR spectrum of non-PJI-related C. acnes, which can suggest a probable decrease of polysaccharides after internalization by MSCs, as we observed in this study [30]. Therefore, we speculate that a structural modification of C. acnes surface or an adaptive response during internalization could lead to the establishment of a modification in biofilm organization of non-PJI-related C. acnes.
The differences observed between titanium and plastic showed that the bacteria do not trigger an universal response but specific ones, regarding the support. This study therefore shows the importance of the model to choose to study the biofilm of C. acnes, such as the use of prosthesis-mimicking titanium in the investigations of PJIs. The interaction of bacteria with bone cells (osteoblasts) induces modification of C. acnes behavior demonstrating the importance of bone environment parameters to be included in in vitro model of PJI. Previous studies have also shown that C. acnes is able to adhere to fibronectin, one of the main components of the bone matrix [31]. However, it is also necessary to consider the presence of the bone cement used during the bone-prosthesis surgeries, which can prone C. acnes adhesion [7] as well as the type and quality of bone another important element to develop an accurate model. In a recent study, Lamret F. et al., 2023, has shown that S. aureus is able to adhere and form a biofilm on decellularized bone explant [32]. Thus, the influence of other supports as bone explant and bone cement have to be explored in future.
Conclusion
In conclusion, our results showed that C. acnes adapts its biofilm formation and composition according to the microenvironment. In a strain dependent way, C. acnes were strongly influenced by the nature of the physical materials mimicking bone prosthesis but also by internalization in osteoblasts, both representing the bone-prosthesis environment. These differential and complex responses emphasize the need to develop a relevant in vitro model toward bone-prosthesis site. The description of the biofilm characteristics formed on titanium, or after contact with osteoblasts, will help to choose the right treatment to fight against this form of bacterial persistence.
Data availability
The data generated and analyzed during the study are available from the corresponding author upon reasonable request.
Abbreviations
- BHI:
-
Brain Heart Infusion
- C. acnes :
-
Cutibacterium acnes
- CFU:
-
Colony Forming Unit
- ConA:
-
Concanavalin A
- CSLM:
-
Confocal Scanning Laser Microscopy
- DMEM:
-
Dulbecco’s Modified Eagle Medium
- FBS:
-
Fetal Bovine Serum
- MOI:
-
Multiplicity of infection
- MSC:
-
Mesenchymal stem cell
- PBS:
-
Phosphate Buffered Saline
- PCR:
-
Polymerase Chain Reaction
- PEEK:
-
Polyether ether ketone
- PI:
-
Propidium Iodide
- PJI:
-
Prosthesis Joint Infection
- PS:
-
Penicillin Streptomycin
- TCA:
-
Tricarboxylic Acid Cycle
- VBNC:
-
Viable Bacteria Non-Cultivable
- WGA:
-
Wheat Germ Agglutinin
References
Im GI. Biomaterials in orthopaedics: the past and future with immune modulation. Biomater Res déc. 2020;24(1):7.
Shoji MM, Chen AF. Biofilms in Periprosthetic Joint Infections: a review of Diagnostic modalities,current treatments, and future directions. J Knee Surg févr. 2020;33(02):119–31.
Aubin GG, Lavigne JP, Foucher Y, Dellière S, Lepelletier D, Gouin F, et al. Tropism and virulence of Cutibacterium (formerly Propionibacterium) acnes involved in implant-associated infection. Anaerobe oct. 2017;47:73–8.
Triffault-Fillit C, Ferry T, Laurent F, Pradat P, Dupieux C, Conrad A, Becker A, Lustig S, Fessy MH, Chidiac C, Valour F. Microbiologic epidemiology depending on time to occurrence of prosthetic joint infection: a prospective cohort study. Clin Microbiol Infect. 2019;25(3):353–8.
Boisrenoult P. Cutibacterium acnes prosthetic joint infection: diagnosis and treatment. Orthop Traumatology: Surg Res févr. 2018;104(1):S19–24.
Patel A, Calfee RP, Plante M, Fischer SA, Green A. Propionibacterium acnes colonization of the human shoulder. J Shoulder Elb Surg Nov. 2009;18(6):897–902.
Tande AJ, Patel R. Prosthetic joint infection. Clin Microbiol Rev Avr. 2014;27(2):302–45.
Aubin GG, Baud’huin M, Lavigne JP, Brion R, Gouin F, Lepelletier D, et al. Interaction of Cutibacterium (formerly Propionibacterium) acnes with bone cells: a step toward understanding bone and joint infection development. Sci Rep 20 févr. 2017;7(1):42918.
Mongaret C, Varin-Simon J, Lamret F, El-Mahdy TS, Brasme L, Vernet-Garnier V, et al. Cutibacterium acnes Biofilm Study during bone cells Interaction. Microorganisms. sept 2020;12(9):1409.
Dubus M, Varin J, Papa S, Rammal H, Chevrier J, Maisonneuve E, et al. Interaction of Cutibacterium acnes with human bone marrow derived mesenchymal stem cells: a step toward understanding bone implant- associated infection development. Acta Biomater 1 mars. 2020;104:124–34.
Hall-Stoodley L, Costerton JW, Stoodley P. Bacterial biofilms: from the natural environment to infectious diseases. Nat Rev Microbiol févr. 2004;2(2):95–108.
Stewart PS, Franklin MJ. Physiological heterogeneity in biofilms. Nat Rev Microbiol mars. 2008;6(3):199–210.
Stewart PS. Antimicrobial Tolerance in Biofilms., Ghannoum M, Parsek M, Whiteley M, Mukherjee P. éditeurs. Microbiol Spectr. 18 juin 2015;3(3):3.3.07.
Bidossi A, Bottagisio M, De Grandi R, De Vecchi E. Ability of adhesion and biofilm formation of pathogens of periprosthetic joint infections on titanium-niobium nitride (TiNbN) ceramic coatings. J Orthop Surg Res déc. 2020;15(1):90.
Garcia D, Mayfield CK, Leong J, Deckey DG, Zega A, Glasser J, et al. Early adherence and biofilm formation of Cutibacterium acnes (formerly Propionibacterium acnes) on spinal implant materials. Spine J juin. 2020;20(6):981–7.
Ramage G, Tunney MM, Patrick S, Gorman SP, Nixon JR. Formation of Propionibacterium acnes biofilms on orthopaedic biomaterials and their susceptibility to antimicrobials. Biomaterials août. 2003;24(19):3221–7.
Kuehnast T, Cakar F, Weinhäupl T, Pilz A, Selak S, Schmidt MA, et al. Comparative analyses of biofilm formation among different Cutibacterium acnes isolates. Int J Med Microbiol déc. 2018;308(8):1027–35.
Brzuszkiewicz E, Weiner J, Wollherr A, Thürmer A, Hüpeden J, Lomholt HB et al. Comparative Genomics and Transcriptomics of Propionibacterium acnes. Horsburgh MJ, éditeur. PLoS ONE. 27 juin. 2011;6(6):e21581.
Gannesen AV, Zdorovenko EL, Botchkova EA, Hardouin J, Massier S, Kopitsyn DS, et al. Composition of the Biofilm Matrix of Cutibacterium acnes Acneic strain RT5. Front Microbiol 21 juin. 2019;10:1284.
Jahns AC, Eilers H, Alexeyev OA. Transcriptomic analysis of Propionibacterium acnes biofilms in vitro. Anaerobe déc. 2016;42:111–8.
Achermann Y, Tran B, Kang M, Harro JM, Shirtliff ME. Immunoproteomic identification of in vivo -produced Propionibacterium acnes proteins in a rabbit biofilm infection model. Staats HF, éditeur. Clin Vaccine Immunol Mai. 2015;22(5):467–76.
Bjarnsholt T, Whiteley M, Rumbaugh KP, Stewart PS, Jensen PØ, Frimodt-Møller N. The importance of understanding the infectious microenvironment. Lancet Infect Dis mars. 2022;22(3):e88–92.
Shiono Y, Ishii K, Nagai S, Kakinuma H, Sasaki A, Funao H, et al. Delayed Propionibacterium acnes surgical site infections occur only in the presence of an implant. Sci Rep 12 sept. 2016;6(1):32758.
Josse J, Guillaume C, Bour C, Lemaire F, Mongaret C, Draux F et al. Impact of the maturation of human primary bone-forming cells on their behavior in Acute or Persistent Staphylococcus aureus infection models. Front Cell Infect Microbiol [Internet] 21 juin 2016 [cité 28 nov 2023];6.
Achermann Y, Goldstein EJC, Coenye T, Shirtliff ME. Propionibacterium acnes: from Commensal to Opportunistic Biofilm-Associated Implant Pathogen. Clin Microbiol Rev Juill. 2014;27(3):419–40.
Dodson CC, Craig EV, Cordasco FA, Dines DM, Dines JS, DiCarlo E, et al. Propionibacterium acnes infection after shoulder arthroplasty: a diagnostic challenge. J Shoulder Elb Surg mars. 2010;19(2):303–7.
Levy PY, Fenollar F, Stein A, Borrione F, Cohen E, Lebail B, et al. Propionibacterium acnes postoperative shoulder arthritis: an emerging clinical entity. CLIN INFECT DIS 15 juin. 2008;46(12):1884–6.
Arciola CR, Campoccia D, Montanaro L. Implant infections: adhesion, biofilm formation and immune evasion. Nat Rev Microbiol Juill. 2018;16(7):397–409.
Okuda Kichi, Nagahori R, Yamada S, Sugimoto S, Sato C, Sato M et al. The Composition and Structure of Biofilms Developed by Propionibacterium acnes Isolated from Cardiac Pacemaker Devices. Front Microbiol. 14 févr. 2018;9:182.
Dubus M, Varin J, Papa S, Chevrier J, Quilès F, Francius G, et al. Bone marrow mesenchymal stem cells offer an immune-privileged niche to Cutibacterium acnes in case of implant-associated osteomyelitis. Acta Biomater Janv. 2022;137:305–15.
Yu JL, Månsson R, Flock JI, Ljungh Å. Fibronectin binding by Propionibacterium acnes. FEMS Immunol Med Microbiol 17 janv. 2006;19(3):247–53.
Lamret F, Lemaire A, Lagoutte M, Varin-Simon J, Abraham L, Colin M, et al. Approaching prosthesis infection environment: development of an innovative in vitro Staphylococcus aureus biofilm model. Biofilm déc. 2023;5:100120.
Acknowledgements
The authors thank Véronique Vernet-Garnier for providing C. acnes strains (Reims University Hospital), URCATech (University of Reims Champagne-Ardenne) for imaging core facilities as well as Christine Terryn who provided methodologies to perform and analyze CLSM acquisitions and Clémence Demangel for microblasting titanium discs (CRITT-MI, Charleville-Mézière).
Funding
This research received funding from the University of Reims Champagne Ardenne (URCA), ESCMID and MICA Carnot Institute (InVitrOs project).
Author information
Authors and Affiliations
Contributions
F.R conceptualized the study and F.R and S.G led the project. J.V.S, F.V, C.M and X.O participated in the elaboration of methodology. J.V.S performed the experiments and analyzed all data. F.R, M.C and S.G supervised and validated the results. J.V.S, F.R, C.M and M.F.T participated to the investigation of this study. J.V.S, F.R, M.C and F.V participated in the initial draft of the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
Clinical strains were registered on clinicaltrials.gov (NCT03950063).
Consent for publication
Not applicable.
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Below is the link to the electronic supplementary material.
![](http://media.springernature.com/lw1/springer-static/esm/art%3A10.1186%2Fs12866-024-03422-1/MediaObjects/12866_2024_3422_MOESM1_ESM.jpg)
![](http://media.springernature.com/lw1/springer-static/esm/art%3A10.1186%2Fs12866-024-03422-1/MediaObjects/12866_2024_3422_MOESM2_ESM.jpg)
![](http://media.springernature.com/lw1/springer-static/esm/art%3A10.1186%2Fs12866-024-03422-1/MediaObjects/12866_2024_3422_MOESM3_ESM.jpg)
![](http://media.springernature.com/lw1/springer-static/esm/art%3A10.1186%2Fs12866-024-03422-1/MediaObjects/12866_2024_3422_MOESM5_ESM.jpg)
![](http://media.springernature.com/lw1/springer-static/esm/art%3A10.1186%2Fs12866-024-03422-1/MediaObjects/12866_2024_3422_MOESM6_ESM.jpg)
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
About this article
Cite this article
Varin-Simon, J., Colin, M., Velard, F. et al. Cutibacterium acnes biofilm formation is influenced by bone microenvironment, implant surfaces and bacterial internalization. BMC Microbiol 24, 270 (2024). https://doi.org/10.1186/s12866-024-03422-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s12866-024-03422-1