Abstract
Unsaturated polyester/montmorillonite nanocomposite were obtained and characterized. Montmorillonite (MMT) used as inorganic filler was modified with incorporation of metal complexes (CuEDA2Cl2). The effect of chemical modification of this clay on the mechanical properties of unsaturated polyester matrix was analyzed. The results clearly show that the incorporation of copper complexes in the clay (CuEDA2-MMT) caused a desired effect on its final properties improving the performance of the nanocomposites. The improvement could be directly related to the dispersion of the clay inside the matrix, as shown by scanning electron microscopy. The ultraviolet-visible spectra showed that the absorbance of unsaturated polyester films increased with incorporation of complexed clay CuEDA2-MMT, especially at wavelengths of 300–500 nm. The corrosion performance of unsaturated polyester nanocomposite coating stainless steel was realized by electrochemical impedance spectroscopy. The corrosion protection of steel coating UP was increased after incorporation of clay montmorillonite and with CuEDA2-MMT.
Similar content being viewed by others
References
Mortaigne, B., Bourbigot, S., Le Bras, M., et al., Polym. Degrad. Stab., 1999, vol. 64, p. 443.
Shahid, N., Villate, R.G., and Baron, A.R., Compos. Sci. Technol., 2005, vol. 27, p. 1123.
He, H., Duchet, J., Gérard, J.F., and Galy, J., J. Colloid Interface Sci., 2006, vol. 295, p. 202.
Mandalia, T. and Bergaya, F., J. Phys. Chem. Solids, 2006, vol. 67, p. 836.
Hedley, C.B., Yuan, G., and Theng, B.K.G., Appl. Clay Sci., 2007, vol. 35, p. 180.
Bala, P., Samantaray, B.K., and Srivastava, S.K., Mater. Res. Bull., 2000, vol. 35, p. 1717.
Dias, P.M., Faria, D.L.A., and Constantino, V.R.L., Clay Miner., 2005, vol. 53, p. 362.
Bekri, I.A. and Srasra, E., Mater. Res. Bull., 2010, vol. 45, p. 1941.
Chieruzzi, M., Miliozzi, A., and Kenny, J.M., Composites, Part A, 2013, vol. 45, p. 44.
Bellisario, D., Quadrini, F., and Santo, L., Prog. Org. Coat., 2013, vol. 76, p. 1863.
Ollier, R., Rodriguez, E., and Alvarez, V., Composites, Part A, 2013, vol. 48, p. 137.
Laatar, F., Gomez, M., Ben Romdhane, M.R., and Srasra, E., J. Polym. Res., 2016, vol. 23, p. 239.
Mathew, A.M. and Predeep, P., Prog. Org. Coat., 2012, vol. 74, p. 14.
Gu, A. and Liang, G., Polym. Degrad. Stab., 2003, vol. 80, p. 383.
Bekri, I.A. and Srasra, E., Mater. Res. Bull., 2010, vol. 45, p. 1941.
Ollier, R., Vazquez, A., and Alvarez, V., Biodegradable Nanocomposites Based Modified Bentonite and Polycaprolactone, New York: Nova Publ., 2011.
Pereira, C.M.C., Herrero, M., Labajos, F.M., et al., Polym. Degrad. Stab., 2009, vol. 94, p. 939.
Poznyak, S.K., Zheludkevich, M.L., Raps, D., et al., Prog. Org. Coat., 2008, vol. 62, p. 226.
Mansfeld, F., Kendig, M.W., and Tsai, S., Corrosion, 1982, vol. 38, p. 478.
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Laatar, F., Predeep, P., Romdhane, M.R.B. et al. Effect of Nanoclay on the Corrosion Protection Efficiency of UP/CuEDA2-MMT Nanocomposite Coatings Assessed by EIS Measurements. Prot Met Phys Chem Surf 54, 541–547 (2018). https://doi.org/10.1134/S2070205118030310
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S2070205118030310