Abstract—The physicochemical and service properties of new complex Nb–Si–Al–Fe–Ti alloys containing (wt %) 0–25 Si, 20–23 Nb, 5–6 Al, and 3–4 Ti are studied and compared with the well-known two-component Fe–60% Nb alloy. The two-component Fe–Nb alloy belongs to the group of super-refractory ferroalloys with a solidification temperature of 1720°C. A decrease in the niobium concentration and an increase in the content of Si, Al, and Ti make it possible to transfer the alloys to the group of refractory ferroalloys with a melting temperature of 1550–1584°C. The lowest solidification temperature (1550°C) is characteristic of an alloy containing the maximum silicon content (25 wt %) and the minimum niobium content (20 wt %). A pycnometric study of the densities of the complex ferroalloys shows that an increase in the silicon concentration to 21–25 wt % leads to a decrease in the alloy density to optimum values (5000–7000 kg/m3). The melting of the complex niobium alloys with a lump diameter of 2–100 mm in an iron–carbon melt under static conditions has been studied by mathematical modeling. The melting of all complex alloys is found to proceed in three stages. Due to high melting temperatures, super-refractory ferroalloys, which include the two-component alloy with 60 wt % Nb, dissolve at the temperature of liquid steel; therefore, their assimilation mechanism proceeds in two stages. The alloy containing 25 wt % Si and 20 wt % Nb has the shortest melting time at all lump sizes. The ferroalloy lump size is shown to affect the melting/dissolution time most strongly. This is explained by the fact that the alloy mass increases with the lump size, which brings about an increase in the heat content and the frozen steel skin thickness. The complex alloys are shown to have the most favorable densities and solidification temperatures as compared to standard ferroniobium. The alloy containing (wt %) 25 Si, 20 Nb, 5 Al, and 3 Ti has the best complex of physicochemical and service properties.
This is a preview of subscription content, log in via an institution to check access.
REFERENCES
J. Takahashi, K. Kawakami, J. Hamada, et al., “Direct observation of niobium segregation to dislocations in steel,” Acta Mater. 107, 415–422 (2016). https://doi.org/10.1016/j.actamat.2016.01.070
Ly. Sun, X. Liu, X. Xu, et al., “Review on niobium application in microalloyed steel,” J. Iron Steel Res. Int. 29 (10), 1513–1525 (2022). https://doi.org/10.1007/s42243-022-00789-1
P. Yan and H. Bhadeshia, “Austenite–ferrite transformation in enhanced niobium, low carbon steel,” Mater. Sci. Technol. 31 (9), 1066–1076 (2015). https://doi.org/10.1179/1743284714Y.0000000673
V. I. Zhuchkov, A. S. Noskov, and A. L. Zav’yalov, Dissolution of Ferroalloys in Liquid Metal (UrO AN SSSR, Sverdlovsk, 1990).
V. I. Zhuchkov and O. V. Zayakin, “Development of the composition and process of producing multicomponent ferroalloys,” Izv. Vyssh. Uchebn. Zaved., Chern. Metall. 63 (10), 791–795 (2020). https://doi.org/10.17073/0368-0797-2020-10-791-795
I. N. Kel, V. I. Zhuchkov, D. S. Renev, et al., “Study of the physicochemical characteristics of complex boron-containing ferroalloys,” AIP Conf. Proc. 2313 (1), 050015 (2020). https://doi.org/10.1063/5.0032689
B. I. Emlin and M. I. Gasik, Handbook of Electrothermic Processes (Metallurgiya, Moscow, 1978).
L. N. Gasik, V. S. Ignatiev, and M. I. Gasik, Structure and Quality of Industrial Ferroalloys and Master Alloys (Technika, Kiev, 1975).
A. I. Stroganov, “Requirements for ferroalloys for deoxidation and alloying,” in Production of Ferroalloys (Izd. Kuz. PI, Novokuznetsk, 1980), pp. 5–24.
V. S. Ignat’ev, I. A. Bespalova, V. S. Tikhorevskii, et al., Physical Properties of Alloying Alloys. Ferroalloy Production (Chermetinformatsiya, Moscow, 1973), Vol. 2.
V. I. Zhuchkov, N. A. Vatolin, and A. L. Zav’yalov, “On the melting temperatures of ferroalloys,” Metally, No. 4, 45–46 (1982).
I. B. Parimonchik, I. P. Kazachkov, and V. G. Rezchik, “Modeling of the dissolution of ferroalloys in a steel ladle,” Metallurg. Koksokhim, No. 31, 62–65 (1972).
A. F. Petrov, O. V. Kuksa, L. A. Golovko, et al., “Prediction of the physicochemical and thermophysical properties of ferroniobium of standard grades,” in Fundamental and Applied Problems of Ferrous Metallurgy (IChM NAS of Ukraine, Dnipro, 2017), No. 31, pp. 260–265.
D. S. Renev, O. V. Zayakin, and V. I. Zhuchkov, “Study of the melting time of complex nickel-containing ferroalloys in liquid steel,” Steel Transl. 52 (8), 731–735 (2022). https://doi.org/10.3103/S0967091222080095
Y. Jiang, F. Li, S.-R. Li, et al., “Thermodynamic assessment of the Fe–Nb–Si System,” J. Mining Metallurg., Sec. B: Metallurg. 57 (3), 331–340 (2021). https://doi.org/10.2298/JMMB191220029J
D. Wang, Sh. Yang, M. Yang, et al., “Experimental investigation of phase equilibrium in the Fe–Nb–Si ternary system,” J. Alloys Compd. 605, 183–192 (2014). https://doi.org/10.1016/j.jallcom.2014.03.167
N. V. Korchemkina, “Estimation of mixing enthalpies based on experimental data on the kinematic viscosity and density of iron–niobium–silicon (aluminum) melts,” in Proceedings of the XI Russian Conference on Structure and Properties of Metal and Slag Melts (2004), pp. 158–161.
Funding
This work was supported by the Russian Russian Science Foundation, project no. 21-19-00252, https://rscf.ru/project/21-19-00252.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors of this work declare that they have no conflicts of interest.
Additional information
Translated by K. Shakhlevich
Publisher’s Note.
Pleiades Publishing remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Zayakin, O.V., Kel, I.N., Renev, D.S. et al. Physicochemical and Service Properties of Nb–Si–Al–Fe–Ti Alloys. Russ. Metall. 2023, 1193–1200 (2023). https://doi.org/10.1134/S0036029523080347
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0036029523080347