Abstract
High energy particle radiations induce severe microstructural damage in metallic materials. Nanoporous materials with a giant surface-to-volume ratio may alleviate radiation damage in irradiated metallic materials as free surface are defect sinks. Here we show, by using in situ Kr ion irradiation in a transmission electron microscope at room temperature, that nanoporous Au indeed has significantly improved radiation tolerance comparing with coarse-grained, fully dense Au. In situ studies show that nanopores can absorb and eliminate a large number of radiation-induced defect clusters. Meanwhile, nanopores shrink (self-heal) during radiation, and their shrinkage rate is pore size dependent. Furthermore, the in situ studies show dose-rate-dependent diffusivity of defect clusters. This study sheds light on the design of radiation-tolerant nanoporous metallic materials for advanced nuclear reactor applications.
Similar content being viewed by others
Introduction
Energetic particle (such as ions, neutrons and protons) radiations induce a large population of vacancies and self-interstitial atoms (SIAs) in metallic materials, and these point defects can combine into clusters, in the form of dislocation loops and networks, voids, bubbles and stacking fault tetrahedra (SFTs)1,2,3,4. As a result of severe radiation, the microstructure and mechanical properties of the materials can be significantly degraded as evidenced by void swelling, radiation hardening, embrittlement and significant loss of ductility5,6,7,8,9. The search for radiation tolerant materials has been a subject of intense research for decades. Numerous approaches have been adopted to design radiation-resistant materials. The central premise is that certain types of defect sinks may promote the absorption and recombination of interstitials and vacancies and thus enhance the radiation tolerance of materials. Consequently, various types of defect sinks have been investigated, including grain boundary (GB), twin boundary (TB), phase boundary, etc10,11,12,13,14,15,16,17,18. Nanocrystalline materials have abundant GBs and may have extraordinary radiation resistance because GBs act as defect sinks that can absorb irradiation induced defects, and in some cases may serve as sources to emit interstitials and annihilate vacancies19,20,21,22,23. TBs are low energy boundaries and are generally considered to be weak defect sinks. However, recent studies reported that TBs in nanotwinned (nt) metals can capture and rapidly transport defect clusters, remove irradiation-induced defects (including SFTs) effectively, form a TB affected zone within which the accumulative defect cluster density is lower than that in crystal interior, and thus nt metals may have remarkable radiation resistance20,24,25. Layer interface is another effective defect sink and its influence on radiation tolerance of materials has been extensively studied14,15,17,26. For instance, significant layer thickness-dependent reduction of both helium bubble density and alleviation of radiation hardening were reported in some of the immiscible systems, such as Cu/Nb27 and Cu/V28. MD simulations of Cu/Nb also indicate that the Cu-Nb interface is a highly efficient sink for the annihilation of irradiation-induced defects29.
Free surface is typically considered as an unsaturable defect sink, and nanoporous (np) materials with a giant surface-to-volume ratio may have enhanced radiation tolerance compared to the fully dense coarse-grained (cg) counterparts30,31,32. There are extensive studies on mechanical properties of np metals33,34,35,36. However, there are limited cases on irradiation responses of np materials12,31. Ex situ study on np Au under 400 keV Ne++ ion irradiation shows that defect accumulation depends on dose rate37. More specifically, SFTs form at high dose rate, while few SFTs are generated at low dose rate. Their MD simulations indicate that low dose rate leaves ample time for SIAs and vacancies to diffuse to the surface or recombine, whereas at higher dose rate, the time interval between cascades is shorter than the time needed for migration of defects to the surface. Consequently, vacancies have enough time to aggregate and form SFTs. Previous in situ study on np Ag shows the removal of various types of defect clusters, including SFTs, small dislocation loops and large dislocation segments, by the free surface in np Ag under 1 MeV Kr++ ion irradiation32. Furthermore, the in situ study shows that both the global and instantaneous diffusivities in np Ag are lower than those in cg Ag.
Despite these findings, the number of in situ studies on irradiation response of np metals remains scarce. In addition, defect migration kinetics, which is crucial for the modeling of defect evolution in irradiated metals, remains largely unknown38,39. The influence of dose rate on defect diffusivities is still unclear2,31,40.
Here we present in situ Kr ion irradiation studies on cg and np Au. The migration of defect clusters and their elimination by free surfaces are captured by in situ video. Our studies show32 that np Au has significantly better radiation tolerance than coarse-grained Au in terms of reduced size and density of radiation-induced defect clusters. Furthermore, we report on the dose-rate-dependent defect global and instantaneous diffusivities in np Au, which has not been studied in np Ag previously. In addition, nanovoids shrink due to the absorption of defect clusters by nanovoids during irradiation in np Au, and their shrinkage rate depends on pore size. The outstanding irradiation tolerance of np Au has important implications for the design of advanced np materials under extreme radiation environment.
Results
As-prepared cg Au and np Au were both transparent to the electron beam. The diameter of nanovoids varies from ~10 to 100 nm, and the selected area diffraction (SAD) pattern suggests the film was highly textured (see Suppl. Fig. S1a). Figure 1 compares the microstructural evolution in cg and np Au under 1 MeV Kr++ ion irradiation at room temperature. Before irradiation, both np Au and cg Au had little preexisting defects (Fig. 1a–a’). Radiation leads to a gradual and moderate increase of defect density in np Au, up to 0.5 dpa (Fig. 1b–d). In contrast, cg Au has accumulated much more defects rapidly by 0.5 dpa (Fig. 1b’–d’). Bright field and weak beam dark field (WBDF) TEM images show that a majority of defect clusters are dislocation loops and SFTs (Supp. Fig. S1b–d). TEM snapshots from in situ videos compare cg and np Au irradiated to several doses. From 0 to 0.02 dpa (Fig. 1b and 1b’), few defect clusters formed in np Au, whereas defect density in cg Au increased rapidly (Supp. Video 1: 0–0.02 dpa). By 0.2 dpa, both the diameter and density of defect clusters in cg Au increased significantly (Fig. 1c’), while only a few defect clusters were generated in np Au (Fig. 1c and Supp. Video 2: 0.15–0.2 dpa). By 0.5 dpa (Fig. 1d and d’), the average diameter of defect clusters in np Au appeared much smaller than that in cg Au. Figure 2 shows the statistics of the diameter and density of defect clusters in np Au and cg Au. The average defect size is ~10 and 4 nm for cg and np Au, respectively (Fig. 2a). The defect density in both cg and np Au reached saturation at similar dose, ~0.1 dpa (Fig. 2b).
The migration of a large number of defect clusters in np Au has also been examined to estimate their global and instantaneous diffusivities. The global diffusivity, DGlobal, of a defect cluster is determined by using the square of overall defect migration distance (L2) over the accumulative defect lifetime, which includes the migration time and dwelling time. Most defects migrate in a ‘stick-slip’ manner, that is a defect cluster migrates instantaneously within a fraction of a second, and then stays for a while (dwelling time) before its next movement. Thus DGlobal is correlated qualitatively to the average migration speed of a defect cluster over its entire lifetime. Meanwhile, we have also determined the instantaneous diffusivity, DInst., of a defect cluster by only considering the diffusion distance over its migration time (excluding dwelling time). Thus DInst. appears much greater (by an order of magnitude) than DGlobal. The detailed methods to determine diffusivity have been shown previously25. Figure 3a shows DGlobal of defect clusters in np Au at a higher dose rate of 3.2 × 10−3 is ~23 ± 5 nm2/s (), significantly greater than ~4 ± 2 nm2/s at a lower dose rate of 5 × 10−4 dpa/s (). Meanwhile, Fig. 3b shows the DInst. of defect clusters of irradiated np Au varies from 200 to 800 nm2/s, and due to a large scattering, the average value of DInst. shows little dependence on dose rate.
Typical examples of the evolution and interaction of defect clusters with nanovoids are demonstrated by in situ video snapshots over 0.02–0.04 dpa in Fig. 4 (Supp. Video 3). Two small isolated loops were identified at 0 s, one of them (outlined by red dots) was several nm away from the nanovoid, and the other one was adjacent to the void (marked in green) (Fig. 4a). After 2.8 s, two other loops (indicated by the yellow dotted lines) and an SFT (blue marker) emerged near the void (Fig. 4b). Figure. 4c–e show the individual loops combined into a dislocation segment. Meanwhile, the SFT interacted with the void surface and was destructed. In Fig. 4f–h, the same video also shows a small dislocation loop (marked by the red dotted line) migrated towards the void and was captured by 15.9 s. The dislocation segment combined more defects and then interacted with an adjacent SFT, leading to their mutual destruction (Fig. 4i–l). Later a cluster of small SFTs emerged at 25.7 s during irradiation (Fig. 4l).
Another phenomenon is the universal shrinkage of numerous nanopores during in situ radiation of np Au and an example is shown in Fig. 5. Three pores with diameters of 15, 12 and 11 nm were tracked during radiation over 2 dpa (~1600 s). During irradiation, a significant number of defect clusters migrated to these pores (defect absorption), and the dimension of pores decreased continuously (Fig. 5a–e). For instance, by 1.25 dpa (Fig. 5f), the diameter of the pore (marked by red arrows) decreased substantially from 12 to merely 3 nm, and eventually disappeared by 1.5 dpa (Fig. 5g). The diameter of the other two nanopores changed from 15 to 8 nm, and 11 to 8 nm, respectively over 2 dpa. Statistical data in Fig. 6a show that nanopores shrink much faster at higher dose rate, 3.2 × 10− 3 dpa/s, compared to lower dose rate, 5 × 10− 4 dpa/s. Furthermore, the normalized shrinkage of pores, Δd/d, decreases rapidly with increasing pore size (Fig. 6b), indicating smaller pores shrink faster during irradiation.
Discussion
Free surfaces are perfect sinks for defects, so it is natural to speculate that np Au with high surface-to-volume ratio would be more radiation tolerant compared to its cg counterpart. Indeed, our in situ studies show np Au has excellent radiation resistance as evidenced by its substantially lower defect dimension and density than those in cg Au. During irradiation, although the defect density in both cg and np Au reached saturation at similar dose level, the continuous migration of point defects and their clusters towards nanovoids leads to significant reduction of defect concentration, manifested by an overall decrease in defect size and density. Although it appears that there is only a moderate reduction of defect cluster density (a factor of 2) and cluster size (a factor of ~2.5) for np Au compared to cg Au, the point defect concentration difference can be substantial. Assuming all defect clusters are spherical, the point defect concentration amounts to (2.5)3 × 2 ≈ 30. Furthermore, many of the defect clusters in cg Au are much greater than the average defect diameter, whereas the defect clusters in np Au has a much narrower size distribution. In situ studies show the capturing of numerous types of defect clusters (including SFTs, individual dislocation loops, and dislocation segments) by nanovoids. The removal of various types of defect clusters by free surface has been reported previously during in situ radiation study of np Ag32.
Another significant observation revealed by in situ radiation study is the shrinkage of nanovoids in np Au at room temperature. During radiation, most of the vacancies are bound in the form of sessile defect clusters, and thus there may be insufficient vacancies to support void growth. Meanwhile, there is a continuously biased flock of interstitials and their clusters to nanovoids during irradiation. As void shrinkage in the current study is caused by the absorption of irradiation-induced defects, these deliberately introduced nanovoids are effective defect sinks, providing np Au much better radiation tolerance than their cg counterparts. Furthermore, it is natural to speculate that the void shrinkage rate could be determined by the defect capture (absorption) rate or the frequency of interactions between nanovoids and defects. Figure 6a confirms this hypothesis by tracking the evolution of diameters for a number of nanovoids. When the dose rate is increased by ~ six times, the void area, A, decreased much faster. Void shrinkage rate (indicated by the slope of the plots) in the high dose rate area (shaded by yellow color) is ~ six-times larger than the slope of the data in low dose rate area (highlighted in blue color), indicating the void shrinkage rate scales with dose rate.
Besides the direct observation of defect absorption events, another benefit of in situ study is that it allows us to estimate global and instantaneous diffusivities of defect clusters by carefully analyzing the videos and tracking the migration of defect clusters continuously during irradiation. More details on the methods to estimate diffusivity can be found in previous studies24,25,32. The global diffusivity for defect clusters in np Au is calculated to be 4 ± 2 nm2/s when the dose rate is 5 × 10−4 dpa/s, and 23 ± 5 nm2/s at a higher dose rate of 3.2 × 10−3 dpa/s. Clearly, the global diffusivity is significantly reduced (by six times) when the dose rate decreases. However, the instantaneous diffusivity in np Au varies from 200 to 800 nm2/s and shows little dependence on dose rate. Such intriguing phenomena clearly warrant further discussions.
Both global and instantaneous diffusivities are determined by two factors: diffusion distance and a defect’s lifetime. In this study, the diffusivities of defect clusters were estimated when defect density reached saturation. The saturated defect cluster density in np Au is ~15 × 1022 m−3 as shown in Fig. 2b, and therefore, the distance between two defect clusters can be simply estimated to be 15 ~21 nm (these values considered (1) average defect diameter, 4 nm, and (2) the length between two defect clusters can be either edge length or diagonal length in a square). Although the dose rate has been changed, the defect density has reached a plateau (independent of dose rate from ~0.1–2.0 dpa). It follows that the average diffusion distance (limited by defect separation distance) for both high and low dose rate is nearly the same, ~18 nm (see Fig. 3a). Thus the global diffusivity of defects may be largely determined by defects’ lifetime.
A defect’s lifetime includes two components, defect migration time (hopping time) and dwell time (rest time). To estimate the global diffusivity, both migration and dwell time were taken into account. As a defect migrate very rapidly, the lifetime of a defect is dominated by its dwell time. Supplementary Video 4 shows the drastic difference in defect migration activity in np Au irradiated at low and high dose rate. Compared to low dose rate, both defect generation rate and recombination rate increase prominently at higher dose rate. As a consequence, a defect cluster cannot dwell for a long time. Instead, it will frequently migrate toward the free surface, or combine with other clusters. Thus the defect’s dwell time significantly decreases at higher dose rate. Since diffusion lengths are similar in both cases (low vs. high dose rate), the global diffusivity at high dose rate is larger than that at low dose rate.
In contrast to global diffusivity, only a defect’s migration time is considered to determine the instantaneous diffusivity. Nearly all defects migrated within a single frame, and therefore, a defect’s migration time is assumed to be 66 ms for a single migration event (limited by the camera’s capture speed of 15 frame/s). Notice that such an assumption may overestimate a defect’s migration time. There is a large scattering of instantaneous diffusivity. Consequently, the instantaneous diffusivity appears to have an insignificant dependence on dose rate and defect dimension.
We now examine the shrinkage of nanovoids in np Au. Void swelling is frequently observed in many neutron and heavy ion irradiated metals at elevated temperatures41,42,43,44,45, while void shrinkage is commonly observed at room temperature or at the temperature much below the material’s melting point46,47,48,49. It is known that vacancies will be bundled in thermally stable defect clusters, such as vacancy loops and SFTs, during energetic displacement cascade under heavy ion irradiation, and interstitials are mobile near room temperature50,51,52. Therefore, void shrinkage may be anticipated in the current study. However, a question remains to be addressed is: Does defect absorption efficiency dependents on void size in np materials? Figure 6b may provide some clues to this question.
Assuming the incoming flux of defects into a single void is a constant J (unit: volume/area·second), and these defects will fill in the voids (leading to the reduction of void diameter), then J can be simply estimated by (assuming that most nanovoids are through thickness nanopores with cylindrical shape):
where V is the volume of voids, R (=d/2) is the radius of voids, h is the film thickness. ΔR is the reduction of void radius over a period of Δt. It is readily seen thatΔR = JΔt, i.e., Δd = 2JΔt. Consequently the relation between normalized void shrinkage, Δd/d, and void size d can be expressed as:
Thus, the normalized void shrinkage is inversely proportional to the initial defect diameter. This is very close to what has been captured experimentally (Fig. 6b). Furthermore, the attempt to use a constant J to fit all data point (Olive dash line) seems to underestimate (overestimate) Δd/d for smaller (larger) voids. Such systematic deviation suggests that J is greater for smaller voids and less for larger voids. In other words, defects may interact more frequently with smaller voids than the larger ones during irradiation, and therefore, defect absorption efficiency is higher for smaller voids than larger voids. In a recent study on nanovoid-nanotwinned Cu (with an average void diameter of ~10 nm), significant loop-void interactions were observed. Analytical calculations show the existence of significant tensile stress surrounding voids53. When a loop moves closer to a void, its migration rate increases drastically due to the substantial reduction of formation and migration energies of the loop under tensile stress. Compared to larger voids, smaller voids generate higher stress field near void surfaces and therefore, smaller voids capture defects more rapidly during irradiation.
It may appear that the irradiation resistance of np metals will degrade over the long term if most of the nanovoids are completely filled with radiation induced defect clusters. Such concern can be eased for the following reasons. First, bulk (fully dense) Au is extremely vulnerable to radiation damage as shown by severe radiation damage at merely 0.02 dpa. It is clear that nanovoids significantly delay damage accumulation in Au by more than an order of magnitude, rendering np Au resistance to heavy ion irradiations to a much greater dose (1 dpa). Furthermore, the foregoing studies show that the concentration of point defects (such as SIAs) could also be an order of magnitude lower in np Au than that in cg Au. Such a concept derived from the current study indicates that the safe operation period (lifetime) of nuclear reactor steels, if engineered with nanoporous structures, could also be significantly extended. Second, Au is a model system that is known to be vulnerable to radiation damage than many other alloys, such as austenitic stainless steels. One can envision that for a practical reactor steel, the incorporation of nanovoids/nanopores could achieve even greater radiation tolerance than what has been demonstrated in the current model system. Third, although nanovoids may be eliminated during radiation, modeling tool (such as phase field models), may reliably predict the correlation between the service lifetime and desirable combination of different diameter and density nanovoids for design purposes. As Fig. 6(b) suggested, smaller voids shrink faster than the larger ones. Therefore, by deliberately introducing nanovoids with different diameters and density, the radiation stability of reactor steels may be significantly prolonged. Of course, further improvements in nanopore stability might also be beneficial before this concept transfers into a practical option for future reactor steels.
Conclusion
In situ heavy ion irradiation studies were performed on nanoporous Au at room temperature. Dose-rate-dependent defect migration diffusivities were examined, and the global diffusivity is significantly reduced when the dose rate decreases, while the instantaneous diffusivity shows little dependence on dose rate. Nanovoids are effective defect sinks where various types of defect clusters can be absorbed during irradiation. The absorption of defect clusters leads to the shrinkage of nanovoids, and the shrinkage rate, or defect absorption efficiency, is size-dependent. Comparing to larger voids, smaller voids exhibit higher defect absorption efficiency. This study provides significant insight into the design of radiation-tolerant nanoporous metallic materials, such as nanoporous reactor steels for advanced nuclear reactors.
Method
The Ag65Au35 (atomic ratio) leaves (procured from New York Central Art Co.) with dimensions 20 mm × 20 mm × 120 nm were sandwiched by two 304 stainless steel plates and then cold rolled up to ~20% strain so as to reduce the foil thickness and achieve electron beam transparent specimens. The rolled Ag65Au35 leaves were then chemically de-alloyed in a 70% HNO3 solution for 4 h at room temperature. The etched leaves were repeatedly rinsed in deionized water to remove residual acid and eventually lifted off by Cu grids (400 mesh) for in situ radiation studies. All specimens were investigated using an FEI Tecnai G2 F20 ST microscope before and after irradiation. In situ irradiation experiment was performed at room temperature at the IVEM-TANDEM facility at Argonne National Laboratory. An 1 MeV Kr++ ion beam was used for radiation experiments to a maximum fluence of 2 × 1014 ions cm−2 (∼1 dpa). The dose rate applied during in situ radiation experiments varied from 3.2 × 10−3 to 5 × 10−4 dpa/s. SRIM (Kinchin-Pease method) simulation was used to estimate the displacement damage profile (in the unit of displacements-per-atom (DPA)) and Kr ion distribution. Most Kr ions (99.99%) penetrated directly through the specimen and the residual Kr ion concentration in the TEM thin foil is ~0.01 at.%. The temperature rise of specimens during in situ Kr ion irradiation measured by thermocouple is less than 10 °C.
Additional Information
How to cite this article: Li, J. et al. In situ heavy ion irradiation studies of nanopore shrinkage and enhanced radiation tolerance of nanoporous Au. Sci. Rep. 7, 39484; doi: 10.1038/srep39484 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Bacon, D. J. & Diaz de la Rubia, T. Molecular dynamics computer simulations of displacement cascades in metals. Journal of Nuclear Materials 216, 275–290 (1994).
Fu, C.-C., Torre, J. D., Willaime, F., Bocquet, J.-L. & Barbu, A. Multiscale modelling of defect kinetics in irradiated iron. Nat Mater 4, 68–74 (2005).
Uberuaga, B. P., Hoagland, R. G., Voter, A. F. & Valone, S. M. Direct Transformation of Vacancy Voids to Stacking Fault Tetrahedra. Physical Review Letters 99, 135501 (2007).
Was, G. S. Fundamental of radiation materials science: metals and alloys. Springer: New York, 827 (2007).
Stoller, R. E., Odette, G. R. & Wirth, B. D. Primary damage formation in bcc iron. Journal of Nuclear Materials 251, 49–60 (1997).
Odette, G. R., Alinger, M. J. & Wirth, B. D. Recent Developments in Irradiation-Resistant Steels. Annual Review of Materials Research 38, 471–503 (2008).
Mansur, L. K. et al. Materials needs for fusion, Generation IV fission reactors and spallation neutron sources – similarities and differences. Journal of Nuclear Materials 329–333, 166–172 (2004).
Zinkle, S. J. Fusion materials science: Overview of challenges and recent progress. Physics of Plasmas 12, 058101 (2005).
Grimes, R. W., Konings, R. J. M. & Edwards, L. Greater tolerance for nuclear materials. Nat Mater 7, 683–685 (2008).
Guo, Q., Landau, P., Hosemann, P., Wang, Y. & Greer, J. R. Helium Implantation Effects on the Compressive Response of Cu Nanopillars. Small 9, 691–696 (2013).
Liontas, R. et al. Effects of Helium Implantation on the Tensile Properties and Microstructure of Ni73P27 Metallic Glass Nanostructures. Nano letters 14, 5176–5183 (2014).
Caro, M. et al. Radiation induced effects on mechanical properties of nanoporous gold foams. Applied Physics Letters 104, 233109 (2014).
Maloy, S. A. et al. The mechanical properties of 316L/304L stainless steels, Alloy 718 and Mod 9Cr–1Mo after irradiation in a spallation environment. Journal of Nuclear Materials 296, 119–128 (2001).
Chen, Y. et al. Unusual size-dependent strengthening mechanisms in helium ion-irradiated immiscible coherent Cu/Co nanolayers. Acta Materialia 84, 393–404 (2015).
Yu, K. Y. et al. Superior tolerance of Ag/Ni multilayers against Kr ion irradiation: an in situ study. Philosophical Magazine 93, 3547–3562 (2013).
Demkowicz, M. J., Misra, A. & Caro, A. The role of interface structure in controlling high helium concentrations. Current Opinion in Solid State and Materials Science 16, 101–108 (2012).
Wei, Q. M., Li, N., Mara, N., Nastasi, M. & Misra, A. Suppression of irradiation hardening in nanoscale V/Ag multilayers. Acta Materialia 59, 6331–6340 (2011).
Yu, K. Y. et al. In situObservation of Defect Annihilation in Kr Ion-Irradiated Bulk Fe/Amorphous-Fe2Zr Nanocomposite Alloy. Materials Research Letters 3, 35–42 (2014).
Song, M. et al. Response of equal channel angular extrusion processed ultrafine-grained T91 steel subjected to high temperature heavy ion irradiation. Acta Materialia 74, 285–295 (2014).
Yu, K. Y. et al. Removal of stacking-fault tetrahedra by twin boundaries in nanotwinned metals. Nature communications 4, 1377 (2013).
Wang, H. et al. Ion irradiation effects in nanocrystalline TiN coatings. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms 261, 1162–1166 (2007).
Bai, X.-M., Voter, A. F., Hoagland, R. G., Nastasi, M. & Uberuaga, B. P. Efficient Annealing of Radiation Damage Near Grain Boundaries via Interstitial Emission. Science 327, 1631–1634 (2010).
Yu, K. Y. et al. Radiation damage in helium ion irradiated nanocrystalline Fe. Journal of Nuclear Materials 425, 140–146 (2012).
Chen, Y. et al. In situ studies on radiation tolerance of nanotwinned Cu. Acta Materialia 111, 148–156 (2016).
Li, J. et al. In situ study of defect migration kinetics and self-healing of twin boundaries in heavy ion irradiated nanotwinned metals. Nano letters 15, 2922–2927 (2015).
Chen, Y. et al. In situ studies of radiation induced crystallization in Fe/a-Y2O3 nanolayers. Journal of Nuclear Materials 452, 321–327 (2014).
Misra, A., Demkowicz, M. J., Zhang, X. & Hoagland, R. G. The radiation damage tolerance of ultra-high strength nanolayered composites. JOM 59, 62–65 (2007).
Fu, E. G., Misra, A., Wang, H., Shao, L. & Zhang, X. Interface enabled defects reduction in helium ion irradiated Cu/V nanolayers. Journal of Nuclear Materials 407, 178–188 (2010).
Demkowicz, M. J., Hoagland, R. G. & Hirth, J. P. Interface Structure and Radiation Damage Resistance in Cu-Nb Multilayer Nanocomposites. Physical Review Letters 100, 136102 (2008).
Sun, C. et al. Resilient ZnO nanowires in an irradiation environment: An in situ study. Acta Materialia 95, 156–163 (2015).
Bringa, E. M. et al. Are nanoporous materials radiation resistant? Nano letters 12, 3351–3355 (2012).
Sun, C. et al. In situ study of defect migration kinetics in nanoporous Ag with enhanced radiation tolerance. Scientific reports 4, 3737 (2014).
Sun, Y., Ye, J., Minor, A. M. & Balk, T. J. In situ indentation of nanoporous gold thin films in the transmission electron microscope. Microscopy Research and Technique 72, 232–241 (2009).
Sun, X.-Y., Xu, G.-K., Li, X., Feng, X.-Q. & Gao, H. Mechanical properties and scaling laws of nanoporous gold. Journal of Applied Physics 113, 023505 (2013).
Jin, H.-J. et al. Deforming nanoporous metal: Role of lattice coherency. Acta Materialia 57, 2665–2672 (2009).
Biener, J., Hodge, A. M., Hamza, A. V., Hsiung, L. M. & Satcher, J. H. Nanoporous Au: A high yield strength material. Journal of Applied Physics 97, 024301 (2005).
Fu, E. G. et al. Surface effects on the radiation response of nanoporous Au foams. Applied Physics Letters 101, 191607 (2012).
Matsukawa, Y. & Zinkle, S. J. One-Dimensional Fast Migration of Vacancy Clusters in Metals. Science 318, 959–962 (2007).
Osetsky, Y. N., Bacon, D. J., Serra, A., Singh, B. N. & Golubov, S. I. One-dimensional atomic transport by clusters of self-interstitial atoms in iron and copper. Philosophical Magazine 83, 61–91 (2003).
Wirth, B. D., Odette, G. R., Maroudas, D. & Lucas, G. E. Energetics of formation and migration of self-interstitials and self-interstitial clusters in α-iron. Journal of Nuclear Materials 244, 185–194 (1997).
Mansur, L. K. Void swelling in metals and alloys under irradiation: an assessment of the theory. Nuclear Technology 40, 5–34 (1978).
Norris, D. The use of the high voltage electron microscope to simulate fast neutron-induced void swelling in metals. Journal of Nuclear Materials 40, 66–76 (1971).
Little, E. & Stow, D. Void-swelling in irons and ferritic steels: II. An experimental survey of materials irradiated in a fast reactor. Journal of Nuclear Materials 87, 25–39 (1979).
Garner, F., Brager, H., Gelles, D. & McCarthy, J. Neutron irradiation of FeMn, FeCrMn and FeCrNi alloys and an explanation of their differences in swelling behavior. Journal of Nuclear Materials 148, 294–301 (1987).
Packan, N., Farrell, K. & Stiegler, J. Correlation of neutron and heavy-ion damage: I. The influence of dose rate and injected helium on swelling in pure nickel. Journal of Nuclear Materials 78, 143–155 (1978).
Zhu, X. F. et al. Direct observation of irradiation-induced nanocavity shrinkage in Si. Applied Physics Letters 79, 3416 (2001).
Zheng, H. et al. Electron beam-assisted healing of nanopores in magnesium alloys. Sci Rep 3, 1920 (2013).
Evans, J. H. Void swelling and irradiation-induced void shrinkage in neutron irradiated molybdenum and TZM. Journal of Nuclear Materials 88, 31–41 (1980).
Krishan, K. & Nandedkar, R. V. Mechanisms for radiation-induced shrinkage of voids. Nature 280, 253–253 (1979).
Bullough, R., Eyre, B. L. & Krishan, K. Cascade Damage Effects on the Swelling of Irradiated Materials. Proceedings of the Royal Society of London. Series A, Mathematical and Physical Sciences 346, 81–102 (1975).
Eyre, B. L. Transmission electron microscope studies of point defect clusters in fcc and bcc metals. Journal of Physics F: Metal Physics 3, 422 (1973).
Zinkle, S. J. in Comprehensive Nuclear Materials pp. 65–98 (Elsevier, Oxford, 2012).
Chen, Y. et al. Damage-tolerant nanotwinned metals with nanovoids under radiation environments. Nature communications 6, 7036 (2015).
Acknowledgements
We acknowledge financial support by NSF-DMR-Metallic Materials and Nanostructures Program under grant no. 1643915. JD is supported financially by Petroleum Research Foundation # 53741 -ND10. S. Xue is supported by DoE-OBES under grant no. DE-SC0016337. H.W. acknowledges the support from the US Office of Naval Research (ONR, N00014-16-1-2778). We also acknowledge the use of microscopes at the Microscopy and Imaging Center at Texas A&M University and the DoE Center for Integrated Nanotechnologies managed by Los Alamos National Laboratory. The IVEM facility at Argonne National Laboratory is supported by DOE-Office of Nuclear Energy.
Author information
Authors and Affiliations
Contributions
J.L., J.D. and Q.L. prepared np Au specimens for in situ Kr ion irradiation; J.L., C.F. and S.X. performed the in situ Kr ion irradiation experiments at Argonne National Laboratory. J.L. performed post irradiation study at the Microscopy and Imaging Center at Texas A&M University. Y.C., H.W. and X.Z. assisted with data analyses and interpretation. X.Z. developed the concept and directed the project. J.L. wrote the original draft of the paper and all authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, J., Fan, C., Ding, J. et al. In situ heavy ion irradiation studies of nanopore shrinkage and enhanced radiation tolerance of nanoporous Au. Sci Rep 7, 39484 (2017). https://doi.org/10.1038/srep39484
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep39484
- Springer Nature Limited
This article is cited by
-
The In Situ Ion Irradiation Toolbox: Time-Resolved Structure and Property Measurements
JOM (2022)
-
Recent progress of radiation response in nanostructured tungsten for nuclear application
Tungsten (2021)
-
Recent Studies on Void Shrinkage in Metallic Materials Subjected to In Situ Heavy Ion Irradiations
JOM (2020)
-
Recent Studies on the Microstructural Response of Nanotwinned Metals to In Situ Heavy Ion Irradiation
JOM (2020)
-
In situ TEM investigation of self-ion irradiation of nanoporous gold
Journal of Materials Science (2019)