Abstract
The one of main reasons of the premature failure of Ti-based implants is infections. The metal- and metal oxide-based nanoparticles have very high potential on controlling of infections. In this work, the randomly distributed AgNPs-deposited onto well-ordered TiO2 nanotube surfaces were fabricated on titanium by anodic oxidation (AO) and electrochemical deposition (ED) processes. AgNPs-deposited nanotube surfaces, which is beneficial for bone tissue growth exhibited hydrophilic behaviors. Moreover, the AgNPs-deposited nanotube surfaces, which prevent the leaching of metallic Ti ions from the implant surface, indicated great corrosion resistance under SBF conditions. The electrochemical corrosion resistance of AgNPs-deposited nanotube surfaces was improved up to about 145% compared to bare Gr2 surface. The cell viability of AgNPs-deposited nanotube surfaces was improved. Importantly, the AgNPs-deposited nanotube surfaces exhibited antibacterial activity for Gram-positive and Gram-negative bacteria. Eventually, it can be concluded that the AgNPs-deposited nanotube surfaces possess high stability for long-term usage of implant applications.
Similar content being viewed by others
Introduction
The TiO2 nanotube arrays produced on titanium and its alloys have made a great impact in different areas such as solar cells, photocatalytic systems, water splitting, sensor, drug delivery and biomedical implants at last year’s1,2,3,4,5. The nanotubes that could be produced by anodic oxidation process refer to tubular surface structures in the nanometer scale. TiO2 nanotubes with nano-topography mimics bone surface morphology and contain bioactive and biocompatible oxide phases. TiO2 nanotubes have positive effect on cell adhesion, proliferation, differentiation and apatite formation6. Thus, they are regarded as being more biocompatible than bare titanium and its alloys7,8,9. This surface structure leads to increase surface area promoting greater osseo-integration. However, this is resulted in creating more favorable conditions for bacterial proliferation10.
Nano-structured surfaces which are expressed as “promising” to control bacterial adhesion and biofilm formation can be based on well- or random-formation11. Nano-structured surfaces usually provide low bacterial adhesion. Moreover, adhered bacteria have multiple contact sites with the surface. Adhered bacteria onto nanostructured surfaces suffer localized cell wall deformation. This adhesion onto contact sites can be resulted in causing bacterial death12,13.
AgNPs (silver nanoparticles) have many advantages such as good antibacterial activity, excellent biocompatibility, and satisfactory stability against to antibiotics and antibiotic organic antimicrobials for medical applications14. It is well known that AgNPs are one of the most commonly tested nanoparticles in nanobiotechnology due to their unique physical, chemical and biological properties15. AgNPs which affect cellular functions as well as structures exhibits very strong antibacterial effect compared to other Ag structures such as microparticles and ionic compounds16. Ag has a toxicity effect over extensive bacteria types. Thus, it has been widely exploited for its antibacterial applications17. The releasing of Ag+ ions is reduced by the penetration of AgNPs onto the nanotube structure. Thus, it was stated that AgNPs on the nanotube structure provides a long-lasting antibacterial capability and less cytotoxic Ag concentration compared to other Ag structures such as microparticles, ionic or compounds18.
There are many studies on the fabrication and investigation of Ag ions-, Ag-incorporated and AgNPs-doped TiO2 nanotubes for photocatalytic, sensor, agricultural and water splitting in the literature19,20,21,22,23,24. However, the investigations on biological properties of Ag ions-, Ag-incorporated and AgNPs-doped TiO2 nanotubes for medical applications are limited in the literature. To prevent biofilm formation and bacterial growth, AgNPs were doped onto TiO2 nanotube surfaces by various methods such as ultraviolet radiation, magnetron sputtering, immersion test, spray deposition, e-beam evaporation etc.12,25,26,27,28,29,30,31,32,33,34. Wei et al. evaluated Ag nanoparticles and Ag ions were both loaded on TiO2 nanotubes by immersion in AgNO3 solutions followed by ultraviolet light radiation34. Di et al. investigated the antibacterial and antioxidant properties of AgNPs incorporated tannic acid/nanoapatite composite coating on Ti by AO and immersion tests35. Zhao et al. evaluated antibacterial properties of AgNPs-doped nanotube coatings by AO and immersion processes31. Bilek et al. examined antibacterial activity of commercial AgNPs decorated–TiO2 nanotubes36. Hyuk Uhm et al. investigated AgNPs-doped nanotubes by AO and e-beam processes33. Sudhisha et al. evaluated antibacterial and biocompatibility of AgNPs doped poly(3,4-ethylene dioxythiophene) on nanotubes by AO and electro-polymerization37. Perumal et al. examined AgNPs incorporated polyaniline on TiO2 nanotube array by AO and electro-polymerization6. Staats et al. investigated antimicrobial potential and osteoblastic cell growth at selenium or silver incorporation onto nanotubes on Ti6Al4V38. However, the wettability, electrochemical, biocompatibility and antibacterial of AgNPs-deposited nanotube surfaces fabricated by AO and ED processes have not been investigated in detail whereas many investigations were carried out on Ag ions-, Ag-incorporated and AgNPs-doped nanotube surfaces.
This work aimed to develop and characterize a novel AgNPs-deposited nanotube surfaces on titanium substrates by combined AO and ED processes and to investigate biocompatiblitiy and antibacterial properties. All surfaces were characterized by XRD, SEM, EDX-mapping and contact angle goniometer. The electrochemical properties of the surfaces were investigated under SBF conditions by Tafel extrapolation methods. Furthermore, cell viability, alkaline phosphatase activity and blood protein adhesion were evaluated and antibacterial properties of the surfaces were assessed against to Gram-positive bacteria (Streptococcus pyogenes, Bacillus subtilis, Staphylococcus aureus) and Gram-negative (Salmonella typhimurium, Pseudomonas aeruginosa, Escherichia coli). Our results indicated that the AgNPs-deposited nanotube surfaces have an important role on electrochemical properties, biocompatiliblity and antibacterial properties. Thus, they should be addressed for designing antibacterial surfaces for implant applications.
Experimental details
Sample preparation and coating fabrication
Grade 2 titanium (ASTM F67 cp-Ti; Shaanxi Aone Titanium) plates (10 mm × 10 mm × 1 mm) were polished from 180# to 2000# sandpapers. Afterwards, all prepared plates were cleaned in an ultrasonic bath and dried.
The cp-Ti plates were anodized in 0.5% wt. NH4F and 5.0% vol. deionized water containing ethylene glycol-based solution at 50 V for 1 h below 30 °C by using a DC power supply (Good Will Instek PSU 400). They were ultrasonically cleaned in distilled water solution for 15 min and then dried in warm air (40 °C) for 1 min by heat gun. All AO coated samples were transferred to muffle furnace. After AO process, the heat treatment was carried out to transform from amorphous to crystalline form at 450 °C for 1 h as reported previous works39,40. The cp-Ti and Pt were served as positive and negative electrodes through AO process, respectively.
Antibacterial AgNPs on nanotube surfaces were deposited at a constant potential value of − 1 V for 0.5 min (Gr2-50 V-Ag-0.5 m), 1 min (Gr2-50 V-Ag-1 m) and 5 min (Gr2-50 V-Ag-5 m) by using a potentiostat/galvanostat device (Gamry 1010E). Nanotube-coated surfaces in an aqueous electrolyte consist of 10 mM AgNO3 (Merck, ACS, ISO, Reag. Ph Eur) were dipped and coated. The Ag structure was randomly deposited as nanoparticles on the nanotube surfaces by ED process. After ED process, all samples were cleaned in distilled water solution for 15 min by in an ultrasonic bath.
Characterization of the surfaces
The surface morphology was taken at 20,000× and 50,000× of magnifications with using 15 kV of accelerating voltage by SEM (Hitachi SU 1510). The elemental distribution and elemental amount of the surfaces were investigated at 500× of magnification with using 15 kV of accelerating voltage by EDX-mapping and -area. The surface roughness (Sa) and topography were evaluated in the 2.5 µm × 2.5 µm with using a TAP-190 cantilever by a Nanosurf C3000 Atomic Force Microscopy (AFM). Average contact angles of the surfaces were investigated with a sessile constant drop technique by a Dataphysics OCA-15EC contact angle goniometer. All contact angles were measured within 1 min after the water droplets with 1 µL contacted the surfaces.
Electrochemical test
Electrochemical tests were carried out in SBF solution41 at body temperature (36.5 °C) by using Tafel extrapolation test (Metrohm Autolab PGSTAT101 potentiostat/galvanostat). To determine Tafel potential values, the OCP (open circuit potentials) were initially measured for all samples. Tafel extrapolation test were carried out at 1 mV/s between − 500 and 500 mV of OCP. A conventional three-electrode cell such as the sample working, Ag/AgCl reference and Pt counter was used for electrochemical tests as described previous work42.
Cell viability test
Biomaterials used in medical applications should be biocompatible with blood and should not exhibit cytotoxicity. The cytotoxic effect of each coating was determined by MTT test using RPMI 8866 (Cell Linehuman)-Lymphoblastoid cell cells. Cells were incubated at 37 °C (5% CO2) in a solution containing 2 mM Glutamine, 100 IU/mL penicillin, RPMI 1640, 10% Fetal Bovine Serum and 100 µg/mL streptomycin. Each coating (0.5 cm2) was sterilized in an autoclave and placed in cell culture wells. Media containing 2 × 105 cells/mL cells was transferred to the wells. Coatings and cells were incubated for 48 h. Then, 200 µL of medium containing 20 µL of 5 µg/mL MTT and 200 µL of isopropanol containing 0.04 M HCl were added to each well. After 4 h of incubation, absorbances were measured at 570 nm by spectrophotometer. Cell viability was evaluated according to the positive control in which DMSO was used.
Alkaline phosphatase activity
ALP activity is a significant indicator in determining the activity of osteoblastic cells. The principle of this test is based on the conversion of p-nitrophenyl phosphate to p-nitrophenol and phosphate by hydrolysis. SAOS-2 (primary osteogenic sarcoma, Cell Line human) cells were grown by incubating for 72 h in medium containing McCoy's 5A (l-Glutamine, serum-free), penicillin–streptomycin (1%) and fetal calf serum (15%). Coatings (0.5 cm2) and 2 × 105 cells/mL of cells were interacted for 48 h. At the end of the interaction, cells were collected and washed with lysis buffer (250 µL, 0.5% v/v Triton X-100). Cells were incubated in 1 mM MgCl2 and Tris (pH 7.6), then centrifuged at 5000 rpm for 10 min. 50 µL of supernatant and 50 µL of ALP reagent were mixed and spectrophotometric measurements were performed at 410 nm.
Artificial blood protein adhesion
Adhesion of blood proteins in blood compatibility of biomaterials is also one of the tested parameters. The adhesion of blood proteins to a hemocompatible surface reduces its compatibility. For this purpose, the interactions of the coatings with gamma-globulin, albumin and fibrinogen proteins were investigated. Commercially purchased albumin, gamma-globulin and fibrinogen proteins were prepared at 20 mg/mL concentration and incubated with the coating surfaces at 37 °C for 2 h in a batch system. After incubation, the coatings were washed twice with 15 mL of saline solution to remove surface proteins. Ultrasonic vibration at 35 kHz frequency for 5 min was applied to obtain the proteins that adhere to the coating surface. The concentrations of proteins, which separated from the surface and passed into the solution, were determined at 280 nm.
Bacterial adhesion test
Bacterial adhesion assays were performed against Gram-positive bacteria (Streptococcus pyogenes, Bacillus subtilis, Staphylococcus aureus) and Gram-negative (Salmonella typhimurium, Pseudomonas aeruginosa, Escherichia coli). Bacterial suspension was prepared using 5 mL of sterile medium from bacterial stock cultures. 100 μL of the suspension adjusted according to 0.5 McFarland, was combined with broth medium and interacted with the coating surface (0.5 cm2). After incubation for 24 h at 37 °C, the coatings removed from the medium were washed twice with 15 mL of saline solution to remove bacteria that did not adhere to the surface. Each coating was taken into tubes containing 2 mL of physiological solution and subjected to ultrasonic vibration at 35 kHz frequency for 5 min. After sonication, the samples taken from the tubes were transferred to agar medium and colonies of each bacteria were counted after 24 h of incubation.
Statistical analysis
Statistical analysis was performed using “IBM SPSS Statistics 22 SP” and all results are given as mean ± SD. p < 0.05 was considered statistically significant.
Results and discussion
The morphologies of the surfaces
The surface morphologies of bare nanotube array and AgNPs-deposited at 0.5 min, 1 min and 5 min on nanotube surfaces are given in Fig. 1. The average diameter was measured as approximately 110 nm for nanotubes on cp-Ti. A small addition of fluoride ions into ethylene glycol is one of the key factors to form well-ordered TiO2 nanotube structures. The typical amount of fluoride ion addition leading to well-ordered TiO2 array is between 0.3 and 0.5 wt% as reported in the literature43. F− ions in the electrolyte, which have great reactivity, form many pits on the compact oxide layer through AO process. The chemical dissolution process is rapid in electrolytes containing F- ions. This leads enlarging and deepening the pits and elongates them upward44. At the bottom of the pores, chemical dissolution continues to occur, thinning the oxide layer significantly45. As a result of these, TiO2 nanotube arrays form on titanium surface.
As seen in Fig. 1, the amount and size of brightly colored particles accumulated on the surface increase with the increasing time during the ED process. The sizes for 0.5, 1 and 5 min were measured as 85, 113 and 141 nm by Fiji software, respectively. At the first stages of the ED process, while the particles are finer and homogeneous, nanoparticles of different sizes are coated on the nanotube surfaces in a more non-uniform manner depending on the deposition rate with the increase in time. While some nanoparticles enclose a single or more tube structure, some nanoparticles agglomerate further and accumulate on the surface, closing several nanotube structures as shown in Fig. 1b–d. The formation mechanism of AgNPs contains the nucleation and growth of Ag structure during ED process. The top of nanotubes, which is potential nucleation sites for Ag nuclei, become nucleation and growth sites for AgNPs. Thus, Ag nanoparticles can be connected with each other by electrostatic interactions and transform into agglomerates with increasing ED processing time46,47. In fact, an Ag-based surface can be obtained by depositing more particles on the surface by covering the nanotube morphology completely by electro-deposition at much higher times. However, in order not to affect the nanotube morphology too much and not to exceed the cytotoxic limit, the nanoparticles were randomly deposited on the nanotube surfaces, especially at low times.
Elemental analysis of the surfaces
EDX-Mapping and EDX-area analysis were carried out to investigate the distributions and amounts of elements on the bare nanotube and AgNPs-deposited nanotube surfaces. EDX-Mapping analyzes of AgNPs-deposited nanotube surfaces produced on the cp-Ti surface are given in Fig. 2. In addition, the amounts of Ag elements observed on nanotube surfaces are given in the Table 1. As seen in Table 1, the amount of Ag structure increases since the more AgNPs deposits onto nanotube surface with increasing ED time. Due to the presence of the base TiO2 nanotube structure, Ti and O elements were detected in EDX analysis. However, in addition to TiO2 phase, the phase of Ti6O exists on the surface as seen in Fig. 3. Thus, Ti:O ratio is not 1:2 as shown in Table 1. Furthermore, the existence of Ag element was proved as observed as bright nanoparticles on SEM images. In the ED process, AgNPs accumulate randomly on the nanotube surfaces depending on the voltage and time. And, the deposition time values are kept as low as possible in order not to disturb the morphology of the surface and not to exceed the cytotoxic limit. The elemental values for the AgNPs structure were observed below the cytotoxic limit during ED process as reported in the literature48,49.
Phase structures of the surfaces
In order to observe possible Ag structure that may form on nanotube surface; AgNPs-deposited nanotubes produced at 5 min with the highest time was analyzed as seen in Fig. 3. The TiO2 (JCPDS card number: 96-152-6932), anatase-TiO2 (JCPDS card number: 96-720-6076) and Ti6O (JCPDS card number: 96-152-9956) phases were detected on AgNPs-deposited on nanotube surfaces. TiO2 nanotubes are usually exist amorphous form on Ti surfaces at room temperature. Amorphous TiO2 nanotubes are transformed into crystalline anatase or mixed crystalline anatase/rutile phases through annealing at various temperatures50. Amorphous/crystalline anatase phase transition begins to appear at 280 °C as reported in the literature51. Thus, at post-fabrication AO process, the heat treatment is applied on the nanotube surfaces for 60 min at 450 °C as described in experimental section. Thus, these oxide structures in the nanotube structures are transformed from amorphous to crystalline form without any morphological difference under low temperature conditions with by a diffusion mechanism. In our previous works40,52, the anodic oxidation mechanisms under the existence of fluoride ions were discussed in detail. The AO process is the electrolysis of water at the first reaction. Subsequently, a compact TiO2 layer is formed by dissolving of F-ions on bare Gr2 at the second reaction. Eventually, the pits which occur at the third reaction transform into nanotube structures at the suitable voltage and time through AO process. Although Ag structure was observed by EDX-mapping and EDX-area analysis, it could not be detected by XRD. This could be related that the amount of the deposited Ag structures on nanotube surfaces was kept at very low levels for XRD detection limits.
Topography of the surfaces
Average surface roughness (Sa) values of the surfaces were given in Table 2. The average roughness values of AgNPs-deposited nanotube surfaces produced on nanotube surfaces vary between approximately 154.5–269.1 nm while bare Gr2 and bare nanotube surfaces are measured as 10.7 nm and 53.2 nm, respectively. The lowest roughness values were measured on bare Gr2 cp-Ti metal surfaces as expected. The roughness of nanotube surface produced at 50 V improves compared to bare Gr surface owing to the presence of nanotubular morphology. The surface roughness of the nanotube coating usually increases with voltage and time compared to bare substrates. Moreover, an extra contribution of AgNPs on nanotube surfaces increases the surface roughness.
Surface wettability
The hydrophilic/hydrophobic properties of bare Gr2, bare nanotube and AgNPs-deposited nanotube surfaces by the contact angle goniometer (see in Fig. 4). The surfaces with low contact angles show hydrophilic character while the surfaces with high contact angle refer to hydrophobic behavior. The hydrophilic or hydrophobic properties of the surface vary from many parameters such as the surface energy, roughness, porosity and surface charges. The average contact angles of bare Gr2 and bare nanotube surfaces were measured 79.2° ± 0.2 and 140.2° ± 0.2, respectively. Thus, the bare Gr2 surface indicates low wetting angle value respect to the nanotube surface. The nanotube surfaces usually indicate hydrophilic/super hydrophilic behaviors as reported in the literature. The possible reason is anatase causes hydrophilic properties to be generated or another possibility can be the enlarged gap between nanotubes offering more space for liquid penetration53. This refers to the classical Wenzel model54. Wenzel model assumes that a water droplet fills up a rough surface. And, a fully wetted occurs, which depends on the roughness factor and the surface free energy. In other words, the Wenzel model suggests a classical situation of a water droplet on a ‘flat’ surface by roughness parameters. Thus, a hydrophilic/super-hydrophilic surface is created as a material with high surface energy combines with micro- and nanoscale roughness. However, just like in this work, Yang et al. observed the increase of contact angles from 77° to 141° under atmospheric air conditions at post-annealing of TiO2 nanotubes55. This wetting behavior can be ascribed to the replacement of the chemisorbed OH- groups with O2 gaseous56 and the adsorption of organic contaminants on the TiO2 nanotube layer in atmospheric air conditions55. Thus, contact angles of TiO2 nanotubes are greater than one of bare Gr2 surface and previous works55,57,58. This behavior can be attributed to the well-ordered nanotube structure and the greater surface area. This result also refers to the Cassie-Baxter situation. The Cassie-Baxter situation states that the liquid forms a contact line with the air trapped below the contact line on the rough surface. Moreover, TiO2 surfaces are often partially hydroxylated and therefore have a polar structure. This resulted in the measurement of relatively low contact angles59. However, there is an exception for TiO2 nanotube arrays as given in results. The droplet is initially contacted on the protective passive TiO2 oxide layer on bare Gr2 surface. This layer exists naturally on bare Gr2 surface and the surface exhibits hydrophilic character due to its partially hydroxylated polar structure. However, after the droplet contacts on bare TiO2 nanotube surface, the atmospheric gases inside the tubes create resistance for a short time and prevent wettability of the surface. Eventually, this results in higher contact angles. Thus, TiO2 nanotube arrays indicate hydrophobic behavior compared to bare Gr2 surfaces.
In addition, the average contact angle values of AgNPs-deposited nanotube surfaces for 0.5 min, 1 min and 5 min were obtained as 118.5° ± 0.1, 86.6° ± 0.6 and 73.2° ± 0.5, respectively. The wettability (hydrophilic properties) of AgNPs-deposited nanotube surfaces is improved by increasing ED deposition time. However, except for Gr2-50 V-Ag-5 m, the contact angle values for AgNPs-deposited TiO2 nanotubes produced at low ED treatment times are higher than for bare Ti surface. The hydrophilic/hydrophobic surface affects cell adhesion and spreading. While some studies in the literature indicate that cell proliferation is easy on hydrophilic surfaces, some studies have shown that cell adhesion is better on hydrophobic surfaces60,61. However, the number and amounts of AgNPs on TiO2 nanotube layer increase with increasing ED deposition time as seen in Fig. 1. Thus, the number of defective sites increases with increasing AgNPs content for 5 min and this led to the improvement of hydrophilicity62. It could be stated that the deposition of AgNPs on TiO2 nanotube layer improves hydrophilic properties and wettability.
Electrochemical corrosion resistance of the surfaces
The OCP and Tafel extrapolation test results (such as polarization resistance (Rp), corrosion potential (Ecor) and corrosion current density (icor)) of and bare Gr2, bare nanotube and AgNPs-deposited nanotube surfaces are given in Table 3. Also, Tafel extrapolation polarization curves were shown in Fig. 5. It is well known that icor values are inversely proportional to the corrosion rate63. Bare Gr2 surfaces show a higher corrosion current density value and lower corrosion resistance by passivizing at lower potential values compared to bare nanotube and AgNPs-deposited nanotube surfaces. In general, the corrosion resistance depends on the characteristic properties of the surfaces such as the phase structure, elemental amount, surface morphology and wettability.
The passive oxide layer naturally formed on the bare Gr2 surface causes passivation behavior. TiO2 nanotube layer is a ceramic-based structure. The low electrical conductivity of TiO2 nanotube layer reduces charge transport and improves the electrochemical barrier properties compared to bare Gr2. The existence of oxide-based shielding coating can decrease the accessibility of the SBF solution to the bare Gr2 surface64. In addition, surface wettability is an important factor for corrosion resistance. A hydrophobic surface can effectively prevent the corrosive medium from permeating into the interface between the passivation coatings and the substrate. Thus, hydrophobicity inhibits corrosion process65. Predominantly; protective oxide nanotube layer in the AgNPs-deposited nanotube structures creates a barrier between the substrate metal and the atmosphere. This leads to reduce ion release and to increase corrosion resistance. Therefore, AgNPs-deposited nanotube surfaces show lower corrosion current density than the bare Gr2 metal. However, with the increase of the deposition time for the AgNPs structure, the corrosion current density gradually increased. AgNPs can be dissolved under SBF conditions and ionized to the SBF. The dissolution of AgNPs on nanotubes may be increased under SBF conditions with increasing ED time. And, this resulted in decreasing the corrosion resistance with increasing of deposition time whereas AgNPs-deposited nanotube surfaces indicated great corrosion resistance compared to bare Gr2 surface. This may be originated in ionization and dissolution of Ag structure under SBF with increasing ED time. The decrease in corrosion resistance could be due to rapid dissolution along under SBF conditions with agglomeration of Ag structure deposited on the nanotube surface with increasing deposition time. Thus, corrosion resistance of Gr2-50 V-Ag-0.5 min is greater than one of 1 min and 5 min.
Cell viability (cytotoxicity) of the surfaces
The osseointegration of an implant is closely related with the interfacial response of cells contacted to the implant surface. The longevity of an implant preliminary is decided by the interaction and response between cells and biomaterial surface. Inadequately adherent cells inhibit tissue repair and regeneration, resulting in implant failure6,66. The changes in the viability of lymphoblastoid cells that adhere to AgNPs-deposited nanotube surfaces are given in Fig. 6. All AgNPs-deposited nanotube surfaces showed a decrease in cell viability compared to the negative control. Compared to bare Gr2 surface, cell viability varies depending on the amount of AgNPs on nanotube surface. Among AgNPs nanotube surfaces, the cell viability is the most for Gr2-50 V-Ag-1 m. Cell viability determined on Gr2-50 V-Ag-0.5 m and Gr2-50 V-Ag-1 m surfaces was found to be at the same level as negative control values. This shows that the modifications applied to Gr2-50 V-Ag-0.5 m and Gr2-50 V-Ag-1 m surfaces increase cell viability compared to bare Gr2 surfaces. Briefly, except for Gr2-50 V-Ag-5 m, the cell viability of AgNPs-deposited nanotube surfaces was higher than bare Gr2 surface and they indicate non-toxic character. Unlike other Ag coated surfaces, cell viability decreased on Gr2-50 V-Ag-5 m surfaces. While the Gr2-50 V-Ag-5 m surface did not cause any change in cell viability compared to the bare Gr2 surface (p > 0.05), it caused a decrease compared to the negative control (p < 0.05). This indicates that low levels of AgNPs-deposited nanotube surfaces stimulate cell viability and cause a decrease in viability as Ag density increases on the surface. Similarly, Fiedler et al. reported that the proliferation of osteoblastic cells increased on the surface of titanium alloys coated with Ag ion implantation and high-level Ag implantation on the surface reduced the cell proliferation67.
Alkaline phosphatase activity of the surfaces
ALP activities of cells adhering to bare Gr2 and AgNPs-deposited nanotube surfaces are given in Fig. 7. The ALP activity on all AgNPs-deposited nanotube surfaces was decreased compared to the negative control. However, an increase in ALP level on all AgNPs-deposited nanotube surfaces was observed compared to bare Gr2 surfaces. The highest ALP activity was obtained with Gr2-50 V-Ag-5 m, and similar levels of ALP activity were detected on Gr2-50 V-Ag-0.5 m and Gr2-50 V-Ag-1 m coatings.
When ALP activity and cell viability are evaluated together, cell viabilities and ALP levels increased on Gr2-50 V-Ag-0.5 m and Gr2-50 V-Ag-1 m surfaces. But on the Gr2-50 V-Ag-5 m surface, cell viability decreased, while ALP activity increased. Although ALP indicates the presence of osteoblast cells and new bone formation, it is present in many cells. ALP activity in a cell is related to cell viability and may vary with the conditions to which the cell is exposed. In other words, the cell can increase enzyme activity as an adaptation/tolerance mechanism against external factors that reduce its viability. For example, stopping the cell cycle in the G0/G1 phase causes an increase in ALP activity. In other words, cells can increase ALP activity against inhibition of cell proliferation. It is well known that Ag is more toxic compared to other antibacterial elements such as Cu and Zn. The surface of AgNPs attached to nanotubes is cytotoxic at an increased concentration of Ag due to the releasing of high content of Ag+ ions68. However, Ag has more advantage over a broad spectrum of bacteria respect to other antibacterial agents such as Cu and Zn. Sedelnikova et al. reported that cytotoxic effect occurred and ALP activity decreased in fibroblast cells adhering to Zn-, Cu- and Ag-stored titanium surfaces69.
Blood proteins adsorption of the surfaces
The results of protein adsorption on bare Gr2 and AgNPs-deposited nanotube surfaces are given in Table 4. For AgNPs-deposited nanotube surfaces, the highest protein adsorption was obtained at fibrinogen while the lowest adsorption was observed at globulin. The protein adsorption on AgNPs-deposited nanotube surfaces was lower than on bare Gr2 surfaces. In other words, deposition of Ag caused a reduction in the adhesion of blood proteins. The lowest protein adhesion was detected in Gr2-50 V-Ag-5 m. Albumin, globulin and fibrinogen adhesion decreased 36.1%, 34.7% and 25%, respectively, in Gr2-50 V-Ag-5 m compared to bare Gr2 surfaces. Surfaces that are resistant to blood protein adsorption are quite successful in terms of hemocompatibility. Protein adsorption to the surface can be controlled by modifications in the surface properties. Therefore, it is crucial to control an implant's surface chemistry, especially its composition, in order to produce a specific surface with a well-defined biological reaction70. Undesirable reactions (such as coagulation) will occur after the adhesion of blood proteins when the surface comes into contact with blood. Therefore, decreased adhesion of blood proteins increases blood compatibility. Adhesion of extracellular proteins involved in cell–cell adhesion is tested for cells to settle on the surface and proliferate on the surface.
Antimicrobial activity of the surfaces
Inhibition percentages of AgNPs-deposited nanotube surfaces for different gram-positive and gram-negative bacteria are given in Fig. 8. The Ag deposition on nanotube surfaces lead to decrease in the level of bacteria colonies. For all bacteria types, the number of active colonies decreases with increasing AgNPs deposition time. For all AgNPs-deposited nanotube surfaces, the highest antibacterial activity was observed against Gram negative bacteria. Bacterial inhibition was achieved in the range of 68.3–71.7% in Gram-positive bacteria and in the range of 71.6–78.1% in Gram-negative bacteria. The highest bacterial inhibition was obtained on surface of 50 V-Ag-5 m surface against S. typhimurium as seen in Figs. 8 and 9.
The antibacterial mechanism of Ag structure which leads to bacterial death has not been completely clear. Antibacterial activity is not based solely on the release of Ag+ ions from AgNPs71. Although the antibacterial mechanism of AgNPs is still not fully elucidated, several studies have been conducted involving the antibacterial effect of modified TiO2 on Gram-positive/Gram-negative bacteria species72. Initially, AgNPs bind to the bacterial cell wall and leak into it. This leads to cause physical changes and damage the cell wall, resulting in leakage of cell contents. Subsequently, the bacteria are destructed by AgNPs73,74. The antibacterial effects of AgNPs-deposited nanotube surfaces can be explained by the toxic effect of Ag on bacterial cells. The Ag interacts with thiol groups of bacterial macromolecules, inhibiting enzymes and stopping respiratory reactions75. Electrostatic interactions between the positively charged Ag and the negatively charged membrane in contact of Ag-coated surfaces with bacteria cause physical damage to the bacterial membrane and further cidal effects. The denaturation of protein molecules, loss of function and inhibition of DNA synthesis occur when Ag enters into the bacterial cell76,77. As a cumulative result of all these effects on the bacterial cell, the cell cycle is disrupted and proliferation is reduced. Eventually, a decrease in colony formation occurs. It is well known that the Ag has a bacteriostatic/cidal effect by inhibiting phosphate uptake in E. coli and stopping the release of molecules such as phosphate, mannitol, succinate, proline and glutamate. In S. aureus, it has been reported that Ag prevents bacterial growth by damaging the bonds, glycan chains and amino acids in the peptidoglycan structure78,79. One of the important results obtained in this study is that AgNPs-deposited nanotube surfaces show stronger antibacterial effect against Gram negative bacteria. This selectivity in antibacterial activity can be explained by the differences in cell structure of Gram-positive and Gram-negative bacteria. This result is also supported by similar studies in the literature. Durdu et al. reported that there was a 67.2% decrease in the viability of E. coli and a 57.8% decrease in the viability of S. aureus and, Ag was more effective in Gram-negative bacteria80. Feng et al. reported that E. coli is more sensitive to Ag toxicity than S. aureus. This result is related to the defense system and cell structure of S. aureus77.
Conclusion
The randomly distributed AgNPs-deposited TiO2 nanotube surfaces were fabricated on titanium by AO and ED processes. The wettability test confirms that AgNPs-deposited nanotube surfaces are hydrophilic compared to bare Gr2 surface. Moreover, the AgNPs-deposited nanotube surfaces, which prevent the leaching of metallic Ti ions from the implant surface, indicated greater corrosion resistance compared to bare Gr2 surface under SBF conditions. Except for Gr2-50 V-Ag-5 m, the cell viability of AgNPs-deposited nanotube surfaces was improved to bare Gr2 surface and it can be stated that they are non-toxic. Importantly, the AgNPs-deposited nanotube surfaces exhibited antibacterial activity for Gram-positive and Gram-negative bacteria. Eventually, it can be concluded that the AgNPs-deposited nanotube surfaces possess high stability for long-term usage of implant applications.
Data availability
The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.
References
Hou, X., Aitola, K. & Lund, P. D. TiO2 nanotubes for dye-sensitized solar cells—A review. Energy Sci. Eng. 9, 921–937 (2021).
Arifin, K., Yunus, R. M., Minggu, L. J. & Kassim, M. B. Improvement of TiO2 nanotubes for photoelectrochemical water splitting: Review. Int. J. Hydrogen Energy 46, 4998–5024 (2021).
Bindra, P. & Hazra, A. Selective detection of organic vapors using TiO2 nanotubes based single sensor at room temperature. Sens. Actuators B Chem. 290, 684–690 (2019).
Wu, B., Tang, Y., Wang, K., Zhou, X. & Xiang, L. Nanostructured titanium implant surface facilitating osseointegration from protein adsorption to osteogenesis: The example of TiO2 NTAs. Int. J. Nanomed. 17, 1865–1879 (2022).
Vadlamani, B. S., Uppal, T., Verma, S. C. & Misra, M. Functionalized TiO2 nanotube-based electrochemical biosensor for rapid detection of SARS-CoV-2. Sensors 20, 5871 (2020).
Perumal, A., Kannan, S. & Nallaiyan, R. Silver nanoparticles incorporated polyaniline on TiO2 nanotube arrays: A nanocomposite platform to enhance the biocompatibility and antibiofilm. Surfaces Interfaces 22, 100892 (2021).
Gunputh, U. F., Le, H., Handy, R. D. & Tredwin, C. Anodised TiO2 nanotubes as a scaffold for antibacterial silver nanoparticles on titanium implants. Mater. Sci. Eng., C 91, 638–644 (2018).
Liu, W. et al. Optimizing stem cell functions and antibacterial properties of TiO2 nanotubes incorporated with ZnO nanoparticles: Experiments and modeling. Int. J. Nanomed. 10, 1997–2019 (2015).
Brammer, K. S., Frandsen, C. J. & Jin, S. TiO2 nanotubes for bone regeneration. Trends Biotechnol. 30, 315–322 (2012).
Zhang, H. Z. et al. Improved antibacterial activity and biocompatibility on vancomycin-loaded TiO2 nanotubes: In vivo and in vitro studies. Int. J. Nanomed. 8, 4 (2013).
Luan, Y. et al. Bacterial interactions with nanostructured surfaces. Curr. Opin. Colloid Interface Sci. 38, 170–189 (2018).
Ren, X., van der Mei, H. C., Ren, Y., Busscher, H. J. & Peterson, B. W. Antimicrobial loading of nanotubular titanium surfaces favoring surface coverage by mammalian cells over bacterial colonization. Mater. Sci. Eng. C 123, 112021 (2021).
Cao, Y. et al. Nanostructured titanium surfaces exhibit recalcitrance towards Staphylococcus epidermidis biofilm formation. Sci. Rep. https://doi.org/10.1038/s41598-018-19484-x (2018).
Massa, M. A. et al. Synthesis of new antibacterial composite coating for titanium based on highly ordered nanoporous silica and silver nanoparticles. Mater. Sci. Eng. C 45, 146–153 (2014).
Skóra, B. et al. Noncytotoxic silver nanoparticles as a new antimicrobial strategy. Sci. Rep. 11, 13451 (2021).
Kvítek, L. et al. Effect of surfactants and polymers on stability and antibacterial activity of silver nanoparticles (NPs). J. Phys. Chem. C 112, 5825–5834 (2008).
Anees Ahmad, S. et al. Bactericidal activity of silver nanoparticles: A mechanistic review. Mater. Sci. Energy Technol. 3, 756–769 (2020).
Haugen, H. J., Makhtari, S., Ahmadi, S. & Hussain, B. The antibacterial and cytotoxic effects of silver nanoparticles coated titanium implants: A narrative review. Materials. 15(14), 5025 (2022).
Hasani, S., Arvand, M. & Farahmand Habibi, M. Efficient, “on–off” photoelectrochemical sensing platform with layer-by-layer assembly of titanium dioxide nanotube arrays and silver@zinc sulfide nanoparticles for unbiased and accurate monitoring of clonazepam. Microchem. J. 185, 108253 (2023).
Song, X. et al. Solar light-responsive Ag/CdS/TNTs (TiO2 nanotubes) photocatalysts for enhanced CO2 photoreduction and hydrogen evolution. Inorg. Chem. Commun. 146, 110228 (2022).
Butmee, P., Samphao, A. & Tumcharern, G. Reduced graphene oxide on silver nanoparticle layers-decorated titanium dioxide nanotube arrays as SERS-based sensor for glyphosate direct detection in environmental water and soil. J. Hazard. Mater. 437, 129344 (2022).
Jafari, M. et al. A TiO2 nanotube array decorated by Ag nanoparticles for highly sensitive SERS determination and self-cleaning of vitamin B12. Microchem. J. 181, 107813 (2022).
Lei, L., Sang, L. & Gao, Y. Pulse electrodeposition of Ag, Cu nanoparticles on TiO2 nanoring/nanotube arrays for enhanced photoelectrochemical water splitting. Adv. Powder Technol. 33, 103511 (2022).
Momeni, M. M. & Zeinali, P. Photochemical deposition of Ag, Cu, Cu@Ag, and Ag@Cu on TiO2 nanotubes and their optical properties and photoelectrochemical activity. J. Electron. Mater. 50, 5810–5818 (2021).
Wang, Z., Sun, Y., Wang, D., Liu, H. & Boughton, R. I. In situ fabrication of silver nanoparticle-filled hydrogen titanate nanotube layer on metallic titanium surface for bacteriostatic and biocompatible implantation. Int. J. Nanomed. 8, 2903–2916 (2013).
Uhm, S.-H. et al. Tailoring of antibacterial Ag nanostructures on TiO2 nanotube layers by magnetron sputtering. J. Biomed. Mater. Res. B Appl. Biomater. 102, 592–603 (2014).
Li, M. et al. Polydopamine-induced nanocomposite Ag/CaP coatings on the surface of titania nanotubes for antibacterial and osteointegration functions. J. Mater. Chem. B 3, 8796–8805 (2015).
Cheng, H. et al. Strontium (Sr) and silver (Ag) loaded nanotubular structures with combined osteoinductive and antimicrobial activities. Acta Biomater. 31, 388–400 (2016).
Gunputh, U. F. et al. Antibacterial properties of silver nanoparticles grown in situ and anchored to titanium dioxide nanotubes on titanium implant against Staphylococcus aureus. Nanotoxicology 14, 97–110 (2020).
Albashari, A. A. et al. Titanium nanotube modified with silver cross-linked basic fibroblast growth factor improves osteoblastic activities of dental pulp stem cells and antibacterial effect. Front. Cell Dev. Biol. 9, 654654 (2021).
Zhao, L. et al. Antibacterial nano-structured titania coating incorporated with silver nanoparticles. Biomaterials 32, 5706–5716 (2011).
Chen, D. et al. Covalent incorporation of Ag nanoparticles into TiO2 nanotubes on Ti6Al4V by molecular grafting for enhancing antibacterial effect. Surf. Coat. Technol. 426, 127773 (2021).
Uhm, S.-H. et al. E-beam fabrication of antibacterial silver nanoparticles on diameter-controlled TiO2 nanotubes for bio-implants. Surf. Coat. Technol. 228, S360–S366 (2013).
Wei, L. Y., Wang, H. F., Wang, Z. Q., Yu, M. Y. & Chen, S. G. Preparation and long-term antibacterial activity of TiO2 nanotubes loaded with Ag nanoparticles and Ag ions. RSC Adv. 5, 74347–74352 (2015).
Di, H. et al. Ag nanoparticles incorporated tannic acid/nanoapatite composite coating on Ti implant surfaces for enhancement of antibacterial and antioxidant properties. Surf. Coat. Technol. 399, 126169 (2020).
Bilek, O. et al. Antibacterial activity of AgNPs-TiO2 nanotubes: Influence of different nanoparticle stabilizers. RSC Adv. 10, 44601–44610 (2020).
Sudhisha, V., Saranya, K., Kalaiyarasan, M. & Rajendran, N. Silver nanoparticles doped poly(3, 4-ethylene dioxythiophene) on titania nanotubes for orthopaedic application. Appl. Surf. Sci. 610, 155416 (2023).
Staats, K. et al. Antimicrobial potential and osteoblastic cell growth on electrochemically modified titanium surfaces with nanotubes and selenium or silver incorporation. Sci. Rep. 12, 8298 (2022).
Durdu, S., Cihan, G., Yalcin, E. & Altinkok, A. Characterization and mechanical properties of TiO2 nanotubes formed on titanium by anodic oxidation. Ceram. Int. 47, 10972–10979 (2021).
Durdu, S. et al. Surface characterization of TiO2 nanotube arrays produced on Ti6Al4V alloy by anodic oxidation. Surf. Coat. Technol. 428, 127903 (2021).
Kokubo, T. & Takadama, H. How useful is SBF in predicting in vivo bone bioactivity?. Biomaterials 27, 2907–2915 (2006).
Durdu, S. et al. Characterization and investigation of properties of copper nanoparticle coated TiO2 nanotube surfaces on Ti6Al4V alloy. Mater. Chem. Phys. 292, 126741 (2022).
Isa, N. et al. Anodized TiO2 nanotubes using Ti wire in fluorinated ethylene glycol with air bubbles for removal of methylene blue dye. J. Appl. Electrochem. 52, 173–188 (2022).
Macak, J. M., Tsuchiya, H. & Schmuki, P. High-aspect-ratio TiO2 nanotubes by anodization of titanium. Angewandte Chemie-International Edition 44, 2100–2102 (2005).
Roy, P., Berger, S. & Schmuki, P. TiO2 nanotubes: Synthesis and applications. Angew. Chem. Int. Ed. 50, 2904–2939 (2011).
Nycz, M., Arkusz, K. & Pijanowska, D. G. Influence of the silver nanoparticles (AgNPs) formation conditions onto titanium dioxide (TiO2) nanotubes based electrodes on their impedimetric response. Nanomaterials 9, 1072 (2019).
Liang, Y. Q., Cui, Z. D., Zhu, S. L., Liu, Y. & Yang, X. J. Silver nanoparticles supported on TiO2 nanotubes as active catalysts for ethanol oxidation. J. Catal. 278, 276–287 (2011).
Roy, M., Fielding, G. A., Beyenal, H., Bandyopadhyay, A. & Bose, S. Mechanical, in vitro antimicrobial, and biological properties of plasma-sprayed silver-doped hydroxyapatite coating. ACS Appl. Mater. Interfaces. 4, 1341–1349 (2012).
Fidan, S. et al. Fabrication of oxide layer on zirconium by micro-arc oxidation: Structural and antimicrobial characteristics. Mater. Sci. Eng. C-Mater. Biol. Appl. 71, 565–569 (2017).
Zhang, L. et al. Effect of crystalline phase changes in titania (TiO2) nanotube coatings on platelet adhesion and activation. Mater. Sci. Eng. C 82, 91–101 (2018).
Rambabu, Y., Jaiswal, M. & Roy, S. C. Effect of annealing temperature on the phase transition, structural stability and photo-electrochemical performance of TiO2 multi-leg nanotubes. Catal. Today 278, 255–261 (2016).
Nowruzi, F., Imani, R. & Faghihi, S. Effect of electrochemical oxidation and drug loading on the antibacterial properties and cell biocompatibility of titanium substrates. Sci. Rep. 12, 8595 (2022).
Liu, G., Du, K. & Wang, K. Surface wettability of TiO2 nanotube arrays prepared by electrochemical anodization. Appl. Surf. Sci. 388, 313–320 (2016).
Wenzel, R. N. Resistance of solid surfaces to wetting by water. Ind. Eng. Chem. 28, 988–994 (1936).
Yang, L. et al. Effect of annealing temperature on wettability of TiO2 nanotube array films. Nanoscale Res. Lett. 9, 621 (2014).
Wang, R. et al. Photogeneration of highly amphiphilic TiO2 surfaces. Adv. Mater. 10, 135–138 (1998).
Sarraf, M. et al. Effect of microstructural evolution on wettability and tribological behavior of TiO2 nanotubular arrays coated on Ti-6Al-4V. Ceram. Int. 41, 7952–7962 (2015).
Shin, D. H., Shokuhfar, T., Choi, C. K., Lee, S. H. & Friedrich, C. Wettability changes of TiO2 nanotube surfaces. Nanotechnology 22(31), 315704 (2011).
Balaur, E., Macak, J. M., Tsuchiya, H. & Schmuki, P. Wetting behaviour of layers of TiO2 nanotubes with different diameters. J. Mater. Chem. 15, 4488–4491 (2005).
Faucheux, N., Schweiss, R., Lutzow, K., Werner, C. & Groth, T. Self-assembled monolayers with different terminating groups as model substrates for cell adhesion studies. Biomaterials 25, 2721–2730 (2004).
Ikada, Y. Surface modification of polymers for medical applications. Biomaterials 15, 725–736 (1994).
Meng, F. & Sun, Z. A mechanism for enhanced hydrophilicity of silver nanoparticles modified TiO2 thin films deposited by RF magnetron sputtering. Appl. Surf. Sci. 255, 6715–6720 (2009).
Acar, M. T., Kovacı, H. & Çelik, A. Comparison of the structural properties, surface wettability and corrosion resistance of TiO2 nanotubes fabricated on Cp-Ti, Ti6Al4V and Ti45Nb. Mater. Today Commun. 33, 104396 (2022).
Yetim, T. Corrosion behavior of Ag-doped TiO2 coatings on commercially pure titanium in simulated body fluid solution. J. Bionic Eng. 13, 397–405 (2016).
Cao, Z. F. et al. Super-hydrophobic coating used in corrosion protection of metal material: review, discussion and prospects. Metallurgical Res. Technol. 114(2), 203 (2017).
Baxter, L. C., Frauchiger, V., Textor, M., ap Gwynn, I. & Richards, R. G. Fibroblast and osteoblast adhesion and morphology on calcium phosphate surfaces. Eur. Cell Mater. 4, 1–17 (2002).
Fiedler, J. et al. Copper and silver ion implantation of aluminium oxide-blasted titanium surfaces: Proliferative response of osteoblasts and antibacterial effects. Int. J. Artif. Organs 34, 882–888 (2011).
Awad, N. K., Edwards, S. L. & Morsi, Y. S. A review of TiO2 NTs on Ti metal: Electrochemical synthesis, functionalization and potential use as bone implants. Mater. Sci. Eng. C 76, 1401–1412 (2017).
Sedelnikova, M. B. et al. Zn-, Cu- or Ag-incorporated micro-arc coatings on titanium alloys: Properties and behavior in synthetic biological media. Surf. Coat. Technol. 369, 52–68 (2019).
Yang, P. et al. Activation of platelets adhered on amorphous hydrogenated carbon (a-C:H) films synthesized by plasma immersion ion implantation-deposition (PIII-D). Biomaterials 24, 2821–2829 (2003).
Durán, N. et al. Silver nanoparticles: A new view on mechanistic aspects on antimicrobial activity. Nanomed. Nanotechnol. Biol. Med. 12, 789–799 (2016).
Barkema, H. W., Green, M. J., Bradley, A. J. & Zadoks, R. N. Invited review: The role of contagious disease in udder health. J. Dairy Sci. 92, 4717–4729 (2009).
Coman, A. N., Mare, A., Tanase, C., Bud, E. & Rusu, A. Silver-deposited nanoparticles on the titanium nanotubes surface as a promising antibacterial material into implants. Metals 11, 92 (2021).
Qing, Y. et al. Potential antibacterial mechanism of silver nanoparticles and the optimization of orthopedic implants by advanced modification technologies. Int. J. Nanomed. 13, 3311–3327 (2018).
Klasen, H. J. A historical review of the use of silver in the treatment of burns. II. Renewed interest for silver. Burns 26, 131–138 (2000).
Sondi, I. & Salopek-Sondi, B. Silver nanoparticles as antimicrobial agent: A case study on E. coli as a model for Gram-negative bacteria. J. Colloid Interface Sci. 275, 177–182 (2004).
Feng, Q. L. et al. A mechanistic study of the antibacterial effect of silver ions on Escherichia coli and Staphylococcus aureus. J. Biomed. Mater. Res. 52, 662–668 (2000).
Rai, M., Yadav, A. & Gade, A. Silver nanoparticles as a new generation of antimicrobials. Biotechnol. Adv. 27, 76–83 (2009).
Yamanaka, M., Hara, K. & Kudo, J. Bactericidal actions of a silver ion solution on Escherichia coli, studied by energy-filtering transmission electron microscopy and proteomic analysis. Appl. Environ. Microbiol. 71, 7589–7593 (2005).
Durdu, S., Aktug, S. L., Korkmaz, K., Yalcin, E. & Aktas, S. Fabrication, characterization and in vitro properties of silver-incorporated TiO2 coatings on titanium by thermal evaporation and micro-arc oxidation. Surf. Coat. Technol. 352, 600–608 (2018).
Acknowledgements
This work was supported between November 2018 and November 2021 by TUBITAK, Turkey (Project Number—118M766).
Author information
Authors and Affiliations
Contributions
S.D.: conceptualization; methodology; data curation; software; visualization; writing-review and editing. E.Y.: conceptualization; methodology; data curation; writing-review and editing. A.A.: methodology. K.C.: conceptualization; data curation; investigation; methodology; writing-review.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Durdu, S., Yalçin, E., Altinkök, A. et al. Characterization and investigation of electrochemical and biological properties of antibacterial silver nanoparticle-deposited TiO2 nanotube array surfaces. Sci Rep 13, 4699 (2023). https://doi.org/10.1038/s41598-023-31937-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-31937-6
- Springer Nature Limited
This article is cited by
-
Surface characterization and antibacterial efficiency of well-ordered TiO2 nanotube surfaces fabricated on titanium foams
Scientific Reports (2024)
-
Surface characterization, electrochemical properties and in vitro biological properties of Zn-deposited TiO2 nanotube surfaces
Scientific Reports (2023)