Abstract
Nowadays, the existence of metal ions in the environment like chromium (VI) is of significant worry because of its high toxicity to many life forms. Therefore, in this study, an inexpensive and eco-friendly nano-adsorbent was produced from the waste of drinking water industry for effective elimination of Cr (VI) from wastewater. The mineralogical and morphological characterization and compositions of the bulk and nano- adsorbents were performed. The adsorption capabilities of nWTRs for Cr(VI) under different experimental conditions of adsorbent dosage, time, Cr (VI) concentration, solution pH, and competitive ions were investigated. The nWTRs adsorbent exhibits very rapid adsorption potential (92%) for Cr (VI) within the first 15 min. Langmuir model showed high predictive capability for describing Cr (VI) sorption equilibrium data. The estimated maximum sorption capacity (qmax) of nWTRs and bWTRs was found to be 40.65 mg g−1 and 2.78 mg g−1 respectively. The sorption kinetics data of Cr (VI) were perfectly fitted to the model of second-order kinetics. High immobilization capability of nWTRs for sorbed Cr (VI) is evident as most of adsorbed Cr (VI) was associated with the residual fraction. The nWTRs efficiency of Cr (VI) removal from wastewater using batch and column techniques were 98.12 and 96.86% respectively. Electrostatic interactions, outer sphere complexation and pore filling are the main mechanisms suggested for binding of Cr(VI) with functional groups of nWTRs. This study demonstrates that the green low-cost nWTRs have the potential to decontaminate industrial wastewater effluents containing Cr (VI).
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
There is a global concern about the discharge of heavy metals into aquatic ecosystems1, because these toxic elements can lead to serious negative effects on ecological functions and human health2. Among the most toxic elements are chromium and its compounds. Chromium compounds are present in the effluents of many industries like tanneries, metallurgical, electroplating, textiles, and chemical industries3,4. Chromium ions present in the aquatic environment in chromium III (Trivalent) and chromium VI (Hexavalent) forms. The Cr(III) is an important nutrient in humans5, whereas hexavalent is 100 times more toxic than trivalent due to its high oxidative potential and ease of penetration via biological membranes6.
The global market for leather is booming, and the industry has a huge negative environmental impact because of the utilization of toxic chromium used in the tanning process, and thus it is considered one of the biggest pollutants worldwide. Approximately 85% of all leathers produced are tanned with chromium-based process technology, due to its low costs, fast processing, color stability and a high degree of thermal resistance7.The tanning process uses chromium salt with collagen components to prevent water from penetrating the pores of the skin and causing rot. In the chromium tanning process, the skin consumes 60 to 80% of chromium applied and the remainder is frequently released into the drainage system, which has major environmental consequences8.
Many techniques are used for chromium (VI) removal from different wastewaters namely adsorption9,10, nanotechnology treatments11,12, membrane filtration13, ion exchange, chemical precipitation, electrochemical, and advanced oxidation processes14. However, the disadvantage of these techniques such as time-consuming, laborious, costs, generation of sludge that causes disposal problems, and the production of a secondary pollutant are limiting their applicability in a real situation15. Therefore, developing of green, inexpensive and efficient methods for elimination of metals and other pollutants, while avoiding adverse effects on treated systems are needed.
Water treatment residual (WTRs) is a generated waste product of drinking water purification industry when Al2 (SO4)3 is used during the coagulation process. Millions of tons of WTRs are generated every year globally which signify an environmental-economical challenging problem. Amorphous Al (OH)3 and SiO2 mainly constitute WTRs with small percentages of other oxides. The application of WTRs as efficient and low-cost adsorbent for the remediation of heavy metals contaminated soil and water have been reported as a potential and attractive remediation route16,17. Because WTRs is not listed as a harmless “waste” in EU regulations18,19, the use of WTRs as a green adsorbent would greatly strength the sustainable remediation and environmental conservation.
Application of nanosized materials in wastewater treatment has gained much attention lately and has resulted in enhanced performance over their bulk counterparts due to their unique physicochemical characteristics such as small sizes (< 100 nm) and high adsorption capacities20,21,22,23,24. Thus, substituting the expensive commercial nanomaterials by low-cost nanostructured adsorbents with competent adsorption performance, derived from industrial waste product exhibits a new concept and encouraging substitute due to its sustainability, abundant, economic, and environmental footprint25. To the best of authors' knowledge, information is very limited on the production of nanostructured sorbent from water industry byproducts for use in removal of Cr (VI) contaminant from industrial effluents. Therefore, the objectives of the present research were to: (1) transform the byproducts of drinking water industry (WTRs) to valuable nanostructured WTRs (nWTRs) for enhanced removal of Cr (VI) from wastewater effluents, (2) determine the operating status of Cr (VI) sorption onto nWTRs through adsorption isotherms and kinetic studies and (3) examine Cr (VI) adsorption mechanisms onto nWTRs.
Materials and methods
Production of nanostructured WTRs (nWTRs)
The WTRs waste was collected from the drinking water treatment plant (Alexandria, Egypt), air dried for a period of 3 weeks at room temperature, then ground and sieved using 2 mm sieve. The obtained product (bulk WTRs; bWTRs) was stored for analyses. Samples of bWTRs were sieved using 51 μm sieve and were ground using Fritsch planetary mono ball mill (Fritsch, Germany) to obtain WTRs nanoparticles (nWTRs) with particles size < 100 nm following the method of Elkhatib et al.26.
Characterization
Scanning electron microscopy (SEM) with energy dispersive X-ray (EDX), transmission electron microscopy (TEM) (INCAx-Sight model 6587, Oxford Instruments, UK)27, and Fourier transform infrared spectroscopy (FTIR) were used to assay the properties, element compositions, and functional groups of nWTRs before and after loading with Cr (VI).
Sorption kinetics
Sorption kinetic studies were conducted in 50 ml centrifuge tubes containing 100 mg/10 ml of nWTRs and Cr(VI) with 350 mgl−1 initial concentration. The mixtures were shaken (end-over-end shaker) for various time intervals (5, 30, 60, 240,480, and 1440 min) at three different pH levels (5, 7 and 9). Solution pH was adjusted with hydrochloric acid (HCl) and sodium hydroxide (NaOH) with concentrations of 0.1 mol l−1. The liquors were centrifuged and filtered (0.45 um Millipore filter). Using inductively coupled plasma spectrometry (ICPS), the supernatant was analyzed for Cr(VI), and the obtained data were fitted to five kinetic models.
Sorption isotherms
The Cr(VI) sorption equilibrium studies were determined using two different particle sizes of WTRs (2 mm and less than 100 nm) at different concentrations (0, 5 20, 40.80 and 160 mgl−1) in a background electrolyte of 0.005 M KNO3. Solutions obtained were placed in contact with WTRs materials in 50 ml capped polyethylene tubes. The bulk WTRs—Cr(VI) mixtures were equilibrated on a slowly rotating rack for 1440 min at normal pH (7.2), and then removed for centrifugation (4000 rpm) for 15 min, and the data obtained were fitted into different isotherms models. The solid nWTRs—Cr(VI) mixtures after sorption experiments were recovered and examined for sorbed Cr(VI) utilizing SEM, TEM and FTIR analysis.
To study the impact of nWTRs dosage on the Cr(VI) removal, 20, 50, or 100 mg of nWTRs sample were added to 10 ml portions of Cr (VI) with concentration of 200 mgl−1. Competitive adsorption tests in batch (single and multi- ions systems) were performed using nWTRs and solutions containing equal amounts of As (V), Hg (II), and Cr (VI) (multi-ion system) with different concentrations (0, 5, 20, 40.80 and 160 mgl−1) in background electrolyte (0.005 M KNO3). The suspensions were equilibrated for 1440 min.
Results and discussion
Characteristics and chemical composition of nWTRs
SEM and EDX are powerful tools for examining the structure of surface morphology and the elemental features of the sorbents28. The particles morphology and elemental contents of nWTRs and Cr(VI) loaded nWTRs are shown in Fig. 1. The SEM image of the nWTRs sample (Fig. 1A) revealed that the nanoparticles were spherical, with particle sizes < 100 nm in diameter. EDX elemental analysis (Fig. 1C) exhibited the major elements of nWTRs (iron, silicon, calcium, and aluminum) with small amounts of potassium, sulfur, titanium, and manganese. The SEM image of Cr(VI) loaded nWTRs (Fig. 1B) revealed a coating layer of Cr(VI) adsorbed on the nWTRs surface, indicating that the reaction occurred on the nWTRs surface. According to the EDX analysis (Fig. 1D), a Cr (VI) peak (11.80%) is noticed among the elements detected in Cr(VI)-loaded nWTRs.
The TEM image of the nWTRs and Cr(VI) loaded nWTRs (Fig. 1E,F) revealed that the nWTRs are somewhat agglomerated with particle sizes ranging from 18.1 to 76.1 nm.
BET specific surface area (SSA) analysis of bulk and nano particles of WTRs are 53.1 and 129 m2g−1, respectively. It is clear that SSA of nWTRs is 2–3 times higher than that of bWTRs which makes it ideal candidate for use in water treatment.
Surface functional groups of nanoscale WTRs
The sorbents characterization by Fourier transmission infrared (FTIR) spectra reveals the functional group in the sorbent's structure29 which is crucial for understanding mechanisms of metals removal by the solid surfaces. FTIR spectroscopy results of nWTRs and Cr(VI) loaded nWTRs are presented in Fig. 2A. The bands detected at 3619 cm−1, 3417 cm−1 and 1636 cm−1 in the FTIR spectrum of nWTRs (Fig. 2A lower) are assigned to dangling O–H bonds, the HO–H stretching and bending vibrations respectively22,30. Additionally the observed bands at 1449 cm−1,1091 cm−1, and 601 cm−1 are assigned to Fe OH bending vibration-modes of feroxyhyte30,31 and bending vibration of Al single bond OH group32,33. After Cr(VI) adsorption, the bands and peaks between 3417 and 4012 cm−1 (referred to the dangling O–H bonds and O–H bending vibration) as well as the peak at 1793 cm−1 completely disappeared. In addition, shifting of the peak at 1626 cm−1 to higher wavenumber (1646 cm−1) and shifting of the peak at 1091 cm−1 referred to O–Al–O bending vibration was shifted to lower wave number(1016 cm−1) were observed. Disappearance and shifting of peaks and bands suggest molecular interaction and adsorption of Cr(VI) on nWTRs through functional groups34. The FTIR results apparently indicate that presence of O–H and O–Al–O functional groups play significant role in Cr(VI) adsorption on nWTRs adsorbent.
FTIR spectrum analysis of nWTRs before and after Cr(VI) adsorption (A), and Fractionation of adsorbed Cr (VI) on different particle sizes of WTRs Notice that Cr (VI) adsorbed on nWTRs was mostly associated with the less mobile fraction (residual fraction, RS), which indicates the high capability of nWTRs to immobilize Cr (VI) (B).
Fractionation of the Cr(VI)-loaded nWTRs and Cr(VI) mobility
To assess the potential Cr(VI) mobility sorbed onto nWTRs compared to that sorbed onto μWTRs and bWTRs, the distribution of Cr(VI) in the fractions of the sorbents studied was performed using the widely employed sequential extractions(fractionation) scheme35,36. According to this scheme, the unstable Cr (VI) in the non-residual fraction is more mobile than the Cr(VI) in the residual (RS) fraction. Thus, correlating Cr(VI) data with sorbent fractions would determine the mobility of Cr(VI) bound to various sorbent fractions. Figure 2B. Clearly exhibits that Cr(VI) adsorbed by bWTRs was mostly correlated with the more mobile Non-RS fraction (61.67%) while 83.64% of Cr(VI) on nWTRs was related to the less mobile fraction (RS). These variations are referred to the larger surface area and higher adsorption capacity of nWTRs.
Adsorption equilibrium study
Adsorption isotherm models are extremely useful in determining adsorption capacity of the sorbents and in selecting the most suitable sorbent under optimal experimental conditions37,38. The experimental adsorption equilibrium data of the present study were analyzed using six adsorption isotherm models (Table 1). The determination coefficient (R2) and the standard error of estimate (SE) values presented in (Table 1) are indicators of how well the model fits the data. The highest R2 value and the lowest SE value of Langmuir model (Table 1) signalize the best fit of the model to Cr(VI) adsorption data. The Lowest SE values of 0.00062 and 0.000014 (Table 1 and Fig. 4A) of Cr(VI) adsorption onto bWTRs and nWTRs sorbents respectively affirmed that Cr(VI) adsorption onto the studied sorbents fitted best to Langmuir model. The calculated maximum sorption capacity (qmax) of nWTRs and bWTRs were found to be 40.65 mg and 2.78 mg Cr (VI) g−1 respectively. The calculated qmax value of nWTRs was 15 times higher than that of bWTRs.
Effect of the varying different parameters on Cr (VI) adsorption. Initial Cr (VI) concentration
The influence of initial Cr (VI) concentration at a range of 5 to160 mgl−1 on adsorption capacity of nWTRs is shown in Fig. 3A. The results show that increasing Cr (VI) initial concentration has led to increasing Cr (VI) adsorption onto nWTRs adsorbent. The Cr (VI) adsorbed by nWTRs increased from 999 to 31,974 μgg−1 with increasing Cr (VI) initial concentration from 5 to 160 mgl−1 due to the increased mass transfer driving force which encouraged the adsorbate transport from the solution to the adsorbent surface39 and enhanced the interaction between adsorbent and adsorbate40.
Competitive ions
The competition effects of the amounts of Cr (VI) adsorbed by nWTRs in presence or absence of competing cations such as As and Hg at concentrations equal to Cr (VI) concentration were investigated in single and multi-element systems (Fig. 3A). As shown, the power of nWTRs for removing Cr (VI) was highly affected as a result of As and Hg presence in the solution. For instance, at high Cr (VI) initial concentration, Cr (VI) removal dramatically decreased from 99 to 24% due to competition between Cr and As/Hg cations for available sorption sites of nWTRs (Fig. 3A). Similarly, Jain et al.41 indicated that the adsorption capacity of sunflower plant biomass-based carbons for Cr (VI) was reduced in binary and tertiary multi-element systems because of the progressive interference and competition of cations for binding sites on the adsorbent.
Adsorbent dosage
The effect of nWTRs dose (20–100 mg) on Cr(VI) adsorption was studied. Increasing nWTRs dosage from 20 to 100 mg increased the adsorption efficiency of the adsorbent and the adsorbed amount of Cr(VI) increased from 8000 to 17,200 μgg−1 (Fig. 3B). This is because of the greater surface area and the availability of larger number of adsorption sites for HCrO4− and Cr2O4− ions42. Therefore, the dose of 100 mg (nWTRs) was used in the optimization studies.
Solution pH
The Cr (VI) in solution is mostly found in the forms of H2CrO4, HCrO4−, Cr2O72−, CrO42− depending on Cr(VI initial concentration and pH as shown in Fig. 3E. The pH value of sorbent is a significant parameter for metal adsorption43,44,45. Thus, the impact of pH solution on Cr(VI) removal by nWTRs in the pH range (3–11) was examined. Figure (3C) clearly shows that Cr(VI) adsorption on to nWTRs is reduced significantly with increasing pH until it reaches pH 11. For better understanding of Cr(VI) adsorption mechanisms, the point zero charge (pHzpc) of nWTRs was determined and found to be 7.43 (Fig. 3F). At pH values lower than 7.43 the nWTRs surface is positively charged whereas at higher pH values than7.43, the nWTRs surface is negatively charged46,47. Because in acid solutions Cr (VI) exists mainly as negatively charged anions (HCrO4––Cr2O72–), and nWTRs surface is positively charged, strong electrical interactions between Cr(VI) species and positively charged sites on nWTRs surface are taking place and as a result the adsorption capacity of nWTRs increased (Fig. 3C). Conversely, as the pH of the nWTRs increased above its zero point charge (pH > pHzpc), the number of sites that carried negative charges increased while the number of sites that carried positive charges decreased, resulting in a decrease in the adsorption capacity of nWTRs for Cr (CrO42− is the main ionic species)48,49.The obtained result are in agreement with the previous work reported using various adsorbents for Cr(VI) removal43,50,51,52.
At acidic condition:
At basic condition:
Contact time
The effect of contact time (5 to 1440 min) on Cr (VI) adsorption at pH values (5, 7and 9) was studied. As appeared in Fig. 3D, the Cr(VI) adsorption by nanostructured WTRs was instantaneous. Approximately 92% of Cr(VI) was adsorbed within the first 15 min onto nWTRs adsorbent and reached equilibrium in almost one hour with Cr(VI) adsorption efficiency of ~ 99%. The reduced removal efficiency of nWTRs for Cr(VI) at higher pH values(7 and 9) is evident (Fig. 3D) due to the positively charged nWTRs surfaces under acidic conditions.
Modelling adsorption kinetics
Five models were utilized to model the Cr(VI) adsorption kinetics data by nanoscale WTRs at three pH values (5, 7, and 9)53. The adsorption kinetics models used were evaluated to determine the best fit model that could reproduce the results. Table 2 shows the kinetic models tested and its parameters. Generally, higher R2 values and lower SE values better describe the kinetic model of adsorption process. It can be clearly seen (Table 2) that kinetics data of Cr(VI) adsorption by nanoscale WTRs at pH values (5, 7, and 9) are best described by the second-order model based on the lowest standard errors (SE) values and the highest determination coefficient (R2) of the second-order model (Table 2 and Fig. 4B).
Proposed mechanisms of Cr (VI) removal using nWTRs sorbent
The results of Cr(VI) adsorption studies and FTIR analysis of nWTRs and Cr-loaded nWTRs revealed that O–H, O–Al–O and Fe hydroxide functional groups are the main functional groups that significantly facilitate Cr(VI) reactivity with nWTRs. Consequently, the likely mechanisms of Cr(VI) adsorption onto nWTRs surface are suggested in Fig. 5. The proposed figure exhibits the different interactions involved in the Cr(VI) adsorption process including electrostatic interactions (i), Complexation (ii) Pore filling (iii) and Reduction process (iv):
-
(i)
Electrostatic interaction The negatively charged Cr(VI) species, under acidic condition, were favorably migrated to the positively charged surfaces of nWTRs (Al, Fe oxides and OH atoms) (The OH atoms is protonated under acidic conditions to produce—OH2+)54.
-
(ii)
Complexation The Cr(VI) ions could form inner sphere complexes with Fe/Al oxides of nWTRs with a more pronounced effect in acid conditions55.
-
(iii)
Pore filling Chromium ions possibly trapped in the micropores of nWTRs surface because the pores size of the nWTRs are larger than the radiuses of HCrO4− and Cr2O7 ions56.
-
(iv)
Reduction process At a lower pH, Cr(VI) may be reduced to Cr(III)57, which could then be chelated with Al/Fe oxides on the surface of nWTRs.
The feasibility of nWTRs application for Cr(VI) removal from wastewater
The ability of nWTRs to efficiently remove Cr(VI) from actual wastewater was evaluated using batch and packed-bed column techniques. Samples from wastewater discharged from the food processing plant were collected in polyethylene bottles. The pH, electric conductivity (EC), Cr(VI) concentration, major and minor elements, of the wastewater samples were all measured and are presented in Table S1. All wastewater samples (one Liter) were spiked with 100 mgl−1 Cr(VI) solution. A 100 mg nWTRs was added to each wastewater sample. The mixture was shaken for 120 min, then centrifuged and the supernatant solutions were filtered and analyzed.
Packed-bed column technique
The columns were made of plastic (UV stabilized PVC) with 25 cm length and internal diameter of 1.2 cm. Each column was filled with 600 mg nano- WTRs and sand at a specific ratio (5 g fine sand and 5 g coarse sand). The structure of columns bottom consist of a wool layer and a filter paper to preserve the solid contents of the column. Wastewater effluents spiked with Cr(VI) (100 mgl−1) were infiltrated across the column downward at low flow rate of 2 ml/min. The leachate was obtained at regular time intervals and analyzed. The efficiency of nWTRs using a real chromium contaminated wastewater sample, in batch (shaking) and packed-bed column were 98.12 and 96.86 respectively (Fig. 6).
Comparison of adsorption capacity of nWTRs and other adsorbents for Cr(VI) removal
The maximum adsorption capacity (qmax) of nWTRs for chromium is compared with different adsorbents (Table 3). It can be seen that the nanostructured WTRs outperformed all the listed adsorbents in Cr(VI) removal from aqueous solutions.
Conclusions
A low-cost nano-adsorbent (nWTRs) produced from byproducts of water industry has proven to be highly effective in removing Cr(VI) from contaminated wastewater. The linearized Langmuir model was statistically superior to the other models tested and showed excellent ability to model Cr(VI) adsorption data with good accuracy. The calculated maximum sorption capacity (qmax) of nWTRs (40.65 mgg−1) for Cr(VI) was 15 times higher than qmax of bulk WTRs (2.78 mgg−1). The second-order model best described Cr(VI) sorption kinetics data. FTIR and SEM–EDX spectra analysis suggests that the hydroxyls may act as the surface active sites for Cr(VI) binding to nWTRs surfaces. The efficiency of nWTRs in removing Cr (VI) from wastewater effluents using batch and column techniques were 98.12% and 96.86% respectively. It is, therefore, suggested the use of nWTRs as a powerful and rapid sorbent for elimination of Cr (VI) from industrial wastewater effluents.
Data availability
All data generated or analyzed during this study are included in this published article and its supplementary information files.
References
Mane, P. & Bhosle, A. Bioremoval of some metals by living algae Spirogyra sp. and Spirullina sp. from aqueous solution. Int. J. Environ. Res. 6, 571–576 (2012).
Babu, D. J., Kalyani, G., Rao, H. J., Kumar, Y. P. & King, P. Biosorption characteristics of lead onto bentonite clay, as low-cost natural biosorbent. Int. J. Sci. Eng. 3, 1–6 (2012).
Gupta, V. K., Rastogi, A. & Nayak, A. Adsorption studies on the removal of hexavalent chromium from aqueous solution using a low cost fertilizer industry waste material. J. Colloid Interface Sci. 342, 135–141 (2010).
Wang, W.-Q., Li, M.-Y. & Zeng, Q.-X. Thermodynamics of Cr (VI) adsorption on strong alkaline anion exchange fiber. Trans. Nonferrous Met. Soc. Chi. 22, 2831–2839 (2012).
Dula, T., Siraj, K. & Kitte, S. A. Adsorption of hexavalent chromium from aqueous solution using chemically activated carbon prepared from locally available waste of bamboo (Oxytenanthera abyssinica). ISRN Environ. Chem. 2014, 9 (2014).
ATSDR, S. Toxicological profile for chromium. Agency for toxic substances and disease registry. Public Health Service, US Department of Health and Human Services. http://www.atsdr.cdc.gov/toxprofiles/tp.asp (2012).
Fahim, N. F., Barsoum, B. N., Eid, A. E. & Khalil, M. S. Removal of chromium (III) from tannery wastewater using activated carbon from sugar industrial waste. J. Hazard. Mater. 136, 303–309 (2006).
Kowalski, Z. Treatment of chromic tannery wastes. J. Hazard. Mater. 37, 137–141 (1994).
Liu, H., Zhang, F. & Peng, Z. Adsorption mechanism of Cr(VI) onto GO/PAMAMs composites. Sci. Rep. 9, 3663 (2019).
Zhang, S., Zhang, Y., Fu, L. & Jing, M. A chitosan fiber as green material for removing Cr(VI) ions and Cu(II) ions pollutants. Sci. Rep. 11, 22942 (2021).
Choi, K. et al. Chromium removal from aqueous solution by a PEI-silica nanocomposite. Sci. Rep. 8, 1438 (2018).
Ye, J. et al. Removal of hexavalent chromium from wastewater by Cu/Fe bimetallic nanoparticles. Sci. Rep. 11, 10848 (2021).
Muthumareeswaran, M. R., Alhoshan, M. & Agarwal, G. P. Ultrafiltration membrane for effective removal of chromium ions from potable water. Sci. Rep. 7, 41423 (2017).
Azimi, A., Azari, A., Rezakazemi, M. & Ansarpour, M. Removal of heavy metals from industrial wastewaters: A review. Chem. Bio. Eng. Rev. 4, 37–59 (2017).
Deveci, H. & Kar, Y. Adsorption of hexavalent chromium from aqueous solutions by bio-chars obtained during biomass pyrolysis. J. Ind. Eng. Chem. 19, 190–196 (2013).
Chiang, Y. W. et al. Strategic selection of an optimal sorbent mixture for in-situ remediation of heavy metal contaminated sediments: framework and case study. J. Environ. Manag. 105, 1–11 (2012).
Zhao, Y., Doherty, L. & Doyle, D. Fate of water treatment residual: An entire profile of Ireland regarding beneficial reuse. Int. J. Environ. Stud. 68, 161–170 (2011).
Dassanayake, K. B., Jayasinghe, G. Y., Surapaneni, A. & Hetherington, C. A review on alum sludge reuse with special reference to agricultural applications and future challenges. Waste Manag. 38, 321–335 (2015).
Shen, C. et al. Global profile of heavy metals and semimetals adsorption using drinking water treatment residual. Chem. Eng. J. 372, 1019–1027 (2019).
Elkhatib, E., Moharem, M., Mahdy, A. & Mesalem, M. Sorption, release and forms of mercury in contaminated soils stabilized with water treatment residual nanoparticles. Land Degrad. Dev. 28, 752–761 (2017).
Moharem, M., Elkhatib, E. & Mesalem, M. Remediation of chromium and mercury polluted calcareous soils using nanoparticles: Sorption–desorption kinetics, speciation and fractionation. Environ. Res. 170, 366–373 (2019).
Hamadeen, H. M., Elkhatib, E. A., Badawy, M. E. & Abdelgaleil, S. A. Novel low cost nanoparticles for enhanced removal of chlorpyrifos from wastewater: Sorption kinetics, and mechanistic studies. Arab. J. Chem. 14, 102981 (2021).
Hamadeen, H. M. & Elkhatib, E. A. New nanostructured activated biochar for effective removal of antibiotic ciprofloxacin from wastewater: Adsorption dynamics and mechanisms. Environ. Res. 210, 112929 (2022).
Hamadeen, H. M. & Elkhatib, E. A. Nanostructured modified biochar for effective elimination of chlorpyrifos from wastewater: Enhancement, mechanisms and performance. J. Water Process. Eng. 47, 102703 (2022).
Hamadeen, H. M., Elkhatib, E. A., Badawy, M. E. & Abdelgaleil, S. A. Green low cost nanomaterial produced from Moringa oleifera seed waste for enhanced removal of chlorpyrifos from wastewater: Mechanism and sorption studies. J. Environ. Chem. Eng. 9, 105376 (2021).
Elkhatib, E. A., Mahdy, A. M. & Salama, K. A. Green synthesis of nanoparticles by milling residues of water treatment. Environ. Chem. Lett. 13, 333–339 (2015).
Elkhatib, E., Mahdy, A., Sherif, F. & Hamadeen, H. Evaluation of a novel water treatment residual nanoparticles as a sorbent for arsenic removal. J. Nanomater. 2015, 5 (2015).
Akar, T. & Tunali, S. Biosorption performance of Botrytis cinerea fungal by-products for removal of Cd (II) and Cu (II) ions from aqueous solutions. Miner. Eng. 18, 1099–1109 (2005).
Ngah, W. W. & Hanafiah, M. Biosorption of copper ions from dilute aqueous solutions on base treatedrubber (Hevea brasiliensis) leaves powder: kinetics, isotherm, and biosorption mechanisms. J. Environ. Sci. 20, 1168–1176 (2008).
Gotić, M., Popović, S. & Musić, S. Formation and characterization of δ-FeOOH. Mater. Lett. 21, 289–295 (1994).
Carlson, L. & Schwertmann, U. Natural occurrence of feroxyhite (δ′-FeOOH). Clays Clay Miner. 28, 272–280 (1980).
Del Nero, M., Galindo, C., Barillon, R., Halter, E. & Madé, B. Surface reactivity of α-Al2O3 and mechanisms of phosphate sorption: In situ ATR-FTIR spectroscopy and ζ potential studies. J. Colloid Interface Sci. 342, 437–444 (2010).
Gadekar, M. R. & Ahammed, M. M. Use of water treatment residuals for colour removal from real textile dye wastewater. Appl. Water Sci. 10, 1–8 (2020).
Zhang, Y. U., Yang, M. I. N., Dou, X. M., He, H. & Wang, D. S. Arsenate adsorption on an Fe− Ce bimetal oxide adsorbent: Role of surface properties. Technology 39, 7246–7253 (2005).
Zhang, F., Du, N., Li, H., Liang, X. & Hou, W. Sorption of Cr (VI) on Mg–Al–Fe layered double hydroxides synthesized by a mechanochemical method. RSC Adv. 4, 46823–46830 (2014).
Tessier, A., Campbell, P. G. & Bisson, M. Sequential extraction procedure for the speciation of particulate trace metals. Anal. Chem. 51, 844–851 (1979).
Binupriya, A. R., Sathishkumar, M., Jung, S. H., Song, S. H. & Yun, S. I. A novel method in utilization of bokbunja seed wastes from wineries in liquid-phase sequestration of reactive blue 4. Int. J. Environ. Res. 3, 1–12 (2009).
De Gisi, S., Lofrano, G., Grassi, M. & Notarnicola, M. Characteristics and adsorption capacities of low-cost sorbents for wastewater treatment: A review. Sustain. Mater. Technol. 9, 10–40 (2016).
Saravanane, R., Sundararajan, T. & Reddy, S. S. Efficiency of chemically modified low cost adsorbents for the removal of heavy metals from waste water: A comparative study, Indian. J. Environ. Health 44, 78–87 (2002).
Kaveeshwar, A. R. et al. Pecan shell based activated carbon for removal of iron(II) from fracking wastewater: Adsorption kinetics, isotherm and thermodynamic studies. Process Saf. Environ. 114, 107–122 (2018).
Jain, M., Garg, V. K., Kadirvelu, K. & Sillanpää, M. Adsorption of heavy metals from multi-metal aqueous solution by sunflower plant biomass-based carbons. Int. J. Environ. Sci. Technol. 13, 493–500 (2016).
Bansal, M., Singh, D., Garg, V. K. & Rose, P. Mechanisms of Cr(Vi) removal from synthetic wastewater by low cost adsorbents. J. Environ. Res. Dev. 3, 228–243 (2008).
Vinod, V. T. P., Sashidhar, R. B. & Sukumar, A. A. Competitive adsorption of toxic heavy metal contaminants by gum kondagogu (Cochlospermum gossypium): A natural hydrocolloid. Colloids Surf. B Biointerfaces 75, 490–495 (2010).
Wang, H., Zhang, M. & Lv, Q. Removal efficiency and mechanism of Cr(VI) from aqueous solution by maize straw biochars derived at different pyrolysis temperatures. Water 11, 781215 (2019).
Peng, H. & Guo, J. Removal of chromium from wastewater by membrane fltration, chemical precipitation, ion exchange, adsorption electrocoagulation, electrochemical reduction, electrodialysis, electrodeionization, photocatalysis and nanotechnology: A review. Environ. Chem. Lett. 18, 2055–2068 (2020).
Das, N. & Jana, R. K. Adsorption of some bivalent heavy metal ions from aqueous solutions by manganese nodule leached residues. J. Colloid Interface Sci. 293, 253–262 (2006).
Alsaiari, N. S. et al. Synthesis, characterization and application of polypyrrole functionalized nanocellulose for the removal of Cr(VI) from aqueous solution. Polymers 13, 3691 (2021).
Weng, C.-H., Sharma, Y. C. & Chu, S.-H. Adsorption of Cr(VI) from aqueous solutions by spent activated clay. J. Hazard. Mater. 155, 65–75 (2008).
Dehghani, M. H., Sanaei, D., Ali, I. & Bhatnagar, A. Removal of chromium (VI) from aqueous solution using treated waste newspaper as a low-cost adsorbent: kinetic modeling and isotherm studies. J. Mol. Liq. 215, 671–679 (2016).
Park, D., Yun, Y.-S. & Park, J. M. Use of dead fungal biomass for the detoxification of hexavalent chromium: screening and kinetics. Process Biochem. 40, 2559–2565 (2005).
Tewari, N., Vasudevan, P. & Guha, B. Study on biosorption of Cr (VI) by Mucor hiemalis. Biochem. Eng. J. 23, 185–192 (2005).
Parlayici, Ş & Pehlivan, E. Comparative study of Cr (VI) removal by bio-waste adsorbents: Equilibrium, kinetics, and thermodynamic. J. Anal. Sci. Technol. 10, 15 (2019).
Elkhatib, E. A., Mahdy, A. M. & ElManeah, M. M. Effects of drinking water treatment residuals on nickel retention in soils: A macroscopic and thermodynamic study. J. Soils Sediment. 13, 94–105 (2013).
Li, H. et al. Mechanisms of metal sorption by biochars: Biochar characteristics and modifications. Chemosphere 178, 466–478 (2017).
Hmamou, M., Maarouf, F. E., Ammary, B. & Bellaouchou, A. Surface complexation of chromium(VI) on iron(III) hydroxide: Mechanisms and stability constants of surfaces complexes. Indones. J. Chem. 21, 679–768 (2021).
Ma, H. et al. Removal of chromium (VI) from water by porous carbon derived from corn straw: Influencing factors, regeneration and mechanism. J. Hazard. Mater. 369, 550–560 (2019).
Nameni, M., Moghadam, M. A. & Arami, M. Adsorption of hexavalent chromium from aqueous solutions by wheat bran. Int. J. Environ. Sci. Technol. 5, 161–168 (2008).
Fu, R. et al. Fast and highly efficient removal of chromium (VI) using humus-supported nanoscale zero-valent iron: influencing factors, kinetics and mechanism. Sep. Purif. Technol. 174, 362–371 (2017).
Wang, Y.-N. et al. Removal of Cr(VI) from aqueous solution using Fe-modified activated carbon prepared from luffa sponge: Kinetic, thermodynamic, and isotherm studies. Desalin. Water Treat. 57, 29467–29478 (2016).
Wang, H. et al. Enhanced photoreduction of U(VI) on C3N4 by Cr(VI) and Bisphenol A: ESR, XPS, and EXAFS investigation. Environ. Sci. Technol. 53, 6454–6461 (2019).
Yao, L., Esmaeili, H., Haghani, M. & Roco-Videla, A. Activated Carbon/Bentonite/Fe3O4 as novel nanobiocomposite for high removal of Cr(VI) ions. Chem. Eng. Technol. 44, 1908–1918 (2021).
Liang, M. et al. Removal of aqueous Cr(VI) by magnetic biochar derived from bagasse. Sci. Rep. 10, 21473 (2020).
Abshirini, Y., Esmaeili, H. & Foroutan, R. Enhancement removal of Cr (VI) ion using magnetically modified MgO nanoparticles. Mater. Res. Express. 6, 125513 (2019).
Belchik, S. M. et al. Extracellular reduction of hexavalent chromium by cytochromes MtrC and OmcA of Shewanella oneidensis MR-1. Appl. Environ. Microbiol. 77, 4035–4041 (2011).
Hu, J., Lo, I. M. & Chen, G. Performance and mechanism of chromate (VI) adsorption by δ-FeOOH-coated maghemite (γ-Fe2O3) nanoparticles. Sep. Purif. Technol. 58, 76–82 (2007).
Wang, P. & Lo, I. M. Synthesis of mesoporous magnetic γ-Fe2O3 and its application to Cr (VI) removal from contaminated water. Water Res. 43, 3727–3734 (2009).
Jung, C. et al. Hexavalent chromium removal by various adsorbents: powdered activated carbon, chitosan, and single/multi-walled carbon nanotubes. Sep. Purif. Technol. 106, 63–71 (2013).
Adebayo, G. B., Adegoke, H. I. & Fauzeeyat, S. Adsorption of Cr(VI) ions onto goethite, activated carbon and their composite: kinetic and thermodynamic studies. Appl. Water Sci. 10, 213 (2020).
Pandey, P. K., Sharma, S. K. & Sambi, S. S. Kinetics and equilibrium study of chromium adsorption on ZeoliteNaX. Int. J. Environ. Sci. Technol. 7, 395–404 (2010).
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). The funding was provided by Science and Technology Development Fund (Springer Nature OA agreements for Egypt).
Author information
Authors and Affiliations
Contributions
H.H.: Investigation, Methodology, Analysis, and Writing-original draft. E.E.: Conceptualization, Supervision, Validation, Writing-Reviewing and Editing, and M.L.M., Analysis, data validation, writing and editing.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hamadeen, H.M., Elkhatib, E.A. & Moharem, M.L. Optimization and mechanisms of rapid adsorptive removal of chromium (VI) from wastewater using industrial waste derived nanoparticles. Sci Rep 12, 14174 (2022). https://doi.org/10.1038/s41598-022-18494-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-18494-0
- Springer Nature Limited
This article is cited by
-
Eco-friendly nano-enabled fertilizers derived from date industry waste for sustainable and controlled-release of P, K and Mg nutrients: sorption mechanisms, controlled-release performance and kinetics
Bioresources and Bioprocessing (2024)
-
Novel nano-fertilizers derived from drinking water industry waste for sustained release of macronutrients: performance, kinetics and sorption mechanisms
Scientific Reports (2024)
-
Enhanced Adsorptive Removal of Cr (VI) from Plating Industry Wastewater Using CoFe2O4/CTAB Magnetic Nanocomposites
Korean Journal of Chemical Engineering (2024)
-
A novel nanocomposite-based zeolite for efficient remediation of Cd-contaminated industrial wastewater
Applied Water Science (2024)
-
Potential use of nanoparticles produced from byproducts of drinking water industry in stabilizing arsenic in alkaline-contaminated soils
Environmental Geochemistry and Health (2023)