Abstract
This study investigates the effect of using ethanol as the process control agent during the wet ball milling of niobium (Nb). Dried nanocrystal Nb powders, of high purity, with particle sizes, ranging from 8.5 to 14.3 nm, were synthesized by ball milling. Commercial Nb powder of particle sizes of − 44 µm was employed by using the planetary ball mill equipped with stainless still vials with still balls in ethanol. A ball-to-powder mass ratio of 10:1 was used at a rotation speed of 400 rpm, an interval of 15 min with an interval break of 5 s, and a milling time of 10 h. The powder was dried in vacutec at a temperature of 100 °C, using a speed of 15 rpm in the vacuum of 250 mbar at a time of approximately 653 min. The crystal phase of the dried powders was analyzed using X-ray diffraction (XRD) with CuKɑ radiation, and by modification of the Scherrer equation, a single crystallite size of 11.85 nm was obtained. The morphology of the particles was observed using scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDS). The XRD results show that the pure crystal sizes in nanometre (nm), which decreases as the 2θ and the full width at half maximum (FWHM) increases.
Similar content being viewed by others
Introduction
Niobium is a body-centered cubic (bcc) crystallite structure, an essential micro-alloying metallic element for the pipeline steels, steel for structural applications, excellent alloys for aircraft turbine engines, car body steels with high strength, and it is in the utmost demand in the mechanized countries, which is now accounting to a sale capacity of more than 85,000 tonnes every year1,2,3,4. Niobium has exceptional ductility, a high melting point of 2740 K, oxidation and impact resistance, a density of 8.55 g/cm3, high dielectric dissipation, a small neutron-absorbing cross-sectional area, and a high transition temperature of 9.3 K (i.e. − 264 °C, or − 443 °F), among metals. Therefore, the metal is used widely, in nuclear fusion, nuclear industry, space development, high power transmission, and superconductor4.
The decrease in the particle size and the reduction in agglomeration increase the suspension stability of the alloyed materials5. Powder particle size has to be fine enough to gain a smooth surface finish and satisfactory optimal precision6,7. The reduction in particle size of metallic flakes or powders can be achieved by either dry milling or wet milling techniques. The better amongst the two techniques remain insignificant in small-scale milling, but there exists, the main practical problem when huge scale milling in metallurgical manufacturing, is required. In the wet milling technique, process control agents (lubricant or surfactant) such as: ethanol, stearic acid, methanol, hexane etc., are added to the powder mixture during milling to reduce the effect of cold welding8. The ethanol will function as surface-active agents, and will be absorbed on the surface of the powder particles, and minimize cold welding between niobium powder particles and thus slow down agglomeration. The ethanol would interfere with cold welding of the milling particles and therefore, lowered the surface tension of the powdered material. The wet milling process is the main technique used for commercial production9. In ancient times, solvents, e.g., ethanol has been used during the milling process to make metal flakes10. The solvent is much to offer wet milling of metallic powders to form chips. It has been made reported that the use of ethanol and other carbon- and oxygen-containing solvents for either wet-milling or wet-grinding of metal flakes to form powders can create several problems10. The oxygen present in the wet milling solvents can be released from the solvent due to the ease with which carbon to oxygen bonds are broken down. When oxygen comes in the system from the broken solvent molecules, the oxygen can react or be present with the metal chips being formed or with the stainless steel milling intermediate and cause impurities in the resulting chips10. It is assumed that rupture of carbon–oxygen bonds in the wet milling solvents, can leads to a high stage of carbon and iron contaminations in the chips produced and causes a consequential corrosive environment10. The issue of carbon or oxygen contamination depends mainly on further production methods (e.g., consolidation of the powdered particles) and the area of application of the final product. However, the annealing of the powders before the spark plasma sintering (SPS) powder consolidation techniques, can remove/reduce the oxygen contamination11 and if carbon is the major impurity in Nb, as in the case of this study, the powders produced will be mostly a transition metal carbides of niobium carbide (NbC) powders. NbC is an important material and it is often, added as a hard phase in composite materials12. Transition carbide (NbC) possesses a specific combination of thermal, mechanical and electrical conductivity properties, such as: high melting temperature, high hardness, good high-temperature strength and good electrical conductivity13. These materials are also used as high-temperature structural materials in the form of hard constituents in metal matrix composites13,14,15,16,17,18. NbC can find uses as structural materials that are resistant to high temperatures and corrosive atmospheres, like abrasives, supper conductors and high-performance permanent magnets19. In summary, the usefulness of transition carbide cannot be overemphasized.
XRD is a convenient method for determining the mean size of nanocrystallites in nanocrystallite bulk materials20. Paul Scherrer, one of the 1st scientist to work on X-ray diffraction, had his research results in a published paper that incorporated what turned out to be known as the Scherrer equation as shown in Eq. 1, in 191821, which can be employed in the determination of the crystal size.
where L, represents the average crystallite size, K is 0.9 (the Scherrer constant or shape factor), and it is related to crystal shape. ʎ = 0.15405 nm (the CuKα1 wavelength), β is the full width at half maximum (FWHM), whose value on the 2θ axis of the diffraction profile, must be in radian. θ, the Bragg angle is the value of half the angle between the transmitted and reflected beams, 2θ in degrees or radians; since the cosine values of a number in radians correspond to the same value in degree.
In the work of Monshi et al.20, the Scherrer equation was modified to provide a new approach to the use of the Scherrer equation, so that the least square technique can be applied to minimize the source of error. Their work established the modified Scherrer equation, which was a plot of ℓnβ as a function of ℓn(1/Cosθ) and an intercept is obtained of a least square regression, \(\ln = \frac{K\lambda }{L}\), from which a single value of crystal size, L, was obtained through all of the available peaks20.
On the other hand, the current study examines the use of ethanol as a process control agent, used to mill pure niobium powders to nanoparticle sizes. Also, the crystal sizes and the changes in the microstructures of the ethanol wet-milled niobium were determined. However, it is noteworthy to state the fact that the authors could not find any research work on the use of ethanol to mill pure niobium flakes or powders, hence, this study. Besides, the purpose of doing this research is to increase the surface area of the niobium particles for better performance. A nano-sized particle of niobium has a greater surface area than the same niobium as a micro-size particle. To increase the surface area of the niobium particles is to increase the number of catalytic sites to enhance good adhesions of the particles during reactions.
Experimental
In the current study, the raw material used is pure commercial Nb powder (95.7% pure) with a particle size of ~ 44 µm that was supplied by Alfa Aesar Company. Milling was performed under the condition of a wet ball milling process. For the milling process, 40.12 g of the as-received Nb powder were loaded into two separate hardened steel containers of 125 ml volume with steel balls of 0.4 mm diameter, in a ball-to-powder weight ratio of ~ 10:1.80% volume of the hardened steel containers were filled with 5 ml of absolute ethanol that served as the process-controlling agent. The containers were closed and weighed, to balance their weights and to avoid imbalance in the milling machine. The powder was wet-milled for 10 h at a speed of 400 rpm, at an interval of 15 min, and with an interval break of 5 s. After the wet milling procedure, the powders were recovered through drying in a vacuum oven, at a temperature of 100 °C, a speed of 15 rpm, a time of 653 min, and in vacuum at 250 mbar. The crystal phase of the dried powders was analyzed by using the X-ray diffraction (XRD) analyzer, the EMPYREAN DIFFRACTOMER with CuKɑ radiation and was analyzed by using the Highscore with software. The morphology and the elemental compositions of the dried powders were investigated by using the High-Resolution Field Emission Scanning Electron Microscope (SEM), (JEOL-JSM-7600F), attached with energy dispersive x-ray spectroscopy (EDS) (Fig. 1).
Results and discussion
XRD results
The XRD diffractograph of the milled Nb powder is shown in Fig. 2, consisting of four sharp peaks. The sharpness of the peaks decreased with an increase in 2θ, which indicated a decrease in the crystal size of the powders. Table 1 summarises the Scherrer equation data for the milled powders. In the Table, there is a moderately gradual increase in the values of β · cosθ and 2θ with decreases in the crystal size, L values. Figure 3 shows the graph of the crystal size of the milled powders against the angle between the transmitted beam and the reflected beam, 2θ and Fig. 4 shows the graph of the crystal size, Las a function of FWHM of the peak profile. It was observed that there is a decrease in the crystal sizes as the 2θ and FWHM values increase; this behavior might be a result of the crystalline nature of the Nb powdered material.
Table 2 is the summary of the modified Scherrer’s equation data (values of ℓnβ and ℓn(1/cosθ)) and Fig. 5 shows the modified Scherrer’s equation (the plot of ℓnβ as a function of ℓn(1/cosθ)) of the milled powders. Since β · Cosθ value is, in fact, not a constant value for all the four peaks, this was the cause of the deviation from a 45° slope, observed in Fig. 5. The slope of the modified Scherrer’s equation plot in this study is negative. This is as a result of the fact that at high 2θ angles, with low values of Cosθ and higher values of ℓn(1/Cosθ), the sizes of the β values obtained are less than what it must be when applied to the Scherrer’s Eq. 20. The modified Scherrer equation can offer the advantage of reducing the size of the absolute values, thereby, producing a single line throughout the points and hence, yielding a single value of the intercept, where a single value of the crystal size, L, of the available peaks, can be obtained20.
Monshi et al.20, reported the fact that if the result of ℓnβ is plotted as a function of ℓn(1/cosθ), a straight-line graph with a slope of around one and an intercept of about ℓn \(\frac{K}{L}\), should result. After obtaining the intercept, the exponential of the intercept is obtained, which is equal to \(\frac{K\lambda }{L}\) and knowing the values of K and ʎ, a single value of L in nanometer, can be calculated20,22. However, in this study, Fig. 5 is the plot of ℓnβ as a function of ℓn(1/cosθ). The intercept of the resulting graph is:
Therefore, \(\frac{K\lambda }{L} = 0.0{117}.\)
The single crystallite size, L of the four peaks is,
Therefore, the single average crystallite size of the whole peaks is,
SEM and EDS of the milled Nb powder
Figure 6 shows the SEM of the milled Nb powder. The points labeled: 1, 2, 3 and4are the spectra identified by the EDS (Fig. 7). The microstructure image in Fig. 6 shows that ethanol wet milling can reduce the particle sizes and minimize the rate of agglomeration of the Nb powders after milling. The particle size of the powder, slowly decreased with the increasing rotation speed, from 200 to 400 rpm of the milling machine, owing to the high energy milling process23. During the ethanol wet milling process, the Nb powder, ethanol, and the steel balls were subjected to high energy particle-to-particle interaction, and the steel milling balls collision at a high revolution speed of 400 rpm. It appeared achievable that these outcomes are appropriate to the initial grains, which were broken down into unit squashed portions. However, looking at the upper left side of the SEM image (Fig. 6) it can be observed that the powder attained a certain level of agglomeration after 10 h of the ethanol-wet milling. Hence, more time is required in achieving, often tiny particle sizes, during the ethanol wet milling of the Nb powder. The high definite surface area of the particles increases the van der Waals forces between them and this is the basis of the de-agglomeration of the powdered particles6,24, following wet milling.
This present work is significant, considering the possibility of reducing the particle size and the minimization of agglomeration, which will result in the better sintering of the Nb powders. Also, Nb being a good alloying element, the enhancement of the particle surface area will influence the interfacial-adhesion of the Nb powder particles, which enable them to marry well with the particles of the base element (different material). The results of the current study are consistent with those of Fayyaz et al.6, Yang and German25, who found out that wet milling is appropriate to decrease the rate of agglomeration and reduce the particle size of pre-alloy nanophase metallic powders. Figure 7 shows the EDS elemental compositions of the ethanol wet-milled Nb powder. Fe, O, and C were observed as impurities in the EDS analysis. The Fe presence may be from the steel balls used in the milling since Fe is the major component of steel. The presence of oxygen could be due to the native oxide layer at the surface of Nb (Fig. 1), which then enhances the admission of more oxygen from the processing liquid (ethanol). It is frequently mentioned in the literature, in the study of niobium that the existence of a native oxide layer on the surface of Nb, exposed it to oxygen, and Nb is characterized by its high attraction and binding energy to oxygen26,27,28. To obtain a highly pure Nb surface, without the presence of oxygen or oxide layer, the metal powder was annealed or heated above the temperature of 2000 K, in ultra-high vacuum conditions11,26,27. A significant presence of carbon, C (up to 36 wt.%) was observed in the milled powder when compared to other impurities (Fe = 0.8 wt.%, O = 14 wt.%) and this is purely from the ethanol used in the milling. Nb can form very stable carbides, possessing high inter-atomic bonding energy and it is used in the stabilization of stainless steels to prevent intergranular corrosion since it helps to lower the content of carbon in the steel27,29. The relevance of this study cannot be overemphasized, since the results of this study, have shown another means of extracting important and useful transition carbide (niobium carbide, NbC).
Conclusion
-
1.
The use of ethanol in the wet milling of Nb powder enhanced the reduction of the particle sizes, from -44 µm to an average crystallite size of 11.85 nm, according to the modified Scherrer’s equation employed in the determination of crystal size. The application of the Scherrer’s equation systematically shows increases in the values of nano crystallite size as FWHM and 2θ values decrease since β · cosθ cannot be maintained as constant.
-
2.
In the plot of ℓnβ as a function of ℓn(1/cosθ), the exponent of the intercept was equal to \(\frac{K\lambda }{L}\) , from which a single average value of L = 11.85 nm was obtained.
-
3.
The study can be another way of synthesizing important transition carbide, e.g., NbC, as exemplified in the SEM and EDS results.
References
Awasthi, A., Bhatt, Y., Krishnamurthy, N., Ueda, Y. & Garg, S. The reduction of niobium and tantalum pentoxides by silicon in vacuum. J. Alloy. Compd. 315, 187–192 (2001).
Soisson, D. J., McLafferty, J. & Pierret, J. A. STAFF-INDUSTRY COLLABORATIVE REPORT tantalum and niobium. Ind. Eng. Chem. 53, 861–868 (1961).
Woydt, M., Mohrbacher, H., Vleugels, J. & Huang, S. Niobium carbide for wear protection–tailoring its properties by processing and stoichiometry. Met. Powder Rep. 71, 265–272 (2016).
Yoon, J.-S., Goto, S. & Kim, B. I. Characteristic variation of niobium powder produced under various reduction temperature and amount of reductant addition. Mater. Trans. 51, 354–358 (2010).
Wang, J., Li, X., Shaw, L. L., Marcus, H. L. & Cameron, T. B. in 2001 International Solid Freeform Fabrication Symposium.
Fayyaz, A. et al. Effect of dry and wet ball milling process on critical powder loading and mixture properties of fine WC-10Co-0.8 VC powder. Jurnal Teknologi 59, 13 (2012).
Gietzelt, T., Jacobi, O., Piotter, V., Ruprecht, R. & Hausselt, J. Development of a micro annular gear pump by micro powder injection molding. J. Mater. Sci. 39, 2113–2119 (2004).
Suryanarayana, C. Mechanical alloying and milling. Prog. Mater Sci. 46, 1–184 (2001).
Savin, R. R. (Google Patents, 2006).
Habecker, K. A. & Fife, J. A. (Google Patents, 2002).
Wen, H. et al. The influence of oxygen and nitrogen contamination on the densification behavior of cryomilled copper powders during spark plasma sintering. J. Mater. Sci. 46, 3006–3012 (2011).
Kim, B.-R., Woo, K.-D., Yoon, J.-K., Doh, J.-M. & Shon, I.-J. Mechanical properties and rapid consolidation of binderless niobium carbide. J. Alloy. Compd. 481, 573–576 (2009).
Joshi, K. & Paliwal, U. First-principles study of structural and bonding properties of vanadium carbide and niobium carbide. Physica Scripta 80, 055601 (2009).
Kral, C., Lengauer, W., Rafaja, D. & Ettmayer, P. Critical review on the elastic properties of transition metal carbides, nitrides and carbonitrides. J. Alloy. Compd. 265, 215–233 (1998).
Liermann, H. et al. Compression behavior of VC0. 85 up to 53 GPa. Int. J. Refract. Metals Hard Mater. 22, 129–132 (2004).
Oyama, S. T. in The Chemistry of Transition Metal Carbides and Nitrides 1–27 (Springer, 1996).
Toth, L. E. Refractory materials. Trans. Metal Carbides Nitrides. 7, 88 (1971).
Upadhyaya, G. Nature and Properties of Refractory Carbides. (Nova Science Pub Incorporated, 1996).
da Teixeira, S. V., Ko, E., Schmal, M. & Oyama, S. Synthesis of niobium carbide from niobium oxide aerogels. Chem. Mater. 7, 179–184 (1995).
Monshi, A., Foroughi, M. R. & Monshi, M. R. Modified Scherrer equation to estimate more accurately nano-crystallite size using XRD. World J. Nano Sci. Eng. 2, 154–160 (2012).
Scherrer, P. Determination of the size and internal structure of colloidal particles using X-rays. Nachr. Ges. Wiss. Göttingen 2, 98–100 (1918).
Monshi, A. & SOLTAN, A. S. A new method to measure nano size crystals by scherrer equation using XRD. (2008).
Munkhbayar, B. et al. Influence of dry and wet ball milling on dispersion characteristics of the multi-walled carbon nanotubes in aqueous solution with and without surfactant. Powder Technol. 234, 132–140 (2013).
De Souza, J. P., Atre, S. V., Suri, P. K., Thomas, J. A. & German, R. M. Understanding homogeneity of powder-polymer mixtures–effect of mixing on tungsten powder injection molding feedstock. Revista Metalurgia e Materials 59, 16–19 (2003).
Yang, M.-J. & German, R. M. Nanophase and superfine cemented carbides processed by powder injection molding. Int. J. Refract Metal Hard Mater. 16, 107–117 (1998).
Halbritter, J. On the oxidation and on the superconductivity of niobium. Appl. Phys. A 43, 1–28 (1987).
Nico, C., Monteiro, T. & Graça, M. P. Niobium oxides and niobates physical properties: review and prospects. Prog. Mater Sci. 80, 1–37 (2016).
Shamrai, V., Blagoveshchenski, Y. V., Gordeev, A., Mitin, A. & Drobinova, I. Structural states and electrical conductivity of oxidized niobium nanopowders. Russian Metall. (Metally) 2007, 322–326 (2007).
Williams, W. S. Transition metal carbides, nitrides, and borides for electronic applications. Jom 49, 38–42 (1997).
Acknowledgements
The authors acknowledge the Department of Science and Technology (DST), South Africa for financial support.
Author information
Authors and Affiliations
Contributions
A.A.E.: Conceptualization, Methodology, Writing an original draft. E.R.S.: Supervisor, validation, editorial. W.K.K.: Visualization, Investigation. J.S.: Visualization, Investigation. J.M.N.: Supervision. T.J.: Validation. M.O.D.: Visualization, Investigation. I.D.I.: Visualization, Validation. M.B.S.: Validation. D.A.D.: Validation.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Eze, A.A., Sadiku, E.R., Kupolati, W.K. et al. Wet ball milling of niobium by using ethanol, determination of the crystallite size and microstructures. Sci Rep 11, 22422 (2021). https://doi.org/10.1038/s41598-021-01916-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-01916-w
- Springer Nature Limited