Abstract
Tungsten disulfide (WS2) quantum dots (QDs) embedded in polyvinylpyrrolidone (PVP) based flexible memristive devices were prepared, and those devices exhibited typical bistable electrical switching and remarkable nonvolatile memristive behaviors. Maximum electricity ON/OFF ratio obtained from the current–voltage (I-V) curves of the device is close to 104. The set voltage of the device is +0.7 V, which effectively reduced the energy consumption. The retention times extracted from data for the devices were as large as 1 × 104 s, which points to these devices having nonvolatile characteristics. Moreover, the highly flexible characteristics of the devices were demonstrated by bending the devices. The carrier transport mechanisms were explained by fitting the I-V curves, and possible operating mechanisms of the devices can be described based on the electron trapping and detrapping processes. WS2 QDs uniformly dispersed in pure transparent N, N-Dimethylformamide (DMF) were obtained by using ultrasonication and a hydrothermal process in this work.
Similar content being viewed by others
Introduction
Over the past decade, hybrid inorganic/organic nanocomposites (HION) based thin film memory devices have been attractive subjects and have received great attention because of their superiority of low cost and power consumption, simple fabrication, which manifest their attractive and noteworthy applications in next generation memory cells, biomarker and artificial intelligence technologies, and logic computing1,2,3,4,5,6,7,8,9,10,11,12. Furthermore, HION-based memory devices are superior to other devices in the following aspects: the films are sturdy, and the active layers can be easily deposited. The devices can be manufactured using solution process and have both flexibility and mechanical strength, which are typical properties of polymer and inorganic materials, respectively13,14,15,16. Another advantage, which has attracted much attention, is that HION materials can be used as the active layers for bistable nonvolatile devices, with such devices exhibiting storage characteristics by trapping and releasing charges1,2,3,4. Among the various types of HION based memory device, nanoparticles and nanosheets of two-dimensional (2D) materials embedded HION memory devices are particularly attractive due to their properties of high flexibility and charge storage capability2,4,5. The appropriate energy levels and quantum confinement effects of 2D materials turn them into outstanding alternative materials for providing charge-trapping sites in memristive devices9,10,11,12.
As a typical 2D material, graphene has led to wide range of investigations on next generation electronic and optoelectronic systems due to its unique structure and optoelectronic properties. Many interesting applications of graphene, such as fuel cells, supercapacitors, hydrogen storages, and sensors, have been reported17,18,19. Because of the large number of reports on the achievements of graphene, research on tungsten disulfide (WS2) and molybdenum disulfide (MoS2), which are analogues of graphene, is once again receiving great attention. As a typical, nontoxic, semiconducting, transition metal dichalcogenide (TMD), WS2 has shown unprecedented promise in material science, with possible technological applications in optoelectronics, energy harvesting devices, chemical catalysts, sensors, and bio-markers20,21,22,23,24. The band gap of the WS2 can be changed from an indirect gap to a direct gap by exfoliating WS2 flakes to a lower-dimensional form of WS2, such as a nanosheet, which allows the WS2 material to exhibit remarkable properties20,21. The most noteworthy matter is that WS2 quantum dots (QDs) having more distinct and excellent optoelectronic properties due to its stronger quantum confinement effect than WS2 nanosheets16,17,18.
In this contribution, uniformly dispersed WS2 QDs with sizes of 10 nm were synthesized by using a combination of ultra-sonication and a hydrothermal exfoliating process. WS2 flakes were first exfoliated into nanosheets by ultrasonic treatment, and the WS2 QDs were synthesized by a facile hydrothermal process, which a means of cutting the precursor nanosheets placed in the autoclave in a high temperature and pressure environment22,23,24,25,26,27,28,29. N, N-Dimethylformamide (DMF), as an efficient catalyst for two-dimensional material exfoliating, has been briefly applied to the exfoliating of the WS2 flakes28,29,30,31,32,33,34. As a proof of our inference, we present a simple techniques for fabricating a memristive device that was embedded with synthesized WS2 QDs in a polymer matrix acting as an active layer and that exhibited excellent memory characteristics. The matrix material, polyvinylpyrrolidone (PVP), is a nontoxic, nonionic polymer having an excellent wetting property; it enable the fabricated device very flexible5,6,7,8,9,10,11,12,13,14,15,16,35,36,37,38. The nanomaterial of the active layer was synthesized by mixing the prepared WS2 quantum dots with PVP under laboratory conditions by a simply magnetic string process. In this investigation, the exfoliated WS2 QDs played important roles at charge-trapping sites, which resulted in the bistable electrical characteristics of the nonvolatile memory device. The nonvolatile rewritable properties of the device was investigated, and the possible conduction mechanisms were determined by several linear fitting models of measured I-V results. Also the device shows high stability and flexibility. We infer that the performance of this device is attributed to the extremely strong quantum confinement effect of WS2 QDs. These experiment results observed in this work provide valuable information for further investigations about 2D material QD-based organic bistable memory devices in the future39,40,41,42,43,44,45.
Methods
Tungsten disulfide (WS2, 40–80 nm, 99.99%, amorphous) was purchased from 3302 Twig Leaf Ln, Houston, TX 77084, USA. Polyvinylpyrrolidone (PVP, NW-10000) was purchased from Aldrich Co. The suspension of WS2 dispersed N,N-Dimethylformamide (DMF) was prepared through a solution process, in a laboratory condition. We first added 10 mg of WS2 to 2.5 mL of DMF, the mixture was treated by sonicating for 5 h and then centrifuged for 20 min at 8000 rpm to remove the residual WS2 flakes at room temperature. Acquired suspension was transferred into a Teflon-lined stainless-steel autoclave and kept temperature at 200 °C for 10 h, subsequently cooled to room temperature naturally. The PVP powder was dissolved in liquid state DMF with a concentration of 10 mg/ml, and magnetically stirred the mixture for 3 hours in a room temperature afterward. A WS2 QD-PVP colloid with a WS2 QD/DMF colloid concentration of 0.8 wt%. The obtained solution was sequentially mixed by magnetic stirring process for 10 hours at an ambient of room temperature.
Memristive devices were fabricated by coating the synthesized WS2 QD-PVP nanocomposite on an indium tin oxide (ITO)-coated polyethylene glycol naphthalate (PEN) flexible substrates with a size of 2.5 cm × 2.5 cm. The WS2-PVP solution was deposited on the ITO film by spin coating at 300 and 3000 rpm for 20 and 40 s, respectively, and was annealed at 100 °C for 1 hour to evaporate the excess DMF. After annealing process, the Al electrodes with thicknesses of 200 nm were evaporated on the WS2 QD-PVP layer by utilizing a metal mask in a pressure of 1 × 10−6 Torr in a thermal condition.
The electrical performances were measured with the aid of Keithley 2400 Digital Source Meter. An external bias voltage was exerted to the Al electrode all the while, at the state of setting the ITO electrode ground. Atomic force microscopy (AFM) images were recorded by using a Dimension 3100 (Vecco, CA) system in the tapping mode. The photoluminescence (PL) measurements were recorded by using a spectrophotometer (Unico 4802). UV-vis spectra of synthesized WS2 QDs were investigated by utilizing a Shimadzu UV-3600 spectrometer. The image of Transmission electron microscopy (TEM) was carried out by a CM30 transmission electron microscope at a driving voltage of 300 kV. Ultraviolet photoelectron spectroscopy (UPS) imaging was carried out by using a Thetaprobe (UV source: He1, 21.2 eV; pass energy: 1 eV; energy step size: 0.05 eV).
Results and Discussion
WS2 QDs with DMF-assisted exfoliation were prepared from WS2 flakes, and the WS2 QDs were successfully synthesized, as schematically shown in Fig. 1(a). In contrast, the WS2 flakes were also exfoliated in pure ethanol and de-ionized (DI) water, which can vaporize at high temperatures, leading to increased pressure in sealed autoclaves. The suspension obtained via the catalyst DMF exhibited high stability, but no precipitation could be observed even after it had been held at room temperature for several months. The experimental results shown in Fig. 1(b) clearly demonstrate that in a thermal environment, pure DMF can effectively exfoliate the layered WS2 flakes and disperse them into the catalyst. The TEM measurements on the diluted WS2 QDs solution, which were used to observe the appearance of the synthesized WS2 QDs on a nanoscale, were in progress. Figure 1(c,d) exhibits a distinctly dispersion of WS2 QDs and electron diffraction (ED) image, respectively. The observed specimens, as shown in the figure, were seen to express circular shapes and diameters ranging from 3 to 5.5 nm; the ED image manifestly shows the crystalline structure of the WS2 QDs catalytically synthesized by using pure DMF utilizing a combination of ultra-sonication and a hydrothermal process
(a) Schematic illustration of catalyst-assisted exfoliation of WS2. After the WS2 flakes had been mixed with DMF, sonication was used to exfoliate the WS2 flakes to obtain a few WS2 nanosheets, and the hydrothermal method was used to obtain the WS2 QDs. (b) Photos of the solutions of exfoliated WS2 flakes in (1) ethanol, (2) DI water, and (3) DMF. (c) Transmission electron microscopy image of the WS2 QDs and (d) ED image of the WS2 QDs.
Figure 2(a) presents the ultraviolet (UV)-visible-infrared absorption spectrum of the WS2 QD solution taken under 365-nm UV light. Synthesized WS2 QDs dispersed suspension were clearly attested of high purity due to the unique single peak absorption value at the wavelength of 220 nm. The PL intensity emitted by the excited WS2 QD dispersion was investigated as a function of the excitation wavelength, and the results are shown in Fig. 2(b). Blue photoluminescent WS2 QDs were observed. An excitation-dependent PL is observed, and the peak is in reasonable agreement with the QD size distribution. The emission is seen to increase with increasing excitation until it reaches its maximum at an excitation wavelength of 420 nm, which according with the results for WS2 QDs manufactured via other approaches23. The excitation-dependent PL spectrum indicates polydispersity of the prepared WS2 QDs, which agrees with the characteristics of our synthesis method. The initial ultraviolet photoelectron spectroscopy (UPS) measurements were also obtained, the work function of the WS2 material is approximately 4.22 eV through the curve carried out, as shown in Fig. 2(c).
A schematic diagram of the device configuration with active layers and the practicality of the device for everyday use are shown in Fig. 3(a,b), respectively. Figure 3(c) shows a cross-sectional FE-SEM image of the WS2 QD-PVP nanocomposites formed on an ITO-coated substrate. The WS2 QD-PVP layer can be seen to have been uniformly coated on the ITO electrode. The image of atomic force microscopy (AFM) is shown in Fig. 3(d). An AFM determination was taken to characterize the surface roughness to characterize the deposited WS2 QD-PVP nanocomposites. The root-mean-square (rms) roughness of the WS2 QD-PVP nanocomposite layer is approximately 0.250 nm which strongly shows that the highly smooth and uniform WS2 QD-PVP active layer could be easily obtained by spin-coating process.
The memory effects of the Al/WS2 QD-PVP/ITO/PEN memristive device were characterized by using current-voltage (I-V) curves, and the results were exhibited in Fig. 4(a). Firstly, when the device was swept positively from 0 to +3 V, the current significantly increased with gradually increasing applied voltage, and increase abruptly from 1.0 × 10−5 to 1.0 × 10−2 A when the bias voltage increased to +0.7 V, indicating that the state of the device had transitioned from a high resistance state (HRS, which is denoted as an OFF state) to a low resistance state (LRS, which is denoted as an ON state). For the I-V curves, the process of device transition from HRS to LRS is seen as the ‘writing’ process in memory circuit cells, and an electricity ON/OFF ratio observed was as high as 104. The features of our Al/WS2 QD-PVP/ITO/PEN memristive device promise low energy consumption and a low information loss rate during operation35. When the sweeping process in stage 1 and 2 applied again, the state of device can be maintained in LRS and even with the power was off, indicative of excellent stability and nonvolatile memristive characteristics of the memory device. Another attractive features of the device is that HRS of the device can be retrieved by applying a low negative voltage of −2.7 V, which is equivalent to the ‘erase’ process of a flash memory device. The process of second sweep shows electrical properties similar with the first sweep. Due to such properties of nonvolatile and rewritable, WS2 QD-PVP nanocomposites will allowed to be used as an electrically bistable material in flash memory devices.
(a) Current-voltage characteristics of Al/WS2 QD-PVP/ITO/PEN memristive devices. (b) Current in the LRS and the HRS at −0.5 V for the endurance test. (c) Retention characteristics. (d) Current-voltage curves for the Al/WS2 QD-PVP/ITO/PEN devices for bending radius of 0, 10, and 20 mm. (e) Endurance measurements according to the bending cycles number of the device over 100 bending cycles under a reading bias voltage of −0.5 V. (f) Retention measurements after bending the Al/WS2 QD-PVP/ITO/PEN devices under a reading bias voltage of −0.5 V.
Figure 4(b) exhibits the endurance performances of the devices. Cycling frequency in the process of measurements was approximately 0.3 Hz. No performance damping of the device occurred in the process of measurements. Results measured of retention characteristics on the LRS and the HRS for the devices were displayed in Fig. 4(c). Different resistance states remained a charge conservation for 104 seconds under the normal condition, furthermore the observation that the conduction states were clearly distinguishable during that time indicative of the outstanding stability of the device.
In order to investigate the flexibility of the device, we bent the fabricated specimen so that its radii of curvature were 10 and 20 mm respectively, and the I-V results are shown in Fig. 4(d). I-V curve for the device under bending can be confirmed to be similar to that for the device without bending. No considerable variation in the ON/OFF current ratio was observed after the device had been bent. Also, as can be observed in Fig. 4(e,f), very few variation of the current values occurred by bended ITO electrode which slightly decrease the conductivity of the devices were seen during the endurance and retention tests respectively, indicative of the highly stable of the highly flexible memory device13.
Additionally, we point out that no bistability phenomenon was observed when a pure PVP layer without WS2 QDs was used. Figure 5(a) shows the I–V curves for pure PVP-based devices, and no bistability phenomenon is observed when an external sweeping bias is applied to the Al electrode. Furthermore, we investigated the influence of interface states at the junction of the PVP layer and the Al electrode, so we prepared pure PVP-based devices with different Al electrode areas, and we investigated their I–V characteristics6,8,46. Figure 5(b) presents the I-V curves for pure PVP-based devices with electrode areas of 0.008, 0.018 and 1 cm2; similarly, no bistability phenomenon were observed. Such results strongly demonstrate that the WS2 QDs play a key role in the electrical bistable behavior of our devices; accordingly, the charge trapping and releasing are attributed to the embedded WS2 QDs.
The obtained I–V data were fitted by using various conduction models to clarify the carrier transport mechanism, and the results are shown in Fig. 6(a). Fitting of the data was executed by utilizing two models, the space-charge-limited current (SCLC) and the Ohmic conduction models. Three distinct regions can be observed in the I-V plots, suggesting that a different conduction mechanism is operating in each region. In the OFF state, as the voltage applied was increased from 0 to +0.7 V, the current increased exponentially as I~Vm (m = 2.255) in the switching region 1 (shown in Fig. 6(b)). Such a linear characteristic on a ln-ln scale implies that the conduction mechanism in this process is most likely related to a space-charge-limited current, which can be fitted by using the following equation:
In the fitting equation, ε is the dielectric constant of the polymer (in this work, it’s PVP), μ is the mobility of the carriers in the active layer, V is the value of the external bias voltage, and L is the thickness of the active layer47,48. In the ln (I) ~ ln (V) of Fig. 6(c), a linear relation with a slope of 0.911 was observed in region 2 as the voltage was swept from +0.7 to +3.0 V, suggesting that Ohmic conduction was dominant. When the voltage was returned to the original applied voltage of 0 V, the plot of ln (I) ~ ln (V) remained nearly linear with a slope of 1.04, indicating the continuing dominance of Ohm’s law in region 3. The carrier transport at the LRS was not affected with the direction of the applied voltage due to the Ohmic conduction dominates for the LRS. It also indicates that the I-V curves for the LRS states in the voltages of positive range can be fitted by utllizing Ohmic conducting model completely, which displayed in Fig. 6(d).
According to the results and discussions, we propose that the electronic transition between HRS and LRS can be explained by the mechanisms of carrier trapping and releasing behaviors of WS2 in the matrix of PVP. The proposed energy band diagram for the fabricated Al/WS2 QD-PVP/ITO device has shown in Fig. 7. The material work functions of the ITO and the Al electrode are −4.8 and −4.3 eV, respectively11. For the material of PVP, the highest occupied molecular orbital (HOMO) level is −6.2 eV, and the lowest unoccupied molecular orbital (LUMO) is −2.8 eV23. The electron affinity of the WS2 nanoparticles with a bandgap of 1.3 to 1.8 eV is low (−3.0 eV), which induces a large electron and hole injection barrier due to the applied voltage. The large barrier at the low voltage region (region 1 in Fig. 6(a)) results in a low injection of carriers. The carriers at higher voltage (region 2 in Fig. 6(a)) are injected into the PVP dielectric layer by tunneling through the barrier. The carriers are trapped by the WS2 QDs due to their having a lower energy level and to the quantum confinement effect. The amount of injected charge increases with any further increase in the applied switching voltage, leading to an abrupt current transition, at which time nearly all of the traps in the active layer are filled with charges. Subsequently, the device exhibits phenomenon of Ohmic conduction while the state get ON. Furthermore, the charges remained in the WS2 QDs were maintained even after cease the bias on the electrode, which accounts for the high conductivity and stability of our memory device. When a reset voltage is applied, the trapped charges are released. Then, the device returns to its initial HRS, which is called an erasing process; this indicates data storage has been achieved.
Conclusions
A facile approach for exfoliating and dispersing WS2 flakes into a QD state with the aid of DMF has been reported. This approach provides a method for mass production of WS2 QDs stably dispersed in DMF. WS2 QDs stably dispersed in DMF and embedded in PVP exhibit high electrical bistability and flexibility, and we assume that the excellent performance of the devices can be attributed to the high quantum confinement of WS2 QDs; thus, this kind of nanocomposite can be used as an active layer in nonvolatile memristive devices. The thin-film memristive device based on the WS2 QD-PVP nanocomposite showed an electrically bistable behavior. The carrier transport mechanisms in the device may have resulted from the carrier trapping and releasing behaviors due to the trap sites formed by the WS2 QDs embedded in PVP organic matrix under the condition of applying external bias. This memristive device, by virtue of its nonvolatile and writable/erasable features, exhibits potential for applications in flexible organic memory cells, USB drives, bio-sensors, and other types of electronic and optoelectronic systems.
References
Kim, T. W., Yang, Y., Li, F. & Kwan, W. L. Electrical Memory Devices Based on Inorganic/Organic Nanocomposites. NPG Asia Mater. 4, e18 (2012).
Son, D. I. et al. Flexible Organic Bistable Devices Based on Graphene Embedded in an Insulating Poly(methyl methacrylate) Polymer Layer. Nano Lett. 10, 2441–2447 (2010).
Wu, C., Kim, T. W., Choi, H. Y., Strukov, D. B. & Yang, J. J. Flexible three-dimensional artificial synapse networks with correlated learning and trainable memory capability. Nat. Commun. 8, 752 (2017).
Bok, C. H., Wu, C. & Kim, T. W. Operating mechanisms of highly-reproducible write-once-read-many-times memory devices based on graphene quantum dot:poly(methyl silsesquioxane) nanocomposites. Appl. Phys. Lett. 110, 013301 (2017).
Choi, M. K. et al. Flexible memristive devices based on polyimide:mica nanosheet nanocomposites with an embedded PEDOT:PSS layer. Sci. Rep. 8, 12275 (2018).
Fuji, T. et al. Hysteretic current–voltage characteristics and resistance switching at an epitaxial oxide Schottky junction SrRuO3/SrTi0.99Nb0.01O3. Appl. Phys. Lett. 86, 012107 (2005).
Choi, M. S. et al. Controlled charge trapping by molybdenum disulphide and graphene in ultrathin heterostructured memory devices. Nat. Commun. 4, 1624 (2013).
Scott, J. C. & Bozano, L. D. Nonvolatile Memory Elements Based on Organic Materials. Adv. Mater. 19, 1452–1463 (2007).
Bok, C. H., Woo, S. J., Wu, C., Park, J. H. & Kim, T. W. Flexible bio-memristive devices based on chicken egg albumen:Au@SiO2 core-shell nanoparticle nanocomposites. Sci. Rep. 7, 12033 (2017).
Yun, D. Y., Kim, T. W. & Kim, S. W. Effect of the ZnS Shell Layer on The Charge Storage Capabilities of Organic Bistable Memory Devices Fabricated Utilizing CuInS2-ZnS Core-Shell Quantum Dots Embedded in a Ppoly(methylmethacrylate) Layer. Thin Solid Films 544, 433–436 (2013).
Kim, D. H. et al. Flexible Memristive Devices Based on InP/ZnSe/ZnS Core−Multishell Quantum Dot Nanocomposites. ACS Appl. Mater. Interfaces 10, 14843–14849 (2018).
Yun, D. Y., Song, W. S., Kim, T. W., Kim, S. W. & Kim, S. W. Electrical Stabilities and Carrier Transport Mechanisms of Flexible Organic Bistable Devices Based on CdSe-InP Core-Shell Nanoparticle/Polystyrene Nanocomposites. Appl. Phys. Lett. 101, 103305 (2012).
Lee, J. H., Wu, C., Sung, S., An, H. & Kim, T. W. Highly flexible and stable resistive switching devices based on WS2 nanosheets:poly(methylmethacrylate) nanocomposites. Sci. Rep. 9, 19316 (2019).
Yang, Y., Ouyang, J., Ma, L., Tseng, R. J. H. & Chu, C. W. Electrical Switching and Bistability in Organic/Polymeric Thin Films and Memory Devices. Adv. Funct. Mater. 16, 1001–1014 (2006).
Chujo, Y. & Tamaki, R. New Preparation Methods for Organic–Inorganic Polymer Hybrids. MRS Bulletin 26, 389 (2001).
Ogoshi, T. & Chujo, Y. Organic–inorganic polymer hybrids prepared by the sol-gel method. Composite Interfaces 11, 539 (2005).
Novoselov, K. S. et al. Two-Dimensional Gas of Massless Dirac Fermions in Graphene. Nature 438, 197–200 (2005).
Christian, K. K. et al. Environmental applications using graphene composites: water remediation and gas adsorption. Nanoscale 5, 3149 (2013).
Li, X. et al. Large-Area Synthesis of High-Quality and Uniform Graphene Films on Copper Foils. Science 324, 1312–1314 (2009).
Lan, C., Li, C., Yin, Y. & Liu, Y. Large-area synthesis of monolayer WS2 and its ambient-sensitive photo-detecting performance. Nanoscale 7, 5974 (2015).
Matte., H. S. S. R. et al. MoS2 and WS2 Analogues of Graphene. Angew. Chemie. 49, 4059–4062 (2010).
Ren, X. et al. One-step hydrothermal synthesis of monolayer MoS2 quantum dots for highly efficient electrocatalytic hydrogen evolution. J. Mater. Chem. A 3, 10693–10697 (2015).
Kim, D. H., Kim, W. K., Woo, S. J., Wu, C. & Kim, T. W. Highly-reproducible nonvolatile memristive devices based on polyvinylpyrrolidone: Graphene quantum-dot nanocomposites. Org. Elecron. 51, 156–161 (2017).
Gu, W. et al. One-Step Synthesis of Water-Soluble MoS2 Quantum Dots via a Hydrothermal Method as a Fluorescent Probe for Hyaluronidase Detection. ACS Appl. Mater. Interfaces 8, 11272–11279 (2016).
Zhao, G. et al. Chemical Weathering Exfoliation of Atom-Thick Transition Metal Dichalcogenides and Their Ultrafast Saturable Absorption Properties. Adv. Funct. Mater. 25, 5292–5299 (2015).
Lin, H. et al. Rapid and highly efficient chemical exfoliation of layered MoS2 and WS2. J. Alloy. Compd. 699, 222–229 (2017).
Bayat, A. & Saievar-Iranizad, E. Synthesis of blue photo luminescent WS2 quantum dots via ultrasonic cavitation. J. Lumin 185, 236–240 (2017).
Cai, D.; Song, M. Preparation of fully exfoliated graphite oxide nanoplatelets in organic solvents. J. Mater. Chem. 17, 3678−3680 (2007).
Keeley, G. et al. Electrochemical ascorbic acid sensor based on DMF-exfoliated graphene. J. Mater. Chem. 20, 7864–7869 (2010).
Shelke, N. T. & Karche, B. R. Hydrothermal synthesis of WS2/RGO sheet and their application in UV photodetector. J. alloy compo. 653, 298–303 (2015).
Ohuchi, F. S., Jaegermann, W., Pettenkofer, C. & Parkison, B. A. Semiconductor to Metal Transition of WS2 Induced by K Intercalation in Ultrahigh Vacuum. Langmuir 5, 439–442 (1989).
Raza, F. et al. Visible-Light-Driven Oxidative Coupling Reactions of Amines by Photoactive WS2 Nanosheets. ACS Catal 5, 2754–2759 (2016).
Zhou, K. G., Mao, N. N., Wang, H. X., Peng, Y. & Zhang, H. L. A Mixed-Solvent Strategy for Efficient Exfoliation of Inorganic Graphene Analogues. Angew. Chemie. 50, 10839–10842 (2011).
Barga, D., Lezama, I. G., Berger, H. & Morpurgo, A. F. Quantitative Determination of the Band Gap of WS2 with Ambipolar Ionic Liquid-Gated Transistors. Nano Lett. 12, 5218–5223 (2012).
Wang, Y. et al. Electrochemical Control of Photoluminescence in Two-Dimensional MoS2 Nanoflakes. ACS Nano 7, 10083–10093 (2013).
Koo, C. M., Ham, H. T., Choi, M. H., Kim, S. O. & Chung, I. J. Characteristics of polyvinylpyrrolidone-layered silicate nanocomposites prepared by attrition ball milling. Polymer 44, 681–689 (2003).
Bourlinos, A. B. et al. Aqueous-phase exfoliation of graphite in the presence of polyvinylpyrrolidone for the production of water-soluble graphenes. Solid State Commun. 149, 2172–2176 (2009).
Wang, L., Zhang, L. & Tian, M. Improved polyvinylpyrrolidone (PVP)/graphite nanocomposites by solution compounding and spray drying. Polym. Adv. Technol. 23, 652–659 (2011).
Wang, D. et al. Quantum conductance in MoS2 quantum dots-based nonvolatile resistive memory device. Appl. Phys Lett. 110, 093501 (2017).
Wu, C., Li, F. & Guo, T. Efficient tristable resistive memory based on single layer graphene/insulating polymer multi-stacking layer. Appl. Phys. Lett. 104, 183105 (2014).
Zhang, P. et al. Structural Phase Transition Effect on Resistive Switching Behavior of MoS2-Polyvinylpyrrolidone NanocompositesFilms for Flexible Memory Devices. Small 15, 2077–2084 (2016).
Wu, C., Li, F., Zhang, Y., Guo, T. & Chen, T. Highly Reproducible Memory Effect of Organic Multilevel Resistive-Switch Device Utilizing Graphene Oxide Sheets/Polyimide Hybrid Nanocomposite. Appl. Phys. Lett. 99, 042108 (2011).
Ooi, P. C., Lin, J., Kim, T. W. & Li, F. Tristable switching of the electrical conductivity through graphene quantum dots sandwiched in multi-stacked poly (methyl methacrylate) layers. Org. Electron. 38, 379–383 (2016).
Jung, J. H. & Kim, T. W. The Effect of the Trap Density and Depth on the Current Bistability in Organic Bistable Devices. J. Appl. Phys. 110, 043721 (2011).
Ma, Z., Wu, C., Lee, D. U., Li, F. & Kim, T. W. Carrier transport and memory mechanisms of multilevel resistive memory devices with an intermediate state based on double-stacked organic/inorganic nanocomposites. Org. Electron. 28, 20–24 (2016).
Lanza, M. et al. Recommended Methods to Study Resistive Switching Devices. Adv, Electron. Mater. 5, 1800143 (2019).
Lim, E. W. & Ismail, R. Conduction Mechanism of Valence Change Resistive Switching Memory: A Survey. Electronics 4, 586–613 (2015).
Yu, S., Guan, X. & Philip Wong, H.-S. Conduction mechanism of TiN/HfOx/Pt resistive switching memory: A trap-assisted-tunneling model. Appl. Phys. Lett. 99, 063507 (2011).
Acknowledgements
This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (2019R1A2B5B03069968).
Author information
Authors and Affiliations
Contributions
T.W.K. conceived the project, and H.A. designed the experiments and collected the data. H.A. and Y.H.L., carried out the synthesis of the WS2 QDs. H.A. fabricated the devices and carried out the Current-voltage measurement and all the experimental images. H.A. and J.H.L. carried out the retention and endurance measurements. H.A., Y.H.L., J.H.L., C.W., B.M.K. and T.W.K. analyzed and discussed the data. All the authors discussed the results and contributed to the writing of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
An, H., Lee, Y.H., Lee, J.H. et al. Highly Stable and Flexible Memristive Devices Based on Polyvinylpyrrolidone: WS2 Quantum Dots. Sci Rep 10, 5793 (2020). https://doi.org/10.1038/s41598-020-62721-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-62721-5
- Springer Nature Limited