Abstract
Flexible memristive devices with a structure of Al/polyimide:mica/poly(3,4-ethylenedioxythiophene) polystyrene sulfonate/indium-tin-oxide/polyethylene glycol naphthalate showed electrical bistability characteristics. The maximum current margin of the devices with mica nanosheets was much larger than that of the devices without mica nanosheets. For these devices, the current vs. time curves showed nonvolatile characteristics with a retention time of more than 1 × 104 s, and the current vs. number-of-cycles curves demonstrated an endurance for high resistance state/low resistance state switchings of 1 × 102 cycles. As to the operation performance, the “reset” voltage was distributed between 2.5 and 3 V, and the “set” voltage was distributed between −0.7 and −0.5 V, indicative of high uniformity. The electrical characteristics of the devices after full bendings with various radii of curvature were similar to those before bending, which was indicative of devices having ultra-flexibility. The carrier transport and the operation mechanisms of the devices were explained based on the current vs. voltage curves and the energy band diagrams.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Extensive investigations concerning flexible organic electronics, including memories, memristors, synaptic devices and nanogenerators, have been performed to improve their performance and efficiency for promising applications in flexible systems. Memristive devices are subjects of great scientific interest because they are highly integrable and can be fabricated using simple process1,2,3,4. Memristive devices based on various kinds of nanocomposites have been actively investigated to find ways to improve their electrical characteristics, and memristive devices based on hybrid inorganic/organic nanocomposites containing nanomaterials have currently emerged as excellent candidates for promising applications in flexible/wearable memristive devices due to their having high-mechanical flexibility and relatively low-cost5,6,7,8,9. Among the several kinds of nanomaterials, two dimensional (2D) materials with a monolayer thickness, such as graphene, are attractive because they have high conductivity, good flexibility, and high transparency. The use of 2D materials is limited by the narrowing of their bandgaps; that narrowing occurs because, precise control of the bandgaps for nanomaterials is very difficult10,11,12,13. Among the various kinds of 2D materials, a muscovite-type mica bulk has a large band gap, resulting in its having insulating properties. Worthy of note are the observation that a bulk mica layer can be reduced by using a liquid-phase exfoliation method and that the band gap can be reduced by decreasing the number mica layers. Multilayer mica materials have been employed in electronic and optoelectronic devices due to their unique properties14,15. On the other hand, the polymer acting as the insulating matrix plays an important role in memristive devices. Although polyimide (PI) was extensively used in electronics due to its strong thermal and mechanical stability, low toxicity, and excellent electrical properties, in various industrial fields, it has recently been replaced by inorganic glass and metal oxides16,17,18. Given the advantages of PI and mica, investigations concerning memristive devices based on PI:mica nanosheet nanocomposites should be important; nevertheless, such investigations, to the best of our knowledge, have not yet been performed.
This paper reports data, obtained both before and after bending, for the electrical bistabilities, the memory stabilities, and the memory mechanisms of ultra-flexible memristive devices based on PI:mica nanosheet hybrid nanocomposites fabricated on flexible polyethylene glycol naphthalate (PEN) substrates. Because the electrical performances might have been impaired due to the weak adhesive force the occurred between the bottom indium-tin-oxide (ITO) electrode and the PI:mica active layer when the electrode was being repeatedly bent, poly(3, 4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS), acting as an adhesive buffer layer, was inserted between the ITO electrode and the active layer19,20,21. The PI:mica nanocomposite were measured by using scanning electron microscopy (SEM), and the current-voltage (I–V) characteristics were measured to confirm the memristive performances. Endurance and retention measurements were performed to clarify the stabilities of the devices under mechanical bending conditions, and the results were used to investigate the stabilities under different degrees of mechanical deformations. Finally, the carrier transport and the operation mechanisms were explained based on the I–V curves and the energy band diagram.
Methods
An ITO film was used as the bottom electrode, and an Al thin film was used as the top electrode. After the PEDOT:PSS film had been deposited on a PEN substrate, the PI:mica nanocomposite was spin-coated on a PEDOT:PSS film. The PI used in this experiment was prepared by dissolving p-phenylene biphenyltetracarboximide (BPDA-PDA)-type polyamic acid in N-methy1–2-pyrrolidone (NMP) with a concentration of 1 wt%16,22. The exfoliated muscovite-type mica nanosheets used in this experiment were prepared by using ultrasonication, centrifugation, and ultrasonication14. The ultrasonic treatment was performed for 4 h to obtain a uniform mica nanosheet suspension. After the ultrasonic treatment of the mica nanosheet, the PI solution and the mica suspension were mixed in a mass ratio of 4:1. Then, another ultrasonic treatment was performed at 27 °C for 4 h to achieve a uniform suspension. ITO/PEN substrates were cleaned ultrasonically in acetone, methanol, and deionized water at 27 °C for 20 min each. The substrates were dried by using N2 gas. The PEDOT:PSS solution with a concentration of 1.1 wt% was spin-coated onto the cleaned ITO/PEN substrate at 500 rpm for 5 s, 1000 rpm for 15 s, 2000 rpm for 30 s, 1000 rpm 15 s, and 500 rpm 5 s. Then, the sample was thermally annealed at 100 °C for 20 min. The PI:mica solution was spin-coated onto the PEDOT:PSS/ITO/PEN substrate at 500 rpm for 5 s, 1000 rpm for 15 s, 2000 rpm for 30 s, 1000 rpm 15 s, and 500 rpm 5 s, followed by thermal annealing at 100 °C for 20 min to remove the residual solvent on the PI:mica nanocomposite. Al electrodes (diameters: 1 mm; thicknesses: 200 nm) were deposited on the PI:mica layer by using thermal evaporation at a chamber pressure of 1 × 10−6 Torr. SEM (NOVA NanoSEM 450 system), transmission electron microscopy (TEM, JEM-2100F), and atomic force microscopy (AFM, XE-100) were used to characterize the device, the as-prepared mica nanosheets, and the PI:mica nanocomposite. The I–V curves of the memristive devices were measured by using a Keithley 2400 digital source meter.
Results and Discussion
Figure 1(a) shows a typical TEM image of the exfoliated mica nanosheets. Characterization by using AFM detected a sheet-like morphology with a thickness ranging from 1 to 4 nm and with a layer number ranging from 1 to 3, as shown in Fig. 1(b)14. The thinnest sheets corresponded to monolayer nanosheets. A schematic of the memristive devices is shown in Fig. 1(c,d) shows a cross-sectional SEM image of the memristive device without top electrodes. The SEM image shows that the PI:mica and the PEDOT:PSS layers were precisely deposited on the ITO-coated PEN substrate. The thicknesses of the PEDOT:PSS layers and the PI:mica layer, as determined form the SEM image, were 338 and 424 nm, respectively. Note that after an ultrasonic treatment for 4 h, the exfoliated muscovite-type mica was uniformly mixed with the PI layer in the NMP solvent. As a result, a homogeneous solution of exfoliated mica and PI without any precipitate was obtained, as shown in inset of Fig. 1(e). Because the exfoliated muscovite-type mica was uniformly distributed in the PI solution, the mica nanosheets should be uniformly distributed in the PI:mica layer, as shown in the SEM image in Fig. 1(e). The AFM images in Fig. 1(f) show the roughness of the PI:mica layer. The value of the root-mean-square (RMS) roughness of the PI:mica layer was 5.377 nm.
(a) TEM image of a mica nanosheet. (b) Typical AFM image of mica nanosheets on a Si substrate. (c) Schematic diagram of an Al/PI:mica/PEDOT:PSS/ITO device fabricated on a PEN substrate. (d) Cross-sectional SEM image of the PI:mica/PEDOT:PSS/ITO device. (e) SEM image of the PI:mica surface. Inset is the photo of mica:PI solution. (f) Atomic force microscopy image of the PI:mica surface.
Because the PI:mica nanocomposite forms a uniform structure, the memristive device exhibits stable memory switching characteristics. The I–V curves in Fig. 2(a) show the switching characteristics of the memristive device. The black and the red circles represent the I–V curves of the Al/PI:mica/PEDOT:PSS/ITO device and the Al/PI/PEDOT:PSS/ITO device, respectively. The I–V curve of the Al/PI:mica/PEDOT:PSS/ITO device shows hysteresis characteristics, which is an essential feature of memristive memory devices23. Two different resistance states, the high resistance state (HRS) and the low resistance state (LRS), were clearly observed. Initially, the device in its initial state stayed in the HRS. When the negative bias voltage reached −0.3 V, the current increased from 1.03 × 10−6 to 1.22 × 10−2 A, indicative of the switch from the HRS to the LRS. The HRS-to-LRS transition corresponds to a set process in a memory cell. After the device had switched from the HRS to the LRS, it stayed in the LRS. However, when the positive bias voltage was increased to 3 V or more, the current decreased from 4.15 × 10−2 to 3.29 × 10−5 A, as shown in Fig. 2(a), indicative of a switch from the LRS to the HRS. The LRS-to-HRS transition corresponds to a reset process in a memory cell. The LRS/HRS current ratio of the device containing mica at a reading voltage of 1 V was approximately 4.28 × 103, as shown by the black circles in Fig. 2(a). However, the device without the mica nanosheets did not clearly show any the memory characteristics, as shown by the red circles in Fig. 2(a). Therefore, one can conclude that the mica nanosheets play an important role in the appearance of memory characteristics for the Al/PI:mica/PEDOT:PSS/ITO device. One should note that mica concentration of 1 wt% used in this work is the concentration required for optimal device performance. When the mica concentration was lower than 1 wt%, the ON/OFF ratio of the device gradually increased with increasing mica concentration. This behavior indicated that the mica was acting as carrier trap sites in the device, resulting in an increase in the number of electrons trapped in the active layer. However, the ON/OFF ratio decreased with increasing mica concentration when the mica concentration was higher than 1 wt%, which might results from the aggregation of mica nanosheets in the active layer.
(a) Current-voltage curves for the Al/PI:mica/PEDOT:PSS/ITO/PEN devices (black circles) and the Al/PI/PEDOT:PSS/ITO/PEN devices (red circles). (b) Endurance characteristics of the Al/PI:mica/PEDOT:PSS/ITO/PEN device before bending at a reading voltage of 1 V. (c) Retention characteristics of the Al/PI:mica/PEDOT:PSS/ITO/PEN devices at a reading voltage of 1 V. (d) Probability distributions for the ‘Set’ and the ‘Reset’ threshold voltages of the Al/PI:mica/PEDOT:PSS/ITO/PEN devices.
Figure 2(b) shows the endurance reliability results for the Al/PI:mica/PEDOT:PSS/ITO device. The endurance reliability measurements were carried out at room temperature. The memristive device could be repeatedly switched between the LRS and the HRS for 100 cycles without any noticeable deterioration in its performance. Figure 2(c) shows the retention performance of the device. The retention performances show the variations of the currents in the LRS and in the HRS as functions of time. As can be seen, a stable LRS/HRS current ratio was maintained for a time longer than 1 × 104 s, indicating that the device remained stable even during long operations. Figure 2(d) shows the probability distributions of the reset voltage (Vreset) and the set voltage (Vset) for the device. The values of the Vreset for the device were dominantly distributed between 2.0 and 3.5 V, and those of the Vset were mainly dispersed between −1.0 and −0.1 V. Therefore, the Vset and the Vreset for the devices could be defined as −1.0 V and 3.5 V, respectively.
The I–V curves for the Al/PI:mica/PEDOT:PSS/ITO devices before and after bending with bending radii of 10 and 20 mm are shown in Fig. 3(a). The I–V results demonstrate that the memory performances of the devices bent at different radii were similar to those of the device in its flat state, indicative of strong bending stability. The LRS/HRS current ratios of the devices after bending at radii of 20 and 10 mm were approximately 7.67 × 102 and 1.08 × 102, as shown by the orange and the green circles in Fig. 3(a), respectively. Because the bending of the device might break the ITO electrode due to its fragility, resulting in a remarkable decrease in the LRS current, the LRS/HRS current ratio for the curving device should be reduced in comparison with that before bending24. The PEDOT:PSS film was used to improve the stability of the device when suffered to mechanical bending. The PEDOT:PSS thin film was used to improve the stability of the device while it was being subjected to repeated mechanical bending. As is well known, the poor wettability of polymer layers on ITO electrodes can lead to poor stability of the device because of an unfavorable disparity in the surface energy25. Especially, the repetitive mechanical curving could cause the device’s performance to deteriorate. Therefore, a modified layer between the ITO electrode and the active film is important to the improvement of the stability of flexible devices. The LRS/HRS ratio for the device without the PEDOT:PSS layer decreased under repeated bending, as shown in Fig. 3(b). However, the device with the PEDOT:PSS layer could be stably operated under repeated bending without any noticeable degradation. Figure 3(b) shows the endurance reliability of the device after bending. The device could be repetitively operated without any noticeable variation, regardless of bending, indicating that the electrical characteristics of the device were very stable. Figure 3(c) show the retention performances of the device after bending. The device maintains the LRS/HRS ratio for at least 1 × 104 s after bending, indicating that, regardless of bending, the device was very reliable, even for lengthy operations.
(a) Current-voltage curves for the Al/PI:mica/PEDOT:PSS/ITO/PEN devices for bending radii of 0, 10, and 20 mm. (b) Endurance characteristics as a function of the number of bending cycles of the device with and without PEDOT:PSS layer, respectively. (c) Endurance characteristics after bending of the Al/PI:mica/PEDOT:PSS/ITO/PEN devices at a reading voltage of 1 V. (d) Retention characteristics after bending of the Al/PI:mica/PEDOT:PSS/ITO/PEN devices at a reading voltage of 1 V.
The device was repeatedly bent 30 times at different angles in order to further investigate characteristics of the flexible memristive device, and the I–V characteristics after bending were compared with those before bending (flat state). Figure 4(a) presents the geometry of the device when it is bent, where R is the bending radius, D is the thickness of the device, θ is the central angle, and L is the distance of the line connecting the two endpoints, which is the chord. The bending angle can be determined from the value of L after bending, as shown in Fig. 4(b,c) shows that the electrical properties of the device did not vary significantly as a result of its being bent. Figure 4(d) shows the distribution of the LRS/HRS ratios for 30 devices with bending different bending angles.
(a) Schematic illustration of the flexible ITO-coated PEN substrate, where θ is the corresponding central angle after bending. (b) Photographs of the Al/PI:mica/PEDOT:PSS/ITO/PEN devices being bent. (c) Current-voltage curves for the devices after bending were compared with those before bending (flat state). (d) Bending-angle distribution of the LRS/HRS ratios for the Al/PI:mica/PEDOT:PSS/ITO/PEN devices.
Several conduction models, as determined from fittings of the I–V curves on a log-log scale, can be used to clarify the carrier transport and memory mechanisms of the memristive device26, and Fig. 5(a,b) show the results of such fittings. When a set bias voltage was applied to the device, the device switched to the LRS, as shown in Fig. 5(a). The carrier transport mechanism of the device under negative bias voltage exhibited a linear relationship between I and V, indicative of Ohmic conduction. Thus, one can speculate that a conduction filament was formed in the PI:mica layer when the device stayed in the LRS27. However, the carrier transport mechanisms in the HRS were found to be related to both Ohmic conduction and space-charge-limited-current (SCLC) conduction. The slope of the fitting curve at low voltage for the HRS was approximately 1, as shown in Fig. 5(b), indicative of Ohmic conduction. However, the charge transport mechanism under low applied bias voltage was controlled by thermally generated free electrons, with the number of electrons injected from the electrode increasing with increasing electric field. Therefore, the carrier transport mechanism is dominantly affected by the injected electrons, resulting in their capture in trap sites. As a result, the current increased rapidly in a manner consistent with Child’s square law (I~V2). From the Ohmic region to the Child’s square region, the threshold voltage coincides with a transition from a trap-unfilled state to a trap-filled state28,29. Thus, immediately after the transition to the HRS, the charge transport mechanism exhibits a SCLC conduction behavior, with a slope of approximately 2, because some electrons remain trapped.
The set/reset operation mechanisms of the memristive device based on the charge-trapping mechanism are illustrated in Fig. 6(a–d). One should note that the mica nanosheets employed in this work had layer numbers ranging from 1 to 3 and bandgap energies ranging from 2.5 to 3.2 eV14. The trapping procedure corresponds to the memory process. The mica nanosheets act as electron trapping sites because the energy level of the conduction band for the mica nanosheets is lower than the lowest unoccupied orbital (LUMO) level of the PI layer, as shown in Fig. 6(a). The electrons emitted from the Al electrode in the HRS are partly captured in the mica nanosheets as trapped electrons, so the HRS current of the device at low voltages can be attributed to the SCLC process, as shown in Fig. 6(b)30,31,32. When higher voltages are applied, the number of injected electrons increases, and more electrons are captured by the mica nanosheets. As a result, the electron occupation probability for the mica increases as the Fermi level shifts to the LUMO level of the PI layer30,31,32. When the trap sites are fully occupied by electrons, the device switches from the HRS to the LRS, as shown in Fig. 6(c)33. The LRS current is attributed to the Ohmic process because of the trap-filled state and the possible presence of filamentary channels34. Even after the applied voltage is removed, the device remains in the LRS, indicative of non-volatility. When a positive voltage is applied, the device remains in the LRS until the reset voltage approaches 3 V. When that happens, the electrons trapped in the mica are emitted due to the positive voltage, as shown in Fig. 6(d), which corresponds to the erase process in the memory33.
Conclusion
Flexible memristive devices based on PI:mica nanocomposites were investigated due to their superior mechanical flexibility. The bistable characteristics of the memristive devices were investigated in order to understand their stabilities and conduction mechanisms. The mica nanosheets embedded in the PI layer enhanced the resistive switching characteristics. The LRS/HRS current ratio for the devices before bending was 4.28 × 103, and the LRS/HRS current ratios after bending at radii of 20 and 10 mm were 7.67 × 102 and 1.08 × 102, respectively. The endurance and the retention results before and after bending demonstrated that the flexible devices were stable and reliable. According to the fittings of the I–V curves, the carrier transport mechanism in the LRS could be attributed to Ohmic conduction and those in the HRS to Ohmic and SCLC behaviors. Furthermore, the mechanisms of the devices could be explained by using an energy band diagram. These results indicate that mica nanosheets should be useful for potential applications in flexible memristive devices.
References
Kim, T. W., Yang, Y., Li, F. & Kwan, W. L. Electrical memory devices based on inorganic/organic nanocomposites. NPG Asia Materials 4, e18 (2012).
Wu, C., Kim, T. W., Choi, H. Y., Strukov, D. B. & Yang, J. J. Flexible three-dimensional artificial synapse networks with correlated learning and trainable memory capability. Nat. Commun. 8, 752 (2017).
Wu, C., Kim, T. W., Li, F. & Guo, T. Wearable electricity generators fabricated utilizing transparent electronic textiles based on polyester/Ag nanowires/graphene core–shell nanocomposites. ACS Nano 10, 6449–6457 (2016).
Burgt, Y. V. et al. A non-volatile organic electrochemical device as a low-voltage artificial synapse for neuromorphic computing. Nat. Mater. 16, 414–418 (2017).
Kim, D. H., Kim, W. K., Woo, S. J., Wu, C. & Kim, T. K. Highly-reproducible nonvolatile memristive devices based on polyvinylpyrrolidone: graphene quantum-dot nanocomposites. Org. Electronics. 51, 156–161 (2017).
Wu, C. et al. Mimicking classical conditioning based on a single flexible memristor. Adv. Mater 29, 1602890 (2017).
Liu, Q. et al. Controllable growth of nanoscale conductive filaments in solid-electrolyte-based ReRAM by using a metal nanocrystal covered bottom electrode. ACS Nano 4, 6162–6188 (2010).
Chen, X., Zhou, Y., Roy, V. A. L. & Han, S. T. Evolutionary metal oxide clusters for novel applications: toward high-density data storage in nonvolatile memories. Adv. Mater. 30, 1703950 (2018).
Kim, D. H. et al. Flexible memristive device based on InP/ZnSe/ZnS core-multishell quantum dot nanocomosites. ACS Appl. Mater. Interfaces 10, 14843–14849 (2018).
Liu, J. et al. Preparation of MoS2-polyvinylpyrrolideone nanocomposites for flexible nonvolatile rewriteable memory devices with reduced graphene oxide electrodes. Small 10, 3517–3522 (2012).
Schniepp, H. C. et al. Functionalized single graphene sheets derived from splitting graphite oxide. J. Phys. Chem. B 110, 8535–8539 (2006).
Hu, K., Kulkarni, D. D., Choi, I. & Tsukruk, V. V. Graphene-polymer nanocomposites for structural and functional applications. Prog. Polym. Sci. 39, 1934–1972 (2014).
Zhuang, T. Z. et al. Rational integration of polypropylene/graphene oxide/nafion as ternary-layered separator to retard the shuttle of polysulfides for lithium-sulfur batteries. Small 12, 381 (2016).
Kim, S. S. et al. Tunable bandgap narrowing induced by controlled molecular thickness in 2D mica nanosheets. Chem. Mat. 27, 4222–4228 (2015).
Kim, W. K., Wu, C., Lee, D. U., Kim, H. W. & Kim, T. W. Enhancements of the memory margin and the stability of an organic bistable device due to a graphene oxide:mica nanocomposite sandwiched between two polymer(9-vinylcarbazole) buffer layers. Appl. Surf. Sci. 429, 231–236 (2018).
Wachsman, E. D. & Frank, C. W. Effect of cure history on the morphology of polyimide: Fluorescence spectroscopy as a method for determining the degree of cure. Polymer 29, 1191–1197 (1988).
Tseng, I. H., Laio, Y. F., Chiang, J. C. & Tsai, M. H. Transparent polyimide/graphene oxide nanocomposite with improved moisture barrier property. Mater. Chem. Phys. 136, 247–253 (2012).
Wang, J. Y. et al. Preparation and properties of graphene oxide/polyimide composite films with low dielectric constant an ultrahigh strength via in situ polymerization. J. Mater. Chem. 21, 13569–13575 (2011).
Kim, N. R. et al. Highly conductive PEDOT:PSS nanofibrils induced by solution-processed crystallization. Adv. Mater. 26, 2268–2272 (2014).
Zhou, L. et al. Recent advances of flexible data storage devices based on organic nanoscaled materials. Small 14, 1703126 (2018).
Liu, D. et al. Flexible all-inorganic perovskite CsPbBr3 nonvolatile memory device. ACS Appl. Mater. Interfaces 9, 6171–6176 (2017).
Liao, W. H. et al. Effect of molecular chain length on the mechanical and thermal properties of amine-functionalized graphene oxide/polyimide composite films prepared by in situ polymerization. ACS Appl. Mater. Interfaces. 5, 869–877 (2013).
Wu, C., Li, F., Guo, T. & Kim, T. W. Controlling memory effects of three-layer structured hybrid bistable devices based on graphene sheets sandwiched between two laminated polymer layers. Org. Electronics. 13, 178–183 (2012).
Zhou, Y., Han, S. Y., Xu, Z. X. & Roy, V. A. L. The strain and thermal induced tunable charging phenomenon in low power flexible memory arrays with a gold nanoparticle monolayer. Nanoscale 5, 1972 (2013).
Kim, W. K., Wu, C. & Kim, T. K. Effect of aPEDOT:PSS modified layer on the electrical characteristics of flexible memristive devices based on graphene oxide:polyvinylpyrrolidone nanocomposites. Appl. Surf. Sci. 444, 65–70 (2018).
Zhou, Y. et al. Ultra-flexible nonvolatile memory based on donor-acceptor diketopyrrolopyrrole polymer blends. Sci. Rep. 5, 10683 (2015).
Son, D. I. et al. Flexible organic bistable devices based on graphene embedded in an insulating poly(methylmethacrylate) polymer layer. Nano Lett. 10, 2441–2447 (2010).
Chen, X., Hu, W., Wu, S. & Bao, D. Stabilizing resistive switching performances of TiN/MgZnO/ZnO/Pt heterostructure memory devices by programming the proper compliance current. Appl. Phys. Lett. 104, 043508 (2014).
Chen, X., Hu, W., Li, Y., Wu, S. & Bao, D. Complementary resistive switching behaviors evolved from bipolar TiN/HfO2/Pt device. Appl. Phys. Lett. 108, 053504 (2016).
An, H., Kim, W. K., Wu, C. & Kim, T. W. Highly-stable memristive devices based on poly (methylmethacrylate): CsPbCl3 perovskite quantum dot hybrid nanocomposites. Org. Electronics. 56, 41–45 (2018).
Pranab, K. S., Snigdha, B., Manoj, P. & Asim, R. Incorporation of SnO2 nanoparticles in PMMA for performance enhancement of a transparent organic resistive memory device. RSC Adv. 5, 105661–105667 (2015).
Zhou, Y. et al. Real-time storage of thermal signals in organic memory with floating core-shell nanoparticles. J. Mater. Chem. C. 5, 8415 (2017).
Wu, C., Li, F. & Guo, T. Efficient tristable resistive memory based on single layer graphene/insulating polymer multi-stacking layer. Appl. Phys. Lett. 104, 183105 (2014).
Tian, H. et al. Extremely low operating current resistive memory based on exfoliated 2D perovskite single crystals for neuromorphic computing. ACS Nano 10, 12247–12256 (2017).
Acknowledgements
This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (2016R1A2A1A05005502).
Author information
Authors and Affiliations
Contributions
M.K.C., C.W. and T.W.K. conceived the project, and M.K.C. designed and performed the experiments and collected the data. M.K.C., W.K.K., C.W., S.S., H.W.K. and T.W.K. analyzed and discussed the data. All authors discussed the results and contributed to the writing of the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Choi, M.K., Kim, W.K., Sung, S. et al. Flexible memristive devices based on polyimide:mica nanosheet nanocomposites with an embedded PEDOT:PSS layer. Sci Rep 8, 12275 (2018). https://doi.org/10.1038/s41598-018-30771-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-30771-5
- Springer Nature Limited
This article is cited by
-
Neuromorphic properties of flexible carbon nanotube/polydimethylsiloxane nanocomposites
Advanced Composites and Hybrid Materials (2023)
-
Highly Stable and Flexible Memristive Devices Based on Polyvinylpyrrolidone: WS2 Quantum Dots
Scientific Reports (2020)