Abstract
Red mud as a waste material is produced in large quantities by the aluminum industry. Heat activation has been used to enhance sorption capacity of red mud for its beneficial reuse as an effective sorbent. In this study, heat-activated red mud (HARM) was investigated for its Cd(II) sorption capacity under various process conditions (Cd concentration, pH and contact time) using response surface methodology (RSM). Analysis with RSM identified pH as the most important process parameter. The positive correlation between higher pH and greater Cd(II) sorption was likely due to: (i) decreased proton competition with Cd(II) for sorption sites at higher pH; (ii) enhanced sorption via ion exchange by monovalent Cd species from hydrolysis at higher pH; and (iii) improved thermodynamics of sorption at higher pH as protons are being released as products. Further analysis indicated the sorption process was thermodynamically favorable with a negative change in Gibbs free energy. Additionally, the sorption process exhibited a positive change in enthalpy, indicative of endothermic nature of sorption; this is consistent with sorption increase at higher temperature. These findings provide needed insight into the mechanisms underlying Cd(II) sorption by HARM for more effective applications of heat-activated red mud as sorbents for Cd(II) removal.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Red mud is an abundant solid waste generated during the caustic digestion of bauxite ores with sodium hydroxide at increasing temperature and pressure for the production of alumina1. Red mud has shown characteristics as a promising sorbent due to its high surface reactivity2 and heterogeneous mineral composition1,3,4. Many studies have confirmed the sorption capacity of red mud for some anions such as phosphate5,6, fluoride7, and boron8. More importantly, red mud has been shown to be potentially effective in the sorptive removal of many cationic contaminants, particularly for certain toxic heavy metals9,10,11.
Cadmium (Cd) has been exerting a great pressure on the environment due to its increasingly higher input flux from anthropogenic sources like battery, alloy, and metal plating industries12,13. Moreover, Cd(II) is highly toxic to human. Intake of Cd(II) through drinking water damages the vital body organs like lungs14 and kidneys, which are two of the primary sites of injury after chronic Cd(II) exposure15. Cd(II) intake may further increase the risk of death from cancer, cardiovascular disease, and Alzheimer’s disease15; therefore it is necessary to develop effective remediation methods for Cd(II) contamination12. Sorption has proven to be an effective and economical method for the removal of Cd(II) in the aqueous environment12,16; thus using mineral wastes, red mud, as sorbents to remediate toxic Cd(II) should be a promising strategy.
Given the potential of red mud in the sorptive removal of heavy metals, efforts have been made to improving the sorption capacity of red mud. Heat activation has been proven to be an effective strategy to enhance the sorption capacity1,17. The effectiveness of heat activation in enhancing sorption performance has been conducted on a number of other heavy metals such as nickel18 and manganese19. Based on these studies, process parameters including pH, contact time, and adsorbate concentration have been shown to have a major influence on the sorption of heavy metals by heat-activated red mud. Due to the considerable differences in the investigated sorbates, as well as in the characteristics of starting red mud samples, the effects of process parameters on sorption were different; so it is necessary to study the Cd(II) sorption by heat-activated red mud which has seldom been reported.
The objectives of this work are to characterize Cd(II) sorption by heat-activated red mud using a mathematical model developed by response surface methodology (RSM) and to predict sorption behavior under various process conditions.
Materials and Methods
Preparation and characterization of heat-activated red mud
The original red mud samples were taken from the red mud disposal site of an alumina refinery in China. Samples were air-dried before passing through a 140-mesh sieve. Then 10 g portions were heated in an electrical furnace (Thermolyne, U.S.) at 200 °C, 400 °C, 500 °C, 800 °C and 900 °C for 3 hours, respectively. Since the result of Cd(II) sorption tests showed that the most effective red mud sample was the one obtained by heating at 500 °C (detailed results were provided in Results and Discussion section), denoted as HARM, samples heated to this temperature were selected for next analyses.
The mineralogical composition of HARM was studied by X-ray diffraction (XRD) analysis using a D2 PHASER Diffractometer with CuKα radiation, and a step/time scan mode of 0.75°/1 min. The crystalline phase was identified by comparing the XRD patterns with standards available in the powder diffraction file (PDF2) database. XPS data were acquired with a Phoibos 150 with Al Ka radiation (SPECS, U.S.). The binding energy correction due to the charging effects has been based on the main contribution of the carbon C1s line, assuming it corresponds to adventitious carbon at 284.8 eV. Scanning electron microscopy (SEM) was performed using a Zeiss LEO 1525 SEM. Particle size analysis of the components of HARM was obtained using the laser diffraction method with a Malvern Mastersizer S instrument, long bench with 300RF lens. The specific surface area of HARM was determined by Brunauer–Emmett–Teller (BET)/N2 adsorption method using an automatic specific surface area measurement (Belsorp-max, MicrotracBEL, Japan). To determine the pH of HARM, 1 g of air-dried HARM was mixed with 5 mL of deionized water for 5 minutes and left to stand for 30 minutes. The supernatant was used to measure pH with a combination pH electrode (Oakton pH 700, U.S.). The batch equilibrium method was used for the determination of the point of zero charge (pHPZC) of HARM20. 0.1 g of dried HARM was shaken at 250 rpm in a glass vial for 24 h with 20 mL of 0.1 mol∙L−1 NaCl solution of a known initial pH. Initial pH values of solution were adjusted in a wide pH range (from 1 to 11) by adding either 0.1 mol∙L−1 HCl or 0.1 mol∙L−1 NaOH. The pHPZC values were determined using the plateau of a graph of the final pH against the initial pH.
Sorption experiments
Sorption was tested in batch conditions by shaking suspensions of 0.01 g of red mud and 20 mL of CdCl2 solution in closed glass bottles on a horizontal laboratory shaker (New Brunswick Scientific Co., Inc, U.S.) at a constant speed of 250 rpm. Each process parametric sorption experiment was tested in triplicate. After each set of sorption experiments, the liquid phase was separated from the solid residue by centrifugation (SORVALL RC 6, Thermo Scientific, U.S.) for 15 min at 14000 rpm, and the remaining Cd(II) concentrations (Ce) were determined by ICP-OES (iCAP 7000, ThermoFisher Scientific, U.S.). Sorption efficiency was evaluated by calculating the amount of metal sorbed (qe, mg∙g−1) (Equation 1).
where V (L) is solution volume, m (g) is red mud sample mass, C0 (mg∙L−1) is initial Cd(II) concentration, and Ce (mg∙L−1) is equilibrium Cd(II) concentration in the solution.
Effect of heat treatment
The maximum Cd(II) sorption capacities of original red mud and red mud heat-treated at different temperatures (200–900 °C) were evaluated through batch sorption experiments. The sorbent dosage, initial pH, temperature, initial Cd(II) solution concentration, and contact time were 0.5 g∙L−1, 6, 20 °C, 200 mg∙L−1 and 24 hours, respectively.
Effect of pH
The effect of initial pH was examined using HARM at 20 °C and a contact time of 24 h. The initial Cd(II) concentration was 10 mg∙L−1, and initial pH of the suspension was adjusted between 2–8 at the beginning of the experiment by adding a negligible volume of 1 mol∙L−1 or 0.1 mol∙L−1 HCl. After sorption, the solid phase was separated from the solution by centrifugation, and final pH value was measured in the supernatant.
Effect of Cd(II) concentration and reaction temperature
The impacts from the Cd(II) concentration and the reaction temperature were evaluated at an initial pH 6, and contact time of 24 h. Batch sorption experiments were conducted at 20 °C, 30 °C and 40 °C with varying initial Cd(II) concentrations ranging from 1 mg∙L−1 to 227 mg∙L−1. The final pH was measured as the last section.
Response surface methodology modeling
Response surface methodology (RSM) is a mathematical model used to predict sorption behavior and to evaluate the relative importance and interaction of each parameter21. In this study, the 3-factor 3-level Box-Behnken experimental design (BBD) was applied in the RSM model. The BBD design was capable of streamlining experimental setup22. Table 1 shows the results of sorption experiments which were conducted on the base of BBD. The analysis of variables was evaluated by Design-Expert V10.0 (Stat-Ease Inc., U.S.). The quadratic equation model was used in RSM modeling (Equation 2).
where Y is the process response, k is the number of the patterns, i and j are the index numbers for pattern, β0 is the offset term, βi is the linear effect of the input factor xi, βii is the quadratic effect of input factor xi, and βij is the interaction effect23.
Results and Discussion
Effect of heat treatment on red mud Cd(II) sorption capacity
The maximum sorption capacities of all red mud samples in this study were evaluated through batch sorption experiments. The sorbent dosage, initial pH and temperature were 0.5 g∙L−1, 6 and 20 °C, respectively. In order to reach maximum sorption, the initial Cd(II) solution concentration and contact time were fixed at the high level (200 mg∙L−1 and 24 hours, respectively). According to Fig. 1, compared with other red mud samples in this work, red mud heat-activated at 500 °C (HARM) exhibited the highest sorption capacity. From Table 2, compared with other industrial wastes tested under room temperature (20–25 °C) in previous literature, HARM showed higher Cd(II) sorption capacity, although the sorption capacity of HARM was lower than the Cd(II) sorption capacities of some synthetic materials or/and the modified typical sorbents such as activated carbon and metal oxides24. So, HARM was selected for further investigations in this study.
The maximum Cd(II) sorption capacities of original red mud (RM), red mud heat-activated at 500 °C (HARM) and red mud heat-treated at 200, 400, 800, 900 °C (RM200–RM900). The means are not significantly different from each other in columns labeled with the same lowercase letters (ANOVA, LSD test, p < 0.05).
Characteristics of heat-activated red mud
The mineralogical composition of HARM was investigated using XRD analysis (Fig. 2). The main crystalline phases were determined to be hematite (Fe2O3) and sodalite (Na8Si6Al6O24Cl2), which was consistent with findings from previous studies on the XRD patterns of heat-treated red mud samples18,25. Additional peaks detected in the XRD diffractogram also indicated the presence of anatase (TiO2) and quartz (SiO2) phases in the HARM. As shown in XPS spectrum of HARM (Fig. 3), Fe, Al, O, Na, C, Ti and Si were detected on the surface of RM500, which was consistent with XRD analyzed above (Fig. 2). The morphologies of HARM particles were investigated by scanning electron microscopy (SEM) shown in the Fig. 4. HARM contained various particles with different size and shape (Fig. 4). Particle size analysis of HARM showed that over 90% of particles had a diameter smaller than 50 μm (Table 3). Based on soil texture classification26, this HARM could be classified as a silty clay. Table 3 shows the specific surface area of 32.77 m2∙g−1, and mean pore diameter and total pore volume were 5.37 nm and 44 mm3∙g−1, respectively. The HARM samples tested in this study exhibited high alkalinity with a pH of approximately 10.9. The pHPZC value for HARM was approximately 10.6 which was determined from the plateau region of the initial pH vs. final pH plot (Supplementary Fig. S1).
Modeling by heat-activated red mud with response surface methodology (RSM)
Model development with RSM and statistical evaluation
The sorption of Cd(II) was expected to be impacted by the Cd(II) concentration, pH, and contact time for the sorption process. It is expected that Cd(II) concentration and pH will deviate with sorption process. For modeling, initial Cd(II) concentration and initial pH were used. Therefore, initial Cd(II) concentration and initial pH would be referred to as Cd(II) concentration and pH, respectively. A regression model was developed to investigate the effect of these three parameters on the Cd(II) sorption behavior to heat-activated red mud using the response surface methodology (RSM). A Box-Behnken experimental design (BBD) was used to develop the experimental matrix of 15 sorption experiments with Cd(II) concentration, pH, and contact time as the independent variables (Table 4). Application of RSM yielded the following equation to describe sorption of Cd(II) to heat-activated red mud (Equation 3):
where Y is the predicted amount of Cd(II) sorbed (mg∙g−1); X1, X2, and X3 represent the three independent variables — Cd concentration (mg∙L−1), pH, and contact time (h), respectively.
The analysis of variance (ANOVA) was conducted to test the significance of the fit of the established quadratic model for the experimental data, and significant effect of the terms in the model on the response (Table 5). ANOVA is a statistical technique that subdivides the total variation in a set of data into component parts associated with specific sources of variation for the purpose of testing hypotheses on the parameters of the model27. The ANOVA of the regression model (Equation 3) indicated that the model could explain a considerable amount of the variation in the dependent variable (the amount of Cd(II) sorbed) with 95% certainty, as was evident from the high F value (30.16) which was higher than the tabulated F value (F0.05, 9, 5 = 4.77) at the 5% level (Table 5). Further, the p-value (0.0008) was lower than 0.05, indicating that this quadratic model was statistically significant27,28. The coefficient of determination (R2) (Equation 4) describes the amount of variation in the observed responses that can be explained by the model29. In this case, R2 was 98.19% indicating that only 1.81% of total variations could not be explained by this model.
where SS is sum of squares.
Validation of Cd(II) sorption model
To further validate the Cd(II) sorption model (Equation 3) developed with RSM, additional sorption experiments were conducted to compare actual Cd(II) sorption performance with model prediction (Supplementary Table S1). The distributions of experimental results and model predictions were close to normal based on the Kolmogorov-Smirnov Test30; therefore a two-sample, unpaired t-test was conducted to test the difference between experimental results and those predicted by the sorption model (Equation 3). Since p > α (0.93 > 0.05), the experimental results and model predictions were not considered to be significantly different22, indicating the sorption model (Equation 3) provided a good fit to experiment results. The validity of the sorption model was also evident from the strong correlation between experimental result and model prediction according to Pearson’s correlation analysis (Fig. 5). Further, the model predictions and experimental results were very similar in value (Fig. 5), suggesting the accuracy of the sorption model in describing Cd(II) sorption behavior.
Correlation between Cd(II) sorption experimental result and model prediction. The diagonal line indicates equality between experimental result and model prediction. qe is the amount of Cd(II) sorbed. r (correlation coefficient) is a parameter of Pearson’s correlation analysis between experimental result and model prediction. **Indicates correlation is significant at 0.01 level.
Effect of model components and their interactions on Cd(II) sorption
X1, X2, X3, X1X2, X1X3, X12, X22 and X32 were significant model terms based on the p-value of each component (Table 5). The sum of square (SS) of each component obtained from ANOVA quantifies the importance of each component in the sorption process. As the value of the SS increases, the significance of the corresponding component in the undergoing process also increases29. Based on the SS obtained from the ANOVA (Table 5), the percent contribution of each RSM model component to Cd(II) sorption (PC) was calculated (Equation 5):
where SSi is the sum of squares of i component of the model, and c is the total number of components of the model.
From examining the PC values of the components, the first-order term showed the highest level of significance, followed by interaction and quadratic terms (Fig. 6). pH was dominant with a contribution of 36.9%, followed by Cd(II) concentration and contact time (Fig. 6).
To further explore the effects of pH on the Cd(II) sorption behavior, contour plot was carried out (Fig. 7). Contour plots of experimental factors can only show two factors at a time, the other factor which was not included in the figure was held at the center level (Cd(II) concentration = 102 mg∙L−1). In general, pH had a positive correlation with Cd(II) sorption. In the pH ranged from 2 to 4, Cd(II) sorption capacity was relatively low. However, the considerable increase in sorption was observed at higher pH. To elucidate the mechanism of the effect of pH on the sorption, other batch sorption experiments and chemical analysis were conducted.
The effect of pH on Cd(II) sorption
The batch sorption experiments were conducted to further confirm and try to explain the effect of pH on the Cd(II) sorption by HARM. Initial Cd(II) concentration, contact time, HARM dosage and reaction temperature were 10 mg∙L−1, 24 h, 0.5 g∙L−1 and 20 °C, respectively. The initial pH was adjusted between 2–8. From Fig. 8, the amount of Cd(II) sorbed onto HARM (qe) increased with an increase of pH was consistent with the RSM result. This is in agreement with previous research on the effect of pH on the sorption of metal cations to red mud14,18,19 and other adsorbents31,32. At lower pH, the amount of Cd(II) sorbed was relatively low due to competitive sorption between more H+ and Cd(II) cations (Fig. 8). However, at higher pH, with less H+ in the solution, the competitive sorption was weak, contributing to a higher sorption efficiency.
Moreover, the distribution of the Cd(II) speciation in the solution which is controlled by pH also has an effect on Cd(II) sorption onto HARM. Using appropriate Cd2+ and Cl− concentrations, Visual MINTEQ software (EPA, U.S.) was applied for the calculation of the speciation of Cd(II) vs. pH (Fig. 9). At higher pH (pH > 8), the hydrolysis of Cd2+ initiates contributing to the increase in the percentage of monovalent Cd species (CdCl+ and CdOH+) (Fig. 9). As a result, sorption efficiency was enhanced as greater Cd(II) sorption occurred via ion exchange, when equilibrium pH (final pH) exceeded 8 (Fig. 8). For further verification of this result, the effect of pH on ion exchange process during Cd(II) sorption, and the mechanism of ion exchange were explored based on the number of exchangeable metal cations released from HARM when the Cd(II) was sorbed onto HARM with different pH. Two sorption experiments were conducted at 24 h (contact time), 0.5 g∙L−1 (dose), 20 °C (reaction temperature), and 200 mg∙L−1 (initial Cd(II) concentration). The initial pH values of these two sorption experiments were 6 and 8, respectively where the corresponding final pH values were 7 and 9. In order to suppress the effect of pH on HARM dissolving, two control experiments were carried out in the absence of Cd(II) with the same experimental procedure and the same final pH (7 and 9, respectively) as the sorption experiments. Distilled water (DI water) was used as reference instead of Cd(II) solution. After equilibration, the mixtures HARM/DI water and HARM/Cd(II) solution were centrifuged, and the concentrations of cations including Na+, Ca2+, K+, Mg2+ and Cd(II) in the supernatant were recorded (Table 6). The results showed K+ and Mg2+ were not detected. Compared with control, it was observed that Cd(II) sorption was accompanied by the stoichiometric release of the Na+ and Ca2+ (Table 6). The concentrations of Na+ and Ca2+ released on the Cd(II) uptake by HARM were used to calculate the number of positive charges released through ion exchange (Equation 6).
The number of positive charges released at final pH 7 and it at final pH 9 were similar (0.027 and 0.029 mmol∙g−1, respectively). However, at pH 7, Cd2+ cations are prevalent ( > 80%), and at pH 9, the fraction of Cd2+ cations decreased, and the percentage of monovalent Cd species (CdCl+ and CdOH+) increased (Fig. 9) contributing to the stronger ion exchange. So, it could be concluded that the ion exchange process was stronger at higher pH due to the increase in the percentage of monovalent Cd species which contributed to the higher sorption capacity shown in Table 6. From Fig. 9, the precipitation of Cd(OH)2 could contribute to the Cd ion removal, where equilibrium pH (final pH) was greater than 9.
The effect of pH on the Cd(II) sorption can be interpreted through other batch sorption experiments (1.15 mg∙L−1–227.34 mg∙L−1 initial Cd(II) concentration, 0.5 g∙L−1 HARM dosage, 24 h contact time, 6 initial pH and 20 °C reaction temperature). The results indicated that Cd(II) sorption onto HARM (qe) increased with initial Cd(II) concentration increase, then reached saturation sorption capacity (Fig. 10a). The increased sorption capacity of Cd(II) was followed by considerable proton release, resulting in a decrease in final pH (Fig. 10b). This demonstrated that based on sorption capacity increase, more H+ on the surface of HARM was replaced by Cd2+ through specific cation sorption18. Specific sorption can be expressed by surface complexation model demonstrating that Cd2+ could be sorbed to the hydroxyl functional groups of red mud and the H+ could be replaced by Cd ions33,34,35 (Eqs 7 and 8).
and/or
where SOH represents the functional groups of Fe– and Al–oxyhydroxide mineral phases in red mud.
Equations 7 and 8 indicated another reason for the positive relationship between higher pH and greater sorption capacity (Fig. 8). At lower pH, more H+ in the solution suppressed the specific sorption process through increasing in ΔG of the specific sorption.
The effect of reaction temperature on Cd(II) sorption
In order to elaborate the feasibility of the sorption process, thermodynamic studies were carried out based on the effect of reaction temperature on the Cd(II) sorption at different initial Cd(II) concentration levels. Moreover, isotherm study at different reaction temperature could confirm the feasibility of the sorption, while also provide a mechanistic understanding of sorption.
In isotherm and thermodynamic studies, different initial Cd(II) concentrations (1.15 mg∙L−1–227.34 mg∙L−1) were used in conjunction with a 24 h contact time, an initial pH of 6, a HARM dose of 0.5 g∙L−1, and three different temperatures (20 °C, 30 °C and 40 °C) to perform the sorption experiments. At higher initial Cd(II) concentrations, increasing reaction temperature could enhance the sorption capacity (Fig. 11); however at lower initial concentrations (C0 < 11 mg∙L−1), the amount of Cd(II) sorbed (qe) was independent of reaction temperature. This may be because when compared with the lower Cd(II) sorbates concentration, sorption sites on the surface of HARM were sufficient causing the decrease of sorption enhancement by higher temperature.
The Langmuir isotherm model was used for equilibrium data fitting (Equation 9)36.
where qe (mg∙g−1) and Ce (mg∙L−1) denote the equilibrium concentrations of Cd(II) in the solid and liquid phases, respectively, q0 (mg∙g−1) is the maximum sorption capacity, b (L∙mg−1) is the Langmuir constant related to the sorption energy.
The dimensionless separation factor RL shows the feasibility of the process (Equation 10)37.
The RL values lie in the range of 0–1, demonstrating the sorption is a favorable process14,38.
The values of q0 and b in the Langmuir isotherm model were evaluated from the slope and intercept of plots of Ce/qe vs. Ce at 20 °C, 30 °C and 40 °C (Supplementary Fig. S2) (Table 7). The Langmuir model had a higher regression coefficient (R2), indicating that sorption corresponds to a monolayer formation of Cd(II) onto the HARM surface14 (Table 7). The maximum sorption capacity (q0) and the sorption capacity at unit concentration (kF) increased with increasing temperature, indicating the endothermic nature of sorption. The calculated RL values were in the range of 0–1, indicating favorable sorption of Cd(II) onto HARM39.
The change in free energy (ΔG0 (kJ∙mol−1)) was calculated using Langmuir constant, b (Equation 11). The values of change in enthalpy (ΔH0 (kJ∙mol−1)) and entropy (ΔS0 (kJ∙mol−1)) were calculated from the intercept and slope of the linear plot of ΔG0 vs. T (Equations 11 and 12) (Supplementary Fig. S3). Negative ΔG0 values indicated the spontaneous nature of the sorption of Cd(II) onto HARM (Table 8). The positive ΔH0 value confirmed the endothermic nature of the process while the positive value of ΔS0 indicated an increase in the degree of freedom of this adsorbing system, which may be attributed to the cation exchange process and specific sorption process. Because during these processes the amount of Na+ and H+ released was more than the amount of Cd2+ sorbed by red mud40, however there was no remarkable change in the structure of HARM during the sorption process because ΔS0 was not considerable14.
where R is the universal gas constant (8.314 J∙mol−1∙K−1), T is temperature in Kelvin, the Langmuir constant, b is simply recalculated as dimensionless.
Conclusion
In this study, the heat-activated red mud (HARM) sorbent was prepared and characterized by XRD and other physicochemical methods. To characterize the Cd(II) sorption behavior of HARM under various process conditions, a three-factor, three-level Box-Behnken experimental design combined with response surface methodology (RSM) was employed to develop a mathematical model. Based on the RSM result, initial pH was identified as the most important process parameter and had a positive correlation with sorption. Greater Cd(II) sorption exhibited at higher pH could be attributed to weaker H+ competition with Cd(II) cations for HARM sorption sites at lower H+ concentration. It might also be the result of enhanced Cd(II) sorption via ion exchange due to increases in monovalent Cd species from hydrolysis at higher pH. Moreover, less H+ in the solution enhanced specific sorption through decreasing ΔG of the specific sorption. Isotherm and thermodynamic studies demonstrated that sorption was a favorable and spontaneous process. A positive ΔH0 value indicated the endothermic nature of the process, which was consistent with the increase in sorption at higher temperature; however the sorption was independent of reaction temperature at lower initial Cd concentrations (C0 < 11 mg∙L−1). It may be because when compared with the lower Cd(II) sorbates concentration, sorption sites on the surface of HARM were sufficient, causing the decrease of sorption enhancement by increasing temperature.
Data Availability
All data generated or analyzed during this study are included in this published article and its Supplementary Information file.
References
Wang, S., Ang, H. M. & Tadé, M. O. Novel applications of red mud as coagulant, adsorbent and catalyst for environmentally benign processes. Chemosphere 72, 1621–1635 (2008).
Ahmed, M. J. K. & Ahmaruzzaman, M. A review on potential usage of industrial waste materials for binding heavy metal ions from aqueous solutions. J. Water Process Eng. 10, 39–47 (2016).
Paramguru, R., Rath, P. & Misra, V. Trends in red mud utilization – a review, Mineral Process. Extr. Metall. Rev. 26, 1–29 (2004).
Lopez, E. et al. Adsorbent properties of red mud and its use for wastewater treatment. Water Res. 32, 1314–1322 (1998).
Linh, V. D., Chi, T. D. & Hai, H. T. The comparison of red mud modification by acid and heat for phosphate removal from aqueous solution. Int. J. Innovative Stud. Sci. Eng. Technol. 2, 76–83 (2016).
Tangde, V., Prajapati, S., Mandal, B. & Kulkarni, N. Study of kinetics and thermodynamics of removal of phosphate from aqueous solution using activated red mud. Int. J. Environ. Res. 11, 39–47 (2017).
Çengeloğlu, Y., Kır, E. & Ersöz, M. Removal of fluoride from aqueous solution by using red mud. Sep. Purif. Technol. 28, 81–86 (2002).
Cengeloglu, Y., Tor, A., Arslan, G., Ersoz, M. & Gezgin, S. Removal of boron from aqueous solution by using neutralized red mud. J. Hazard. Mater. 142, 412–417 (2007).
Luo, L. et al. New insights into the sorption mechanism of cadmium on red mud. Environ. Pollut. 159, 1108–1113 (2011).
Smičiklas, I. et al. Effect of acid treatment on red mud properties with implications on Ni(II) sorption and stability. Chem. Eng. J. 242, 27–35 (2014).
Vaclavikova, M., Misaelides, P., Gallios, G., Jakabsky, S. & Hredzak, S. Removal of cadmium, zinc, copper and lead by red mud, an iron oxides containing hydrometallurgical waste. Stud. Surf. Sci. Catal. 155, 517–525 (2005).
Gupta, S. S. & Bhattacharyya, K. G. Removal of Cd(II) from aqueous solution by kaolinite, montmorillonite and their poly (oxo zirconium) and tetrabutylammonium derivatives. J. Hazard. Mater. 128, 247–257 (2006).
Luo, L., Ma, Y. B., Zhang, S. Z., Wei, D. P. & Zhu, Y. G. An inventory of trace element inputs to agricultural soils in China. J. Environ Manage. 90, 2524–2530 (2009).
Khan, T. A., Chaudhry, S. A. & Ali, I. Equilibrium uptake, isotherm and kinetic studies of Cd(II) adsorption onto iron oxide activated red mud from aqueous solution. J. Mol. Liq. 202, 165–175 (2015).
Satarug, S., Vesey, D. A. & Gobe, G. C. Health risk assessment of dietary cadmium intake: do current guidelines indicate how much is safe? Environ. Health Perspect. 125, 284–288 (2017).
Uddin, M. K. A review on the adsorption of heavy metals by clay minerals, with special focus on the past decade. Chem. Eng. J. 308, 438–462 (2017).
Altundoğan, H. S. & Tümen, F. Removal of phosphates from aqueous solutions by using bauxite. II: the activation study. J. Chem. Technol. Biotechnol. 78, 824–833 (2003).
Smiljanić, S., Smičiklas, I., Perić-Grujić, A., Lončar, B. & Mitrić, M. Rinsed and thermally treated red mud sorbents for aqueous Ni2+ ions. Chem. Eng. J. 162, 75–83 (2010).
Chen, H., Zheng, J., Zhang, Z., Long, Q. & Zhang, Q. Application of annealed red mud to Mn2+ ion adsorption from aqueous solution. Water Sci. Tech. 73, 2761–2771 (2016).
Milonjić, S., Ruvarac, A. L. & Šušić, M. The heat of immersion of natural magnetite in aqueous solutions. Thermochim. Acta 11, 261–266 (1975).
Hanrahan, G. & Lu, K. Application of factorial and response surface methodology in modern experimental design and optimization. Crit. Rev. Anal. Chem. 36, 141–151 (2006).
Yetilmezsoy, K., Demirel, S. & Vanderbei, R. J. Response surface modeling of Pb (II) removal from aqueous solution by Pistacia vera L.: Box – Behnken experimental design. J. Hazard. Mater. 171, 551–562 (2009).
Benyounis, K. Y., Olabi, A. G. & Hashmi, M. S. J. Effect of laser welding parameters on the heat input and weld-bead profile. J. Mater. Process. Technol. 164, 978–985 (2005).
Lin, S. et al. Study on the influence of thiolation on the adsorption and magnetic recovery of superparamagnetic nanoadsorbents for Cd2+ removal. Appl. Surf. Sci. 425, 141–147 (2017).
Antunes, M. L. P. et al. Red mud from Brazil: thermal behavior and physical properties. Eng. Chem. Res. 51, 775–779 (2011).
Brown, R. B. Soil texture. (ed. Soil and Water Science Department, University of Florida Cooperative Extension Service, Institute of Food and AgricultureSciences, EDIS) (1998).
Tripathi, P., Srivastava, V. C. & Kumar, A. Optimization of an azo dye batch adsorption parameters using Box – Behnken design. Desalin. 249, 1273–1279 (2009).
Liu, H. L., Lan, Y. W. & Cheng, Y. C. Optimal production of sulphuric acid by Thiobacillus thiooxidans using response surface methodology. Process Biochem. 39, 1953–1961 (2004).
Geyikçi, F., Kılıç, E., Çoruh, S. & Elevli, S. Modelling of lead adsorption from industrial sludge leachate on red mud by using RSM and ANN. Chem. Eng. J. 183, 53–59 (2012).
Lilliefors, H. W. On the Kolmogorov-Smirnov Test for normality with mean and variance unknown. J. Am. Stat. Assoc. 62, 399–402 (1967).
Srivastava, V. C., Mall, I. D. & Mishra, I. M. Equilibrium modelling of single and binary adsorption of cadmium and nickel onto bagasse fly ash. Chem. Eng. J. 117, 79–91 (2006).
Wang, C., Liu, J., Zhang, Z., Wang, B. & Sun, H. Adsorption of Cd(II), Ni(II), and Zn(II) by tourmaline at acidic conditions: kinetics, thermodynamics, and mechanisms. Ind. Eng. Chem. Res. 51, 4397–4406 (2012).
Lackovic, K., Angove, M. J., Wells, J. D. & Johnson, B. B. Modeling the adsorption of Cd (II) onto Muloorina illite and related clay minerals. J. Colloid Interface Sci. 257, 31–40 (2003).
Srivastava, P., Singh, B. & Angove, M. Competitive adsorption behavior of heavy metals on kaolinite. J. Colloid Interface Sci. 290, 28–38 (2005).
Serrano, S., O’Day, P. A., Vlassopoulos, D., García-González, M. T. & Garrido, F. A surface complexation and ion exchange model of Pb and Cd competitive sorption on natural soils. Geochim. Cosmochim. Acta 73, 543–558 (2009).
Langmuir, I. The adsorption of gases on plane surfaces of glass, mica and platinum. J. Am. Chem. Soc. 40, 1361–1403 (1918).
Weber, T. W. & Chakravorti, R. K. Pore and solid diffusion models for fixed‐bed adsorbers. AIChE J. 20, 228–238 (1974).
Gupta, V. K. & Sharma, S. Removal of cadmium and zinc from aqueous solutions using red mud. Environ. Sci. Technol. 36, 3612–3617 (2002).
Mishra, P. C. & Patel, R. K. Removal of lead and zinc ions from water by low cost adsorbents. J. Hazard. Mater. 168, 319–325 (2009).
Crist, R. H., Martin, J. R. & Crist, D. R. Heavy metal uptake by lignin: comparison of biotic ligand models with an ion-exchange process. Environ. Sci. Technol. 36, 1485–1490 (2002).
Mohan, S. & Gandhimathi, R. Removal of heavy metal ions from municipal solid waste leachate using coal fly ash as an adsorbent. J. Hazard. Mater. 169, 351–359 (2009).
He, J. Y. et al. Rapid adsorption of Pb, Cu and Cd from aqueous solutions by β-cyclodextrin polymers. Appl. Surf. Sci. 426, 29–39 (2017).
Guo, X. Y., Zhang, S. Z. & Shan, X. Q. Adsorption of metal ions on lignin. J. Hazard. Mater. 151, 134–142 (2008).
Jia, J. Z., Liu, C. K., Wang, L., Liang, X. Y. & Chai, X. Y. Double functional polymer brush-grafted cotton fiber for the fast visual detection and efficient adsorption of cadmium ions. Chem. Eng. J. 347, 631–639 (2018).
Babić, B. M., Milonjić, S. K., Polovina, M. J. & Kaludierović, B. V. Point of zero charge and intrinsic equilibrium constants of activated carbon cloth. Carbon 37, 477–481 (1999).
Kataria, N. & Garg, V. K. Green synthesis of Fe3O4 nanoparticles loaded sawdust carbon for cadmium (II) removal from water: Regeneration and mechanism. Chemophere 208, 818–828 (2018).
Visa, M., Isac, L. & Duta, A. Fly ash adsorbents for multi-cation wastewater treatment. Appl. Surf. Sci. 258, 6345–6352 (2012).
Koju, N. K., Song, X., Wang, Q., Hu, Z. H. & Colombo, C. Cadmium removal from simulated groundwater using alumina nanoparticles: behaviors and mechanisms. Environ. Pollut. 240, 255–266 (2018).
Visa, M. & Duta, A. TiO2/fly ash novel substrate for simultaneous removal of heavy metals and surfactants. Chem. Eng. J. 223, 860–868 (2013).
Sahu, M. K., Mandal, S., Yadav, L. S., Dash, S. S. & Patel, R. K. Equilibrium and kinetic studies of Cd(II) ion adsorption from aqueous solution by activated red mud. Desalin. Water Treat. 57, 14251–14265 (2016).
Chen, G. N., Shah, K. J., Shi, L. & Chiang, P. C. Removal of Cd(II) and Pb(II) ions from aqueous solutions by synthetic mineral adsorbent: Performance and mechanisms. Appl. Surf. Sci. 409, 296–305 (2017).
Tang, N. et al. Efficient removal of Cd2+ and Pb2+ from aqueous solution with amino- and thiol-functionalized activated carbon: Isotherm and kinetics modeling. Sci. Total Environ. 635, 1331–1344 (2018).
Xiong, T. et al. Insight into highly efficient removal of cadmium and methylene blue by eco-friendly magnesium silicate-hydrothermal carbon composite. Appl. Surf. Sci. 427, 1107–1117 (2018).
Acknowledgements
This work was partly supported by the China Scholarship Council and the Foundation of Top Talents of Hebei Province, China Grant E2015100006. KNW was partly supported by the Department of Civil and Environmental Engineering at the University of Tennessee, Knoxville.
Author information
Authors and Affiliations
Contributions
T.Y., L.S. and Q.H. designed experiments. T.Y., Y.W., K.W. and C.H. organized and performed experiments. T.Y. and Q.H. wrote the manuscript, which was reviewed and corrected by all authors.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, T., Sheng, L., Wang, Y. et al. Characteristics of Cadmium Sorption by Heat-Activated Red Mud in Aqueous Solution. Sci Rep 8, 13558 (2018). https://doi.org/10.1038/s41598-018-31967-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-31967-5
- Springer Nature Limited
This article is cited by
-
Functionalized natural fibre composite filter for the removal of microplastics and heavy metal ions from water
International Journal of Environmental Science and Technology (2024)
-
Experimental design of polymer synthesis applied to the removal of Cd2+ ions from water via adsorption
Discover Water (2024)
-
Removal of cadmium ions from water using coaxially electrospun PAN/ZnO-encapsulated PVDF nanofiber membranes
Polymer Bulletin (2022)