Abstract
Both steelmaking via an electric arc furnace and manufacturing of portland cement are energy-intensive and resource-exploiting processes, with great amounts of carbon dioxide (CO2) emission and alkaline solid waste generation. In fact, most CO2 capture and storage technologies are currently too expensive to be widely applied in industries. Moreover, proper stabilization prior to utilization of electric arc furnace slag are still challenging due to its high alkalinity, heavy metal leaching potentials and volume instability. Here we deploy an integrated approach to mineralizing flue gas CO2 using electric arc furnace slag while utilizing the reacted product as supplementary cementitious materials to establish a waste-to-resource supply chain toward a circular economy. We found that the flue gas CO2 was rapidly mineralized into calcite precipitates using electric arc furnace slag. The carbonated slag can be successfully utilized as green construction materials in blended cement mortar. By this modulus, the global CO2 reduction potential using iron and steel slags was estimated to be ~138 million tons per year.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Carbon dioxide (CO2) mineralization and utilization has been considered one of the imperative strategies on combating climate change and global warming1,2. It is noted that whilst CO2 capture and storage (CCS) may be an important economic incentive for some early CCS projects, CO2 utilization via chemical conversion may prove to be a costly distraction, financially and politically, from the real task of mitigation3. The main contributors to global CO2 emissions from industrial sectors are the steelmaking and cement industries. Both steelmaking via electric arc furnace and manufacturing of portland cement are energy-intensive and resource-exploiting processes4, with great amounts of CO2 and alkaline solid wastes, such as electric arc furnace reducing slag (EAFRS), released into the environment. In particular, stabilization and utilization of the alkaline solid wastes are critical concerns at steelmaking industries5.
World Steel Association estimates that over 400 million tonnes of iron and steel slags is produced each year6. Among various types of steel slags, basic oxygen furnace and electric arc furnace slags are the major by-products worldwide in terms of annual production quantities. In our previous research, we have evaluated the performance of CO2 mineralization and utilization using basic oxygen furnace slag7. The results indicate that the reacted basic oxygen furnace slag could be suitably utilized as supplementary cementitious materials in cement mortars. Compared to other steel slags such as basic oxygen furnace slag, the utilization of electric arc furnace slag is relatively limited. From the viewpoint of chemical compositions, EAFRS could potentially become raw materials for partial substitution in clinker or as an aggregate in concrete once it is properly stabilized8. In general, EAFRS has been found to be rich in CaO (45.0–50.0%), with minor phases of SiO2 (15.0–30.0%), Al2O3 (3.0–20.0%), and MgO (5.0–15.0%), and trace phases of MnO, Al2O3 and SO3 at percentages ranging from 0.2% to 5.0%9. The cementitious and pozzolanic characteristics of fresh EAFRS have been extensively studied in the literature to evaluate its potential for use in construction industry10. However, several barriers, including heavy metal leaching potentials and volume instability, have hindered its widespread use due to the presence of active components such as free lime (CaO f ).
These active components in EAFRS can be easily reacted with CO2 via an accelerated carbonation reaction11, which is similar to the natural weathering processes. Since the accelerated carbonation is a diffusion control reaction, several innovative methods such as high-gravity carbonation12,13 have been proposed to enhance the CO2 mineralization efficiency and capacity. Through the reaction, the CO2 will convert to stable and insoluble carbonates (e.g., CaCO3), which are rarely released afterward14,15. Therefore, it can be used as an integrated approach to mineralizing CO2 in the flue gas while stabilizing the EAFRS. Moreover, due to its similar physico-chemical properties to Portland cement, the carbonated EAFRS product might be used as supplementary cementitious materials in blended cement10. However, to the best of our knowledge, few research has been focused on both the efficiency of CO2 mineralization using EARFS, as well as on the utilization of carbonated EAFRS as supplementary cementitious materials in blended cement.
In this research, the negative stereotype of industrial hazardous wastes (e.g., EAFRS) and greenhouse gases (e.g., CO2) was converted to the green resources (e.g., supplementary cementitious materials). With the use of EAFRS, significant quantities of CO2 in the flue gas can be removed and mineralized as carbonate precipitates via accelerated carbonation. Then, the reacted EAFRS product is further utilized as supplementary cementitious materials in cement mortar. In other words, a waste-to-resource supply chain could be established to achieve a circular economy. The objectives of this study are (1) to determine the performance of flue gas CO2 mineralization via accelerated carbonation using EAFRS; (2) to evaluate the improvement on physico-chemical properties of EAFRS after accelerated carbonation; (3) to determine the feasibility of utilizing carbonated EAFRS as green construction materials, including the workability, compressive strength and durability; and (4) to estimate the worldwide CO2 reduction potential by mineralization using iron and steel slags.
Via the concept of waste-to-resource supply chain, one ton of EAFRS from steelmaking industry can be used to mineralize 0.38 tons of CO2 in the flue gas, corresponding to the carbonation conversion of 83.7%, through an accelerated carbonation process. After carbonation, the reacted EAFRS product is successfully utilized as supplementary cementitious materials, with a substitution ratio of 10%, in cement mortar. Additional benefits from using carbonated EAFRS product in cement mortar, such as reduced leaching potentials of heavy metals, enhanced strength development of mortar, and reduced autoclave expansion, can be realized. We also estimate the global CO2 reduction potential by applying CO2 mineralization using iron and steel slags, where the amount of annually direct CO2 reduction from the flue gas is approximately 0.137 Gt CO2.
Results
Flue Gas CO2 Mineralization via Accelerated Carbonation
Reaction time (i.e., hydraulic retention time), associated with slurry flow rate and rotating speed, is one of the important design parameters for accelerated carbonation in a rotating packed bed reactor, since it is significantly related to carbonation conversion of alkaline wastes, capacity of CO2 mineralization and energy consumption of process. It also affects the pH value of EAFRS slurry along with operation of experiment. Figure 1(a) to (c) show the trends of pH value of EAFRS slurry during a 40-min accelerated carbonation with different operation conditions. The initial pH value of EAFRS slurry was relatively high (i.e., 10.6–12.9), and began to decrease with reaction time after CO2 was introduced. After 40-min carbonation, the pH value of EARFS slurry decreased to between 6.5 and 4.5. It is noted that both the dissolution of gaseous CO2 and the leaching of calcium ions from solid matrix of EAFRS depend on the pH value. According to Eqs [1] to [3], carbonate (CO3 2−) is the dominant species in the EAFRS slurry when pH is higher than 10.3, and bicarbonate (HCO3 −) is the dominant species in the slurry when pH is between 6.3 to 10.3. Since carbonate is the main species in carbonation reaction, the efficiency of carbonation decreases as the pH value deceases.
On the other hand, the leaching of calcium ions increases in a low pH value solute, as shown in Eq. [4]:
Therefore, the pH value of EAFRS slurry should be carefully controlled to maximize the carbonation efficiency and capacity. The results indicated that the highest carbonation conversion of EAFRS was about 83.7%, corresponding to a mineralization capacity of 0.38 kg CO2 per kg EAFRS. Several operating factors, such as slurry flow rate, temperature and rotating speed, play key roles in the performance of accelerated carbonation. For instance, slurry flow rate would influence volumetric mass transfer rate of both liquid- and gas-phase transport phenomena. In general, a higher liquid flow rate would make a thinner liquid film16, thereby enhancing the mass transfer between liquid and gas phases based on the two-film theory, as shown in Eq. [5]:
where D CO2 (m2/s) is the diffusivity of CO2 species which is a function of temperature17, δ is the film thickness (m), and k CO2 is the mass transfer coefficient (m/s). According to our previous study18, the gas-phase mass transfer coefficient significantly increased (e.g., from 0.094 s−1 to 0.366 s−1) as the gas-to-slurry ratio decreased (e.g., from 20 to 13, respectively, by increasing slurry flow rate). However, as shown in Fig. 1(d), as the slurry flow rate further increased from 0.6 to 1.4 L/min, the carbonation conversion of EAFRS trend to decrease. This was attributed to the fact that the rapid decrease of pH value under a higher slurry flow rate would restrict carbonation reaction and lead to a lower carbonation conversion of EAFRS. Moreover, a higher slurry flow rate would result in a lower residence time of EAFRS slurry in the reactor, thereby decreasing the carbonation conversion.
(a) Effect of slurry flow rate on pH value, operated at 20 °C and a rotating speed of 700 rpm; (b) effect of temperature on pH value, operated at a rotating speed of 700 rpm and a slurry flow rate of 1.0 L/min; (c) effect of rotating speed on pH value at 20 °C and a slurry flow rate of 1.0 L/min; (d) effect of slurry flow rate on carbonation conversion of EAFRS at 20 °C with an L/S ratio of 25 mL/g and a rotating speed of 700 rpm; (e) effect of temperature on carbonation conversion of EAFRS, operated with an L/S ratio of 25 mL/g, a rotating speed of 700 rpm, and a slurry flow rate of 1.0 L/min; (f) effect of rotation speed on carbonation conversion of EAFRS at 20 °C with an L/S ratio of 25 mL/g and a slurry flow rate of 1.0 L/min; (g) prediction versus actual values of response surface model for carbonation conversion of EAFRS; (h) 2D contour and (I) 3D response surface plot of carbonation conversion of EAFRS (condition of predicted maximal conversion at a slurry flow rate of 0.6 L/min).
Temperature has a significant influence on the carbonation conversion of EAFRS since it is related to (i) the dissolution of reactive oxide from solid waste into solution, (ii) the solubility of CO2 into aqueous carbonic species, and (iii) growth and nucleation of carbonate precipitates. For example, under high temperatures, the CO2 dissolution from the gas phase into the liquid phase is restricted since the Henry’s constant (H) is a function of temperature as described by Eq. [6]19:
where C is the constant for all gases (2400 K for CO2) and T is the temperature (K). In other words, the nucleation and growth of CaCO3 precipitates were slow due to the solubility of CO2 was low which is disadvantageous to carbonation reaction. On the other hand, the leaching of calcium ion from EAFRS increased with the increase of temperature, which is beneficial to carbonation reaction. Therefore, as indicated in Fig. 1(e), a range of optimal temperature from 50–55 °C can be found. In contrast to operating at 20 °C, the calcium ions in EAFRS can be rapidly dissolved into the slurry at 55 °C and compensate for the disadvantage of lower CO2 solubility at higher temperatures. While the temperature was over 55 °C the carbonation conversion of EAFRS started decreasing due to the restricted CO2 dissolution from the gas phase into the liquid phase. Furthermore, the effect of temperature on pH value was remarkable. The decrease of pH value at high temperatures was much rapid than that at low temperatures.
In addition, since accelerated carbonation is a diffusion control reaction, the effect of rotating speed (i.e., mass transfer rate) on carbonation efficiency should be remarkable. It was observed that the gas-phase mass transfer rate was moderately intensified with an increase of rotor speed18. In other words, the mass transfer resistance was reduced as the rotating speed increased. However, a high rotating speed may also cause a reduction in the residence time, resulting in a decrease of carbonation conversion. As shown in Fig. 1(f), the optimal rotating speed for accelerated carbonation of EAFRS should be around 700 rpm. Beyond the optimal point, the contribution of high mass transfer rate would be compensated by the low residence time. In the case of carbonation reaction using basic oxygen furnace slag, the gas-phase mass transfer coefficients varied with the centrifugal acceleration to the 0.33 power18, while the liquid-phase mass transfer coefficient was at a scale of 9.23 × 10−4 s−1 based on the shell mass balance model20.
To visualize the carbonation conversion of various operation parameters, the experimental data of accelerated carbonation was further analyzed by the response surface methodology. A D-optimal design was applied to develop a mathematical model of carbonation conversion under various operating conditions, as shown in Eq. [7]:
where Y is the carbonation conversion of EAFRS; and A, B, and C is independent coded variables of temperature, slurry flow rate, and rotating speed, respectively. Figure 1(g) shows the comparison of the carbonation conversion estimated by the developed model with the experimental data, which indicates that the conversion predicted by the developed model are similar to the experimental value. It was also found that the influence of temperature on carbonation conversion was the most significant (p < 0.001). According to the developed model, the maximal conversion of EAFRS should be 86.3% (as shown in Fig. 1(h)), corresponding to a mineralization capacity of 0.394 kg CO2 per kg EAFRS, at 49.2 °C with a rotating speed of 733 rpm and a slurry flow rate of 0.6 L/min (as shown in Fig. 1(i)).
It was noted that, in addition to temperature, slurry flow rate, and rotating speed, the CO2 concentration in the feed gas stream would affect the accelerated carbonation rate and the CO2 fixation capacity of slags21,22. In practice, the CO2 concentration of the flue gas in the steel industry typically ranges from 10% to 30%. For the sake of comparison, additional experiments of CO2 mineralization using EAFRS were operated at a representative CO2 concentration of ~30%. With similar operating conditions, the fixation capacity of EAFRS was found to be approximately 0.25 kg CO2 per kg of EAFRS, while the corresponding carbonation conversion of EAFRS was about 57.1% with a slurry flow rate of 0.75 L/min at 60 °C.
Improvement on Physico-Chemical Properties of Alkaline Wastes
Accelerated carbonation exhibits the potency of upgrading the physico-chemical properties of alkaline wastes, e.g., high alkalinity and heavy metal leaching. Figure 2 shows the scanning electron microscope (SEM) photos of both the fresh and carbonated EAFRS. Before carbonation, the surface of fresh EAFRS was smooth and flat, as shown in Fig. 2(a) and (b). Compared to the fresh EAFRS, a layer of white material was observed to accumulate on the surface of the carbonated EAFRS, as shown in Fig. 2(c) and (d). The cubic particles with sizes ranging from 1 to 2 μm in diameter were composed primarily of Ca, O, and C (according to the energy-dispersive X-ray spectroscopy (EDX) analyses), which indicated a calcium carbonate composition. The reaction product was also characterized by X-ray diffraction (XRD), as shown in Fig. S1. The main crystal phases of fresh EAFRS were Ca2SiO4 (calcio-olivine), Ca2SiO5 (dicalcium silicate), Ca(OH)2 (portlandite), and CaO f (lime). After carbonation, a significant increase of peak intensities for CaCO3 (calcite) was observed, while peaks for both Ca(OH)2 and CaO f were eliminated. This indicated that the Ca-bearing phases in EAFRS were the main reacting components with CO2 to form the carbonate minerals, where the mechanisms can be briefly described as Eqs [8] and [9]:
After carbonation, the precipitate products (e.g., CaCO3) can form a protective layer on the surface of EAFRS, thereby preventing leaching of heavy metals into the solution. Table 1 presents the toxicity characteristic leaching procedure (TCLP) test of fresh and carbonated EAFRS, associated with the limits by regulations in Taiwan. TCLP is an essential indicator for utilizing the carbonated product as construction materials. The results indicate that several metal and non-metal elements in EAFRS can be inhibited from leaching into solution after carbonation. For example, a significant reduction of barium (Ba) ions leaching was achieved after carbonation, e.g., from 0.601 mg/L (in fresh EAFRS) to 0.377 mg/L (in carbonated EAFRS), respectively. The leaching of elements such as selenium (Se) and arsenic (As) with trace leaching concentrations of 0.006 and 0.004 mg/L from fresh EAFRS, respectively, were slightly reduced after carbonation. It thus suggests that the heavy metals in EAFRS can be successfully restricted from leaching into solution via accelerated carbonation. On the other hand, the formed CaCO3 protective layer may reduce further diffusion of CO2 through the EAFRS, thereby causing the decrease of CO2 adsorption ability and carbonation rate. Several studies have been conducted to evaluate the effect of protective product layer on the reaction kinetics23. For instance, in the case of accelerated carbonation, since the thickness of product layer was typically much smaller than the particle size of EAFRS, the reduced reaction rate would be neglected24.
Accelerated carbonation can upgrade the chemical properties of EAFRS, which is beneficial to subsequent utilization as construction materials in blended cement or concrete. Table 2 presents the chemical properties of EAFRS with various carbonation conversions and their associated properties as supplementary cementitious materials with a substitution ratio of 10% in blended cement clinker. The results indicated that, after carbonation, the contents of SiO2, MgO and CaO in EAFRS increased while the SO3 decreased significantly. Also, no presence of CaO f was observed in the carbonated EAFRS, which is beneficial to preventing the cement mortar from expanding in a moist environment. On the other hand, the changes in chemical properties will have an influence on the performance of blended cement. The main components in the ordinary portland cement (OPC) were found to be CaO, SiO2, Fe2O3, Al2O3 and MgO. It is noted that the major components in carbonated EAFRS are similar to that of OPC, with the percentages of 58.1–58.3% CaO, 17.5–17.6% SiO2, 5.4–5.7% Al2O3, 5.6–6.0% MgO, and 7.8–7.9% Fe2O3.
On the other hand, the effect of carbonation conversion on initial and final setting time of blended cement mortar was remarkable. In general, the addition of supplementary cementitious materials in cement mortar would slightly increase setting time, which is attributed to the cement dilution effect. In this study, the setting time of paste with fresh EAFRS did not increase significantly in comparison with the OPC. In contrast, the setting time of blended cement mortar with carbonated EAFRS decreased as the carbonation conversion increased. This may be attributed that the nucleation sites of EAFRS increases significantly after the carbonation reaction, leading to formation of more hydration products. The well-crystalline CaCO3 particles on the surface of carbonated EAFRS can act as seeds for the nucleation of calcium silicate hydrates (CSH), thereby accelerating the formation of the major cement hydration. Additionally, the increased silica ratio after carbonation, to the range of 1.29–1.32, could lead to the reduction in setting time of the mortar. Furthermore, the content of SO3 in the cement plays an important role in the compressive strength development. In generally, 2–3% should be the optimum SO3 content for cement. Once beyond that (i.e., >4%), compressive strength of cement mortar starts to decline, particularly at early ages. In this study, the content of SO3 in cement mortar met the aforementioned criteria.
Utilization of Carbonated EAFRS as Green Construction Materials
The performance of utilizing the carbonated EARFS product as supplementary cementitious materials in blended cement mortar, including compressive strength and autoclave expansion, was evaluated, as shown in Fig. 3. In general, the compressive strength increased continuously with the curing age till 28 days, while only a slight increment was observed from 28 to 56 days. The hydration reaction begins after the water is mixed with OPC. As long as the reaction time increases, the hydration product increases as well, thereby enhancing the compressive strength of cement mortar. It is noted that the compressive strength of cement is determined by the mineralogical composition of mortar, such as Ca3SiO5 (C3S), Ca2SiO4 (C2S), Ca3Al2O6 (C3A), and Ca4Al2Fe2O10 (C4AF). For instance, triclinic (C3S) contributes to the initial strength development for the early 28 days, while dicalcium silicate (C2S) contributes to the ultimate strength for at least one year25. Tricalcium aluminate (C3A) provides strength for the early stage hydration but few for late stage.
Compressive strength development of various carbonation conversions of EAFRS at (a) 3, (b) 7, (c) 28, and (d) 56 days. The ASTM C109/C109M requirements for minimal compressive strength at 3 and 7 d are 12.0 and 19.0 MPa, respectively. (e) Photos of autoclave soundness expansion for different cement mortars; (f) autoclave soundness expansion of cement mortar using different carbonation conversions of EAFRS.
The compressive strengths of all fresh (F-) and carbonated (C-) EAFRS specimen could meet the American Society for Testing and Materials (ASTM) requirements at 3 and 7 days, as shown in Fig. 3(a) and (b), respectively. In general, the C-EAFRS exhibits relatively higher compressive strength than the F-EAFRS, especially at early ages. In the case of C-EAFRS, additional sites for nucleation of the hydration product could be provided due to its high surface area, resulting in a higher compressive strength. It thus suggests that the use of C-EAFRS as supplementary cementitious materials in cement mortar would enhance the mechanical properties to a greater degree than using F-EAFRS.
Compared to blended cement mortar with fresh and carbonated EAFRS substitution, the OPC mortar generally exhibits higher compressive strength at all curing ages. Only at the curing age of 28 days, the blended cement mortar with C-EAFRS (i.e., C-EAFRS-2, C-EAFRS-3 and C-EAFRS-4) obtained higher compressive strength than that with OPC and F-EAFRS, as shown in Fig. 3(c). This might be attributed to the interaction of C3A (in OPC) and CaCO3 (in C-EAFRS), resulting in the formation of calcium carboaluminate hydrate (C3A·CaCO3·11 H) and C3A·0.5CaCO3·0.5Ca(OH)2·11.5 H, as shown in Eq. [10]. The calcium carboaluminate hydrate could contribute to a higher mechanical strength.
where H represents H2O. On the other hand, the C3A hydration would generate a great amount of hardening heat, which might lead to a negative effect on the compressive strength. The resulted hardening heat would weaken the cement matrix bond with microcrack formation, slightly decreasing the compressive strength on 56 days, as shown in Fig. 3(d). Therefore, there is a trade-off between the initial and ultimate compressive strength, which should be addressed by formulating appropriate ratios of key cementitious compositions (e.g., C3S, C2S, and C3A) with the carbonate products (largely related to the substitution ratios and carbonation conversion of C-EAFRS).
Regarding the volume stability of cement mortar, the autoclave soundness test can provide an index of potential delayed expansion caused by the hydration of free lime (CaO f ), when they present in hydraulic cement. It is noted that the CaO f in fresh EAFRS would react with moisture in the air to form Ca(OH)2, thereby causing volume expansion. Figure 3(e) and (f) show the specimens and results of autoclave soundness expansion for cement mortars with EAFRS of different carbonation conversions, respectively. The results indicated that the effluence of EAFRS on autoclave expansion was not remarkable. The maximal expansion of blended cement mortar was only 0.076% in the case of C-EAFRS-2. All results of autoclave soundness expansion of cement mortar could reach the ASTM C 150 standard, i.e., less than 0.8%.
Potency of Worldwide CO2 Reduction
A district green supply chain can be established by considering the iron and steel industry as a district supply center of green resources. The worldwide crude steel production in 2016 was approximately 1628 Mt, where the percentages of oxygen furnace and electric furnace were 74.3% and 25.3%, respectively26. In other words, significant quantities of iron and steel slags will be generated along the steelmaking process. Figure 4 estimates the worldwide potency of annual direct CO2 reduction by establishing the waste-to-resource supply chain exemplified by iron and steel slags. The amount of worldwide reduction by CO2 mineralization using iron and steel slags was approximately 137.5 Mt per year, contributing to a reduction of the global anthropogenic CO2 emissions (i.e., ~36 Gt of CO2 per year) by 0.38%. The Asia Pacific area exhibits the greatest potential of direct CO2 reduction, i.e., around 94.9 Mt of CO2 per year, followed by the Europe (i.e., about 16.9 Mt of CO2 per year). In particular, China possesses the largest annual CO2 reduction potential of 74.9 Mt, although it also contributes a great amount of anthropogenic CO2 emissions annually. The second large potential of CO2 reduction is Japan at about 9.2 Mt CO2 per year.
Potency of direct CO2 reduction by establishing waste-to-resource supply chain exemplified by iron and steel slags including blast furnace slag (BFS), basic oxygen furnace slag (BOFS), and electric arc furnace slag (EAFS). The maps were generated using Geographic Information Systems software ArcGIS ver. 10.229 (http://www.esri.com/). The World spatial boundary GIS data is from the Open Database of Global Administrative Areas (GADM) ver. 2.030 (http://www.gadm.org/), which provides the basic GIS data for the World Imagery.
Discussion
The chemical compositions of EAFRS largely affect the performance of CO2 mineralization, as well as the subsequent utilization as supplementary cementitious materials in cement mortar. For CO2 fixation, both Ca- and Mg-bearing species are usually considered as the major reactive components to form carbonate precipitates. Typical reaction temperature and CO2 pressure for the formation of MgCO3 via aqueous carbonation should be higher than 144 °C and 100 kg/cm2, respectively27. Therefore, in this study, the potency of MgCO3 formation could be neglected due to its relatively low operating temperature and pressure of CO2. Other components in EAFRS, such as SiO2, Al2O3, Fe2O3, and SO3, do not contribute to CO2 fixation. However, for utilization of EAFRS in cement mortar, the content of SiO2 in EAFRS would contribute to pozzolanic activity of cement mortars, which is highly related to strength development. Similarly, Al2O3 may cause the change in viscosity of blended cement or concrete pastes, affecting their self-leveling and pumping behavior, as well as related to solid particles segregation.
In this study, we report an integrated approach to mineralizing CO2 in the flue gas as carbonate precipitates via accelerated carbonation, while utilizing the reacted product as supplementary cementitious materials in cement mortar. Under this framework, a waste-to-resource supply chain could be established toward a circular economy, as shown in Fig. 5. The maximum carbonation conversion of 86.3%, corresponding to a capacity of 0.38 t-CO2 per ton of EAFRS, can be obtained at 55 °C. In addition, the use of carbonated EAFRS as supplementary cementitious materials in cement mortars exhibited superior performance on the workability, mechanical strength development, and durability to that of using fresh EAFRS. Moreover, the leaching potentials for several heavy metals (e.g., Ba, Se, and As) from EAFRS were significantly reduced after carbonation.
However, the amounts of CO2 fixation by the mineralization process could be offset by the energy usage of the process (e.g., grinding unit, reactor, agitator, slurry pump and heater) since electricity generation may cause additional CO2 emissions. Therefore, the net CO2 fixation amounts of the entire waste-to-supply chain should be critically evaluated by the life cycle assessment. It is worth mentioning that cement production is a CO2-intensive process, in which roughly 0.73–1.00 tons of CO2 are generated for one ton of cement production28. By utilization of the carbonated EAFRS as supplementary cementitious materials, a significant amount of CO2 emission could be indirectly avoided. This would contribute more to the reduction of total CO2 emissions than mineralization. Thus, increasing the substitution ratio of reacted EAFRS in cement mortar while meeting the ASTM requirement for essential characteristics, functions and qualities became more critical to maximize the overall CO2 mitigation capacity.
From the perspective of material flow, a huge amount of water is needed to enhance the reaction kinetics of accelerated carbonation. On the other hand, freshwater stress and scarcity are two of the most challenging issues caused by climate change, rapid population growth, and urbanization. Therefore, utilizing industrial wastewater should be a resource-efficient approach to CO2 minimization via accelerated carbonation, especially for the industries in water-scarce regions. It is noted that the chemical properties of industrial wastewater can be upgraded after accelerated carbonation via several mechanisms, such as neutralization and precipitation. In this work, the pH value of EARFS slurry was found to decrease to 4.5–6.5 after 40-min carbonation.
To achieve a circular economy, the utilization of industrial solid wastes should be considered as one of the available demonstration portfolio for establishing the waste-to-resource supply chain. It is noted that the worldwide CO2 reduction by mineralization using iron and steel slags (only) is approximately 0.137 Gt per year, corresponding to a global CO2 emission reduction by 0.38%. In addition to iron and steel slags, there are numerous industrial alkaline solid wastes, such as cement kiln dust, municipal solid waste incinerator ashes, air pollution control ashes, shell ashes and sludge, that can be used for CO2 mineralization and utilization. On the other hand, the reacted product can be used as substitution materials in cement/concrete, which can further contribute to a more significant amount of indirect CO2 reduction. Therefore, the overall potential of CO2 reduction should be critically assessed by considering both the direct portions (via the mineralization process) and indirect avoidance (due to the product utilization) of CO2 reduction. Future research should focus on technology evaluation, including life cycle assessment, techno-economic analysis, and waste-water-energy nexus, for system optimization.
Methods
Materials
In this study, EAFRS was provided by Tung Ho Steel Enterprise Corporation, Taiwan. The EAFRS was crushed into smaller debris and then milled into fine particles by a ball-mill machine. Afterwards, the EAFRS was sieved to a particle size less than 15 µm and then dried in an oven at 105 °C overnight to eliminate moisture. The components in EAFRS include CaO (56.4%), SiO2 (26.6%), Al2O3 (6.3%), MgO (5.3%), Fe2O3 (2.0%), SO3 (1.1%), and free lime (CaO f , 0.8%). For the CO2 mineralization experiments, de-ionized (DI) water with 18.2 MΩ/cm was used to form the EAFRS slurry. High-pressure CO2 and N2 gases (with a purity of 99.5%) were purchased from Ching-Feng Gas Corporation, Taiwan. For the product utilization experiments, the physico-chemical properties of OPC were checked in compliance with ASTM C150 specifications. Graded standard sand (Ottawa sand) following ASTM C778 was used to prepare mortar specimens.
CO2 Mineralization through Accelerated Carbonation
In this study, CO2 mineralization through accelerated carbonation of EAFRS was conducted in a rotating packed bed reactor, known as a high-gravity carbonation process. It was noted that the carbonation conversion of basic oxygen furnace slag can be significantly improved within a short reaction time at ambient temperatures and pressure12. Stainless steel wire was used as a packing material in the rotating packed bed reactor. The reactor, with an inner and outer radius of 0.077 and 0.165 m, respectively, can be operated at a rotating speed up to 1,800 rpm. The packing zone had an axial height of 0.020 m.
The EAFRS is well-mixed with DI water to form EAFRS slurry at a liquid-to-solid (L/S) ratio of 25 mL/g. When the experiment begins, CO2 gas flows into the reactor, and then carbonation reaction begins; at the same time, the slurry will pump into the reactor for further reaction. The gas flow rate was 2.5 L/min with a CO2 concentration of 99.9 vol% at a pressure of 1.03 kg/cm2. The ranges of variable parameters for temperature, EAFRS slurry flow rate and rotating speed were 25–80 °C, 0.6–1.5 L/min, and 300–1,100 rpm, respectively. The samples were taken at 1, 2, 3, 4, 5, 7.5, 10, 15, 20, 30 and 40 mins, and then dried in an oven at 105 °C overnight to eliminate moisture. Afterward, the carbonation conversion of EAFRS samples was analyzed by thermogravimetric analysis (TGA).
Preparation of Cement Mortar with EAFRS
In this study, blended cement mortars were prepared by mixing with fresh or carbonated EAFRS at a substitution ratio of 10%. Different carbonation conversions of EAFRS (i.e., 0.7%, 1.0%, 4.0%, 8.0%, and 16.0%) were blended in cement mortar for evaluating the performance of compressive strength and autoclave expansion. To maintain consistent workability in cement pastes, a standard flow of 110 ± 5%, as specified by ASTM C230, was maintained by adjusting the quantity of mixing water in a blended cement mortar. For evaluation of compressive strength, the standard sand was mixed with cement and EAFRS to become a paste, and then put into cubic molds with a size of 5 mm × 5 mm × 5 mm. The molds were cured for 24 h to set the specimens, and then the cubic specimens were demolded afterward. The cubic specimens were cured in a saturated lime solution at room temperature for time intervals of 3, 7, 28, and 56 days, which were used for compressive strength testing.
Performance Evaluation of Blended Cement Mortars
The determination of setting time for cement blended was in accordance with ASTM C191 using a Vicat needle. The initial and final setting times should be no less than 45 min and no more than 7 h, respectively. Compressive strength is one of the most important mechanical property of blended cement mortar. The ASTM C109/C109M for minimal compressive strength at 3 and 7 days are 12.0 and 19.0 MPa, respectively (i.e., 1760 and 2760 psi, respectively). In this study, the mass ratio of sand, OPC and supplementary cementitious materials in blended cement mortar was 2.75: 0.90: 0.10, and all blended cement mortars were cured in a saturated lime solution for 56 days. For the control group, a cube paste with 100% OPC type I (i.e., no replacement using EAFRS) was prepared. On the other hand, autoclave expansion is one of the useful indicators for the stability of construction materials. The ASTM C151 requirement for portland cement specifies a maximum autoclave expansion of 0.80%. In the autoclave expansion tests, cement paste bars were first cured at room temperature for 24 h, and then placed in an autoclave equipment with the steam pressure of 2.00 ± 0.07 MPa at 216 ± 2 °C for 3 h.
Analytical Techniques
After CO2 mineralization experiments, the sampled EAFRS slurry was treated by vacuum filtration and then dried in an oven to 105 °C. Then, TGA (STA6000, PerkinElmer) was used to determine the carbonation conversion of EAFRS. The EAFRS sample was heated directly from 50 to 950 °C at a heating rate of 10 °C per min. The chemical composition, mineralogy and microstructure of EAFRS before and after carbonation were evaluated by XRF (PW2430, Phillips), XRD (Bruker D8), and SEM (JSM-4500, JEOL), respectively. The distributions of elements on the surface of fresh and carbonated EAFRS were detected using energy-dispersive X-ray (EDX) spectroscopy. The EDX can be employed for characterizing the formed CaCO3 during the carbonation reaction. In addition, the toxicity characteristic leaching procedure (TCLP) for fresh and carbonated EAFRS was carried out. The leaching limits for hazardous industrial wastes, specified by NIEA R201.14 C, as well as green building material, regulated by the Taiwan Architecture & Building Center, were used to determine if the product could be utilized as a construction material.
Estimate of Worldwide CO2 Reduction Potency
World maps of CO2 emissions, as well as the CO2 reduction potential contributed by carbon mineralization of steel slags were compiled using Geographic Information Systems (GIS) software ArcGIS (v. 10.2; http://www.esri.com/)29. The World spatial boundary GIS data is from the Open Database of GADM (v. 2.0; http://www.gadm.org/)30. The International Energy Agency (IEA) provided CO2 emissions by regions and countries31. The information of worldwide production of crude steel, as well as oxygen furnace and electric furnace slags in 2016 was gathered from the World Steel Association26. The CO2 reduction potential contributed by carbon mineralization of steel slags, including blast furnace slag, basic oxygen furnace slag and electric arc furnace slag, was estimated by multiplying their annual production with the maximum achievable carbonation conversion obtained in this study and those in the literature7.
Data Statement
Readers can access the data via contact to the authors.
References
Matter, J. M. et al. Rapid carbon mineralization for permanent disposal of anthropogenic carbon dioxide emissions. Science. 352, 1312–1314 (2016).
Markewitz, P. et al. Worldwide innovations in the development of carbon capture technologies and the utilization of CO2. Energy & Environmental Science. 5, 7281–7305 (2012).
Mac Dowell, N., Fennell, P. S., Shah, N. & Maitland, G. C. The role of CO2 capture and utilization in mitigating climate change. Nature Clim. Change. 7, 243–249 (2017).
Kirchofer, A., Brandt, A., Krevor, S., Prigiobbe, V. & Wilcox, J. Impact of alkalinity sources on the life-cycle energy efficiency of mineral carbonation technologies. Energy & Environmental Science. 5, 8631 (2012).
Gao, Y. et al. BOF steel slag as a low-cost sorbent for vanadium (V) removal from soil washing effluent. Sci Rep. 7, 11177 (2017).
World Steel Association. Steel industry by-products. 2 (2016).
Pan, S. Y. et al. High-Gravity Carbonation Process for Enhancing CO2 Fixation and Utilization Exemplified by the Steelmaking Industry. Environ Sci Technol. 49, 12380–12387 (2015).
Bourzac, K., Savage, N., Owens, B. & Scott, A. R. Materials and engineering: Rebuilding the world. Nature. 545, S15–S20 (2017).
Pan, S.-Y., Adhikari, R., Chen, Y.-H., Li, P. & Chiang, P.-C. Integrated and innovative steel slag utilization for iron reclamation, green material production and CO2 fixation via accelerated carbonation. Journal of Cleaner Production. 137, 617–631 (2016).
Sanna, A., Uibu, M., Caramanna, G., Kuusik, R. & Maroto-Valer, M. M. A review of mineral carbonation technologies to sequester CO2. Chemical Society reviews. 43, 8049–8080 (2014).
Lackner, K. S. Climate change. A guide to CO2 sequestration. Science. 300, 1677–1678 (2003).
Pan, S. Y., Chiang, P. C., Chen, Y. H., Tan, C. S. & Chang, E. E. Ex Situ CO2 capture by carbonation of steelmaking slag coupled with metalworking wastewater in a rotating packed bed. Environ Sci Technol. 47, 3308–3315 (2013).
Pan, S. Y. et al. Systematic Approach to Determination of Maximum Achievable Capture Capacity via Leaching and Carbonation Processes for Alkaline Steelmaking Wastes in a Rotating Packed Bed. Environ Sci Technol. 47, 13677–13685 (2013).
Mikkelsen, M., Jørgensen, M. & Krebs, F. C. The teraton challenge. A review of fixation and transformation of carbon dioxide. Energy & Environmental Science. 3, 43 (2010).
Tomkinson, T., Lee, M. R., Mark, D. F. & Smith, C. L. Sequestration of Martian CO2 by mineral carbonation. Nat Commun. 4, 2662 (2013).
Liu, H. & Kuo, C. Quantitative multiphase determination using the Rietveld method with high accuracy. Materials Letters. 26, 171–175 (1996).
Chiang, P.-C. & Pan, S.-Y. In Carbon Dioxide Mineralization and Utilization Ch. 7, (Springer Nature Singapore Pte Ltd., 2017).
Pan, S. Y. et al. Systematic approach to determination of optimum gas-phase mass transfer rate for high-gravity carbonation process of steelmaking slags in a rotating packed bed. Applied Energy. 148, 23–31 (2015).
Morel, F. M. & Hering, J. G. Principles and applications of aquatic chemistry. (John Wiley & Sons, 1993).
Chang, E. E., Chen, T.-L., Pan, S.-Y., Chen, Y.-H. & Chiang, P.-C. Kinetic modeling on CO2 capture using basic oxygen furnace slag coupled with cold-rolling wastewater in a rotating packed bed. J Hazard Mater. 260, 937–946 (2013).
Chang, E. E. et al. Accelerated carbonation using municipal solid waste incinerator bottom ash and cold-rolling wastewater: Performance evaluation and reaction kinetics. Waste Manag. 43, 283–292 (2015).
Chang, E. E., Wang, Y.-C., Pan, S.-Y., Chen, Y.-H. & Chiang, P.-C. CO2 Capture by Using Blended Hydraulic Slag Cement via a Slurry Reactor. Aerosol and Air Quality Research. 12, 1433–1443 (2012).
Sohn, H. Y. The effects of reactant starvation and mass transfer in the rate measurement of fluid–solid reactions with small equilibrium constants. Chemical Engineering Science. 59, 4361–4368 (2004).
Chang, E. E., Pan, S. Y., Chen, Y. H., Tan, C. S. & Chiang, P. C. Accelerated carbonation of steelmaking slags in a high-gravity rotating packed bed. J Hazard Mater. 227–228, 97–106 (2012).
Pan, S.-Y. et al. Integrated CO2 Fixation, Waste Stabilization, and Product Utilization via High-Gravity Carbonation Process Exemplified by Circular Fluidized Bed Fly Ash. ACS Sustainable Chemistry & Engineering. 4, 3045–3052 (2016).
World Steel Association. World Steel in Figures 2017. 10 (World Steel Association, 2017).
Teir, S. Fixation of carbon dioxide by producing carbonates from minerals and steelmaking slags Doctoral Dissertation thesis, Helsinki University of Technology, (2008).
Hasanbeigi, A., Price, L. & Lin, E. Emerging energy-efficiency and CO2 emission-reduction technologies for cement and concrete production: A technical review. Renewable and Sustainable Energy Reviews. 16, 6220–6238 (2012).
ArcGIS. (ed Environmental Systems Research Institute) (http://www.esri.com/legal/copyright-trademarks, Redlands, CA, 2011).
GADM. (ed Global Administrative Areas) (GADM database of Global Administrative Areas, http://www.gadm.org/, 2012).
IEA. Key World Energy Statistics. 100 (OECD, International Energy Agency, France, 2017).
Acknowledgements
This study was supported by the Ministry of Science and Technology (MOST), Taiwan (ROC) under Grant No. MOST-106-E-3113-007-002. In addition, the Tung Ho Steel Enterprise Corporation was highly appreciated for their financial and technical supports.
Author information
Authors and Affiliations
Contributions
P.C.C. designed and directed the study. T.C.C. performed the experiments as well as most of the coordination with XRD and SEM laboratories. C.C.H., C.J.H. and Y.H.C. took part in the discussion of reaction processes. S.Y.P. interpreted the raw data, estimated the global reduction potential, and wrote the manuscript. All authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pan, SY., Chung, TC., Ho, CC. et al. CO2 Mineralization and Utilization using Steel Slag for Establishing a Waste-to-Resource Supply Chain. Sci Rep 7, 17227 (2017). https://doi.org/10.1038/s41598-017-17648-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-17648-9
- Springer Nature Limited
This article is cited by
-
Managing carbon waste in a decarbonized industry: Assessing the potential of concrete mixing storage
Environmental Science and Pollution Research (2024)
-
Breakthrough innovations in carbon dioxide mineralization for a sustainable future
Reviews in Environmental Science and Bio/Technology (2024)
-
Enhanced Carbonation of Free CaO in Basic Oxygen Furnace Slag Under High Temperature and Moderate Pressure and Its Kinetics
JOM (2024)
-
Synergistic Use of CO2 Pretreatment and Accelerated Carbonation Curing for Maximum Recycling of Steel Slag
Journal of Wuhan University of Technology-Mater. Sci. Ed. (2023)
-
Characterization and numerical analysis of the utilization of iron mill scale in soil improvement: a case study from the Kingdom of Bahrain
Arabian Journal of Geosciences (2023)