Abstract
Many insect species reversibly adhere to surfaces by combining contact splitting (contact formation via fibrillar contact elements) and wet adhesion (supply of liquid secretion via pores in the insects’ feet). Here, we fabricate insect-inspired fibrillar pads for wet adhesion containing continuous pore systems through which liquid is supplied to the contact interfaces. Synergistic interaction of capillarity and humidity-induced pad softening increases the pull-off force and the work of adhesion by two orders of magnitude. This increase and the independence of pull-off force on the applied load are caused by the capillarity-supported formation of solid–solid contact between pad and the surface. Solid–solid contact dominates adhesion at high humidity and capillarity at low humidity. At low humidity, the work of adhesion strongly depends on the amount of liquid deposited on the surface and, therefore, on contact duration. These results may pave the way for the design of insect-inspired adhesive pads.
Similar content being viewed by others
Introduction
Micro- and nano-scaled fibrillar adhesive pads based on the contact splitting principle may show adhesive strengths matching or even surpass those of natural systems1,2. The contact splitting principle involves the contact formation between the discrete fibrillar contact elements of an adhesive pad and a counterpart surface at a large number of discrete contact points. Thus, fibrillar adhesive pads exhibit high adaptability to rough or curved counterpart surfaces, constrained crack propagation, pronounced adhesion reversibility and high durability. While bioinspired fibrillar adhesive pads have predominantly been designed for dry adhesion based on van der Waals forces mimicking gecko adhesion3,4, nature has developed elegant solutions to further optimize the performance of biological fibrillar adhesive pads. Softening of fibrillar adhesive pads by the presence of hydrated biopolymers increases their mechanical compliance, their adaptability to rough counterpart surfaces and ultimately their adhesive strength. For example, the hydration of resilin drastically decreases the Young’s modulus in the setal tips of the beetle Coccinella septempunctata from 7.2 GPa to 1.2 MPa, resulting in a significantly improved adhesion performance5. Furthermore, enhanced compliance of fibrillar adhesive pads by hydration has been considered as the reason for the pronounced dependence of dry gecko adhesion on relative humidity (RH)6. On the other hand, wet adhesion of insects7,8,9,10,11,12 is caused by capillary forces related to the presence of adhesive secretions at the contact interface. Direct solid–solid interactions between cuticle pad and counterpart surface, as well as capillary contributions related to the presence of adhesive liquids at the contact interface, were reported to concurrently contribute to the adhesion of Asian weaver ants (Oecophylla smaragdina)9. The adhesive secretions are transported to the contact interfaces through channels or sponge-like pore systems inside the insects’ setae13,14. Secretion footprints remaining after the contact between insect feet and counterpart surfaces have been related to mechanically controlled, continuous supply of secretion from the interior of insects’ setae on the feet to the contact interface15,16. Despite the intriguing design principles biological models use to supply adhesive secretions to contact interfaces, little efforts have been directed to the design of artificial fibrillar adhesive pads exploiting wet adhesion. One of the few examples reported to date enables adhesion switching by pumping water forth and back through micromachined arrays of holes with diameters of several tens of microns17.
In this work, we transfer a combination of wet adhesion and hydration-induced softening to bioinspired porous fibrillar adhesive pads (PFAPs). PFAPs consist of arrays of block copolymer nanorods serving as fibrillar contact elements, which are supported by a film-like substrate consisting of the same material. Most importantly, PFAPs contain continuous sponge-like pore systems open to the environment that enable the delivery of liquid from the smooth underside of the PFAP substrate to the tips of the fibrillar contact elements. As shown below, synergistic interaction of humidity-induced PFAP softening and wet adhesion via liquids supplied from PFAP undersides results in capillarity-supported formation of solid–solid contact between the liquid-infused PFAP and the counterpart surface (Fig. 1), resulting in adhesion enhancement and increase in the work of adhesion by two orders of magnitude. Capillarity-supported formation of solid–solid contact also results in the independence of pull-off force and work of adhesion from the applied load. At low RH, capillarity contributions (which are independent on RH) dominate the work of adhesion; the more the liquid is deposited on the counterpart surface, the higher are the work of adhesion and rupture distances of liquid bridges between the liquid-infused PFAP and the counterpart surface.
Results
Supply of liquid to the contact interface
The PFAPs (Fig. 2a,b) with an overall thickness of ≈110 μm consisted of the block copolymer polystyrene-block-poly(vinyl-2-pyridine) (PS-b-P2VP) and were prepared as described elsewhere18. The hydrophobic component PS formed a rigid, glassy skeleton, whereas the internal pore walls, as well as the outer surfaces, consisted of the polar component P2VP. The fibrillar contact elements (diameter≈300 nm; length≈1.5 μm) with hemispherical tips formed an array with a nearest-neighbour distance of≈500 nm. The average diameter of the internal pores of the PFAPs amounted to≈98 nm. The permeability of PFAPs was tested with mineral oil, which we selected as model for the oily secretions of insect setae19. The contact angles of mineral oil on P2VP and the spherical sapphire probe used for adhesion tests (see below) are summarized in the Supplementary Table 1. Imbibition tests with mineral oil revealed that the imbibition front propagated with an initial velocity of≈180 μm s−1 in the substrate planes of the tested PFAPs, whereas propagation slowed down after travel distances in the millimetre range (Fig. 2c). This outcome is in qualitative accordance with a Lucas–Washburn-type imbibition kinetics20. We estimate that mineral oil supplied from the smooth underside of a ~110 μm-thick PFAP reaches the tips of the fibrillar contact elements in <600 ms.
To demonstrate liquid delivery from the smooth undersides of PFAPs to the tips of the fibrillar contact elements, the smooth underside of a PFAP was placed on tissue paper (Fig. 3a). Mineral oil (typically 10 μl) was then dropped on the tissue paper in such a way that the tissue paper and the continuous pore system of the tested PFAP were just saturated, while submersion of the fibrillar contact elements was avoided (Fig. 3b). Mineral oil-infused PFAPs will thereafter be referred to as oPFAPs. In a typical experiment, the fibrillar contact elements of an oPFAP were carefully brought into contact with a glass slide and then detached. As revealed by white-light interferometry, discrete oil droplets with diameters ranging from ~300 nm to ~2.5 μm and heights of several tens of nanometres were deposited on the glass slide (Fig. 3c). The sizes of the mineral oil droplets were commensurate with the diameters of single fibrillar contact elements or small bunches of them. It is reasonable to assume that mineral oil bridges formed between single fibrillar contact element or small clusters of fibrillar contact elements and the counterpart surface, and ruptured upon detachment thus generating the droplet pattern seen in Fig. 3c.
Differences between wet adhesion and dry adhesion
Adhesion on PFAPs at RH≈25% was measured using a previously described method18,21 at room temperature. In brief, force-displacement curves were obtained by employing spherical sapphire probes with a diameter of 3 mm mounted on metal springs. A force-displacement curve measured on a PFAP in the absence of liquid at the contact interface representing a typical dry adhesion scenario is shown in Fig. 4a. For comparison, Fig. 4b shows a force-displacement curve measured on an oPFAP with a spherical sapphire probe already contaminated with mineral oil representing a typical wet adhesion scenario. In the approach branch of the force–distance curve (Fig. 4a) detected force equalled to zero until solid–solid contact between the spherical sapphire probe and the tested PFAP was formed. The solid–solid contact is assumed to form as soon as a positive force has to be applied to further displace the spherical sapphire probe into the tested PFAP. After the formation of solid–solid contact, the spherical sapphire probe was further displaced into the PFAP until a predefined positive loading force FL was reached. In contrast to the approach part seen in Fig. 4a, the approach part seen in Fig. 4b shows a marked jump-in event before the formation of the solid–solid contact. The jump-in associated with an attractive (that is, negative) jump-in force FJ started at the jump-in distance DJ. DJ corresponds to the displacement of the spherical sapphire probe from the position where the jump-in started to the position where the solid–solid contact is formed. The jump-in events, observed during the approach of mineral oil-contaminated spherical sapphire probes to the oPFAPs, were reminiscent of the jump-in events commonly observed during the approach of atomic force microscopy cantilever tips to counterpart surfaces caused by capillary condensation of water bridges22. We observed no jump-in during the first attach/detach cycle after mineral oil supply (for example, attach/detach cycle 1 in Fig. 5a), because the surface of the spherical sapphire probe was not contaminated with mineral oil during approach. However, the formation of solid–solid contact in the course of the first attach/detach cycle resulted in the transfer of mineral oil to the surface of the spherical sapphire probe. Thus, jump-in occurred in the second attach/detach cycle after mineral oil supply (for example, attach/detach cycle 2 in Fig. 5a) and in any further attach/detach cycle (attach/detach cycles 3–6 in Fig. 5a). Humidity can be ruled out as the origin of jump-in, since no indications of jump-in were apparent in the control experiments conducted in the absence of mineral oil within a RH range from 25 to 90% (ref. 18).
The retraction branch of the force-displacement curve seen in Fig. 4a starts as soon as the force maximum corresponding to FL has been passed. The applied force decreases during retraction and passes the zero-force line. Beyond the intersection of the retraction branch and the zero-force line, adhesion to the spherical sapphire probe drags the tested PFAP out of its equilibrium position, and the measured force becomes negative. Eventually, the retraction branch passes a sharp force minimum that is immediately followed by a sharp increase in force to the zero-force line. This shape of the retraction branch indicates instantaneous solid–solid separation at the displacement corresponding to the force minimum. The force minimum corresponds to the pull-off force (or adhesion force) Fad required to detach the spherical sapphire probe from the tested PFAP. In the presence of mineral oil at the contact interface (Fig. 4b), the retraction branch of the force-displacement curve also shows a distinct force minimum corresponding to Fad. However, after having passed the force minimum, the force–distance curve does not instantaneously relax to the zero-force line. Instead, it slowly approaches the zero-force line as the spherical sapphire probe is further retracted beyond the position of the force minimum. This feature of force-displacement curves measured in the presence of mineral oil at the contact interface can be attributed to the stretching and rupturing of liquid bridges formed between the oPFAP and the spherical sapphire probe after the separation of the solid–solid contact. The apparent rupture distance DR corresponds to the distance between the position of the force minimum Fad and the position beyond which the retraction branch coincides with the zero-force line. Thus, in the presence of mineral oil at the contact interface the force–distance curve shows pronounced hysteresis similar to atomic force microscopy force–distance curves measured with blunt cantilever tips23.
Wet adhesion at RH=25%
Figure 5a shows DJ, FJ, Fad and DR values obtained from a series of force–distance curves successively measured at the same position on a PFAP/oPFAP before and after the supply of mineral oil at FL≈500 μN and RH=25%. Supply of mineral oil resulted in an increase in Fad by one order of magnitude from 3.1±1.9 μN (average of three measurements at different positions on the tested PFAP) before mineral oil supply to 74.5 μN in the first attach/detach cycle after mineral oil supply (attach/detach cycle 1 in Fig. 5a). Further attach/detach cycles carried out at the same location yielded slightly decreased Fad values of≈56.7 μN that remained by and large constant over five further attach/detach cycles. FJ apparent in attach/detach cycles 2–6 after supply of mineral oil amounted to≈52.8 μN and remained by and large constant too. It is interesting to note that Fad approximately equalled FJ. DJ increased from 0.9 μm in the second attach/detach cycle after mineral oil supply (first occurrence of a jump-in) to 1.9 μm in the third attach/detach cycle and leveled off at ~3.0 μm in the attach/detach cycles subsequently measured at the same location. DR continuously increased from 4.8 μm in the first attach/detach cycle after mineral oil supply to≈18 μm. To investigate the dependence of Fad and DR on FL, we measured a series of force-displacement curves with successively increased FL at the same position on an oPFAP. Before the FL-dependent adhesion measurements, the spherical sapphire probe had 13 contacts with the same oPFAP at different positions. Fad and DR are largely independent of FL in the FL range from 45 to 800 μN (Fig. 5b). The Fad value of ~56 μN apparent from Fig. 5b corresponded to the Fad value obtained in the six successive attach/detach cycles measured at FL=500 μN seen in Fig. 5a. Moreover, Fig. 5b reveals that DR leveled off at ~22 μm. This outcome indicates that at RH=25% DR does not depend on FL. Moreover, the spherical sapphire probe was evidently saturated with mineral oil after the 13 previous contacts with the oPFAP so that during each of the measurements displayed in Fig. 5b liquid bridge rupture during retraction occurred in the same way.
Wet adhesion at RH=90%
While at RH=25% the effective elastic modulus Eeff of PFAPs amounted to 25.0 MPa, exposure of PFAPs to RH=90% for 4 min reduced Eeff to 4.2 MPa (Supplementary Fig. 1). Because of their enhanced mechanical compliance at RH=90%, PFAPs exhibit significantly better adhesive performance than at RH=25% (ref. 18). Supply of mineral oil at RH=90% led to an additional sharp jump in Fad by 389 μN from 166.3±25.4 μN (average of three measurements at different positions on the tested PFAP) to 569 μN for FL≈390 μN (Fig. 5c). In the five subsequent attach/detach cycles, Fad leveled off at≈530 μN. Similar to the results obtained for wet adhesion at RH=25%, at RH=90% the DR values were larger than the DJ values, and both the DR and DJ values increased in successively performed attach/detach cycles. At RH=90% FJ also increased during attach/detach cycles 2–6 after the supply of mineral oil but remained much smaller than Fad (Fig. 5c). The dependence of Fad and DR on FL is shown in Fig. 5d. Before the FL-dependent measurements, the sapphire sphere had 10 contacts with the tested oPFAP at a different position and was saturated with mineral oil. Such as at RH=25%, at RH=90% Fad was independent of FL within the tested FL range. In the absence of liquid at the contact interface, Fad at RH=90% monotonically increased along with FL within the considered FL range from Fad=16.2 μN for FL=39.4 μN to Fad=135.2 μN for FL=552.7 μN (Supplementary Fig. 2). Likewise, DR had a constant value of ~35 μm independent of FL.
Work of adhesion
The work of adhesion Wad is defined as the work required to separate the contacting surfaces. Wad corresponds to the area enclosed by the retraction branch of a force-displacement curve and the zero-force line between the intersection retraction branch/zero-force line and the displacement beyond which the retraction branch coincides with the zero-force line (Fig. 6). Wad can be separated into a contribution Wad,S required to break the solid–solid contact between fibrillar contact elements and spherical sapphire probe and a capillary contribution Wad,C required for stretching and rupturing the liquid bridges between the oPFAP and the spherical sapphire probe. Wad,S corresponds to the area enclosed by the retraction branch and the zero-force line between the intersection retraction branch/zero-force line and the displacement corresponding to the force minimum Fad (area marked by dark blue lines in Fig. 6). Wad,C corresponds to the area enclosed by the retraction branch and the zero-force line between the displacement corresponding to the force minimum Fad and the displacement beyond which the retraction branch coincides with the zero-force line (area marked by lines in magenta in Fig. 6).
Delivery of mineral oil to the contact interface resulted in a sharp increase in Wad. Wad at RH=25% and FL≈500 μN (Wad,25%) measured in the first attach/detach cycle after mineral oil supply amounted to 1.2 × 10−10 J and was 24.5 times larger than Wad,25% before mineral oil supply at the same FL value. Such as Fad, Wad,S remained by and large constant in attach/detach cycles 1–6 after the supply of mineral oil, even though the Wad,S values scattered to some extent from 6.4 × 10−11 J to 2.9 × 10−11 J (Fig. 7a). Wad,C monotonically increased in the six attach/detach cycles successively measured after mineral oil supply from 5.5 × 10−11 J (first attach/detach cycle after mineral oil supply) to 2.6 × 10−10 J (sixth attach/detach cycle after mineral oil supply). In the second attach/detach cycle after mineral oil supply and in all further cycles, Wad,C was by far the dominant contribution to Wad,25%. After >10 contacts of spherical sapphire probe and oPFAP, the sapphire surface was apparently saturated with mineral oil; Wad,C leveled off at ~4 × 10−10 J and Wad,S at 4 × 10−11 J. Once Wad,S and Wad,C had reached these values, Wad,S and Wad,C were evidently independent of FL (Fig. 7b).
Wad at RH=90% (Wad,90%) was 8.5 times larger in the presence than in the absence of mineral oil. In the first attach/detach cycle after delivery of mineral oil, Wad,90% amounted to 22.7 × 10−10 J (Fig. 7c) and was almost 20 times larger than Wad,25%=1.2 × 10−10 J. The difference between Wad,25% and Wad,90% was nearly exclusively caused by the difference in Wad,S. Wad,S at RH=90% and FL≈390 μN lay in the range from 19.3 × 10−10 J to 23.3 × 10−10 J (Fig. 7c) and was, therefore, nearly one order of magnitude larger than at RH=25% and FL≈500 μN. In contrast to the situation at RH=25%, in all attach/detach cycles at RH=90% Wad,S was by far the dominating contribution to Wad,90%. In the first two attach/detach cycles after supply to mineral oil, the contribution of Wad,C to Wad,90% was negligible. In attach/detach cycles 3–6 after mineral oil supply, a slight increase in Wad,C to 5.1 × 10−10 J occurred. After >10 contacts of spherical sapphire probe and oPFAP, Wad,S levelled off at ~18 × 10−10 J and Wad,C at 5 × 10−11 J. Again, Wad,S and Wad,C were independent of FL once Wad,S and Wad,C had reached these values (Fig. 7d).
In contrast to the significantly different Wad,S values at RH values of 25 and 90%, the Wad,C values obtained at these two RHs lay in a similar range, as obvious from Fig. 7b,d. Therefore, the capillary contribution Wad,C to Wad is, if at all, only weakly dependent on RH. It is, however, obvious that Wad,C correlates with DR; the larger DR is, the larger is Wad,C (Fig. 8). Once DR remains constant, Wad,C also remains constant (Figs 5b and 7b and Figs. 5d and 7d, respectively, show the same set of measurements).
Discussion
The capillarity contribution to adhesion is caused by the formation of liquid bridges after the separation of the solid–solid contact between the spherical sapphire probe and the oPFAP at the position of the force minimum Fad. Further retraction leads to the stretching and eventually to the rupture of the liquid bridges. DR can be interpreted as the distance between the position of solid–solid contact separation and the position at which all the liquid bridges are ruptured. Consequently, Wad,C is the work required to stretch and rupture all the liquid bridges. In contrast to Wad,S, Wad,C does apparently not depend on RH; the magnitude of Wad,C was the same for RH values of 25 and 90% (Fig. 8). The implications of this outcome are as follows. (i) Wad,25% at RH=25% is dominated by the capillarity contribution Wad,C, whereas Wad,90% at RH=90% is dominated by the solid–solid contribution Wad,S. (ii) The properties of the liquid bridges formed between the spherical sapphire probe and the oPFAP are not influenced by RH as such or by the humidity-induced softening of the oPFAP induced by an increase in RH. This finding may be rationalized as follows. Before the emergence of liquid bridges, the oPFAPs mechanically relax. Thus, at the moment of liquid bridge formation the actual contact area between the spherical sapphire probe and the oPFAP is similar for the tested RHs. This view is supported by the finding that independent of RH, neither DR (Fig. 5b,d) nor Wad,C (Fig. 7b,d) depends on FL in the tested FL range from 45 to 800 μN. Hence, FL does not influence liquid bridge formation and rupture. (iii) We can rule out that capillary condensation of water from the gas phase significantly influences adhesion.
Before the first contact between the spherical sapphire probe and the oPFAP after mineral oil supply, the spherical sapphire probe is not contaminated with mineral oil. During retraction in the course of the first attach/detach cycle after mineral oil supply, liquid bridges between single fibrillar contact elements or small bunches of fibrillar contact elements and the spherical sapphire probe form once the solid–solid contact is separated. Hence, patterns of discrete mineral oil droplets remain on counterpart surfaces after rupture of the liquid bridges (see Fig. 3c). Because the spherical sapphire probe has a much smaller curvature than the tips of the fibrillar contact elements, the larger portion of the mineral oil forming the liquid bridges will remain on the spherical sapphire probe when the liquid bridges rupture24,25. In the first attach/detach cycle after supply of mineral oil and in attach/detach cycles carried out thereafter the rupture of the liquid bridges will redistribute liquid from the oPFAP to the spherical sapphire probe. Hence, the amount of mineral oil on the surface of the spherical sapphire probe increases after every attach/detach cycle. The amount of mineral oil that can be supplied from the surface of the spherical sapphire probe to the formation of the liquid bridges in turn increases in each successively performed attach/detach cycle.
DR increases along with the volumes of the rupturing liquid bridges23,26,27,28. In attach/detach cycles 1–6 after the supply of mineral oil, DR gradually increases for both the tested RH values of 25 and 90%. It is reasonable to assume that the volumes of the liquid bridges formed between the oPFAP and the spherical sapphire probe increase along with the amount of mineral oil that can be supplied to the liquid bridges from the surface of the spherical sapphire probe. Hence, the observed increase in DR in attach/detach cycles 1–6 after mineral oil supply (Fig. 5a,c) is presumably related to the ability of the spherical sapphire probe to supply more mineral oil to the liquid bridges as the more mineral oil is available on its surface the more attach/detach cycles were performed. Therefore, DR depends on the distribution of liquid between the oPFAP and the spherical sapphire probe; the more mineral oil redistributed to the spherical sapphire probe, the higher is the apparent DR value. Wad,C increases along with DR (Fig. 8). Hence, Wad,C gradually increases in attach/detach cycles 1–6 after mineral oil supply (Fig. 7a,c). After about six attach/detach cycles, DR (Fig. 5b,d) as well as Wad,C (Fig. 7b,d) reach a plateau and remain constant in further attach/detach cycles. Apparently, the liquid distribution between the oPFAP and the spherical sapphire sphere reaches a state of saturation. Either the liquid is no longer redistributed or further liquid redistribution does not influence the structure and the rupture of the liquid bridges. The apparent DR values of ~22 μm at RH=25% and of ~35 μm at RH=90% in the saturated state indicate that the liquid bridges are no longer formed between single contact elements or small bunches of contact elements of the oPFAP and the spherical sapphire probe. Instead, the oPFAP apparently immerses into the mineral oil layer on the spherical sapphire probe so that one single liquid bridge between the oPFAP and the spherical sapphire probe is formed.
The contribution of solid–solid contact is represented by Fad and Wad,S. In the retraction branches, Fad marks the position at which solid–solid contact is separated, and Wad,S is the work required to separate the solid–solid contact. The increases in Fad by humidity-induced softening and by the supply of mineral oil to the contact interface are synergistic, resulting in an increase in Fad by two orders of magnitude. The increase in Fad caused by mineral oil supply at the given RH is evidently larger at RH=90% (increase in Fad=389 μN; Fig. 5c) than at RH=25% (increase in Fad=70 μN; Fig. 5a). We assume that this outcome can be rationalized by the larger actual solid–solid contact area at higher RH caused by humidity-induced softening of the PFAPs/oPFAPs. This view is supported by the fact that the presence of mineral oil at the contact interface Wad,S increases by nearly one order of magnitude when RH is increased from 25 to 90% (Fig. 7).
In the case of oPFAPs, both Fad (Fig. 5a,c) and Wad,S (Fig. 7a,c) are independent of the amount of liquid deposited on the spherical sapphire probe. In contrast to DR and Wad,C, both the parameters remain by and large constant in the attach/detach cycles 1–6 performed after the supply of mineral oil as well as after the saturation of the spherical sapphire probe with mineral oil. While DR no longer reflects contact splitting if the spherical sapphire probe is saturated with mineral oil, it appears that the solid–solid contact is still dominated by the contact between the single contact elements (or small clusters of contact elements) and the spherical sapphire probe.
The independence of Fad on FL is a striking difference between wet adhesion on oPFAPs and dry adhesion on PFAPs. Under dry adhesion conditions, Fad increases along with FL until a plateau is reached. This behaviour could be reproduced with a modified Schargott−Popov−Gorb (SPG) model18,21. The modified SPG model introduces an additional parameter, the probability of the contact formation between the contact elements and the spherical sapphire probe as a function of FL. Thus, only a FL-dependent fraction of contact elements within the contact area is in contact with the spherical sapphire probe. Fad depends on the fraction of the contact elements in contact with the spherical sapphire probe and, therefore, on FL. Only above a certain FL threshold value, all the contact elements are in contact with the spherical sapphire probe and Fad does not change if FL is further increased.
The independence of Fad on FL, which is in agreement with the classical Johnson−Kendall−Roberts theory29, as well as the strong increase in Fad upon supply of mineral oil independent of RH may be rationalized by assuming capillarity-supported formation of solid-solid contact (Fig. 1). In the absence of mineral oil at the contact interface, the contact formation between the PFAP and the spherical sapphire probe is imperfect, as predicted by the modified SPG model. However, as an oPFAP is approached to a counterpart surface such as a spherical sapphire probe (Fig. 1a), liquid bridges form and exert attractive forces between the two solid surfaces connected by the liquid bridges (Fig. 1b). These attractive forces may be related to the surface tension of the liquid bridge (and the resulting capillary pressure) as well as to contact line tension. The tendency to form liquid bridges between the contact elements soaked with mineral oil and spherical sapphire probe tethers the contact elements to the spherical sapphire probe without the need of applying load (Fig. 1c). The enhanced solid–solid contact mediated by capillarity in turn increases Fad and Wad,S.
oPFAPs may represent the starting point for the deliberate implementation of insect-inspired wet adhesion in the design of artificial adhesive systems. However, several features of oPFAPs may be further improved in the future. For example, we are not able to completely avoid the clustering of the fibrillar contact elements of oPFAPs. Enhancing the performance of oPFAPs by the prevention of clustering is a challenging optimization problem. On the one hand, clustering deteriorates the performance of fibrillar adhesive systems. On the other hand, straightforward changes in the array geometry that prevent clustering, such as the reduction of the contact elements’ aspect ratio or increasing in the nearest-neighbour distance between the contact elements, also inevitably reduce adhesion. We believe that hybrid systems consisting of contact elements of a stiffer material connected to compliant substrates may show even better performance than the oPFAPs tested in this work.
Methods
Materials
PS-b-P2VP (Mn(PS)=101,000 g mol−1; Mn(P2VP)=29,000 g mol−1; Mw/Mn (PS-b-P2VP)=1.60) was obtained from Polymer Source Inc., Canada and used as received. Mineral oil, tetrahydrofuran and ethanol were purchased from Sigma-Aldrich.
Microscopic characterization
SEM and cryo-SEM investigations were carried out on a Zeiss Auriga microscope operated at an accelerating voltage of 3 kV. The samples were sputter-coated with a 5 nm-thick iridium layer. White-light interferometry, an established non-contact surface profiling method30, was carried out using a NewView 6200 white-light interferometer (ZygoLOT GmbH, Darmstadt, Germany). The light reflection from the boundary between two materials with different refractive indexes is registered with the white-light interferometer. Because of the small difference in the refractive indexes, the reflection from the interface between oil (n=1.40) and the glass (n=1.47) is neglected compared with the reflection from the interface between oil and air (n=1.00).
Adhesion tests
Force-displacement curves were measured at 20 °C on PFAPs and oPFAPs with areas of about 5 × 5 mm2 mounted on a hexapod nanopositioning stage (Physik Instrumente, Karlsruhe, Germany) using a home-built force tester Basalt-02. Sapphire spheres with a diameter of 3 mm glued to the free end of a metal spring with a spring constant Cspring=69.8 N m−1 were used as probes that could be vertically moved with a piezo drive. The spherical sapphire probes were cleaned with acetone before a new series of measurements was carried out. The approach and retraction speeds of the spherical sapphire probes during the measurements were 2 μm s−1. Retraction started immediately when the predefined FL values were reached. The deflection of the metal spring during the approach and the retraction was monitored with a laser interferometer and converted into force. For data collection, a custom-made Labview software package was used. All force-displacement curves were acquired in a homemade humidity chamber at room temperature, as described in detail in the supporting information to ref. 18. RH values were controlled by mixing dry N2 and saturated water vapour at different ratios.
Additional information
How to cite this article: Xue L. et al. Humidity-enhanced wet adhesion on insect-inspired fibrillar adhesive pads. Nat. Commun. 6:6621 doi: 10.1038/ncomms7621 (2015).
References
Kamperman, M. et al. Functional adhesive surfaces with "gecko" effect: the concept of contact splitting. Adv. Eng. Mater. 12, 335–348 (2010) .
Xue, L., Steinhart, M. & Gorb, S. N. Biological and bioinspired micro- and nanostructured adhesives. Biomater. Surf. Sci. Ch. 14 Wiley-VCH (2013) .
Autumn, K. et al. Adhesive force of a single gecko foot-hair. Nature 405, 681–685 (2000) .
Autumn, K. et al. Evidence for van der Waals adhesion in gecko setae. Proc. Natl Acad. Sci. USA 99, 12252–12256 (2002) .
Peisker, H., Michels, J. & Gorb, S. N. Evidence for a material gradient in the adhesive tarsal setae of the ladybird beetle Coccinella septempunctata. Nat. Commun. 4, 1661 (2013) .
Puthoff, J. B., Prowse, M. S., Wilkinson, M. & Autumn, K. Changes in materials properties explain the effects of humidity on gecko adhesion. J. Exp. Biol. 213, 3699–3704 (2010) .
Gorb, S. N. et al. Silk-like secretion from tarantula feet. Nature 443, 407 (2006) .
Eisner, T. & Aneshansley, D. J. Defense by foot adhesion in a beetle (Hemisphaerota cyanea). Proc. Natl Acad. Sci. USA 97, 6568–6573 (2000) .
Federle, W., Riehle, M., Curtis, A. S. G. & Full, R. J. An integrative study of insect adhesion: mechanics and wet adhesion of pretarsal pads in ants. Integr.Comp. Biol. 42, 1100–1106 (2002) .
Langer, M. G., Ruppersberg, J. P. & Gorb, S. Adhesion forces measured at the level of a terminal plate of the fly’s seta. Proc. R. Soc. Lond. B 271, 2209–2215 (2004) .
Gorb, E. V., Hosoda, N., Miksch, C. & Gorb, S. N. Slippery pores: anti-adhesive effect of nanoporous substrates on the beetle attachment system. J. R. Soc. Interface 7, 1571–1579 (2010) .
Dirks, J.-H. & Federle, W. Fluid-based adhesion in insects – principles and challenges. Soft Matter 7, 11047–11053 (2011) .
Gorb, S. N. The design of the fly adhesive pad: distal tenent setae are adapted to the delivery of an adhesive secretion. Proc. R. Soc. Lond. B 265, 747–752 (1998) .
Gorb, S. N. Porous channels in the cuticle of the head-arrester system in dragon/damselflies. Microsc. Res. Tech. 37, 583–591 (1997) .
Bauchhenß, E. Die Pulvillen von Calliphoraerythrocephala (Diptera, Brachycera) als Adhäsionsorgane. Zoomorphologie 93, 99–123 (1979) .
Dirks, J.-H. & Federle, W. Mechanisms of fluid production in smooth adhesive pads of insects. J. R. Soc. Interface 8, 952–960 (2011) .
Vogel, M. J. & Steen, P. H. Capillarity-based switchable adhesion. Proc. Natl Acad. Sci. USA 107, 3377–3381 (2010) .
Xue, L. et al. Reversible adhesion switching of porous fibrillar adhesive pads by humidity. Nano Lett. 13, 5541–5548 (2013) .
Peisker, H. & Gorb, S. N. Evaporation dynamics of tarsal liquid footprints in flies (Calliphora vicina) and beetles (Coccinella septempunctata). J. Exp. Biol. 215, 1266–1271 (2012) .
Gruener, S. & Huber, P. Imbibition in mesoporous silica: rheological concepts and experiments on water and a liquid crystal. J. Phys. Condens. Matter 23, 184109 (2011) .
Xue, L. et al. Tailoring normal adhesion of arrays of thermoplastic, spring-like polymer nanorods by shaping nanorod tips. Langmuir 28, 10781–10788 (2012) .
Butt, H.-J. & Kappl, M. Normal capillary forces. Adv. Colloid Interface Sci. 146, 48–60 (2009) .
Sirghi, L., Szoszkiewicz, R. & Riedo, E. Volume of a nanoscale water bridge. Langmuir 22, 1093–1098 (2006) .
Pepin, X., Rossetti, D., Iveson, S. M. & Simons, S. J. R. Modeling the evolution and rupture of pendular liquid bridges in the presence of large wetting hysteresis. J. Colloid Interfe Sci. 232, 289–297 (2000) .
Deliang, S. & McCarthy, J. J. Numerical simulation of liquid transfer between particles. Powder Technol. 184, 64–75 (2008) .
Lian, G., Thornton, C. & Adams, M. J. A theoretical study of the liquid bridge forces between two rigid spherical bodies. J. Colloid Interface Sci. 161, 138–147 (1993) .
Willett, C. D., Adams, M. J., Johnson, S. A. & Seville, J. P. K. Capillary bridges between two spherical bodies. Langmuir 16, 9396–9405 (2000) .
Slater, D. M., Vogel, M. J., Ashley, M., Macner, A. M. & Steen, P. H. Beetle-inspired adhesion by capillary-bridge arrays: pull-off detachment. J. Adhes. Sci. Technol. 28, 273–289 (2014) .
Prokopovich, P. & Starov, V. Adhesion models: From single to multiple asperity contacts. Adv. Colloid Interface Sci. 168, 210–222 (2011) .
Abdulhalim, I. Spatial and temporal coherence effects in interference microscopy and full-field optical coherence tomography. Ann. Phys. (Berlin) 524, 787–804 (2012) .
Acknowledgements
We thank C. Hess and H. Tobergte for the preparation of AAO membranes. This study was partly supported by the SPP 1420 of the German Science Foundation (DFG) ‘Biomimetic Materials Research: Functionality by Hierarchical Structuring of Materials and by the project number C-10 within DFG SFB 677’. L.X. thanks the Alexander-von-Humboldt Foundation for a fellowship.
Author information
Authors and Affiliations
Contributions
L.X., M.S. and S.N.G. designed the project. L.X. and A.E-V. fabricated the structure and measured with SEM. L.X. performed adhesion measurements and analysed the data. L.X. and M.S. wrote the paper. L.X., M.S., A.K. and S.N.G. discussed the results and commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-2, Supplementary Table 1 and Supplementary References (PDF 173 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Xue, L., Kovalev, A., Eichler-Volf, A. et al. Humidity-enhanced wet adhesion on insect-inspired fibrillar adhesive pads. Nat Commun 6, 6621 (2015). https://doi.org/10.1038/ncomms7621
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms7621
- Springer Nature Limited
This article is cited by
-
Development of wet adhesion of honeybee arolium incorporated polygonal structure with three-phase composite interfaces
Friction (2024)
-
Intelligent structured nanocomposite adhesive for bioelectronics and soft robots
Nano Research (2024)
-
Nature-inspired micropatterns
Nature Reviews Methods Primers (2023)
-
Electrically switched underwater capillary adhesion
Nature Communications (2022)
-
Locally coupled electromechanical interfaces based on cytoadhesion-inspired hybrids to identify muscular excitation-contraction signatures
Nature Communications (2020)