Influence of Residual Stress on Shape of Heavy-gauge, High-strength Steel Caused by Cooling Process after Hot Rolling

  • Metallurgy and Metal Working
  • Published:
Journal of Iron and Steel Research International Aims and scope Submit manuscript

Abstract

The cooling process following hot rolling has a significant effect on the shape quality of a hot-rolled strip. The temperature and stress fields in the cooling process for a 14 mm thick strip with yield strength of 500 MPa grade were analyzed by the finite element method and actual test data, and the relationship between residual stress and shape defects was described. Subsequently, the small-crown rolling process and the coil slow cooling process were investigated. The results indicate that these processes improved the shape quality of the final product significantly.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others

References

  1. H. B. Xie, X. H. Liu, G. D. Wang, Z. P. Zhang, J. Iron Steel Res. Int. 13 (2006) No. 1, 18–22.

    Article  Google Scholar 

  2. J. Wang, G. D. Wang, X. H. Liu, J. Iron Steel Res. Int. 11 (2004) No. 5, 13–17.

    Google Scholar 

  3. D. H. Zhang, N. Zhou, B. X. Wang, M. Zhang, J. Iron Steel Res. Int. 17 (2010) No. 1, 18–21.

    Article  Google Scholar 

  4. V. B. Ginzburg, High Quality Steel Rolling Theory and Practice, Metallurgical Industry Press, Beijing, 2002.

    Google Scholar 

  5. C. X. Xiao, Baosteel Technology (2000) No. 3, 1–5.

    Google Scholar 

  6. Q. L. Cui, M. Zhao, G. Yuan, X. H. Liu, G. D. Wang, J. Iron Steel Res. 19 (2007) No. 9, 21–23.

    Google Scholar 

  7. Z. Cai, G. D. Wang, X. H. Liu, K. Zhao, J. G. Yuan, Iron and Steel 35 (2000) No. 6, 33–36.

    Google Scholar 

  8. X. H. Cai, Z. A. Luo, G. D. Wang, X. H. Liu, J. Iron Steel Res. Int. 11 (2004) No. 1, 26–28.

    Google Scholar 

  9. W. Yu, X. J. Lu, Y. L. Chen, B. Bai, Iron and Steel 46 (2011) No. 4, 44–45.

    Google Scholar 

  10. S. J. Lu, Wide and Heavy Plate 9 (2003) No. 6, 34–35.

    Google Scholar 

  11. Y. P. Su, Q. Yang, A. R. He, X. D. Wang, H. T. Bian, Steel-making 43 (2008) No. 5, 55–59.

    Google Scholar 

  12. J. F. Chen, Z. D. Liu, H. Dong, Y. Gan, Iron and Steel 39 (2004) No. 10, 40–44.

    Google Scholar 

  13. J. Q. Sun, J. C. Lian, J. Yanshan Univ. 22 (1998) No. 3, 222–223.

    Google Scholar 

  14. J. Q. Sun, J. H. Sun, B. Wu, J. C. Lian, J. Iron Steel Res. Int. 12 (2005) No. 2, 33–36.

    Google Scholar 

  15. X. D. Wang, F. Li, Q. Yang, A. R. He, Applied Mathematical Model 37 (2013) 586–609.

    Article  MathSciNet  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Yong-lin Kang.

Additional information

Foundation Item: Item Sponsored by National Natural Science Foundation of China (U1460101)

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Wang, Sz., Kang, Yl., Zhu, Gm. et al. Influence of Residual Stress on Shape of Heavy-gauge, High-strength Steel Caused by Cooling Process after Hot Rolling. J. Iron Steel Res. Int. 23, 547–552 (2016). https://doi.org/10.1016/S1006-706X(16)30086-3

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1016/S1006-706X(16)30086-3

Key words

Navigation