Abstract
This study reports the synthesis and photoluminescence spectroscopic studies of Cr3+-doped Mg2SnO4–SnO2 ceramics. The crystal structure was analyzed by X-ray powder diffraction, and photoluminescence was investigated at room temperature. The diffractogram confirmed the presence of Mg2SnO4 and SnO2 phases. Photoluminescence spectroscopy identified broad and intense emission bands assigned to the Cr3+ cation occupation in octahedral Mg2SnO4 sites and an orange band assigned to SnO2 emission. All spectra were analyzed and interpreted according to crystal field theory and Tanabe–Sugano theory for the d3 electronic configuration. The broad and intense emission band covering the visible/near-infrared region suggests that this system may be a promising material for use as an active medium in a broadband light source at room temperature.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Ceramics with multifunctional applications have been widely explored both commercially and scientifically. The physical properties of ceramics are currently being studied to discover and optimize new applications, with the advantage of being environmentally friendly and relatively inexpensive. A successful example is magnesium stannate (Mg2SnO4) ceramics, which exhibit dielectric, semiconductor, photocatalytic and luminescent properties. These properties make these ceramics suitable for applications at high temperatures and frequencies as electronic ceramics in thermally stable capacitors [1, 2]; as monopole antennas for radio and wireless communications [3]; as an alternative anode material in Li-ion batteries [4, 5]; and for photocatalysis [6, 7], optical storage and optical communications [8], among other uses. The synthesis of these ceramics is relatively easy, mostly carried out by solid-state reactions at high temperatures [1, 5, 9], although other routes have also been explored [4, 6, 10].
Luminescent undoped Mg2SnO4 properties are intimately related to its crystal environment. The Mg2SnO4 crystal structure is a cubic inverse spinel of the II–IV type (with the molecular formula A2+2B4+O2−4), where Mg2+ and Sn4+ are randomly located in octahedral sites, while tetrahedral sites are fully occupied by Mg2+ [11,12,13,14]. Several authors report the emission of undoped Mg2SnO4 through thermoluminescence and photoluminescence mechanisms [8, 11, 15, 16]. Behrh [11] and Zhang [15] proposed that the high disorder degree originating from lattice defects is responsible for the luminescent properties of this system. Zhang also observed that the undoped compound exhibits a band centered at 498 nm when irradiated with ultraviolet radiation due to the recombination of oxygen vacancies with crystal structure holes. To the best of our knowledge, no reports on undoped Mg2SnO4 emissions in the infrared region are available. The electron trapping feature makes magnesium stannate an adequate material for use in optical storage and imaging techniques [15].
The doped Mg2SnO4 crystal system has been studied using transition metals and lanthanide cations as activators. Zhang and Li reported the broadband emission of Mg2SnO4:Ti4+ in the blue–green region under ultraviolet excitation [9, 12]. Li pointed out that Mn2+-doping enlarged the undoped band emission in the green region [9], while other authors have also studied Mn2+-doped samples [17,18,19]. When doped with divalent cobalt, the compound exhibits an intense broadband in the red–infrared range due to the Co2+ activator in tetrahedral sites [20]. Recently, Cai et al. presented results for single-phase Mg2-xSnO4:xCr3+ [21], observing emission bands centered at approximately 750 nm for several Cr3+ concentrations. Zhang detailed the photoluminescent properties of Mg2SnO4:Eu3+, reporting reddish emission at room temperature [22], while Guo analyzed Mg2SnO4:Pr3+ emissions, detecting bands centered at 530 nm and 570 nm [23].
The crystal structure of tin oxide (SnO2) is usually reported as rutile type, with tetragonal symmetry where the Sn4+ cations are in the center of the octahedra formed by O2− anions [24]. The luminescent properties of this system have been previously investigated by Gu and coauthors, who observed a band in the emission spectrum between 400 and 450 nm [25]. The authors claim that this emission originates from electron transitions mediated by oxygen vacancies. Garcia-Tecedor et al. reported broad emission in undoped SnO2 [26], with peaks centered at 1.94 eV (639 nm), 2.25 eV (551 nm) and 2.58 eV (480 nm) also originating from oxygen vacancies and surface defects. To the best of our knowledge, no reports of undoped SnO2 emissions in the infrared region are available.
It is well known that the trivalent chromium cation is used as an activator in ceramic systems, inducing intense red–infrared emission caused by its optical transitions related to the splitting of its energy levels in an octahedral environment. This intense luminescence presents several applications depending on the lattice. For example, NaAl(WO4)2:Cr3+ has been used as a broadband laser source [27], LiInSi2O6:Cr3+ in LED-based devices [28], ZnGa2O4:Cr3+ and LaAlO3:Cr3+ in in vivo imaging [29, 30], LaAlO3:Cr3+, Ca2+ in energy-saving applications [31] and NaGd0.78F4:Yb0.2/Er0.02/Cr3+x in luminescence-based temperature sensors [32].
In this context, as Mg2SnO4 and SnO2 single phases have been reported as presenting emissions separately at room temperature, the aim of the present study was to investigate whether it is possible to obtain a system exhibiting broadband emissions from the combination of both compounds and the addition of Cr3+ as an activator. The present study reports the structural and photoluminescent properties of a Cr3+-doped Mg2SnO4–SnO2 system. Samples were prepared through the solid-state method at high temperatures. The system structure was investigated by X-ray diffraction, and the relevant crystallographic parameters were obtained using the Rietveld method. Elemental analysis was performed using X-ray microfluorescence. Photoluminescence emission and excitation at room temperature were used to identify the optical transitions. The results indicate broadband emission, leading to a system with a photoluminescent signal covering almost the entire visible/near-infrared range.
2 Experimental
Samples were synthesized using the raw chemicals MgO (99%, Riedel-de Häen), SnO2 (99.9%, Sigma-Aldrich) and Cr2O3 (99%, Vetec) as starting materials in powder form to obtain Mg2(1−x)Cr2xSnO4 (x = 0.001) + SnO2. The samples were prepared by the conventional solid-state reaction. Powder oxides were manually weighed and crushed for homogenization. Subsequently, the powder was pressed in an axial direction into 13-mm-diameter and 1-mm-thick pellets under 296 MPa pressure. The pellets were then deposited in alumina crucibles for sintering, undergoing a thermal treatment where they were heated until 1200 °C in an electric furnace under atmospheric pressure at a heating rate of 10 °C/min, remaining at 1200 °C for 6 h. Then, the pellets were removed from the furnace at room temperature, and one pellet was crushed until a homogeneous, thin powder was obtained for the X-ray diffraction experiments.
The diffraction pattern was obtained at room temperature using a Bruker D2 Phaser diffractometer with Cu-Kα1 radiation (λ = 1.54056 Å) operating at 30 kV and 10 mA. Data were collected in a Bragg–Brentano geometry with 15° < 2θ < 80° and a step size of 0.01°. X-ray diffraction data were refined by the Rietveld method using the FullProf package [33] with comparative data from the Inorganic Crystal Structure Database (ICSD). The Rietveld refinement provides information about the space group, lattice parameters and phase quantification.
The sample chemical composition was verified through elemental analysis by X-ray microfluorescence (μXRF) using an M4 Tornado Bruker system with a Rh target X-ray tube operating at 40 kV and 500 μA. The spectra were collected in distinct spots in one pellet for 30 s.
Photoluminescence experiments (emission and excitation spectra) were performed at room temperature using a PTI 300 QuantaMaster spectrofluorometer equipped with a 75 W pulsed xenon lamp operating at 200 Hz and 1 nm spectral resolution. A PTI 914 Photomultiplier Detection System model R928 (185–900 nm range, peak at 400 nm) was used for signal detection. Filters were used to block excitation and scattered lights in the emission detection apparatus. All photoluminescence spectra were corrected by the apparatus sensitivity response.
3 Results
3.1 Crystal structure and elemental analysis
Figure 1 displays the powder diffractogram recorded at room temperature. The most intense peaks were assigned to the Mg2SnO4 phase, while some peaks that did not match this phase were identified to be the SnO2 phase. Rietveld refinement was performed using cubic Mg2SnO4 (ICSD code 28199) and tetragonal SnO2 (ICSD code 84576) data files as input. According to the refinement, the phase proportion in the sample was 59% Mg2SnO4 and 41% SnO2. Mg2SnO4 crystallized in the \(Fd\bar{3}m\) space group with cubic symmetry. The observed SnO2 phase exhibited a rutile-type structure in the \(P4_{2} /{\text{mnm}}\) space group and tetragonal symmetry. Structural details obtained from the Rietveld refinement are displayed in Table 1. The agreement factors presented in Table 1 indicate good correspondence between the calculated and observed patterns. The goodness-of-fit index (GOF index) extracted from the refinement was 1.6, indicating high refinement quality.
It was important to estimate the Cr3+ occupation position in the identified phases in the sample, keeping in mind that the percentage difference between the atomic radii of the inserted and replaced cations must be lower than 15% [34]. The atomic radius of Mg2+ is 0.57 Å when its coordination number (CN) is 4 and 0.72 Å when CN = 6, changing to 0.69 Å and 0.62 Å for Sn4+ and Cr3+, respectively, with CN = 6 [35]. Therefore, when assessing ionic radius and cation symmetry, it was noted that Cr3+ can replace both Mg2+ and Sn4+ in octahedral symmetry, since the ionic radius percentage difference is close to 14% between Mg2+ and Cr3+, while it is 10% between Sn4+ and Cr3+, considering CN = 6 for all cations. When assessing the cation valence involved in the occupation of the octahedral sites (Cr3+, Mg2+ and Sn4+), we believe that the most likely replacement to occur will be with Cr3+-occupying octahedral Mg2+ sites. This replacement would be more favorable, requiring only one electron to perform charge compensation, and this electron could then be shared by the O2− anions with Cr3+, generating a covalent bond between O2− and Cr3+, allowing for Mg2+ replacement.
As mentioned previously, Mg2SnO4 contains tetrahedral and octahedral sites, while SnO2 is composed of Sn4+ surrounded by oxygen anions, with octahedral symmetry in a tetragonal system. It is well known that Cr3+ tends to preferably occupy octahedral sites. Photoluminescence spectroscopy may indicate the occupation symmetry of Cr3+ in the occupied phase(s), according to the position and shape of the observed emission and excitation bands.
The room temperature X-ray microfluorescence spectrum for the sample is depicted in Fig. 2. The measurements were performed in several regions on the sample surface, with similar results showing sample homogeneity. Peaks at 1.2651 keV (Mg-Kα1), 3.4549 keV (Sn-Lα1), 3.6948 keV (Sn-Lβ1) and 5.4247 keV (Mg-Kα1) were identified. The weakest peaks close to the intense Sn peaks were identified as weak Sn lines. The Rh peak was due to the anode of the X-ray tube.
3.2 Emission and excitation spectra
Figure 3 exhibits the photoluminescence spectra of the Cr3+-doped sample with excitations at (a) 300 nm and (b) 450 nm at room temperature. Under 300 nm excitation (Fig. 3a), the sample displayed broad emission in the visible/near-infrared range, exhibiting two intense bands with maxima located at 614 nm and 783 nm, in addition to a weak signal at 701 nm. The width of the band at 783 nm is related to a characteristic emission from an energy level strongly dependent on the crystal field in an octahedral environment. From this evidence, the band at 783 nm was assigned to the 4T2(4F) → 4A2(4F) Cr3+ transition [36, 37].
Several studies have reported lattice emissions near 500 nm under ultraviolet excitation, originating from the recombination of oxygen vacancies with holes in the Mg2SnO4 lattice, probably caused by the number of defects generated by the cation disorder commonly found in the inverse spinel structure [11, 12, 14, 15]. This emission was not observed herein, and the band at 614 nm was far from the previously reported Mg2SnO4 emission.
Previous studies have described characteristic undoped SnO2 emissions of approximately 1.94 eV (639 nm) [26, 38]. Arai and Adachi reported an emission signal at approximately 610 nm (λexc = 290 nm) in undoped SnO2 nanopowder [39]. Based on these studies, the band located at 614 nm was assigned to the SnO2 lattice emission. The bluish Mg2SnO4 emission mentioned previously at approximately 500 nm was probably hidden by the SnO2 emission band. Figure 3a displays intense broadband emission over a broad range from the blue to infrared region (450–850 nm), indicating that the Mg2SnO4:Cr3+ + SnO2 system was highly effective in achieving a system with intense broadband emission at room temperature.
Figure 3b displays the emission spectrum under 450 nm excitation, exhibiting a broadband located in the near-infrared range with a maximum at 792 nm. Two weak structures were observed in this spectrum at 695 nm and 703 nm. The emission signal increased over twofold (relative to Fig. 3a) under 450 nm excitation. This can be an indication that the main emitting centers in the sample are the Cr3+ cations located in the octahedral sites since it is known that wavelengths in the blue region are easily absorbed by Cr3+ ions in this coordination. The emission at 792 nm was assigned to the 4T2(4F) → 4A2(4F) Cr3+ transition in octahedral symmetry for the same reasons explained above. The structures overlapping with the broadband at 701 nm in Fig. 3a and 695 nm and 703 nm in Fig. 3b nm were identified as the R-lines corresponding to the 2E(2G) → 4A2(4F) spin-forbidden Cr3+ transition. The splitting of the observed R-lines (164 cm−1) in Fig. 3b might indicate that these lines do not belong to the same type of emitting center. The decrease in signal at approximately 854 nm was due to the experimental setup, which did not respond efficiently to wavelengths above this.
Cai and coauthors [21] observed a broadband emission centered at 750 nm for single-phase Mg2-xSnO4:xCr3+ under 470 nm excitation and associated this emission with the presence of Cr3+ ions in the Mg2SnO4 lattice. The difference between the bands observed herein and the results reported in [21] may be explained mainly by the fact that the sample in [21] was of a single phase, while in the present study, the system contained two phases in which band overlapping was observed.
Considering Fig. 3, it is possible to say that under 300 nm excitation, the luminescent centers from both Mg2SnO4:Cr3+ and SnO2 were excited (Fig. 3a), but under 450 nm excitation, only Mg2SnO4:Cr3+ luminescent centers were excited (Fig. 3b).
Figure 4 depicts the photoluminescence excitation spectrum with monitored emission at 785 nm. The two bands in the visible region present features related to electronic Cr3+ transitions situated in octahedral sites. The band positions were obtained by Gaussian fitting. The band centered at 21,746 cm−1 (460 nm) was assigned to the 4A2(4F) → 4T1(4F) electronic transition, while the band centered at 15,998 cm−1 (625 nm) was assigned to the 4A2(4F) → 4T2(4F) electronic transition. The band shapes and energy intervals are a certain indication that the Cr3+ ions were situated in an octahedral environment in the lattice. The emission and excitation results agree with the X-ray fluorescence data since none of the techniques detected possible emitting centers other than chromium atoms.
Transition metal cations in a crystalline environment are subjected to changes in their energy levels due to crystal field action. If this environment presents octahedral or tetrahedral symmetry, these changes can be analyzed using the Tanabe–Sugano theory [40,41,42], which was developed to estimate the energies involved in the electronic transitions in systems doped by cations with incomplete d shells (d2–d8) and to determine the crystal field strength and the interelectronic parameters from the transition energies. The energy values to be used in the Tanabe–Sugano theory are obtained from the photoluminescence spectra, where the energy of the levels involved in the electronic transitions and the intensity of the crystal field, represented by the Dq parameter [42], can then be estimated. The Cr3+ cation possesses three electrons in its outer shell (d3 system). The energy matrices and energy level diagram developed by Tanabe–Sugano were used to understand the photoluminescent properties observed herein [40,41,42,43].
Analyzing the d3 energy level diagram for octahedral symmetry [43], the ground level is labeled 4A2(4F), with the first excited state changing if the cation experiences an intense (Dq/B > 2.3) or weak crystal field (Dq/B < 2.3), where B is the Racah parameter. A weak crystal field environment usually generates a broadband associated with the 4T2(4F) → 4A2(4F) transition, as the 4T2(4F) level is the first excited state, while an intense crystal field environment is correlated with the sharp 2E(2G) → 4A2(4F) transition since 2E(2G) is the first excited state in this situation. Although the broadband signal is related to a weak crystal field, previous studies report broadband emission for Dq/B > 2.3 [27, 44].
An interesting case where both transitions can be observed in the same spectrum happens around the crossing level region (Dq/B ≃ 2.3), where both levels are relatively close to each other. Wojtowicz and coauthors describe two types of coupling between 2E(2G) and 4T2(4F) states [45]: the electron–phonon interaction, which can contribute to the mixing of 2E(2G) and 4T2(4F) states in a lattice with octahedral site distortion, and the spin–orbit coupling between 2E(2G) and 4T2(4F) states, which breaks the spin multiplicity selection rule, allowing the 2E(2G) → 4A2(4F) transition. These interactions result in broadband emission from the 4T2(4F) → 4A2(4F) spin-allowed transition accompanied by a structure assigned to the 2E(2G) → 4A2(4F) transition in the emission spectrum.
The Dq and B parameter values are usually determined from the Tanabe–Sugano matrices for d3 systems [40,41,42,43] using the transition energy values obtained from the excitation spectrum as input. The excitation band energies related to the 4A2(4F) → 4T2(4F) and 4A2(4F) → 4T1(4F) transitions were used to calculate Dq and B through Eqs. 1 and 2 [43]:
where ∆E = E(4T1(4F)) − E(4T2(4F)).
The calculated values from Eqs. (1) and (2) were Dq = 1,600 cm−1 and B = 556 cm−1. The Dq/B ratio was 2.88. This value seemed to be higher than expected for systems containing Cr3+ as an activator [46].
Adachi [46, 47] recently proposed a model for the calculation of the Dq and B parameters, starting from the energies of the 2E(2G) and 4T2(4F) states and the C/B ratio. Assuming C/B = 4.8 (a reasonable value for d3 systems [43]) and using the energies of the 4A2(4F) → 4T2(4F) transition (band at 15,998 cm−1 in the excitation spectrum) and the 2E(2G) → 4A2(4F) transition (structure at 695 nm (14,388 cm−1) in the emission spectrum)) observed in the present work, the found values of the parameters from the Adachi model were Dq = 1,600 cm−1 and B = 691 cm−1, with Dq/B = 2.32. The Dq/B value was relatively close to that reported in the literature for oxide systems that use Cr3+ as an activator [36, 43].
This Dq/B value obtained from the Adachi model is distinct from the Dq/B ratio obtained using Eqs. (1) and (2), probably due to energy deviations between the observed and expected energies since the energies related to the 4T1(4F) and 4T2(4F) states are both used in the B calculation using the energy matrices [46, 47]. The energy of the 4A2(4F) → 4T1(4F) transition estimated by the Adachi model was 22,771 cm−1, which gives a difference close to 5% of the observed value (21,746 cm−1), which can be considered a good result.
It is also possible to estimate the energy parameter values using a method where the Dq/B ratio is obtained from the d3 Tanabe–Sugano diagram alongside the band energy positions observed in the excitation spectrum [48, 49]. Initially, a selected transition will serve as a parameter for indexing the other transitions. In the case of the d3 system (such as that studied herein), the 2E(2G) → 4A2(4F) transition observed in the emission spectrum was chosen. It is important to note that since the 2E(2G) state can be considered (in the intermediate–strong field region) independent from the crystal field, theoretically, it is expected that its energy position in the emission spectrum will be the same energy position in the excitation spectrum [50]. Therefore, even if it has not been observed in the excitation spectrum, this transition will be compared to the energy positions of the other transitions in the excitation spectrum. For the same reason, this transition was used in the Adachi model described previously. Among the crystal field-dependent transitions, the energy determination of the 4A2(4F) → 4T2(4F) transition is more accurate than that of 4A2(4F) → 4T1(4F), where the last transition is found in a higher-lying energy position [46, 47].
The 4T2(4F)/2E(2G) energy ratio was obtained using the observed energies of the 4T2(4F) and 2E(2G) levels, considering 4A2(4F) as the ground level. With the 2E(2G) energy level used as a reference, it was possible to identify the height of the 4T2(4F) level in the Tanabe–Sugano diagram, which was 4T2(4F)/2E(2G) times the height of the 2E(2G) energy level. For this height (a point on the 4T2(4F) energy level), the E/B value was obtained on the vertical axis of the Tanabe–Sugano d3 diagram. Using the energy of the 4A2(4F) → 4T2(4F) transition observed in the excitation spectrum in E/B, a B value was obtained. A similar procedure was performed for the 4T1(4F)/2E(2G) ratio, and a second B value was obtained. In addition, an E/B value can be obtained from the 2E(2G) → 4A2(4F) transition, leading to a third B value. The average B value (< B >) obtained from this procedure was 690 cm−1, with Dq = 1,600 cm−1 obtained from the 4A2(4F) → 4T2(4F) transition. From this method, the Dq/B ratio was 2.32, located close to the crossing level region. The Dq, B and Dq/B values were relatively close to the values determined using the Adachi model [46, 47].
Figure 5 displays an energy level diagram, showing the energy levels involved in the Cr3+ excitation and emission processes in the Mg2SnO4–SnO2 system. During the excitation process, the Cr3+ outer shell electrons are promoted from the 4A2(4F) ground level to the 4T1(4F) and 4T2(4F) excited levels (green arrows in Fig. 5a). After some time, the electrons return to ground level, emitting light with a specific energy. This situation is observed in Fig. 5b and is represented by red arrows. Before arriving at the ground level, the system nonradiatively decays from the higher excited state 4T1(4F) to the lower 4T2(4F) and 2E(2G) excited states (black arrows in Fig. 5b), from which they decay again, emitting light.
The energy related to the emission from the 4T2(4F) state is lower than that observed in the excitation process. This energy difference can be explained by the fact that part of the energy used to excite the system is converted into nonradiative emission (related to lattice vibrations). Therefore, the phonon-assisted emission in the infrared region assigned as the 4T2(4F) → 4A2(4F) transition occurs at a longer wavelength (and lower energy) than the excitation band assigned to the 4A2(4F) → 4T2(4F) transition. This energy difference (called the Stokes shift) was calculated as 3,372 cm−1 using the emission value at 450 nm excitation. A large Stokes shift, as observed in the present study, is advantageous because it is related to a large difference in energy between the emission and excitation bands. This large energy difference between the emission and excitation bands prevents the emitted radiation from being reabsorbed by the activator ions in the vicinity of each emitting ion. Consequently, a large Stokes shift favors luminescence because it avoids intensity losses that could be caused by emitted radiation reabsorption.
The nonradiative processes also populate the 2E(2G) level, generating the R-lines to be observed in Fig. 3. The system decays nonradiatively from the 4T1(4F) level, populating the 4T2(4F) and 2E(2G) levels, from which radiative transitions to the ground level occur. This behavior was reported by Martín–Rodriguez and coauthors in Gd3Ga5O12:Cr3+ nanoparticles [51], where the authors observed sharp lines related to the 2E(2G) → 4A2(4F) emission together with a broad emission identified as the 4T2(4F) → 4A2(4F) emission at room temperature.
The energy difference between the 2E(2G) and 4T2(4F) levels is relatively small (1586 cm−1 under 450 nm excitation), considering the 4T2(4F) energy level identified in the excitation spectra and the energy related to the 2E(2G) emission observed in the emission spectra. This behavior indicates that the emitting system is near the level crossing point in the d3 Tanabe–Sugano diagram.
The Dq value (1600 cm−1) is compatible with Cr3+ introduced into an octahedral environment, and the Dq/B ratio obtained from the Tanabe–Sugano diagram and the Adachi model [46, 47] indicates that the Cr3+ cations are subjected to an intermediate crystal field [36, 52]. The Racah B value is lower than the free-ion value (918 cm−1 [43]), which indicates the covalent character of the Cr3+–O2− bond. This corroborates the hypothesis that Cr3+ occupies the octahedral Mg2+ host sites with charge compensation by electron sharing.
Figure 6 exhibits the CIE 1931 chromaticity coordinates determined at room temperature based on emission spectra at 300 nm excitation (Fig. 3a). The calculated x and y color coordinates were 0.4791 and 0.4524, respectively. The chromaticity coordinate value indicated that sample emission was in the visible region under 300 nm excitation.
This result can be compared to the undoped Mg2SnO4 reported by Tsega and coauthors [16], who obtained CIE coordinates in the bluish region of the CIE chromaticity diagram. The sample of the present study had CIE coordinate positions shifted to the orange–yellow region.
The photoluminescence quantum efficiency (QE) was estimated from the emission intensity using the method described in detail in [53]. The obtained value using the results from the emission under 450 nm excitation was 31%. This value can be compared to other Cr3+-doped systems [54,55,56] and is greater than the value obtained for LiNbO3:ZnO:Cr3+ (QE = 10%) [54] and mullite glass (QE = 28%) [55] but very far from that of alexandrite (QE = 95%) [56].
4 Conclusions
The synthesis, crystal structure and photoluminescent properties of an Mg2SnO4–SnO2 system with Cr3+ cations as activators are presented herein. X-ray diffraction confirmed that Mg2SnO4 was accompanied by SnO2. X-ray microfluorescence identified the presence of peaks related to Mg, Sn and Cr chemical elements. Peaks related to other elements were not observed, confirming the desired chemical composition. Photoluminescence experiments confirmed that the emission band was an overlapping emission from Cr3+ incorporated into the octahedral sites of the Mg2SnO4 and SnO2 emission originating from oxygen vacancies, displaying a broad and intense band in the orange–infrared region. The Dq/B ratio indicated that Cr3+ was under an intermediate crystal field, and the Racah B parameter indicated the covalent character of the Cr3+–O2− bond. The sample presented an intense emission that covered a large wavelength interval from 450 to 900 nm when excited at 300 nm, indicating that the (Mg2SnO4–SnO2):Cr3+ material can be used to obtain a light-emitting system at room temperature that covers the visible/near-infrared region.
References
Al-Shahrani AA (2005) Sintering behavior and thermal property of Mg2SnO4. J Mater Sci Lett 16:193–196
Azad A, Min LJ, Alim MA (2001) Mg2SnO4 ceramics II. Electrical characterization. Ceram Int 27:335–341
Chen Y, Wang Y, Hsu C (2011) Elucidating the dielectric properties of Mg2SnO4 ceramics at microwave frequency. J Alloys Compd 509:9650–9653
Premkumar VK, Sivakumar G (2017) Hydrothermally synthesized cubic magnesium stannate (Mg2SnO4) nanoparticles and its electrochemical performances. J Mater Sci Lett 28:14226–14233
Berbenni V, Milanese C, Bruni G, Girella A, Marini A (2012) Mechanically assisted solid state synthesis of Mg2SnO4. J Therm Anal Calorim 110:831–837
Costa JM, Lima LC, Li MS, Santos IMG, Silva MRS, Maia AS (2019) Structural and photocatalytic properties of Mg2SnO4 spinel obtained by modified Pechini method. Mater Lett 236:320–323
Qin Y, Xiong J, Zhang W, Liu L, Cui Y, Gu H (2015) Facile synthesis and photocatalytic performance of Mg2SnO4/SnO2 heterostructures. J Mater Sci 50:5865–5872
Zhang J, Yu M, Qin Q, Zhou H, Zhou M, Xu X, Wang Y (2010) The persistent luminescence and up conversion photostimulated luminescence properties of nondoped Mg2SnO4 material. J Appl Phys 108:123518
Li G, Zhang X, Peng C, Shang M, Geng D, Cheng Z, Lin J (2011) Cyan-emitting Ti4+- and Mn2+-coactivated Mg2SnO4 as a potential phosphor to enlarge the color gamut for field emission display. J Mater Chem 21:6477–6479
Chen C, Li C (2016) Improving quality factor of Mg2SnO4 ceramics by removing moisture content from starting raw materials. Ceram Int 42:9749–9751
Behrh G, Isobe M, Massuyeau F, Serier-Braut H, Gordon EE, Koo H, Whangbo M, Gautier R, Jobic S (2017) Oxygen-vacancy-induced midgap states responsible for the complex luminescence of the inverse spinel Mg(MgSn)O4. Chem Mater 29:1069–1075
Jia-Chi Z, Qing-Song Q, Ming-Hui Y, Hong-Liang Z, Mei-Jiao Z (2011) Photoluminescence and persistent luminescence properties of non-doped and Ti4+-doped Mg2SnO4 phosphors. Chin Phys B 9:094211
Lodha R, Oprea G, Troczynski T (2011) Role of Ti4+ and Sn4+ ions in spinel formation and reactive sintering of magnesia-rich ceramics. Ceram Int 37:465–470
Seko A, Oba F, Tanaka I (2010) Classification of spinel structures based on first-principles cluster expansion analysis. Phys Rev B 81:054114
Zhang J, Qing Q, Yu M, Sun J, Shi L, Ma X (2011) Up-conversion photostimulated luminescence of Mg2SnO4 for optical storage. Chin Phys Lett 28:027802
Tsega M, Dejene FB (2018) Photoluminescence and Thermoluminescence properties of sol-gel auto-combustion driven Mg2SnO4 nanophosphor. ECS J Solid State Sci Technol 7:R183–R189
Kim KN, Jung HK, Park HD, Ki D (2002) High luminance of new green emitting phosphor, Mg2SnO4:Mn. J Lumin 99:169–173
Kitaura M, Tani S, Mitsudo S, Kukui K (2010) Photoluminescence enhancement in manganese-doped magnesium stannate phosphors synthesized by millimeter-wave irradiation. Radiat Meas 45:503–505
Lei B, Li B, Wang X, Li W (2006) Green emitting long lasting phosphorescence (LLP) properties of Mg2SnO4:Mn2+ phosphor. J Lumin 118:173–178
Junior EBS, López A, Pedro SS, Sosman LP (2019) Photoluminescence of Co2+ ions in Mg2SnO4 tetrahedral sites. Opt Mater 95:109202
Cai J, Pang R, Yu Z, Liu L, Li C (2019) Preparation and luminescent properties of near-infrared luminescent material Mg2SnO4:Cr3+. Chin J Lumin 40:1505–1513
Zhang J, Qin Q, Yu M, Zhou M, Wang Y (2012) The photoluminescence, afterglow, and up conversion photostimulated luminescence of Eu3+ doped Mg2SnO4 phosphors. J Lumin 132:23–26
Guo P, Peng L, Zhang W, Liu L, Xiong J (2015) Preparation and photoluminescence properties of Pr-doped Mg2SnO4 nanoparticles. J Inorg Mater 30:1172–1176
Bolzan AA, Fong C, Kennedy BJ, Howard CJ (1997) Structural studies of rutile-type metal dioxides. Acta Crystallographica B 53:373–380
Gu F, Wang SF, Song CF, Lu MK, Qi YX, Zhou GJ, Xu D, Yuan DR (2003) Synthesis and luminescence properties of SnO2 nanoparticles. Chem Phys Lett 372:451–454
García-Tecedor M, Maestre D, Cremades A, Piqueras J (2016) Influence of Cr doping on the morphology and luminescence of SnO2 structures. J Phys Chem C 120:22028–22034
Nikolov I, Mateos X, Guell F, Massons J, Nikolov V, Peshev P, Díaz F (2004) Optical properties of Cr3+:NaAl(WO4)2 crystals, a new candidate for broadband laser applications. Opt Mater 25:53–58
Xu X, Shao Q, Yao L, Dong Y, Jiang J (2020) Highly efficient and thermally stable Cr3+ activated silicate phosphors for broadband near-infrared LED applications. Chem Eng J 383:123108
Katayama Y, Kobayashi H, Tanabe S (2015) Deep-red persistent luminescence in Cr3+-doped LaAlO3 perovskite phosphor for in vivo imaging. Appl Phys Express 8:012102
Viana B, Sharma SK, Gourier D, Maldiney T, Teston E, Scherman D, Richard C (2016) Long term in vivo imaging with Cr3+ doped spinel nanoparticles exhibiting persistent luminescence. J Lumin 170:879–887
Han Z, Li X, Ye J, Kang L, Chen Y, Li J, Lin Z (2015) Significantly enhanced infrared emissivity of LaAlO3 by co-doping with Ca2+ and Cr3+ for energy-saving applications. J Am Ceram Soc 98:2336–2339
Mikalauskaite I, Pleckaityte G, Skapas M, Zarkov A, Katelnikovas A, Beganskiene A (2019) Emission spectra tuning of upconverting NaGdF4:20% Yb, 2% Er nanoparticles by Cr3+ co-doping for optical temperature sensing. J Lumin 213:210–217
Roisnel T, Rodriguez-Carvajal J (2010) FullProf Suite Program FullProf.2k V. 4.80 Laboratoire Leon Brillouin (CEA-CNRS). Available at https://www.ill.eu/sites/fullprof/
Goldschmidt VM (1926) Die Gesetze der Krystallochemie. Naturwissenschaften, 14:477-485
Shannon RD (1976) Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallogr A 32:751–767
Malysa B, Meijerink A, Justel T (2018) Temperature dependent Cr3+ photoluminescence in garnets of the type X3Sc2Ga3O12 (X=Lu, Y, Gd, La). J Lumin 202:523–531
Costa GKB, Pedro SS, López A, Carvalho ICS, Cella N, Sosman LP (2016) Niobium-gallium oxide with a high concentration of Cr3+ ions: Photoluminescence and structural characteristics. Opt Mater 60:506–512
Peche-Herrero MA, Maestre D, Ramírez-Castellanos J, Cremades A, Piqueras J, Gonzalez-Calbet JM (2014) The controlled transition-metal doping of SnO2 nanoparticles with tunable luminescence. CrystEngComm 16:2969–2976
Arai T, Adachi S (2012) Synthesis and photoluminescence properties of SnO2 nanopowder. Jpn J Appl Phys 51:105002
Tanabe Y, Sugano S (1954) On the absorption spectra of complex ions. I J Phys Soc Jpn 9:753–766
Tanabe Y, Sugano S (1954) On the absorption spectra of complex ions. II J Phys Soc Jpn 9:766–779
Tanabe Y, Sugano S (1956) On the absorption spectra of complex ions. III The calculation of the crystalline field strength. J Phys Soc Jpn 11:864–877
Henderson B, Imbusch GF (1989) Optical spectroscopy of inorganic solids. Oxford University Press, Oxford
Kück S, Fornasiero L, Mix E, Huber G (2000) Spectroscopic properties of Cr-doped Sc2O3. J Lumin 87–89:1122–1125
Wojtowicz AJ, Grinberg M, Lempicki A (1991) The coupling of 4T2 and 2E states of the Cr3+ ion in solid state materials. J Lumin 50:231–242
Adachi S (2020) Mn4+ and Cr3+ ions in red and deep red-emitting phosphors: spectral analysis and racah parameter determination. J Lumin 223:117217
Adachi S (2020) New analysis model for the determination of racah and crystal-field splitting parameters: verification and case studies. ECS J Solid State Sci Technol 9:046004
Ionita I (2015) Condensed matter optical spectroscopy, an illustrated introduction. CRC Press, Boca Raton
Espinoza VAA, López A, Neumann R, Sosman LP, Pedro SS (2017) Photoluminescence of divalent cobalt ions in tetrahedral sites of zinc orthotitanate. J Alloys Compd 720:417–422
Brik MG, Camardello SJ, Srivastava AM, Avram NM, Suchocki A (2016) Spin-forbidden transition metal ions and nephelauxetic effect. ECS J Solid State Sci Technol 5(1):R3067–R3077
Martín-Rodríguez R, Valiente R, Rodríguez F, Bettinelli M (2011) Temperature and pressure dependence of the optical properties of Cr3+-doped Gd3Ga5O12 nanoparticles. Nanotechnology 22:265707
Pratapkumar C, Prashantha SC, Nagabhushana H, Jnaneshwara DM (2018) Photoluminescence and photometric studies of low temperature prepared red emitting MgAl2O4:Cr3+ nanophosphors for solid state displays. J Sci Adv Mater Dev 3:464–470
Chiara PN, Pedro SS, López A, Carvalho ICS, Sosman LP (2017) Photoluminescence of the manganese ions on Mg2Si2O6-Mg2SiO4 compounds. J Lumin 182:39–44
Torchia GA, Muñoz JA, Cussó F, Jaque F, Tocho JO (2001) The luminescent quantum efficiency of Cr3+ ions in co-doped crystals of LiNbO3:ZnO determined by simultaneous multiple-wavelength photoacoustic and luminescence experiments. J Lumin 92:317–322
Andrews LJ, Beall GH, Lempicki A (1986) Luminescence of Cr3+ in mullite transparent glass ceramics. J Lumin 36:65–74
Shand ML (1983) Quantum efficiency of alexandrite. J Appl Phys 54:2602–3260
Acknowledgements
This study was financed in part by the Coordenação de Aperfeiçoamento de Pessoal de Nível Superior—Brasil (CAPES)—Finance Code 001. The authors are also grateful to the Fundação de Amparo à Pesquisa do Estado do Rio de Janeiro (FAPERJ) and Financiadora de Estudos e Projetos (FINEP) for financial support. The authors would also like to thank LIETA-UERJ, Brazil, for the X-ray diffraction measurements. L. P. Sosman and S. S. Pedro thank Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) for their Research Productivity fellowships. S. S. Pedro thanks FAPERJ for a Jovem Cientista do Nosso Estado (JCNE) fellowship.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Santana, N.D.C., López, A., Sosman, L.P. et al. Broadband photoluminescence in a ceramic (Mg2SnO4–SnO2):Cr3+ system. SN Appl. Sci. 3, 125 (2021). https://doi.org/10.1007/s42452-021-04161-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s42452-021-04161-y