Abstract
It is urgent to develop low-cost but efficient oxygen reduction reaction (ORR) catalysts for the emerging clean energy devices of fuel cells based on proton exchange membrane. Herein, we report a facile method to covert the biomass of black fungus into an efficient ORR catalyst. The black fungus undergoes hydrothermal and pyrolysis processes to transform into carbon-based materials. The as-obtained BF-N-950 catalyst shows prominent ORR catalytic activities in both acidic and alkaline electrolytes with a half-wave potential reaching 0.77 and 0.91 V, respectively. A membrane electrolyte assembly was fabricated with the as-obtained BF-N-950 as the cathode catalyst which shows a high peak power density of 255 mW cm-2. The study shows the potential of converting conventional biomass into low-cost ORR catalyst, which is promising for the fuel cell technology.
摘要
制备廉价、高活性氧还原催化剂对于发展氢氧燃料电池清洁能源极为重要. 在本论文中, 我们利用黑木耳作为生物质材料, 通过一种便捷的方法合成了高活性氧还原催化剂. 黑木耳经水热和热解两个步骤, 碳化形成BF-N-950催化剂. 该催化剂在酸性和碱性溶液中的半波电势分别为0.77和0.91 V. 采用BF-N-950催化剂作为膜电极得到的氢氧燃料单电池, 峰值功率可达255 mW cm−2. 本文提出了使用生物质材料合成高性能氧还原催化剂的方法, 为氢氧燃料电池的应用提供了有益探索.
Article PDF
Similar content being viewed by others
References
Ellingsen LAW, Hung CR, Majeau-Bettez G, et al. Nanotechnology for environmentally sustainable electromobility. Nat Nanotech, 2016, 11: 1039–1051
Dai L, Xue Y, Qu L, et al. Metal-free catalysts for oxygen reduction reaction. Chem Rev, 2015, 115: 4823–4892
Thompson ST, Papageorgopoulos D. Platinum group metal-free catalysts boost cost competitiveness of fuel cell vehicles. Nat Catal, 2019, 2: 558–561
Xiao M, Zhu J, Feng L, et al. Meso/macroporous nitrogen-doped carbon architectures with iron carbide encapsulated in graphitic layers as an efficient and robust catalyst for the oxygen reduction reaction in both acidic and alkaline solutions. Adv Mater, 2015, 27: 2521–2527
Wang XX, Swihart MT, Wu G. Achievements, challenges and perspectives on cathode catalysts in proton exchange membrane fuel cells for transportation. Nat Catal, 2019, 2: 578–589
Wang S, Yu D, Dai L. Polyelectrolyte functionalized carbon nanotubes as efficient metal-free electrocatalysts for oxygen reduction. J Am Chem Soc, 2011, 133: 5182–5185
Meng FL, Wang ZL, Zhong HX, et al. Reactive multifunctional template-induced preparation of Fe-N-doped mesoporous carbon microspheres towards highly efficient electrocatalysts for oxygen reduction. Adv Mater, 2016, 28: 7948–7955
Gewirth AA, Varnell JA, DiAscro AM. Nonprecious metal catalysts for oxygen reduction in heterogeneous aqueous systems. Chem Rev, 2018, 118: 2313–2339
Yan D, Guo L, Xie C, et al. N, P-dual doped carbon with trace Co and rich edge sites as highly efficient electrocatalyst for oxygen reduction reaction. Sci China Mater, 2018, 61: 679–685
Yang T, Liu J, Zhou R, et al. N-doped mesoporous carbon spheres as the oxygen reduction reaction catalysts. J Mater Chem A, 2014, 2: 18139–18146
Liu Q, Liu X, Zheng L, et al. The solid-phase synthesis of an Fe-N-C electrocatalyst for high-power proton-exchange membrane fuel cells. Angew Chem Int Ed, 2018, 57: 1204–1208
Chung HT, Cullen DA, Higgins D, et al. Direct atomic-level insight into the active sites of a high-performance PGM-free ORR catalyst. Science, 2017, 357: 479–484
Collman JP, Denisevich P, Konai Y, et al. Electrode catalysis of the four-electron reduction of oxygen to water by dicobalt face-to-face porphyrins. J Am Chem Soc, 1980, 102: 6027–6036
Shigehara K, Anson FC. Electrocatalytic activity of three iron porphyrins in the reductions of dioxygen and hydrogen peroxide at graphite electrodes. J Phys Chem, 1982, 86: 2776–2783
Okada T. Oxygen reduction characteristics of heat-treated catalysts based on cobalt-porphyrin ion complexes. J Electrochem Soc, 1998, 145: 815–822
Jiang R, Tran DT, McClure JP, et al. Ordered mesoporous FeNx-doped carbon: a class of highly active and stable catalysts in acids, bases and polymer electrolyte membrane fuel cells. J Mater Chem A, 2018, 6: 3941–3953
Wu G, More KL, Johnston CM, et al. High-performance electro-catalysts for oxygen reduction derived from polyaniline, iron, and cobalt. Science, 2011, 332: 443–447
Jahan M, Bao Q, Loh KP. Electrocatalytically active graphene- porphyrin MOF composite for oxygen reduction reaction. J Am Chem Soc, 2012, 134: 6707–6713
Liu YL, Shi CX, Xu XY, et al. Nitrogen-doped hierarchically porous carbon spheres as efficient metal-free electrocatalysts for an oxygen reduction reaction. J Power Sources, 2015, 283: 389–396
Yu C, Yuan P, Erickson EM, et al. Oxygen reduction reaction induced pH-responsive chemo-mechanical hydrogel actuators. Soft Matter, 2015, 11: 7953–7959
Borghei M, Lehtonen J, Liu L, et al. Advanced biomass-derived electrocatalysts for the oxygen reduction reaction. Adv Mater, 2018, 30: 1703691
Dou M, He D, Shao W, et al. Pyrolysis of animal bones with vitamin B12: A facile route to efficient transition metal-nitrogen-carbon (TM-N-C) electrocatalysts for oxygen reduction. Chem Eur J, 2016, 22: 2896–2901
Chaudhari KN, Song MY, Yu JS. Transforming hair into het-eroatom-doped carbon with high surface area. Small, 2014, 10: 2625–2636
Song MY, Park HY, Yang DS, et al. Seaweed-derived heteroatomdoped highly porous carbon as an electrocatalyst for the oxygen reduction reaction. ChemSusChem, 2014, 7: 1755–1763
Zheng J, Guo C, Chen C, et al. High content of pyridinic- and pyrrolic-nitrogen-modified carbon nanotubes derived from blood biomass for the electrocatalysis of oxygen reduction reaction in alkaline medium. Electrochim Acta, 2015, 168: 386–393
Zhang Y, Wang B, Nie A, et al. Carbonaceous photonic crystals prepared by high-temperature/hydrothermal carbonization as high-performance microwave absorbers. J Mater Sci, 2019, 54: 14343–14353
Amiinu IS, Zhang J, Kou Z, et al. Self-organized 3D porous graphene dual-doped with biomass-sponsored nitrogen and sulfur for oxygen reduction and evolution. ACS Appl Mater Interfaces, 2016, 8: 29408–29418
Guo C, Liao W, Li Z, et al. Easy conversion of protein-rich enoki mushroom biomass to a nitrogen-doped carbon nanomaterial as a promising metal-free catalyst for oxygen reduction reaction. Nanoscale, 2015, 7: 15990–15998
Liu Z, Li Z, Tian S, et al. Conversion of peanut biomass into electrocatalysts with vitamin B12 for oxygen reduction reaction in Zn-air battery. Int J Hydrogen Energy, 2019, 44: 11788–11796
Liu R, Zhang H, Liu S, et al. Shrimp-shell derived carbon nanodots as carbon and nitrogen sources to fabricate three-dimensional N-doped porous carbon electrocatalysts for the oxygen reduction reaction. Phys Chem Chem Phys, 2016, 18: 4095–4101
Zhang Y, Liu X, Wang X, et al. Research progress in the nutritional components and biological activities of Auricularia auricula. South China Agr, 2018, 12: 130–134
Zhao J, Guo X, Guo Q, et al. Growth of carbon nanotubes on natural organic precursors by chemical vapor deposition. Carbon, 2011, 49: 2155–2158
Feng X, Zhao N, Ze S, et al. Determination of mineral elements in Auriculayia auricular from different habitats. Guizhou Agr Sci, 2016, 44: 35–38
Sassin MB, Garsany Y, Gould BD, et al. Fabrication method for laboratory-scale high-performance membrane electrode assemblies for fuel cells. Anal Chem, 2017, 89: 511–518
Kambo HS, Dutta A. A comparative review of biochar and hydrochar in terms of production, physico-chemical properties and applications. Renew Sustain Energy Rev, 2015, 45: 359–378
Guan Z, Zhang X, Chen W, et al. Mesoporous S doped Fe-N-C materials as highly active oxygen reduction reaction catalyst. Chem Commun, 2018, 54: 12073–12076
Zhu Y, Zhang B, Liu X, et al. Unravelling the structure of electrocatalytically active Fe-N complexes in carbon for the oxygen reduction reaction. Angew Chem Int Ed, 2014, 53: 10673–10677
Hayashi J', Kazehaya A, Muroyama K, et al. Preparation of activated carbon from lignin by chemical activation. Carbon, 2000, 38: 1873–1878
Caturla F, Molina-Sabio M, Rodríguez-Reinoso F. Preparation of activated carbon by chemical activation with ZnCl2. Carbon, 1991, 29: 999–1007
Zhang G, Jin X, Li H, et al. N-doped crumpled graphene: bottom-up synthesis and its superior oxygen reduction performance. Sci China Mater, 2016, 59: 337–347
Shen W, Fan W. Nitrogen-containing porous carbons: synthesis and application. J Mater Chem A, 2013, 1: 999–1013
Tian M, Zhu Y, Zhang D, et al. Pyrrolic-nitrogen-rich biomass-derived catalyst for sustainable degradation of organic pollutant via a self-powered electro-Fenton process. Nano Energy, 2019, 64: 103940
Biddinger EJ, von Deak D, Ozkan US. Nitrogen-containing carbon nanostructures as oxygen-reduction catalysts. Top Catal, 2009, 52: 1566–1574
Artyushkova K, Serov A, Rojas-Carbonell S, et al. Chemistry of multitudinous active sites for oxygen reduction reaction in transition metal-nitrogen-carbon electrocatalysts. J Phys Chem C, 2015, 119: 25917–25928
Wei J, Hing P, Mo ZQ. TEM, XPS and FTIR characterization of sputtered carbon nitride films. Surf Interface Anal, 1999, 28: 208–211
Wan X, Liu X, Li Y, et al. Fe-N-C electrocatalyst with dense active sites and efficient mass transport for high-performance proton exchange membrane fuel cells. Nat Catal, 2019, 2: 259–268
Wang YC, Lai YJ, Song L, et al. S-doping of an Fe/N/C ORR catalyst for polymer electrolyte membrane fuel cells with high power density. Angew Chem Int Ed, 2015, 54: 9907–9910
Wang T, Wang J, Wang X, et al. Graphene-templated synthesis of sandwich-like porous carbon nanosheets for efficient oxygen reduction reaction in both alkaline and acidic media. Sci China Mater, 2018, 61: 915–925
Acknowledgements
This work was financially supported by the National Key Research and Development Program of China (2017YFA0206500), the National Natural Science Foundation of China (21671014), and the Fundamental Research Funds for the Central Universities (buctrc201823).
Author information
Authors and Affiliations
Contributions
Author contributions Wang X, Zhu W and Zhuang Z conceived and designed the experiments. Wang X performed the synthesis of catalyst and the test of the fuel cell. Wang X, Fang J, Liu X, Zhang X, Lv Q and Xu Z characterized the materials and discussed the results of the experiments. Wang X and Zhuang Z wrote the paper. All authors participated in the general discussion.
Corresponding authors
Additional information
Conflict of interest The authors declare no conflict of interest.
Supplementary information Experimental details and supporting data are available in the online version of the paper.
Xingdong Wang is now a graduate student at Beijing University of Chemical Technology under the supervision of Prof. Zhongbin Zhuang. His research interest focuses on the non-precious metal-based catalysts and their application in proton exchange membrane fuel cell.
Wei Zhu received his PhD degree from Peking University in 2014. After postdoctoral work at Tsinghua University, he joined Beijing University of Chemical Technology as an associate professor in 2018. His main research interests lie in the controllable synthesis of functional nanocatalysts, experimental study of nano-electrocatalytic mechanism, and application exploration of nanomaterials in newly developed electrolyser devices.
Zhongbin Zhuang received his PhD degree from Tsinghua University in 2010. After postdoctoral work at the University of California, Riverside and University of Delaware, he joined Beijing University of Chemical Technology as a professor in 2015. His current research interests include electrocatalysts for fuel cell and electrolysers, interfacial electrochemistry and methodology for nanocrystal synthesis.
Rights and permissions
About this article
Cite this article
Wang, X., Fang, J., Liu, X. et al. Converting biomass into efficient oxygen reduction reaction catalysts for proton exchange membrane fuel cells. Sci. China Mater. 63, 524–532 (2020). https://doi.org/10.1007/s40843-019-1224-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40843-019-1224-5