Durability of Glass Fibre Reinforced Polymer Pultruded Profiles: Comparison Between QUV Accelerated Exposure and Natural Weathering in a Mediterranean Climate

  • Published:
Experimental Techniques Aims and scope Submit manuscript

Abstract

This paper presents the results of an experimental study about the durability of E-glass fibre reinforced polymer (GFRP) pultruded profiles when exposed to environmental degradation agents. Small-scale coupons obtained from commercial GFRP profiles, made of either unsaturated polyester or vinylester resins, were exposed to natural ageing in the city centre of Lisbon, an urban Mediterranean environment, during 42 months (3.5 years) and to artificial accelerated ageing in a Q-Lab Ultraviolet accelerated weathering chamber (QUV) chamber up to 3000 h. The effects of such exposure conditions on both types of profiles were assessed and compared regarding the changes on the following physical, chemical, aesthetical, and mechanical properties: (1) colour and gloss variations, (2) viscoelastic response, evaluated by means of dynamic mechanical analysis (DMA), (3)mechanical response in tension, bending and interlaminar shear, and (4) chemical changes, assessed through Fourier transform infrared spectroscopy (FTIR). Both types of environmental exposure caused significant aesthetical changes. Mechanical and viscoelastic properties presented slight changes, suggesting evidence of post-curing phenomena and confirming that ultraviolet (UV) radiation affects essentially the outermost layers of GFRP profiles. In general, the GFRP profile made of polyester presented worse durability performance than the vinylester one, in terms of mechanical performance and especially of aesthetical (surface) performance. QUV and natural ageing could be correlated, particularly in what concerns colour and gloss changes; regarding physical and mechanical changes, in general, properties after ageing in those environments are of the same order of magnitude and exhibit comparable variation trends.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Keller, T., “Recent All-Composite and Hybrid Fibre-Reinforced Polymer Bridges and Buildings,” Progress in Structural Engineering and Materials 3: 132–140 (2001).

  2. Keller, T., “Towards Structural Forms for Composite Fibre Materials,” Structural Engineering International 9: 297–300 (1999).

  3. Sobrino, J.A., and Pulido, M.D.G., “Towards Advanced Composite Material Footbridges,” Structural Engineering International 12: 84–86 (2002).

  4. Gago, A., Proença, J., Cardoso, J., Cóias, V., and Paula, R., “Seismic Strengthening of Stone Masonry Walls with Glass Fiber Reinforced Polymer Strips and Mechanical Anchorages,” Experimental Techniques 35(1): 45–53 (2011).

  5. Jayaguru, C., and Subramanian, K., “Seismic Behavior of a Partially Infilled RC Frame Retrofitted Using GFRP Laminates,” Experimental Techniques 36(5): 82–91 (2012).

  6. Correia, J.R., Branco, F.A., Silva, N.M.F., Camotim, D., and Silvestre, N., “First-Order, Buckling and Post-Buckling Behaviour of GFRP Pultruded Beams. Part 1: Experimental Study,” Computers and Structures 89(21–22): 2052–2064 (2011).

  7. Correia, J.R., Branco, F.A., Gonilha, J.A., Silva, N., and Camotim, D., “GFRP Pultruded Flexural Members: Assessment of Existing Design Methods,” Structural Engineering International 20(4): 362–369 (2012).

  8. Correia, J.R., GFRP Pultruded Profiles in Civil Engineering: Hybrid Solutions, Bonded Connections and Fire Behaviour. PhD Thesis in Civil Engineering, Instituto Superior Técnico, Technical University of Lisbon (2008).

  9. Karbhari, V.M., Durability of Composites for Civil Structural Applications, Woodhead Publishing, Boca Raton, FL (2007).

  10. Karbhari, V.M., and Seible, F., “Fiber Reinforced Composites—Advanced Materials for the Renewal of Civil Infrastructure,” Applied Composite Materials 7(2–3): 95–124 (2000).

  11. Sousa, J.M., Durability of GFRP Pultruded Profiles Made of Vinylester Resin. MSc Dissertation in Civil Engineering. Instituto Superior Técnico, Technical University of Lisbon (2011).

  12. Karbhari, V.M., and Zhang, S., “E-Glass/Vinylester Composites in Aqueous Environments—I: Experimental Results,” Applied Composite Materials 10: 19–48 (2003).

  13. Schuttle, C.L., “Environmental Durability of Glass-Fiber Composites,” Materials Science and Engineering 13: 265–323 (1994).

  14. Liao, K., Schultheisz, C.R., Hunston, D.L., and Brinson, L.C., “Long-Term Durability of Fiber-Reinforced Polymer Matrix Composite Materials for Infrastructure Applications: A Review,” Journal of Advanced Materials 30(4): 3–40 (1998).

  15. Karbhari, V.M., Chin, J.W., Hunston, D., et al., “Durability Gap Analysis for Fiber-Reinforced Polymer Composites in Civil Infrastructure,” Journal of Composites for Construction 7(3): 238–247 (2003).

  16. Bogner, B.E., and Borja, P.P., “Strength Retention of Pultruded Composites After Exposure to Ultra-Violet (UV) Light,” Research Report. BP Amoco Research Center, Naperville, IL, (1997).

  17. Chin, J.W., Nguyen, T., and Aouadi, K., “Effects of Environmental Exposure on Fiber-Reinforced Plastic (FRP) Materials Used in Construction,” Journal of Composites, Technology and Research 19(4): 205–213 (1997).

  18. Bank, L.C., Gentry, T.R., and Barkatt, A., “Accelerated Test Methods to Determine the Long-Term Behavior of FRP Composite Structures: Environmental Effects,” Journal of Reinforced Plastics and Composites 14: 559–587 (1995).

  19. Bogner, B.E., and Borja, P.P., “Ultra-Violet Light Resistance of Pultruded Composites,” Paper presented at the European Pultrusion Technology Association, Venice, Italy (1994).

  20. Nguyen, T.-C., Bai, Y., Zhao, X.-L., and Al-Mahaidi, R., “Effects of Ultraviolet Radiation and Associated Elevated Temperature on Mechanical Performance of Steel/CFRP Double Strap Joints,” Composite Structures 94(12): 3563–3573 (2012).

  21. Cabral-Fonseca, S., Correia, J.R., Rodrigues, M.P., and Branco, F.A., “Artificial Accelerated Ageing of GFRP Pultruded Profiles Made of Polyester and Vinylester Resins: Characterisation of Physical–Chemical and Mechanical Damage,” Strain 48(2): 162–173 (2012).

  22. ISO 4892, Plastics—Methods of Exposure to Laboratory Light Sources—Part 1: General Guidance. Part 3: Fluorescent UV Lamps, International Organization for Standardization, Genève (1996).

  23. ISO 7724, Paints and Varnishes—Colorimetry—Part 1: Principles. Part 2: Colour Management, International Organization for Standardization, Genève (1997).

  24. ISO 2813, Paints and Varnishes—Determination of Specular Gloss of Non-Metalic Paint Films at 20°, 60°, 85°, International Organization for Standardization, Genève (1994).

  25. ISO 6721, Plastics—Determination of Dynamic Mechanical Properties—Part 1: General Principles. Part 5: Flexural Vibration—Non-Resonance Method, International Organization for Standardization, Genève (1996).

  26. ISO 14125, Fibre-Reinforced Plastic Composites—Determination of Flexural Properties, International Organization for Standardization, Genève (1998).

  27. ISO 527, Plastics—Determination of Tensile Properties—Part 1: General Principles. Part 4: Test Conditions for Isotropic and Orthotropic Fibre-Reinforced Plastic Composites, International Organization for Standardization, Genève (1997).

  28. ASTM D 2344, Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates, American Society for Testing and Materials, West Conshohocken, PA (2000).

  29. ASTM E 1252, Standard Practice for General Techniques for Obtaining Spectra for Qualitative Analysis, American Society for Testing and Materials, West Conshohocken, PA (2007).

  30. ASTM D 3171, Standard Test Method for Constituent of Composite Materials, American Society for Testing and Materials, West Conshohocken, PA (2009).

  31. ISO 1183, Plastics—Methods for Determining the Density of Non-Cellular Plastics. Part 1: Immersion Method, Liquid Pyknometer and Titration Method, International Organization for Standardization, Genève (2004).

  32. Chu, W., and Karbhari, V.M., “Effect of Water Sorption on Performance of Pultruded E-Glass/Vinylester Composites,” Journal of Materials in Civil Engineering 17: 63–71 (2005).

  33. Correia, J.R., Cabral-Fonseca, S., Costa, R., et al., “Environmental Degradation of GFRP Pultruded Profiles made of Polyester and Vinylester Resins,” CD-Rom Proceedings of the 15th International Conference on Composite Structures, Porto (2008).

  34. Merah, N., Nizamuddin, S., Khan, Z., Al-Sulaiman, F., and Mehdi, M., “Natural Weathering and Sea Water Effects on the Durability of Glass Fiber Reinforced Vinylester: Fractographic Analysis,” Applied Composite Materials 17(4): 363–372 (2010).

  35. Segovia, F., Ferrer, C., Salvador, M.D., and Amigo, V., “Influence of Processing Variables on Mechanical Characteristics of Sunlight Aged Polyester-Glass Fibre Composites,” Polymer Degradation and Stability 71(1): 179–184 (2001).

  36. Correia, J.R., Cabral-Fonseca, S., Branco, F.A., Ferreira, J.G., Eusébio, M.I., and Rodrigues, M.P., “Durability of Pultruded Glass-Fiber-Reinforced Polyester Profiles for Structural Applications,” Mechanics of Composite Materials 42(4): 325–338 (2006).

Download references

Author information

Authors and Affiliations

  1. Department of Civil Engineering, Architecture and Georesources, Instituto Superior Técnico/ICIST, Technical University of Lisbon, Av., Rovisco Pais, 1049-001, Lisboa, Portugal

    J.M. Sousa & J.R. Correia

  2. Materials Department, Organic Materials Division (NMO), National Laboratory of Civil Engineering (LNEC), Lisboa, Portugal

    S. Cabral-Fonseca

Authors
  1. J.M. Sousa
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. J.R. Correia
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. S. Cabral-Fonseca
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to J.R. Correia.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sousa, J., Correia, J. & Cabral-Fonseca, S. Durability of Glass Fibre Reinforced Polymer Pultruded Profiles: Comparison Between QUV Accelerated Exposure and Natural Weathering in a Mediterranean Climate. Exp Tech 40, 207–219 (2016). https://doi.org/10.1007/s40799-016-0024-x

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40799-016-0024-x

Keywords

Search

Navigation