Experiments were carried out with bypass-current MIG welding–brazing of magnesium alloy to galvanized steel to investigate the effect of heat input on the microstructure and mechanical properties of lap joints. Experimental results indicated that the joint efficiency tended to increase at first and then to reduce with the increase of heat input. The joint efficiency reached its maximum of about 70% when the heat input was 155 J/mm. The metallurgical bonding between magnesium alloy and steel was a thin continuous reaction layer, and the intermetallic compound layer consisted of Mg–Zn and slight Fe–Al phases. It is concluded that bypass-current MIG welding–brazing is a stable welding process, which can be used to achieve defect-free joining of magnesium alloy to steel with good weld appearances.
Similar content being viewed by others
References
B.L. Mordike, T. Ebert, Mater. Sci. Eng. A 302, 37 (2001)
W. Elthalabawy, T. Khan, J. Mater. Sci. Technol. 27, 22 (2011)
S.J. Wang, G.L. Qin, Y.H. Su, Acta Metall. Sin. (Engl. Lett) 26, 177 (2013)
Y.N. Wei, J.L. Li, J.T. Xiong, F. Huang, F.S. Zhang, Mater. Des. 33, 111 (2012)
C. Schneider, T. Weinberger, J. Inoue, T. Koseki, N. Enzinger, Sci. Technol. Weld. Join. 16, 100 (2011)
W. Xu, D.L. Chen, L. Liu, H. Mori, Y. Zhou, Mater. Sci. Eng. A 537, 11 (2012)
L. Liu, L. Xiao, J.C. Feng, Y.H. Tian, S.Q. Zhou, Y. Zhou, Metall. Mater. Trans. A 41, 2651 (2010)
W. Elthalabawy, T. Khan, Mater. Charact. 61, 703 (2010)
W. Elthalabawy, T. Khan, Key Eng. Mater. 442, 26 (2010)
G. Song, G.Y. An, L.M. Liu, Mater. Des. 35, 323 (2012)
X.D. Qi, G. Song, Mater. Des. 31, 605 (2010)
Y.C. Chen, K. Nakata, Mater. Trans. 50, 2598 (2009)
T. Tachibana, S. Hojo, S. Iwatani, T. Quart, S. Nakagawa, J. Jpn. Weld. Soc. 27, 183 (2009)
L.M. Liu, X. Zhao, Mater. Charact. 61, 1279 (2008)
Y.G. Miao, D.F. Han, J.Z. Yao, F. Li, Sci. Technol. Weld. Join. 15, 97 (2010)
Y.G. Miao, D.F. Han, J.Z. Yao, F. Li, Mater. Des. 31, 3121 (2010)
Y.M. Zhang, M. Jiang, W. Lu, Weld. J. 83, 39 (2004)
L. Ma, D.Y. He, X.Y. Li, J.M. Jiang, Mater. Lett. 64, 596 (2010)
L.Q. Li, C.W. Tan, Y.B. Chen, W. Guo, F. Song, Mater. Des. 43, 59 (2013)
S. Jana, Y. Hovanski, G.J. Grant, Metall. Mater. Trans. A 41, 3173 (2010)
Y.X. Gu, Particular Engineering Materials Welding, 1st edn. (Liaoning Science and Technology Press, Shenyang, 1998), p. 72. (in Chinese)
Acknowledgments
This work was financially supported by the National Natural Science Foundation of China (No. 51005049).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Miao, Y., Wu, B., Xu, X. et al. Effect of Heat Input on Microstructure and Mechanical Properties of Joints Made by Bypass-Current MIG Welding–Brazing of Magnesium Alloy to Galvanized Steel. Acta Metall. Sin. (Engl. Lett.) 27, 1038–1045 (2014). https://doi.org/10.1007/s40195-014-0118-3
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-014-0118-3