Abstract
Conventionally, the effects of mean stress on fatigue strength of welded structure are regarded to be small. However, based on fatigue damage experience occurring in ship structures, it is obvious that the effect of mean stress on fatigue strength should be large. This relates to the large change of mean stress condition associated with the change in loading conditions during ship operations. In this study, fatigue damage experienced in the end connections of side longitudinal stiffeners of single-hull very large crude oil carriers (SHVLCC) were investigated to understand the effects of mean stress on fatigue strength. The fatigue evaluation method which considers the effect of mean stress was also examined. This method was verified by the evaluation of existing data on fatigue tests and residual stress measurements. This method was confirmed to be effective in understanding the occurrence tendency of fatigue damage in ship structures by its evaluation. This method was applied to the example of actual fatigue damage in the end connections of side longitudinal stiffeners of midsize double-hull tanker to demonstrate the effectiveness of the method.
Similar content being viewed by others
References
API RP 2A–LRFD (1997) Recommended practice for planning, designing and constructing fixed offshore platforms—load and resistance factor design
U.K. Department of Energy Offshore Installations (1990) Guidance on design, construction and certification, 4th edition
BS 5400–10 (1980) Steel, concrete and composite bridges. Code of practice for fatigue
Hobbacher A (2009) IIW recommendations for fatigue design of welded joints and components, WRC Bulletin 520. The Welding Research Council, New York
JSSC (2011) Fatigue design recommendation for steel structures
Nippon Kaiji Kyokai (ClassNK) (1998) Survey on damages in 2nd generation VLCC. J Nippon Kaiji Kyokai No.245, pp.172–192 (in Japanese)
Polezhayeva H, Kang JK, Kudryavtsev Y (2010) A study on residual stress distribution and relaxation in welded components, Proc. of the 20th International Offshore and Polar Engineering Conference
Sonsino CM, Kaufmann H, Wagener R, Fisher C, Eufinger J (2011) Interpretation of overload effects under spectrum loading of welded high-strength steel joints. Welding in the World 55(11):66–78
Hensel, J., Nitschke-Pagel, T., Schonborn, S. and Dilger, K. (2012) Factors affecting the knee point position of S-N curves of welds with longitudinal stiffeners, XIII-2441-12
Farajian M (2013) Welding residual stress behavior under mechanical loading. Welding in the World 57(2):157–169
Hensel J, Nitschke-Pagel T, Dilger K (2016) Effects of residual stress and compressive mean stress on the fatigue strength of longitudinal fillet-welded gusets. Welding in the World 60(2):267–281
Leitner M, Mossler W, Putz A, Stoschka M (2015) Effect of post-weld heat treatment on the fatigue strength of HFMI-treated mild steel joints. Welding in the World 59(6):861–873
Baumgartner J, Bruder T (2013) Influence of weld geometry and residual stresses on the fatigue strength of longitudinal stiffeners. Welding in the World 57(6):841–855
Shimanuki H, Mori T, Tanaka M (2013) Study of a method for estimating the fatigue strength of welded joints improved by UIT, XIII-2495-13
Yildirim HC, Marquis GB (2013) A round robin study of high frequency mechanical impact (HFMI) treated welded joints subjected to variable amplitude loading. Welding in the World 57(3):437–447
Okawa T, Shimanuki H, Funatsu Y, Nose T, Sumi Y (2013) Effect of preload and stress ratio on fatigue strength of welded joints improved by ultrasonic impact treatment. Welding in the World 57(2):235–241
Polezhayeva H, Howarth D, Kumar M, Ahmad B, Fitzpatrick E (2015) The effect of compressive fatigue loads on fatigue strength of non-load carrying specimens subjected to ultrasonic impact treatment. Welding in the World 59(5):713–721
Yildirim HC, Marquis GB (2012) Overview of fatigue data for high frequency mechanical impact treated welded joints. Welding in the World 56(7):82–96
Leitner M, Stoschka M, Eichlseder W (2014) Fatigue enhancement of thin-walled, high-strength steel joints by high-frequency mechanical impact treatment. Welding in the World 58(1):29–39
Weidner P, Ummenhofer T (2013) Fatigue testing data of HFMI-treated joints—verification of existing design recommendations with regards to increased plate thickness and fatigue preloading. XIII-2500-13
Mikkola E, Dore M, Marquis G, Khurshid M (2013) Experimental observations of HFMI treated joints subjected to high R-ratio and variable amplitude loading, XIII-2480-13
Maddox SJ (2010) Fatigue life improvement of steel fillet welds by hammer, needle or shot peening, XIII-2327-10
Le Quilliec G, Lieurade HP, Drissi-Habti M, Inglebert G, Macquet P, Jubin L (2011) Fatigue behavior of welded joints treated by high frequency hammer peening: part 1, Experimental study, XIII-2394-11
Mori T, Shimanuki H, Tanaka M (2015) Effect of UIT on atigue strength of web-gusset welded joints considering service condition of steel structures. Welding in the World 56(9–10):141–149
Tai M, Miki C (2012) Improvement effects of fatigue strength by burr grinding and hammer peening under variable amplitude loading. Welding in the World 56(7):109–117
Matsuoka K, Fujii E (1995) An evaluation method on fatigue crack initiation life at welded joint in steel structures. Journals of SNAJ 178:513–522 (in Japanese)
US Military Standard (1983) MIL-HDBK-5D, pp.I-16 - 18
IACS (2015) Common structural rules for tankers and bulk carriers
Author information
Authors and Affiliations
Corresponding author
Additional information
Recommended for publication by Commission XIII - Fatigue of Welded Components and Structures
Rights and permissions
About this article
Cite this article
Yamamoto, N. Fatigue evaluation of ship structures considering change in mean stress condition. Weld World 61, 987–995 (2017). https://doi.org/10.1007/s40194-017-0461-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40194-017-0461-x