Abstract
The compositional dependence of optical, mechanical, thermal properties, and lattice vibrations of InPxAsySb1–x–y quaternary semiconductor alloys lattice-matched to InAs substrate has been studied. In this study, the physical properties of the binary elements InAs, InSb, and InP that make up the quaternary alloy were employed. Under the virtual crystal approximation (VCA), the empirical pseudo-potential model (EPM) was used to carry out the research. Our findings are in good agreement with the available experimental and theoretical values. In the literature, the composition effect on the optical, mechanical and thermal properties of the InPxAsySb1–x–y/InAs system has not been thoroughly investigated. As a result, we focused on these properties as a function of composition.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Semiconductors that involve components from group III and group V of the periodic table, provide the main resources used in manufacturing great-speed electronics and optoelectronics [1,2,3,4,5]. The quaternary compounds of the III–V groups were liable to an enormous experimental and hypothetical examinations in the ongoing years, and the logical writing contains an enormous quantity of valuable information [6,7,8,9,10,11,12,13]. The understanding of the significance of phonons in electrical and thermal properties of materials requires knowledge of their frequency. They have an important role in the transport characteristics of technologically important semiconductors. Debye temperature relates phonons, thermal expansion, thermal conductivity, specific heat, and lattice enthalpy to thermodynamic characteristics.
Over the whole range of the composition parameters of x and y, the binary compounds InSb, InAs, and InP form a continuous sequence of alloys represented by InPxAsySb1–x–y. The data available for the binary materials that make up these quaternary alloys are used to examine them. The alloy InPxAsySb1–x–y is a potential of great importance in many industrial applications specially thermo-photovoltaic devices. The investigation of the optical, mechanical, thermal properties and lattice vibrations of this alloy is critical, because it gives us control over the planning high-performance electronic systems [10, 14,15,16,17,18,19,20]. Two distinct substrates, InAs and GaSb, can be lattice-matched to the quaternary InPxAsySb1–x–y alloy [21].
The current computations use the (EPM) with (VCA). The lattice constant and the pseudo-potential from factors of the quaternary alloy can be calculated in terms of those of its binary constituent elements. Knowledge of the fundamental energy bandgap, the calculations can be done to obtain the index of refraction\(n\), high-frequency dielectric constant \(\varepsilon_{\infty }\), static dielectric constant \(\varepsilon_{{\text{s}}}\). The polarity \(\alpha_{{\text{p}}}\) of a semiconductor can be calculated from the symmetric and anti-symmetric form factors at G (1,1,1) [22] and using them in calculating the elastic constants \(c_{11} ,c_{12} ,c_{44}\) and elastic moduli bulk \(B_{{\text{u}}}\), shear \(C_{{\text{s}}}\), young \(Y_{{\text{o}}}\).The longitudinal and transverse phonon frequencies \(\omega_{{{\text{LO}}}} , \omega_{{{\text{TO}}}}\) and the Debye temperature \(\theta_{{\text{D}}}\) could be successfully determined.
2 Theory and calculation
Using the EPM technique [23,24,25], in which the symmetric and anti-symmetric pseudo-potential form factors have been adjusted to fit the experimental band gap energies of parent compounds of the studied alloy, namely InP, InAs, and InSb at selected high symmetry points (Γ, X, L) in the first Brillouin zone. In this work, some of the optical, mechanical, and thermal properties of the quaternary alloy InPxAsySb1–x–y lattice-matched to InAs as a substrate have been calculated. The general form of the lattice matching condition is \(x = ay + b\) [21], where:
For InAs as a substrate, we find the lattice match condition between x and y to be:
The study of InPxAsySb1–x–y alloy relies on the physical properties of the binary compounds that constitute it. The calculations are first performed for the binary compounds using (EPM), where a linear superposition of atomic potentials represents the crystal pseudo-potential as:
The energy eigenvalues can be found using pseudo-potential form factors and numerical approaches to solve the secular determinant [26,27,28].
The energy band gaps might be calculated using the obtained energy eigenvalues and. More information on this method can be found in the references [26,27,28]. To start the EPM calculations for the quaternary InPxAsySb1–x–y alloy, we need to know its lattice constant \(^{\prime}a^{\prime}\) and the pseudo-potential form factors, which could be obtained in terms of those of the binary materials according to the relations reported by Adachi [21], where
The polarity \(\alpha\)p of the quaternary alloy is calculated according to Vogl’s relation [22] as:
Knowledge of the polarities, the elastic parameters C11, C12, C44, \(B_{{\text{u}}} , Y_{{\text{o}}}\) and \(C_{{\text{s}}}\) of the studied alloys could be determined [18, 29, 30]. The elastic constants of the investigated material are determined using Baranowski’s improved description [31,32,33].
where \(d = \frac{{\sqrt {3\,} a}}{4}\) is the nearest-neighbor distance, \(\lambda\) is a dimensionless parameter which has a constant value of 0.738 [29]. The determination of \(C_{11}\), \(C_{12}\) and \(C_{44}\) makes it is possible to proceed with their related parameters. The bulk modulus \(B_{{\text{u}}}\) which describes the material’s response to uniform pressure related to the elastic constants by the expression [34]
The shear modulus \(C_{s}\) which describes the material’s response to shearing strains related to the elastic constants by the equation [34]
The young’s modulus \(Y_{0}\) which is a measure of stiffness of a given material related to the elastic constants by the expression [35].
The energy bandgap \({E}_{\Gamma }\) of the InPxAsySb1–x–y alloy are calculated and used to determine its refractive index ‘n’ . This can be done through many empirical formulae [36,37,38] and in this work, we adopted Vandamme’s formula [38]. The calculated refractive index is used to determine the high frequency and the static dielectric constants \(\varepsilon_{\infty }\), \(\varepsilon_{{\text{s}}}\), respectively, using the following formulae [39, 40].
where \(\alpha_{{\text{c}}}\), is the covalency factor which is defined as:
The optical phonon frequencies \({\upomega }_{{{\text{LO}}}}\) and \({\upomega }_{{{\text{TO}}}}\) could be obtained by solving the Lyddane–Sachs–Teller relation [41, 42].
where \(M\) \(\Omega_{{\text{o}}}\) are twice of reduced mass and the volume occupied by one atom.
Finally, knowing the longitudinal phonon frequencies \(\omega_{{{\text{LO}}}} ,\) the Debye temperature \(\theta_{D}\) could be successfully determined [43, 44].
where \(R\) is the universal gas constant \(R = 8.314 \;{\text{J/Mol.K}}\), where the quantity \(\left( {\frac{T}{{\theta_{{\text{D}}} }}} \right)^{3} \int_{0}^{{\theta_{{\text{D}}} /T}} {\frac{{3x^{4} e^{x} }}{{\left( {e^{x} - 1} \right)^{2} }}{\text{d}}x}\) called the Debye function \(F(\theta_{D} /T\))
No table of contents entries found.
3 Results and discussion
Table 1 shows the calculated direct and indirect energy band gaps of the binary compounds InSb, InAs, and InP which establish the InPxAsySb1–x–y alloy. The calculated energy band gaps are matched with the available experimental data and displayed good agreement. To calculate the bandgap energies of the InPxAsySb1–x–y alloys, we required its compositional lattice constants and its form factors. The calculated band gap energies for different values of ‘As’ concentration at standard temperature and pressure are recorded in Table 2 and exhibited in Fig. 1. The calculated results showed that InPxAsySb1–x–y alloys are direct bandgap semiconductors over the whole region of Arsenide concentration ‘y’. The bandgap energies of the quaternary alloy are almost linearly decreased with enhancing the compositional parameter ‘y’. InPxAsySb1–x–y alloy becomes a binary material (InAs) when y = 1 and its energy gaps give excellent accord with the experimental ones [43, 45].
Table 3 and Fig. 2 show the variation of the elastic constants C11, C12, and C44 as a function of As concentration for InPxAsySb1–x–y lattice-matched to InAs substrate. We note that C11 is slightly increased with increasing ‘As’ content on going from InP to InAs, however, C12 and C44 are slightly affected with As concentration. The values of the elastic constants in Table 3 satisfy the stability conditions C11–C12 > 0, C11 > 0, C44 > 0, C11 + 2C12 > 0 [48], which indicating that InPxAsySb1–x–y alloys are mechanically stable in their structure over the whole region of As concentration. The calculated elastic constants for y = 1 are matched with the published results and present good agreement.
The obtained elastic constants have permitted us to determine the Bu, Y0, and Cs moduli of the studied alloy for different values of compositional parameter y as shown in Table 4 and Fig. 3. It is being observed that all quantities are slightly increased with increasing the compositional parameter y. Since, the bulk modulus of a crystalline substance is a measurement of its hardness, so the InPxAsySb1–x–y becomes harder as the composition y increases. Likewise, the increase of shear modulus Cs with increasing As concentration gives high lattice stability. Also, the enhancement of Young’s modulus Y0 with increasing y increases the stiffness of the studied material [6, 50, 51]. The calculated \({B}_{\mathrm{u}}/{C}_{\mathrm{s}}\) ratio for InPxAsySb1–x–y/InAs system is lie between 2.18 and 2.19 which larger than 1.75, which indicates that the studied alloy is in the ductile manner [48].
The accurate knowledge of the n and its related dielectric constants of a semiconductor is a significant part of the strategy and investigation of micro-cavities, solar cells, and injection lasers [52]. In the current work, the compositional dependences of the \(n\) that calculated from the Vandamme’s principle [38], the \({\varepsilon }_{\infty }\) and \({\varepsilon }_{\mathrm{s}}\) are determined and recorded in Table 7 and demonstrated in Fig. 4. The refractive index is somewhat enhanced with enhancing y; however, the dielectric constants are enhanced with the same rate by increasing the compositional parameter y.
Table 8 displays the compositional dependence of the phonon frequencies, Longitudinal \(\omega_{{{\text{LO}}}}\), transverse \(\omega_{{{\text{TO}}}}\), and the Debye temperature \(\theta_{{\text{D}}}\) of InPxAsySb1–x–y/InAs system. The calculated values of them versus As concentration y are plotted in Figs. 5 and 6, respectively. Both phonon frequencies and the Debye temperature are decreased nonlinearly with increasing the compositional parameter ‘y’. Generally, all calculated results regarding the quaternary alloy of interest for y = 1 are compared to publicly available data and found to be in good accord which gives credibility to our findings for InPxAsySb1–x–y /InAs system.
4 Conclusion
Using the (EPM) under the (VCA), the energy band gaps of the InPxAsySb1–x–y/InAs system in the composition range 0 < y < 1 were calculated. The polarities of the quaternary alloys are obtained through Vogl’s relation and used in determining the elastic parameters Cij and (\({B}_{\mathrm{u}}\)), (\({C}_{\mathrm{s}}\)) and (\({Y}_{0}\)) for different values of ‘As’ concentration in InPxAsySb1–x–y/InAs system. The compositional dependence of the \(n\), \({\varepsilon }_{\infty }\) and \({\varepsilon }_{\mathrm{s}}\) of \({\mathrm{InP}}_{x}{\mathrm{As}}_{y}{\mathrm{Sb}}_{1-x-y}\) /InAs were determined. Also, the longitudinal \({\omega }_{\mathrm{LO}}\), the transverse \({\omega }_{\mathrm{TO}}\) phonon frequencies and the \({\theta }_{\mathrm{D}}\) of the studied alloy for different values of compositional parameter y have been examined. The majority of our findings in this article are predictions and can be used as a guide for future research. The studied properties could be beneficial in optoelectronic devices.
References
I. Vurgaftman, Já.R. Meyer, Lá.R. Ram-Mohan, J. Appl. Phys. 89, 5815 (2001)
K. Iga, S. Kinoshita, Process Technology for Semiconductor Lasers: Crystal Growth and Microprocesses (Springer Science & Business Media, 2013)
M.I. Ziane, Z. Bensaad, B. Labdelli, H. Bennacer, Sens. Transducers 27, 374 (2014)
M. Hadjab, S. Berrah, H. Abid, M.I. Ziane, H. Bennacer, B.G. Yalcin, Optik (Stuttg). 127, 9280 (2016)
T. Tsuruta, K. Yamashita, S. Adachi, Y. Hayakawa, M. Kumagawa, Jpn. J. Appl. Phys. 31, 23 (1992)
S. Adachi, Properties of Group-Iv, III-v and II-VI Semiconductors (Wiley, 2005)
A.R. Degheidy, A.M. Elabsy, H.G. Abdelwahed, E.B. Elkenany, Indian J. Phys. 86(5), 363–369 (2012)
A.R. Degheidy, E.B. Elkenany, Semiconductors 45(10), 1251–1257 (2011)
A.R. Degheidy, E.B. Elkenany, Mater. Sci. Semicond. Process. 15, 505 (2012)
A.R.A.R. Degheidy, E.B.E.B. Elkenany, M.A.K.M.A.K. Madkour, A.M. AbuAli, Comput. Condens. Matter 16, e00308 (2018)
A.R. Degheidy, E.B. Elkenany, O.A. Alfrnwani, Computational Condensed Matte 16, e00310 (2018)
A.R. Degheidy, E.B. Elkenany, J. Alloys Compd. 652, 379 (2015)
N.E.-H. Fares, N. Bouarissa, Infrared Phys. Technol. 71, 396 (2015)
A.R. Degheidy, E.B. Elkenany, O. Alfrnwani, Comput. Condens. Matter 15, 55–60 (2018)
S. Bacha, A. Bechiri, F. Benmakhlouf, H. Allouache, N. Bouarissa, Phys. B Condens. Matter 406, 2021 (2011)
A. Alahmary, N. Bouarissa, A. Kamli, Phys. B Condens. Matter 403, 1990 (2008)
B. Ghebouli, M.A. Ghebouli, M. Fatmi, N. Lebgaa, Mater. Chem. Phys. 128, 195 (2011)
N. Bouarissa, Mater. Chem. Phys. 100, 41 (2006)
A.R. Degheidy, E.B. Elkenany, Semiconductors 47(10), 1283–1291 (2013)
A.R. Degheidy, E.B. Elkenany, O.A. Alfrnwani, Comput. Condens. Matter 16, e00300 (2018)
S. Adachi, Properties of Semiconductor Alloys: Group-IV, III-V and II-VI Semiconductors (Wiley, 2009)
P. Vogl, J. Phys. C Solid State Phys. 11, 251 (1978)
E.B. Elkenany, Infrared Phys. Technol. 115, 103720 (2021)
A.R. Degheidy, E.B. Elkenany, Phys. B Condens. Matter 456, 213–220 (2015)
E.B. Elkenany, SILICON 8(3), 391–396 (2016)
P. Harrison, Quantum Wells, Wires and Dots (Wiley Online Library, 2016)
B.K. Ridley, Quantum Processes in Semiconductors (Oxford University Press, 2013)
R. Martin, Electronic Structure-Basic Theory and Practical Methods (Cambridge Univ. Pr., West Nyack, 2004)
J.M. Baranowski, J. Phys. C Solid State Phys. 17, 6287 (1984)
A.R. Degheidy, E.B. Elkenany, Materials Chemistry and Physics 157, 108–115 (2015)
S. Saib, N. Bouarissa, Solid. State. Electron. 50, 763 (2006)
W.A. Harrison, Solid State Theory (Courier Corporation, New York, 1980)
S.-G. Shen, J. Phys. Condens. Matter 6, 8733 (1994)
M. Levinshtein, S. Rumyantsev, M. Shur, Handb. Ser. Semicond Parameters 2, 205 (1999)
N. Bouarissa, M. Boucenna, Phys. Scr. 79, 15701 (2008)
T.S. Moss, Proc. Phys. Soc. Sect. B 63, 167 (1950)
N.M. Ravindra, P. Ganapathy, J. Choi, Infrared Phys. Technol. 50, 21 (2007)
P. Herve, L.K.J. Vandamme, Infrared Phys. Technol. 35, 609 (1994)
G.A. Samara, Phys. Rev. B 27, 3494 (1983)
S.Y. Davydov, S.K. Tikhonov, Semiconductors 32, 947 (1998)
C. Kittel, P. McEuen, P. McEuen, Introduction to Solid State Physics (Wiley, New York, 1996)
C. Kittel, P. McEuen, Introduction to Solid State Physics (Wiley, New York, 1976)
S. Adachi, J. Appl. Phys. 61, 4869 (1987)
S. Adachi, J. Appl. Phys. 58, R1 (1985)
N. Bouarissa, H. Aourag, Phys. Status Solidi 190, 227 (1995)
M. Boucenna, N. Bouarissa, F. Mezrag, Infrared Phys. Technol. 67, 318 (2014)
S. Zerroug, F.A. Sahraoui, N. Bouarissa, Mater. Lett. 60, 546 (2006)
X. Zhang, C. Ying, Z. Li, G. Shi, Superlattices Microstruct. 52, 459 (2012)
M. Boucenna, N. Bouarissa, Mater. Sci. Eng. B 138, 228 (2007)
U. Rössler, New Data and Updates for IV-IV, III-V, II-VI and I-VII Compounds, Their Mixed Crystals and Diluted Magnetic Semiconductors, vol. 44 (2011)
Y. Asadi, Z. Nourbakhsh, J. Phys. Chem. Solids 132, 213 (2019)
J. Piprek, Semiconductor Optoelectronic Devices: Introduction to Physics and Simulation (Elsevier, 2013)
N. Bouarissa, Mater. Lett. 60, 2974 (2006)
N. Bouarissa, Phys. B Condens. Matter 393, 73 (2007)
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Degheidy, A.R., Abuali, A.M. & Elkenany, E.B. Response of mechanical and optoelectronic properties for InPxAsySb1–x–y/InAs system to composition. J. Korean Phys. Soc. 81, 291–297 (2022). https://doi.org/10.1007/s40042-022-00545-4
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40042-022-00545-4