Exceptional Cross-Tension Property in Resistance Spot Welded 7Mn Steels by Combining Cyclic Heat Treatment and Intercritical Annealing

  • Published:
International Journal of Steel Structures Aims and scope Submit manuscript

Abstract

Among the 3rd generation advanced high strength steels, medium Mn steels receive extensive attention sed in modern automotive industry attributing to their encouraging mechanical performance and lower production cost. Unfortunately, the poor cross-tension property of 7Mn steel, one of the typical medium Mn steels, remains a key challenge to hinder its application in automotive industry. In this study, multiple post-weld heat treatment (MPWHT) consisting of cyclic heat treatment and intercritical annealing was employed to improve the cross-tension property of the resistance spot weld of 7Mn steel. With this method, the diffusion of Mn was significantly enhanced, eliminating their severe segregation along the martensite lath boundaries. Additionally, MPWHT facilitated the structure tailoring: the cyclic heat treatment between room and austenization temperature produced the so-called martensitic transformation induced grain refinement and austenite stability while the intercritical annealing triggered austenite reversion transformation, leading to a mixed structure of refined ferrite and austenite across the weld. With the optimization in composition homogeneity and structure tuning, the cross-tension strength (CTS) of a resistance spot welded 7Mn steel stood at 12.7 kN, which is so far the ultrahigh level to our best knowledge. Moreover, this effort brought on button failure mode, suggesting the dominant ductility deformation during the cross-tension test. In a word, the current study achieved an exceptional trade-off between the outstanding CTS and ductility of the resistance spot weld of 7Mn steel by the MPWHT consisting of cyclic heat treatment and intercritical annealing.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  • Amirthalingam, M., van der Aa, E. M., Kwakernaak, C., Hermans, M. J., & Richardson, I. M. (2015). Elemental segregation during resistance spot welding of boron containing advanced high strength steels. Weld World, 59(5), 743–755.

    Article  Google Scholar 

  • Aydin, H., Essadiqi, E., Jung, I., & Yue, S. (2013). Development of 3rd generation AHSS with medium Mn content alloying compositions. Materials Science and Engineering A, 564, 501–508.

    Article  Google Scholar 

  • Cai, Z. H., Ding, H., Misra, R. D. K., & Ying, Z. Y. (2015). Austenite stability and deformation behavior in a cold-rolled transformation-induced plasticity steel with medium manganese content. Acta Materialia, 84, 229–236.

    Article  Google Scholar 

  • Chang, Y., Wang, C. Y., Zhao, K. M., Dong, H., & Yan, J. W. (2016). An introduction to medium-Mn steel: Metallurgy, mechanical properties and warm stamping process. Materials and Design, 94, 424–432.

    Article  Google Scholar 

  • Chao, Y. J. (2003). Ultimate strength and failure mechanism of resistance spot weld subjected to tensile, shear, or combined tensile/shear loads. Journal of Engineering Materials and Technology, 125(2), 125–132.

    Article  Google Scholar 

  • Dutta, A., Park, T. M., Nam, J. H., Lee, S. I., Hwang, B., Choi, W. S., Sandlöbes, S., Ponge, D., & Han, J. (2021). Enhancement of the tensile properties and impact toughness of a medium-Mn steel through the homogeneous microstrain distribution. Materials Characterization, 174, 110992.

    Article  Google Scholar 

  • Gao, Y., Zhao, B., Vlassak, J. J., & Schick, C. (2019). Nanocalorimetry: Door opened for in situ material characterization under extreme non-equilibrium conditions. Progress in Materials Science, 104, 53–137.

    Article  Google Scholar 

  • Gibbs, P. J., De Moor, E., Merwin, M. J., Clausen, B., Speer, J. G., & Matlock, D. K. (2011). Austenite stability effects on tensile behavior of manganese-enriched-austenite transformation-induced plasticity steel. Metallurgical and Materials Transactions A, 42(12), 3691–3702.

    Article  Google Scholar 

  • Hall, E. O. (1951). The deformation and ageing of mild steel: III discussion of results. Proceedings of the Physical Society B, 64(9), 747–753.

    Article  Google Scholar 

  • Han, J., Kang, S., Lee, S., Kawasaki, M., Lee, H., Ponge, D., Raabe, D., & Lee, Y. (2017). Superplasticity in a lean Fe-Mn-Al steel. Nature Communications, 8(1), 751.

    Article  Google Scholar 

  • Han, J., Lee, S., Jung, J., & Lee, Y. (2014). The effects of the initial martensite microstructure on the microstructure and tensile properties of intercritically annealed Fe–9Mn–0.05C steel. Acta Materialia, 78, 369–377.

    Article  Google Scholar 

  • Han, J., & Lee, Y. (2014). The effects of the heating rate on the reverse transformation mechanism and the phase stability of reverted austenite in medium Mn steels. Acta Materialia, 67, 354–361.

    Article  Google Scholar 

  • He, B. B., Hu, B., Yen, H. W., Cheng, G. J., Wang, Z. K., Luo, H. W., & Huang, M. X. (2017). High dislocation density–induced large ductility in deformed and partitioned steels. Science, 357(6355), 1029–1032.

    Article  Google Scholar 

  • Hou, Z. R., Opitz, T., Xiong, X. C., Zhao, X. M., & Yi, H. L. (2019). Bake-partitioning in a press-hardening steel. Scripta Materialia, 162, 492–496.

    Article  Google Scholar 

  • Hu, B., Luo, H., Yang, F., & Dong, H. (2017). Recent progress in medium-Mn steels made with new designing strategies, a review. Journal of Materials Science and Technology, 33(12), 1457–1464.

    Article  Google Scholar 

  • Kazunori, O., Yoshitsugu, S., & Shungo, T. (2003). TS590~980 MPa grade low-carbon equivalent type galvannealed sheet steels with superior spot-weldability. Kawasaki Steel Tech Rep, 48, 9–16.

    Google Scholar 

  • Krajcarz, F., Gourgues-Lorenzon, A. F., & Lucas, E. (2016). Influence of carbon content on the primary solidification mode of high strength steels in resistance spot welding conditions. Scripta Materialia, 120, 98–102.

    Article  Google Scholar 

  • Kujanpää, V. P., & David, S. A. (1986). Microsegregation in high-molybdenum austenitic stainless steel laser beam and gas tungsten arc welds. ICALEO, 1986(S2), 63–69.

    Google Scholar 

  • Lee, Y., & Han, J. (2015). Current opinion in medium manganese steel. Materials Science and Technology, 31(7), 843–856.

    Article  Google Scholar 

  • Lesch, C., Kwiaton, N., & Klose, F. B. (2017). Advanced high strength steels (AHSS) for automotive applications-tailored properties by smart microstructural adjustments. Steel Research International, 88(10), 1700210.

    Article  Google Scholar 

  • Li, S., Yang, S., Lu, Q., Luo, H., & Tao, W. (2019). A novel shim-assisted resistance spot welding process to improve weldability of medium-Mn transformation-induced plasticity steel. Metallurgical and Materials Transactions B, 50(1), 1–9.

    Article  Google Scholar 

  • Li, Y., Li, W., Min, N., Liu, W., & Jin, X. (2017). Effects of hot/cold deformation on the microstructures and mechanical properties of ultra-low carbon medium manganese quenching-partitioning-tempering steels. Acta Materialia, 139, 96–108.

    Article  Google Scholar 

  • Luo, H., Shi, J., Wang, C., Cao, W., Sun, X., & Dong, H. (2011). Experimental and numerical analysis on formation of stable austenite during the intercritical annealing of 5Mn steel. Acta Materialia, 59(10), 4002–4014.

    Article  Google Scholar 

  • Miller, R. L. (1972). Ultrafine-grained microstructures and mechanical properties of alloy steels. Metallurgical and Materials Transactions b: Process Metallurgy and Materials Processing Science, 3(4), 905–912.

    Google Scholar 

  • Mishra, A., Saha, A., & Maity, J. (2016). Development of high strength ductile eutectoid steel through cyclic heat treatment involving incomplete austenitization followed by forced air cooling. Materials Characterization, 114, 277–288.

    Article  Google Scholar 

  • Park, G., Kim, K., Uhm, S., & Lee, C. (2019a). Remarkable improvement in resistance spot weldability of medium-Mn TRIP steel by paint-baking heat treatment. Materials Science and Engineering A, 766, 138401.

    Article  Google Scholar 

  • Park, G., Kim, K., Uhm, S., & Lee, C. (2019b). A comparison of cross-tension properties and fracture behavior between similar and dissimilar resistance spot-weldments in medium-Mn TRIP steel. Materials Science and Engineering A, 752, 206–216.

    Article  Google Scholar 

  • Petch, N. J. (1953). The cleavage strength of polycrystals. Journal of Iron Steel institute, 173(5), 25–28.

    Google Scholar 

  • Pouranvari, M., Sobhani, S., & Goodarzi, F. (2018). Resistance spot welding of MS1200 martensitic advanced high strength steel: Microstructure-properties relationship. Journal of Manufacturing Processes, 31, 867–874.

    Article  Google Scholar 

  • Sadeghpour, S., Somani, M. C., Kömi, J., & Karjalainen, L. P. (2021). A new combinatorial processing route to achieve an ultrafine-grained, multiphase microstructure in a medium Mn steel. Journal of Materials Research and Technology, 15, 3426–3446.

    Article  Google Scholar 

  • Saha, A., Mondal, D. K., Biswas, K., & Maity, J. (2012a). Microstructural modifications and changes in mechanical properties during cyclic heat treatment of 0.16% carbon steel. Materials Science and Engineering A, 534, 465–475.

    Article  Google Scholar 

  • Saha, D. C., Cho, Y., & Park, Y. (2013). Metallographic and fracture characteristics of resistance spot welded TWIP steels. Science and Technology of Welding and Joining, 18(8), 711–720.

    Article  Google Scholar 

  • Saha, D. C., Han, S., Chin, K. G., Choi, I., & Park, Y. (2012b). Weldability evaluation and microstructure analysis of resistance-spot-welded high-Mn steel in automotive application. Steel Research International, 83(4), 352–357.

    Article  Google Scholar 

  • Shirmohammadi, D., Movahedi, M., & Pouranvari, M. (2017). Resistance spot welding of martensitic stainless steel: Effect of initial base metal microstructure on weld microstructure and mechanical performance. Materials Science and Engineering A, 703, 154–161.

    Article  Google Scholar 

  • Smoljan, B. (2004). An analysis of combined cyclic heat treatment performance. Journal of Materials Processing Technology, 155–156, 1704–1707.

    Article  Google Scholar 

  • Stadler, M., Gruber, M., Schnitzer, R., & Hofer, C. (2020). Microstructural characterization of a double pulse resistance spot welded 1200 MPa TBF steel. Weld World, 64(2), 335–343.

    Article  Google Scholar 

  • Wang Y., Ding K., Zhao B., Zhang Y., Wu G., Wei T., Pan H., Gao Y. (2020a). Effect of the cooling time on the cross tensile strength of the resistance spot welded medium manganese steel. In TMS 2020a 149th annual meeting & exhibition supplemental proceedings. Springer International Publishing, pp 515–523

  • Wang Y., Ding K., Zhao B., Zhang Y., Wu G., Wei T., Pan H., Gao Y. (2020b) Highly enhanced cross tensile strength of the resistance spot welded medium manganese steel by optimized post-heating pulse. In TMS 2020b 149th annual meeting & exhibition supplemental proceedings. Springer International Publishing, pp 1871–1880

  • Wei, R., Enomoto, M., Hadian, R., Zurob, H. S., & Purdy, G. R. (2013). Growth of austenite from as-quenched martensite during intercritical annealing in an Fe–01C–3Mn–15Si alloy. Acta Mater, 61(2), 697–707.

    Article  Google Scholar 

  • William, J. H., & Morris, C. (1949). Stabilization of the austenite-martensite transformation. Transactions of the Metallurgical Society of AIME, 180, 447–470.

    Google Scholar 

  • Wu, G., Chan, K., Zhu, L., Sun, L., & Lu, J. (2017). Dual-phase nanostructuring as a route to high-strength magnesium alloys. Nature, 545, 80–83.

    Article  Google Scholar 

  • Yang, F., Luo, H., Hu, C., Pu, E., & Dong, H. (2017). Effects of intercritical annealing process on microstructures and tensile properties of cold-rolled 7Mn steel. Materials Science and Engineering A, 685, 115–122.

    Article  Google Scholar 

  • Zhang, X., Teng, R., Liu, T., Shi, Y., Lv, Z., Zhou, Q., Wang, X., Wang, Y., Liu, H., & Xing, Z. (2022). Improving strength–ductility synergy in medium Mn steel by combining heterogeneous structure and TRIP effect. Materials Characterization, 184, 111661.

    Article  Google Scholar 

  • Zhao, B., Wang, Y., Ding, K., Wu, G., Wei, T., Pan, H., & Gao, Y. (2021a). Role of intercritical annealing in enhancing the cross-tension property of resistance spot-welded medium Mn steel. Journal of Materials Engineering and Performance, 30, 1259–1269.

    Article  Google Scholar 

  • Zhao, B., Wang, Y., Ding, K., Wu, G., Wei, T., Pan, H., & Gao, Y. (2021b). Enhanced cross-tension property of the resistance spot welded medium-Mn steel by in situ microstructure tailoring. International Journal of Steel Structures, 212(2), 666–675.

    Article  Google Scholar 

  • Zhong, L., Wang, J., Sheng, H., Zhang, Z., & Mao, S. X. (2014). Formation of monatomic metallic glasses through ultrafast liquid quenching. Nature, 512(7513), 177–180.

    Article  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Natural Science Foundation of China (Grant no. U1760102), Independent Research Project of State Key Laboratory of Advanced Special Steel and Shanghai Key Laboratory of Advanced Ferrometallurgy (Shanghai University, Grant no. 19DZ2270200), the State Key Laboratory of Development and Application Technology of Automotive Steels (Baosteel Group, Grant no. Y17ECEQ05Y).

Author information

Authors and Affiliations

  1. State Key Laboratory of Advanced Special Steel and Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai, 200444, People’s Republic of China

    Bingge Zhao, Yuanfang Wang, Kai Ding, Guanzhi Wu, Tao Wei & Yulai Gao

  2. Center for Advanced Solidification Technology (CAST), School of Materials Science and Engineering, Shanghai University, Shanghai, 200444, People’s Republic of China

    Bingge Zhao, Yuanfang Wang, Kai Ding, Guanzhi Wu, Tao Wei & Yulai Gao

  3. State Key Laboratory of Development and Application Technology of Automotive Steels, Shanghai, 201900, People’s Republic of China

    Hua Pan

  4. Automobile Steel Research Institute, R&D Center, Baoshan Iron and Steel Co., Ltd., Shanghai, 201900, People’s Republic of China

    Hua Pan

Authors
  1. Bingge Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Yuanfang Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Kai Ding
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Guanzhi Wu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Tao Wei
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Hua Pan
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Yulai Gao
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Yulai Gao.

Ethics declarations

Competing interest

The authors declare that they have no known competing financial interest.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Zhao, B., Wang, Y., Ding, K. et al. Exceptional Cross-Tension Property in Resistance Spot Welded 7Mn Steels by Combining Cyclic Heat Treatment and Intercritical Annealing. Int J Steel Struct 23, 1020–1030 (2023). https://doi.org/10.1007/s13296-023-00748-w

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s13296-023-00748-w

Keywords

Search

Navigation