Abstract
The mechanical properties and microstructure of 7075 aluminum alloy during the two-stage aging process have been studied by means of Rockwell hardness test, tensile test, X-ray diffraction, scanning electron microscopy, transmission electron microscopy (TEM) and high-resolution TEM. The results illustrated that there existed double peaks for both the hardness and strength in 7075 aluminum alloy during the two-stage aging process. Furthermore, the aging time to reach the second peak was obviously shortened compared to single-stage aging process. At the first peak aging state, the strengthening effect of the alloy was dominated by high-density GP zones, but η′ phase (MgZn2) was mainly the strengthening phase at the second peak aging state.
Similar content being viewed by others
References
Li R X, Li R D, Zhao Y H, He L Z, Li C X, Guan H R, and Hu Z Q, Mater Lett58 (2004) 2096.
Yang X, Liu J, Chen J, Wan C, Fang L, Liu P, and Wu C, Acta Metall Sin27 (2014) 1070.
Zhao Y L, Yang Z Q, Zhang Z, Su G Y, and Ma X L, Acta Mater61 (2013) 1624.
Berg L K, Gjønnes J, Hansen V, Li X Z, Knutson-Wedel M, Waterloo G, and Wallenberg L R, Acta Mater49 (2001) 3443.
Vasudevan A K, and Doherty R D, Treatise Mater Sci Technol31(1989) 27.
Song R G, and Zhang Q Z, Mater Sci Eng C17(2001) 133.
Yan D J, and Zhang Y D, J Mater Eng4 (1993) 13.
Chen X M, and Song R G, Hot Work Technol3 (2009) 93.
Ren J P, Song R G, Chen X M, and Li J, Hot Work Technol38 (2009) 119.
He C D, Ren J P, and Xu B, Appl Mech Mater157 (2012) 331.
Wen K, Xiong B Q, Zhang Y A, Li Z H, Li X W, Huang S H, Yang L Z, Yan H W, and Liu H W, Mater Sci Forum941 (2018) 949.
Wang Y L, Jiang H C, Li Z M, Yan D S, Zhang D, and Rong L J, J Mater Sci Technol34 (2018) 1250.
Rout P K, Ghosh M, and Ghosh K, J Mater Eng Perform24(2015)2792.
Robinson J S, and Tanner D A, Mater Sci Forum524–525 (2006) 305.
Wloka J, Hack T, and Virtanen S, Corr Sci49 (2007)1437.
Li M H, Yang Y Q, Feng Z Q, Feng G H,. Huang B, Chen X Y, Han M, and Ru J G, Intermetallics55 (2014) 49.
Song R G, Dietzel W, Zhang B J, Liu W J, Tseng M K, and Atrens A, Acta Mater52 (2004) 4727.
Han B Q, Lavernia E J, and Mohamed F A, Philos Mag Lett83 (2003) 89.
Orowan E, Engineering164 (1947) 581.
Lin Y C, Jiang Y Q, Zhang J L, and Chen X M, Adv Eng Mater (2017) 1700583.
Liu Y R, Pan Q L, Li H, Huang Z Q, and Ye J, J Alloy Compd792 (2019) 32.
Srivatsan T S, Sriram S, Veeraraghavan D, and Vasudevan V K, J Mater Sci32 (1997) 2883.
Acknowledgements
The financial aid of the National Natural Science Foundation of China under Grant No. 51871031 is gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Cai, S.W., He, Y. & Song, R.G. Study on the Strengthening Mechanism of Two-Stage Double-Peaks Aging in 7075 Aluminum Alloy. Trans Indian Inst Met 73, 109–117 (2020). https://doi.org/10.1007/s12666-019-01809-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-019-01809-7