Introduction

Vivianite is a hydrous ferrous iron phosphate mineral [Fe3(PO4)2·8H2O] named after John Henry Vivian (1785–1855), an English mineralogist, by Abraham Gottlob Werner (1749–1817). It crystallizes in the monoclinic system in the form of needle-shaped crystals or spherical aggregates with sizes ranging from some micrometers to some centimeters. In its original state vivianite is colorless, however, due to gradual oxidization of ferrous iron, it turns to vivid blue in air. When values of ferric iron exceed 50% vivianite will alter to metavivianite [Fe2+Fe3+2(PO4)2(OH)2·6H2O] (Rouzies and Millet 1993). At higher temperatures further oxidization may result in the formation of ferric phosphate minerals, for example lipscombite [(Fe2+,Mn2+)(Fe3+)2(PO4)2(OH)2], rockbridgeite [Fe2+Fe3+4(PO4)3(OH)5] and strengite (FePO4⋅2H2O) (Nriagu and Dell 1974).

Vivianite may occur in different geological environments. Its formation requires reducing conditions with high ferric iron and orthophosphate as well as very low S2− concentrations in the solution (Nriagu 1972). Vivianite can be formed as a secondary mineral in the oxidation zone of ore deposits, and it may precipitate in sediments under reducing conditions in fluvial, lacustrine, marine and estuarine environments, and waterlogged soils (Rothe et al. 2016; Grizelj et al. 2017). Moreover, it can be found in organic-rich, highly contaminated canal beds (Dodd et al. 2000, 2003; Taylor and Boult, 2007), in wastewater sludge (Frossard et al. 1997) as well as in archeological settings (McGowan and Prangnell 2006). Since increased nutrient supply is favorable for vivianite authigenesis, its occurrence in sedimentary settings may indicate human impact (Goslar et al. 1999).

Since vivianite is stable under reducing conditions, the phosphorus bound in its crystal structure. Consequently, eutrophication of freshwaters due to human activities could be controlled using Fe salts for removing significant amount of phosphorus from the water through vivianite formation (Gunnars et al. 2002; Gächter and Müller 2003; Kleeberg et al. 2012; Rothe et al. 2014; O’Connell et al. 2015). Similarly, by the formation of iron(II) phosphate minerals, ferric iron amendments may also increase phosphorus retention in wastewater-treating constructed wetlands (Vymazal 2007) and in septic tank wastewaters (Azam and Finneran 2014).

It seems that vivianite may play important role in controlling arsenic release in groundwater environments. Some experiments suggest that vivianite can adsorb dissolved arsenic(V) (Islam et al. 2007; Hudson-Edwards et al. 2008; Thinnappan et al. 2008), and others found that arsenate(V) can partly replace the phosphate anion forming a vivianite–symplesite [Fe3(PO4)1.7(AsO4)0.3·8H2O] solid solution (Muehe et al. 2016).

In Hungary, vivianite occurs in several localities of different geological settings (Szakáll et al. 2005). It can be found in close vicinity of iron ore bodies (Rudabánya, NE Hungary), recent or former swampy areas together with bog iron (Somogyszob, South Transdanubian region; Nyírség, East Hungary; Bagamér and Létavértes villages at the Hungarian–Romanian border; Fertő Lake at the Austrian–Hungarian border), in oil shale from the Little Hungarian Plain as well as in clays mainly in the Great Hungarian Plain.

The study area is situated in the central part of a chemical plan. The environmental geological survey was begun before 2000; and, up till now, several hundred drillings of different depth and engineering geological sounding have been made. Most of the drillings are shallower than 15 m (although some drillings exceed the depth of 30 m), and several dozen ones reach 8 m in depth. In the cores there is no vivianite detectable by the naked eye, or only some traces can be noticed. However, in 2007 the occurrence of vivianite was observed in a discrete part of clustered monitoring wells No. ICE-113 drilled in the central part of the area of the chemical works. The drilled clayey–silty layers contain numerous vivianite aggregates of some millimeters in size at 7.6–8.5 m depth from the surface. Archive aerial photograph in Fig. 1 shows that next to the site of monitoring well cluster No. ICE-113 an earth-bedded sewage pond with the size of approximately 30 × 12 m had been formed where plant waste coming from the technological process had been disposed of. There is hardly any information on the date of the building and the depth of the pond, and the quantity of the plant material has not been known, either. It can be seen on aerial photos taken in 1956 (Fig. 1a) and its contour and the cassettes can be noticed on an aerial photo taken in 1965 (Fig. 1b). However, it no longer visible on the aerial photo taken in 1967 (Fig. 1c); the sewage pond was filled up, covered with concrete, and different containers and tanks were deposited on the site. The aim of this study was to reveal factors (both natural and anthropogenic) that play a key role in the formation of this distinct vivianite occurrence.

Fig. 1
figure 1

a Pond (blue line) for disposal of plant waste coming from extraction and its environments on aerial photographs taken in 1956. b Contour of the pond and the cassettes are still recognizable on the aerial photograph taken in 1965. c The ponds and the cassettes are no longer visible on the aerial photograph taken in 1967. b and c available from fentrol.hu.

Full size image

Geological settings

Quaternary geological history of the Great Hungarian Plain, the largest landscape unit of Hungary, has been basically determined by two geological events. The first is the formation of the Pannonian Basin in a structural sense at the end of the Miocene. This relatively young basin (around 15 million years old) has an anomalous thin lithosphere and is filled with several thousand meters thick sediment layers; simultaneous to their accumulation intense volcanism took place as late as the Quaternary (Jámbor 2001; Zelenka et al. 2004; Harangi, 2001; Balázs et al. 2016). Geological development of the Pannonian Basin was in close relationship with that of the Central Paratethys (middle part of the Paratethys extending from the northern foreland of the Alps to the Aral Lake). Its final occlusion from the ocean resulted in a peculiar endemic fauna. Rivers coming from the surrounding mountainous area formed huge delta systems, and 4.5–6.5 mys BP the Pannonian Lake, a remnant of the Paratethys was filled with prograding delta sediments; the area became a fluvial plain with several small lakes (Kázmér 1990; Gábris and Nádor 2007).

The second is the fact that the area of the Great Hungarian Plain belonged to the periglacial area, where one of the most complex fluvial systems in Europe developed under the given climatic conditions (Rónai 1985; Jámbor 2001; Nádor et al. 2007; Kiss et al. 2015). The Danube and the Tisza, the two main rivers of the Great Hungarian Plain, and their tributaries formed alluvial plains and fans, where large areas were covered with loess and loess derivatives transported by strong wind from different source areas (Lehmkuhl et al. 2018). Simultaneously, wind-blown sand and mixed sediments of sand and loess coming from local fluvial sources were also formed (Rónai 1985).

The study area is situated in the border area of Hortobágy and Hajdúság regions, which are lowland terrains of recent and young sedimentary deposits (Fig. 2). The western part of the site belongs to Hortobágy plain with a height of 90 m a.s.l., and the eastern part to the loessy ridge of Hajdúság has an elevation of 120–150 m a.s.l. The biggest watercourse in the region is the Tisza River.

Fig. 2
figure 2

Simplified geological map of the study area based on 1:100,000 surface geological map series of Hungary (https://map.mbfsz.gov.hu/fdt100/)

Full size image

On and near the surface there are dominantly fluvial, subordinately eolian and lacustrine Pleistocene and Holocene sedimentary formations. Consequently, these sediments have a quite complex structure with highly varying lithologic character, thickness, extension, and, due to the fluvial environment, interfingering and wedging of the strata.

The thickness of the Quaternary formations accumulated on the Pannonian strata ranges from 125 to 160 m (Franyó 1992). This dominantly fluvial sediment formation is well-bedded; its lower part is dominated by gravel and sand layers with interbedded clayey layers, and its upper part is characterized by fine-grained sediments, i.e. sand–silt–clay layers and interbeddings (Rónai and Moldvay 1966).

The oldest formations on the surface (loess, loess derivative, fluvial sandy gravel, gravel, and eolian sand) were deposited in the Late Pleistocene. In the Hortobágy area, which is situated at a lower altitude, fluvial silt and clayey silt as well as fluvial clay, silt and lacustrine clayey silt settled in the Old and the New Holocene, respectively. Salinization is common, and it may occur in almost every sediment type.

Geological features of the study area can be summarized as it follows. In the industrial area, highly cohesive loamy–clayey solonetz is the dominant soil type with a maximum thickness of 1 m. The original Holocene soil occurs only in smaller or larger patches, it is changed by anthropogenic landfill of varying composition and thickness. Beneath the soil, there is a 1–3 m thick fine-silty coarse silt layer with varying clay content (loess derivative). It is friable above the level of the water table, and plastic beneath it. The loess derivative was deposited on gray or yellow fine-grained sand, silty fine sand, which is the first groundwater aquifer. Here and there the proportion of silt is significant, and the sediment should be regarded as fine sandy silt. It is not a horizontal formation therefore it can be pitched out. Its thickness ranges from 1 to 2.5 m.

Beneath this aquifer, there is a cohesive clayey fine silt (“basal clay” or “underlying clay”) layer with a thickness ranging from 1.5 to 4 m. Considering sedimentary facies, it can be regarded as a floodplain deposit, however, the upper part of the “basal clay” proved to be fat clay based on soil mechanics consistency tests; therefore, it can be interpreted as an aquitard layer.

Beneath the “basal clay” gray or brown alternating fine-layered fine sandy silt and silty sand layers with varying clay content can be found, the thickness of this formation is 12–15 m. It can be interpreted as a floodplain deposit interfingering with levee sandy deposits.

The next formation extends down to 35 m. It is built up with fine- and coarse-grained channel deposits alternating with bluish gray, highly carbonaceous alluvial silts and clays deposited in a dead water environment.

The potentiometric contour map based on synchronous hydraulic head data suggests that the horizontal flow of the groundwater in the first aquifer has a dominantly western direction (from ~ 2 to 6 m) (Fig. 3). Using HydrogeoEstimatorXL Excel-based tool (Devlin and Schillig 2017) the estimated mean horizontal hydraulic gradient is 0.004 for the first aquifer. The potentiometric contour map based on synchronous hydraulic head data measured in the second aquifer shows a simpler flow pattern and indicates a characteristic western flow direction. The value of the mean horizontal hydraulic gradient estimated using HydrogeoEstimatorXL (Devlin and Schillig 2017) for the second aquifer is 0.003. The vertical hydraulic gradient between the first and second aquifers varies between − 0.02 and − 0.06.

Fig. 3
figure 3

Groundwater contour map and flow direction of the site showing the elevation of piezometric surface for the a first and b second aquifers during the autumn season of 2013

Full size image

Methods

Soil samples of the underlying clay bed were taken from the cutting of the drilling of well cluster No. ICE-113 from various depths. Vivianite was separated manually under binocular stereomicroscope for X-ray powder diffraction (XRPD), thermal analysis (TG/DTG), and scanning electron microscopic and energy dispersive spectrometry (SEM–EDS) study.

Sieve and hydrometer analyses were combined to define the grain-size distribution of seven soil samples derived from well cluster No. ICE-113 drilling (4.0–4.25, 6.5–6.6, 7.6–7.8, 7.8–8.0, 8.0–8.2, 8.2–8.4, 8.4–8.5 m).

To identify the mineralogical composition of the underlying clay layer, as well as the presence of vivianite, XRPD analysis was performed on soil samples derived from 4.0 to 4.25 m and 6.5–6.6 m and on separated vivianite from 7.6 to 8.5 m depth intervals. XRPD analysis was carried out on air-dried and pulverized soil samples at the Institute of Mineralogy and Geology, University of Miskolc. A Bruker D8 Advance type diffractometer was used in Bragg–Brentano geometry, equipped with Cu anode. During the measurement fixed slit system and a dynamic scintillation detector with secondary graphite monochromator were applied. The accelerating voltage and current were 40 kV and 40 mA, respectively. Identification of mineral phases was achieved using Search/Match option of DiffracPlus EVA. Quantitative determination of crystalline phases was performed by full pattern matching procedure of the DiffracPlus Basic Evaluation Package software (EVA 11, Release 2005).

Thermal analysis (thermogravimetry) of separated vivianite from 7.6 to 8.5 m depth interval was carried out at the Department of Mineralogy and Geology, University of Debrecen using a Mettler-Toledo TGA/SDTA 851e thermos-microbalance equipment. Approximately 25 mg of the vivianite sample was heated in an open ceramic crucible at a rate of 10.0 °C/min up to 800 °C under static air atmospheric condition.

The morphology and chemical composition of vivianite was investigated by SEM–EDS. A JEOL JXA-8600 Superprobe unit equipped with three wavelength-dispersive spectrometers and an EDX silicon drift detector (SDD) was used. These examinations were carried out at the Institute of Mineralogy and Geology, University of Miskolc. For EDX measurements 20 kV accelerating voltage was used, with a probe current of 20 nA.

To demonstrate the spatial distribution of hydrochemical parameters and selected chemical constituents, the available data concerning drillings and hydrochemical analyses were collected. Field measurements were performed by Terrapeuta Ltd. using Hanna Instruments HI-9828 Multiparameter Portable Meter. For mapping the distribution of relevant data kriging interpolation method was used.

Results

Simplified stratigraphy of well cluster No. ICE-113 is shown in Fig. 4. Beneath the approximately 3 m thick mixed clayey–silty–sandy anthropogenic filling, there is a 1 m thick silt (loess derivatives) of brown color followed by a 4 m thick clayey formation containing vivianite of earthy appearance and bluish color at the depth ranging from 7.6 to 8.5 m showing aggregates of flattened crystals on a background consisting of quartz and phyllosilicates (Fig. 5). According to the drilling protocol, the vivianite-bearing layer was described as homogeneous, cohesive one of gray-grayish yellow color, which contains horizontally oriented carbonate concretions in considerable amounts. Detailed macroscopic observations and grain-size distribution analyses revealed, however, inhomogeneity of the clayey formation (Fig. 6; Table 1).

Fig. 4
figure 4

Schematic geological setting of well cluster No. ICE-113 according to the drilling protocol

Full size image
Fig. 5
figure 5

Macroscopic appearance and SEM photograph of vivianite from the cutting of well cluster No. ICE-113

Full size image
Fig. 6
figure 6

Field of grain-size distribution curves for seven samples of a “clay” layer in the section of 4.0–8.5 m of the well cluster No. ICE-113 (for data see Table 1)

Full size image
Table 1 Particle size distribution of the studied soil sample (dominant fraction in bold)
Full size table

To the depth of 5.2 m, it is light yellow clayey silt containing reddish black iron–manganese patches of some mm in size, fine micas, some carbonate in the matrix, and based on the results of the grain-size distribution (see Table 1, No. ICE-113, 4.0–4.25 m), it can be regarded as clayey silt according to Shepard’s nomenclature (Shepard 1954). XRPD and thermal analytical studies show that the mineral constituents of the layer are quartz (63%), illite ± muscovite (19%), plagioclase (13%), calcite (3%) and chlorite (2%) (Table 2).

Table 2 Results of XRPD studies of the analyzed samples
Full size table

From 5.2 to 6.6 m the formation is mild gray in color, and homogeneous. It contains mollusk shells (both complete and fragmented ones) and sporadically fine mica lamellae in considerable quantity; the matrix contains carbonate in high amount. Based on the grain-size distribution (Table 1, No. ICE-113, 6.5–6.6 m), the dominant fraction is medium- and coarse-grained silt (70 wt%); the proportion of the clayey fraction is less than 15wt%, and that of the (fine-grained) sand fraction is not more than 10 wt%. According to Shepard’s nomenclature (Shepard 1954), it can be classified as clayey silt. XRPD and thermal analytical studies show that the mineral constituents of the layer are quartz (64%), plagioclase (13%), calcite (8%), chlorite (9%), and illite ± muscovite (6%) (Table 2).

Beneath 6.6 m, the formation is relatively homogeneous; light grayish brown in color, fine laminated, and sporadically contains fine mica lamellae. Between 7.6 and 8.5 m, it contains dark blue vivianite of earthy appearance and very low amount of carbonate.

Between 7.8 and 8.5 m fine (sulfate?) precipitation covers the formation. According to the grain-size distribution (No. ICE-113, 7.6–7.8, 7.8–8.0, 8.0–8.2, 8.2–8.4, and 8.4–8.5 m), the dominant fractions are medium- and fine-grained silt; the proportion of the clay fraction considerably decreased (ca. 10 wt%), and the quantity of the sandy fraction is highly varying (from 8 to 25 wt%). Due to the varying proportion of the fine-grained sand and clay fractions, they can be classified as sandy silt or clayey silt according to Shepard’s nomenclature (Shepard 1954).

The separated vivianite material was studied by macroscopic, stereo microscopic scanning microscopic observations, thermal analysis (TG/DTG), and XRPD techniques. Macroscopic and stereo microscopic observations suggest that the vivianite dominantly appears along laminae of the finely layered matrix, as it were, “impregnates” it; subordinately, vivianite forms earthy aggregates. Back-scattered electron microscope image of the separated vivianite material shows the lamellae of the vivianite crystals grew on the grains of the formation and filled the intergranular space (Fig. 5). Thermal features of vivianite have not been understood in all details. Some studies suggest that temperature loss (together 25% loss of mass) due to one-step thermal decomposition occurs between 70 and 500 °C with a peak at about 150 °C (Ogorodova et al. 2017). In contrast, Földvári (2011) suggests that vivianite loses its crystalline water through an endothermic reaction between 250 and 300 °C; this author notes, however, that crystalline water may be removed in several steps, too. TG/DTG curves suggest that vivianite crystalline water is released in several steps (Fig. 7), which is in accordance with some former studies. Results of the XRPD study show that besides vivianite, the separated material contains some quartz, muscovite, chlorite, and feldspars, as well (Table 2; Fig. 8).

Fig. 7
figure 7

TG/DTG curves of vivianite separated from the depth of 7.6–8.5 m

Full size image
Fig. 8
figure 8

taken from the depth of 7.6–8.5 m

X-ray powder diffraction diagram of the separated vivianite material

Full size image

Hydro-chemical parameters and concentrations of some selected chemical constituents from the first and second aquifers are shown in Table 3. Comparing to the background, data indicate increased dissolved orthophosphate, sulfate, iron, and HCO3− concentration, and decreased Eh values in both aquifers in the vicinity of the former sewage pond and well cluster No. ICE-113.

Table 3 Summary of selected chemical constituent concentrations and physico-chemical parameters in samples from wells screened in the first and second aquifers
Full size table

Discussion

As it was mentioned in the introduction, occurrence of vivianite in Hungary is common in terrestrial sediments characterized by reductive environments of high iron(II) and orthophosphate and low S2− concentration of pore water, where pH and Eh conditions are also sufficient (Szakáll et al. 2005). The point is whether the geochemical features in the study area are adequate for the formation of vivianite.

Chemical and physico-chemical conditions of groundwater

In the area of the chemical plant, the “basal clay” forming the floor of the first aquifer was exposed by several drills; however, vivianite has not been found in it. The chemical composition of the pore water in the “basal clay” has not been known; however, chemical composition and physical–chemical features of the first and second aquifers are well studied. Chemical constituent and physico-chemical parameter data listed in Table 3 suggest extremely high orthophosphate concentration in the groundwater within a distance of 150 m NE of the well cluster No. ICE-113 in the first aquifer (2–6 m beneath the surface) with a concentration range between 10 and 40 mg/dm3 and with a maximum value of 80 mg/dm3, while the average orthophosphate concentration for the whole area of the plan is as low as 0.5 mg/dm3 (Table 3). Because of the limitation of available data (n < 10), it is difficult to determine obvious trends by time series analysis (e.g., Mann–Kendall test); it can be stated, however, that in the studied time span orthophosphate concentration in the first aquifer increased in the area of the sewage pond, while no trend could be experienced in the monitoring well cluster No. ICE-113. Moreover, in the vicinity of the sewage pond increased orthophosphate concentration (5–20 mg/dm3) could be detected even in the second aquifer, which possibly shows an increasing trend. Simultaneously to the orthophosphate concentration, sulfate concentration also increased in the first and the second aquifers at the sewage pond (150–400 and 100–270 mg/dm3, respectively); time series of the concentrations suggest increasing–possibly increasing trend, excepting the well cluster No. ICE-113, where a decreasing trend is noticed. This decrease in sulfate can be in relationship with diluting processes at plume margin, and it can be a consequence of increasing sulfate reduction following the iron reduction in the Terminal Electron Accepting Process sequence; as a consequence, HS− is formed from the dissolved orthophosphate (Miao et al., 2012). The sulfate reaction can take place under circumneutral pH conditions with considerable H+ consumption; or due to microbiological activity by requisition of organic carbon or H2, which finally results in pH decrease (Nriagu 1972; Postma 1981; Heiberg et al. 2012; Egger et al. 2015; Rothe et al. 2014, 2016).

Accordingly, values of Eh and dissolved oxygen have decreased in the sewage pond area (particularly, in the first aquifer), while contents of dissolved nitrate and total iron have multiplied. In the area of the former sewage pond ORP values measured in the wells installed into the first aquifer after purging have varied between −365.8 (calculated Eh: −151 mV) and −65.5 mV (calculated Eh: 149 mV) (with an average of −205 mV ORP and of 8 mV Eh), for the last 5 years (2014 and 2018); while in a monitoring well near the site of well cluster No. ICE-113 screened in the first aquifer the ORP values have ranged from −82.5 (calculated Eh: 133 ± 5 mV) to 142.6 mV (calculated Eh: 359 ± 5 mV) (with an average of 22 mV ORP and of 238 mV Eh). The average Eh distribution map calculated from the ORP results of the first aquifer clearly shows that redox potential on the site of the former pond is definitely low even nowadays, which indicates reductive conditions, as it was mentioned previously. This reductive condition tends to change just in the environment of the well cluster No. ICE-113 as it is indicated by ORP, as well as Eh values ranging from 0 to 50 mV and from 200 to 300 mV. The ORP values vary from −50 to −150 mV (Eh of 80–190 mV) in the second aquifer and are also lower than the background in the surroundings of the sewage pond.

A USGD Excel sheet (Jurgens et al. 2009) was used for identifying redox processes in the groundwater. Unfortunately, however, the redox state of iron and manganese was not analyzed, and dissolved sulfur was analyzed as sulfate, therefore, certain forms and the total amount of sulfides is not known. It is obvious, however, that under the sewage pond there are mixed (anoxic) redox conditions in the first aquifer, while mixed (oxic-anoxic) conditions are characteristic for the well cluster No. ICE-113 and the background; then again, everywhere in the second aquifer mixed (anoxic) redox conditions can be detected. Therefore, groundwater data clearly show that in the area of and some meters surrounding the pond physical and chemical conditions dramatically changed compared to the wider environment, and it may have an effect on geochemical and biochemical processes in the area. Distribution maps (Fig. 9) show that the concentration of dissolved oxygen is depleted not only at the pond but at the northern part of the study area, too. Possibly, this depletion has not been the result of the decomposition of the deposed organic material. It is supported by the fact that, parallel to a decrease in DO, an increase in dissolved total iron can be detected in the pond area, which suggests increasing microbial Fe reduction. This phenomenon can also be observed in the second aquifer; although it is not so well-marked there.

Fig. 9
figure 9figure 9figure 9figure 9

Distribution maps based on the average concentrations and values of phosphate, sulfate, pH, Eh, DO, nitrate, iron and manganese in the first and second aquifers in the vicinity of the pond

Full size image

Groundwater in the first aquifer is neutral (pH 7.0–7.4); however, slightly alkaline (7.5–7.8) in the site of the former pond and at the well cluster No. ICE-113. In the second aquifer, pH is 7.2–7.3 in the site of the former pond, and it is 7.3 at the well cluster No. ICE-113.

The pH values do not show a noticeable anomaly, which suggests that the matter released from the pond did not induce an essential modification in the acid–base system. It is important since the formation of vivianite is highly pH-regulated (Liu et al. 2018). Accordingly, XRPD detected vivianite with higher degree of crystallization, which is characteristic for vivianite formed at about pH 7 (Liu et al. 2018). However, pH values of water in the vicinity of the well cluster No. ICE-113 and the pond are slightly increased, which suggests intensification of sulfate reduction. Nitrate concentrations are elevated in both aquifers, but regarding the first aquifer dissolved nitrate input comes from other sources, as well.

The concentration of dissolved HCO3− is particularly important since it fundamentally influences vivianite formation. As Table 3 shows at the well cluster No. ICE-113 HCO3− concentrations of the first and second aquifer are equal to background values; however, they are multiplied under the sewage pond.

In our opinion, the high orthophosphate content of the groundwater is the result of the decomposition of the biomass deposed in the late 1950s and the early 1960s, and this assumption is supported by the map of the dissolved orthophosphate distribution in the groundwater (Fig. 9). In this period, the amount of the processed and then deposited plant litter might be several thousand tons per year. The depth of the sewage pond is unknown; however, the increased (5–20 mg/dm3) orthophosphate concentration in the second aquifer suggests that there could be a direct communication between the aquifers.

Transportation of orthophosphate

The next point is whether the dissolved orthophosphate could filtrate from the pond to the site if the well cluster No. ICE-113 is under natural hydrogeological conditions characteristic for the study area. The upper part of the vivianite-bearing “basal clay” (which can be found from 4.0 to 9.0 m below the surface) can be regarded as clayey fine- and medium-grained silt, while its lower part is silt. The K filtration coefficient of the “basal clay” was calculated using the grain-size distribution curve; this method is widely accepted in hydrogeological-environmental geological practice; however, it should be carefully applied. Several mathematical formulae have been published for estimating filtration coefficient using grain-size distribution curves; however, these can be applied for sediments possessing a given distribution and sorting. We used Devlin’s Excel with a VBA code file (Devlin, 2015). According to the calculations, characteristic filtration coefficient values are 8.2 × 10–9–1.4 × 10–8 m/s and 1.0 × 10–8–1.8 × 10–8 m/s for the more clayey upper, and for the sandy and vivianite-bearing lower part of the “basal clay”, respectively. Therefore, the “basal clay” can be regarded as a leaky confining bed.

Unfortunately, site-specific data for the specific yield of “basal clay” is not known; however, according to Singhal and Gupta (2010) effective porosity (or specific yield which can be regarded as the same) for silt may range from 5 to 20%. Due to high uncertainties, a conservative approach (advection) was applied to predict the fate and transport processes of the dissolved orthophosphate. Considering the calculated horizontal hydraulic gradient of the first aquifer (0.004), the above-mentioned filtration coefficient, and the 5–20% effective porosity values characteristic for silts, we can use the formula

$$ v\, = \,\frac{{K{\text{d}}h}}{{n{\text{d}}l}}, $$
(1)

where v is the seepage velocity of the groundwater in the “basal clay” as a leaky confined bed; K is the hydraulic conductivity; n is the specific storage; and dh/dl is the hydraulic gradient. According to the calculation, during 50 years propagation of the groundwater could range from 3 to 22 m in the lower, silty part of the “basal clay”; considering that the well cluster No. ICE-113 traversing the vivianite-bearing layer is located 15 m of the margin of the former pond, it can be stated the dissolved orthophosphate could be advectively transported by groundwater from the former pond to the site of the drilling.

Origin of iron

Formation of vivianite requires proper quantity of iron in the pore water. In the first and the second aquifer, the concentration of the total dissolved iron is about 1 mg/dm3 in the background, while definitely increased beneath the sewage pond in the first aquifer (1.5–3.5 mg/dm3) and especially in the second aquifer (4–11 mg/dm3). Temporal change in dissolved iron in the underground water suggests intensification of iron reduction, which is not a simple facilitating but indispensable factor of vivianite formation. Considerable amount of reduced sulfur in the system may inhibit this process because it favors the formation of iron sulfides. Precipitation of vivianite is possible under a relatively narrow range of pH-Eh conditions (5–9 pH and from  + 200 to − 200 mV Eh) (Lemos et al. 2007; Dill and Techmer 2009); moreover, low S:Fe ratio also favors this process (Rothe et al. 2016). Depending HCO3− activity (logaHCO3 ≥3) siderite may also form at the expense of vivianite, quasi competing with it for the dissolved Fe2+ (Dill and Techmer 2009); however, XRPD analysis did not detect siderite in our samples. This experience can be explained by low kinetics of formation and growth of siderite (which is also characteristic for vivianite) (Postma 1981), and particularly by the fact that HCO3− concentration in the well cluster No. ICE-113 is almost equal to the background concentration. A considerable increase in HCO3− activity may favor formation of siderite at the expense of that of vivianite (Dill and Techmer 2009). In the surroundings of the well cluster No. ICE-113 the concentrations of HCO3− are favorable for the formation of vivianite, while toward the pond, because of multiplied HCO3− concentrations, formation of siderite can be expected.

As a source of reduced Fe, chlorite and micas should also be considered. On the altered crystal edges and surfaces exposing the octahedral sites occupied by Fe2+, the action of dissolved phosphate in basic pH may induce dissolution of cations and subsequent precipitation through crystallization of a stable product. In such a situation, the action of orthophosphate in basic solution is initiating the reaction on chlorite crystallites, supported by the BSE observations, that vivianite is mostly formed on the surface of chlorite rich aggregates.

Another geological factor may also contribute to vivianite formation. It is highly possible that the water level in the pond was considerably higher than the static water level in the first aquifer; therefore, mobile inorganic components, such as orthophosphate, radially spread from the pond. As Fig. 10 shows the upper surface of the "basal clay" can be dominantly found at 90.0–90.5 m a.s.l. and slopes to the south, however, here and there it is 1.0–1.5 m higher. This kind of elevation of the "basal clay" occurs at the well cluster ICE-113. East of the pond, however, the first aquifer is much thicker, and physical, chemical, and lithological conditions characteristic for this bed do not allow the formation of vivianite.

Fig. 10
figure 10

The topography of the top of the “basal clay” layer

Full size image

Conclusions

Vivianite formation in soils and clayey sediments requires several particular circumstances, such as proper pH and redox conditions, high dissolved PO43+ and Fe2+ as well as low HCO3− and HS− in pore water. These factors are basically influenced by the character of microbial activity, iron-hydroxides, and iron-oxyhydroxides, as well as sorption features of clay minerals. Based on the available geological data, the formation of vivianite in the study area is the result of the fixation of phosphate released by the decomposition of organic by-product material which had been deposed here for decades. Consequently, its mineralogical classification could be ambiguous. According to the recommended definition of the International Mineralogical Association (IMA) Commission on New Minerals and Mineral Names (CNMMN), a mineral is a normally crystalline element or chemical compound formed by the action of geological processes (Nickel 1995); moreover, anthropogenic substances should not be considered minerals even if they were formed by geological processes, although the borderline between natural and man-made (i.e. mineral or non-mineral) substances can be unclear in many cases (Nickel and Grice 1998). The studied vivianite seems to be a simple case in this respect: its crystals were formed of natural substances in natural geological medium by action of geological processes. On the other hand, however, high phosphate concentration at the site is due to human action, and also human intervention made the accelerated horizontal seepage possible; therefore, although vivianite formed by natural mineralization, it was induced by hidden human intervention. The present situation is one of those special cases, where anthropogenic mineral formation is revealing underground processes related to long-term industrial seepage; moreover, our results suggest that the gray zone between ‘natural’ and ‘anthropogenic’ minerals may be wider than it has been generally supposed.