CNTs/CNF-supported multi-active components as highly efficient bifunctional oxygen electrocatalysts and their applications in zinc-air batteries

  • Research Article
  • Published:
Nano Research Aims and scope Submit manuscript

Abstract

Rational construction of active components has been the biggest challenge in preparing efficient bifunctional oxygen electrocatalysts. Herein, electrospinning and chemical vapor deposition (CVD) were employed to embed active species including FeCo nanoparticles, MNx (M = Fe, Co), and FePx in porous and graphitized carbon nanotubes (CNTs)/carbon nanofiber (CNF). The as-prepared FeCo@CoNx@FePx/C exhibited a half-wave potential as high as 0.86 V in oxygen reduction reaction (ORR) and low oxygen evolution reaction (OER) overpotential of 368 mV at 10 mA·cm−2, which are superior to Pt/C (0.83 V) and IrO2 (375 mV) respectively. The assembled Zn-air battery (ZAB) showed a high energy efficiency (Edischarge/Echarge) of 65% at 20 mA·cm−2 and stabilized for 700 charge—discharge cycles. The spectroscopic and microscopic characterizations evidenced that the outstanding bifunctionality of the electrocatalyst can be ascribed to three main reasons: First, FeCo nanoparticles are rich in MOH/MOOH active sites for OER, and FePx/CNTs constructed with CVD also modulate electronic structure to improve electron transfer; second, both MNx in carbon matrix and FePx/CNTs are highly active towards ORR; third, the CNTs/CNF are highly porous and graphitized, which promotes mass transport and improves electrical conductivity and stability of the electrocatalysts. This work gives important implications on the design of bifunctional electrocatalysts.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Xia, Q.; Zhai, Y. J.; Zhao, L. L.; Wang, J.; Li, D. Y.; Zhang, L. L.; Zhang, J. T. Carbon-supported single-atom catalysts for advanced rechargeable metal-air batteries. Energy Mater. 2022, 2, 200015.

    CAS  Google Scholar 

  2. Pan, L.; Chen, D. F.; Pei, P. C.; Huang, S. W.; Ren, P.; Song, X. A novel structural design of air cathodes expanding three-phase reaction interfaces for zinc-air batteries. Appl. Energy 2021, 290, 116777.

    CAS  Google Scholar 

  3. Yin, Z. Y.; He, R.; Xue, H. B.; Chen, J. J.; Wang, Y.; Ye, X. X.; Xu, N. N.; Qiao, J. L.; Huang, H. T. A bimetallic-activated MnO2 self-assembly electrode with a dual heterojunction structure for high-performance rechargeable zinc-air batteries. Energy Mater. 2022, 2, 200021.

    CAS  Google Scholar 

  4. Shi, Q.; Liu, Q.; Ma, Y.; Fang, Z.; Liang, Z.; Shao, G.; Tang, B.; Yang, W. Y.; Qin, L.; Fang, X. S. High-performance trifunctional electrocatalysts based on FeCo/Co2P hybrid nanoparticles for zinc-air battery and self-powered overall water splitting. Adv. Energy Mater. 2020, 10, 1903854.

    CAS  Google Scholar 

  5. Jiao, L.; Li, J. K.; Richard, L. L.; Sun, Q.; Stracensky, T.; Liu, E. S.; Sougrati, M. T.; Zhao, Z. P.; Yang, F.; Zhong, S. C. et al. Chemical vapour deposition of Fe-N-C oxygen reduction catalysts with full utilization of dense Fe-N4 sites. Nat. Mater. 2021, 20, 1385–1391.

    CAS  Google Scholar 

  6. Balamurugan, J.; Nguyen, T. T.; Kim, N. H.; Kim, D. H.; Lee, J. H. Novel core-shell CuMo-oxynitride@N-doped graphene nanohybrid as multifunctional catalysts for rechargeable zinc-air batteries and water splitting. Nano Energy 2021, 85, 105987.

    CAS  Google Scholar 

  7. Wu, M. J.; Wei, Q. L.; Zhang, G. X.; Qiao, J. L.; Wu, M. X.; Zhang, J. H.; Gong, Q. J.; Sun, S. H. Fe/Co double hydroxide/oxide nanoparticles on N-doped CNTs as highly efficient electrocatalyst for rechargeable liquid and quasi-solid-state zinc-air batteries. Adv. Energy Mater. 2018, 8, 1801836.

    Google Scholar 

  8. Chen, D. F.; Pan, L.; Pei, P. C.; Song, X.; Ren, P.; Zhang, L. Cobalt-based oxygen electrocatalysts for zinc-air batteries: Recent progress, challenges, and perspectives. Nano Res. 2022, 15, 5038–5063.

    CAS  Google Scholar 

  9. Zhou, X. W.; Liu, X.; Zhang, J. H.; Zhang, C.; Yoo, S. J.; Kim, J. G.; Chu, X. Y.; Song, C.; Wang, P.; Zhao, Z. Z. et al. Highly-dispersed cobalt clusters decorated onto nitrogen-doped carbon nanotubes as multifunctional electrocatalysts for OER, HER and ORR. Carbon 2020, 166, 284–290.

    CAS  Google Scholar 

  10. Zhang, L.; Zhu, J. W.; Li, X.; Mu, S. C.; Verpoort, F.; Xue, J. M.; Kou, Z. K.; Wang, J. Nurturing the marriages of single atoms with atomic clusters and nanoparticles for better heterogeneous electrocatalysis. Interdiscip. Mater. 2022, 1, 51–87.

    Google Scholar 

  11. Fu, X. G.; Liu, Y. R.; Cao, X. P.; Jin, J. T.; Liu, Q.; Zhang, J. Y. FeCo-Nx embedded graphene as high performance catalysts for oxygen reduction reaction. Appl. Catal. B 2013, 130–131, 143–151.

    Google Scholar 

  12. Zhao, Y. X.; Lai, Q. X.; Wang, Y.; Zhu, J. J.; Liang, Y. Y. Interconnected hierarchically porous Fe, N-codoped carbon nanofibers as efficient oxygen reduction catalysts for Zn-air batteries. ACS Appl. Mater. Interfaces 2017, 9, 16178–16186.

    CAS  Google Scholar 

  13. Zhou, Q. X.; Hou, S. Y.; Cheng, Y. X.; Sun, R. X.; Shen, W. Y.; Tian, R.; Yang, J.; Pang, H.; Xu, L.; Huang, K. et al. Interfacial engineering Co and MnO within N, S co-doped carbon hierarchical branched superstructures toward high-efficiency electrocatalytic oxygen reduction for robust Zn-air batteries. Appl. Catal. B 2021, 295, 120281.

    CAS  Google Scholar 

  14. Xie, W. W.; Huang, J. H.; Huang, L. T.; Geng, S. P.; Song, S. Q.; Tsiakaras, P.; Wang, Y. Novel fluorine-doped cobalt molybdate nanosheets with enriched oxygen-vacancies for improved oxygen evolution reaction activity. Appl. Catal. B 2022, 303, 120871.

    CAS  Google Scholar 

  15. Xu, H.; Wang, D.; Yang, P. X.; Du, L.; Lu, X. Y.; Li, R. P.; Liu, L. L.; Zhang, J. Q.; An, M. Z. A hierarchically porous Fe-N-C synthesized by dual melt-salt-mediated template as advanced electrocatalyst for efficient oxygen reduction in zinc-air battery. Appl. Catal. B 2022, 305, 121040.

    CAS  Google Scholar 

  16. Lv, X. W.; Xu, W. S.; Tian, W. W.; Wang, H. Y.; Yuan, Z. Y. Activity promotion of core and shell in multifunctional core-shell Co2P@NC electrocatalyst by secondary metal doping for water electrolysis and Zn-air batteries. Small 2021, 17, 2101856.

    CAS  Google Scholar 

  17. Jin, H. H.; Zhou, H.; He, D. P.; Wang, Z. H.; Wu, Q. L.; Liang, Q. R.; Liu, S. L.; Mu, S. C. MOF-derived 3D Fe-N-S co-doped carbon matrix/nanotube nanocomposites with advanced oxygen reduction activity and stability in both acidic and alkaline media. Appl. Catal. B 2019, 250, 143–149.

    CAS  Google Scholar 

  18. Yang, X. K.; Yi, Q. F.; Sheng, K.; Wang, T. CoNi loaded C—N tubular nanocomposites as excellent cathodic catalysts of alkaline Zn-air batteries. Catal. Lett. 2020, 150, 2886–2899.

    CAS  Google Scholar 

  19. Wan, W. J.; Liu, X. J.; Li, H. Y.; Peng, X. Y.; Xi, D. S.; Luo, J. 3D carbon framework-supported CoNi nanoparticles as bifunctional oxygen electrocatalyst for rechargeable Zn-air batteries. Appl. Catal. B 2019, 240, 193–200.

    CAS  Google Scholar 

  20. Cui, J.; Leng, Y. M.; Xiang, Z. H. FeNi co-doped electrocatalyst synthesized via binary ligand strategy as a bifunctional catalyst for Zn-air flow battery. Chem. Eng. Sci. 2022, 247, 117038.

    CAS  Google Scholar 

  21. Shi, X. J.; He, B. B.; Zhao, L.; Gong, Y. S.; Wang, R.; Wang, H. W. FeS2-CoS2 incorporated into nitrogen-doped carbon nanofibers to boost oxygen electrocatalysis for durable rechargeable Zn-air batteries. J. Power Sources 2021, 482, 228955.

    CAS  Google Scholar 

  22. Zhang, C. L.; Liu, J. T.; Li, H.; Qin, L.; Cao, F. H.; Zhang, W. The controlled synthesis of Fe3C/Co/N-doped hierarchically structured carbon nanotubes for enhanced electrocatalysis. Appl. Catal. B 2020, 261, 118224.

    CAS  Google Scholar 

  23. Gao, L.; Chang, S. M.; Zhang, Z. Y. High-Quality CoFeP Nanocrystal/N, P dual-doped carbon composite as a novel bifunctional electrocatalyst for rechargeable Zn-air battery. ACS Appl. Mater. Interfaces 2021, 13, 22282–22291.

    CAS  Google Scholar 

  24. Zhang, X. L.; Yang, Z. X.; Lu, Z. S.; Wang, W. C. Bifunctional CoNx embedded graphene electrocatalysts for OER and ORR: A theoretical evaluation. Carbon 2018, 130, 112–119.

    CAS  Google Scholar 

  25. Zhang, Y. Y.; Sun, H. H.; Qiu, Y. F.; Ji, X. Y.; Ma, T. G.; Gao, F.; Ma, Z.; Zhang, B. X.; Hu, P. A. Multiwall carbon nanotube encapsulated Co grown on vertically oriented graphene modified carbon cloth as bifunctional electrocatalysts for solid-state Zn-air battery. Carbon 2019, 144, 370–381.

    CAS  Google Scholar 

  26. Li, R. Z.; Wang, D. S. Understanding the structure-performance relationship of active sites at atomic scale. Nano Res. 2022, 15, 6888–6923.

    CAS  Google Scholar 

  27. Ibraheem, S.; Li, X. T.; Shah, S. S. A.; Najam, T.; Yasin, G.; Iqbal, R.; Hussain, S.; Ding, W. Y.; Shahzad, F. Tellurium triggered formation of Te/Fe-NiOOH nanocubes as an efficient bifunctional electrocatalyst for overall water splitting. ACS Appl. Mater. Interfaces 2021, 13, 10972–10978.

    CAS  Google Scholar 

  28. Chen, D. F.; Pan, L.; Pei, P. C.; Huang, S. W.; Ren, P.; Song, X. Carbon-coated oxygen vacancies-rich Co3O4 nanoarrays grow on nickel foam as efficient bifunctional electrocatalysts for rechargeable zinc-air batteries. Energy 2021, 224, 120142.

    CAS  Google Scholar 

  29. Yan, L.; Xu, Z. Y.; Hu, W. K.; Ning, J. Q.; Zhong, Y. J.; Hu, Y. Formation of sandwiched leaf-like CNTs-Co/ZnCo2O4@NC-CNTs nanohybrids for high-power-density rechargeable Zn-air batteries. Nano Energy 2021, 82, 105710.

    CAS  Google Scholar 

  30. Shi, Q.; Liu, Q.; Zheng, Y. P.; Dong, Y. Q.; Wang, L.; Liu, H. T.; Yang, W. Y. Controllable construction of bifunctional CoxP@N,P-doped carbon electrocatalysts for rechargeable zinc-air batteries. Energy Environ. Mater. 2022, 5, 515–523.

    CAS  Google Scholar 

  31. Liu, Y. F.; Li, Y.; Wu, Q.; Su, Z.; Wang, B.; Chen, Y. F.; Wang, S. F. Hollow CoP/FeP4 heterostructural nanorods interwoven by CNT as a highly efficient electrocatalyst for oxygen evolution reactions. Nanomaterials 2021, 11, 1450.

    CAS  Google Scholar 

  32. Hu, Q.; Wang, Z. Y.; Huang, X. W.; Qin, Y. J.; Yang, H. P.; Ren, X. Z.; Zhang, Q. L.; Liu, J. H.; He, C. X. A unique space confined strategy to construct defective metal oxides within porous nanofibers for electrocatalysis. Energy Environ. Sci. 2020, 13, 5097–5103.

    CAS  Google Scholar 

  33. Wang, Y. Y.; Li, Z. G.; Zhang, P.; Pan, Y.; Zhang, Y.; Cai, Q.; Silva, S. R. P.; Liu, J.; Zhang, G. X.; Sun, X. M. et al. F. Flexible carbon nanofiber film with diatomic Fe-Co sites for efficient oxygen reduction and evolution reactions in wearable zinc-air batteries. Nano Energy 2021, 87, 106147.

    CAS  Google Scholar 

  34. Li, C. L.; Zhang, Z. J.; Wu, M. C.; Liu, R. FeCoNi ternary alloy embedded mesoporous carbon nanofiber: An efficient oxygen evolution catalyst for rechargeable zinc-air battery. Mater. Lett. 2019, 238, 138–142.

    CAS  Google Scholar 

  35. Yu, H.; Zhang, D. D.; Hou, H. L.; Ma, Y.; Fang, Z.; Lu, X. L.; Xu, S.; Hou, P.; Shao, G.; Yang, W. Y. et al. Embedded FeCo alloy nanoparticles in N-doped mesoporous carbon nanofibers as efficient bi-functional electrocatalysts for long-term rechargeable Zn-air batteries. Appl. Surf. Sci. 2022, 571, 151292.

    CAS  Google Scholar 

  36. Yazici, M. S.; Azder, M. A.; Salihoglu, O. CVD grown graphene as catalyst for acid electrolytes. Int. J. Hydrogen Energy 2018, 43, 10710–10716.

    CAS  Google Scholar 

  37. Konar, R.; Das, S.; Teblum, E.; Modak, A.; Perelshtein, I.; Richter, J. J.; Schechter, A.; Nessim, G. D. Facile and scalable ambient pressure chemical vapor deposition-assisted synthesis of layered silver selenide (β-Ag2Se) on Ag foil as a possible oxygen reduction catalyst in alkaline medium. Electrochim. Acta 2021, 370, 137709.

    CAS  Google Scholar 

  38. Wu, Y. C.; Wang, Y. J.; Wang, Z. W.; Li, X. T. Highly dispersed CoP on three-dimensional ordered mesoporous FeP for efficient electrocatalytic hydrogen production. J. Mater. Chem. A. 2021, 9, 23574–23581.

    CAS  Google Scholar 

  39. Chen, S. H.; Huang, Y. Q.; Li, M.; Sun, P. P.; Lv, X. W.; Li, B.; Fang, L.; Sun, X. H. MnOx anchored on N and O Co-doped carbon nanotubes encapsulated with FeCo alloy as highly efficient bifunctional electrocatalyst for rechargeable zinc-air batteries. J. Electroanal. Chem. 2021, 895, 115513.

    CAS  Google Scholar 

  40. Wang, Z.; Ang, J. M.; Zhang, B. W.; Zhang, Y. F.; Ma, X. Y. D.; Yan, T.; Liu, J.; Che, B. Y.; Huang, Y. Z.; Lu, X. H. FeCo/FeCoNi/N-doped carbon nanotubes grafted polyhedron-derived hybrid fibers as bifunctional oxygen electrocatalysts for durable rechargeable zinc-air battery. Appl. Catal. B 2019, 254, 26–36.

    CAS  Google Scholar 

  41. Yang, Z. K.; Zhao, C. M.; Qu, Y. T.; Zhou, H.; Zhou, F. Y.; Wang, J.; Wu, Y. E.; Li, Y. D. Trifunctional self-supporting cobalt-embedded carbon nanotube films for ORR, OER, and HER triggered by solid diffusion from bulk metal. Adv. Mater. 2019, 31, 1808043.

    Google Scholar 

  42. Yang, X. D.; Zheng, Y. P.; Yang, J.; Shi, W.; Zhong, J. H.; Zhang, C. K.; Zhang, X.; Hong, Y. H.; Peng, X. X.; Zhou, Z. Y. et al. Modeling Fe/N/C catalysts in monolayer graphene. ACS Catal. 2017, 7, 139–145.

    CAS  Google Scholar 

  43. Liang, Z. Z.; Kong, N. N.; Yang, C. X.; Zhang, W.; Zheng, H. Q.; Lin, H. P.; Cao, R. Highly curved nanostructure-coated Co, N-doped carbon materials for oxygen electrocatalysis. Angew. Chem., Int. Ed. 2021, 60, 12759–12764.

    CAS  Google Scholar 

  44. Yu, N. F.; Chen, H.; Kuang, J. B.; Bao, K. L.; Yan, W.; Ye, J. L.; Yang, Z. T.; Huang, Q. H.; Wu, Y. P.; Sun, S. G. Efficient oxygen electrocatalysts with highly-exposed Co-N4 active sites on N-doped graphene-like hierarchically porous carbon nanosheets enhancing the performance of rechargeable Zn-air batteries. Nano Res. 2022, 15, 7209–7219.

    CAS  Google Scholar 

  45. Tang, C.; Wang, B.; Wang, H. F.; Zhang, Q. Defect engineering toward atomic Co-Nx-C in hierarchical graphene for rechargeable flexible solid Zn-air batteries. Adv. Mater. 2017, 29, 1703185.

    Google Scholar 

  46. Han, M. N.; Shi, M. J.; Wang, J.; Zhang, M. L.; Yan, C.; Jiang, J. T.; Guo, S. H.; Sun, Z. Y.; Guo, Z. H. Efficient bifunctional Co/N dual-doped carbon electrocatalysts for oxygen reduction and evolution reaction. Carbon 2019, 153, 575–584.

    CAS  Google Scholar 

  47. Zhang, J. T.; Zhang, T.; Ma, J.; Wang, Z.; Liu, J. H.; Gong, X. Z. ORR and OER of Co-N codoped carbon-based electrocatalysts enhanced by boundary layer oxygen molecules transfer. Carbon 2021, 172, 556–568.

    CAS  Google Scholar 

  48. Kim, N. I.; Sa, Y. J.; Yoo, T. S.; Choi, S. R.; Afzal, R. A.; Choi, T.; Seo, Y. S.; Lee, K. S.; Hwang, J. Y.; Choi, W. S. et al. Oxygen-deficient triple perovskites as highly active and durable bifunctional electrocatalysts for oxygen electrode reactions. Sci Adv. 2018, 4, eaap9360.

    Google Scholar 

  49. Li, M. X.; Zhu, Y.; Wang, H. Y.; Wang, C.; Pinna, N.; Lu, X. F. Ni strongly coupled with Mo2C encapsulated in nitrogen-doped carbon nanofibers as robust bifunctional catalyst for overall water splitting. Adv. Energy Mater. 2019, 9, 1803185.

    Google Scholar 

  50. Cao, R. G.; Thapa, R.; Kim, H.; Xu, X. D.; Gyu Kim, M.; Li, Q.; Park, N.; Liu, M. L.; Cho, J. Promotion of oxygen reduction by a bio-inspired tethered iron phthalocyanine carbon nanotube-based catalyst. Nat. Commun. 2013, 4, 2076.

    Google Scholar 

  51. Li, H. X.; Wen, Y. L.; Jiang, M.; Yao, Y.; Zhou, H. H.; Huang, Z. Y.; Li, J. W.; Jiao, S. Q.; Kuang, Y. F.; Luo, S. L. Understanding of neighboring Fe-N4-C and Co-N4-C dual active centers for oxygen reduction reaction. Adv. Funct. Mater. 2021, 31, 2011289.

    CAS  Google Scholar 

  52. Zhou, K. L.; Wang, Z. L.; Han, C. B.; Ke, X. X.; Wang, C. H.; Jin, Y. H.; Zhang, Q. Q.; Liu, J. B.; Wang, H.; Yan, H. Platinum single-atom catalyst coupled with transition metal/metal oxide heterostructure for accelerating alkaline hydrogen evolution reaction. Nat. Commun. 2021, 12, 3783.

    CAS  Google Scholar 

  53. Li, J. J.; Jiang, Y. F.; Wang, Q.; Xu, C. Q.; Wu, D. J.; Banis, M. N.; Adair, K. R.; Doyle-Davis, K.; Meira, D. M.; Finfrock, Y. Z. et al. A general strategy for preparing pyrrolic-N4 type single-atom catalysts via pre-located isolated atoms. Nat. Commun. 2021, 12, 6806.

    CAS  Google Scholar 

  54. Fei, H. L.; Dong, J. C.; Arellano-Jiménez, M. J.; Ye, G. L.; Dong Kim, N.; Samuel, E. L. G.; Peng, Z. W.; Zhu, Z.; Qin, F.; Bao, J. M. et al. Atomic cobalt on nitrogen-doped graphene for hydrogen generation. Nat. Commun. 2015, 6, 8668.

    CAS  Google Scholar 

  55. Tiwari, J. N.; Sultan, S.; Myung, C. W.; Yoon, T.; Li, N. N.; Ha, M. R.; Harzandi, A. M.; Park, H. J.; Kim, D. Y.; Chandrasekaran, S. S. et al. Multicomponent electrocatalyst with ultralow Pt loading and high hydrogen evolution activity. Nat. Energy 2018, 3, 773–782.

    CAS  Google Scholar 

  56. Yan, J. H.; Wang, Y.; Zhang, Y. Y.; Xia, S. H.; Yu, J. Y.; Ding, B. Direct magnetic reinforcement of electrocatalytic ORR/OER with electromagnetic induction of magnetic catalysts. Adv. Mater. 2021, 33, 2007525.

    CAS  Google Scholar 

  57. Wang, T. T.; Liu, M.; Chaemchuen, S.; Wang, J. C.; Yuan, Y.; Chen, C.; Qiao, A.; Verpoort, F.; Kou, Z. K. Constructing a stable cobalt-nitrogen-carbon air cathode from coordinatively unsaturated zeolitic-imidazole frameworks for rechargeable zinc-air batteries. Nano Res. 2022, 15, 5895–5901.

    CAS  Google Scholar 

  58. Yang, G. G.; Zhu, J. W.; Yuan, P. F.; Hu, Y. F.; Qu, G.; Lu, B. A.; Xue, X. Y.; Yin, H. B.; Cheng, W. Z.; Cheng, J. Q. et al. Regulating Fe-spin state by atomically dispersed Mn-N in Fe-N-C catalysts with high oxygen reduction activity. Nat. Commun. 2021, 12, 1734.

    CAS  Google Scholar 

Download references

Acknowledgements

The authors acknowledge the grants from the National Natural Science Foundation of China (No. 22004085) and Regional Joint Fund of Guangdong Province (No. 2019A1515111054). The authors also thank the Instrumental Analysis Center of Shenzhen University for the scanning electron microscopy (SEM) and TEM characterizations. The authors would like to thank Yaping Li for Shiyanjia Lab (https://www.shiyanjia.com) for the XAS analysis.

Author information

Authors and Affiliations

  1. Institute for Advanced Study, Shenzhen University, Shenzhen, 518060, China

    Weiyuan Ding, Ali Saad, Yuchen Wu, Zhiwei Wang & Xiuting Li

  2. College of Physics and Optoelectronic Engineering, Shenzhen University, Shenzhen, 518060, China

    Weiyuan Ding, Yuchen Wu & Zhiwei Wang

Authors
  1. Weiyuan Ding
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Ali Saad
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Yuchen Wu
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Zhiwei Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Xiuting Li
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Xiuting Li.

Electronic Supplementary Material

12274_2022_5261_MOESM1_ESM.pdf

CNTs/CNF-supported multi-active components as highly efficient bifunctional oxygen electrocatalysts and their applications in zinc-air batteries

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Ding, W., Saad, A., Wu, Y. et al. CNTs/CNF-supported multi-active components as highly efficient bifunctional oxygen electrocatalysts and their applications in zinc-air batteries. Nano Res. 16, 4793–4802 (2023). https://doi.org/10.1007/s12274-022-5261-y

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12274-022-5261-y

Keywords

Search

Navigation