Abstract
With the rapid development of white LEDs, the research of new and efficient white light emitting materials has attracted increasing attention. Zero dimensional (0D) organic–inorganic hybrid metal halide perovskites with superior luminescent property are promising candidates for LED application, due to their abundant and tailorable structure. Herein, [(CH3)3S]2SnCl6·H2O is synthesized as a host for dopant ions Bi3+ and Sb3+. The Sb3+ doped, or Bi3+/Sb3+ co-doped, [(CH3)3S]2SnCl6·H2O has a tunable optical emission spectrum by means of varying dopant ratio and excitation wavelength. As a result, we can achieve single-phase materials suitable for emission ranging from cold white light to warm white light. The intrinsic mechanism is examined in this work, to clarify the dopant effect on the optical properties. The high stability of title crystalline material, against water, oxygen and heat, makes it promising for further application.
Graphical Abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Recently, solid-state lighting technology has experienced rapid development, in fields such as inorganic light emitting diodes (LEDs), organic light emitting diodes (OLEDs), polymer light emitting diodes (PLEDs) [1,2,3]. LEDs are more efficient and energy-saving than traditional lighting source [4] so that white LED has already largely replaced traditional lighting equipment (including incandescent lamps and fluorescent lamps). According to the US Department of Energy’s Solid-State Lighting report, electricity consumption for lighting is forecast to decrease by 25% between 2016 and 2035 [5].
The excellent optoelectronic properties of metal halide perovskites (MHPs) make them have potential applications in solar cells [6,7,8] and LEDs [9,10,11]. MHPs have different structural dimensionality ranging from zero-dimensional (0D) to three-dimensional (3D) [12,13,14,15,16,17]. The 0D metal halide has a soft lattice and a large Huang-Rhys factor (S), which is conducive to electron–phonon coupling [18, 19]. Thus, 0D metal halides have a stronger ability to form self-trapped excitons (STEs) than 3D ones do. The STEs have the potential to result in a broad emission with a large Stokes shift, with negligible self-absorption [18]. A2NX6 (A is a monovalent organic/inorganic cation, N is a tetravalent metal ion, and X is a halide ion) is a typical kind of 0D vacancy ordered MHP, exhibiting fruitful structures and good tolerance for guest ions [20,21,22]. For example, Cs2SnCl6 with excellent high stability has attracted considerable research attention. Various guest ions can be doped into Cs2SnCl6 leading to a distinctive performance. Bi3+, Te4+, and Sb3+ guest ions doped in Cs2SnCl6 show blue, yellow and red–orange light emission, respectively [23,24,25,26,27,28]. Through color addition, white light emission can be obtained by co-doping of Bi3+ and Te4+ ions [28, 29]. Based on the blue emission from the defect of Cs2SnCl6 structure, Ce3+ doped into Cs2SnCl6 induces an enhanced blue emission [30], while La3+ doped into Cs2SnCl6 achieves complementary white light [31]. Similar luminescence tuning by guest ions has also been reported in (NH4)2SnCl6 [32, 33].
In addition to the inorganic cation in A2SnX6 systems, organic cations have the potential to generate rich crystal structures due to the tailorable structure of organic cations. For example, (C6N2H16Cl)2SnCl6 (C6N2H16Cl = 2,6-dimethylpiperazine chloride) exhibits blue emission from STEs [34], while (4-APEA)2SnBr6 (4-APEA = 2-(4-aminophenyl) ethylammonium) provides yellow emission [35]. Sb3+ doped (C10H16N2)SnCl6 (C10H16N2 = 1-phenylpiperazine) induces ultra-broadband emission (400–900 nm) with 77% photoluminescence quantum yield (PLQY) [36]. However, most of the organic cation in A2SnX6 is protonated. The aprotic cation study is still in its infancy. To maintain the 216-type highly symmetric perovskite structure, in this work we introduce [(CH3)3S]+ into the A2SnX6 crystal structure. Compared with protonated organic cations, sulfonium cations have several advantages including [37]: (1) the characteristic of proton inertness, so that they do not undergo dehydrogenation reactions initiated by unstable free radicals or bases; (2) the large atomic size of S results in it combining closely with inorganic halide anions, resulting in an improved stability; (3) the use of aprotic sulfonium cation increases the moisture resistance of the perovskite structure. The study of diverse organic molecular structures can help to identify an organic cation that balances device performance and stability.
In this work, the organic–inorganic hybrid tin-based perovskite SSC (SSC = [(CH3)3S]2SnCl6·H2O) was synthesized. Bi3+ and Sb3+ ions were doped into SSC to tune the photoluminescence (PL), resulting in single-phase white light crystals Sb3+ doped [(CH3)3S]2SnCl6·H2O (Sb3+@SSC) and Bi3+/Sb3+ co-doped [(CH3)3S]2SnCl6·H2O (Bi3+/Sb3+@SSC). Their emission spectra are excitation-dependent. Thus, a series of high-quality white light emitting crystals with controllable color temperature can be obtained by adjusting the excitation wavelength. Compared with Sb3+@SSC, an enhanced blue light component, and a longer wavelength excitation (384 nm) for white light emission, can be achieved from Bi3+ in Bi3+/Sb3+@SSC. The title crystals have good acid resistance, water resistance and oxygen resistance, providing application potential for white light emitting diodes (WLEDs).
2 Results and discussion
SSC with/without dopant ions was synthesized by a hydrothermal method (The details can be found in Supporting Information). As shown in Fig. 1a, Sn is coordinated with six Cl forming an isolated [SnCl6]2−. The large organic cation [(CH3)3S]+ and H2O are located in the vacancy among the [SnCl6]2−, leading to a vacancy-ordered 0D MHPs SSC. The elemental analysis could confirm the existence of H2O as shown in Table S1. The crystal belongs to the Fm-3m space group with a unit cell length of 12.43 Å. Sb3+ can be easily doped into SSC structure. The Sb3+ dopant concentrations was tested by inductively coupled plasma atomic emission spectroscopy (ICP-OES), and the molar ratio of Sb/(Sn + Sb) was used to represent the actual dopant content inside the crystal structure. Under the feeding dopant concentrations of 0.002, 0.010, 0.018, 0.026, and 0.030 mol/L, the corresponding Sb3+ molar concentrations inside crystals was 0.019%, 0.12%, 0.25%, 0.31%, and 0.38%, respectively. As shown in Figs. 1b and S1, the good agreement between the experimental and simulated powder X-ray diffraction (PXRD) confirms the pure crystalline phase of title crystals. As shown in Fig. 1c, the Fourier transform infrared spectra (FTIR) of Sb3+@SSC is consistent with that of (CH3)3SCl verifying the organic component in the crystal structure. The characteristic peaks for C, S, Cl, Sn, and Sb elements could be found in the full X-ray photoelectron spectroscopy (XPS) spectrum of Sb3+@SSC as shown in Fig. S2. The fine XPS spectra of Sb and Sn in Sb3+@SSC are shown in Fig. 1d. The peaks located at 539.13 and 530.31 eV are in accordance with 3d3/2 and 3d5/2 of Sb3+, respectively, while those at 495.66 and 487.21 eV are contributed by 3d3/2 and 3d5/2 of Sn4+, respectively [24, 32, 38]. Thus, the elements and valence in Sb3+@SSC are well confirmed.
The optical properties of Sb3+@SSC are studied hereafter. Figure 2a is the UV–vis absorption spectra of xSb3+@SSC (x = 0, 0.019%, 0.12%, 0.25%, 0.31%, and 0.38%). Figure 2b shows the UV–vis absorption (black line), photoluminescence excitation (PLE, yellow and green line), photoluminescence emission (PL, purple line) spectra of 0.31% Sb3+@SSC. The absorption peak around 290 nm arises from the host SSC [39]. Along with the increasing Sb3+ dopant, an additional peak around 340 nm emerges and rises due to the absorption of Sb3+ [18, 40]. This absorption peak induced by Sb3+ dopant can also be found in the PLE spectra as shown in Fig. 2b. The PL of pristine SSC is negligible. After Sb3+ doping, SSC can induce a broad emission with two peaks at 490 nm (named as S) and 660 nm (named as T) under 318 nm excitation light source. The optimal excitation wavelength at 490 nm is 318 nm (The yellow curve in Fig. 2b), while the optimal excitation wavelength at 660 nm is 334 nm (The green curve in Fig. 2b). As a result, Sb3+@SSC shows an excitation-dependent PL (Fig. 2c). When the excitation wavelength changes from 300 to 370 nm, the intensity ratio between S peak and T peak is principally decreased, exhibiting different PL color as shown in Figs. 2e and S3. The PLE spectra with emission wavelength from 490 to 622 nm show different shapes and features (Fig. 2d), suggesting that the broad emission composed of two PL peaks might originate from the relaxation of different excited states. As is the case for Sb3+ doped Cs2SnCl6 at 80 K, the emission peak at 490 nm is derived from 1P1 to 1S0, and the emission peak at 660 nm is derived from 3P1 to 1S0 [24]. The crystal emission close to the standard white light is obtained under the excitation light source of 340 nm (Commission Internationale de l´Eclairage, CIE = 0.37, 0.31) with color rendering index (CRI) 84. The color coordinates, correlated color temperature (CCT) and CRI of white light crystals obtained by different excitation light sources are shown in Table S2.
To understand the PL of Sb3+@SSC, the PL lifetimes for different peaks are measured as shown in Fig. 3a. The PL lifetime of the 490 nm peak is about 14.52 ns, while that of 660 nm peak is about 19.59 μs. The fitting parameters for PL lifetime are shown in Table S3. Thus, the singlet emission (1P1–1S0) and triplet emission (3P1–1S0) of Sb3+ in SSC crystal should give rise to the 490 and 660 nm peaks, respectively [41]. The temperature-dependent PL also takes place (Fig. 3b). When the temperature increases, the intensity of the 660 nm peak reduces rapidly, while the intensity of 490 nm peak enhances a little and then decreases. Two factors can be expected to affect the two peaks’ intensities at different temperatures. One is the electron–phonon coupling and the other is the thermal activated energy transfer between the singlet and triplet states. It seems that the electron–phonon coupling is dominant for the T peak, resulting in the decrease of the peak intensity. However, the energy transfer from the triplet state to singlet state (i.e., reverse intersystem crossing) might play a critical role for S peaks, leading to the increase of the peak intensity initially. The intensity of the T peak at different temperatures is fitted by Arrhenius equation (Eq. (1)), as shown in Fig. 3c.
where I0 is the initial luminescence intensity emitted at 660 nm at low temperature (80 K), K is the Boltzmann constant, a is the pre-exponential factor, and EA is the activation energy of the luminescence peak. The EA of 660 nm emission calculated by the above formula is 265.17 meV; this value is similar to that in our group’s previous work on Sb3+ doped [(CH3)3N]2SnCl6 (288.13 meV) [38].
As shown in Fig. 3d, the PLQY of Sb3+ at different doping concentrations is tested. As further shown in Fig. S4, when the actual doping concentrations with Sb3+ are 0.019%, 0.12%, 0.25%, 0.31%, and 0.38%, the corresponding PLQY values are 15.5%, 51.8%, 61.5%, 75%, and 61.7%, respectively. When Sb3+ concentration ranges from 0.019% to 0.31%, the PLQY will be enhanced with the increasing Sb3+ content, reaching the maximum value of 75% at 0.31% dopant concentration. Subsequently, increase of Sb3+ doping content leads to the decrease of PLQY due to the concentration quenching effect [42].
The density functional theory (DFT) calculation of SSC is shown in Fig. 4a–c. The highest occupied molecular orbital (HOMO) is mainly composed of Cl 3p with a small contribution from organic cation, while the lowest unoccupied molecular orbital (LUMO) is mainly composed of Cl 3p and Sn 5s. After Sb3+ doping, LUMO remains Cl 3p and Sn 5s, while Sb 5s and Cl 3p have obvious contribution to HOMO (Fig. 4d–f). The Cl atom exhibits spatial overlap on HOMO and LUMO in the Sb3+@SSC, which may result in a large energy separation between the lowest excited triplet state and the lowest excited singlet state [21, 43, 44]. The energy difference between singlet emission and triplet emission of Sb3+@SSC is 0.57 eV, comparable with that of Sb3+doped [(CH3)4N]2SnCl6, suggesting the large energy separation between the lowest excited triplet state and the lowest excited singlet state [38]. Thus, not all the electrons in the singlet state transfer into the triplet state, due to the small spin–orbit coupling (SOC). There are still some electrons undergoing radiative transition from the singlet energy level resulting in a spectrum with singlet–triplet dual emission peaks for Sb3+@SSC. The calculated bandgaps and experimental values of SSC and Sb3+@SSC are shown in Figs. S5 and S6. Due to the limitation of the generalized gradient approximation, the calculated bandgaps are smaller than the experimental values [45, 46].
In addition to Sb3+ doping, Bi3+ is doped into SSC to obtain blue-emitting crystals. This is consistent with previous literatures about Bi3+ doped Cs2HfCl6 and Bi3+ doped Cs2ZrCl6 [47, 48]. The UV-vis absorption spectrum of Bi3+ doped [(CH3)3S]2SnCl6·H2O (Bi3+@SSC) is shown in Fig. 5a. After Bi3+ doping, an exciton peak appears at about 340 nm arising from the absorption of Bi3+ [40]. As shown in Fig. 5b and c, the blue emission peak (474 nm) of Bi3+@SSC is obtained under the 384 nm excitation with the PL lifetime of 30.12 ns. The blue light emission may be related to the mixing of the sp excited state of Bi3+ [40, 49].
As shown in Figs. S7 and S8, the introduction of Bi3+ does not change the structure of the SSC crystal. When Bi3+ is co-doped into Sb3+@SSC, the PL of Bi3+/Sb3+@SSC can be tuned efficiently by different Bi3+ concentrations. As shown in Fig. 5d, Bi3+/Sb3+@SSC has an obvious absorption peak at 340 nm, most of which is contributed by Bi3+. With the increase of Bi3+ ion concentration, the intensity of the absorption peak at 340 nm is increased. The emission peak of Bi3+@SSC is 474 nm with optimal excitation 384 nm and the S peak of Sb3+@SSC is at 490 nm with optimal excitation 318 nm. Thus, under different excitation wavelengths, ranging from 310 to 375 nm, as shown in Fig. 5e, the short-wavelength peak of co-doped sample is blue-shifted (i.e., from 490 to 474 nm), while the long-wavelength peaks (660 nm) are almost motionless. The doping with Bi3+ causes the white light emission of co-doped crystal to be excited at a longer wavelength (384 nm) compared with the 318 nm for Sb3+@SSC. The fluorescence emission spectra of xBi3+/0.31% Sb3+@SSC (x is the feeding concentration for Bi3+, including 0.006, 0.014, 0.022, 0.030, and 0.036 mol/L) are shown in Fig. 5f. The fluorescence emission peak intensity at 474 nm is significantly enhanced with the increased Bi3+ concentration. The corresponding CIE, CCT, CRI and PLQY of the co-doped samples are listed in Table S4 and Fig. S9. Doping concentration of 0.006 mol/L Bi3+/0.31% Sb3+@SSC has the highest PLQY value of 29.6% under 330 nm excitation.
Organic sulfonium cations have advantages of good humidity resistance [37, 50]. Figure 6a and b are the fluorescence stability tests of Sb3+@SSC in air. After 7 days and after 140 days in air, the fluorescence intensity does not change significantly. In addition, Sb3+@SSC immersed in water and aqua regia for 72 h. The PXRD after the experiment confirmed that Sb3+@SSC did not undergo phase transition in water or in aqua regia, as shown in Fig. 6b. The corresponding images for doped crystals soaked in water are shown in Fig. 6f. The samples can still maintain good luminescence properties after soaking in water. The thermal stability of single doped and co-doped samples is characterized by a thermogravimetric curve. As shown in Fig. 6c–e, the weight loss starts for pristine sample at 91 °C, while those for Sb3+ doped and Bi3+/Sb3+ co-doped samples it starts at 192 °C and 164 °C, respectively. The stability after doping is significantly improved compared with the undoped stability. The good stability provides a basis for the further application of such luminescent materials.
We assembled 0.31% Sb3+@SSC samples into LED devices. The electroluminescence spectrum of this device under 348 nm chip excitation is shown in Fig. S10. The emission spectrum covers a wide emission in the range of 380 to 760 nm. Under 300 mA current and 3 V voltage, the luminous efficiency is 4.39 lm/W. The mismatch between the ultraviolet LED chip and the optimal excitation wavelength leads to the low device efficiency.
3 Conclusion
A new 0D SSC is synthesized. Bi3+ and Sb3+ are co-doped as dopants to tune the PL of the title crystals. As a result, Sb3+@SSC exhibits dual singlet/triplet emission at 490 and 660 nm, and the overall optical spectrum has a strong dependence on the excitation wavelength. Under excitation at 340 nm, the emission CIE (0.37, 0.31) is closest to the standard white light (CIE = 0.31, 0.31), and the CRI reaches 84 with 75% PLQY. The high energy barrier between singlet and triplet states might be the origin of dual emission in Sb3+@SSC at room temperature. The co-doping with Bi3+ increases the blue band emission in the white light. The white light color can be adjusted by changing the doping concentration ratio of Bi3+ and Sb3+. The excitation wavelength for white light can extend to 384 nm, which is convenient for WLED application. As a highly compatible host, SSC not only allows the doping with multiple ions, but also has enhanced stability, and provides a basis for further application.
Availability of data and materials
The data that support the findings of this study are available from the corresponding author, upon reasonable request.
References
Shang, J., Cong, C., Wang, Z., Peimyoo, N., Wu, L., Zou, C., Chen, Y., Chin, X.Y., Wang, J., Soci, C., Huang, W., Yu, T.: Room-temperature 2D semiconductor activated vertical-cavity surface-emitting lasers. Nat. Commun. 8(1), 543 (2017)
Kitai, A.: Materials for solid state lighting and displays. John Wiley & Sons, Ltd (2016)
Humphreys, C.J.: Solid-state lighting. MRS Bull. 33(4), 459–470 (2008)
Tsao, J.Y., Saunders, H.D., Creighton, J.R., Coltrin, M.E., Simmons, J.A.: Solid-state lighting: an energy-economics perspective. J. Phys. D Appl. Phys. 43(35), 354001 (2010)
Guner, T., Demir, M.: A review on halide perovskites as color conversion layers in white light emitting diode applications. Phys. Status Solidi A Appl. Mater. Sci. 215(13), 1800120 (2018)
Sun, N., Gao, W., Dong, H., Liu, Y., Liu, X., Wu, Z., Song, L., Ran, C., Chen, Y.: Architecture of p-i-n Sn-based perovskite solar cells: characteristics, advances, and perspectives. ACS Energy Lett. 6(8), 2863–2875 (2021)
Lim, E.L., Hagfeldt, A., Bi, D.: Toward highly efficient and stable Sn2+ and mixed Pb2+/Sn2+ based halide perovskite solar cells through device engineering. Energy Environ. Sci. 14(6), 3256–3300 (2021)
Ke, W., Stoumpos, C.C., Kanatzidis, M.G.: “Unleaded” perovskites: status quo and future prospects of tin-based perovskite solar cells. Adv. Mater. 31(47), e1803230 (2019)
Zhang, K., Zhu, N., Zhang, M., Wang, L., Xing, J.: Opportunities and challenges in perovskite LED commercialization. J. Mater. Chem. C Mater. Opt. Electron. Devices 9(11), 3795–3799 (2021)
Pacchioni, G.: Highly efficient perovskite LEDs. Nat. Rev. Mater. 6(2), 108 (2021)
Kim, J.S., Heo, J.M., Park, G.S., Woo, S.J., Cho, C., Yun, H.J., Kim, D.H., Park, J., Lee, S.C., Park, S.H., Yoon, E., Greenham, N.C., Lee, T.W.: Ultra-bright, efficient and stable perovskite light-emitting diodes. Nature 611(7937), 688–694 (2022)
Lin, Y.P., Hu, S., Xia, B., Fan, K.Q., Gong, L.K., Kong, J.T., Huang, X.Y., Xiao, Z., Du, K.Z.: Material design and optoelectronic properties of three-dimensional quadruple perovskite halides. J. Phys. Chem. Lett. 10(17), 5219–5225 (2019)
Lin, Y.P., Xia, B., Hu, S., Zhong, Y., Huang, Y.E., Zhang, Z.Z., Wu, N., Wu, Y.W., Wu, X.H., Huang, X.Y., Xiao, Z., Du, K.Z.: Reversible release and fixation of bromine in vacancy-ordered bromide perovskites. Energy Environ. Mater. 3(4), 535–540 (2020)
Lin, Y.P., Xia, B., Hu, S., Liu, Z., Huang, X.Y., Xiao, Z., Du, K.Z.: Vacancy-ordered chloride perovskites for reversible release–storage of chlorine. J. Mater. Sci. 57(39), 18266–18276 (2022)
Wu, Y.N., Zhu, L.L., Zhao, Y., Xu, S.Y., Huang, P.W., Chen, B.C., Huang, Z.Y., Huang, X.Y., Chen, J., Du, K.Z.: Mussel-inspired two-dimensional halide perovskite facilitated dopamine polymerization and self-adhesive photoelectric coating. Inorg. Chem. 62(2), 1062–1068 (2023)
Zhao, Y., Zhong, H.Y., Li, L., Lin, W.L., Huang, Y.E., Su, B.Y., Wu, X.H., Huang, X.Y., Du, K.Z.: Crystalline intermarriage of hybrid organic–inorganic halide perovskite and epoxide: enhanced stability and modified optical properties. ACS Appl. Energy Mater. 4(12), 13550–13555 (2021)
Chen, Y., Gao, C., Yang, T., Li, W., Xu, H., Sun, Z.: Research advances of ferroelectric semiconductors of 2D hybrid perovskites toward photoelectronic applications. Chin. J. Struct. Chem. 41, 2204001–2204011 (2022)
Jing, Y., Liu, Y., Li, M., Xia, Z.: Photoluminescence of singlet/triplet self-trapped excitons in Sb3+-based metal halides. Adv. Opt. Mater. 9(8), 2002213 (2021)
McCall, K.M., Morad, V., Benin, B.M., Kovalenko, M.V.: Efficient lone-pair-driven luminescence: structure-property relationships in emissive 5s2 metal halides. ACS Mater. Lett. 2(9), 1218–1232 (2020)
Liu, S., Yang, B., Chen, J., Zheng, D., Tang, Z., Deng, W., Han, K.: Colloidal synthesis and tunable multicolor emission of vacancy-ordered Cs2HfCl6 perovskite nanocrystals. Laser Photonics Rev. 16(2), 2100439 (2022)
Liu, S., Yang, B., Chen, J., Wei, D., Zheng, D., Kong, Q., Deng, W., Han, K.: Efficient thermally activated delayed fluorescence from all-inorganic cesium zirconium halide perovskite nanocrystals. Angew. Chem. Int. Ed. Engl. 59(49), 21925–21929 (2020)
Abfalterer, A., Shamsi, J., Kubicki, D., Savory, C., Xiao, J., Divitini, G., Li, W., Macpherson, S., Gałkowski, K., MacManus-Driscoll, J., Scanlon, D., Stranks, S.: Colloidal synthesis and optical properties of perovskite-inspired cesium zirconium halide nanocrystals. ACS Mater. Lett. 2, 1644 (2020)
Arfin, H., Kshirsagar, A., Kaur, J., Mondal, B., Xia, Z., Chakraborty, S., Nag, A.: ns2 electron (Bi3+and Sb3+) doping in lead-free metal halide perovskite derivatives. Chem. Mater. 32(24), 10255 (2020)
Jing, Y., Liu, Y., Zhao, J., Xia, Z.: Sb3+ doping-induced triplet self-trapped excitons emission in lead-free Cs2SnCl6 nanocrystals. J. Phys. Chem. Lett. 10(23), 7439–7444 (2019)
Tan, Z., Li, J., Zhang, C., Li, Z., Hu, Q., Xiao, Z., Kamiya, T., Hosono, H., Niu, G., Lifshitz, E., Cheng, Y., Tang, J.: Highly efficient blue-emitting Bi-doped Cs2SnCl6 perovskite variant: photoluminescence induced by impurity doping. Adv. Funct. Mater. 28(29), 1801131 (2018)
Wei, H., Sun, J., Mao, X., Wang, H., Chen, Z., Bai, T., Cheng, P., Zhang, R., Jin, B., Zhou, P., Liu, F., Han, K.: Cs2SnCl6: to emit or to catalyze? Te4+ ion calls the shots. Adv. Sci. (Weinh.) 10(29), 2302706 (2023)
Yan, A., Li, K., Zhou, Y., Ye, Y., Zhao, X., Liu, C.: Tuning the optical properties of Cs2SnCl6: Bi and Cs2SnCl6: Sb lead-free perovskites via post-annealing for white LEDs. J. Alloys Compd. 822, 153528 (2020)
Das Adhikari, S., Echeverría-Arrondo, C., Sánchez, R.S., Chirvony, V.S., Martínez-Pastor, J.P., Agouram, S., Muñoz-Sanjosé, V., Mora-Seró, I.: White light emission from lead-free mixed-cation doped Cs2SnCl6 nanocrystals. Nanoscale 14(4), 1468–1479 (2022)
Zhong, Y., Huang, Y.E., Deng, T., Lin, Y.T., Huang, X.Y., Deng, Z.H., Du, K.: Multi-dopant engineering in perovskite Cs2SnCl6: white light emitter and spatially luminescent heterostructure. Inorg. Chem. 60, 17357 (2021)
Zhang, H., Zhu, L., Cheng, J., Chen, L., Liu, C., Yuan, S.: Photoluminescence characteristics of Sn2+ and Ce3+-doped Cs2SnCl6 double-perovskite crystals. Materials (Basel) 12(9), 1501 (2019)
Zhu, H., Pan, Y., Peng, C., Ding, Y., Lian, H., Lin, J., Li, L.: Precise hue control in a single-component white-light emitting perovskite Cs2SnCl6 through defect engineering based on La3+ doping. Small 19(21), 2300862 (2023)
Lin, H., Wei, Q., Ke, B., Lin, W., Zhao, H., Zou, B.: Excitation-wavelength-dependent emission behavior in (NH4)2SnCl6 via Sb3+ dopant. J. Phys. Chem. Lett. 14(6), 1460–1469 (2023)
Li, Z., Zhang, C., Li, B., Lin, C., Li, Y., Wang, L., Xie, R.J.: Large-scale room-temperature synthesis of high-efficiency lead-free perovskite derivative (NH4)2SnCl6: Te phosphor for warm wLEDs. Chem. Eng. J. 420, 129740 (2021)
Song, G., Li, M., Yang, Y., Liang, F., Huang, Q., Liu, X., Gong, P., Xia, Z., Lin, Z.: Lead-free tin(IV)-based organic-inorganic metal halide hybrids with excellent stability and blue-broadband emission. J. Phys. Chem. Lett. 11(5), 1808–1813 (2020)
Chen, Q., Zhang, M., Dai, F., Zhao, L., Liu, S., Zhao, H., Zhou, H., Teng, L., Xu, W., Wang, L., Xing, J.: An organic–inorganic tin halide perovskite with over 2000-hour emission stability. Adv. Opt. Mater. 11(5), 2202475 (2023)
Zhang, G., Dang, P., Xiao, H., Lian, H., Liang, S., Yang, L., Cheng, Z., Li, G., Lin, J.: Antimony-doped lead-free zero-dimensional tin(IV)-based organic–inorganic metal halide hybrids with high photoluminescence quantum yield and remarkable stability. Adv. Opt. Mater. 9(24), 2101637 (2021)
Kim, B., Seok, S.I.: Molecular aspects of organic cations affecting the humidity stability of perovskites. Energy Environ. Sci. 13(3), 805–820 (2020)
Zhong, Y., Liu, S.P., Lin, Y.P., Qi, X.H., Yang, B., Zhang, Q., Du, K.Z.: Multi-mode photoluminescence regulation in a zero-dimensional organic–inorganic hybrid metal halide perovskite—[(CH3)4N]2SnCl6. Inorg. Chem. 62(35), 14422–14430 (2023)
Elsenety, M.M., Kaltzoglou, A., Koutselas, I., Psycharis, V., Raptopoulou, C.P., Kontos, A.G., Papadokostaki, K.G., Nasikas, N.K., Falaras, P.: Synthesis, crystal structure, and broadband emission of (CH3)3SSnCl3. Inorg. Chem. 61(11), 4769–4777 (2022)
Vogler, A., Nikol, H.: The structures of s2 metal complexes in the ground and sp. excited states. Comments Mod. Chem. A Comments Inorg. Chem. 14(4), 245–261 (1993)
Li, S., Luo, J., Liu, J., Tang, J.: Self-trapped excitons in all-inorganic halide perovskites: fundamentals, status, and potential applications. J. Phys. Chem. Lett. 10(8), 1999–2007 (2019)
Su, B., Zhou, G., Huang, J., Song, E., Nag, A., Xia, Z.: Mn2+ doped metal halide perovskites: structure, photoluminescence, and application. Laser Photonics Rev. 15(1), 2000334 (2021)
Uoyama, H., Goushi, K., Shizu, K., Nomura, H., Adachi, C.: Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492(7428), 234–238 (2012)
Hofbeck, T., Monkowius, U., Yersin, H.: Highly efficient luminescence of Cu(I) compounds: thermally activated delayed fluorescence combined with short-lived phosphorescence. J. Am. Chem. Soc. 137(1), 399–404 (2015)
Du, K.Z., Feng, M.L., Li, J.R., Huang, X.Y.: Ionothermal synthesis and characterization of two cluster chalcohalides: [Cr7S8Cl2(NH3)14.5(H2O)1.5]Cl3·H2O and [Emim]2. CrystEngComm 15(28), 5594 (2013)
Godby, R.W., Schlüter, M., Sham, L.J.: Trends in self-energy operators and their corresponding exchange-correlation potentials. Phys. Rev. B Condens. Matter 36(12), 6497–6500 (1987)
Liu, R., Zhang, W., Liu, W., Li, G.: Synthesis of a Bi3+-doped Cs2HfCl6 double perovskite with highly efficient blue light emission at room temperature. Inorg. Chem. 60(14), 10451–10458 (2021)
Xiong, G., Yuan, L., Jin, Y., Wu, H., Li, Z., Qu, B., Ju, G., Chen, L., Yang, S., Hu, Y.: Aliovalent doping and surface grafting enable efficient and stable lead-free blue-emitting perovskite derivative. Adv. Opt. Mater. 8(20), 2000779 (2020)
Krasnikov, A., Mihokova, E., Nikl, M., Zazubovich, S., Zhydachevskyy, Y.: Luminescence spectroscopy and origin of luminescence centers in Bi-doped materials. Crystals (Basel) 10(3), 208 (2020)
Hu, R., Ge, C., Chu, L., Feng, Y., Xiao, S., Ma, Y., Liu, W., Li, X., Nazeeruddin, M.K.: Novel photoelectric material of perovskite-like (CH3)3SPbI3 nanorod arrays with high stability. J. Energy Chem. 59, 581–588 (2021)
Acknowledgements
This work was supported by the National Natural Science Foundation of China (NSFC) (Grant Nos. 22373014 and 22371043), the Natural Science Foundation of Fujian Province (No. 2022J06019), and the Open Project Program of Wuhan National Laboratory for Optoelectronics (No. 2020WNLOKF009).
Author information
Authors and Affiliations
Contributions
All authors read and approved the final manuscript. Materials preparation, data collection and analysis through YZ, YL, YL, JL, LP and ZZ. The first draft of the manuscript was written by YL. K-ZD, YZ, YZ and X-YH provides guidance for the writing and revision of this article. All authors commented on previous versions of the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lin, Y., Zhong, Y., Lin, Y. et al. White light emission in 0D halide perovskite [(CH3)3S]2SnCl6·H2O crystals through variation of doping ns2 ions. Front. Optoelectron. 17, 6 (2024). https://doi.org/10.1007/s12200-024-00109-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s12200-024-00109-3