Abstract
The microstructure of the laser powder bed additively manufactured Inconel 625 in post-build stress-relief annealed condition and subsequently annealed at a temperature of 600 °C for 5, 100 and 500 h was investigated by means of light microscopy as well as scanning and transmission electron microscopy. Stress-relieved Inconel 625 exhibited fine cellular–dendritic microstructure characterized by the high dislocation density. Selected area electron diffraction studies allowed to demonstrate that already after 5 h of annealing at a temperature of 600 °C, precipitation of the γ′′ phase in the form of coherent nanoparticles occurred. With the prolongation of the duration of annealing at a temperature of 600 °C from 5 to 500 h, the gradual dissolution of intercellular areas and decrease in the dislocation density were accompanied by enhanced precipitation of the γ′′ phase nanoparticles.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Inconel 625 is a nickel-based superalloy exhibiting high-temperature strength, good corrosion resistance in several aggressive environments and good weldability (Ref 1,2,3). Due to its specific properties, it is widely used in different applications, e.g., in automotive, aeronautics and chemical industries. However, like other nickel-based superalloys, Inconel 625 is difficult to machine. Therefore, additive manufacturing (AM) of Inconel 625 is an attractive process for fabrication of parts with complex geometry (Ref 4). One of the mostly applied AM processes, which is used to make Inconel 625 parts, is laser-based powder bed fusion (L-PBF), in which the layers of powder are successively spread on the platform and selectively fused by a laser beam scanning along the predefined path. The process is repeating until the desired shape is obtained. Due to the rapid melting followed by the rapid cooling during the L-PBF processes, the thin layers of melted powder undergo rapid dendritic solidification and thus, in the post-built condition, Inconel 625 exhibits fine cellular–dendritic microstructure (Ref 5). To reduce residual stresses and thus avoid distortions before cutting built parts from the building platform, routinely stress-relief annealing is performed at a temperature of 870 °C for 1 h (Ref 5,6,7). Examination of the microstructure of L-PBF-processed Inconel 625 in as-built and stress-relief annealed condition was the subject of several reports (Ref 5, 7,8,9,10,11,12). The microstructure after post-build annealing at a temperature of 980 and 1150 °C was also examined (Ref 13). It was revealed that in the as-built condition, the significant segregation of Ni and Cr to dendrite cores as well as enrichment of the interdendritic regions in Nb and Mo occurs (Ref 8, 9, 12, 13). Along the melt pool boundaries, precipitates of the γ′′ phase rich in Nb were observed (Ref 10). Furthermore, in the stress-relieved condition, the presence of the γ′′ phase, δ phase as well as MC, M6C and M23C6 carbides was reported (Ref 7, 11, 12). However, to the knowledge of the authors, there is limited information about the microstructure of L-PBF Inconel 625 subjected to the post-build annealing at a temperature higher than the routinely applied stress annealing. Moreover, there are only a few reports on the evolution of the microstructure during the subsequent exposure at a temperature of 600 °C (Ref 9), which is the working temperature of Inconel 625 in the chemical industry, waste processing and energy systems applications (Ref 14,15,16).
Therefore, the aim of the present study is characterization of the microstructural changes that occur at micron-/submicron- and nanoscale in the L-PBF Inconel 625 subjected to post-build stress-relief annealing at a temperature of 980 °C for 1 h, as well as after subsequent annealing at a temperature of 600 °C for 5, 100 and 500 h.
Materials and Methods
The specimens of Inconel 625 delivered by Bibus Menos Sp. z o.o. (Poland) were fabricated by Direct Metal Laser Sintering® (DMLS), being the commercially available L-PBF process of EOS GmbH (Germany). The chemical composition of the alloy is as follows (wt.%): 63.9Ni-21.5Cr-1.3Fe-8.1Mo-3.9Nb-0.5Si-0.2Al-0.2Ti-0.2Co-0.1C-0.1Mn. The fabricated specimens in cuboidal shape 15 mm × 15 mm × 15 mm in size were subjected to the post-build annealing at a temperature of 980 °C for 1 h and slowly cooled in an argon atmosphere. The purpose of this treatment was stress relieving and also partial solution annealing. Subsequently, the specimens were isothermally annealed at a temperature of 600 °C for 5, 100 and 500 h and cooled in air. The microstructural investigation was performed by means of light microscopy (LM), scanning and transmission electron microscopy (SEM, TEM). The LM and SEM analyses of polished sections were carried out using Axio Imager M1m (ZEISS, Germany) and Nova NanoSEM 450 (FEI, USA) microscopes. Thin foils for TEM were prepared by electropolishing. The TEM investigation was performed using JEM-2010 ARP microscope (Jeol, Japan) equipped with INCA EDS system (Oxford Instruments, UK). Selected area electron diffraction (SAED) patterns were analyzed with the use of JEMS v4.4230 software (Pierre Stadelmann, JEMS-SAS, Switzerland). Dislocation density was estimated by the Ham line-intercept method using TEM bright-field (BF) images acquired in two-beam conditions (Ref 17).
Results and Discussion
Figure 1(a) shows a composite of LM images corresponding to horizontal (XY) and vertical (XZ and YZ) sections of the stress-relief annealed specimen. The built direction is marked by an arrow. In the vertical plane (Fig. 1b), the profiles of melt pools forming a so-called fish scale are visible. Figure 1(d) displays the layers of deposited material observed in the horizontal plane. The angle between the laser paths in the successive layers is equal to 67°, according to the scan strategy applied by EOS in DMLS process. SEM observations revealed the cellular–dendritic microstructure within the layers (Fig. 1c and e), which is typical for L-PBF-processed alloys. The width of cells was in the range of 300-400 nm. EDS microanalysis revealed the preferred segregation of Nb and Mo to the cell walls. The average concentration of Nb and Mo, determined from measurements at 20 points, was equal to 1.2% Nb and 4.0% Mo inside the cells; meanwhile, at the cell walls, it amounted to 5.8% Nb and 6.2% Mo. In both the vertical and horizontal planes, besides the cellular forms, the elongated columnar cells and fine dendrites with very short secondary arms were present (Fig. 1c and e). Such elongated cells and dendrites demonstrated epitaxial growth over melt pool boundaries. This shows that the re-melting of the underlying layers during subsequent laser passes allowed for the restart of the grain growth process in the next layers (Ref 18). In the horizontal plane in the vicinity of melt pool boundaries, also the coarser cellular regions occurred (Fig. 1e). Kruth et al. (Ref 19) postulated that in L-PBF-processed alloys, such regions are not overlapped with alternating layers and thus not re-melted by laser, so in effect are less heat-affected, which leads to a coarse microstructure. Similar findings have been reported in the laser-assisted direct energy deposited Inconel 625 (Ref 20). TEM microstructural analysis showed the high dislocation density inside cells and splits of dislocations within the cell walls (Fig. 2a and b). The estimated dislocation density was equal to 3.65 × 1014 m−2. This observation indicates that the annealing at a temperature of 980 °C for 1 h is not sufficient to relieve the residual stresses in L-PBF Inconel 625. In the cell walls, precipitates of the secondary phases were observed (Fig. 2c). Such particles were of globular or irregular shapes and up to 100 nm in size. Figure 2(d) shows the EDS spectrum of the particle with globular morphology marked in Fig. 2(c) by an arrow. Results of quantitative EDS microanalysis of the matrix and exemplary precipitates are given in Table 1. The concentration of Si, Cr and Fe in individual particles varied in a similar range as in the matrix. The Ni content in the matrix was about 66.6%, while in the precipitates was in the range from 59.0 to 70.4%. In the case of Nb and Mo, in some particles, the concentration of these elements was at a similar level as in the matrix (e.g., precipitates no 1-3 in Table 1), while in most of the analyzed particles, a significant enrichment in Nb and Mo was observed.
The trials of phase identification using SAED patterns revealed that the examined particles may be the precipitates of the γ′′ phase (tetragonal, I4/mmm), δ phase (orthorhombic, Pmmm), P phase (orthorhombic, Pnma), Laves phase (hexagonal, P63mmc) or the M6C carbides (cubic, Fd3m). However, the solutions of the diffraction patterns provided several possible phases; thus, the undoubted phase identification was not possible. In many previous studies, it was demonstrated that Inconel 625 exhibits a complex precipitation behavior, which varies depending on the production method, e.g., wrought, powder metallurgy, welding, laser cladding or cold metal transfer cladding (Ref 1, 2, 20,21,22,23,24,25,26,27,28,29,30). It has been shown that at a temperature range of 550-900 °C, precipitates of the γ′, γ′′, δ and Ni2(Cr,Mo) Laves phases, as well as MC, M6C and M23C6 carbides, can be present in Inconel 625 fabricated using different methods. The further studies are needed to determine which exact phases are present in stress-relief annealed L-PBF Inconel 625.
Figure 3(a), (b), (c) and (d) shows the typical microstructure of the L-PBF Inconel 625 specimen annealed at a temperature of 600 °C for 5 h observed on LM, SEM and TEM images. The LM and SEM images did not reveal the pronounced changes in the microstructure, as compared with the stress-relief annealed condition. However, the dislocation density decreased to 2.77 × 1014 m−2 (Fig. 3c). Besides the precipitates of globular and irregular shapes located in the cell walls, the elongated nanoparticles with oscillating contrast in TEM bright-field images were observed. Examples of such precipitates are marked by arrows in Fig. 3(d). SAED patterns allowed to identify them as the precipitates of the γ′′ phase. Figure 3(e) shows the electron diffraction pattern of the matrix γ phase [100] zone axis with the lower intensity spots of the γ′′ phase [100] and [010] zone axes, which confirms that the precipitates lie on the {100} planes of the γ matrix. Body centered tetragonal Ni3Nb-based γ′′ phase exhibits ordered structure and precipitates from the γ solid solution in the form of coherent precipitates (Ref 31). Precipitates of the γ′′ phase were observed in the thin foils prepared from the sections parallel to the horizontal (XY) and vertical (XZ and YZ) sections of the examined specimen. The evidence of the γ′′ phase was reported also in L-PBF Inconel 625 subjected to stress-relief annealing at a temperature of 870 °C for 1 h (Ref 7). Our studies did not confirm those findings for the specimen stress relieved at the higher temperature of 980 °C, whereas it was demonstrated that precipitation of the γ′′ phase occurs after subsequent annealing at a temperature of 600 °C for 5 h in the whole volume of the L-PBF Inconel 625. Precipitation of the γ′′ phase was also observed in wrought Inconel 625 long-time service exposed and subsequently annealed at the temperature of 650 °C for 1 h (Ref 2) as well as in TIG and GTA welds heat treated at 700 °C for 8 h (Ref 24) and 750 °C for 4 h (Ref 25), respectively. Although welding and L-PBF processes seem similar, the cooling rates in additive manufacturing are much higher, which results in a very fine and highly segregated microstructure. Our observations indicate that such refinement in L-PBF Inconel 625 contributes to precipitation of the γ′′ phase at lower temperature and after a shorter time than in heat-treated welds. Prolongation of the annealing time up to 100 h resulted in the destabilization of the cellular microstructure manifested by breaks in the continuity of the cell walls, as observed in LM images (Fig. 4a) and more clearly in SEM images (Fig. 4b). Due to the intensification of recovery processes, dislocation density inside the cells further decreased and was equal to 2.55 × 1014 m−2 (Fig. 4c). Moreover, the γ′′ phase particles grew and precipitated in all three sets of the {100} planes of the γ phase matrix, what was demonstrated by the presence of the three sets of diffraction spots form the [100], [010] and [001] zone axes of the γ′′ phase (Fig. 4d and e). Streaking of the γ′′ diffraction spots in the principal cubic directions is related to the plate-like shape of the particles precipitated on the {100} γ phase planes. EDS spectra acquired in the locations of the γ′′ phase precipitates revealed the presence of the strong Ni, Cr, Mo and Nb peaks (Fig. 4f). The γ′′ phase nanoparticles were below 100 nm in size, while the foil thickness was about 210 nm; thus, this result represents the sum of the γ and γ′′ phase compositions. It should be pointed out that prolongation of the annealing at a temperature of 600 °C to 100 h did not result in intensive precipitation of the δ phase, as it was shown in other studies even already after stress relieving at a temperature of 870 °C for 1 h (Ref 12).
After annealing for 500 h at a temperature of 600 °C, the progress in homogenizing of the cellular microstructure was insignificant, as compared with the observations of the sample annealed for 100 h (Fig. 5a and b). In turn, dislocation density decreased to 1.68 × 1014 m−2 (Fig. 5c). Pronounced intensification of the γ′′ phase precipitation was also noticed. Densely arranged precipitates were visible in TEM bright-field images (Fig. 5d) as well as the dark-field images recorded in the [002] spot of the γ′′ phase (Fig. 5e and the corresponding SAED pattern in Fig. 5f). The density of the γ′′ phase precipitates was higher in the cell walls areas than in the cell interiors. This observation can be correlated with the results of the EDS microanalysis of the initial stress-relief condition showing the high degree of Nb microsegregation to the cell walls, which creates the more favorable conditions for precipitation of the γ′′ phase.
Conclusions
-
1.
The fine cellular–dendritic microstructure of L-PBF Inconel 625 subjected to stress-relief annealing at a temperature of 980 °C for 1 h is characterized by high dislocation density.
-
2.
Precipitates of the γ′′ phase were found in L-PBF Inconel 625 annealed at a temperature of 600 °C for 5, 100 and 500 h. The plate-shaped nanoparticles of the γ′′ phase precipitated on the {100} planes of the γ phase matrix.
-
3.
With the prolongation of annealing duration at a temperature of 600 °C, the gradual dissolution of intercellular areas and the decrease in the dislocation density was observed.
References
S. Floreen, G.E. Fuchs, and W.J. Yang, Metallurgy of alloy 625, Superalloys 718, 625 and Various Derivatives, E.A. Loria, Ed., The Minerals, Metals and Materials Society, Warrendale, 1994, p 13–37
V. Shankar, K.B.S. Rao, and S.L. Mannan, Microstructure and Mechanical Properties of Inconel 625 Superalloy, J. Nucl. Mater., 2001, 228, p 222–232
L.E. Shoemaker, Alloys 625 and 725: Trends in Properties and Applications, Superalloys 718, 625 and Various Derivatives, E.A. Loria, Ed., The Minerals, Metals and Materials Society, Warrendale, 2005, p 409–418
J.A. Gonzalez, J. Mireles, S.W. Stafford, M.A. Perez, C.A. Terrazas, and R.B. Wicker, Characterization of Inconel 625 Fabricated Using Powder-Bed-Based Additive Manufacturing Technologies, J. Mater. Process. Technol., 2018, 264, p 200–210
E.A. Lass, M.R. Stoudt, M.E. Williams, M.B. Katz, L.E. Levine, T.Q. Phan, T.H. Gnaeupel-Herold, and D.S. Ng, Formation of the Ni3Nb δ-Phase in Stress-Relieved Inconel 625 Produced Via Laser Powder-Bed Fusion Additive Manufacturing, Metall. Mater. Trans., 2017, 48, p 5547–5558
A. Kreitcberg, V. Brailovskia, and S. Turenneb, Effect of Heat Treatment and Hot Isostatic Pressing on the Microstructure and Mechanical Properties of Inconel 625 Alloy Processed by Laser Powder Bed Fusion, Mater. Sci. Eng. A, 2017, 689, p 1–10
E.A. Lass, M.R. Stoudt, M.B. Katz, and M.E. Williams, Precipitation and Dissolution of δ and γ′′ During Heat Treatment of a Laser Powder-Bed Fusion Produced Ni-Based Superalloy, Scr. Mater., 2018, 154, p 83–86
F. Zhang, L.E. Levine, A.J. Allen, C.E. Campbell, E.A. Lass, S. Cheruvathur, M.R. Stoudt, M.E. Williams, and Y. Idell, Homogenization Kinetics of a Nickel-Based Superalloy Produced by Powder Bed Fusion Laser Sintering, Scr. Mater., 2017, 131, p 98–102
G. Marchese, M. Lorusso, S. Parizia, E. Bassini, J.-W. Lee, F. Calignano, D. Manfredi, M. Terner, H.-U. Hong, D. Ugues, M. Lombardi, and S. Biamino, Influence of Heat Treatments on Microstructure Evolution and Mechanical Properties of Inconel 625 Processed by Laser Powder Bed Fusion, Mater. Sci. Eng. A, 2018, 729, p 64–75
K.N. Amato, J. Hernandez, L.E. Murr, E. Martinez, S.M. Gaytan, and P.W. Shindo, Comparison of Microstructures and Properties for a Ni-Base Superalloy (Alloy 625) Fabricated by Electron and Laser Beam Melting, J. Mater. Sci. Res., 2012, 1, p 1–41
T. Keller, G. Lindwall, S. Ghosh, L. Ma, B.M. Lane, F. Zhang, U.R. Kattner, E.A. Lass, J.C. Heigel, Y. Idell, M.E. Williams, A.J. Allen, J.E. Guyer, and L.E. Levine, Application of Finite Element, Phase-Field, and CALPHAD-Based Methods to Additive Manufacturing of Ni-Based Superalloy, Acta Mater., 2017, 139, p 244–253
F. Zhang, L.E. Levine, A.J. Allen, M.R. Stoudt, G. Lindwall, E.A. Lass, M.E. Williams, Y. Idell, and C.E. Campbell, Effect of Heat Treatment on the Microstructural Evolution of a Nickel-Based Superalloy Additive-Manufactured by Laser Powder Bed Fusion, Acta Mater., 2018, 152, p 200–214
C. Li, R. White, X.Y. Fang, M. Weaver, and Y.B. Gu, Microstructure Evolution Characteristics of Inconel 625 Alloy from Selective Laser Melting to Heat Treatment, Mater. Sci. Eng. A, 2017, 705, p 20–31
A. Kruse, A. Krupka, V. Schwarzkopf, C. Gamard, and T. Henningsen, Influence of Proteins on Hydrothermal Gasification and Liquefaction of Biomass. 2. Model Compounds, Ind. Eng. Chem. Res., 2007, 46, p 87–96
S. Saka and D. Kusdiana, Biodiesel Fuel from Rapeseed Oil as Prepared in Supercritical Methanol, Fuel, 2001, 80, p 225–231
K. Özdenkçi, C. De Blasio, G. Sarwar, K. Melin, J. Koskinen, and V. Alopaeus, Techo-Economic Feasibility of Supercritical Water Gasification of Black Liquor, Energy, 2019, 189, p 116284
R.K. Ham, The Determination of Dislocation Densities in Thin Films, Philos. Mag., 1961, 6, p 1183–1184
M. Calandri, S. Yin, B. Aldwell, F. Calignano, R. Lupoi, and D. Ugues, Texture and Microstructural Features at Different Length Scales in Inconel 718 Produced by Selective Laser Melting, Materials, 2019, 12, p 1–32
J.P. Kruth, M. Badrossamay, E. Yasa, J. Deckers, L. Thijs, and J. Van Humbeeck, Part and Material Properties in Selective Laser Melting of Metals, in 16th International Symposium on Electromachining, Shangai, China, 19–23 April 2010, Red Hook, NY (2014), pp. 3–14
G.P. Dinda, A.K. Dasqupta, and J. Mazumder, Laser Aided Direct Metal Deposition of Inconel 625 Superalloy: Microstructural Evolution and Thermal Stability, Mater. Sci. Eng. A, 2009, 509, p 98–104
G.K. Dey, S. Albert, D. Srivastava, M. Sundararaman, and P. Mukhopadhyay, Microstructural Studies on Rapidly Solidified Inconel 625, Mater. Sci. Eng. A, 1989, 119, p 175–184
L.M. Suave, J. Cornier, P. Villechaise, A. Soula, Z. Hervier, D. Bertheau, and J. Laigo, Microstructural Evolution during Thermal Aging of Alloy 625: Impact of Temperature and Forming Process, Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2014, 45, p 2963–2982
F.J. Rizzo and J. Radavich, Microstructural Characterization of PM 625-Type Materials, Superalloys 718, 625 and Various Derivatives, E.A. Loria, Ed., The Minerals Metals and Materials Society, Warrendale, 1991, p 297–308
F. Cortial, J.M. Corrieu, and C. Vernot-Loier, Influence of Heat Treatments on Microstructure, Mechanical Properties, and Corrosion Resistance of Weld Alloy 625, Superalloys 718, 625 and Various Derivatives, E.A. Loria, Ed., The Minerals Metals and Materials Society, Warrendale, 1994, p 859–870
X. Xing, X. Di, and B. Wang, The Effect of Post-Weld Heat Treatment Temperature on the Microstructure of Inconel 625 Deposited Metal, J. Alloys Compd., 2014, 593, p 110–116
T.E. Abioye, D.G. McCartney, and A.T. Clare, Laser Cladding of Inconel 625 Wire for Corrosion Protection, J. Mater. Process. Technol., 2015, 217, p 232–240
P. Petrzak, K. Kowalski, and M. Blicharski, Analysis of Phase Transformations in Inconel 625 Alloy During Annealing, Acta Phys. Pol. A, 2016, 130, p 1041–1044
B. Dubiel and J. Sieniawski, Precipitates in Additively Manufactured Inconel 625 Superalloy, Materials, 2019, 12, p 1–11
M. Solecka, A. Kopia, A. Radziszewska, and B. Rutkowski, Microstructure, Microsegregation and Nanohardness of CMT Clad Layers of Ni-Base Alloy on 16Mo3 Steel, J. Alloys Compd., 2018, 751, p 86–95
M. Rozmus-Górnikowska, Ł. Cieniek, M. Blicharski, and J. Kusiński, Microstructure and Microsegregation of an Inconel 625 Weld Overlay Produced on Steel Pipes by the Cold Metall Tranfer Technique, Arch. Metall. Mater., 2014, 59, p 1081–1084
B. Dubiel, A. Kruk, E. Stępniowska, G. Cempura, D. Geiger, P. Formanek, J. Hernandez, P. Midgley, and A. Czyrska-Filemonowicz, TEM, HRTEM, electron holography and electron tomography studies of γ′ and γ′′ nanoparticles in Inconel 718 superalloy, J. Microsc., 2009, 236, p 149–157
Acknowledgments
This research was funded by the National Science Centre, Poland, Grant No. 2017/27/B/ST8/02244.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
This article is an invited submission to JMEP selected from presentations at The XXII Physical Metallurgy and Materials Science Conference: Advanced Materials and Technologies (AMT 2019) held June 9-12, 2019, in Bukowina Tatrzańska, Poland, and has been expanded from the original presentation.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gola, K., Dubiel, B. & Kalemba-Rec, I. Microstructural Changes in Inconel 625 Alloy Fabricated by Laser-Based Powder Bed Fusion Process and Subjected to High-Temperature Annealing. J. of Materi Eng and Perform 29, 1528–1534 (2020). https://doi.org/10.1007/s11665-020-04605-3
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-020-04605-3