Abstract
In this study, interaction of ionic liquid (IL) and borate esters (SBs) as antiwear (AW) additives with steel surfaces in tribological contacts was examined using blends which contained no prior AW additives but all the other ingredients present in a fully formulated engine oil. In detail, low phosphorus oil blends were prepared by adding trihexyltetradecylphosphonium bis(2-ethylhexyl)phosphate (P_DEHP) at 700 ppm phosphorus and 2-methoxy-4,4,6-trimethyl-1,3,2-dioxaborinane or trimethoxyboroxine at 200 ppm boron treat rate to a partially formulated oil. The tribological properties of these novel ionic liquid (IL) additive and IL + SB additive mixtures were compared with those of zinc dialkyldithiophosphate (ZDDP) at equal phosphorus levels in the oil blends. Tribological experiments with a reciprocating cylinder on flat contact revealed that both P_DEHP and binary mixtures of P_DEHP + SB offer superior wear protection than ZDDP and the partially formulated oil without AW additives, expressed by a wear reduction of minimum 50%. X-ray absorption near edge structure spectroscopy (XANES) analysis revealed that tribologically formed films are primarily composed of calcium phosphate for oils with AW additives. The interaction of P_DEHP with SB results in additional boron oxide/boric acid and to some extent boron phosphate domains incorporated into the tribofilms.
Similar content being viewed by others
References
Sharma, V., Doerr, N., Aswath, P.: Chemical-mechanical properties of tribofilms and its relation to ionic liquid chemistry. RSC Adv. 6, 22341–22356 (2016)
Somers, A.E., Khemchandani, B., Howlett, P.C., Sun, J., MacFarlane, D.R., Forsyth, M.: Ionic liquids as antiwear additives in base oils: influence of structure on miscibility and antiwear performance for steel on aluminum. ACS Appl. Mater. Interfaces 5, 11544–11553 (2013)
Anand, M., Hadfield, M., Viesca, J., Thomas, B., Battez, A.H., Austen, S.: Ionic liquids as tribological performance improving additive for in-service and used fully-formulated diesel engine lubricants. Wear 334, 67–74 (2015)
Barnhill, W.C., Qu, J., Luo, H., Meyer, H.M., Ma, C., Chi, M., et al.: Phosphonium-organophosphate ionic liquids as lubricant additives: effects of cation structure on physicochemical and tribological characteristics. ACS Appl. Mater. Interfaces 6, 22585–22593 (2014)
Pisarova, L., Gabler, C., Dörr, N., Pittenauer, E., Allmaier, G.: Thermo-oxidative stability and corrosion properties of ammonium based ionic liquids. Tribol. Int. 46, 73–83 (2012)
Cai, M., Liang, Y., Yao, M., Xia, Y., Zhou, F., Liu, W.: Imidazolium ionic liquids as antiwear and antioxidant additive in poly (ethylene glycol) for steel/steel contacts. ACS Appl. Mater. Interfaces 2, 870–876 (2010)
Minami, I.: Ionic liquids in tribology. Molecules 14, 2286–2305 (2009)
Yu, B., Bansal, D.G., Qu, J., Sun, X., Luo, H., Dai, S., et al.: Oil-miscible and non-corrosive phosphonium-based ionic liquids as candidate lubricant additives. Wear. 289, 58–64 (2012)
Gusain, R., Gupta, P., Saran, S., Khatri, O.P.: Halogen-free bis (imidazolium)/bis (ammonium)-di [bis (salicylato) borate] ionic liquids as energy efficient and environment-friendly lubricant additives. ACS Appl. Mater. Interfaces 6(17), 15318–15328 (2014)
Qu, J., Luo, H., Chi, M., Ma, C., Blau, P.J., Dai, S., et al.: Comparison of an oil-miscible ionic liquid and ZDDP as a lubricant anti-wear additive. Tribol. Int. 71, 88–97 (2014)
Totolin, V., Minami, I., Gabler, C., Brenner, J., Dörr, N.: Lubrication mechanism of phosphonium phosphate ionic liquid additive in alkylborane–imidazole complexes. Tribol. Lett. 53, 421–432 (2014)
Qu, J., Blau, P.J., Dai, S., Luo, H., Meyer, H.M.: Ionic liquids as novel lubricants and additives for diesel engine applications. Tribol. Lett. 35, 181–189 (2009)
Jiménez, A.E., Bermúdez, M.: Ionic liquids as lubricants of titanium–steel contact. Tribol. Lett. 33, 111–126 (2009)
Jimenez, A., Bermudez, M.: Ionic liquids as lubricants of titanium–steel contact. Part 2: friction, wear and surface interactions at high temperature. Tribol. Lett. 37, 431–443 (2010)
Kronberger, M., Pejaković, V., Gabler, C., Kalin, M.: (2012) How anion and cation species influence the tribology of a green lubricant based on ionic liquids. Proc. Inst. Mech. Eng. Part J. 226, 933–951
Bermúdez, M., Jiménez, A., Sanes, J., Carrión, F.: Ionic liquids as advanced lubricant fluids. Molecules 14, 2888–2908 (2009)
Sharma, V., Gabler, C., Doerr, N., Aswath, P.B.: Mechanism of tribofilm formation with P and S containing ionic liquids. Tribol. Int. 92, 353–364 (2015)
González, R., Bartolomé, M., Blanco, D., Viesca, J., Fernández-González, A., Battez, A.H.: Effectiveness of phosphonium cation-based ionic liquids as lubricant additive. Tribol. Int. 98, 82–93 (2016)
Sharma, V., Doerr, N., Erdemir, A., Aswath, P.: Interaction of phosphonium ionic liquids with borate esters at tribological interfaces. RSC Adv. 6, 53148–53161 (2016)
Qu, J., Bansal, D.G., Yu, B., Howe, J.Y., Luo, H., Dai, S., et al.: Antiwear performance and mechanism of an oil-miscible ionic liquid as a lubricant additive. ACS Appl. Mater. Interfaces 4, 997–1002 (2012)
Grocholski, B.: Additive explanation for anti-wear. Science. 348, 87–88 (2015)
Qu, J., Barnhill, W.C., Luo, H., Meyer, H.M., Leonard, D.N., Landauer, A.K., et al.: Synergistic effects between phosphonium-alkylphosphate ionic liquids and zinc dialkyldithiophosphate (ZDDP) as lubricant additives. Adv. Mater. 27, 4767–4774 (2015)
Kasrai, M., Lennard, W.N., Brunner, R.W., Bancroft, G.M., Bardwell, J.A., Tan, K.H.: Sampling depth of total electron and fluorescence measurements in Si L- and K-edge absorption spectroscopy. Appl. Surf. Sci. 99, 303–312 (1996)
Parekh, K., Chen, X., Aswath, P.B.: Synthesis of fluorinated ZDDP compounds. Tribol. Lett. 34, 141–153 (2009)
Sharma, V., Erdemir, A., Aswath, P.B.: An analytical study of tribofilms generated by the interaction of ashless antiwear additives with ZDDP using XANES and nano-indentation. Tribol. Int. 82, 43–57 (2015)
Sharma, V., Uy, D., Gangopadhyay, A., O’Neill, A., Paxton, W.A., Sammut, A., et al.: Structure and chemistry of crankcase and exhaust soot extracted from diesel engines. Carbon. 103, 327–338 (2016)
Chen, X., Elsenbaumer, R.L., Aswath, P.B.: Synthesis and tribological behavior of ashless alkylphosphorofluoridothioates. Tribol. Int. 69, 114–124 (2013)
Chen, X., Kim, B., Elsenbaumer, R., Aswath, P.B.: Synthesis and antiwear behavior of alkylthioperoxydiphosphates. Tribology 6(3), 121–133 (2012)
Nicholls, M., Najman, M.N., Zhang, Z., Kasrai, M., Norton, P.R., Gilbert, P.U.P.A.: The contribution of XANES spectroscopy to tribology. Can. J. Chem. 85, 816–830 (2007)
Kim, B., Mourhatch, R., Aswath, P.B.: Properties of tribofilms formed with ashless dithiophosphate and zinc dialkyl dithiophosphate under extreme pressure conditions. Wear. 268, 579–591 (2010)
Li, Y., Pereira, G., Lachenwitzer, A., Kasrai, M., Norton, P.R.: X-ray absorption spectroscopy and morphology study on antiwear films derived from ZDDP under different sliding frequencies. Tribol. Lett. 27, 245–253 (2007)
Li, Y., Pereira, G., Kasrai, M., Norton, P.R.: Studies on ZDDP anti-wear films formed under different conditions by XANES spectroscopy, atomic force microscopy and 31P NMR. Tribol. Lett. 28, 319–328 (2007)
Nicholls, M.A., Do, T., Bancroft, G.M., Norton, P.R., Kasrai, M., Capehart, T.W., et al.: Chemical and mechanical properties of ZDDP antiwear films on steel and thermal spray coatings studied by XANES spectroscopy and nanoindentation techniques. Tribol. Lett. 15(3), 241–248 (2003)
Najman, M.N., Kasrai, M., Bancroft, G.M., Frazer, B.H., DeStatio, G.: The correlation of microchemical properties to antiwear (AW) performance in ashless thiophosphate oil additives. Tribol. Lett. 17(4), 811–822 (2004)
Najman, M.N., Kasrai, M., Bancroft, G.M.: Chemistry of anti-wear films from ashless thiophosphate oil additives. Tribol. Lett. 17(2), 217–229 (2004)
Najman, M., Kasrai, M., Michael Bancroft, G., Davidson, R.: Combination of ashless antiwear additives with metallic detergents: Interactions with neutral and overbased calcium sulfonates. Tribol. Int. 39, 342–355 (2006)
Pereira, G., Munoz-Paniagua, D., Lachenwitzer, A., Kasrai, M., Norton, P.R., Capehart, T.W., et al.: A variable temperature mechanical analysis of ZDDP-derived antiwear films formed on 52100 steel. Wear 262, 461–470 (2007)
Warren, O.L., Graham, J.F., Norton, P.R., Houston, J.E., Michalske, T.A.: Nanomechanical properties of films derived from zinc dialkyldithiophosphate. Tribol. Lett. 4, 189–198 (1998)
Aswath, P., Chen, X., Sharma, V., Igartua, M.A., Pagano, F., Binder, W., et al.: (2013) Synergistic mixtures of ionic liquids with other ionic liquids and/or with ashless thiophosphates for antiwear and/or friction reduction applications. U.S. Patent Application No. 13/889,037
Willermet, P.A., Dailey, D.P., Carter, R.O., Schmitz, P.J., Zhu, W., Bell, J.C., et al.: The composition of lubricant-derived surface layers formed in a lubricated cam/tappet contact, II. Effects of adding overbased detergent and dispersant to a simple ZDTP solution. Tribol. Int. 28(3), 163–175 (1995)
Wan, Y., Suominen Fuller, M.L., Kasrai, M., Bancroft, G.M., Fyfe, K., Torkelson, J.R., et al.: Effects of detergent on the chemistry of tribofilms from ZDDP: studied by X-ray absorption spectroscopy and XPS. In: Dowson, D., Priest, M., Dalmaz, G., Lubrecht, A.A. (eds.) Tribology Series, vol. 40, pp. 155–166. Elsevier, Amsterdam (2002)
Kasrai, M., Fuller, M.S., Bancroft, G.M., Ryason, P.R.: X-ray absorption study of the effect of calcium sulfonate on antiwear film formation generated from neutral and basic ZDDPs: part 1—phosphorus species. Tribol. Trans. 46, 534–542 (2003)
Yin, Z., Kasrai, M., Bancroft, G.M., Tan, K.H., Feng, X.: X-ray-absorption spectroscopic studies of sodium polyphosphate glasses. Phys. Rev. B 51, 742–750 (1995)
Kasrai, M., Fleet, M.E., Muthupari, S., Li, D., Bancroft, G.: Surface modification study of borate materials from B K-edge X-ray absorption spectroscopy. Phys. Chem. Miner. 25, 268–272 (1998)
Zhang, Z., Yamaguchi, E.S., Kasrai, M., Bancroft, G.M.: Interaction of ZDDP with borated dispersant using XANES and XPS. Tribol. Trans. 47, 527–536 (2004)
Acknowledgements
XANES experiments were conducted at the Canadian Light Source, Saskatoon, Saskatchewan, Canada that is supported by NSERC, NRC, CIHR and the University of Saskatchewan. Tribological tests were performed at Argonne National Laboratory and were supported by the U.S. Department of Energy, Office of Energy Efficiency and Renewable Energy, Office of Vehicle Technology under contract DE-AC02-06CH11357. Scanning probe microscopy experiments were conducted at Center for Characterization for Materials and Biology at The University of Texas at Arlington. This work was also supported by the “Austrian COMET-Program” in the frame of K2 XTribology (Project No. 849109).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Sharma, V., Dörr, N., Erdemir, A. et al. Antiwear Properties of Binary Ashless Blend of Phosphonium Ionic Liquids and Borate Esters in Partially Formulated Oil (No Zn). Tribol Lett 67, 42 (2019). https://doi.org/10.1007/s11249-019-1152-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11249-019-1152-0