We propose a computational model for the evaluation of the residual service life of a pipe of the oil pipeline weakened by an external surface stress-corrosion crack for a laminar flow of oil with multiple hydraulic shocks. The model is based on the earlier developed energy approach to the investigation of retarded crack propagation, the model of application of pulsed loads, and basic mechanisms of propagation of stress-corrosion cracks. By using the model, we study the dependence of the residual service life of the pipe of oil pipeline made of Kh60 steel on the number of hydraulic shocks in the pipe.
Similar content being viewed by others
References
V. I. Pokhmurskii, Corrosion Fatigue of Metals [in Russian], Metallurgiya, Moscow (1985).
О. N. Romaniv, S. Ya. Yarema, G. N. Nikiforchin, N. А. Makhutov, and M. M. Stadnik, Fatigue and Cyclic Crack Resistance of Structural Materials [in Russian], Naukova Dumka, Kiev (1990).
G. P. Cherepanov, Mechanics of Brittle Fracture [in Russian], Nauka, Moscow (1984).
V. V. Panasyuk and I. M. Dmytrakh, Influence of Corrosive Media on the Local Fracture of Metals Near Stress Concentrators [in Ukrainian], Karpenko Physicomechanical Institute, Ukrainian National Academy of Sciences, Lviv (1999).
V. V. Panasyuk, A. E. Andreikiv, and V. Z. Parton, Fundamentals of Fracture Mechanics [in Russian], Naukova Dumka, Kiev (1988).
V. V. Panasyuk, Mechanics of Quasibrittle Fracture of Materials [in Russian], Naukova Dumka, Kiev (1991).
V. T. Troshchenko, Deformation and Fracture of Metals under Low-Cycle Loading [in Russian], Naukova Dumka, Kiev (1981).
A. Carpinteri (editor), Handbook of Fatigue Crack Propagation in Metallic Structures, Vol. 1, Elsevier, Amsterdam (1994).
V. M. Agapkin and B. L. Krivoshein, Methods for the Protection of Pipelines Against Failures in Nonstationary Modes [in Russian], VNIIOÉNG, Moscow (1976).
O. E. Andreikiv and N. B. Sas, “Subcritical growth of a plane crack in a three-dimensional body under the conditions of hightemperature creep,” Fiz.-Khim. Mekh. Mater., 44, No. 2, 19–26 (2008); English translation: Mater. Sci., 44, No. 2, 163–174 (2008).
O. E. Andreikiv and N. B. Sas, “Fracture mechanics of metallic plates under the conditions of high-temperature creep,” Fiz.-Khim. Mekh. Mater., 42, No. 2, 62–68 (2006); English translation: Mater. Sci., 42, No. 2, 210–219 (2006).
O. E. Andreikiv and O. V. Hembara, Fracture Mechanics and Durability of Metallic Materials in Hydrogen-Containing Media [in Ukrainian], Naukova Dumka, Kyiv (2008).
L. D. Kudryavtsev, A Course of Mathematical Analysis [in Russian], Vol. 1, Vysshaya Shkola, Moscow (1981).
N. I. Tym’yak and O. E. Andreikiv, “Evaluation of crack-growth rate under conditions of simultaneous action of static loading and corrosive media,” Fiz.-Khim. Mekh. Mater., 31, No. 2, 68–74 (1995); English translation: Mater. Sci., 31, No. 2, 219–225 (1995).
O. V. Hembara, Z. O. Terlets’ka, and O. Ya. Chepil,’ “Determination of electric fields in electrolyte–metal systems,” Fiz.-Khim. Mekh. Mater., 43, No. 2, 71−76 (2007); English translation: Mater. Sci., 43, No. 2, 222–229 (2007).
M. Elboujdaini, “Initiation of environmentally assisted cracking in line pipe steel,” in: Proc. of the 16th Europ. Conf. on Fracture (ECF16th) “Fracture of Nano and Engineering Materials and Structures” (Alexandroupolis, Greece, July 3–7, 2006), Springer, Dordrecht (2006), pp. 1007−1008.
Z. V. Slobodyan, H. M. Nykyforchyn, and O. I. Petrushchak, “Corrosion resistance of pipe steel in oil–water media,” Fiz.-Khim. Mekh. Mater., 38, No. 3, 93–96 (2002); English translation: Mater. Sci., 38, No. 3, 424–429 (2002).
O. E. Andreikiv, I. Ya. Dolins’ka, V. Z. Kukhar, and Yu. Ya. Matviiv, “Computational model for the determination of a period of subcritical growth of creep cracks in structural elements under long-term static tensile loads,” Dop. Nats. Akad. Nauk Ukr., No. 4, 50–56 (2012).
O. T. Tsyrul’nyk, Z. V. Slobodyan, O. I. Zvirko, M. I. Hredil’, H. M. Nykyforchyn, and G. Gabetta, “Influence of the operation of Kh52 steel on corrosion processes in a model solution of gas condensate,” Fiz.-Khim. Mekh. Mater., 44, No. 5, 29–37 (2008); English translation: Mater. Sci., 44, No. 5, 619–629 (2008).
О. T. Tsyrul’nyk, Z. V. Slobodyan, М. І. Hredil,’ О. І. Zvirko, and D. М. Zaverbnyi, “Electrochemical characteristics of the inservice degradation of steels of oil and gas pipelines,” Fiz.-Khim. Mekh. Mater., Special Issue, No. 5, 284–289 (2006).
O. E. Andreikiv and N. B. Sas, “Determination of the residual life of a pipe with surface crack under long-term pressure at high temperature,” Mashynoznavstvo, No. 4, 3–6 (2005).
M. P. Savruk, Stress Intensity Factors in Bodies with Cracks [in Russian], Naukova Dumka, Kiev (1988).
О. T. Tsyrul’nyk, E. I. Kryzhanivs’kyi, D. Yu. Petryna, О. S. Taraevs’kyi, and М. І. Hredil,’ “Susceptibility of a welded joint of 17G1S steel of a gas main pipeline to hydrogen brittleness,” Fiz.-Khim. Mekh. Mater., 40, No. 6, 111–114 (2004); English translation: Mater. Sci., 40, No. 6, 844–849 (2004).
E. I. Kryzhanivs’kyi, R. S. Hrabovs’kyi, and O. M. Mandryk, “Estimation of the serviceability of oil and gas pipelines after longterm operation according to the parameters of their defectiveness,” Fiz.-Khim. Mekh. Mater., 49, No. 1, 105–110 (2013); English translation: Mater. Sci., 49, No. 1, 117–123 (2013).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Fizyko-Khimichna Mekhanika Materialiv, Vol. 53, No. 2, pp. 80–88, March–April, 2017.
Rights and permissions
About this article
Cite this article
Andreikiv, О.E., Nykyforchyn, H.М., Shtoiko, І.P. et al. Evaluation of the Residual Life of a Pipe of Oil Pipeline with an External Surface Stress-Corrosion Crack for a Laminar Flow of Oil with Repeated Hydraulic Shocks. Mater Sci 53, 216–225 (2017). https://doi.org/10.1007/s11003-017-0065-z
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11003-017-0065-z