Abstract
This article discusses the influence of MgB2 wire diameter on critical parameters, dominant pinning mechanism, and n value. Studies were conducted on multifilament MgB2 wires of the 0.84 mm and 0.64 mm diameter. The wires were annealed under 1 GPa isostatic pressure, between 650 and 730 °C. Studies show that the best results (Jc, Birr, n value, and point pinning mechanism) for a 0.64-mm wire were obtained with annealing temperature of 650 °C. However, the best results for wires with a 0.84-mm diameter were obtained with annealing temperature of 730 °C. This research was conducted for exploring the use of MgB2 wires in multi-section superconducting coils, e.g., main coils generating magnetic fields and compensation coils—increasing the homogeneity of the magnetic field. Our research indicates that the main coil made with larger diameter wires should be heated at higher temperature (730 °C). In contrast, compensating coils with smaller diameter wires should be heated at a lower temperature (650 °C).
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Research presented by Uchiyama et al. [1], Wang et al. [2], and Gajda et al. [3] showed that the reduction of the diameter of a superconductor wire as the result of cold drawing led to an increase of critical current density, irreversible magnetic field, pinning force, n value, and dominant pinning mechanism for samples heat treated at a constant temperature, due to increased MgB2 density, Mg elongation, formation of a layered structure, and increased density of pinning centers [1,2,3,4,5]. In contrast, Xu et al. indicated that a significant reduction of wire diameter causes a decrease of Jc [6]. The critical current density, irreversible magnetic field, and dominant pinning mechanism in MgB2 material depend on many factors, e.g., connections between grains, nano-additives [7, 8], the purity of the starting materials [9, 10], milling time [9,10,11], type of pinning centers [12,13,14], heat treatment temperature [15], defects, pores, and voids [16]. The n value, which qualifies the transition from the superconducting state to the normal state, is an important factor that influences the selection of the operating current for a superconducting device, coil, magnet, etc. [17]. The n value of a superconductor has a dependency on both intrinsic (connections between grains, grain microstructure, pinning centers) and extrinsic (filament distribution and quantity) [18, 19] factors. Superconducting applications include magnetic resonance imaging (MRI), induction furnace, magnetic separation, energy storage, laboratory magnets, and the International Thermonuclear Experimental Reactor. Many of these applications such as MRI require the generation of magnetic fields with high homogeneity produced from the superconductor coil. Unfortunately, superconducting coils have a large magnetic field gradient (difference in magnetic field between the magnet center and the magnet end). This disadvantage is eliminated by external compensating windings, which are coils that significantly increase the homogeneity of the magnetic field in the magnet. Compensation windings are made with superconductor wires of smaller diameter than the superconductor wires used in the main coil windings. Traditional superconducting magnets in the past were made using reacted superconducting wires (superconductive phase). More often today, coils are made with using unreacted wires and tapes such that the superconducting phase will be produced after the wire is wound on the coil former. This method eliminates cracks (e.g., damage to connections between inbound, Nb barriers) which it might occur during winding the coil. One crack significantly reduces Jc and hinders the use of the superconducting coil. Usually, the superconductor coils are made of several kilometers of superconducting wires. Based on superconductivity characterization and scanning microscope electron (SEM) analyses, small coil (diameter 14 mm) wounds with unreacted MgB2 wires have obtained high critical current density when annealed under high isostatic pressure of 1 GPa. In addition, Gajda et al. showed that the HIP process can be applied to small coils with no loss in superconductivity properties as compared with short samples [20]. The HIP process has been demonstrated to improve homogeneity and density of MgB2; reduce pore size, grains, and voids; improve the connection between grains; create pinning centers with homogeneous distribution; and increase the melting point in wires [21,22,23,24]. Moreover, Gajda et al. demonstrated that high isostatic pressure of 1 GPa significantly increased Jc in high magnetic fields [3].
This research was conducted to determine the impact of MgB2 wire diameter and high isostatic pressure heat treatment on Jc, Birr, n value, Fp, dominant pinning mechanism, and MgB2 material structure. The goal was to identify the optimal heat treatment protocol for the production of multi-sectional superconducting MgB2 coils.
2 Preparation of Samples
The in situ MgB2 wires were made of powders with purity of 99% (the nominal atomic ratio 1.10:2) and average boron and magnesium powder size of 50 nm and 40 μm. The filaments are made with continuous tube forming and filling (CTFF) method and restacked as a 18-filament wire at Hyper Tech Research, Inc. [25]. The wire compositions were Nb chemical barrier, Cu filamentary matrix, and Monel outer sheath; the fill factor was 15%, and the wires were drawn to 0.64 and 0.84 mm. The wires of both sizes were heat treated together at the same temperature (from 650 to 730 °C), pressure (1 GPa), and time (from 15 to 60 min) at the Institute of High Pressure Physics in Warsaw (see Table 1) [26, 27]. Critical current measurements were made at the Institute of Low Temperature and Structure Research PAS in Wroclaw, with a four-probe resistive method. All samples were measured in a perpendicular magnetic field (Bitter-type magnet—14 T) at liquid helium temperature, with constant current, and in accordance with a 1 μV/cm criterion [28]. Sample length was 20 mm. Kramer analysis used the Jc0.5*B0.25 formula [29]; scaling used the k*(hp)*(1-h)q formula [30]. Analysis of the microstructure and composition were performed by FEI Nova Nano 230 SEM at the Institute of Structural Research and Low Temperatures PAS in Wroclaw.
3 SEM Analysis
The results in Fig. 1 show the cross (Fig. 1a, b, e, f) and longitudinal (Fig. 1i and j) sections for sample A and B. Sample B has better connection between particles than sample A. In sample B, the small number of small-sized voids is created. In Fig. 1 we see cross (Fig. 1c, d, g, h) and longitudinal (Fig. 1k and l) sections for sample G and H. These photos indicate the larger and more voids are formed in sample H compared with sample G. This leads to the reduction of the density, homogeneity, and number of grains connections in the sample H. This leads to the reduction of the transport critical parameters in the superconducting materials. Based on the results in Fig. 1, it can be concluded that the synthesis reaction is faster in the of 0.64-mm-diameter wires than 0.84 mm diameter wires. The MgB2 wires of the 0.64 mm diameter are obtained with the MgB2 wires of 0.84 mm diameter by using cold drawing. Susner et al. showed that cold drawing causes elongates and reduces the thickness of Mg grains [5]. This leads to the faster synthesis reaction rate in MgB2 wires of the 0.64 mm diameter.
4 Results and Discussions
4.1 Annealing Temperature (Ta) of 650 °C for 60 min
The measurements and calculations indicate that a reduction of the MgB2 wire diameter from 0.84 to 0.64 mm significantly increases Jc in sample B (1000 A/mm2 in 6.3 T and 100 A/mm2 in 10 T) as compared with sample A (1000 A/mm2 in 5 T and 100 A/mm2 in 8.5 T). The Jc of sample B overall is 50% higher than Jc sample A (Fig. 2a). Comparing these results (sample B) with the results of Li et al. [31] and Yamada et al. [32], our undoped MgB2 wires have higher Jc than undoped MgB2 wires studies by others (1000 A/mm2 in 3 T and 100 A/mm2 in 6.2 T—annealing temperature of 675 °C) [31] and tapes (500 A/mm2 in 7 T and 100 A/mm2 in 9.5 T—annealing temperature of 630 °C) [32]. The maximum pinning force (Fpmax) is in 4 T (6400 MN/m3) for sample A and 5 T (8700 MN/m3) for sample A, Fig. 2b. The 5 T Fpmax is a good result for undoped MgB2 wires. Based on Kramer [29], the irreversible magnetic field (Birr) was 15.2 T for sample A and 16.3 T for sample B (Fig. 3). Analysis of Dew-Hughes in Fig. 4 shows that for sample A, Fp/Fpmax equals 1 is in B/Birr = 0.27, meaning that point dominant pinning mechanism is in ranges from 0 to 0.27, shifting first to surface pinning and then to volume above 0.27. For sample B, Fp/Fpmax equals 1 is in B/Birr = 0.32 (Fig. 4), showing that point dominant pinning mechanism is in ranges from 0 to 0.32 and above 0.32 dominant pinning mechanism shifts first to surface and then to volume. Based on SEM images (Fig. 1), we can conclude that Mg grains of smaller thickness correspond to higher Jc for reaction heat treatments at low temperatures (650 °C).
Critical current density, magnetic field dependency, and n value all are important parameters of a superconductor for the design of coil or magnet using them. The n value parameter describes the quality of the transition of the superconducting material from the superconducting state to the resistive state. In addition, n value influences the selection of the operating current for designing a superconducting coil [17]. In this paper, engineering critical current density (Jec) is the critical current density (Jc) divided by the cross-sectional area of the wire. Currently, applications of superconducting wire should have the engineering critical current density of about 100 A/mm2 and n value of 20 [17]. Measured n values for sample A and B is shown in Fig. 5. Sample A annealed at 650 °C for 60 min with 1 GPa pressure obtained an n value of 20 and Jc of 1600 A/mm2 (240 A/mm2 Jec) at 4 T; sample B annealed with the same parameters had a n value of 20 and Jc of 1260 A/mm2 (Jec—318 A/mm2 Je) at 6 T. Parizh et al. indicated that for n value of 20, the operating current of a superconducting coil would be set to 50% of the critical current [17].
Figure 5 shows the dependencies of n value with both current density Jc and applied field B. The relationship between n value and B indicates that the reduction of the MgB2 wire diameter significantly increases n value in low and middle magnetic fields. It should be recalled that critical current density depends on pinning center density and that the pinning centers are activated by the external magnetic field [14]. Gajda et al. indicated that different types of pinning centers strongly pin the vortex lattice in different ranges of magnetic field [33]. Calculations carried out using the CMF [34] method for sample B with an n value of 20 indicate that the B/Birr (6 T/16.5 T) coefficient is 0.36. This B/Birr coefficient value indicates dominant point pinning centers. On the other hand, calculations for sample C show that the B/Birr coefficient is 0.26 for an n value of 20, meaning that dominant mechanism is surface pinning. Dew-Hughes analysis shows that the reduction of the wire diameter leads to the change of the dominant pinning mechanism. On this basis, it can be deduced that the n value increase in a MgB2 wire with sized to 0.64 mm was a result of a high density of point pinning centers being obtained.
The n value-Jc relationship indicates that the reduction of the MgB2 wire diameter does not influence n value. This indicates that the same pinning force (Fp) is present in both samples A and B. However, Dew-Hughes, SEM, and CMF analysis [34] indicate that the Jc in sample B was created by mainly pinning point centers. On the other hand, the Jc in sample A was formed by mainly surface pinning centers. This difference can only be determined when analyzing n value and Jc in relation to the magnetic field.
4.2 Annealing Temperature (Ta) from 680 to 730 °C by 15 min
Figure 6a, c, and e show that an increase of annealing temperature from 680 to 730 °C in MgB2 wires with a 0.84 mm diameter increases Jc by 50%. SEM results in Fig. 1 indicate that the higher annealing temperature (730 °C) of undoped MgB2 wires with a diameter of 0.84 mm produces a greater number of big and small voids (point and surface pinning centers) and increases the number of connections between grains. Therefore, the Jc for 0.84-mm-undoped MgB2 wires increases with increased annealing temperature. On the other hand, increasing the annealing temperature from 680 to 700 °C in 0.64-mm MgB2 wires reduces Jc by 40%. Increasing the annealing temperature further to 730 °C decreases Jc by 25% between 2 and 8 T and increases Jc by 25% above 8 T (Fig. 7). SEM pictures show that annealing at 730 °C of wires with a 0.64 mm diameter creates big voids, creating surface pinning centers and reducing the number of connections between grains, leading to a decrease in Jc. The improvement of Jc above 8 T in sample H indicates that the annealing temperature of 730 °C led to formation of high-field pinning centers, creating dislocations and strains. At 730 °C and 1 GPa, Mg is in a liquid state and B solid state. Large voids (Fig. 1) and strains (dislocations) are created, while Mg is in the liquid state. Increasing annealing from 680 to 730 °C for 0.84-mm wires significantly increases Fp in low and middle magnetic fields (Fig. 6b, d, and f), suggesting that the higher annealing temperature increased the number of surface and point pinning centers. In Fig. 6b, d, and f, increasing annealing from 680 to 730 °C for 0.64-mm wires significantly decreases Fp in low and middle magnetic fields and shifts Fpmax from 4 to 2.5 T, suggesting that the higher annealing temperature decreased the number of point pinning centers. The Kramer analysis [29] showed that increasing annealing from 680 to 730 °C in 0.84-mm wires increases Birr from 15.9 to 16.3 T and decreases Birr from 16.5 to 15.2 T in 0.64-mm wires. The Birr depends on the type and density of high-field pinning centers. In superconducting material, there are three types of high-field pining centers, e.g., dislocations, strains (e.g., substitution for C by B), and intra-grain precipitation [14]. Serquis et al. [21] showed that HIP process formed dislocations. This indicates that in our undoped MgB2 wires thermally treated under 1 GPa isostatic pressure, it mainly forms high-field pinning centers. On this basis, we can indicate that increase of the annealing temperature from 680 to 730 °C and the isostatic pressure of 1 GPa allows to increase the density of high-field pinning centers in undoped MgB2 wires of 0.84 mm diameter. However, an increase of the annealing temperature and the isostatic pressure of 1 GPa leads to a decrease in the density of high-field pinning centers in undoped MgB2 wires of the 0.64 mm diameter.
This same increase of annealing temperature for 0.64-mm wires causes a shift of maximum ratio Fp/Fpmax = 1 from B/Birr = 0.25 (680 °C) to 0.16 (730 °C) (Fig. 8), indicating that the increase of annealing temperature changes the dominant pinning mechanism from surface to volume (big voids) (Fig. 1). Our calculations and extrapolations for 0.84-mm-undoped MgB2 wire shows that these wires also have the surface dominant pinning mechanism. A longer annealing time (60 min), 700 °C annealing temperature, and 1 GPa isostatic pressure reduces Jc (e.g., 100 A/mm2 at 8.8 T for 0.84-mm wire and 100 A/mm2 at 7.2 T for 0.64 mm) (Fig. 9). Therefore, further studies with longer annealing time (e.g., 60 min) were not conducted for 700 °C and 1 GPa isostatic pressure.
The dependency of n value with B in Fig. 10 shows that increasing the annealing temperature from 700 to 730 °C for 0.84-mm-undoped MgB2 wires n value increases, e.g., to 30 at 700 °C, 5 T and 1129 A/mm2 (Jec—170 A/mm2), and to 45 at 730 °C, 5 T and 1407 A/mm2 (Jec—211 A/mm2). The results for sample F (0.64 mm) show that higher annealing temperature corresponded to a low n value (of 9 at 5 T and 750 A/mm2 (Jec—100 A/mm2)), indicating that wire diameter reduction, high annealing temperature, and 1 GPa high isostatic pressure significantly reduces n value. In Fig. 10 we see the reduction of wire diameter and high annealing temperature (700 °C) significantly reduces n value, e.g., sample E has n value of 50 at 1700 A/mm2 Jc, and sample F has n value of 20 at 1700 A/mm2 Jc. On the other hand, higher annealing temperature for 0.84-mm wires increases the n value, e.g., sample G has n value of 28 at 1000 A/mm2 Jc (150 A/mm2 Jec) and sample G has n value of 35 at 1000 A/mm2 Jc. Previously results indicated that Jc is dependent on the density of the pinning centers and that the pinning centers activate the external magnetic field [14]. Based on these assumptions, Dew-Hughes analysis and CMF method [34], it can be concluded that increasing the annealing temperature from 680 to 730 °C for 0.64-mm wires increases the surface pinning centers density and decreases the point pinning centers density, e.g., sample F with an n value of 20 has a B/Birr coefficient (3 T/15 T) of 0.2—this value indicates surface pinning [34], leading to a reduction of Jc and n value. For 0.84-mm wire samples, increasing the annealing temperature creates a higher density of point pinning centers, e.g., sample E has B/Birr coefficient of 0.38 with an n value of 20—this value indicates point pinning centers, which correspondingly increases Jc and n value.
Based on the results above, multi-sectional wind-and-react coils cannot be fabricated with wires of two different diameters. For example, a low annealing temperature of the coil would produce high current density and n value in the compensating coil windings and low critical current density and n value in the main coil. On the other hand, a high annealing temperature would produce high critical current density and n value in the main coil and low critical current density and n value in the compensation coil. In both cases a homogeneous distribution of the magnetic field in the coil would not be realized. We suggest a better method for fabricating multi-sectional superconducting coils. First the main coil made would be fabricated with unreacted wires of large diameter and annealed at a high temperature for producing high Jc and n value. Secondly, the compensating windings would be wound to the main coil and the combined coil set. These combined coil set will heat treated at a low temperature (e.g. 570 °C [35]) for producing high Jc and n value in the compensation coils. The low annealing temperature would not adversely affect the critical parameters of the main coil, because the already-formed ex situ MgB2 material has the high melting point above 900 °C [36].
5 The Conclusions
Our research shows that the rate of reaction in undoped MgB2 wires with 0.64 mm diameter is faster than the reaction rate in undoped MgB2 wires with 0.84 mm diameter. The faster reaction rates are associated with thinner Mg grains and high isostatic pressure during heat treatment. Moreover, low annealing temperatures (650 °C) for 0.64-mm wire, high isostatic pressure, and long annealing time (60 min) yield smaller grains and voids and an increased number of connection between grains, high MgB2 material density, very high Jc of 1000 A/mm2 at 6 T, Jec of 100 A/mm2 at 7 T, Birr, Fp high n values, and point dominant pinning mechanism. On the other hand, high annealing temperature (730 °C) with high pressure and short annealing time (15 min) produces large grains and voids; reduces the number of connections between grains; reduces the uniformity and density of the MgB2 material; and decreases Jc (1000 A/mm2 at 4 T with Jec of 100 A/mm2 at 5 T), n value, Fp, Birr, and surface dominant pinning mechanism. Critical parameters including n value are reduced in 0.84-mm wires with low annealing temperature and high isostatic pressure. However, a high annealing temperature significantly increases the critical parameters of MgB2 wires sized to 0.84 mm, suggesting that for the manufacturing of multi-sectional superconducting coils, the main coil should be fabricated first and should be annealed at a high temperature. The compensation coil would be fabricated after the main coil and heat treated at a low temperature, which will allow to maintain high magnetic field in both main and compensation coils. This coil manufacturing process will lead to improvements in the homogeneity of the magnetic field in multi-sectional coils. Our analysis of the relationship of n value with Jc and B showed that n value is significantly dependent on the type of pinning centers. Point pinning centers significantly increased n value in middle magnetic fields, whereas surface pinning centers significantly increased n value in low magnetic fields.
References
Uchiyama, D., Mizuno, K., Akao, T., Maeda, M., Kawakami, T., Kobayashi, H., Kubota, Y., Yasohama, K.: Fibrous structure and critical current density of MgB2 superconducting wire. Cryogenics. 47, 282–286 (2007)
Wanga, Q.Y., Jiao, G.F., Liu, G.Q., Xiong, X.M., Yan, S.C., Zhang, P.X., Sulpice, A., Mossang, E., Feng, Y., Yan, G.: Fabrication and properties of multifilamentary MgB2 wires by in-situ powder-in-tube process. Physica C. 470, 1415–1418 (2010)
Gajda, D., Morawski, A., Zaleski, A.J., Häßler, W., Nenkov, K., Rindfleisch, M.A., Żuchowska, E., Gajda, G., Czujko, T., Cetner, T., Hossain, M.S.A.: The critical parameters in in-situ MgB2 wires and tapes with ex-situ MgB2 barrier after hot isostatic pressure, cold drawing, cold rolling and doping. J. Appl. Phys. 117, 173908 (2015)
Mroczek, Z., Morawski, A., Czujko, T., Karaboğa, F., Akdoğan, M., Zaleski, A.J., Małecka, M., Cetner, T., Yetiş, H., Gajda, D., Belenli, I.: Influence of the lamella structure and high isostatic pressure on the critical current density in in situ MgB2 wires without a barrier. J. Alloys Compd. 776, 636–645 (2019)
Susner, M.A., Daniels, T.W., Sumption, M.D., Rindfleisch, M.A., Thong, C.J., Collins, E.W.: Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in situ processed MgB2 strands. Supercond. Sci. Technol. 25, 065002 (2012)
Hu, H.L., Feng, Y., Yan, G., Li, C.S., Xu, Z.: Investigation of MgB2/Fe wires with different diameters. Supercond. Sci. Technol. 19, 1169–1172 (2006)
Ghorbani, S.R., Wang, X.L., Dou, S.X., Lee, S.I.K., Hossain, M.S.A.: Flux-pinning mechanism in silicone-oil-doped MgB2. Evidence for charge-carrier mean free path fluctuation pinning. Phys. Rev. B. 78, 184502 (2008)
Zeng, R., Dou, S.X., Lu, L., Li, W.X., Kim, J.H., Munroe, P., Zheng, R.K., Ringer, S.P.: Thermal-strain-induced enhancement of electromagnetic properties of SiC-MgB2 composites. App. Phys. Lett. 94, 042510 (2009)
Zhang, Y., Xu, X., Zhao, Y., Kim, J.H., Lu, C., Zhou, S.H., Dou, S.X.: Significant improvement of Jc in MgB2 bulk superconductor using ball-milled high-purity crystalline. Supercond. Sci. Technol. 21, 115004 (2008)
Wang, D., Ma, Y., Yu, Z., Gao, Z., Zhang, X., Watanabe, K., Mossang, E.: Strong influence of precursor on the critical current density of Fe sheathed MgB2 tape. Supercond. Sci. Technol. 20, 574–578 (2007)
Takahashi, M., Okada, M., Nakane, T., Kumakura, H.: The influence of magnesium grain size and ball milling time on the phase formation of MgB2 tapes. Supercond. Sci. Technol. 22, 125017 (2009)
Li S, Dou S. Intrinsic behaviour and properties of nanocrystalline MgB2. Studies in High Temperature Superconductors, Nova Science Publishers, Inc. (New York), chapter 5,146–157 (2006)
Serquis, A., Zhu, Y.T., Peterson, E.J., Coulter, J.Y., Peterson, D.E., Mueller, F.M.: Effect of lattice strain and defects on the superconductivity of MgB2. Appl. Phys. Lett. 79, 4399 (2001)
Gajda, D., Zaleski, A., Morawski, A., Hossain, M.S.A.: New types of high field pinning centers and pinning centers for the peak effect. Supercond. Sci. Technol. 30, 085011 (2017)
Li, C., Suo, H., Ma, L., Yang, L., Meda, M., Patel, D., Matsumoto, A., Kumakura, H.: Significant improvement in superconducting properties of in situ powder-in-tube MgB2 wires through anthracene doping and heat treatment optimization. Supercond. Sci. Technol. 32, 105004 (2019)
Vinod, K., Abhilash Kumar, R.G., Syamaprasad, U.: Prospects for MgB2 superconductors for magnet application. Supercond. Sci. Technol. 20, R1–R13 (2007)
Parizh, M., Lvovsky, Y., Sumption, M.: Conductors for commercial MRI magnets beyond NbTi: requirements and challenges. Supercond. Sci. Technol. 30, 014007 (2017)
Ghosh, A.K.: V–I transition and n-value of multifilamentary LTS and HTS wires and cables. Physica C. 401, 15–21 (2004)
Taylor, D.M.J., Hampshire, D.: Relationship between the n-value and critical current in Nb3Sn superconducting wires exhibiting intrinsic and extrinsic behaviour. Supercond. Sci. Technol. 18, 297–302 (2005)
Gajda, D., Morawski, A., Zaleski, A., Cetner, T., Małecka, M., Presz, A., Rindfleisch, M., Tomsic, M., Thong, C.J., Surdacki, P.: Comparison of critical current density in SiC-doped in situ MgB2 coils and straight wire samples processed by HIP. Supercond. Sci. Technol. 26, 115002 (2013)
Serquis, A., Civale, L., Hammon, D.L., Liao, X.Z., Coulter, J.Y., Zhu, Y.T., Jaime, M., Peterson, D.E., Mueller, F.M., Nesterenko, V.F., Gu, Y.: Hot isostatic pressing of powder in tube MgB2 wires. Appl. Phys. Lett. 82, 2847–2849 (2003)
Gajda, D., Morawski, A., Zaleski, A.J., Häßler, W., Nenkov, K., Małecka, M., Rindfleisch, M.A., Hossain, M.S.A., Tomsic, M.: Experimental research of high field pinning centers in 2% C doped MgB2 wires at 20 K and 25 K. J. App. Phys. 120, 113901 (2016)
Gajda, D., Zaleski, A., Morawski, A., Cetner, T., Thong, C.J., Rindfleisch, M.A.: Point pinning centers in SiC doped MgB2 wires after HIP. Supercond. Sci. Technol. 29, 115002 (2016)
Gajda, D., Morawski, A., Zaleski, A.J., Akdoğan, M., Yetiş, H., Karaboğa, F., Cetner, T., Belenli, I.: The influence of HIP process on critical parameters of MgB2/Fe wires with big boron grains and without barriers. J. Alloys Compd. 687, 616–622 (2016)
Tomsic, M., Rindfleisch, M., Yue, J., McFadden, K., Phillips, J., Sumption, M.D., Bhatia, M., Bohnenstiehl, S., Collings, E.W.: Overview of MgB2 superconductor applications. Int. J. Appl. Ceram. Techn. 4, 250 (2007)
Gajda, D., Morawski, A., Zaleski, A.J., Akdoğan, M., Yetiş, H., Karaboğa, F., Cetner, T., Belenli, I.: Formation of high-field pinning centers in superconducting MgB2 wires by using high hot isostatic pressure process. J. Supercond. Nov. Magn. 30, 3397 (2017)
Morawski, A., Cetner, T., Gajda, D., Zaleski, A.J., Häßler, W., Nenkov, K., Rindfleisch, M.A., Tomsic, M., Przysłupsk, P.: MgB2 wire diameter reduction by hot isostatic pressing—a route for enhanced critical current density. Supercond. Sci. Technol. 31, 075008 (2018)
Gajda, D., Zaleski, A.J., Morawski, A., Rindfleisch, M., Thong, C., Tomsic, M.: The electric field jump—detection of damaged Nb barrier in MgB2 wires annealed under pressure. Supercond. Sci. Technol. 28, 115003 (2015)
Xu, X., Kim, J.H., Hossain, M.S.A., Park, J.S., Zhao, Y., Dou, S.X., Yeoh, W.K., Rindfleisch, M., Tomsic, M.J.: Phase transformation and superconducting properties of MgB2 using ball-milled low purity boron. J. Appl. Phys. 103, 023912 (2008)
Shi, Z.X., Susner, M.A., Sumption, M.D., Collings, E.W., Peng, X., Rindfleisch, M., Tomsic, M.J.: Doping effect and flux pinning mechanism of nano-SiC additions in MgB2 strands. Supercond. Sci. Technol. 24, 065015 (2011)
Li, G.Z., Yang, Y., Susner, M.A., Sumption, M.D., Collings, E.W.: Critical current densities and n-values of MgB2 strands over a wide range of temperatures and fields. Supercond. Sci. Technol. 25, 025001 (2012)
Yamada, H., Igarashi, M., Nemoto, Y., Yamada, Y., Tachikawa, K., Kitaguchi, H., Matsumoto, A., Kumakura, H.: Improvement of critical current properties of in situ powder-in-tube-processed MgB2 tape by hot pressing. Supercond. Sci. Technol. 23, 045030 (2010)
Gajda, D.: Analysis method of high-field pinning centers in NbTi wires and MgB2 wires. J. Low Temp. Phys. 194, 166–182 (2019)
Gajda, D., Zaleski, A.J., Morawski, A.J., Haßler, W., Nenkov, K., Rindfleisch, M.A., Hossain, M.S.A.: Pinning mechanism and engineering critical current density considerations in the design of MgB2 superconducting coils. Physica C. 570, 1353606 (2020)
Gajda, D., Morawski, A., Zaleski, A.J., Cetner, T., Häßler, W., Nenkov, K., Małecka, M., Rindfleisch, M.A., Tomsic, M.: Significant enhancement of the critical current of MgB2 wires through a reduction of the diameter using HIP method. Scr. Mater. 143, 77–80 (2018)
Fujii, H., Togano, K., Ozawa, K.: Grain coupling and critical current density in Fe-sheathed carbon-substituted MgB2 tapes fabricated through an ex situ process using chemically treated powder. Supercond. Sci. Technol. 21, 095018 (2008)
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gajda, D., Zaleski, A.J., Morawski, A. et al. The Optimization of Jc, Birr, n value, Wires Diameter, and Research of the Dominant Pinning Mechanism for Applications of Undoped MgB2 in Superconducting Multi-section Coils. J Supercond Nov Magn 33, 3717–3725 (2020). https://doi.org/10.1007/s10948-020-05663-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-020-05663-3