Influence of La2O3 and Ce2O3 additions on structure and properties of aluminoborosilicate glasses

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

Aluminoborosilicate glasses with different amounts of La2O3 and Ce2O3 were prepared respectively by the conventional melting-quenching method. The structure, thermal property parameters and dielectric property parameters were investigated by Fourier-Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry and the impedance analyzer. Results from FTIR displayed that the degree of polymerization increased first and then fell down with the addition of La2O3, and reached the maximum value when the amount was 0.5 mol%. Meanwhile, the degree of polymerization of glasses doped with Ce2O3 arrived at the largest as the content of Ce2O3 reached 2.0 mol%. The thermal stability of glasses doped with La2O3 got enhanced first and then deteriorated, and reached the maximum when the content was 0.5 mol%; Meanwhile, the glasses doped with Ce2O3 also fluctuated a little. The dielectric constant (ε) and dielectric loss (tan α) of the samples fell down as the frequency increased. The ε and tan α of the samples doped with La2O3 reached the minimum value when the amount got to 0.5 mol%; The ε of the glasses doped with Ce2O3 turned minimum when the amount was zero, but the tan α was the smallest when the amount reached 1.0 mol%.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  1. I.J. Choi, S.C. Yong, J. Electroceram. 23, 185 (2009)

    Article  Google Scholar 

  2. S. Kerisit, J.V. Ryan, E.M. Pierce, J. Non-Cryst. Solids 378, 273 (2013)

    Article  Google Scholar 

  3. P. Lin, G. Zhao, Y. Hao, J. Wang, W. Weng, G. Han, J. Chin. Ceram. Soc. 35, 856 (2007)

    Google Scholar 

  4. N. Ollier, T. Charpentier, B. Boizot, G. Wallez, D. Ghaleb, J. Non-Cryst. Solids 341, 26 (2004)

    Article  Google Scholar 

  5. J. Wu, J.F. Stebbins, J. Non-Cryst. Solids 356, 2097 (2010)

    Article  Google Scholar 

  6. X. Zhang, Y. Yue, H. Wu, J. Mater. Sci. Mater. Electron. 24, 2755 (2013)

    Article  Google Scholar 

  7. M. Bengisu, R.K. Brow, E. Yilmaz, S.T. Reis, J. Non-Cryst. Solids 352, 3668 (2006)

    Article  Google Scholar 

  8. J.G. Wood, S. Prabakar, K.T. Mueller, C.G. Pantano, J. Non-Cryst. Solids 349, 276 (2004)

    Article  Google Scholar 

  9. M. Piotrowicz, D. Cianciara XXIst International Congress on Glass (ICG 2007), vol 49 (2011, p. 192)

  10. A. Quintas, O. Majérus, D. Caurant, J.L. Dussossoy, P. Vermaut, J. Am. Ceram. Soc. 90, 712 (2007)

    Article  Google Scholar 

  11. J. Marchi, D.S. Morais, J. Schneider, J.C. Bressiani, A.H.A. Bressiani, J. Non-Cryst. Solids 87, 863 (2005)

    Article  Google Scholar 

  12. D. Caurant, A. Quintas, O. Majérus, T. Charpentier, I. Bardez, Adv. Mater. Res. 39–40, 19 (2008)

    Article  Google Scholar 

  13. S.V. Smiljanić, S.R. Grujić, M.B. Tošić et al., Ceram. Int. 40, 297 (2014)

    Article  Google Scholar 

  14. P. Lu, Y. Zheng, J. Cheng, D. Guo, Ceram. Int. 39, 8207 (2013)

    Article  Google Scholar 

  15. N.S. Rao, L.S. Rao, Y. Gandhi, N. Veeraiah, V. Ravikumar, Phys. B 405, 4092 (2010)

    Article  Google Scholar 

  16. S.M. Lu, X.M. Yuan, X.H. Zhang, Y.J. Cui, H.T. Wu, Y.L. Yue, Adv. Mater. Res. 710, 127 (2013)

    Article  Google Scholar 

  17. X.H. Zhang, Y.L. Yue, H.T. Wu, Surf. Rev. Lett. 19, 1250062 (2012)

    Article  Google Scholar 

  18. Y. Ni, C. Lu, Y. Zhang, Q. Zhang, Z. Xu, J. Rare Earths 25, 94 (2007)

    Article  Google Scholar 

  19. J. Wu, J.F. Stebbins, J. Non-Cryst. Solids 362, 73 (2013)

    Article  Google Scholar 

  20. W. Mozgawa, M. Król, J. Dyczek, J. Deja, Spectrochim. Acta A 132, 889 (2014)

    Article  Google Scholar 

  21. Q. Zheng, M. Potuzak, J.C. Mauro, M.M. Smedskjaer, R.E. Youngman, Y. Yue, J. Non-Cryst. Solids 358, 993 (2012)

    Article  Google Scholar 

  22. N.I. Ya-Ru, L.U. Chun-Hua, Y. Zhang, Q.T. Zhang, X.U. Zhong-Zi, J. Mater. Sci. Eng. 24, 858 (2006)

    Google Scholar 

  23. A. Quintas, O. Majérus, M. Lenoir, D. Caurant, K. Klementiev, A. Webb, J. Non-Cryst. Solids 354, 98 (2008)

    Article  Google Scholar 

  24. E. Malchukova, B. Boizot, G. Petite, D. Ghaleb, J. Non-Cryst. Solids 354, 3592 (2008)

    Article  Google Scholar 

  25. Q. Zheng, M. Potuzak, J.C. Mauro, M.M. Smedskjaer, R.E. Youngman, Y. Yue, J. Non-Cryst. Solids 358, 993 (2012)

    Article  Google Scholar 

  26. A.A. Alemi, H. Sedghi, A.R. Mirmohseni, V. Golsanamlu, Bull. Mater. Sci. 29, 55 (2006)

    Article  Google Scholar 

  27. W. Soppe, C.V.D. Marel, W.F.V. Gunsteren, H.W.D. Hartog, J. Non-Cryst. Solids 103, 201 (1988)

    Article  Google Scholar 

  28. W.W. Wang, Y.L. Yue, H.T. Zhang, Mater. Technol. 28, 370 (2013)

    Article  Google Scholar 

  29. I. Dyamant, E. Korin, J. Hormadaly, J. Non-Cryst. Solids 354, 3135 (2008)

    Article  Google Scholar 

  30. F. He, Q. Zhou, J. Xie, Q. Zhang, Ceram. Int. 41, 3449 (2015)

    Article  Google Scholar 

  31. P.A. Bingham, R.J. Hand, S.D. Forder, Mater. Res. Bull. 41, 1622 (2006)

    Article  Google Scholar 

  32. H.A. Abo-Mosallam, H.C. Park, Mater. Lett. 72, 137 (2012)

    Article  Google Scholar 

  33. A. Arora, K. Singh, O.P. Pandey, Int. J. Hydrogen Energy 36, 14948 (2011)

    Article  Google Scholar 

  34. A. Arora, A. Goel, E.R. Shaaban, K. Singh, O.P. Pandey, J.M.F. Ferreira, Phys. B 403, 1738 (2008)

    Article  Google Scholar 

  35. N.O. Dantas, W.E.F. Ayta, A.C.A. Silva, N.F. Cano, S.W. Silva, P.C. Morais, Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 81, 140 (2011)

    Article  Google Scholar 

  36. S. Nakayama, T. Watanabe, T. Asahi, Ceram. Int. 36, 2323 (2010)

    Article  Google Scholar 

  37. B.S. Prakash, K.B.R. Varma, J. Solid State Chem. 180, 1918 (2007)

    Article  Google Scholar 

  38. X. Zhang, Z. Du, H. Wu, Y. Yue, Surf. Rev. Lett. 20, 1350030 (2013)

    Article  Google Scholar 

Download references

Acknowledgments

This work is supported by Natural Science Foundation of Shandong Province (No. ZR2012EMM019), Natural Science Foundation (Nos. 51172093, 51042009).

Author information

Authors and Affiliations

  1. School of Materials Science and Engineering, University of Jinan, Jinan, 250022, China

    Yadong Lu, Hongting Liu, Ya Qu, Hao Lu & Yunlong Yue

  2. Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, University of Jinan, Jinan, 250022, China

    Yunlong Yue

  3. Nanjing Fiberglass Research and Design Institute, Nanjing, 210012, China

    Sanxi Huang

Authors
  1. Yadong Lu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Hongting Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ya Qu
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Hao Lu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Sanxi Huang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Yunlong Yue
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Yunlong Yue.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Lu, Y., Liu, H., Qu, Y. et al. Influence of La2O3 and Ce2O3 additions on structure and properties of aluminoborosilicate glasses. J Mater Sci: Mater Electron 28, 2716–2722 (2017). https://doi.org/10.1007/s10854-016-5850-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-016-5850-1

Keywords

Search

Navigation