Abstract
The cubic C15 CaAl2 Laves phase is an important brittle intermetallic precipitate in ternary Mg–Al–Ca structural alloys. Although knowledge of the mechanical properties of the co-existing phases is essential for the design of improved alloys, the fracture toughness of the C15 CaAl2 intermetallic has not yet been studied experimentally due to limitations posed by macroscale testing of defect-free specimens. Here, miniaturised testing techniques like micropillar splitting and microcantilever bending methods are used to experimentally determine the fracture toughness of the CaAl2 Laves phase. It is found that the toughness value of ~ 1 MPa·√m obtained from pillar splitting with a sharp cube corner geometry is largely insensitive to sample heat treatment, the ion beam used during fabrication, micropillar diameter, and surface orientation. From correlative nanoindentation and electron channelling contrast imaging supported by electron backscatter diffraction, fracture is observed to take place mostly on {011} planes. Atomistic fracture simulations on a model C15 NbCr2 Laves phase showed that the preference of {011} cleavage planes over the more energetically favourable {111} planes is due to lattice trapping and kinetics controlling fracture planes in complex crystal structures, which may provide insights into the experimental results for CaAl2. Using rectangular microcantilever bending tests where the notch plane was misoriented to the closest possible {112} cleavage plane by ~ 8° and the closest {001}, {011}, and {111} planes by > 20°, a toughness of ~ 2 MPa·√m was determined along with the electron microscopy observation of significant deviations of the crack path, demonstrating that preferential crystallographic cleavage planes determine the toughness in this material. Further investigation using pentagonal microcantilevers with precise alignment of the notch with the cleavage planes revealed similar fracture toughness values for different low-index planes. The results presented here are the first detailed experimental study of fracture toughness of the C15 CaAl2 Laves phase and can be understood in terms of crack plane and crack front-dependent fracture toughness.
Graphical Abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Laves phases are amongst the most common intermetallic phases and are frequently present in metallic alloys as nano- to microscale inclusions. These tetrahedrally close-packed intermetallic phases either have a cubic (C15, MgCu2 type) or hexagonal crystal structure (C14 MgZn2 type, or C36 MgNi2 type) [1]. They are generally hard and brittle, and therefore, their presence largely determines the response of engineering materials to deformation [2]. Laves phase intermetallics can influence the overall deformation of metallic alloys in various ways—by acting as reinforcement to enhance strength, undergo cracking and decohesion with the metal interface, thereby controlling failure, or even exhibit plasticity and co-deformation by slip transfer with the surrounding metal [3, 4]. In aluminium and magnesium alloys, the cubic C15 CaAl2 Laves phase is often present. In the Mg-based alloy AZ31, for example, the CaAl2 Laves phase has been demonstrated to promote grain refinement during alloy processing [5]. The precipitation of Laves phases can be favourable to improve the strength of Mg alloys [6], as mentioned above. In particular, CaAl2 is known to be deformable, and precipitation of this phase is often considered attractive due to the action of the inclusions in impeding dislocation motion leading to strong hardening [6, 7]. This is of particular importance for highly formable Mg–Al–Ca alloys, which currently attract attention due to the non-rare-earth combination of Al and Ca promoting 〈c + a〉 dislocation plasticity in Mg when in solid solution, while suppressing twin formation [8]. CaAl2 precipitates have recently been shown to plastically deform via full and partial dislocations (the latter leaving stacking faults), relieving interfacial stress concentrations at the Mg matrix and improving tensile elongation in a Mg–Al–Ca alloy [6].
Despite these useful properties, there is limited understanding of the room-temperature fracture behaviour of the CaAl2 Laves phase, and few studies on the deformation behaviour of Laves phases in general [9]. Since most other Laves phases are brittle at room temperature, it is crucial to determine the fracture toughness of the CaAl2 intermetallic for an improved understanding of the mechanical response of co-existing phases in Mg–Al–Ca alloys. As most readily available as precipitates on nano- to micrometre length scales, there is an inherent difficulty in extracting their intrinsic mechanical properties from these inclusions. For determination of the critical resolved shear stress (CRSS) of CaAl2, microcompression approaches harnessing focussed ion beam milling of micropillars have recently been extended to precipitates in a Mg–Al–Ca alloy [7], where a CRSS of 164.9 MPa was determined for the {111}〈1–10〉 slip system. For determination of the fracture toughness, however, larger specimens > 10 µm are generally required to accommodate the processing of a pre-fabricated defect (usually a sharp notch) and the formation of a KI-dominated stress field under the defect, dimensions which far exceed the geometry of intermetallic inclusions. Moreover, sub-micron volumes of brittle material generally favour plastic deformation [10], suppressing an investigation of fracture.
A promising approach is to investigate bulk intermetallic samples. However, determining the fracture toughness of bulk-scale Laves phases is hindered by significant concentrations of pre-existing cracks and defects. This makes classical macroscopic fracture toughness testing of a single-phase Laves phase sample practically impossible, since the production of defect-free single-phase material on a centimetre scale already poses a significant challenge [11]. Nevertheless, it is possible to comprehensively investigate the mechanical response of Laves phases by applying small-scale testing methods in large single Laves phase grains in bulk pieces. In studying plasticity, Zehnder et al. investigated the C14 CaMg2 Laves phase through micropillar compression [12], which was recently extended to compression to 250 °C by Freund et al. on the same bulk C14 sample [13]. Furthermore, similar micropillar compression studies were recently performed on bulk single-phase C15 CaAl2 Laves phase specimens [14]. Bulk-scale diffusion couples are also a viable approach for studying the mechanical properties of Laves phases, including as a function of local chemistry. This was demonstrated by Luo et al. through nanoindentation and micropillar compression tests on the binary NbCo2 Laves phase, which exists in the three crystallographic structure variants C14, C15, and C36 depending on composition [15, 16]. By a similar approach, the fracture toughness was also determined for the NbCo2 Laves phases using focussed ion beam (FIB)-milled microcantilevers [17]. In that work, the authors determined that local composition affected the elastic modulus and hardness, but a constant fracture toughness value of ~ 4.2 MPa·√m was extracted for all three Laves phases irrespective of crystal structure and stoichiometry, with the notch plane for the C15 phase aligned along close-packed {111} planes.
As the fracture toughness of the C15 CaAl2 phase has not yet been studied experimentally, a comprehensive investigation of its toughness using micromechanical testing methods is presented here. A heat-treated cast material containing large grains of the CaAl2 Laves phase was fabricated, and the fracture toughness was investigated using both micropillar splitting and microcantilever testing techniques. Spherical nanoindentation allowed for a rationalisation of preferential fracture planes in this system, which was further supported by atomistic simulations on a model C15 Laves phase.
Materials and methods
Sample fabrication and surface characterisation
The intermetallic C15 CaAl2 specimen was cast into a cylindrical mould (size D15) to target a composition of 67 at.% Al and 33 at.% Ca. Granular elemental materials for Al (99.999% purity, HMW Hauner GmbH & Co. KG, Germany) and Ca (> 98.8% purity, Alfa Aesar, Germany—Lot no: 61200136) were used in sample preparation. The sample was then annealed at 600 °C under an argon atmosphere for 24 h to improve homogeneity, reduce residual stresses, and promote the target phase growth. Subsequently, the annealed material was cut into smaller pieces using electric discharge machining, and further analysis presented in this manuscript is for the cross-section of the cast cylindrical rod. Details of the sample surface preparation can be found in Ref. [18]. Imaging of the sample was performed in a Zeiss Auriga scanning electron microscope (SEM) at 10 kV primarily using both backscattered electron (BSE) and secondary electron (SE) detectors, while electron backscatter diffraction (EBSD) measurements were performed using the same machine at 20 kV and a step size of 0.3 µm with an EDAX TSL-OIM version 6.0 data acquisition system. The chemical composition was analysed using electron probe microanalysis (EPMA) on the metallographically prepared specimen. EPMA analysis was performed at an acceleration voltage of 10 kV, and the resulting chemical composition was averaged over 12 areas of interest per phase.
Nanoindentation
Nanoindentation using a commercial nanoindenter (G200, Brucker/KLA) was performed to determine the hardness and elastic modulus of the heat-treated intermetallic phase. A diamond Berkovich tip (Synton-MDP, Switzerland) was used with a constant indentation strain rate of 0.05 s−1, maximum indentation depth of 500 nm, and peak hold time of 2 s. The elastic modulus E and hardness H were determined using the Oliver–Pharr method [19]. Before performing the test, tip and instrument calibrations were performed on a fused silica reference sample. Spherical nanoindentation was performed using a diamond spherical counterbody with radius of 1 µm (Synton-MDP, Switzerland) into three grains of the annealed sample with distinct surface crystallographic planes, to a displacement target set-point of 500 nm. In each studied grain, five indents were performed using the G200 nanoindenter. The deformation zones, and particularly cracks around the indents, were characterised in a SEM (Zeiss MERLIN), by electron channelling contrast imaging (ECCI), using an accelerating voltage of 30 kV, a beam current of 2 nA, and a working distance of 7.5 mm. For the crack trace analysis, EBSD in conjunction with the ECCI was employed to reveal the crystallographic family of crack planes. The asymmetric domain method was employed to obtain Euler angles in each grain that reside in the same symmetric sub-set of orientation space [20]. Using a Mathematica© script [21], the obtained Bunge–Euler angles were used to generate crystallographic plane traces for the specific grains of interest.
Micropillar splitting
Micropillars were fabricated using an outer-to-inner pass milling procedure with a focussed ion beam (FIB) of both Ga (Zeiss Auriga) and Xe (ThermoFischer Helios PFIB) ions. The two ion sources were utilised to mill pillars in order to investigate ion damage effects on the obtained fracture toughness values. For 5 µm-diameter Ga+-FIB pillars, annular milling was performed using an acceleration voltage of 30 kV and probe current of 2 nA. The current was lowered to 600 pA for fine milling to reduce the impact of ion damage and re-deposition around the pillar. For the 10 µm pillars, a fine milling current of 2 nA was used. For Xe+-FIB pillars, a course milling current of 15 nA and a fine milling current of 1 nA were employed. Testing was performed using a commercial in situ nanoindentation device (ASMEC UNAT-II, Germany) installed in a Zeiss Gemini SEM. A diamond cube corner tip was used for these tests (Synton-MDP, Switzerland), and the measurements were taken in displacement control with 10 nm/s, and the tests stopped once failure was initiated.
Microcantilever bending
Rectangular and pentagonal microcantilevers for the bending experiments were milled with 30 kV and 2 nA current using the Ga+-FIB, while a final polishing step with 240 pA was used for each beam to remove any damaged material and redeposition. The dimensions of the rectangular beams were maintained at 15 µm length (L), 3 µm width (W), and 3 µm breadth (B). These dimensions are annotated on a SEM image of a microcantilever in Fig. 6b. Beams were milled in two different grains, four on an approximate (111) surface and two on a ~ (113) surface orientation, evaluated using EBSD prior to milling. Pentagonal beams were prepared in two different grains with surface orientation (1 1 10) and \(\left( {\overline{2}\;\overline{1}\;4} \right)\) targeting alignment of the crack plane with low-index planes in the C15 crystal structure. Final notching was achieved using a line scan applying 50 pA current for 30 s, for a targeted notch depth (a) equating to a ratio of a/W ≈ 0.3 (for rectangular cantilevers) or a/2c ≈ 0.3 (for pentagonal cantilevers, where c is the vertical distance between the top surface and the neutral plane). Testing was performed with the ASMEC in situ nanoindenter equipped with a diamond wedge indenter (length 10 µm, tip radius ~ 200 nm, Synton-MDP Switzerland). Tests were performed in displacement control mode with displacement rate of 5 nm/s. The distance between the notch and indenter contact was maintained at L = 12 µm (and L/W ~ 4) for rectangular beams and L = 11 µm for the pentagonal beams. Both load–time and displacement–time data were smoothed for noise using a Savitzky–Golay filter.
Atomistic simulations
Any atomistic simulations critically depend on the choice of the interaction potential. In particular, when studying fracture, care must be taken that the potential correctly reproduces the bonding situation around the highly stressed crack tip [22]. Initial fracture tests with a modified embedded atom method (M-EAM) potential for the Ca–Al system [23], which was successfully used for simulations of plasticity in CaAl2 [24], showed artificial phase transformations at the crack tip. Therefore, we performed all fracture simulations on a model NbCr2 C15 Laves phase, for which an EAM potential was specifically fitted to replicate crack advance [25]. The fracture toughness and lattice trapping range were determined following [26, 27]. The stress intensity factor KI was controlled by displacing all atoms according to the linear elastic anisotropic solution of a semi-infinite sharp crack under plane strain, mode I loading [28]. The atomically sharp crack thereby is located at the centre of a cylinder of radius R = 22 nm, with the x, y, and z directions aligned along the crack propagation, crack plane normal, and crack front directions, respectively. Atoms with a distance larger than R of 2 nm from the centre are fixed, and periodic boundary conditions are applied along the z (crack front) direction. After minimisation by the FIRE algorithm [29], the load is increased in increments of \(\Delta {K}_{I}\)= 0.005 MPa·√m and again minimised in an iterative process until the crack advances, which determines the critical load or atomistic fracture toughness value \({K}_{IC}\). All molecular statics simulations are performed using the Large-scale Atomic/Molecular Massively Parallel Simulator (LAMMPS) [30], and OVITO [31] was used for analysis and visualisation.
Results and discussion
Microstructural and chemical characterisation
The microstructure of the as-cast material exhibited significant compositional gradients and a large number of cracks and defects as observed by EPMA and SEM (for a representative SEM image, see Supplementary Information Fig. S1a). After annealing at 600 °C for 24 h, the initial defect structure of the material was significantly improved (Fig. S1b), and chemically homogeneous equilibrium phase(s) were obtained. The BSE image of Fig. 1a shows the annealed microstructure with the matrix phase having typical grain sizes > 100 µm and with a small volume fraction of a second phase precipitated along the grain boundaries. EPMA analyses confirmed the matrix phase to be the CaAl2 Laves phase, while the grain boundary phase was found to be CaAl4. EBSD showed the matrix phase to be cubic C15 CaAl2 as was confirmed by comparing with data from a crystal structure database [32]. No textural preferences were observed, and grains extended towards the surface of the cylindrical cast piece. Microgeometries for small-scale fracture toughness testing were next prepared on the specimen surface. Positions for nanoindents were selected, and sets of micropillars and microcantilevers were milled in grains of known orientation to control against variations in surface orientations of the polycrystal. The respective results are discussed in the following sections.
Nanoindentation
For purposes of materials characterisation, but also for the following fracture toughness analyses, the hardness and elastic modulus are required. From nanoindentation over several grains pre-characterised using EBSD, the average values for hardness and elastic modulus at 500 nm indentation depth were determined from 25 indents to be H = 5.8 ± 0.1 GPa and E = 110 ± 2 GPa, respectively. These values were found to be independent of the surface orientation. The collected load–displacement curves for the indents can be seen in Fig. S2, and they show excellent consistency between measurements. Also shown in Fig. S2 are exemplary SE images of Berkovich indents into the as-cast and annealed material, where some cracking could be observed in a small sub-set of indents mainly from the corners of the Berkovich geometry. Indentation using a diamond cube corner counterbody was also performed, with the aim of extracting nanoindentation fracture toughness estimates for the annealed C15 phase; however, significant damage was accumulated around the indent together with uneven and asymmetric crack lengths (Fig. S3), inappropriate for toughness evaluation.
Micropillar splitting
To investigate the fracture toughness, a micropillar splitting technique was utilised on pillars with an aspect ratio (height/diameter) maintained at ~ 1.0. As discussed in the seminal work by Sebastiani et al. [33], such geometrical considerations ensure a relaxed residual stress state. The fracture toughness KC using pillar splitting can be determined as [33]:
The critical load Pc was determined from the load–displacement data collected during measurement, and the micropillar radius R was determined from SEM imaging of the final polished pillars. A gauge factor γ was determined using the ratio of the indentation elastic modulus (E) and hardness (H) from the Berkovich nanoindentation measurements of Section "Nanoindentation". Using linear fitting and evaluation based on the data set of γ against E/H reported in Ref. [34] for a cube corner indenter geometry, the gauge factor for the annealed CaAl2 phase was determined to be 0.8 for an E/H ratio of 19. This factor was used in the pillar splitting fracture toughness Eq. 1, and it was also found to be consistent for the as-cast material. This equation assumes an idealised, isotropic, elastic-perfect plastic material for the cohesive zone finite element simulations used to estimate instability loads from the micropillar radius and fracture toughness, along with no friction between the indenter and top of the pillar, and a plastic zone size small compared to the pillar diameter [33].
As a preliminary step, four 5 µm-diameter Ga+-FIB pillars were milled into the as-cast C15 Laves phase sample, and the fracture toughness was determined to be 1.22 ± 0.12 MPa·√m, independent of surface orientation. Pillars were observed to generally split evenly. Due to the significant number of defects observed in the as-cast material, however, the remainder of the fracture analysis of the C15 CaAl2 phase is based on the annealed bulk Laves phase.
Examining the effect of crystallographic orientation
In determining the fracture toughness of the annealed material, two different grain orientations were selected in which micropillars with a diameter of 5 µm were cut using a Ga+-FIB. These measurements allowed a comparison with the as-cast material, together with understanding whether there is an orientation dependence on the toughness from pillar splitting in the annealed material. A weak orientation dependence of the nanoindentation hardness has been previously reported for the hexagonal C14 NbCo2 Laves phase, while the hardness of cubic C15 NbCo2 appeared to be independent of orientation [16]. Load–displacement curves were collected from the splitting measurements (Fig. 2a), and post-mortem SE images for the 5 µm Ga+-FIB pillars are shown in Fig. 2b, c. For both tested grains, ideal three-way splitting was observed in the post-mortem images, with three cracks propagating from a single point underneath the indenter. The uniform cracking in all three directions of the pillars also suggests negligible anisotropy with respect to the indentation direction in pillar splitting, which is predominantly influenced by the complex stress state beneath the cube corner indenter. It is also noted that deviations in indent placement with respect to the pillar centre were within 10% of the pillar’s radius R, and no influence on the toughness from the indenter placement should therefore result, as has been demonstrated for pillar splitting of Si [35].
Using the gauge factor (γ) obtained through nanoindentation, the critical load PC, and the pillar radius R, the fracture toughness KC is evaluated applying Eq. 1. Average values of KC = 1.20 ± 0.17 MPa·√m for grain 1 (four pillars) and 1.23 ± 0.13 MPa·√m for grain 2 (four pillars) were obtained. These results indicate that orientation does not have an impact on the measured indentation-based fracture toughness tests in the present case, in line with our reported nanoindentation results of Section "Nanoindentation". It is also noted that the toughness values agree with the as-cast result of 1.22 ± 0.12 MPa·√m within a single standard deviation, indicating that the heat treatment did not have a notable effect on the intrinsic phase properties, but rather the bulk properties from a reduction of larger defects and minimisation of the CaAl4 skeleton phase.
Ion beam and size effects
A consideration for the toughness evaluation using micropillar splitting is ion beam damage effects from the Ga ions [35]. To understand whether the ion type used for the FIB milling had an impact on the fracture toughness, 5 µm pillars were milled using Xe+ ions instead of Ga. These pillars were milled in a single grain with orientation close to that of grain 1 in Fig. 2. Figure 3 presents the load–displacement curves, together with a post-mortem image of a 5 µm Xe+-FIB pillar. The load–displacement curves show a similar relation as for the Ga+-FIB pillars in Fig. 2a up to the point of fracture. Using the maximum loads obtained from the load–displacement curves, an average fracture toughness of 1.08 ± 0.15 MPa·√m results from the eight pillars successfully tested. This value lies within the standard deviation of both sets of Ga+-FIB pillars, confirming that the choice of ions used for the FIB milling process did not have a significant impact on the fracture toughness values obtained using the pillar splitting technique.
Further, pillars of 10 µm diameter were fabricated to rule out size effects on the obtained fracture toughness values, using both Ga+- and Xe+-FIB sources. Figure 4 shows load–displacement curves and post-mortem images of 10 µm pillars fabricated using both FIB machines. In both cases, an ideal three-way split was seen, and the maximum loads were reasonably constant. The fracture toughness of the 10 µm Ga+-FIB pillars was determined as 1.02 ± 0.15 MPa·√m, while the 10 µm Xe+-FIB pillars had a toughness of 0.97 ± 0.20 MPa·√m. These values also fall within the standard deviation of the previous results on 5 µm pillars. However, the mean value drops by about 20% for the 10 µm Ga+-FIB pillars and about 10% for the 10 µm Xe+-FIB pillars as compared to the 5 µm pillars discussed previously. Such a reduction in toughness with increasing pillar diameter is consistent with observations for Si pillars, where at ca. 10 µm pillar diameter, the toughness values stabilised [35]. This has been put down to FIB damage effects for smaller pillars, but interactions of the plastic zone with the pillar outer perimeter could also result in artificial toughening. Considering this, the impact of measurement artefacts on the fracture toughness for the C15 CaAl2 Laves phase is negligible as the pillar size increases to 10 µm.
In combining the micropillar splitting results, it is clear that only minor variability exists between the cases tested (Table 1). It is possible that for the 5 µm pillars, ion beam damage and plastic zone considerations artificially elevated the toughness measured. However, the results are within a single standard deviation. This indicates that the ion beam used during FIB preparation, pillar diameter, and micropillar orientation have negligible effects on the evaluated KC from pillar splitting with a diamond cube corner counterbody. Comparing the results of the as-cast and the annealed sample, it can also be concluded that the annealing does not have a significant impact on the toughness of the C15 Laves phase at the microscale. Comparison with indentation-based fracture toughness measurements of other C15 Laves phases (such as NbCr2, NbCo2, etc. where KC is ~ 1 MPa·√m [25, 36, 37]) highlights that the toughness values lie in a similar range as those obtained for the C15 CaAl2 Laves phase by the pillar splitting technique (also an indentation-based fracture testing method).
Fracture plane analysis from spherical nanoindentation
Spherical nanoindentation was carried out on three grains with nominal surface planes of (3 2 6), (3 1 10), and (7 4 9) as marked in green, orange, and blue diffraction points, respectively, in the inverse pole figure of Fig. 5a. Spherical nanoindentation was performed to obtain a symmetrical stress distribution under the indent. The alignment of surface cracks in each of the grains is consistent in all five indents within the same grain. However, these directions differ between the grains. Figure 5b–d shows selected ECCI micrographs of indents in three selected grains with a consistent colour code. Cracks are marked with red arrows, while the white lines indicate surface plane traces for a selection of the {011} family. These traces were determined using a slip trace analysis done by an in-house developed Mathematica code. It must be noted that less than 5% of the cracks are aligned with {112} planes (an example is shown in Fig. S4), while > 95% of the cracks are aligned with {011} planes. The full planes are given in the pole figures of Fig. 5e–g, while the dots indicate the diffraction points from the surface of the grain. Evidently, the crack planes match very well with the generated plane traces corresponding to the {011} set, indicating a preferential plane for cleavage fracture. This is an intriguing result, as ab initio calculations of the surface energies and critical stress for C15 NbCr2 on (100), (110), and (111) cleavage planes show that the (111) plane has the lowest surface energy [38], although the toughness was not calculated. In the results of Fig. 5, however, it is found that the preferential cracking on {110} planes during spherical nanoindentation is largely insensitive to crystallographic orientation. Using the stress field of a spherical indenter in isotropic elasticity [39], the opening stresses on different crystallographic planes were calculated. This showed similarly no strong dependence on crystallographic orientation, with the {110} not being the most stressed planes (see Fig. S5 in the Supplementary Information). These findings are strong indications that {110} planes are the natural cleavage planes of C15 Laves phases.
Microcantilever bending experiments
While a phenomenological relationship between the critical load in pillar splitting and the fracture toughness exists, pillar splitting is not a true fracture mechanics test due to the lack of a pre-existing crack [40]. Experiments on notched microcantilevers allow for a comparison between the fracture toughness quantification from a mode I loaded pre-crack against those from pillar splitting. Moreover, such measurements allow to gain insights into fracture along pre-defined planes and directions, as well as into possible competition between different cleavage planes. First, a total of six beams were milled in two different grains, four in grain 1 with a ~ {111} surface and two in grain 2 with a ~ {113} surface orientation as indicated in the IPF shown in Fig. 6a. The crystallographic direction along the beam length L for both beams was not aligned with any of the low-index planes. Further details of the crystallographic orientation along different directions of the cantilevers and corresponding pre-cracks are given later in Table 3; Fig. 6b shows an SEM image of the notched cantilever beams. As all microcantilevers fail within the linear-elastic region of the deformation curve without showing plasticity (Fig. 6c), energy dissipation through plastic deformation is negligible. The fracture toughness for mode I loading can therefore be calculated according to the following equation [17]:
where Pc is the critical load where failure occurs, L is the distance between the notch and the point of load application using the wedge indenter, B is the thickness, and W is the width of the beam. The dimensions L, B, and W are depicted schematically in Fig. 6b. The dimensionless geometric factor f(a/W) was obtained using an approach for fracture toughness quantification described in detail by Matoy et al. [41]. Using Eq. 2, the fracture toughness of the cantilevers is 1.88 ± 0.45 MPa·√m for microcantilevers in grain 1 and 2.13 ± 0.38 MPa·√m for grain 2.
From Fig. 6d, it is observed that fracture did not proceed in a purely mode I manner; the fracture plane deviated from the notch plane and does not match any clear single crystallographic plane, as most prominently observed for grain 1. From calculations of the misorientation angle between the notch plane and low-index fracture planes (determined by the cross-product of the respective plane normals, shown in Table 2), the deviation could be analysed in detail. Orienting the post-mortem SEM micrographs edge-on and tilting at 45° allowed for a direct comparison of the calculated lowest misorientation crystal planes to the deviations of the crack path (Fig. 7).
For grain 1 (Fig. 7a, b), the fracture surface is closest to the \(\left( {1\;\overline{1}\;\overline{2}} \right)\) plane, which according to Table 2 has the least misorientation (8.4°) of the possible low-index planes. For grain 2 (Fig. 7c, d), fracture proceeds approximately in mode I, and the fracture surface does not align with any of the lowest misorientation projections. However, here, the lowest misorientation is 14.3° with the \(\left( {\overline{1}\;1\;2} \right)\) plane, and it is possible that the crack progresses through a combination of crack planes. The fracture surfaces of Fig. 7b, d appear smooth, and a detailed analysis of the crack trajectory is therefore not possible.
Additional fracture toughness tests were performed using pentagonal microbeams away from the sample edge, where the notch plane was aligned with two low-index crystallographic planes, {110} and {112}. The pentagonal beams were milled on two grains having different surface orientation for each of the low-index planes. The cantilevers with notch parallel to the \(\left( {\overline{1}\;1\;0} \right)\) plane were prepared in grain 3 with surface orientation of (1 1 10), whereas those parallel to the (121) plane were prepared in grain 4 with surface orientation of \(\left( {\overline{2}\;\overline{1}\;4} \right)\). Figure 8a shows such a pentagonal cantilever prior to testing inside the SEM, and the inset in the figures shows the pentagonal cross-section of the beams. The relevant dimensions are annotated in the figure. Figure 8b shows representative load–displacement curves for the two notch planes, and the IPF in the figure shows the corresponding grain orientations for the two sets of cantilevers. The load–displacement curve is linear, indicating that both sets of beams deformed in a linear-elastic manner, similar to the rectangular cantilevers in Fig. 6. This is further evident from the fracture surfaces of the two notch systems in Fig. 8c, d which show flat surfaces indicating brittle failure. However, no crystallographic facets can be observed. The fracture toughness of the pentagonal beams was determined using the following equation [17, 42]:
where \({P}_{c}\) is the maximum load where failure occurs and is determined from Fig. 8b, \(L\) is the distance between notch and the loading point, \(I\) is the moment of inertia of the cross-section of beam, and \(a\) is the notch depth determined from the fracture surfaces in Fig. 8c, d, while the distance \(c\) between top surface and neutral plane of the beam is computed according to Eq. 4 [17, 42, 43].
The geometric factor f(a/2c) for the pentagonal beam as computed by Chan et al. in Ref. [42] is given in Eq. 5:
The value of a/2c was ~ 0.3 and was similar to the a/W ratio of the rectangular beams. Using Eq. 3, a fracture toughness KIC, {110} = 1.80 and 1.89 MPa·√m is obtained for the two beams with {110} notch plane, and KIC, {112} = 1.87 and 2.17 MPa·√m is obtained for the two beams with {112} notch plane, both of which are similar to the toughness obtained earlier from rectangular cantilevers. It is worth mentioning that the cantilever geometry, i.e. rectangular or pentagonal cross-section, does not influence the linear-elastic fracture toughness values obtained, in alignment with Luo et al. for C15 NbCo2 [17]. The microcantilever results suggest that the fracture toughness of the C15 CaAl2 Laves phase does not vary significantly with notch plane orientation and is of the order of KIC = 2.0 ± 0.5 MPa·√m. This can be put into context with the fracture toughness of other C15 Laves phases such as NbCr2, for which KC ~ 1 to 2 MPa·√m has been reported [36, 44]. It needs to be emphasised, however, that due to experimental constraints, the study of specific crack systems characterised by both low-index crack plane and the crack front directions was not possible. It is well known that the cleavage process is anisotropic with respect to propagation direction within a specific cleavage plane. The influence of the propagation direction on the fracture toughness can have a similar magnitude to that of the crack plane [45, 46]. It seems unlikely but cannot be excluded that well-defined crack systems with lower fracture toughness do exist in the C15 CaAl2 Laves phase that have not been tested here. Table 3 summarises the microcantilever fracture toughness values of C15 CaAl2 obtained from rectangular and pentagonal beams, along with the corresponding crystallographic configuration of the notch plane in each case.
Insights from atomistic simulations
In the case of negligible plastic deformation, the theoretical fracture toughness according to Griffith KIG is related to the critical energy release rate GC, i.e. the change in elastic strain energy per unit area of crack advance, by:
where E* denotes an appropriate elastic modulus [40]. For brittle fracture, GC = γ1 + γ2, with γ1,2 being the energies of the two surfaces created by crack advance. Due to the different possible terminations of the {111} planes, these can be different in C15 Laves phases (see Fig. S7 in the Supplementary Information). With the material properties from Table S1,KIG can be calculated for different crack systems, including different terminations, for our C15 NbCr2 model system (Table 4), where it must be noted that the lattice constants vary to those of CaAl2. For CaAl2, KIG as determined from the DFT calculations in Ref. [38] is presented in Table S2. It can be clearly seen that {111} planes with the termination A (Table 4, Fig. S7) should have, in thermodynamic equilibrium, the lowest fracture toughness.
The critical fracture toughness \({K}_{\text{IC}}\) values obtained by direct K-controlled atomistic simulations are also shown in Table 4. All crack systems showed brittle cleavage without any indication of dislocation activity. Examples of crack tip configurations before and after crack advance (i.e. bond breaking) are shown in Fig. S8. In all cases, the atomistically determined \({K}_{\text{IC}}\) is larger than the corresponding KIG. In addition, \({K}_{\text{IC}}\) is now actually the lowest for {110} planes - in accordance with experimental observation of cracks along {110} planes instead of {111} plane during spherical nanoindentation.
The well known observations that atomistically determined KIC are, even for perfectly brittle fracture, larger than KIG are due to the fact that the latter is based on a thermodynamic treatment of fracture in terms of continuum properties and neglects the underlying atomic nature of the material [45, 46]. This effect is called lattice trapping and is determined by the forces required to break the bonds directly at the crack tip, i.e. by kinetics. An atomically sharp crack tip can remain stable until a load K+ larger than KIG is reached. This load is called the upper trapping limit. Similarly, a lower trapping limit K− < KIG exists, above which the crack will not heal [45]. The trapping range is defined as ΔK = K+/K− −1. The lattice trapping range can be quantified from the bonding distance-K plots where bonding distance is the distance between the bonds at the crack tip where the initial breaking occurs and K is the applied K field. An example of this plot is shown in Fig. S8a for two crack systems. As can be seen in Figs. S8a and S9a, the lattice trapping range is much larger for breaking the Nb–Cr crack tip bond for the (111)[11-2] and (112)[-110] crack systems than for the Cr–Cr crack tip bond in the (-110)[111] system (ΔK(110) = 0.04 < ΔK(111) = 0.19). As can be seen from Fig. S8b, crack propagation in the (-110)[111] system takes place by breaking only one bond. In contrast, for the (111)[11-2] system, the load at the crack tip is distributed amongst many bonds as shown by their relaxation after unloading by crack propagation. Similar behaviour can be observed for the (112) [-110] system as shown in Fig. S9b. This shows that the lattice trapping is intimately connected to the local crystal structure at the crack tip, and our results therefore are most likely valid for other C15 structures. Lattice trapping was already shown to be the underlying reason for the preference of (100) cleavage over cleavage on the lower-energy (110) planes in tungsten [46] and to influence the crack propagation direction in Si [45]. Lattice trapping is therefore also most probably the cause for the experimentally observed preference of the {110} fracture plane over the low-energy {111} cleavage plane in C15 CaAl2.
Conclusions
In this study, a detailed micromechanical analysis of fracture in bulk cast C15 CaAl2 Laves phase was performed. Annealing of the sample removed bulk-scale defects and led to improved handling of the sample for metallographic preparation and in situ nanomechanical testing. The indentation hardness and elastic modulus for the C15 phase were determined to be H = 5.8 ± 0.1 GPa and E = 110 ± 2 GPa, respectively.
Using micropillar splitting, values of ~ 1 MPa·√m were determined for the fracture toughness of pillars of 10 µm diameter, while effects of ion beam damage, pillar diameter, and crystal surface orientation were deemed negligible. For spherical indentation on three grain orientations, the {110} family of crystallographic planes consistently showed preferential fracture, and only a small number of cracks were observed on {112} planes. Fracture experiments using microcantilevers were inconclusive concerning quantitative differences in fracture toughness and fracture plane anisotropy. No crystallographic facets could be identified on the fracture surfaces. While a possible deviation of the crack plane towards a close-lying {112} plane was observed in a rectangular microcantilever, the fracture toughness values of cantilevers with {112} and {110} notch planes were indistinguishable. However, the crack front directions in these fracture tests could not be chosen to be parallel to special, low-index directions. Atomistic simulations showed clearly that {110} had the lowest lattice trapping, based on a model C15 NbCr2 potential, suggesting that the preference for cleavage along {110} planes observed during spherical nanoindentation is due to kinetic rather than energetic reasons (which would predict {111} cleavage planes).
The microcantilever results showed that the fracture toughness of the C15 CaAl2 Laves phase does not vary significantly with notch plane orientation and is of the order of KIC = 2.0 ± 0.5 MPa·√m. This value clearly deviates from the fracture toughness of KC = 1.0 ± 0.2 MPa·√m obtained from indentation-based pillar splitting (10 µm diameter, Xe+-FIB) through Eq. (1). Similar deviations between toughness values from indentation-based testing and microcantilever testing were reported for C15 NbCo2 Laves phase [17, 36, 37] and for tungsten carbide particles [47]. In contrast, the KC obtained from microcantilever bending and indentation-based pillar splitting for single-crystal Si(100) were in good agreement [48]. Such differences can be attributed to the inherently different assumptions of the two testing methods. In the indentation-based pillar splitting technique, it is reasoned that at the point of fracture instability, the cleavage planes are directly activated resulting from the complex 3D stress distributions present under the sharp cube corner indenter tip. Furthermore, it is speculated that few dislocations formed below the indenter tip during indentation, in the particular pile-ups needed to create the crack nuclei, can lead to anti-shielding (local stress enhancement) effects, meaning that the local stress intensity at the crack tip is much higher than from the far-field indenter loading. Such effects are not accounted for in elasto-plastically isotropic models such as those used to derive Eq. 1. Furthermore, the derivation of Eq. 1 in Ref. [31] does not consider the well known direction dependence of fracture toughness [44, 45]. While the semi-circular cracks in indentation-based techniques sample all propagation directions that lie in the fracture plane, cracks in microcantilever setups are restricted by the notch direction, i.e. a crack on the same plane could start propagating in a low-toughness direction and provide crack front kinks to the remaining semi-circular crack front at a lower stress intensity factor in indentation-based techniques as a crack with a given, arbitrary high-toughness crack front orientation in the microcantilever.
In conclusion, our results reveal that while the C15 CaAl2 Laves phase shows a low fracture toughness value around KIC = 2.0 ± 0.5 MPa·√m for arbitrary crack systems, kinetic effects like direction- and plane-dependent lattice trapping may play a role for this complex crystal structure and lead to a preference of {110} cleavage planes.
Data availability
Underlying data for this publication are available at https://doi.org/10.5281/zenodo.12183604.
References
Stein F, Leineweber A (2021) Laves phases: a review of their functional and structural applications and an improved fundamental understanding of stability and properties. J Mater Sci 56:5321–5427. https://doi.org/10.1007/s10853-020-05509-2
Zubair M, Sandlöbes S, Wollenweber MA et al (2019) On the role of Laves phases on the mechanical properties of Mg–Al–Ca alloys. Mater Sci Eng A 756:272–283. https://doi.org/10.1016/j.msea.2019.04.048
Medghalchi S, Zubair M, Karimi E et al (2023) Determination of the rate dependence of damage formation in metallic-intermetallic Mg–Al–Ca composites at elevated temperature using panoramic image analysis. Adv Eng Mater 25:2300956. https://doi.org/10.1002/adem.202300956
Guénolé J, Zubair M, Roy S et al (2021) Exploring the transfer of plasticity across laves phase interfaces in a dual phase magnesium alloy. Mater Des 202:109572. https://doi.org/10.1016/j.matdes.2021.109572
Jiang Z, Jiang B, Zhang J et al (2016) Effect of Al2Ca intermetallic compound addition on grain refinement of AZ31 magnesium alloy. Trans Nonferrous Met Soc China 26:1284–1293. https://doi.org/10.1016/S1003-6326(16)64229-2
Zhu G, Wang L, Wang J et al (2020) Highly deformable Mg–Al–Ca alloy with Al2Ca precipitates. Acta Mater 200:236–245. https://doi.org/10.1016/j.actamat.2020.09.006
Luo S, Wang L, Wang J et al (2022) Micro-compression of Al2Ca particles in a Mg–Al–Ca alloy. Materialia 21:101300. https://doi.org/10.1016/j.mtla.2021.101300
Sandlöbes S, Friák M, Korte-Kerzel S et al (2017) A rare-earth free magnesium alloy with improved intrinsic ductility. Sci Rep 7:10458. https://doi.org/10.1038/s41598-017-10384-0
Kumar KS (1996) Laves phase-based materials: microstructure, deformation modes and properties. MRS Proc 460:677–688. https://doi.org/10.1557/PROC-460-677
Korte-Kerzel S (2017) Microcompression of brittle and anisotropic crystals: recent advances and current challenges in studying plasticity in hard materials. MRS Commun 7:109–120. https://doi.org/10.1557/mrc.2017.15
Voß S, Stein F, Palm M, Raabe D (2010) Synthesis of defect-free single-phase bars of high-melting laves phases through modified cold crucible levitation melting. Mater Sci Eng A 527:7848–7853. https://doi.org/10.1016/j.msea.2010.08.066
Zehnder C, Czerwinski K, Molodov KD et al (2019) Plastic deformation of single crystalline C14 Mg2Ca Laves phase at room temperature. Mater Sci Eng A 759:754–761. https://doi.org/10.1016/j.msea.2019.05.092
Freund M, Andre D, Zehnder C et al (2021) Plastic deformation of the CaMg2 C14-Laves phase from 50–250°C. Materialia 20:101237. https://doi.org/10.1016/j.mtla.2021.101237
Freund M, Andre D, Sun PL et al (2023) Plasticity of the C15-CaAl2 laves phase at room temperature. Mater Des 225:111504. https://doi.org/10.1016/j.matdes.2022.111504
Luo W, Kirchlechner C, Zavašnik J et al (2020) Crystal structure and composition dependence of mechanical properties of single-crystalline NbCo2 Laves phase. Acta Mater 184:151–163. https://doi.org/10.1016/j.actamat.2019.11.036
Luo W, Kirchlechner C, Li J et al (2020) Composition dependence of hardness and elastic modulus of the cubic and hexagonal NbCo2 Laves phase polytypes studied by nanoindentation. J Mater Res 35:185–195. https://doi.org/10.1557/jmr.2019.384
Luo W, Kirchlechner C, Fang X et al (2018) Influence of composition and crystal structure on the fracture toughness of NbCo2 Laves phase studied by micro-cantilever bending tests. Mater Des 145:116–121. https://doi.org/10.1016/j.matdes.2018.02.045
Andre D, Freund M, Rehman U, Delis W, Felten M, Nowak J, Tian C, Zubair M, Tanure L, Abdellaoui L, Springer H, Best JP, Zander D, Dehm G, Sandlöbes-Haut S, Korte-Kerzel S (2022) Metallographic preparation methods for the Mg based system Mg–Al–Ca and its laves phases. Mater Charact 192:112187. https://doi.org/10.1016/j.matchar.2022.112187
Oliver WC, Pharr GM (1992) An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 7:1564–1583. https://doi.org/10.1557/JMR.1992.1564
Bieler TR, Alizadeh R, Peña-Ortega M, Llorca J (2019) An analysis of (the lack of) slip transfer between near-cube oriented grains in pure Al. Int J Plast 118:269–290. https://doi.org/10.1016/j.ijplas.2019.02.014
Tian C, Dehm G, Kirchlechner C (2021) Influence of strain rate on the activation of {110}, {112}, {123} slip in ferrite of DP800. Materialia 15:100983. https://doi.org/10.1016/j.mtla.2020.100983
Hiremath P, Melin S, Bitzek E, Olsson PAT (2022) Effects of interatomic potential on fracture behaviour in single- and bicrystalline tungsten. Comput Mater Sci 207:111283. https://doi.org/10.1016/j.commatsci.2022.111283
Jang H-S, Seol D, Lee B-J (2021) Modified embedded-atom method interatomic potentials for Mg–Al–Ca and Mg–Al–Zn ternary systems. J Magnes Alloy 9:317–335. https://doi.org/10.1016/j.jma.2020.09.006
Xie Z, Chauraud D, Atila A et al (2023) Unveiling the mechanisms of motion of synchro-Shockley dislocations in Laves phases. Phys Rev Mater 7:053605. https://doi.org/10.1103/PhysRevMaterials.7.053605
Rösch F, Trebin H-R, Gumbsch P (2006) Interatomic potentials and the simulation of fracture: C15 NbCr2. Int J Fract 139:517–526. https://doi.org/10.1007/s10704-006-0065-8
Andric P, Curtin WA (2018) Atomistic modeling of fracture. Model Simul Mater Sci Eng 27:013001. https://doi.org/10.1088/1361-651X/aae40c
Möller JJ, Bitzek E (2014) Fracture toughness and bond trapping of grain boundary cracks. Acta Mater 73:1–11. https://doi.org/10.1016/j.actamat.2014.03.035
Liebowitz H, Sih GC (1968) Mathematical theories of brittle fracture. Fracture 2:67–190
Guénolé J, Nöhring WG, Vaid A et al (2020) Assessment and optimization of the fast inertial relaxation engine (fire) for energy minimization in atomistic simulations and its implementation in LAMMPS. Comput Mater Sci 175:109584. https://doi.org/10.1016/j.commatsci.2020.109584
Thompson AP, Aktulga HM, Berger R et al (2022) LAMMPS—a flexible simulation tool for particle-based materials modeling at the atomic, meso, and continuum scales. Comput Phys Commun 271:108171. https://doi.org/10.1016/j.cpc.2021.108171
Stukowski A (2009) Visualization and analysis of atomistic simulation data with OVITO–the Open Visualization Tool. Modell Simul Mater Sci Eng 18:015012. https://doi.org/10.1088/0965-0393/18/1/015012
CaAl2 Crystal Structure: Datasheet from “PAULING FILE Multinaries Edition—2012” in Springer Materials (https://materials.springer.com/isp/crystallographic/docs/sd_0260702)
Sebastiani M, Johanns KE, Herbert EG et al (2015) A novel pillar indentation splitting test for measuring fracture toughness of thin ceramic coatings. Philos Mag 95:1928–1944. https://doi.org/10.1080/14786435.2014.913110
Ghidelli M, Sebastiani M, Johanns KE, Pharr GM (2017) Effects of indenter angle on micro-scale fracture toughness measurement by pillar splitting. J Am Ceram Soc 100:5731–5738. https://doi.org/10.1111/jace.15093
Lauener CM, Petho L, Chen M et al (2018) Fracture of Silicon: influence of rate, positioning accuracy, FIB machining, and elevated temperatures on toughness measured by pillar indentation splitting. Mater Des 142:340–349. https://doi.org/10.1016/j.matdes.2018.01.015
Liu CT, Zhu JH, Brady MP et al (2000) Physical metallurgy and mechanical properties of transition-metal Laves phase alloys. Intermetallics 8:1119–1129. https://doi.org/10.1016/S0966-9795(00)00109-6
Zhu JH, Pike LM, Liu CT, Liaw PK (1999) Point defects in binary laves phase alloys. Acta Mater 47:2003–2018. https://doi.org/10.1016/S1359-6454(99)00090-7
Li C, Wang B, Li Y, Wang R (2009) First-principles study of the ideal cleavage fracture of Cr2Nb microalloyed by X (Al, Ni Co, Ti). Intermetallics 17:394–399. https://doi.org/10.1016/j.intermet.2008.11.012
Johnson KL (1987) Contact mechanics. Cambridge University Press
Kanninen MF, Popelar CA, Saunders H (1988) Advanced fracture mechanics. J Vib Acoust Stress Reliab Des 110:419–420. https://doi.org/10.1115/1.3269540
Matoy K, Schönherr H, Detzel T et al (2009) A comparative micro-cantilever study of the mechanical behavior of silicon based passivation films. Thin Solid Films 518:247–256. https://doi.org/10.1016/j.tsf.2009.07.143
Chan H, Roberts SG, Gong J (2016) Micro-scale fracture experiments on zirconium hydrides and phase boundaries. J Nucl Mater 475:105–112. https://doi.org/10.1016/j.jnucmat.2016.03.026
Lubliner J, Papadopoulos P (2014) Introduction to solid mechanics: an integrated approach. Springer, New York
Ohta T, Nakagawa Y, Kaneno Y et al (2003) Microstructures and mechanical properties of NbCr2 and ZrCr2 Laves phase alloys prepared by powder metallurgy. J Mater Sci 38:657–665. https://doi.org/10.1023/A:1021807519728
Pérez R, Gumbsch P (2000) Directional anisotropy in the cleavage fracture of silicon. Phys Rev Lett 84:5347–5350. https://doi.org/10.1103/PhysRevLett.84.5347
Riedle J, Gumbsch P, Fischmeister HF (1996) Cleavage anisotropy in tungsten single crystals. Phys Rev Lett 76:3594–3597. https://doi.org/10.1103/PhysRevLett.76.3594
Ortiz-Membrado L, Cuadrado N, Casellas D et al (2021) Measuring the fracture toughness of single WC grains of cemented carbides by means of microcantilever bending and micropillar splitting. Int J Refract Metal Hard Mater 98:105529. https://doi.org/10.1016/j.ijrmhm.2021.105529
Jaya BN, Kirchlechner C, Dehm G (2015) Can microscale fracture tests provide reliable fracture toughness values? A case study in silicon. J Mater Res 30:686–698. https://doi.org/10.1557/jmr.2015.2
Acknowledgements
The authors gratefully acknowledge the financial support of the Deutsche Forschungsgemeinschaft (DFG) within projects B06 and A02 of the Collaborative Research Centre (SFB) 1394 “Structural and Chemical Atomic Complexity—from defect phase diagrams to material properties”—project number 409476157. Funding by the European Research Council (ERC) under the EU's Horizon 2020 Research and Innovation Programme is gratefully acknowledged by AG and EB (ERC Consolidator Grant, microKIc, Grant No. 725483). The C15 intermetallic was synthesised within Project S of SFB 1394, and Hauke Springer and Michael Kulse are acknowledged for preparation and heat treatment of the sample, along with Leandro Tanure from the IBF at the RWTH-Aachen University. We would like to further acknowledge Sandra Korte-Kerzel and Martina Freund from the Institute for Physical Metallurgy and Materials Physics at the RWTH-Aachen University for fruitful discussion. Martin Palm and Irina Wossack from MPIE are acknowledged for support during EPMA measurement and analysis, while Christoph Kirchlechner is finally acknowledged for development of the Mathematica script used for crack plane analysis.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interests
The authors declare that no conflict of interest or competing interests exist.
Additional information
Handling Editor: Zhao Shen.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Best, J.P., Kanjilal, A., Ghafarollahi, A. et al. Fracture of the C15 CaAl2 Laves phase at small length scales. J Mater Sci (2024). https://doi.org/10.1007/s10853-024-09887-9