Introduction

Melt blowing is one of industrial approaches for manufacturing nonwoven materials. Because of the fiber diameter produced by melt blowing is commonly in the range from about 1 μm to several micrometers, the melt-blown nonwoven materials have found a variety of advanced applications in areas of filtration, life science, medicine and industry [1, 2].

During melt-blowing process, the microfibers are manufactured by extruding a polymer melt through an orifice (a component of die), and attenuating the extrudate with a jet of high velocity hot air (see Fig. 1). Obviously, the air flow field plays a crucial role in fiber formation during melt blowing. Until now, the air flow fields in melt blowing have been researched mostly by methods of computational fluid dynamics (CFD) numerical simulation and experimental measurement. Shambaugh and his co-workers [3,4,5,6,7] have systematically numerical simulated the air flow fields in different kinds of die melt blowing, including slot die, annular die and swirl die. Their numerical simulations obtained the profiles of the whole air flow fields including the profiles of air velocity and temperature. Not only this, they have also experimental measured the air velocity and temperature below the die, using a Pitot tube and a thermocouples (or infrared thermometer), respectively [8,9,10,11]. However, for the limitation of Pitot tube, air velocities they measured were far below the industrial level, about velocity of sound [12]. Later, more advanced equipments with higher accuracy, such as hot-wire anemometer and laser Doppler velocimeter were applied to measuring the air flow fields [13,14,15,16], the maximum velocity they measured increased to be about 150 m s−1. It noted that the air flow fields all they have measured were described by average values, namely, the turbulent characteristic of air flow field was not provided.

Figure 1
figure 1

a Schematic of the process of slot-die melt blowing [21], b the structure of single-orifice slot die and, c the real single-orifice slot die used in this work. The configuration of the air channel is similar to the letter of ‘V,’ and this kind of die is also called V-slot die

Full size image

In commercial slot-die melt blowing, after the two streams of high velocity hot air are extruded out from the air channels of the die, they undergo the processes of converging, merging and combining (as shown in Fig. 2a) [17], illustrating that the air flow field in melt blowing has obvious characteristic of turbulence. Research group of Kumar and Bates [18,19,20,21,22] has done some theoretical and experimental work on the fiber formation, onset of fiber whipping and fiber breakup as well as utilizing an innovative Laval nozzle in melt blowing, their work had a significant contribution to the research on melt blowing, and they also mentioned that, in melt blowing, whipping-like motion of fiber was due to turbulent air [20]. Furthermore, the fiber motion in melt blowing can indirectly reflects the turbulent characteristic of air flow field. Vibration of fiber was firstly recorded by Shambaugh and his co-workers [23], at that time, a bundle of fibers appeared to be splaying rather than single fiber were captured. Bresee et al. [24,25,26] also devoted some experimental measurements to fiber motion using the equipment of high-speed photography. Xie and Zeng [27] discovered the fiber whipping motion in slot-die melt blowing, appeared to be a fiber path with two groups of loops moving downward. These revealed fiber vibration or whipping motion indirectly confirms that air flow field in melt blowing is turbulent flow. However, few published papers on turbulent air flow field in melt blowing have been found, Xie and Zeng [28] preliminarily measured the fluctuating air velocity in slot-die melt blowing by hot-wire anemometer, it was regretful that the characteristic of temperature was not provided.

Figure 2
figure 2

a The profile of air flow field in slot-die melt blowing which was obtained by CFD numerical simulation [29]. b Schematic of devices for measuring the air flow field in slot-die melt blowing. The anemometer probe was set below the die, c the structure of one-dimensional velocity probe used by previous researchers [14,15,16, 28], d the structure of two-dimensional probe used in the present work. It noted that the measurement of air flow field was taken in the absence of fiber. The air velocity and air temperature along z-axis were measured

Full size image

In the present work, our study still focused on discovering the characteristics of turbulent air flow field in slot-die melt blowing. Compared to the previous works [13,14,15,16, 28], innovations of researching turbulent air flow field in this work were: (1) an advanced two-dimensional velocity probe instead of one-dimensional velocity probe was applied in hot-wire anemometer for measuring the fluctuation of air velocity, (2) the fluctuation of air temperature was originally measured, which has not been reported until now, (3) the coupling effect between air velocity and temperature was also analyzed by processing the data of measurements.

Experiments and measurements

Melt-blowing setups and conditions

The measurement of the air flow field in this study was taken on the single-orifice melt-blowing device; Fig. 1a shows the schematic of single-orifice melt blowing. The structure of this single-orifice slot die is shown in Fig. 1b, this type of die is referred to as a blunt-edge with a nose piece width (f) of 1.28 mm, a slot angle (α) of 30°, and a slot width (e) of 0.65 mm, the orifice diameter for polymer melt was 0.42 mm. Figure 1c shows the real slot die used in this work. The details of this slot die can be found in Xie and Zeng [28]. The coordinate system used is also shown in Fig. 1a, all coordinates are relative to the die face. Its origin is at the center of the die face, the x direction is along the major axis of the nose piece and slots, whereas the y direction is transverse to the major axis of the nose piece and slots. The z direction is directed vertically downward.

Our previous work [27] online measured the fiber whipping motion in slot-die melt blowing for the gauge air pressure of 1.0 atm (All air pressures used in this work refer to gauge pressures.), in view of discovering the relationship of turbulent air flow field and fiber motion, therefore, an air pressure of 1.0 atm was chosen again for measuring the turbulent air flow field. It is worth noting that, although the air pressure of 1.0 atm was higher than those used in previous work [23,24,25,26], it was still lower than the air pressure used in commercial manufacturing. For example, nonwoven fibers with diameter of 18 μm could be produced with air pressure of 1.0 atm in this melt-blowing device, whereas the fiber diameter of the commercial nonwoven products was about 1–5 μm. For air temperature, the mean air temperature can be measured by the thermocouples with high accuracy, in this study, we focused on the fluctuation of the air temperature; therefore, a low and a medium initial air temperatures of 50 and 100 °C were applied in consideration of the limitation of the measuring equipment (hot-wire anemometer).

Measurements

Air velocity and temperature below the die were measured online with a hot-wire anemometer (Dantec StreamLine CTA90C10 and Dantec StreamLine CTA90C20, Dantec Dynamics, Skovlunde, Denmark) in the absence of the polymer stream, i.e., the polymer flow was stopped during measurements. Figure 2b shows the relative positions of the hot-wire anemometer and the melt-blowing die.

During using hot-wire anemometer for measuring air velocity, the melt-blowing air takes away the heat of the wire, the temperature of the wire is kept constant by applying voltage on it (The constant temperature of the wire is kept 220 °C higher than the ambient temperature, and the ambient temperature is 18 °C.). The corresponding air velocity can be calculated from the applied voltage by the following equation

$$ \frac{E}{{R_{\text{w}} }} = \left[ {\frac{{(R_{\text{w}} - R_{\text{f}} )(A + Bv^{1/2} )}}{{\alpha_{0} R_{\text{f}} R_{\text{w}} }}} \right] $$
(1)

where E is the heating voltage applied on the wire; Rw and Rf are the resistance of the wire at temperature of wire and air, respectively; A and B are constant numbers; v is the air velocity and α0 is the temperature coefficient of resistance.

Compared to one-dimensional velocity probe used in previous researchers [14,15,16, 28], a two-dimensional velocity probe was attempted for the velocity measurement in this work; Figs. 2c and 2d illustrate the structures of one-dimensional and two-dimensional velocity probe. The two-dimensional velocity probe is consisted of two systems of one-dimensional probes; each one-dimensional velocity probe has a metal wire with a 5-μm diameter and a 1.6-mm length suspended between two needle-shaped prongs. As shown in Fig. 2d, the two wires are placed in paralleled planes, the projection on y–z plane and x–z plane of the two wires is vertical and paralleled, respectively. Compared to one-dimensional velocity probe for measuring air velocity, two-dimensional probe has better stability, for the reason that the wire undergoes drastic and continual air flow during measurement, the junction of wire and the needle-shaped prongs or the wire itself probably become exfoliated or broken, resulting in incontinuity of measurement. However, if two-dimensional velocity probe is applied, the measurement will be suspended only in the case of the two wires are all disabled.

For the measurement of air temperature, a dedicated one-dimensional temperature probe (55P31) with a 1-μm diameter and a 1.2-mm length metal wire was used. The structure of this one-dimensional temperature probe is similar to the one-dimensional velocity probe shown in Fig. 2c. This temperature probe operates at temperatures up to 150 °C. Unlike the principle of velocity measurement, air temperature has linear relationship with applied voltage, namely

$$ T = C_{0} + C_{1} E $$
(2)

where T is the air temperature; C0 and C1 are coefficients and E is the voltage provided from the hot-wire anemometer.

During the measurements of air velocity and temperature, the corresponding velocity and temperature probe was positioned with a one-dimensional traversing system as shown in Fig. 2b, which permitted up or down motion along z-axis in 2-mm increments. It was found that during the measurements, although two-dimensional velocity probe was applied, the wires were easily broken when it was very close to the die; therefore, the minimum distance below the die was set to z = 6 mm.

Calibrations

Calibrations including velocity calibration and temperature calibration were accomplished on calibration device at ambient temperature of 18 °C, before formal measurements.

For velocity calibration, the calibration device provided air with different rated velocities blowing to the wire, the corresponding voltages applied on the wire to maintain its temperature were also been collected, and the rated velocities and voltages were fitted into quartic-polynomial-equation, i.e., velocity-calibration curve. Later, during the formal measurement, the air velocities could be calculated from the voltage signals according to the known velocity-calibration curve. Because each wire in the two-dimensional velocity probe had an independent electrical circuit, two velocity-calibration curves were obtained simultaneously after each velocity calibration. Figure 3a shows the calibration curves of the two wires in two-dimensional velocity probe, and the two curves are almost coincided; however, the existed no coincided points illustrate that the microstructure of the two wires are not completely uniform. The quartic-polynomial-equation for wire 1 and wire 2 is

$$ v = 0.00005E^{4} + 126.810379E^{3} - 691.024170E^{2} + 1417.843384E - 870.765686 $$
(3)
$$ v = 0.00007E^{4} + 152.901855E^{3} - 860.379089E^{2} + 1687.597290E - 1141.561890 $$
(4)
Figure 3
figure 3

a The velocity-calibration curves for the two wires in the two-dimensional velocity probe. b The temperature-calibration curve for the one-dimensional temperature probe

Full size image

For temperature calibration, the calibration air temperatures, T, were measured in advance by thermocouples, and the corresponding applied voltages, E, provided by hot-wire anemometer were also collected. Air temperatures, T, and the corresponding applied voltages, E, constitute the temperature-calibration curve, which is shown in Fig. 3b, and the linear equation for temperature calibration is

$$ T = 3.9094E - 5.2452 $$
(5)

Results and discussion

Fluctuation of velocity

The instantaneous velocities at points along z-axis were measured by the hot-wire anemometer. The instantaneous velocity can be expressed as the sum of the mean and fluctuating velocities, namely \( v_{t} = \overline{v} + v^{{\prime }} \). The instantaneous velocities, vt, at the points of z = 6, 50 and 100 mm as a function of time are shown in Fig. 4. A time segment of 0.2 s (from 0.5 to 0.7 s) was chosen for demonstration of the instantaneous velocity. Figure 4 shows that the instantaneous velocity signal is irregular, and the fluctuating velocity, v′, damps gradually as far away from the die (from z = 6 mm to z = 100 mm). Figure 5 illustrates the probability distribution of the instantaneous velocity in twenty velocity sections; information of the maximum and minimum velocities as well as standard deviation of instantaneous velocity are also included. Probability distribution presents unimodal distribution. Here, we build two parameters, |v′| and Δv, for representing the turbulent characteristics of velocity. |v′| is absolute value of fluctuating velocity, v′, which can represent the average intensity of the turbulence, Δv is the range of the instantaneous velocity, vt, which represents the amplitude changing of the instantaneous velocity. |v′| and Δv are described as

$$ \left| {v^{{\prime }} } \right| = \frac{{\sum\limits_{1}^{N} {\left| {v_{t} - \overline{v} } \right|} }}{N} $$
(6)

where vt and \( \overline{v} \) are the instantaneous and mean fluctuating velocities; N is the number of acquainted velocities in the time segment of 0.2 s.

Figure 4
figure 4

The instantaneous velocity, vt, at the points a z = 6 mm, b 50 mm and c 100 mm as a function of time, t

Full size image
Figure 5
figure 5

The probability distribution of the instantaneous velocity in twenty velocity sections for the positions of a z = 6 mm, b z = 50 mm and c z = 100 mm. These statistical results were obtained from Fig. 4. The δ is standard deviation of instantaneous velocity

Full size image
$$ \Delta v = \hbox{max} (v^{{\prime }} ) - \hbox{min} (v^{{\prime }} ) $$
(7)

Figure 6a shows the detailed evolution of the fluctuating velocity, |v′|, along z-axis. The maximum peak is at the point of z = 8 mm, where as locating below the position where the two air streams merged [17]. This reveals that the fluctuation of the air flow field continues increasing in the region where as several millimeters lag behind the merging point of the two air streams. It noted that an obvious second peak is located at the point of z = 14 mm, although the reason for the second peak cannot be explicated according to the present knowledge we have, we believe the second peak hides some special characteristics of turbulence in slot-die melt blowing. Figure 5b shows the evolution of Δv along z-axis, the velocity fluctuation is strong, for example, the maximum Δv = 185 m s−1 is at the point of z = 6 mm, and even if at the point of z = 100 mm, the Δv is still as large as 50 m s−1. The obvious large Δv plays a crucial role in inducing to the fluctuating attenuation of the fiber in melt blowing, resulting in deteriorating the evenness of the nonwoven fibers. In addition, there exists a second peak of Δv at the point of z = 14 mm which is interesting coincided with the point of the second peak of |v′| shown in Fig. 6a, we predict that, there may exist a steady vortex at the position near the point of z = 14 mm. The fiber whipping motion in slot-die melt blowing discovered by our previous work [27] via high-speed photography appeared to be a fiber path with two groups of loops moving downward (see Fig. 7), the generation of the left–right alternating loops was accomplished coincidently in the region near the point of z = 14 mm. It illustrates that the characteristic of turbulent air flow field has obvious effect on fiber formation during melt-blowing process.

Figure 6
figure 6

The evolutions of a the fluctuating velocity, |v′|, and b the range of instantaneous velocity, Δv, along z-axis

Full size image
Figure 7
figure 7

Evolutions of fiber paths below the slot die under experimental air pressure of 1.0 atm [27]. The real image size for all the images is 26.2 mm × 19.6 mm. The evolution of the left–right alternating loops is also shown; fiber paths in the two elliptical annotations are the generated left and right loops

Full size image

Fluctuation of temperature

Figure 8 shows the instantaneous air temperatures, Tt, at the points of z = 6, 50 and 100 mm, as a function of time, t. Figure 8 shows that the instantaneous temperature signal in time segment of 0.2 is as regular as sine or cosine curve. It is worth noting that there are ten peaks or troughs of signal-wave existed in time segment of 0.2 s at z = 6, 50 and 100 mm, illustrates that the frequency of the sine or cosine curve-like instantaneous temperature signal is changeless no matter where the measuring points are. Correspondingly, Fig. 9 illustrates the probability distribution of the instantaneous temperature in twenty temperature sections. Comparing to probability distribution of instantaneous velocity shown in Fig. 5, the obvious difference is that the probability distribution of temperature presents bimodal distribution.

Figure 8
figure 8

The instantaneous temperature, Tt, at the positions of a z = 6 mm, b 50 mm and c 100 mm as a function of time, t

Full size image
Figure 9
figure 9

The probability distribution of the instantaneous temperature in twenty velocity sections for the positions of a z = 6 mm, b z = 50 mm and c z = 100 mm. These statistical results were obtained from Fig. 8. The δ is standard deviation of instantaneous temperature

Full size image

Similar to the definition of the instantaneous velocity, vt, the instantaneous air temperature, Tt, is expressed as the sum of the mean and fluctuating temperatures, namely \( T_{t} = \overline{T} + T^{{\prime }} \). A time segment of 0.2 s (from 0.5 to 0.7 s) was chosen again for comparing the profile of temperature, Tt, with the instantaneous velocity, vt. Figure 10a and b shows the detailed evolution of the fluctuating temperature, |T′|, and ΔT, along z-axis. The parameters of |T′| and ΔT are defined similarly to |v′| and Δv of the air velocity, as

$$ \left| {T^{{\prime }} } \right| = \frac{{\sum\limits_{1}^{N} {\left| {T_{\text{t}} - \overline{T} } \right|} }}{N} $$
(8)

where Tt and \( \overline{T} \) are the instantaneous and mean fluctuating temperatures; N is the number of acquainted temperatures in the time segment of 0.2 s.

Figure 10
figure 10

The evolutions of a the fluctuating temperature, |T′|, and b the range of instantaneous temperature, ΔT, along z-axis

Full size image
$$ \Delta T = \hbox{max} (T^{{\prime }} ) - \hbox{min} (T^{{\prime }} ) $$
(9)

The maximum value of |T′| is about 0.82 °C as locating at the point of z = 6 mm, and then decreased as far away from the die. Comparing to the |v′| shown in Fig. 6a, the obvious difference is that, there is no second peak existed, we deduce that the temperature fluctuation has little relationship with the velocity fluctuation, for the velocity is a vector, whereas the temperature is a scalar. As shown in Fig. 10b, the maximum value of ΔT = 5.5 °C is still at the point of z = 6 mm and then sharply decreases to about 4 °C at the point of z = 14 mm, the ΔT continues decreasing gradually but with gradually increasing fluctuation in the region of 14 mm ≤ z ≤ 100 mm. At the point of z = 6 mm, ΔT = 5.5 °C is nonnegligible when comparing with the mean air temperature of 63 °C (shown in Fig. 11b in the next part). It is well known that temperature largely determines the molten fibers viscosity, and correspondingly affects the dynamic viscoelastic force of fiber. The obviously fluctuating ΔT in the region of 14 mm ≤ z ≤ 100 mm also contributes the fluctuating attenuation of dynamic viscoelastic force of fiber in melt blowing.

Figure 11
figure 11

a The profile of measured mean air velocity along z-axis by hot-wire anemometer. The evolution of fiber velocity along z-axis [27] is added for comparison with air velocity. b The evolution profile of measured mean air temperature along z-axis, the initial temperature at z = 0 mm is 100 °C

Full size image

From Figs. 4 and 8, although air velocity and temperature have obviously different fluctuating characteristics in melt blowing, their characteristics of fluctuation play an important effect in fluctuating attenuation of the fiber. We suppose that the later research on fiber attenuation, fiber motion as well as the evenness of the nonwoven fibers in melt blowing should take the characteristics of fluctuating air velocity and temperature simultaneously into consideration.

Mean velocity and temperature profiles

Figure 11a shows the development of the mean air velocity profile as a function of the distance, z, along z-axis. It is shown that mean velocity decreases rapidly with increasing distance from the die until reaching the point of z = 50 mm. A maximum mean velocity of 183 m s−1 is obtained at the point of z = 6 mm, which is about 30 m s−1 higher than the maximum velocity measured by previous researchers [13,14,15,16]. Although air velocity in the region of 0 mm < z < 6 mm is not shown in this work, it is no doubt that fiber undergoes strong attenuation effect by the high-speed air velocity in this region. However, as shown in Fig. 11a, the fiber velocity not increases rapidly but increases linearly and gradually, the measurement of the fiber velocity was described in our previous work [27], and the fiber was produced under the same air pressure using in this work. Moreover, in consideration of the fiber whipping paths shown in Fig. 7, we confirm that the turbulent air near the die with high-speed velocity results in inducing the lateral two-dimensional or three-dimensional whipping motion of the fiber, rather than rapidly increasing the fiber velocity along z direction.

Figure 11b shows the mean air temperature profiles along z-axis. The trend of the temperature decay is similar to the velocity decay shown in Fig. 11a. In view of the initial air temperature is 100 °C (air temperature at point of z = 0 is 100 °C), the air temperature decreases to be 50% of itself at the point of z = 13 mm. It is this temperature drop that is believed to be the driving force for crystallization of the polymer melt and fiber solidification in the melt-blowing process.

During melt-blowing process, both air velocity and temperature determine the attenuation of fiber, a lot of work have been done on optimizing the air flow field by designing new structure of the die [30, 31], these optimizations of air flow field were refer to that the new designed dies could provided air flow field with higher velocity and higher temperature, simultaneously. It is accessible that air with higher velocity can provide stronger attenuation of fiber and air with higher temperature can maintain molten status of fiber in longer time. However, Xie and Zeng [32] showed that higher air velocity and higher air temperature not always produced fibers with smaller diameter. In their work, a gauge air pressure of 1.0 atm created initial air velocities about 300 and 150 m s−1 for slot-die and swirl-die melt blowing; however, the fibers collected at 25-mm distance below the die have a mean diameter of 75.2 µm for the slot die, and 58.3 µm for the swirl die, for the reason that the type of turbulence also determines attenuating ratio of fiber. In addition, we think that the energy wasting should be considered in optimizing air flow field in melt blowing, in other description, the attenuation effect provided by the relative velocity of air and fiber occurs just in the region where the fiber is at the status of molten; otherwise, high air velocity has no contribution to fiber attenuation where fiber is solidified, i.e., velocity energy wasting appears. Similarly, temperature wasting appears where fiber attenuation effect disappears, not only this, the molten fiber tends to rebound under its internal viscoelastic force resulting in fiber diameter re-increasing. The phenomenon of fiber rebound has been discovered [33, 34], which is very harmful to melt-blowing productions.

Coupling effect of velocity and temperature

In melt blowing, air velocity and temperature exist simultaneously for fiber attenuation. The coupling effect between air flow field and the fiber is the essential mechanical mechanism for fiber attenuation. Besides this coupling effect, the coupling effect of velocity and temperature may exist. In this part, we have done a tentative research on this coupling effect, in particular, the effect of temperature on velocity was revealed by processing data of measurements.

As mentioned above, before formal velocity measurement, the velocity calibration was carried out on calibrating device at ambient temperature, i.e., 18 °C. Figure 12a shows the air velocities measured by hot-wire anemometer at initial air temperature of 18, 50 and 100 °C. For higher initial air temperature, the measured air velocity along z-axis is lower at any points below the die. Take the results at the point of z = 6 mm for example, the measured air velocities are about 182, 150 and 90 m s−1 at initial air temperature of 18, 50 and 100 °C. It noted that these velocities are just measured values, rather than the real velocities. According to the principle of velocity measurement of hot-wire anemometer, melt-blowing air with higher temperature takes less temperature of the wire, resulting in lower voltage is needed for maintaining the constant temperature of the wire, the measured air velocity calculated by the velocity-calibration curve are corresponding lower. Fortunately, a correcting formula provided by hot-wire anemometer can be applied for converting the measured voltages applied on the wires at initial temperatures of 50 and 100 °C, into the standard voltage applied on the wires at ambient temperature. As

$$ E_{\text{corr}} = \sqrt {\frac{{T_{\text{w}} - T_{0} }}{{T_{\text{w}} - T}}} \cdot E $$
(10)
Figure 12
figure 12

a The air velocities measured by hot-wire anemometer at initial air temperatures of 18, 50 and 100 °C. It noted that the measured air velocities by the hot-wire anemometer are calculated according to the velocity-calibration curves shown in Fig. 3a, b the corrected air velocities as well as the standard air velocity measured at ambient temperature, along z-axis (the inset shows the air velocities on an expanded scale)

Full size image

Here Ecorr is the converted voltage; Tw is the constant temperature of the wires, i.e., 238 °C; T0 is the ambient temperature, 18 °C, and T is the temperature of the melt-blowing air, T at different points can be obtained from Fig. 9b.

By substituting Ecorr into the velocity-calibration curve shown in Fig. 3a, the corrected air velocities which are equal to the real velocities can be obtained. Figure 12b shows the corrected air velocities as well as the standard air velocity measured at ambient temperature, along z-axis (The inset shows the air velocities on an expanded scale.). Although Fig. 12b illustrates that the profile of air velocities along z-axis are almost coincided with each other at different initial air temperatures, there still exists a nonnegligible difference of the air velocities by analyzing the inset of Fig. 12b. The inset shows that temperature has an enhanced effect on velocity, at the point of z = 6 mm, air velocities are about 182.5, 186 and 188.5 m s−1 at the initial air temperatures of 18, 50 and 100 °C, respectively. Actually, air with initial temperatures of 50 and 100 °C decrease to about 35 and 63 °C, respectively, at z = 6 mm. In other words, air temperature difference of 45 °C (i.e., 45 = 63 − 18 °C) generates velocity difference of 6 m/s (i.e., 6 = 188.5 − 182.5 m s−1). In commercial melt blowing, the initial air temperature is commonly set to about 300 °C or above, moreover, with in view of Fig. 10b, we speculate that the temperature fluctuation, ΔT, will become larger in commercial condition, correspondingly resulting in enhanced fluctuation of the air velocity. Fluctuations of both velocity and temperature may account for the reason why the evenness of fiber diameter produced by melt blowing is poor. The typical melt-blowing fibers with poor diameter evenness are shown in Fig. 13a. Figure 13a shows the SEM image of fibers produced by the melt-blowing equipment described in this work, using a scanning electron microscope (JSM-5600LV, JEOL, Tokyo, Japan), Fig. 13b illustrates the corresponding probability distribution of the fiber diameters.

Figure 13
figure 13

a The SEM image of fibers produced by the melt-blowing equipment described in this work, using a scanning electron microscope (JSM-5600LV, JEOL, Tokyo, Japan), b the corresponding probability distribution of the fiber diameters

Full size image

Conclusions

Turbulent air flow field in slot-die melt blowing was experimentally studied by using hot-wire anemometer. The fluctuating characteristics of the velocity and temperature as well as mean velocity and temperature were obtained. The results showed that the characteristics of velocity and temperature fluctuations were obviously different, the velocity fluctuation was irregular and strong, and it contained some unexplored characteristics of the turbulence, such as a predicted steady vortex existed at the position near z = 14 mm. The fluctuation of temperature revealed a regular profile like sine or cosine curve, moreover, the frequency of the sine or cosine curve was changeless at different points along z-axis. In the last part of this study, the coupling effect of velocity and temperature was analyzed; the results showed that temperature has an enhanced effect on velocity. The fluctuation of temperature not only contributed to changing of viscosity of the fiber but also generated fluctuation of velocity. Fluctuation of both velocity and temperature could account for the reason why the evenness of fiber diameter produced by melt blowing was poor.

This work discovered that the characteristics of turbulent air flow field had great relationship with the fiber motion as well as fiber diameter evenness of melt-blowing products. Indicated that turbulent air flow field deserved to be further discovering in order to fully research on melt blowing.