An improved method for the matrix dissolution extraction of nanoparticles from microalloyed steel

  • Metals
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The chemical extraction of niobium and titanium carbonitride precipitates from microalloyed steels was studied. Steel samples and chemically synthesized reference nanoparticles were subjected to commonly used extraction protocols, and conditions were systematically varied. High acid concentrations led to particle etching with losses above 10%; long extraction times and small etchant volumes led to the formation of dense SiOx networks that engulfed the extracted particles. The addition of surfactants was found to reduce agglomeration and limit etching. We developed an optimized extraction protocol that can extract and retain particles with diameters below 10 nm with reduced etching and negligible network formation. The resulting particle dispersions are suitable both for efficient electron microscopy of large particle numbers in a single run and colloidal analysis of large numbers of particles in dispersion.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6

Similar content being viewed by others

Notes

  1. The standard uses 5 g of steel that are dissolved in 100 mL HCl (6 mol L−1) and later filled up with 150 mL water.

  2. V ∼ r3: a reduction of 15% in volume/mass goes along with a reduction of approx. 5% in radius.

  3. For an image resolution with 2 pixels/nm and a particle size of 30 nm, the error in size determination is 1.6%.

References

  1. Vega MI, Medina SF, Quispe A et al (2005) Influence of TiN particle precipitation state on static recrystallisation in structural steels. ISIJ Int 45:1878–1886. https://doi.org/10.2355/45.1878

    Article  Google Scholar 

  2. Nishioka K, Ichikawa K (2012) Progress in thermomechanical control of steel plates and their commercialization. Sci Technol Adv Mater 13:023001. https://doi.org/10.1088/1468-6996/13/2/023001

    Article  Google Scholar 

  3. Baker TN (2016) Microalloyed steels. Ironmak Steelmak 43:264–307. https://doi.org/10.1179/1743281215Y.0000000063

    Article  Google Scholar 

  4. Gladman T (1997) The physical metallurgy of microalloyed steels. The Institute of Materials, London

    Google Scholar 

  5. Craven AJ, He K, Garvie LAJ, Baker TN (2000) Complex heterogeneous precipitation in titanium–niobium microalloyed Al-killed HSLA steels—I. (Ti, Nb)(C, N) particles. Acta Mater 48:3857–3868. https://doi.org/10.1016/S1359-6454(00)00194-4

    Article  Google Scholar 

  6. Craven AJ, He K, Garvie LAJ, Baker TN (2000) Complex heterogeneous precipitation in titanium–niobium microalloyed Al-killed HSLA steels—II. Non-titanium based particles. Acta Mater 48:3869–3878. https://doi.org/10.1016/S1359-6454(00)00193-2

    Article  Google Scholar 

  7. Courtois E, Epicier T, Scott C (2006) EELS study of niobium carbo-nitride nano-precipitates in ferrite. Micron 37:492–502. https://doi.org/10.1016/j.micron.2005.10.009

    Article  Google Scholar 

  8. Lee Y, De Cooman BC (2014) TiN/NbC compound particle formation during thin slab direct rolling of HSLA steel. Steel Res Int 85:1158–1172. https://doi.org/10.1002/srin.201300280

    Article  Google Scholar 

  9. Xie ZJ, Ma XP, Shang CJ et al (2015) Nano-sized precipitation and properties of a low carbon niobium micro-alloyed bainitic steel. Mater Sci Eng A 641:37–44. https://doi.org/10.1016/j.msea.2015.05.101

    Article  Google Scholar 

  10. Li Z, Liu D, Zhang J, Tian W (2013) Precipitates in Nb and Nb–V microalloyed X80 pipeline steel. Microsc Microanal 19:62–65. https://doi.org/10.1017/S1431927613012348

    Article  Google Scholar 

  11. Béreš M, Weirich TE, Hulka K, Mayer J (2004) TEM investigations of fine niobium precipitates in HSLA steel. Steel Res Int 75:753–758

    Article  Google Scholar 

  12. Klinkenberg C, Hulka K, Bleck W (2004) Niobium carbide precipitation in microalloyed steel. Steel Res Int 11:744–752

    Article  Google Scholar 

  13. Tirumalasetty GK, van Huis MA, Fang CM et al (2011) Characterization of NbC and (Nb, Ti)N nanoprecipitates in TRIP assisted multiphase steels. Acta Mater 59:7406–7415. https://doi.org/10.1016/j.actamat.2011.08.012

    Article  Google Scholar 

  14. Mukherjee T, Stumpf WE, Sellars CM (1968) Quantitative assessment of extraction replicas for particle analysis. J Mater Sci 3:127–135. https://doi.org/10.1007/BF00585479

    Article  Google Scholar 

  15. Shen YF, Wang CM, Sun X (2011) A micro-alloyed ferritic steel strengthened by nanoscale precipitates. Mater Sci Eng A 528:8150–8156. https://doi.org/10.1016/j.msea.2011.07.065

    Article  Google Scholar 

  16. Bonevich JE, Haller WK (2010) NIST—NCL joint assay protocol, PCC-X: measuring the size of nanoparticles using transmission electron microscopy (TEM). National Institute of Standards and Technology, Gaithersburg, MD. https://ws680.nist.gov/publication/get_pdf.cfm?pub_id=854083. Accessed 19 Dec 2018

  17. Rice SB, Chan C, Brown SC et al (2013) Particle size distributions by transmission electron microscopy: an interlaboratory comparison case study. Metrologia 50:663–678. https://doi.org/10.1088/0026-1394/50/6/663

    Article  Google Scholar 

  18. Masuda H, Gotoh K (1999) Study on the sample size required for the estimation of mean particle diameter. Adv Powder Technol 10:159–173. https://doi.org/10.1016/S0921-8831(08)60447-1

    Article  Google Scholar 

  19. Cunningham TR, Price RJ (1933) Determination of nonmetallic inclusions in plain carbon and manganese steels iodine and nitric acid extraction methods. Ind Eng Chem Anal Ed 5:27–29. https://doi.org/10.1021/ac50081a018

    Article  Google Scholar 

  20. Klinger P, Koch W (1938) Beitrag zur elektrolytischen Bestimmung von nichtmetallischen Einschlüssen im Stahl. Arch für das Eisenhüttenwes 11:569–582. https://doi.org/10.1002/srin.193801061

    Article  Google Scholar 

  21. Inoue R, Ueda S, Ariyama T, Suito H (2011) Extraction of nonmetallic inclusion particles containing MgO from steel. ISIJ Int 51:2050–2055

    Article  Google Scholar 

  22. Garside JE, Rooney TE, Belli JJJ (1957) The alcoholic-iodine method for the extraction of inclusions from steel. J Iron Steel Inst 185:95–103

    Google Scholar 

  23. Fernandes M, Cheung N, Garcia A (2002) Investigation of nonmetallic inclusions in continuously cast carbon steel by dissolution of the ferritic matrix. Mater Charact 48:255–261. https://doi.org/10.1016/S1044-5803(02)00246-2

    Article  Google Scholar 

  24. Lu J, Ivey D, Henein H (2006) Quantification of nano-sized precipitates in microalloyed steels by matrix dissolution. In: Proceedings of international pipeline conference, pp 635–642. https://doi.org/10.1115/ipc2006-10600

  25. Lu J, Ivey DG, Henein H et al (2008) Extraction and characterization of nano-precipitates in microalloyed steels. In: Proceedings of the international pipeline conference, Calgary, pp 85–94

  26. Lu J, Wiskel JB, Omotoso O et al (2011) Matrix dissolution techniques applied to extract and quantify precipitates from a microalloyed steel. Metall Mater Trans A 42:1767–1784. https://doi.org/10.1007/s11661-010-0579-6

    Article  Google Scholar 

  27. Hegetschweiler A, Kraus T, Staudt T (2017) Colloidal analysis of particles extracted from microalloyed steel. Metall Ital 109:23–28

    Google Scholar 

  28. Wiskel J, Lu J, Omotoso O et al (2016) Characterization of precipitates in a microalloyed steel using quantitative X-ray diffraction. Metals (Basel) 6:90. https://doi.org/10.3390/met6040090

    Article  Google Scholar 

  29. Rivas AL, Vidal E, Matlock DK, Speer JG (2008) Electrochemical extraction of microalloy carbides in Nb-steel. Rev Metal 44:447–456. https://doi.org/10.3989/revmetalm.0771

    Article  Google Scholar 

  30. ASTM E194-10 (2015) Standard test method for acid-insoluble content of copper and iron powders, West Conshohocken

  31. Pierson HO (1996) Carbides of group IV: titanium, zirconium, and hafnium carbides. In: Pierson HO (ed) Handbook of refractory carbides and nitrides: properties, characteristics, processing and applications. Noyes Publications, Westwood, p 362

    Google Scholar 

  32. Pierson HO (1996) Carbides of group V: vanadium, niobium and tantalum carbides. In: Pierson HO (ed) Handbook of refractory carbides and nitrides: properties, characteristics, processing and applications. Noyes Publications, Westwood, p 362

    Google Scholar 

  33. Pierson HO (1996) The refractory nitrides. In: Pierson HO (ed) Handbook of refractory carbides and nitrides. Noyes Publications, Westwood, pp 156–162

    Chapter  Google Scholar 

  34. Kosolapova TY (2012) Carbides. Springer, Boston

    Google Scholar 

  35. Lengauer W (2000) Transition metal carbides, nitrides, and carbonitrides. In: Riedel R (ed) Handbook of ceramic hard materials. Wiley, Weinheim, pp 202–252

    Chapter  Google Scholar 

  36. Giordano C, Erpen C, Yao W et al (2009) Metal nitride and metal carbide nanoparticles by a soft urea pathway. Chem Mater 21:5136–5144. https://doi.org/10.1021/cm9018953

    Article  Google Scholar 

  37. Read S, Gibbs R, Parker B (1990) Extraction and characterization of precipitates formed in a niobium HSLA steel. Mater Forum 14:304–307

    Google Scholar 

  38. Duan J, Gregory J (2003) Coagulation by hydrolysing metal salts. Adv Colloid Interface Sci 100–102:475–502. https://doi.org/10.1016/S0001-8686(02)00067-2

    Article  Google Scholar 

Download references

Acknowledgements

The authors would like to thank Eduard Arzt for his continuing support of the project. Andrea Jung is also acknowledged for the elementary analysis, Kathrin Alt for particle dissolution experiments, and Bastian Philippi for Matcalc Simulations.

Funding

This work was funded by the “AG der Dillinger Hüttenwerke” in Germany and a patent for a particle extraction procedure aided by a dispersant was submitted.

Author information

Authors and Affiliations

  1. INM - Leibniz Institute for New Materials, Campus D2 2, 66123, Saarbrücken, Germany

    Andreas Hegetschweiler & Tobias Kraus

  2. AG der Dillinger Hüttenwerke, Werkstraße 1, 66763, Dillingen/Saar, Germany

    Thorsten Staudt

  3. Colloid and Interface Chemistry, Saarland University, Campus D2 2, 66123, Saarbrücken, Germany

    Tobias Kraus

Authors
  1. Andreas Hegetschweiler
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Thorsten Staudt
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Tobias Kraus
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Tobias Kraus.

Electronic supplementary material

Below is the link to the electronic supplementary material.

Supplementary material 1 (DOCX 18 kb)

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Hegetschweiler, A., Staudt, T. & Kraus, T. An improved method for the matrix dissolution extraction of nanoparticles from microalloyed steel. J Mater Sci 54, 5813–5824 (2019). https://doi.org/10.1007/s10853-018-03263-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-018-03263-0

Search

Navigation