Abstract
This research intended to improve the hydrophilic behavior of starch-based films in food packaging by using surface coating with maleated epoxidized natural rubber (MENR) and then mechanically reinforced film through compositing with cellulose additive addition. The biocomposite was created from cellulose fiber (CF) and cassava starch (CS) by using carboxyl styrene butadiene as a crosslinker with green route. The MENR was employed for improving hydrophobic behavior for CS composites by using immersion method. Results showed that no delamination and a continuous covering of latex onto the both sides of MENR coated composites observed by SEM was found. The thickness of these films increased with increasing MENR coating time. The ester groups occurrence indicated new peaks occurring due to a reaction during melt blending between starch and MENR by using FTIR. Moreover, the high-water resistance was helped by coating with the MENR. The swelling ratio in water, moisture content and moisture absorption were decreased with increasing number of coating cycle. The elongation at break of this sample increased with increasing the coating cycles. The cured CS/CF blend was used polymer matrix for encapsulated essential oil. The EO release was significantly decreased owing to coating relative to the uncoating control which rapidly release rate. The CS composite exhibited a good polymer matrix which was decomposed in natural soil after utilization.
Similar content being viewed by others
Data availability
Not applicable.
References
Acar I, Acisli O (2018) Mechano-chemical surface modification of calcite by wet-stirred ball milling. Appl Surf Sci 457:208–213. https://doi.org/10.1016/j.apsus2018.06.2
Badshah M, Ullah H, Khan AR, Khan S, Park J, Khan T (2018) Surface modification and evaluation of bacterial cellulose for drug delivery. Int J Biol Macromol 113:526–533. https://doi.org/10.1016/j.ijbiomac.2018.02.135
Bangyekan C, Aht-Ong D, Srikulkit K (2006) Preparation and properties evaluation of chitosan-coated cassava starch films. Carbohydr Polym 63:61–71. https://doi.org/10.1016/j.carbpol.2005.07.032
Bastos DC, Santos ACEFD, Simao RA (2013) Acetylene coating on cornstarch plastics produced by cold plasma technology. Starch/stärke 66:267–273. https://doi.org/10.1002/star.201200219
Goiana ML, Fernandes FAN (2023) Influence of dielectric barrier discharge plasma treatment on corn starch properties. Processes 11(7):1966. https://doi.org/10.3390/pr11071966
Hu Y, Lu K, Yan F, Shi Y, Yu P, Yu S, Li S, Gao C (2016) Enhancing the performance of aromatic polyamide reverse osmosis membrane by surface modification via covalent attachment of polyvinyl alcohol (PVA). J Membr Sci 501:209–219. https://doi.org/10.1016/j.memsci.2015.12.003
Jantanasakulwong K, Leksawasdi N, Seesuriyachan P, Wongsuriyasak S, Techapun C, Ougizawa T (2016) Reactive blending of thermoplastic starch, epoxidized natural rubber and chitosan. Eur Polym J 84:292–299. https://doi.org/10.1016/j.eurpolymj.2016.09.035
Kebebew D, Linbo D, Huang WFF (2023) PBAT-based biodegradable nanocomposite coating films with ultra-high oxygen barrier and balanced mechanical properties. Polym Degrad Stab 216:110489. https://doi.org/10.1016/j.polymdegradstab
Li M, Tian X, Jin R, Li D (2018) Preparation and characterization of nanocomposite films containing starch and cellulose nanofibers. Industrial Crop Product 123:654–660. https://doi.org/10.1016/j.indcrop.2018.07.043
Liu Z, Yao L, Pan X, Liu Q, Huang H (2018) A green and facile approach to the efficient surface modification of alumina nanoparticles with fatty acids. Appl Surf Sci 447:664–672. https://doi.org/10.1016/j.apsusc.2018.04.035
Mui TSM, Mota RP, Quade A, de Oliveira Hein LR, Kostov KG (2018) Uniform surface modification of polyethylene terephthalate (PET) by atmospheric pressure plasma jet with a horn-like nozzle. Surf Coat Technol 352:338–347. https://doi.org/10.1016/j.surfcoat.2018.08.014
Paris MJ, Ramírez-Corona N, Palou E, López-Malo A (2020) Modelling release mechanisms of cinnamon (Cinnamomum zeylanicum) essential oil encapsulated in alginate beads during vapor-phase application. J Food Eng 282:110024. https://doi.org/10.1016/j.jfoodeng.2020.110024
Pashkuleva I, Marques AP, Vaz F, Reis RL (2010) Surface modification of starch based biomaterials by oxygen plasma or UV-irradiation. J Mater Sci 21(1):21–32. https://doi.org/10.1007/s10856-009-3831-0
Riyajan S (2015) Robust and biodegradable polymer of cassava starch and modified natural rubber. Carbohydr Polym 134:267–277. https://doi.org/10.1016/j.carbpol.2015.07.038
Riyajan S (2018) Novel polymer from a cassava starch/carboxylated styrene-butadiene blend containing potassium persulfate: design and properties. Polym Bull 75:4377–4395. https://doi.org/10.1007/s00289-018-2273-6
Riyajan S-A, Chantawee K (2020) Cassava starch composite based films for encapsulated neem: effect of carboxylated styrene-butadiene rubber coating. Food Packag Shelf Life 23:100438. https://doi.org/10.1016/j.fpsl.2019.100438
Riyajan S-A, Sakdapipanich JT (2009) Development of a controlled release neem capsule with a sodium alginate matrix, crosslinked by glutaraldehyde and coated with natural rubber. Polym Bull 63:609–622. https://doi.org/10.1007/S00289-009-0126-Z
Riyajan S, Teprak A (2019) A novel environmentally friendly biopolymer product from gelatin and natural rubber: effect of bagasse fiber and urea. J Polym Environ 27:225–233. https://doi.org/10.1016/S0257-8972(97)00360-5
Riyapan D, Riyajan S, Kowalczyk A (2015) Green synthesis” and characterization of the maleated epoxidized natural rubber latex. Polym Bull 72:671–691. https://doi.org/10.1007/s00289-014-1298-8
Saegeman V, Ectors NL, Lismont D, Bert Verduyckt B (2008) Short- and long-term bacterial inhibiting effect of high concentrations of glycerol used in the preservation of skin allografts. Burns 34:205–211. https://doi.org/10.1016/j.burns.2007.02.009
Shen L, Wang Y (2018) Efficient surface modification of thin-film composite membranes with self-catalyzed tris (2-aminoethyl)amine for forward osmosis separation. Chem Eng Sci 178:82–92. https://doi.org/10.1016/J.CES.2017.12.026
Shuang Er G, Yhaya MF, Teik PB (2023) Characterisation and adhesion properties of UV-cured natural rubber-based adhesives. Int J Adhes Adhes 123:103347. https://doi.org/10.1016/j.ijadhadh.2023.103347
Soares FC, Yamashita F, Müller CMO, Pires ATN (2013) Thermoplastic starch/poly(lactic acid) sheets coated with cross-linked chitosan. Polym Test 32:94–98. https://doi.org/10.1016/j.polymertesting.2012.09.005
Tajik M, Torshizi HJ, Resalati H, Hamzeh Y (2018) Effects of cationic starch in the presence of cellulose nanofibrils on structural, optical and strength properties of paper from soda bagasse pulp. Carbohydr Polym 194:1–8. https://doi.org/10.1016/j.carbpol.2018.04.026
Tripathi BP, Das P, Simon F, Stam M (2018) Ultralow fouling membranes by surface modification with functional polydopamine. Eur Polym J 99:80–89. https://doi.org/10.1016/j.eurpolymj.2017.12.006
Xu C, Cao L, Zhao P, Zhou Z, Cao C, Li F, Huang Q (2018) Emulsion-based synchronous pesticide encapsulation and surface modification of mesoporous silica nanoparticles with carboxymethyl chitosan for controlled azoxystrobin release. Chem Eng J 348:244–254. https://doi.org/10.1016/j.cej.2018.05.008
Xue X, Liu Y-L, Dai J-G, Poon C-S, Zhang W-D, Zhang P (2018) Inhibiting efflorescence formation on fly ash–based geopolymer via silane surface modification. Cement Concrete Composite 94:43–52. https://doi.org/10.1016/j.cemconcomp.2018.08.013
Yang P, Moloney MG, Zhang F, Ji W (2018) Surface hydrophobic modification of polymers with fluorodiazomethanes. Mater Lett 210:295–297. https://doi.org/10.1016/j.matlet.2017.09.008
Zhang N, Gao C, Meng L, Tang X (2023a) Preparation and characterization of carnauba wax-based particle with hierarchical structure and its use as hydrophobic coating for chitosan films. Carbohydr Polym 319:121224. https://doi.org/10.1016/j.carbpol.2023.121224
Zhang T, Yu Q, Zhang Y, Wang X, Xu L, Wang J, Pingan Song P (2023b) One-step assembly of poly(vinyl alcohol)/tannic acid complexes as a high oxygen barrier coating for poly(lactic acid) packaging films. Prog Org Coat 184:107880. https://doi.org/10.1016/j.porgcoat.2023.10788
Zhu W, Chen J, Dong Q, Luan D, Tao N, Deng S, Wang L, Hao Y, Li L (2023) Development of organic-inorganic hybrid antimicrobial materials by mechanical force and application for active packaging. Food Packag Shelf Life 37:101060. https://doi.org/10.1016/j.fpsl.2023.101060
Acknowledgments
Saad Riyajan gratefully thank the financial support received by Thailand Science Research and Innovation Fundamental Fund xxx/2566) and Thailand Institute of Nuclear Technology (Public Organization), the Center of Scientific Equipment for Advanced Research, Thammasat University, Thammasat University Research Unit in Smart Material from Biomass and the Center of Scientific Equipment, Faculty of Science and Technology, Thammasat University. This study was supported by Thailand Science Research and Innovation Fundamental Fund (TUFF05/2565)” and Thammasat University.
Funding
The funding was supported by Thammasat University and Thailand Science Research and Innovation Fundamental Fund xxx/2566) and Thailand Institute of Nuclear Technology (Public Organization).
Author information
Authors and Affiliations
Contributions
Saad did experiment and conceived of the presented idea, verified the analytical methods and supervised the findings of this work as discussed, the results and contributed to the final manuscript.
Corresponding author
Ethics declarations
Conflict of interest
The authors inform that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper or work.
Ethical approval and consent to participate
Manuscripts reporting studies not involving human participants, human data or human tissue must.
Informed consent statement
Not applicable.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Riyajan, SA. Cellulose additive for cassava starch packaging: physical properties. Cellulose 31, 1659–1674 (2024). https://doi.org/10.1007/s10570-023-05642-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10570-023-05642-6