Abstract
The electrochemical behaviour of 2-dimethylaminoethanol (DMA) on the corrosion of Type 304 austenitic stainless steel in dilute hydrochloric solution was investigated through a weight-loss technique, open circuit potential measurement and potentiodynamic polarization tests at specific concentrations of DMA. Results show the compound to be highly effective with a maximum inhibition efficiency of 79 % from weight loss analyses and 80.9 % from polarization tests at 12.5 % DMA. The mean corrosion potential of −321 mV, obtained from open circuit potential measurement is within passivation potentials. DMA inhibition protection was determined to occur through a physicochemical reaction mechanism on the steel surface, confirmed from calculated thermodynamic values. DMA obeyed the Langmuir isotherm model. Data obtained for inhibition efficiency from the three test techniques are in reasonably good agreement. The potentiodynamic test showed that the compounds acted as a cathodic type inhibitor.
Similar content being viewed by others
References
Ariga K, Yamauchi Y, Rydzek G, Ji Q, Yonamine Y, Wu KCW, Hill JP (2014) Layer-by-layer nanoarchitectonics: invention, innovation, and evolution. Chem Lett 43:36–68
Matsumoto T, Sata N, Kobayashi K, Yamabe-Mitarai Y (2013) Surface structures and electrochemical activity of palladium–niobium binary alloy electrodes, and glucose biosensor with palladium–niobium binary alloy electrode. Bull Chem Soc Jpn 86:1317–1322
Bodhak S, Kikuchi M, Sogo Y, Tsurushima H, Ito A, Oyan A (2013) Calcium phosphate coating on a bioresorbable hydroxyapatite/collagen nanocomposite for surface functionalization. Chem Lett 42:1029–1031
Masuda K, Matsune H, Takenaka S, Kishida M (2014) Synthesis of silica-coated AgCl nanoparticles in aqueous poly(vinylpyrrolidone) solution. Bull Chem Soc Jpn 87:573–575
Singh DDN, Singh TB, Gaur B (1995) The role of metal cations in improving the inhibitive performance of hexamine on the corrosion of steel in hydrochloric acid solution. Corros Sci 37:1005–1019
Jayalakshmi M, Muralidharan VS (1998) Correlation between structure and inhibition of organic compounds for acid corrosion of transition metals. Ind J Chem Tech 5:16–28
Granese SL (1998) Study of the inhibitory action of nitrogen-containing compounds. Corrosion Corro J 44:322– 329
Granese SL, Rosales BM, Oviedo C, Zebrino JO (1992) The inhibition action of heterocyclic nitrogen organic compounds on Fe and steel in HCl media. Corros Sci 33:1439– 1453
Raicheva SN, Aleksiev BV, Sokolova EI (1993) The effect of the chemical structure of some nitrogen- and sulphur-containing organic compounds on their corrosion inhibiting action. Corros Sci 34:343–350
Frignani A, Monticelli C, Brunoro G, Zucchi M, Hashi OI (1987) Inhibitors for Armco iron and ASTM A106 plain steel in hydrofluoric acid. Brit Corr J 22:103–108
Cheng XL, Ma HY, Chen SH, Yu R, Chen X, Yao ZM (1999) Corrosion of stainless steels in acid solutions with organic sulfur-containing compounds. Corros Sci 41:321– 333
El-Sayed A (1997) Phenothiazine as inhibitor of the corrosion of cadmium in acidic solutions. J Appl Electrochem 27:193– 200
Schmitt G (1984) Application of inhibitors for acid media: report prepared for the European federation of corrosion working party on inhibitors. Brit Corr J 19:165–176
Abd El Rehim SS, Ibrahim MAM, Khalid KF (1999) 4-Aminoantipyrine as an inhibitor of mild steel corrosion in HCl solution. J Appl Electrochem 29:593–599
Hluchan V, Wheeler BL, Hackerman N (1988) Amino acids as corrosion inhibitors in hydrochloric acid solutions. Mats Corr 39(11):512–517
Behpour M, Ghoreishi SM, Soltani N, Salavati-Niasari M, Hamadanian M, Gandomi A (2008) Electrochemical and theoretical investigation on the corrosion inhibition of mild steel by thiosalicylaldehyde derivatives in hydrochloric acid solution. Corros Sci 50:2172–2188
Morad MS, Sarhan AAO (2008) Application of some ferrocene derivatives in the field of corrosion inhibition. Corros Sci 50:744–753
Khaled KF (2008) Magnetic properties of nanocomposite Fe-doped SBA-15 magnetic materials. Mats Chem Phys 112:290–300
Hosseini MG, Arshadi MR (2009) Study of 2-butyne-1,4-diol as acid corrosion inhibitor for mild steel with electrochemical, infrared and AFM techniques. Int J Electrochem Sci 4:1339– 1350
Growcock FB, Lopp VR (1998) The inhibition of steel corrosion in hydrochloric acid with 3-phenyl-2-propyn-1-ol. Corros Sci 28:397–410
Tedeschi RJ (1975) Acetylenic corrosion inhibitors. Corros J 31:130–134
Yazdzad AR, Shahrabi T, Hosseini MG (2008) Inhibition of 3003 aluminum alloy corrosion by propargyl alcohol and tartrate ion and their synergistic effects in 0.5 % NaCl solution. Mat Chem Phy 109:199–205
Shahrabi T, Yazdzad AR, Hosseini MR (2008) Inhibition behaviour of 2-butine1, 4diol and tartrate salt, and their synergistic effects on corrosion of AA3003 aluminium alloy in 0.5 % NaCl solution. J Mat Sci Tech 24:427–432
Hosseini MG, Shahrabi T, Tavakholi HJ (2008) Synergism in copper corrosion inhibition by sodium dodecylbenzenesulphonate and 2-mercaptobenzoimidazole. J Appl Elec 38:1629– 1636
Paty BB, Singh DDN (1992) Solvents’ role on HCl-induced corrosion of mild steel: its control by propargyl alcohol and metal cations. Corros J 48:442–527
Bartos M, Hackerman N (1992) A study of inhibition action of propargyl alcohol during anodic dissolution of iron in hydrochloric acid. J Electrochem Soc 139:3428–3433
Bilgiç S, Sahin M (2001) The corrosion inhibition of austenitic chromium–nickel steel in H2SO4 by 2-butyn-1-ol. Mat Chem Phy 70:290–295
Fontana MG, Staehle RW (1974) Plenum (Eds.), Advances in Corrosion Science and Technology, New York, pp 229
Putilova JN (1966) Comptes Rendus du 2eme. In: Symposium Europeen sur les Inhibiteurs de Corrosion, Annali University, Ferrara
Hosseini MG, Mertens SFL, Nichols RJ, Ghorbani M, Arshadi MR (2002) Eurocorr. Madrid, pp 24
Morris W, Vázquez M (2002) A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides. Cem Concr Res 32:259–267
Elsener B, Büchler M, Stalder F, Böhni H (1999) Migrating corrosion inhibitor blend for reinforced concrete: part 1—prevention of corrosion. Corros J 55:1155–1163
Elsener B, Büchler M, Stalder F, Böhni H (2000) Migrating corrosion inhibitor blend for reinforced concrete: part 2—inhibitor as repair strategy. Corros J 56:727–732
Rosenberg A (2000) Discussion: migrating corrosion inhibitor blend for reinforcing concrete: part 1—prevention of corrosion. Corros J 56:986–987
Maeder U, Swamy RN (eds) (1994) Corrosion and corrosion protection of steel in concrete. Sheffield, U.K., p 851
Batis G, Routoulas A, Rakanta E (2003b) Effects of migrating inhibitors on corrosion of reinforcing steel covered with repair mortar. Cem Concr Compos 25:109–115
Jamil HE, Shriri A, Boulif R, Bastos C, Montemor MF, Ferreira MGS (2004) Electrochemical behaviour of amino alcohol-based inhibitors used to control corrosion of reinforcing steel. Electrochim Acta 49:2753–2760
Machnikova E, Kenton HW, Hackerman N (2008) Corrosion inhibition of carbon steel in hydrochloric acid by furan derivatives. Electroch Acta 53(20):6024–6032
Vaidyanathan H, Hackerman N (1971) Effect of furan derivatives on the anodic dissolution of Fe. Corros Sci 11:737–750
Moretti G, Guidi F, Grion G (2004) Tryptamine as a green iron corrosion inhibitor in 0.5 M deaerated sulphuric acid. Corros Sci 46:387–403
Oliveres O, Likhanova NV, Gomez B, Navarrete J, Llanos-Serrano ME, Arce E, Hallen JM (2006). Appl Surf Sci 252:2894–2909
Zhang DQ, Gao LX, Zhou GD (2003) Synergistic effect of 2-mercapto benzimidazole and KI on copper corrosion inhibition in aerated sulfuric acid solution. J Appl Electrochem 33:361–366
Oguzie EE, Unaegbu C, Ogukwe CN, Okolue BN, Onuchukwu AI (2004) Inhibition of mild steel corrosion in sulphuric acid using indigo dye and synergistic halide additives. Mater Chem Phys 84:363–368
Shibli SMA, Saji VS (2005) Co-inhibition characteristics of sodium tungstate with potassium iodate on mild steel corrosion. Corros Sci 47:2213–2224
Mu G, Li X (2005) Inhibition of cold rolled steel corrosion by Tween-20 in sulfuric acid: weight loss, electrochemical and AFM approaches. J Colloid Interface Sci 289 :184–192
Feng Y, Siow KS, Teo WK, Hsieh AK (1999) The synergistic effects of propargyl alcohol and potassium iodide on the inhibition of mild steel in 0.5 M sulfuric acid solution. Corros Sci 41:829–852
Villamil RFV, Corio P, Rubin JC, Agostinho SMI (1999) Effect of sodium dodecylsulfate on copper corrosion in sulfuric acid media in the absence and presence of benzotriazole. J Electroanal Chem 472:112–119
Wang B, Du M, Zhang J, Gao CJ (2011) Electrochemical and surface analysis studies on corrosion inhibition of Q235 steel by imidazoline derivative against CO2 corrosion. Corros Sci 53:353–361
Brett CMA, Gomes IAR, Martins JPS (1994) The electrochemical behaviour and corrosion of aluminium in chloride media. The effect of inhibitor anions. Corros Sci 36:915– 923
Olivares O, Likhanova NV, Gomez B, Navarrete J, Llanos-Serrano ME, Arce E, Hallen JM (2006) Electrochemical and XPS studies of decylamides of a-amino acids adsorption on carbon steel in acidic environment. Appl Surf Sci 252:2894–2909
Trasatti S (1992) Adsorption of organic substances at electrodes: recent advances. Electrochim Acta 37:2137–2144
Popova A, Sokolova E, Raicheva S, Christov M (2003) AC and DC study of the temperature effect on mild steel corrosion in acid media in the presence of benzimidazole derivatives. Corros Sci 45:33–58
Revie RW (2000) Uhlig’s corrosion handbook. Wiley, New York
Altsybeeva AI, Burlov VV, Fedorova NS, Reshetnikov SM (2013) Volatile inhibitors of atmospheric corrosion of ferrous and nonferrous metals. V. Study of the adsorption of inhibitors on steel from an aqueous electrolyte solution. Int J Corros Scale Inhib 2(4):277–286
Yasser K, Mohammed El AB, Ali D, Belkheir H (2014) A theoretical investigation on the corrosion inhibition of mild steel by piperidine derivatives in hydrochloric acid solution. J of Chem Pharm Research 6(4):689–696
Amitha RBE, Bharathi Bai JB (2012) Green inhibitors for corrosion protection of metals and alloys: an overview. Int J of Corrosion. doi:10.1155/2012/380217
Noor EA, Al-Moubaraki AH (2008) Thermodynamic study of metal corrosion and inhibitor adsorption processes in mild steel/1-methyl-4[4 ′(-X)-styryl pyridinium iodides/hydrochloric acid systems. Mats Chem Phys 110(1):145–154
Aljourani J, Raeissi K, Golozar MA (2009) Benzimidazole and its derivatives as corrosion inhibitors for mild steel in 1 M HCl solution. Corros Sci 51(8):1836–1843
Obot B, Obi-Egbedi NO, Umoren SA (2009) Experimental and theoretical investigation of clotrimazole as corrosion inhibitor for aluminium in hydrochloric acid and effect of iodide ion addition. Der Pharm Chem 1:151–166
Hosseini MG, Mertens SFL, Arshadi MR (2009) Synergism and antagonism in mild steel corrosion inhibition by sodium dodecylbenzenesulphonate and hexamethylenetetramine. Corros Sci 45:1473–1489
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Loto, R.T., Loto, C.A., Popoola, A.P. et al. Electrochemical Studies of the Inhibition Effect of 2-Dimethylaminoethanol on the Corrosion of Austenitic Stainless Steel Type 304 in Dilute Hydrochloric Acid. Silicon 8, 145–158 (2016). https://doi.org/10.1007/s12633-015-9344-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12633-015-9344-1