Abstract
Decomposition of the ferritic phase is studied in isothermally aged SAF 2507 superduplex stainless steel (SDSS) by means of different examination methods. The ferritic phase (δ) undergoes an eutectoid transformation into secondary austenite (γ 2) and σ-phase between 650 and 1000 °C. Samples were treated at 900 °C because the incubation time of this transformation is the shortest at this temperature. In order to follow the microstructural changes, x-ray diffraction analysis (XRD), automated electron backscatter diffraction (EBSD), applied magnetic investigation [vibrating sample magnetometer (VSM)], micro-hardness tests, and differential thermal analysis (DTA) were used. The results of XRD and EBSD methods for phase quantification showed nearly the same amounts for all three phases. The results of applied magnetic investigation for the fraction of ferritic phase were also in good agreement with the corresponding results of XRD and EBSD methods. Decomposition of ferrite is similarly well-traceable on EBSD phase maps where the coherent ferritic areas gradually broke into pieces with increasing time of heat treatment. According to the EBSD measurements the σ-phase grains appeared and started to grow after 2 min aging time in the ferritic-austenitic matrix, usually on the boundaries of ferritic and austenitic grains. After 15 min treating time, the microstructure consisted of mainly σ- and austenitic (primary and secondary) phases with negligible amount of ferrite. Chemical composition of the σ-phase was measured by energy-dispersive x-ray spectroscopy (EDS) at different aging times. Activation energies of σ-phase precipitation and α′-phase formation were determined by the Kissinger plot, through DTA measurements; they are 243 and 261 kJ/mol, respectively. Using the results of phase quantifications, the Johnson-Mehl-Avrami equation was fitted.
Similar content being viewed by others
References
R.N. Gunn, Duplex Stainless Steels, Abington Publishing, Cambridge, 1997
A. Kashiwar, N. Phani Vennela, S.L. Kamath, and R.K. Khatirkar, Effect of Solution Annealing Temperature on Precipitation in 2205 Duplex Stainless Steel, Mater. Charact., 2012, 74, p 55–63
A.R. Akisanya, U. Obi, and N.C. Renton, Effect of Ageing on Phase Evolution and Mechanical Properties of a High Tungsten Super-Duplex Stainless Steel, Mater. Sci. Eng. A-Struct., 2012, 535, p 281–289
Y.H. Yang, B. Yan, J. Wang, and J.L. Yin, The Influence of Solution Treatment Temperature on Microstructure and Corrosion Behavior of High Temperature Ageing in 25% Cr Duplex Stainless Steel, J. Alloy. Compd., 2011, 509, p 8870–8879
J. Dobránszky and P.J. Szabó, EDS-Analysis of Intermetallic Precipitation in Thermally aged SAF 2507 Type Superduplex Stainless Steel, Mater. Sci. Forum, 2003, 414–415, p 189–194
J. Dobránszky and J. Ginsztler, Microstructural Stability of Duplex Stainless Steel Weldments, Mater. Sci. Forum, 2007, 561–565, p 2119–2122
R. Badji, M. Bouabdallah, B. Bacroix, C. Kahloun, B. Belkessa, and H. Maza, Phase Transformation and Mechanical Behavior in Annealed 2205 Duplex Stainless Steel Welds, Mater. Charact., 2008, 59, p 447–453
M. Breda, I. Calliari, E. Ramous, M. Pizzo, L. Corain, and G. Straffelini, Ductile-to-Brittle Transition in a Zeron®100 SDSS in Wrought and Aged Conditions, Mater. Sci. Eng. A-Struct., 2013, 585, p 57–65
I. Calliari, M. Breda, E. Ramous, K. Brunelli, M. Pizzo, and C. Menapace, Impact Toughness of an Isothermally Treated Zeron®100 SDSS, J. Mater. Eng. Perform., 2012, 21(10), p 2117–2123
M. Martins and L.C. Casteletti, Heat Treatment Temperature Influence on ASTM A890 GR 6A Super Duplex Stainless Steel Microstructure, Mater. Charact., 2005, 55, p 225–233
C.M. Souza, Jr., H.F.G. Abreu, S.S.M. Tavares, and J.M.A. Rebello, The σ-Phase Formation in Annealed UNS S31803 Duplex Stainless Steel: Texture Aspects, Mater. Charact., 2008, 59, p 1301–1306
E.O. Hall and S.H. Algie, The Sigma Phase, Metall. Rev., 1966, 11, p 61–88
S. Nenno, M. Tagaya, and Z. Nishiyama, Orientation Relationships Between Gamma (fcc) and Sigma Phases in an Iron-Chromium-Nickel Alloy, Trans. Jpn. Inst. Met., 1962, 3, p 82–94
T.H. Chen and J.R. Yang, Effects of Solution Treatment and Continuous Cooling on σ-Phase Precipitation in a 2205 Duplex Stainless Steel, Mater. Sci. Eng. A-Struct., 2001, 311, p 28–41
G. Kurdjumov and Z. Sachs, Over the Mechanisms of Steel Hardening, Z. Phys., 1930, 64, p 325–343
Y.-J. Kim, L. Scott Chumbley, and B. Gleeson, Determination of Isothermal Transformation Diagrams for Sigma-Phase Formation in Cast Duplex Stainless Steels CD3MN and CD3MWCuN, Metall. Mater. Trans. A, 2004, 35A, p 3377–3386
E. Johnson, Y.-J. Kim, L. Scott Chumbley, and B. Gleeson, Initial Phase Transformation Diagram Determination for the CD3MN Cast Duplex Stainless Steel, Scr. Mater., 2004, 50, p 1351–1354
I. Mészáros and J. Prohászka, Magnetic Investigation of the Effect of Martensite on the Properties of Austenitic Stainless Steel, J. Mater. Process. Technol., 2005, 161, p 162–168
I. Mészáros, Magnetic Characterisation of Duplex Stainless Steel, Phys. B, 2006, 372, p 181–184
F. Fiorillo, Measurements and Characterization Of Magnetic Materials, Elsevier-Academic, San Diego, 2004
A. Błachowski, S.M. Dubiel, and J. Żukrowski, On the Activation Energy of the σ-Phase Formation in a Pure and Ti-Doped Fe-Cr Alloy, Intermetallics, 2001, 9, p 493–498
P. Ferro, A Dissolution Kinetics Model and Its Application to Duplex Stainless Steels, Acta Mater., 2013, 61, p 3141–3147
B.F.O. Costa, J. Cieslak, and S.M. Dubiel, Kinetics of σ-Phase Formation in Equiatomic Cold-Rolled Fe-V Alloys, Mater. Chem. Phys., 2013, 143, p 19–25
H.E. Kissinger, Reaction Kinetics in Differential Thermal Analysis, Anal. Chem., 1957, 29, p 1702–1706
J.A. Augis and J.E. Bennett, Calculation of the Avrami Parameters for Heterogeneous Solid State Reactions Using a Modified the Kissinger Method, J. Therm. Anal., 1978, 13, p 283–292
Z.B. Wang, N.R. Tao, W.P. Tong, L. Lu, and K. Lu, Diffusion of Chromium in Nanocrystalline Iron Produced by Means of Surface Mechanical Attrition Treatment, Acta Mater., 2003, 51, p 4319–4329
W. Bowen and G.M. Leak, Diffusion in BCC Iron Base Alloys, Metall. Trans., 1970, 1(10), p 2767–2773
W. Bowen and G.M. Leak, Solute Diffusion in Alpha- and Gamma-Iron, Metall. Trans., 1970, 1(6), p 1695–1700
H. Nitta, K. Miura, and Y. Iijima, Self-Diffusion in Iron-Based Fe-Mo Alloys, Acta Mater., 2006, 54, p 2833–2847
H. Nitta, T. Yamamoto, R. Kanno, K. Takasawa, T. Iida, Y. Yamazaki, S. Ogu, and Y. Iijima, Diffusion of Molybdenum in α-Iron, Acta Mater., 2002, 50, p 4117–4125
M. Avrami, Kinetics of Phase Change. I. General Theory, J. Chem. Phys., 1939, 7(12), p 1103–1112
M. Avrami, Kinetics of Phase Change. II. Transformation-Time Relations for Random Distribution Of Nuclei, J. Chem. Phys., 1940, 8(2), p 212–224
M. Avrami, Kinetics of Phase Change. III. Granulation, Phase Change and Microstructure, J. Chem. Phys., 1941, 9(2), p 177–184
R. Magnabosco, Kinetics of Sigma Phase Formation in a Duplex Stainless Steel, Mater. Res., 2009, 12(3), p 321–327
N.O. Lara, A. Ruiz, C. Rubio, R.R. Ambriz, and A. Medina, Nondestructive Assessing of the Aging Effects in 2205 Duplex Stainless Steel Using Thermoelectric Power, NDT&E Int., 2011, 44, p 463–468
R. Badji, M. Bouabdallah, B. Bacroix, C. Kahloun, K. Bettahar, and N. Kherrouba, Effect of Solution Treatment Temperature on the Precipitation Kinetic of σ-Phase in 2205 Duplex Stainless Steel Welds, Mater. Sci. Eng. A-Struct., 2008, 496, p 447–454
J.W. Christian, The theory of Transformations in Metals and Alloys, Part I, 2nd ed., Pergamon Press, Oxford, 1975
Acknowledgment
Authors express their thanks to Dr. András Éva for the useful remarks.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Berecz, T., Fazakas, É., Mészáros, I. et al. Decomposition Kinetics of Ferrite in Isothermally Aged SAF 2507-Type Duplex Stainless Steel. J. of Materi Eng and Perform 24, 4777–4788 (2015). https://doi.org/10.1007/s11665-015-1793-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-015-1793-6