Thermoelectric Properties of p-Type La1−z Pr z Fe4−x Co x Sb12 Skutterudites

  • Published:
Journal of Electronic Materials Aims and scope Submit manuscript

Abstract

p-Type La1−z Pr z Fe4−x Co x Sb12 skutterudites were prepared by encapsulated melting, quenching, annealing, and hot pressing. The skutterudite phase was successfully synthesized but small amounts of FeSb2 and (La,Pr)Sb2 secondary phases were also observed, especially for the Co-substituted specimens. Carrier concentration decreased with increasing Pr and Co content. Electrical conductivity decreased with increasing temperature, showing that all specimens were heavily-doped semiconductors. Electrical conductivity also decreased with increasing Pr and Co content. The Hall and the Seebeck coefficients revealed that all specimens had p-type characteristics. Seebeck coefficients increased with increasing temperature, with maximum values occurring between 723 and 823 K. The maximum power factor (PF) was 3.1 m Wm−1 K−2, at 823 K and 723 K for La0.75Pr0.25Fe4Sb12 and La0.75Pr0.25 Fe3.75Co0.25Sb12, respectively. Thermal conductivity decreased with increasing Pr and Co content, and increased because of bipolar conduction at temperatures above 723 K. For a fixed Co content, lattice thermal conductivity decreased with increasing Pr content; this may be attributed to a larger contribution from Pr than from La to the decrease in lattice thermal conductivity. The dimensionless figure of merit (ZT) had maximum values of 0.83 at 823 K for La0.75Pr0.25Fe4Sb12 and 0.81 at 723 K for La0.75Pr0.25Fe3.75Co0.25Sb12.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. B.C. Sales, D. Mandrus, and R.K. Williams, Science 272, 1325 (1996).

    Article  Google Scholar 

  2. B.C. Sales, D. Mandrus, B.C. Chakoumakos, V. Keppens, and J.R. Thompson, Phys. Rev. B 56, 15081 (1997).

    Article  Google Scholar 

  3. G.A. Slack, Handbook of Thermoelectrics, edited by D.M. Rowe (CRC Press, Boca Raton, FL, 1995), p. 407.

  4. G.S. Nolas, G.A. Slack, and S.B. Schujman, Semiconductors and Semimetals, vol. 69, ed. T. M. Tritt (Academic Press, San Diego, 2001), p. 255.

  5. Y.Z. Pei, L.D. Chen, W. Zhang, X. Shi, S.Q. Bai, X.Y. Zhao, Z.G. Mei, and X.Y. Li, Appl. Phys. Lett. 89, 221107 (2006).

    Article  Google Scholar 

  6. Y.Z. Pei, J. Yang, L.D. Chen, W. Zhang, J.R. Salvador, and J.H. Yang, Appl. Phys. Lett. 95, 042101 (2009).

    Article  Google Scholar 

  7. L.D. Chen, T. Kawahara, X.F. Tang, T. Goto, T. Hira, J.S. Dyck, W. Chen, and C. Uher, J. Appl. Phys. 90, 1864 (2001).

    Article  Google Scholar 

  8. M. Puyet, B. Lenoir, A. Dauscher, M. Dehmas, C. Stiewe, and E. Muller, J. Appl. Phys. 95, 4852 (2004).

    Article  Google Scholar 

  9. X.Y. Zhao, X. Shi, L.D. Chen, W.Q. Zhang, W.B. Zhang, and Y.Z. Pei, J. Appl. Phys. 99, 053711 (2006).

    Article  Google Scholar 

  10. D.T. Morelli, G.P. Meisner, B. Chen, S. Hu, and C. Uher, Phys. Rev. B 56, 7376 (1997).

    Article  Google Scholar 

  11. G.S. Nolas, M. Kaeser, R.T. Littleton IV, and T.M. Tritt, Appl. Phys. Lett. 77, 1855 (2000).

    Article  Google Scholar 

  12. J.G.A. Lamberton, S. Bhattacharya, R.T. Littleton IV, M.A. Kaeser, R.H. Tedstrom, T.M. Tritt, J. Yang, and G.S. Nolas, Appl. Phys. Lett. 80, 598 (2002).

    Article  Google Scholar 

  13. V.L. Kuznetsov, L.A. Kuznetsova, and D.M. Rowe, J. Phys.: Condens. Matter 15, 5035 (2003).

    Google Scholar 

  14. W. Jeitschko and D.J. Brown, Acta Crystallogr. B 33, 3401 (1977).

    Article  Google Scholar 

  15. D.J. Singh and M.H. Du, Phys. Rev. B: Condens. Matter Mater. Phys. 82, 075115 (2010).

    Article  Google Scholar 

  16. M.V. Keepens, D. Mandrus, B.C. Sales, B.C. Chakoumakos, P. Day, R. Coldea, B. Maple, D.A. Gajewski, E.J. Freeman, and S. Bennington, Nature 395, 876 (1998).

    Article  Google Scholar 

  17. L. Zhang, A. Grytsiv, P. Rogl, E. Bauer, and M. Zehebauer, J. Phys. D Appl. Phys. 42, 225405 (2009).

    Article  Google Scholar 

  18. J. Yang, W. Zhang, Z.Q. Bai, Z. Mei, and L.D. Chen, Appl. Phys. Lett. 90, 192111 (2007).

    Article  Google Scholar 

  19. X.F. Tang, Q. Zhang, L.D. Chen, T. Goto, and T. Hirai, J. Appl. Phys. 97, 093712 (2005).

    Article  Google Scholar 

  20. X. Shi, J. Yang, J.R. Salvador, M.F. Chi, J.Y. Cho, H. Wang, S.Q. Bai, J.H. Wang, W.Q. Zhang, and L.D. Chen, J. Am. Chem. Soc. 133, 7837 (2011).

    Article  Google Scholar 

  21. X. Shi, H. Kong, C.P. Li, C. Uher, J. Yang, J.R. Salvador, H. Wang, L. Chen, and W. Zhang, Appl. Phys. Lett. 92, 182101 (2008).

    Article  Google Scholar 

  22. W. Zhao, P. Wei, Q. Zhang, C. Dong, L. Liu, and X.F. Tang, J. Am. Chem. Soc. 131, 3713 (2009).

    Article  Google Scholar 

  23. G.P. Meisner, D.T. Morelli, S. Hu, J. Yang, and C. Uher, Phys. Rev. Lett. 80, 3551 (1998).

    Article  Google Scholar 

  24. Y. Tang, S. Chen, and G.J. Snyder, J. Mater. 1, 75 (2015).

    Google Scholar 

  25. G.P. Meisner, D.T. Morelli, S. Hu, J. Yang, and C. Uher, Phys. Rev. Lett. 80, 3551 (1998).

    Article  Google Scholar 

  26. Y.C. Lan, A.J. Minnich, G. Chen, and Z.F. Ren, Adv. Funct. Mater. 20, 357 (2010).

    Article  Google Scholar 

  27. C. Kittel, Introduction to Solid State Physics, 6th ed. (New York: Wiley, 1986), p. 152.

    Google Scholar 

  28. K.H. Park, I.H. Kim, S.M. Choi, Y.S. Lim, W.S. Seo, and K.H. Kim, Jpn. J. Appl. Phys. 52, 10MB18 (2013).

Download references

Author information

Authors and Affiliations

  1. Department of Materials Science and Engineering, Korea National University of Transportation, Chungju, Chungbuk, 380-702, Korea

    Kwon-Min Song, Dong-Kil Shin & Il-Ho Kim

Authors
  1. Kwon-Min Song
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Dong-Kil Shin
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Il-Ho Kim
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Il-Ho Kim.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Song, KM., Shin, DK. & Kim, IH. Thermoelectric Properties of p-Type La1−z Pr z Fe4−x Co x Sb12 Skutterudites. J. Electron. Mater. 45, 1227–1233 (2016). https://doi.org/10.1007/s11664-015-3952-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11664-015-3952-9

Keywords

Search

Navigation