Abstract
A biomimetic method was used to promote a bioactive surface on a CoCrMo alloy (ASTM F75). To enhance the nucleation of apatite on the metallic substrate, wollastonite ceramics (W), bioactive glass (BG) or hydroxyapatite (HA) were used in the biomimetic method. Metallic samples were chemically treated and immersed for 7 days in SBF on a bed of bioactive material (W, BG or HA) followed by an immersion in 1.5SBF for 7 or 14 days without bioactive system.
A bonelike apatite layer was formed on the surface of all the samples tested. The samples treated with wollastonite showed a higher rate of apatite formation and the morphology of the layer was closer to that of the existing bioactive systems. A higher crystallinity of the apatite layer was also observed by using wollastonite. The pH of the SBF, the Ca/P ratio and the thickness of the layer on the samples treated with wollastonite and bioactive glass increased as increasing the immersion time. The thickness of the layer on the samples treated with hydroxyapatite also increased with time, but the pH of the SBF and the Ca/P ratio changed with no a defined trend.
Similar content being viewed by others
References
L. HENCH, J. Am. Ceram. Soc. 74(7) (1991) 1487.
L. HENCH and D. E. CLARK, J. Non-Cryst. Solids 28 (1978) 83.
T. KOKUBO, M. SHIGEMATSU, Y. NAGASHIMA, M. TASHIRO, T. NAKAMURA, T. YAMAMURO, and S. HIGASHI, Bull. Inst. Chem. Res. (Kyoto Univ). 60(3–4) (1982) 260.
P. N. DE AZA, F. GUITIAN and S. DE AZA, Scripta Mater. 31(8) (1994) 1001.
P. HABIBOVIC, F. BARRERE, C. BLITTERSWIJK, K. DE GROOT and P. LAYROLLE, J. Am. Ceram. Soc. 85(3) (2002) 517.
F. MIYAJI, H. M. KIM, T. KOKUBO, T. KITSUGI and T. NAKAMURA, in “Bioceramics 8,” edited by J. Wilson, L. Hench and D. Greenspan (Elsevier Science Ltd., 1998) p. 323.
T. MIYAZAKI, H. M. KIM, F. MIYAJI, T. KOKUBO and T. NAKAMURA, in “Bioceramics 10,” edited by L. Sedel and C. Rey (Elsevier Science Ltd., 1997) p. 11.
H. M. KIM, F. MIYAJI, T. KOKUBO and T. NAKAMURA, J. Ceram. Soc. Jpn. 105(2) (1997) 111.
Y. ABE and T. KOKUBO, J. Mater. Sci .- Mater. M. 1 (1990) 233.
K. HATA and T. KOKUBO, J. Am. Ceram. Soc. 78(4) (1995) 1049.
M. TANAHASHI, T. YAO, T. KOKUBO, M. MINODA, T. MIYAMOTO, T. NAKAMURA and T. YAMAMURO, J. Biomed. Mater. Res. 29 (1995) 349.
H. M. KIM, K. KISHIMOTO, F. MIYAJI, T. KOKUBO, T. YAO, Y. SUETSUGU, J. TANAKA and T. NAKAMURA, J. Biomed. Mater. Res. 46 (1999) 228.
C. DU, P. KLASENS, R. E. HAAN, J. BEZENER, F. Z. CI, K. DE GROOT and P. LAYROLLE, J. Biomed. Mater. Res. 59 (2002) 535.
K. DE GROOT, in “Bioceramics 11,” edited by R. Z. LeGeros (World Scientific Publishing, New York, 1998) p. 41.
D. A. CORTÉS, J. C. Escobedo, A. Nogiwa and R. MUÑOZ, Mater. Sci. Forum 442 (2003) 61.
M. WEI, A. J. RUYS, B. K. MILTHORPE and C. C. SORRELL, J. Biomed. Mater. Res. 45 (1999) 11.
T. KOKUBO, H. KUSHITANI and S. SAKKA, J. Biomed. Mater. Res. 24 (1990) 721.
P. SEPULVEDA, J. R. JONES and L. L. HENCH, J. Biomed. Mater. Res. 61 (2002) 301.
P. N. DE AZA, F. GUITIAN, A. MELOS, E. LORA-TAMAYO and S. DE AZA, J. Mater. Sci. -Mater. M. 7 (1996) 399.
R. Z. LEGEROS and J. P. LEGEROS, in “An introduction to bioceramics,” edited by L. L. Hench and J. Wilson (World Scientific, Singapore, 1993) p. 139.
Q. AHANG, J. CHEN, J. FENG, Y. CAO, C. DENG and X. ZHANG, Biomaterials 24 (2003) 4741.
T. KOKUBO, J. Non-Cryst. Solids 120 (1990) 138.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cortés, D.A., Medina, A., Escobedo, S. et al. Biomimetic apatite formation on a CoCrMo alloy by using wollastonite, bioactive glass or hydroxyapatite. J Mater Sci 40, 3509–3515 (2005). https://doi.org/10.1007/s10853-005-2856-0
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-2856-0