Abstract
A novel ITO/NiO/Cu2O structure served as photocathodes was applied in photoelectrochemical (PEC) water splitting for the first time. The NiO integration is found to slightly ameliorate the crystalline structure of Cu2O. PEC measurements showed that NiO-modified Cu2O photocathodes can deliver a higher PEC performance, as the photocurrent density was up to − 1.68 mA/cm2 at − 0.6 V versus RHE under simulated AM 1.5G illumination, which is 2.8 times higher than that of nude one. The enhanced PEC performance may come from the improved charge separation and migration properties of NiO modification.
References
O. Khaselev, J.A. Turner, Science 280, 425 (1998)
J.Y. Kim, J.H. Noh, K. Zhu et al., ACS Nano 5, 2647–2656 (2011)
Y.Y. Lan, Z.F. Liu, Z.G. Guo et al., Dalton Trans. 47, 12181–12187 (2018)
Z.F. Liu, J.Y. Wu, J. Zhang, Int. J. Hydrogen Energy 41, 20529–20535 (2016)
A. Wolcott, W.A. Smith, T.R. Kuyke et al., Adv. Funct. Mater. 19, 1849–1856 (2009)
D. Chen, Z.F. Liu, Z.G. Guo et al., J. Mater. Chem. A. 6, 20393–20401 (2018)
A. Paracchino, V. Laporte, K. Sivula et al., Nat. Mater. 10, 456–461 (2011)
H. Michikazu, K. Takeshi, K. Mutsuko et al., Chem. Commun. 3, 357–358 (1998)
Z.F. Liu, X. Wang, Int. J. Hydrogen Energy 43, 13276–13283 (2018)
Z. Zhang, R. Dua, L. Zhang, H. Zhu, H. Zhang, P. Wang, ACS Nano 7(2), 1709–1717 (2013)
C. Li, T. Hisatomi, O. Watanabe, M. Nakabayashi, N. Shibata, K. Domen, J.-J. Delaunay, Energy Environ. Sci. 8, 1493–1500 (2015)
Y.K. Hsu, C.H. Yu, Y.C. Chen, Y.G. Lin, Electrochim. Acta 105, 62–68 (2013)
A. Kargar, S.S. Partokia, M.T. Niu, P. Allameh, M. Yang, S. May, J.S. Cheung, K. Sun, K. Xu, D.L.S. Wang, Nanotechnology 25, 205401 (2014)
G.H. Yue, Y. Zhang, X.Q. Zhang, C.G. Wang, Y.C. Zhao, D.L. Peng, Appl. Phys. A 118, 763–767 (2015)
J.S. Luo, L. Steier, M.K. Son, M. Schreier, M.T. Mayer, M. Grätzel, Nano Lett. 16(3), 1848–1857 (2016)
Z. Liu, X. Lu, D. Chen, ACS Sustain. Chem. Eng. 6, 10289–10294 (2018)
G.J. Ai, H.X. Li, S.P. Liu et al., Adv. Funct. Mater. 25(35), 5706–5713 (2015)
S.L. Bai, X.J. Yang, C.Y. Liu et al., ACS Sust. Chem. Eng. 6(10), 12906–12913 (2018)
Y. Bai, H. Chen, S. Xiao et al., Adv. Funct. Mater. 2, 62950–62958 (2016)
J.H. Park, J. Seo, S. Park et al., Adv. Mater. 27, 4013 (2015)
C. Terrier, J.P. Chatelon, R. Berjoanb, J.A. Roger, Thin Solid Films 263, 37–41 (1995)
Acknowledgements
The authors gratefully acknowledge financial support from Tianjin High School Science and Technology Fund Planning Project (170401017), and Science and technology achievements transformation projects of Tianjin Chengjian University (201703235).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic Supplementary Material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Li, G., Wei, L. & Yang, Y. Novel NiO-modified Cu2O photocathode for photoelectrochemical water splitting. Appl. Phys. A 126, 306 (2020). https://doi.org/10.1007/s00339-020-03491-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00339-020-03491-9