Abstract
Cracking of neopentane was catalyzed by a sulfated oxide of zirconium promoted with iron and manganese. Reaction at 300–450°C, atmospheric pressure, and neopentane partial pressures of 0.00025–0.005 bar gave methane as the principal product, along with C2 and C3 hydrocarbons, butenes, and coke. The order of reaction in neopentane was determined to be 1, consistent with a monomolecular reaction mechanism and with the formation of methane andt-butyl cations; the latter was presumably converted into several products, including only little isobutylene. At 450°C and a neopentane partial pressure of 0.005 bar, the rate of cracking at 5 min onstream was 5×10−8 mol/(g of catalyst s). Under the same conditions, the rates observed for unpromoted sulfated zirconia and USY zeolite were 3×10−8 and 6×10−9 mol/ (g of catalyst s), respectively. The observation that the promoted sulfated zirconia is not much more active than the other catalysts is contrasted to published results showing that the former catalyst is more than two orders of magnitude more active than the others forn-butane isomerization at temperatures <100°C. The results raise a question about whether the superacidity attributed to sulfated zirconia as a low-temperature butane isomerization catalyst pertains at the high temperatures of cracking.
Similar content being viewed by others
References
C.-Y. Hsu, C.R. Heimbuch, C.T. Armes and B.C. Gates, J. Chem. Soc. Chem. Commun. (1992) 1645.
C.-H. Lin and C.-Y. Hsu, J. Chem. Soc. Chem. Commun. (1992) 1479.
T.-K. Cheung, J.L. d'Itri and B.C. Gates, J. Catal., in press.
T.-K. Cheung, J.L. d'Itri and B.C. Gates, J. Catal., submitted.
T.M. Gairbekov, S.N. Khadzhiev and A.M. Rossinskii, Kinet. Catal. 29 (1988) 1301.
J. Engelhardt and W.K. Hall, J. Catal. 125 (1990) 472.
C. Morterra, G. Cerrato, F. Pinna and M. Signoretto, J. Phys. Chem. 98 (1994) 12373.
E.A. Lombardo, R. Pierantozzi and W.K. Hall, J. Catal. 110 (1988) 171.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cheung, TK., d'Itri, J.L., Lange, F.C. et al. Neopentane cracking catalyzed by iron- and manganese-promoted sulfated zirconia. Catal Lett 31, 153–163 (1995). https://doi.org/10.1007/BF00808829
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00808829