Abstract
Effect of Ni:Al blending ratio on porous structure of porous nickel aluminides fabricated through reactive synthesis with space holder particles were investigated. Fabricated porous nickel aluminides had large pores derived from NaCl space holder particles and small pores derived from reactions between Ni and Al. Porosity and size of the small pores increased with increasing Al content in the raw powder mixture. Compressive property of porous NiAl are also investigated. porous NiAl exhibited good energy-absorption properties with relatively high plateau stress, high plateau end strain, and relatively flat plateau stress. This study suggests the possibility of intermetallic-based porous materials as high-performance energy absorber.
Similar content being viewed by others
References
J. Banhart, Progress in Materials Science 46 559–632 (2001).
F. G. Moreno, Materials 9(2) 85 (2016).
M. Adeli, S.H. Seyedein, M.R. Aboutalebi, M. Kobashi, N. Kanetake, Journal of Alloys and Compounds 497 100–104 (2010).
Y. Shu, A. Suzuki, N. Takata, M. Kobashi, Journal of Materials Processing Tech. 264 182–189 (2019).
H. Okamoto, J. Ph. Equilib. 14 257–259 (1993).
International Organization for Standardization: Metallic materials-Ductility testing-Compression test for porous and cellular metals, ISO 13314 (2011).
J. Wu, H. Cui, L.L. Cao, Z.Z. Gu, Trans. Nonferrous Met. Soc. China 21 1750–1754 (2011).
Y. He, Y. Jiang, N. Xu, J. Zou, Adv. Mater. 19 (2007) 2102–2106.
N. Takata, K Uematsu, M. Kobashi, Materials Science & Engineering A 697 (2017) 66–70.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shu, Y., Suzuki, A., Takata, N. et al. Microstructure and Mechanical property of Porous Nickel aluminides Fabricated by Reactive Synthesis with Space Holder Powder. MRS Advances 4, 1515–1521 (2019). https://doi.org/10.1557/adv.2019.153
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2019.153