Abstract
A comparative study of the structure and mechanical properties of single-crystal samples 〈001〉 of VKNA-1V and VKNA-4U alloys (cast and after heat treatment) has been performed using tensile tests in a temperature range of 1100–1250°C. In the case of the VKNA-4U alloy, samples of different crystallographic orientations have also been tested. At 1100°C, recrystallization was observed near the zone of fracture. The basic mechanism of relaxation at 1200–1250°C was found to be dynamic recovery. At 1250°C, the strength properties of the VKNA-4U alloy are higher than those of the VKNA-1V alloy.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
K. B. Povarova, V. P. Buntushkin, N. K. Kazanskaya, and A. A. Drozdov, “Analysis of Creation Principles of High Temperature Nickel Superalloys and Alloys Based on the Ni3Al ([gamma′]-Phase) Intermetallic Compound,” Perspekt. Mater., No. 2, 10–19 (2005).
E. N. Kablov, O. A. Bazyleva, and M. A. Vorontsov, “A New Base for Creating Castable High-Temperature Superalloys,” Metalloved. Term. Obrab. Met., No. 8, 21–25 (2006) [Met. Sci. Heat Treat. 48 (7–8), 348–351 (2006)].
K. B. Povarova, N. K. Kazanskaya, V. P. Buntushkin, et al., “Thermal Structural Stability of an Ni3Al-Based Alloy and Its Application for Blades in Small Gas-Turbine Engines,” Izv. Ross. Akad. Nauk, Met., No. 3, 95–100 (2003) [Russ. Metall. (Metally), No.3, 269–274 (2003)].
E. N. Kablov, V. P. Buntushkin, O. A. Bazyleva, et al., “Heat-Resistant Alloys on the Base of Ni3Al Intermetallic Compound,” in Proc. of Int. Conf. on the S.T. Kishkin’s Scientific Ideas and Modern Materials Science, April 25–26, 2006 (VIAM, Moscow, 2006)
G. P. Grabovetskaya, Yu. R. Kolobov, E. V. Kozlov, et al., “Effect of Alloying by Renium on High-Temperature Creep of Heterophase Single-Crystal Heat Resistant Nickel Alloys on the Ni3Al Base,” Zh. Funkts. Mater. 1(8), 289–294 (2007).
N. N. Stepanova, V. A. Sazonova, D. P. Rodionov, et al., “High-Temperature X-ray Examination of 〈001〉 Single Crystals of the Ni3Al-Based Superalloy,” Fiz. Met. Metalloved. 84(6), 130–138 (1997) [Phys. Met. Metallogr. 84 (6), 655–662 (1997)].
N. D. Bakhteeva, “Peculiarities of Formation of Microstructure in Heat-Strength Alloys on the Base of Nickel at Thermal and Mechanical Impact,” Tekhn. Metallov, No. 7, 15–26 (2006).
V. I. Levit and M. A. Smirnov, High-Temperature Thermomechanical Treatment of Austenitic Steels and Alloys (Chelyabinsk. Gos. Tekhn. Univ., Chelyabinsk, 1995) [in Russian].
N. V. Kazantseva, N. I. Vinogradova, N. N. Stepanova, et al., “Structural Changes in Heat-Resistant EP-800 Alloy upon Dynamical Stress,” Deform. Razr. Mater., No. 8, 10–16 (2008).
A. B. Rinkevich, N. N. Stepanova, and A. M. Burkhanov, “Acoustical Properties of Ni3Al Single Crystals Alloyed with Cobalt and Niobium,” Fiz. Met. Metalloved. 102(6), 678–682 (2006) [Phys. Met. Metallogr. 102 (6), 632–636 (2006)].
Author information
Authors and Affiliations
Additional information
Original Russian Text © D.P. Rodionov, D.I. Davydov, N.N. Stepanova, V.G. Pushin, Yu.I. Filippov, N.I. Vinogradov, Yu.N. Akshentsev, V.A. Sazonova, 2010, published in Fizika Metallov i Metallovedenie, 2010, Vol. 109, No. 3, pp. 302–309.
Rights and permissions
About this article
Cite this article
Rodionov, D.P., Davydov, D.I., Stepanova, N.N. et al. Deformation and fracture of single crystals of VKNA-type alloys at 1100–1250°C. Phys. Metals Metallogr. 109, 278–285 (2010). https://doi.org/10.1134/S0031918X10030105
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0031918X10030105