Abstract
Turbine blades, produced by the directional solidification (DS) process, often require high dimensional accuracy and excellent mechanical properties. A critical step in their production is the fabrication of wax patterns. However, the traditional manufacturing process has many disadvantages, such as long-term production, low material utilization rate, and the high cost of producing a complex-shaped wax pattern. Selective laser sintering (SLS) is one of the most extensively used additive manufacturing techniques that substantially shortens the production cycle. In this study, SLS was adopted to fabricate the wax pattern instead of the traditional manufacturing process. The orthogonal experiment method was carried out to investigate the effects of laser power, scanning speed, scanning space, and layer thickness on the dimensional precision and morphologies of the SLS parts. The SLS parts showed a minimum dimensional deviation when laser power, scanning speed, scanning space, and layer thickness were 10 W, 3000 mm•s-1, 0.18 mm, and 0.25 mm, respectively. In addition, the tensile strength and fracture morphologies were closely associated with the laser volumetric energy density (VED). The tensile strength reached a maximum when the VED was 0.0762 J•mm-3, with an evident brittle fracture morphology. The wax pattern manufactured in this way meets the accuracy and strength requirements for investment casting. This research offers a novel path for the production of wax patterns for complex-shaped turbine blades by SLS.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Pradyumna R, Sridhar S, Satyanarayana A, et al. Wax patterns for integrally cast rotors/stators of aeroengine gas turbines. Materials Today: Proceedings, 2015, 2(4): 1714–1722.
Taşcıoğlu S, Akar N. A novel alternative to the additives in investment casting pattern wax compositions. Materials & Design, 2003, 24(8): 693–698.
Liu K, Shi Y S, Li C H, et al. Indirect selective laser sintering of epoxy resin-Al2O3 ceramic powders combined with cold isostatic pressing. Ceramics International, 2014, 40(5): 7099–7106.
Zheng H Z, Zhang J, Lu S Q. Effect of core-shell composite particles on the sintering behavior and properties of nano-Al2O3/polystyrene composite prepared by SLS. Materials Letters, 2006(60): 1219–1223.
Athreya S R, Kalaitzidou K, Das S. Processing and characterization of a carbon black-filled electrically conductive Nylon-12 nanocomposite produced by selective laser sintering. Materials Science and Engineering: A, 2010, 527(10): 2637–2642.
Wang R J, Wang L L, Zhao L H. Influence of process parameters on part shrinkage in SLS. International Journal of Advanced Manufacturing Technology, 2007, 5–6(33): 498–504.
Strano G, Hao L, Everson R, et al. Multi-objective optimization of selective laser sintering processes for surface quality and energy saving. Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, 2011, 9(225): 1673–1682.
Ho H C H, Gibson I, Cheung W L. Effects of energy density on morphology and properties of selective laser sintered polycarbonate. Journal of Materials Processing Technology, 1999, 89–90: 204–210.
Pavan M, Faes M, Strobbe D, et al. On the influence of interlayer time and energy density on selected critical-to-quality properties of PA12 parts produced via laser sintering. Polymer Testing, 2017, 61: 386–395.
Childs T H C, Berzins M, Ryder G R, et al. Selective laser sintering of an amorphous polymer—simulations and experiments. Proceedings of the Institution of Mechanical Engineers Part B Journal of Engineering Manufacture, 1999, 4(213): 333–349.
He W T, Wei Q S, Liu K, et al. Numerical simulation of cold isostatic pressed alumina parts produced by selective laser sintering and part shape optimization. Ceramics International, 2013, 39(8): 9683–9690.
Ganeriwala R, Zohdi T I. Multiphysics modeling and simulation of selective laser sintering manufacturing processes. Procedia CIRP, 2014, 14: 299–304.
Wang Z J, He W T, Shi Y S, et al. Experimental based full process simulation of alumina selective laser processed parts densified by cold isostatic pressing and solid state sintering. Journal of the European Ceramic Society, 2014, 34(7): 1853–1863.
Kolossov S, Boillat E, Glardon R, et al. 3D FE simulation for temperature evolution in the selective laser sintering process. International Journal of Machine Tools and Manufacture, 2004, 44(2): 117–123.
Peyre P, Rouchausse Y, Defauchy D, et al. Experimental and numerical analysis of the selective laser sintering (SLS) of PA12 and PEKK semi-crystalline polymers. Journal of Materials Processing Technology, 2015, 225: 326–336.
Yang J S, Shi Y S, Shen Q W, et al. Selective laser sintering of HIPS and investment casting technology. Journal of Materials Processing Technology, 2009, 209(4): 1901–1908.
Freyer F, Wirtz H, Freyer C. Investment casting shell in 1 day using selective laser sintering (SLS). Foundryman, 2000, 1(93): 63–65.
Yan M X, Zhou C, Tian X Y, et al. Design and selective laser sintering of complex porous polyamide mould for pressure slip casting. Materials & Design, 2016, 111: 198–205.
Dey A. Orthogonal fractional factorial designs. New York: Wiley, 1985.
Standard Test Method for Tensile Properties of Plastics. ASTM D638-14, 2015.
Ciurana J, Hernandez L, Delgado J. Energy density analysis on single tracks formed by selective laser melting with CoCrMo powder material. The International Journal of Advanced Manufacturing Technology, 2013, 68(5–8): 1103–1110.
Author information
Authors and Affiliations
Corresponding author
Additional information
Qing-yan Xu Male, born in 1971, Ph.D, Professor. Research interests: materials processing engineering, modeling and simulation of directional solidification process for superalloy turbine blade.
Rights and permissions
About this article
Cite this article
Wei, Q., Wang, Rn., Xu, Qy. et al. Effects of process parameters on dimensional precision and tensile strength of wax patterns for investment casting by selective laser sintering. China Foundry 15, 299–306 (2018). https://doi.org/10.1007/s41230-018-8047-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-018-8047-9