Abstract
Corrosion studies of sputtered alumina thin films grown on stainless steel (SS) 304 were carried out by linear polarization and electrochemical impedance spectroscopy. Noticeable changes were not observed in morphology and surface roughness of films after carrying out the corrosion test. Corrosion current density (icorr) of alumina coated SS decreased up to 10−10 A cm−2 while icorr value in the range of 10−5–10−6 A cm−2 was observed for bare SS. The direct sputtered film showed superior corrosion resistance behaviour than the reactive sputtered film. This might be attributed to the difference in thickness of the films sputtered by direct and reactive methods. The electronic structure of deposited alumina films was studied both before and after corrosion test by X-ray photoelectron spectroscopy technique which also confirmed no structural changes of alumina film after exposing it to corrosive environment.
Similar content being viewed by others
References
M.A. El Hakim, M.D. Abad, M.M. Abdelhameed, M.A. Shalaby, S.C. Veldhuis, Wear behavior of some cutting tool materials in hard turning of HSS. Tribol. Int. 44, 1174–1181 (2011)
A.A.D. Sarhan, E. Zalnezhad, M. Hamdi, The influence of higher surface hardness on fretting fatigue life of hard anodized aerospace AL7075-T6 alloy. Mater. Sci. Eng. A 560, 377–387 (2013)
S. Baradaran, W.J. Basirun, E. Zalnezhad, M. Hamdi, A.A.D. Sarhan, Y. Alias, Fabrication and deformation behaviour of multilayer Al2O3/Ti/TiO2 nanotube arrays. J. Mech. Behav. Biomed. Mater. 20, 272–282 (2013)
J.B. Kim, C. Fuentes-Hernandez, W.J. Potscavage Jr, X.-H. Zhang, B. Kippelen, Low-voltage InGaZnO thin-film transistors with Al2O3 gate insulator grown by atomic layer deposition. Appl. Phys. Lett. 94, 142107 (2009)
N. Avci, P.F. Smet, J. Lauwaert, H. Vrielinck, D. Poelman, Optical and structural properties of aluminium oxide thin films prepared by a non-aqueous sol–gel technique. J. Sol-Gel. Sci. Technol. 59, 327–333 (2011)
I.N. Reddy, V.R. Reddy, N. Sridhara, S. Basavaraja, A.K. Sharma, A. Dey, Optical and microstructural characterisations of pulsed rf magnetron sputtered alumina thin film. J. Mater. Sci. Technol. 29, 929–936 (2013)
I.N. Reddy, V.R. Reddy, N. Sridhara, V.S. Rao, M. Bhattacharya, P. Bandyopadhyay, S. Basavaraja, A.K. Mukhopadhyay, A.K. Sharma, A. Dey, Pulsed rf magnetron sputtered alumina thin films. Ceram. Int. 40, 9571–9582 (2014)
J. Masalski, J. Gluszek, J. Zabrzeski, K. Nitsch, P. Gluszek, Improvement in corrosion resistance of the 316L stainless steel by means of Al2O3 coatings deposited by the sol-gel method. Thin Solid Films 349, 186–190 (1999)
E. Marin, A. Lanzutti, M. Lekka, L. Guzman, W. Ensinger, L. Fedrizzi, Chemical and mechanical characterization of TiO2/Al2O3 atomic layer depositions on AISI 316 L stainless steel. Surf. Coat. Technol. 211, 84–88 (2012)
S.E. Potts, L. Schmalz, M. Fenker, B. Díaz, J. Światowska, V. Maurice, A. Seyeux, P. Marcus, G. Radnóczi, L. Tóth, W.M.M. Kessels, Ultra-thin aluminium oxide films deposited by plasma-enhanced atomic layer deposition for corrosion protection. J. Electrochem. Soc. 158, C132–C138 (2011)
B. Díaz, E. Härkönen, J. Światowska, V. Maurice, A. Seyeux, P. Marcus, M. Ritala, Low-temperature atomic layer deposition of Al2O3 thin coatings for corrosion protection of steel: Surface and electrochemical analysis. Corros. Sci. 53, 2168–2175 (2011)
F. Stippich, E. Vera, H. Scheerer, G.K. Wolf, X. Jian-Ming, Corrosion properties of alumina coatings on steel and aluminum deposited by ion beam assisted deposition. Surf. Coat. Technol. 98, 997–1001 (1998)
R. Emmerich, B. Enders, H. Martin, F. Stippich, G.K. Wolf, P.E. Andersen, J. Küdelha, P. Lukác, H. Hasuyama, Y. Shima, Corrosion protection ability of Al2O3 coatings deposited with ion beam assisted deposition. Surf. Coat. Technol. 89, 47–51 (1997)
I.N. Reddy, V.R. Reddy, N. Sridhara, S. Basavaraja, M. Venkatanarayana, V.S. Rao, A.K. Sharma, A. Dey, Development of SiO2 based thin film on metal foils for space application. Ceram. Int. 39, 8493–8498 (2013)
C.N. Rao, Principle of corrosion electrochemistry (Chemistry Industry Press, Beijing, 2004)
S.V. Phadnis, A.K. Satpati, K.P. Muthe, J.C. Vyas, R.I. Sundaresan, Comparison of rolled and heat treated SS304 in chloride solution using electrochemical and XPS techniques. Corros. Sci. 45, 2467–2483 (2003)
I.N. Reddy, P. Bera, V.R. Reddy, N. Sridhara, A. Dey, C. Anandan, A.K. Sharma, XPS study of sputtered alumina thin films. Ceram. Int. 40, 11099–11107 (2014)
I.N. Reddy, V.R. Reddy, A. Dey, N. Sridhara, S. Basavaraja, P. Bera, C. Anandan, A.K. Sharma, Microstructural studies of e-beam evaporated alumina thin films. Surf. Eng. 30, 594–599 (2014)
M. Popinciuc, H.T. Jonkman, B.J. van Wees, Energy level alignment at Co/AlOx/pentacene interfaces. J. Appl. Phys. 101, 093701 (2007)
C.S. Yang, J.S. Kim, J.W. Choi, M.H. Kwon, Y.J. Kim, J.G. Choi, G.T. Kim, XPS study of aluminum oxides deposited on PET thin film. J. Ind. Eng. Chem. 6, 149–156 (2000)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Reddy, I.N., Dey, A., Sridhara, N. et al. Corrosion Behaviour of Sputtered Alumina Thin Films. J. Inst. Eng. India Ser. D 96, 105–112 (2015). https://doi.org/10.1007/s40033-015-0072-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40033-015-0072-x