Abstract
A new copolymer (PONTET), composed of dialkoxy napthalene as donor and a carbonylated thieno [3,4-b]thiophene group as an acceptor, was obtained by Suzuki coupling polymerization. The number average molecular weight (M n ) of PONTET is 6.4 kg mol−1 with a polydispersity index of 1.20, determined by gel permeation chromatography using chloroform. PONTET showed broad absorption with a maximum at 534 nm in solution and 618 nm in a thin film, respectively. The hole mobility of PONTET was 1.5×10−3 cm2/Vs and the I on /I off ratio was 7.7×104. The maximum power conversion efficiency of a PONTET:PC70BM (1:4)-based solar cell reached 1.3% with an open circuit voltage (V oc ) of 0.56 V, a short circuit current density (J sc ) of 5.6 mA/cm2, and a fill factor (FF) of 41.3%.
Similar content being viewed by others
References
G. Yu, J. Gao, J. C. Hummelen, F. Wudl, and A. J. Heeger, Science, 270, 1789 (1995).
M. C. Hwang, J. W. Jang, T. K. An, C. E. Park, Y. H. Kim, and S. K. Kwon, Macromolecules, 45, 4520 (2012).
H. J. Son, B. Carsten, I. H. Jung, and L. Yu, Energy Environ. Sci., 5, 8158 (2012).
H. J. Koh, S. H. Jang, C. Y. Kim, S. C. Shin, Y. H. Kim, and S. K. Kwon, J. Nanosci. Nanotechnol., 12, 4299 (2012).
S. H. Jang, D. S. Chung, J. Y. An, I. Kang, H. Kim, C. E. Park, Y. H. Kim, S. K. Kwon, and S. G. Lee, J. Nanosci. Nanotechnol., 12, 4340 (2012).
H. J. Yun, D. S. Chung, I. Kang, J. W. Park, Y. H. Kim and S. K. Kwon J. Mater. Chem., 22, 24924 (2012).
K. Li, Z. Li, K. Feng, X. Xu, L. Wang, and Q. Peng, J. Am. Chem. Soc., 135, 13549 (2013).
I. Kang, T. K. An, J. Hong, H. J. Yun, R. Kim, D. S. Chung, C. E. Park, Y. H. Kim, and S. K. Kwon, Adv. Mater., 25, 524 (2013).
S. O. Kim, T. K. An, J. Chen, I. Kang, S. H. Kang, D. S. Chung, C. E. Park, Y. H. Kim, and S. K. Kwon, Adv. Funct. Mater., 21, 1616 (2011).
M. H. Chen, J. Hou, Z. Hong, G. Yang, S. Sista, L. M. Chen, and Y. Yang, Adv. Mater., 21, 4236 (2009).
Y. Dong, X. Hu, C. Duan, P. Liu, S. Liu, L. Lan, D. Chen, L. Ying, S. Su, X. Gong, F. Huang, and Y. Cao, Adv. Mater., 25, 3683 (2013).
S. O. Kim, Y. S. Kim, H. J. Yun, I. Kang, Y. W. Yoon, N. R. Shin, H. J. Son, H. G. Kim, M. J. Ko, B. S. Kim, K. K. Kim, Y. H. Kim, and S. K. Kwon, Macromolecules, 46, 3861 (2013).
H. Zhou, L. Yang, A. C. Stuart, S. C. Price, S. Liu, and W. You, Angew. Chem. Int. Ed., 50, 2995 (2011).
S. O. Kim, D. S. Chung, H.J. Cha, J. W. Jang Y. H. Kim, J. W. Kang, Y. S. Jeong. C. E. Park, and S. K. Kwon, Sol. Energy Mater. Sol. Cells, 95, 432 (2011).
H. J. Son, W. Wang, T. Xu, Y. Liang, Y. Wu, G. Li, and L. Yu, J. Am. Chem. Soc., 133, 1885 (2011).
H. J. Cha, D. S. Chung, S. Y. Bae, M. J. Lee, T. K. An, J. H. Hwang, K. H. Kim, Y. H. Kim, D. H. Choi, and C. E. Park, Adv. Funct. Mater., 23, 1556 (2013).
I. Kang, H. J. Yun, D. S. Chung, S. K. Kwon, and Y. H. Kim, J. Am. Chem. Soc., 135, 14896 (2013).
J. H. Kwon, H. D. Yeo, H. J. Cha, M. J. Lee, H. T. Park, J. H. Park, C. E. Park, and Y. H. Kim, Macromol. Res., 19, 197 (2011).
J. H. Kwon, J. Y. An, H. M. Jang, S. J. Choi, D. S. Chung, M. J. Lee, H. J. Cha, J. H. Park, C. E. Park, and Y. H. Kim, J. Polym. Sci. Part A: Polym. Chem., 49, 1119 (2011).
S. W. Jeong, G. B. Lee, H. J. Ha, S. K. Kwon, Y. H. Kim, and B. K. Ju, Appl. Phys. Lett., 101, 243301 (2012).
M. J. Baek, S. H. Lee, K. K. Zong, and Y. S. Lee, Synth. Met., 160, 1197 (2010).
L. Huo, S. Zhang, X. Guo, F. Xu, Y. Li, and J. Hou, Angew. Chem. Int. Ed., 50, 9697 (2011).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Lee, G.B., Kim, R., Cha, HJ. et al. New donor-acceptor copolymer containing dialkoxy naphthalene and carbonylated thieno[3,4-b]thiophene for OTFT and OPV. Macromol. Res. 22, 569–573 (2014). https://doi.org/10.1007/s13233-014-2068-z
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13233-014-2068-z