Abstract
Attenuated total reflection (ATR)–Fourier transform infrared (FTIR) spectroscopy was used to characterize the chemical nature of fouling species on different spiral wound membranes operated at Al-Jubail SWRO plant. Three membranes from different companies operated for a period of 1 year were opened for autopsy, and difference spectra were obtained for the fouled membrane from virgin membranes. The spectra of the foulants were easy to distinguish from the spectra of membrane material. The results showed that the membrane surface of the feed end element was more heavily fouled than the brine end of the element. ATR/FTIR indicated a distinct enhancement to the amide I (1650 cm−1) and amide II (1550 cm−1) bands indicative of protein, and the C–O stretching band associated with polysaccharides is visible near 1040 cm−1. The deposits removed from the surface of membranes showed distinctive bands at 3270 and 1080 cm−1 associated with amino group/polysaccharide.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Membrane technology is the most widely used and accepted around the world for the treatment and improvement of various water resources. Advancements in membrane materials and other aspects of membrane desalination technology have lowered overall operating costs, which have ultimately reduced the cost of implementing public water quality improvement programmes. Membrane processes are very effective in removing many harmful constituents in water and are deemed the most appropriate water treatment technology for many years. There are different types of membrane desalination processes used in the potable water treatment field. A particular process should be selected based on the most cost-effective way to remove constituents in the feed water to meet the water quality goals. Reverse osmosis (RO) membranes are found to be more effective in removing majority of constituents. The pore size of a RO membrane is so small that it functions primarily by diffusion instead of filtration or adsorption (Jim 1995). Most of the membranes applicable to water treatment are prepared from synthetic organic polymers and have been classified into cellulosic or non-cellulosic membrane types. The cellulosic types include cellulose diacetate, cellulose triacetate and blends of these. The non-cellulosic types include polyamides (both aliphatic and aromatic), polyurea, polysulfone, etc. (Lozier and Bergman 1990). Manufacturers produce different types of membranes designed for various types of feed water. RO membranes can be classified by cross-sectional form into (1) asymmetric (2) composite. Asymmetric membranes are composed of a single polymer type and contain a thin dense skin that serves as the active desalination barrier layer. Thin-film composite membranes are formed by depositing a very thin polymer film which acts as the active barrier layer onto the surface of a different polymer that serves as the porous support layer (Lozier and Bergman 1990). In spite of several advantages of recently manufactured membranes, composite membranes experienced substantial membrane fouling and/or membrane degradation, due to improperly designed or poorly operated RO system, resulting in the decrease in productivity and also rejection. Membrane fouling could be either chemical or biological. Chemical fouling of membrane is due to particulate, colloidal matter, silica, oxides of metals and mineral scales, viz. CaCO3, CaSO4, Mg (OH)2, Fe (OH)3, FeCl3 and organic matter (David and Rehman 1990; Lepore and Ahlert 1988; Vaugham 1989; Farooque et al. 1999), whereas biological fouling is due to bacteria (Lepore and Ahlert 1988; Vaugham 1989; Farooque et al. 1999; Wolfaardt and Cloete 1992; Brayers and Chraklis 1981; Ridgway 1989; Saad 1992). Degradation of the membranes can be either due to physical deformation or chemical changes (hydrolysis or oxidation). Fouling and degradation of membrane not only reduce the production and quality but also result in increase in operating expenditure. Thus, it is imperative to investigate and understand the causes of any decline in RO system performance and thereby employ necessary measures to avoid either degradation or fouling of membrane. One of the causes of the decline in productivity of RO system is the chemical degradation of RO membrane itself.
Feed water for RO system is generally injected with chlorine as a biocide which can damage the membrane thereby decreasing the salt rejection and increase the permeate rate. Reverse osmosis desalination plant in Jeddah (Phase I) has been in operation since 1989, and it was discovered that due to chlorine attack, quality of permeate deteriorated (David 1991; Green et al. 2011). Chlorinated sea water also contains trace metals (Fujiwara et al. 1994; Kumano et al. 1994), which may either accelerate or retard the degradation of membrane due to their presence with residual chlorine. The presence of trace metals in water may yield a variety of oxidizing and/or reducing species, which may also be responsible for oxidation of membrane. Sea water has both oxidizing and reducing agents in solution (Nagai et al. 1994), which may react and chemically damage the membrane. It was observed that in the first two years performance was satisfactory; however, after two years performance started deteriorating slowly. Recently, it has been found that the variation of transport properties of synthetic membranes in the presence of organic substances is not due to transport coupling but is rather the result of deswelling effects caused by the interaction of the organic substances with at least the active layer of the membrane (Pusch et al. 1989; Pusch 1990). These swelling effects lead to irreversible changes of membrane properties. In another investigation, it was found that fouling is especially determined by the structure of the membrane surface (Pusch et al. 1989). From the above literature review, it is observed that the fouling and/or degradation of the membrane is determined by the structure of the membrane. To understand the structural and surface properties of the membrane, ATR/FTIR study can be used for getting in depth knowledge.
The entire field of polymer studies by FTIR spectrometry is extremely broad. Extensive reviews of Infrared polymer spectrometry are available (Koenig 1980a, , b; D’Esposito and Koenig 1978; Zahid 1993; Griffiths and Haseth 1986; Belfer et al. 1999). Vibrational spectrometry has been applied to the identification of polymeric materials for both qualitative and quantitative determination of chemical composition. Many parameters can be investigated including polymer end groups, chain branching, configuration and steric and geometric isomerism. It can also be used to identify and determine the concentration of impurities, additives and residual monomers in polymeric materials. The effects of external conditions on polymers, the change in state with temperature and pressure as well as the effects of deformation, fatiguing and weathering can also be studied. The analysis of polymers using FTIR spectrometry is done by isolation of spectral features. Spectral subtraction is frequently employed to isolate spectral features of a component in a polymer blend, to remove solvent bands or to isolate spectral features after a chemical reaction or physical change in the sample (Lin et al. 2001). By this method, known as scaled absorbance subtraction, bands of constituents of interest can be isolated and contaminants can be identified. Some studies on the effect of interactions of water and foulants with membrane surfaces by ATR/FTIR have been reported (Cho et al. 1998; Santos and Duarte 1998; MacCarthy and Rice 1985). Recent studies on the characterization on UF membranes used as pretreatment for seawater desalination have been reported using ATR/FTIR as tool (Shona et al. 2009).
But very little literature is available on the characterization of the membrane and effect of foulants on the structure that result in the degradation of the membrane. This paper describes the investigations carried out in detail the structural and surface properties of membranes using ATR/FTIR and for characterization of commercial RO membranes. Also the study presents a comparative study of new and fouled membrane to identify the adsorbed foulants under the following objectives.
-
1.
To identify the functional groups and to understand the structural configuration of virgin (new) RO membranes.
-
2.
To develop a methodology for measuring membrane degradation by ATR/FTIR.
-
3.
To identify adsorbed foulants and observe their effects on the membrane structure.
Experimental
Membranes
Three spiral wound SWRO virgin membranes from different companies Hydranautics (type-SWC4+), Saehan (type RE 8040-SR) and Koch (KPN 8282203) were obtained. Similar membranes were installed at the Al-Jubail seawater reverse osmosis (SWRO) plant. Membranes received pretreated sea water from Al-Jubail SWRO plant pretreatment section. The pretreatment involved the following:
Before dual media filters, ferric chloride was dosed at a concentration of 3.0 mg/l and also sulphuric acid was dosed to maintain a pH value of 6.9 at the inlet of dual media filter. Acid was further dosed just before the cartridge filters to achieve a pH value of 6.8. After the cartridge filters, sodium bisulphite (SBS) was also dosed to remove chlorine from RO feed water. As a dual protection, SBS was also dosed at the suction of high-pressure pumps. Product water was passivated by dosing limewater and carbon dioxide to maintain a positive LSI and was disinfected with calcium hypochlorite (Table 1).
ATIR/FTIR spectroscopy
ATR/FTIR analyses were performed on freeze-dried fouled membrane samples and virgin membranes of about 45 by 10 mm. IR spectra were recorded on a Perkin-Elmer spectrometer (Spectrum one) using UATR accessory. The UATR accessory contained a ZnSe/diamond flat plate crystal at a nominal incident angle of 45°, and an average depth penetration of 2 μm. Each spectrum presented is the result of 32 accumulations obtained with a resolution of 4 cm−1 with air as the background. All the samples were pressed with the same force to obtain equivalent intimate contact between ATR crystal and sample surface. Spectra were corrected to take into account the wavelength dependence of ATR and baseline corrected. Difference spectra of fouled membrane from virgin membrane were obtained by subtraction method using Perkin-Elmer software. The use of spectral subtraction software supplied with FTIR unit allows the ATR spectrum of the clean membrane to be subtracted from that of the fouled membrane leaving only the ATR spectrum of the foulants.
The deposits on the membrane were removed by scraping from the membrane and freeze-dried, and the dried powder was analysed by ATR/FTIR.
Material from membrane swatches
Membrane swatches recovered from the feed and brine end of the RO membranes were divided into strips of known surface area and the biofilm material scrapped off and organic analysis conducted by modified methyl tertiary-butyl ether (MTBE) extraction (Green et al. 2017). Mass recovered was in all the cases normalized with respect to membrane surface area.
Results and discussion
ATR/FTIR results: virgin membranes
A number of problems were encountered in the characterization of RO membranes. These membranes have asymmetric structure generally consisting of a thin selective skin layer supported by porous substructure (Belfer et al. 2000). ATIR/FTIR spectra of virgin membranes are shown in Figs. 1, 2, 3 and 4. All the membranes show almost the same spectral pattern with slightly different intensities. The FTIR spectra are very similar to that reported in the literature for membranes made of Udel polysulphone polymer (Pihlajamäki et al. 1998; Hummel 1984). The three large peaks at 3340, 2920 and 1660 cm−1 represent either aliphatic alcohols or ether alcohols (Hummel 1978). The peaks represent primary, secondary, tertiary and cyclic alcohols, and probably come from the manufacturer’s preservation agent, glycerine. The peaks between wavelengths of 1700–1500 cm−1 are typical of those for a polymer made of Udel polysulphone. The only peak that is unusual for polysulphone occurs at 1040 cm−1. The search programme indicates that this peak comes from an aliphatic alcohol, probably glycerine.
The intensity of peaks for the Saehan polysulphone membrane is much greater than both Koch and Hydranautics membrane. Figure 4 shows ATR/FTIR spectra of all the three virgin membranes.
Visual inspection of the fouled membranes
Visual inspection of membranes surface indicated that the feed surfaces were more heavily fouled than the reject element (Fig. 5). There was a general increase in density of surface foulant towards the feed end of the module. In addition to surface fouling, a brown colouration was noted on both the feed and brine end of the module. Hydranautics membrane indicated a substantial fouling on the membrane and was slightly more fouled than Saehan but less than Koch membrane. However, the membrane autopsy assay revealed that the foulant and its organic content are much higher than that of Saehan and Koch membranes (Fig. 6).
ATR/FTIR results for fouled membranes
Figure 7 shows ATR/FTIR spectra of virgin and fouled Hydranautics membrane. There is a distinct enhancement of the peaks in the range of 3450–3200 and 3080–2850 cm−1 indicative of membrane fouled by either hydroxy (or amino group) or phenoxy group compounds. The enhancement of the peaks at 1650 cm−1 (amide I) and 1550 cm−1 (amide II) is indicative of proteins. High absorption peak at 2920 cm−1 may be probably due to the membrane fouled by phenoxy group. The C–O stretching band associated with carbohydrate or polysaccharides is visible near 1040 cm−1. Figure 8 shows the difference spectrum of the fouled from the virgin Hydranautics membrane. The spectrum reveals that the foulants are composed of either hydroxy or amino groups as distinct from the bands at 3280 and 2920 cm−1. Also the bands at 1650 and 1550 cm−1 may be due to combination of amides and carbonyl groups with other substituents. The peak at 875 cm−1 is probably due to aromatic carbon. The presence of absorption in these regions suggests a significant amount of organic fouling.
As the mass of the foulants on the membrane surfaces increases, it begins to mask the IR spectrum of the membrane. The foulants vibrational bands increase in intensity relative to the membrane vibrational bands of the membrane. It is apparent that the vibrational bands for the membrane in the region 1300–1000 cm−1 (Fig. 7) decrease in magnitude. The negative peaks near 1060 cm−1 are due to over-subtraction of carbohydrate group. The membrane foulant(s) is a mixture of compounds, and thus, the vibrational bands are broader with overlapping bands.
The fouled spectrum for Koch membrane in Fig. 9 shows enhancement of the peaks at 3278 and 2925 cm−1. This is similar to that observed for fouled Hydranautics membrane showing fouling due to amino group, phenol or aryl amine. Also peaks in the region 1600–1100 cm−1 show a distinct enhancement, indicating the membrane is fouled with amide and carbonyl groups. The two negative peaks in the difference spectrum (Fig. 10) at 3200 and 1650 cm−1 are due to over-subtraction of C-H stretching bands. There is evidence of protein on the surface of the membrane as amide I and amide II bands are visible near 1650 and 1550 cm−1.Carbohydrate is also likely to be present as evident from the spectrum showing a peak near 1060 cm−1.
The fouled Saehan membrane spectrum (Fig. 11) shows enhancement of the absorption bands near 3200, 1650 and 1550 cm−1 indicative of either aliphatic secondary amide or amino group, and the C–O stretching band associated with polysaccharides is visible near 1060 cm−1. This is evident from the difference spectrum (Fig. 12) which shows distinct bands in this region. The vibrational bands for the membrane in the region 1300–1000 cm−1 show significant decrease in magnitude indicating fouling of the membrane. Some negative peaks observed in the difference spectrum at 1500, 1240 and 1150 cm−1 are probably due to over-subtraction.
ATR/FTIR of foulant deposits
ATR/FTIR analysis was conducted to investigate the functional groups in the foulant deposits on the membrane surface (Fig. 13). Spectra of foulant deposits for all three membranes showed the bands in the range of 3400–3150 cm−1 indicating either amino or aliphatic secondary amide groups and near 1650 and 1550 cm−1 indicating amide group.
Conclusions
-
1.
ATIR/FTIR spectra of all the three virgin membranes showed almost the same spectral pattern with slightly different intensities. The FTIR spectra are very similar to that reported in the literature for membranes made of Udel polysulphone polymer.
-
2.
Fouled membranes showed a distinct enhancement of the peaks in the range of 3450–3200 and 3080–2850 cm−1 indicating the membranes fouled by either hydroxy (or amino group) or phenoxy group compounds.
-
3.
ATR/FTIR indicated a distinct enhancement to the amide I (1650 cm−1) and amide II (1550 cm−1) bands indicative of protein, and the C–O stretching band associated with polysaccharides is visible near 1040 cm−1.
-
4.
The ATR/FTIR difference spectra and of foulant deposits spectra confirmed that the RO membrane surfaces were mostly proteins and carbohydrates or polysaccharides.
References
Belfer S, Gilron J, Kedem (1999) Characterization of commercial RO and UF modified and fouled membranes by means of ATR/FTIR. Desal 124:175–180
Belfer S, Fainchtain R, Purinson Y, Kedem O (2000) Surface Characterization by FTIR-ATR spectroscopy of polyethersulfone membranes-unmodified, modified and protein fouled. J Membr Sci 172:113–124
Brayers J, Chraklis W (1981) Early fouling biofilm formation in turbulent flow system. Overall kinetics. Water Res. 15:483–491
Cho J, Amy G, Pellegrino J, Yoon Y (1998) Characterization of clean and natural organic matter fouled NF and UF membranes, and foulants characterization. Desal 118:101–108
D’Esposito L, Koenig JL (1978) Applications of FT-IR to synthetic polymers and biological macromolecules. In: Feraro JR, Basile LJ (eds) FT-IR spectroscopy: applications to chemical systems, vol 1. Academic Press, New York
David H (1991) Reverse osmosis: scaling, fouling and chemical attack. Desal Water Reuse 1(4):8–11
David P, Rehman A (1990) Reverse osmosis membrane fouling - the final frontier. Ultra Pure Water 7:25–36
Farooque AM, Ahamed A-A, Numota K (1999), Degradation study of cellulose triacetate hollow fine fiber SWRO membranes. In: WSTA 4th Gulf water conference, Desal. vol 123 (1999) pp 567–573, 165–171
Fujiwara N, Numata K, Kumana A, Ogino Y, Nagai M, Iwahashi H (1994) The effects of heavy metal ions on the oxidation of cellulose triacetate membranes. Desal 96:431–439
Green TN, Saeed MO, Al-Otaibi GF, Al-Mobaid AS (2011) Biofouling process profile of a commercial 24 MGD SWRO Plant, Saudi Arabia. IDA World Congress, Perth
Green TN, Al-Tisan I, Rahman M, Al-Jehani Y, Al-hakamy A-M (2017) Foulant analysis of hollow fine fiber (HFF) membranes in Red Sea SWRO plants using membrane punch autopsy (MPA). Desalination Water Treat 71:45–51
Griffiths PR, Haseth JA (1986) Fourier transform infrared spectrometry, vol 83. Wiley, New York
Hummel DO (1978) Atlas of polymer and plastics analysis. In: Polymers: structure and spectra, vol 1, 2nd ed., Hanser-VCH, Weinheim
Hummel DO (1984) Atlas of polymer and plastics analysis. Part a/II. In: Plastics, fibres, rubbers, resins, starting and auxiliary materials: degradation products, vol 2, 2nd ed., Hanser-VCH, Weinheim
Jim P (1995) General aspects and characteristics of desalination membranes. IDA: 3–35
Koenig JL (1980a) Chemical micro structure of polymer chains. Wiley, New York
Koenig JL (1980b) Applications of FT-IR to polymers. In: Durig JR, Raidal D (eds) Analytical applications of FT-IR to molecular and biological systems. Holland, Dordrecht
Kumano A, Matsui Y, Numata K, Fujiwara N, Iwahashi H, Nagi M (1994) Performance change formula of cellulose triacetate hollow fiber RO membranes due to oxidation and hydrolysis. Desal 96:441–450
Lepore J, Ahlert R (1988) Fouling in membrane process, RO technology B. Parekh Fd. Marcell Deckker NY
Lin C-F, Liu S-H, Hao OJ (2001) Effect of functional groups of humic substances on UF performance. Water Res 35(10):2395–2402
Lozier JC, Bergman RA (1990) Expanding application of membrane processes in water treatment. In: Technical proceedings of the NSWIA biennial conference, vol 1
MacCarthy P, Rice IA (1985) Spectroscopic methods (other than NMR) for determining functionality in humic substances. In: Aiken GR, McKnight DM, Wershaw RL, MacCarthy P (eds) Humic substances in soil, sediment and water: geochemistry, isolation and characterization. Wiley, New York, pp 527–559
Nagai M, Iwahashi Y, Ogino Y (1994) The behavior of an oxidizing/reducing agent in seawater. Desal 96:291–301
Pihlajamäki A, Väisänen P, Nyström M (1998) Characterization of clean and fouled polymeric ultrafiltration membranes by Fourier transform IR spectroscopy-attenuated total reflection, Colloid. Surf A: Physicochem Eng Aspects 138:323–333
Pusch W (1990) Performance of RO membranes in correlation with membrane structure, transport mechanisms of matter and module design (Fouling). State of the Art. Desal 77:35–54
Pusch W, Yu YL, Zheng LY (1989) Solute-solute and solute membrane interactions in hyper filtration of binary and ternary aqueous organic feed solutions. Desal 75:3
Ridgway H (1989) Biofilm of RO membrane, its nature and effect on treatment. Water Reuse
Saad MA (1992) Biofouling prevention on RO polymeric membrane system. Desal 88:85–105
Santos EBH, Duarte AC (1998) The influence of pulp and paper mill effluents on the composition of the humic fraction of aquatic organic matter. Water Res 32(3):597–608
Shona HK, Kima SH, Vigneswarana S, Ben Aimb R, Leec S, Cho J (2009) Physicochemical pretreatment of seawater: fouling reduction and membrane characterization. Desalination 238:10–21
Vaugham D (1989) The evaluation of pre RO filters by SDI. Ultra Pure Water 6(9):22–26
Wolfaardt GM, Cloete TE (1992) The effect of some environment parameters on surface colonization by microorganism. Water Res 26:527–537
Zahid A (1993) Reverse osmosis, membrane technology, water chemistry and industrial applications. Chapman and Hall, New York
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Rahman, M.M., Al-Sulaimi, S. & Farooque, A.M. Characterization of new and fouled SWRO membranes by ATR/FTIR spectroscopy. Appl Water Sci 8, 183 (2018). https://doi.org/10.1007/s13201-018-0806-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s13201-018-0806-7