Abstract
Alkyds are widely used polymers in the coating industry for decorative and industrial applications due to their low price, performance, diversity, and containment of renewable constituents. They have been of particular interest in research over the past decade owing to new legislative requirements focused on the reduction of volatile organic coatings (VOC) and the replacement of Cobalt (Co) driers. In the present work, the commercially accessible Fe (bispidon) drier and the Co (bis (2-ethylhexanoate)) drier were studied in high-solid (HS) alkyd coatings that are consistent with allowed VOC values as stipulated by actual EU legislation. Curing kinetic properties of the alkyd oxidation process were analyzed using FTIR spectroscopy. The influence of Fe and Co driers on crosslinking was further evaluated in terms of viscoelastic properties and surface hardness measurements. Finally, cured coating films were compared with the EIS method in order to determine the influence of driers on crosslinked polymer structures and pore resistance of HS alkyd coatings. We compared Fe and Co driers in HS long-oil alkyd coatings. Coatings with Fe drier showed comparable Final Drying Times but dissimilar crosslinking kinetic activity compared with the Co drier. Fe drier enable more uniformity through the entire thickness of the HS alkyd coating and consequently has lower diffusion of ions through the film.
Similar content being viewed by others
References
Hofland, A, “Alkyd Resins: From Down and Out to Alive and Kicking.” Prog. Org. Coat., 73 274–282 (2012)
Mischke, P, Film Formation. Vincentz, Hanover (2010)
Mirone, G, Marton, B, Vanecso, GJ, “Elastic Modulus Profiles in the Cross Sections of Drying Alkyd Coating Films: Modelling and Experiments.” Eur. Poly. J., 40 549–560 (2004)
Oyman, ZO, “Towards Environmentally Friendly Catalysts for Alkyd Coatings.” PhD thesis, TechnischeUniversiteit Eindhoven, 1–183, 2005
Soucek, MD, Khattab, T, Wu, J, “Review of Autooxidation and Driers.” Prog. Org. Coat., 73 435–454 (2012)
Pilemand, C, Wallström, E, Poulsen, PB, “Substitution of Cobalt Driers and Methyl Ethyl Ketoxime in Oxidative Drying Systems.” Eur. Coat., 2 7–20 (2005)
Lindeboom, J, “Air-Drying High Solids Alkyd Paints for Decorative Coatings.” Prog. Org. Coat., 34 147–151 (1998)
de Boer, JW, Wesenhagen, PV, Wenker, ECM, Maaijen, K, Gol, F, Gibbs, H, Hage, R, “The Quest for Cobalt-free Alkyd Paint Driers.” Eur. J. Inorg. Chem., 2013 3581–3591 (2013)
Erich, SJF, Laven, J, Pel, L, Huinink, HP, Kopinga, K, “NMR Depth Profiling of Drying Alkyd Coatings with Different Catalysts.” Prog. Org. Coat., 55 105–111 (2006)
Erich, SJF, Laven, J, Pel, L, Huinink, HP, Kopinga, K, “Influence of Catalyst Type on the Curing Process and Network Structure of Alkyd Coatings.” Polymer, 47 1141–1149 (2006)
Kalenda, P, Veselý, D, Kalendová, A, Št`áva, V, “Ferrocene-Based Catalyst Systems for Alkyd Paint Drying.” Pigm. Resin. Technol., 39 (6) 342–347 (2010)
Stava, V, Erben, M, Vesely, D, Kalenda, P, “Properties of Metallocene Complexes During the Oxidative Crosslinking of Air Drying Coatings.” J. Phys. Chem. Solids, 68 799–802 (2007)
Erben, M, Veselý, D, Vinklárek, J, Honzíček, J, “Acyl-Substituted Ferrocenes as Driers for Solvent-Borne Alkyd Paints.” J. Mol. Catal. A, 353–354 13–21 (2012)
Micciche, F, Oostveen, E, Van Haveren, J, Van der Linde, R, “The Combination of Reducing Agents/Iron as Environmentally Friendlier Alternatives for Co-Based Driers in the Drying of Alkyd Paints.” Prog. Org. Coat., 53 99–105 (2005)
Tanase, S, Hierso, JC, Bouwman, E, Reedijk, J, ter Borg, J, Bieleman, JH, Schut, A, “New Insights on the Anti-Skinning Effect of Methyl Ethyl Ketoxime in Alkyd Paints.” New J. Chem., 27 854–859 (2003)
ASTM International, “Standard Test Methods for Evaluating Drying or Curing During Film Formation of Organic Coatings Using Mechanical Recorders” Designation 5895–03.
Swartz, NA, Clare, LT, “Understanding the Differences in Film Formation Mechanism of Two Comparable Solvent Based and Water-Borne Coatings on Bronze Substrates by Electrochemical Impedance Spectroscopy.” Electrochim. Acta, 62 199–206 (2012)
Vandenberg, JT, Anderson, DG, Dufler, JK, Julian, JM, Scott, RW, Sutliff, TM, Vaickus, MJ, An Infrared Spectroscopy Atlas for the Coatings Industry. Federation of societies of coatings Technology, Philadelphia, PA (1980)
Ye, G, Courtecuisse, F, Allonas, X, Ley, C, Croutxe-Barghorn, C, Raja, P, Taylor, P, Bescond, G, “Photoassisted Oxypolymerization of Alkyd Resins: Kinetics and Mechanisms.” Prog. Org. Coat., 73 366–373 (2012)
Liu, Z, Kooijman, H, Spek, AL, Bouwman, E, “New Manganese-Based Catalyst Systems for Alkyd Paint Drying.” Prog. Org. Coat., 60 343–349 (2007)
Bouwman, E, Van Gorkum, R, “A Study of New Manganese Complexes as Potential Driers for Alkyd Paints.” J. Coat. Technol. Res., 4 (4) 491–503 (2007)
Preininger, O, Honzíček, J, Vinklárek, J, Erben, M, “The Effect of [(η3-C3H5)(η5-C5H5)Mo(CO2)] on Drying of Solvent-Borne Alkyd Paints.” Prog. Org. Coat., 77 292–297 (2014)
Mezger, TG, The Rheology Handbook. Vincentz, Hanover (2011)
Skale, S, Doleček, V, Slemnik, M, “Subtitution of the Constant Phase Element by Warburg Impedance for Protective Coatings.” Corros. Sci., 49 1045–1055 (2007)
Skale, S, Doleček, V, Slemnik, M, “Impedance Studies of Corrosion Protected Surfaces Covered by Epoxy Poliamide Coating Systems.” Prog. Org. Coat., 62 387–392 (2008)
Acknowledgments
Operation part was financed by the European Union, European Social Fund. Operation was implemented in the framework of the Operational Program for Human Resources Development for the Period 2007-2013, Priority axis 1: Promoting entrepreneurship and adaptability, Main type of activity 1.1: Experts and researchers for competitive enterprises.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Pirš, B., Znoj, B., Skale, S. et al. Iron as an alternative drier for curing of high-solid alkyd coatings. J Coat Technol Res 12, 965–974 (2015). https://doi.org/10.1007/s11998-015-9724-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11998-015-9724-x